Patent Application
20170346145
This application claims under 35 U.S.C. §119(a) the benefit of Korean Patent Application No. 10-2016-0063583, filed on May 24, 2016, the entire contents of which are incorporated herein by reference in its entirety for all purposes.
Exemplary embodiments of the present invention relate to a technology for aluminum material to which a diecasting method may be applied. In some embodiments, an aluminum alloy composition for diecasting having improved thermal conductivity and castability can be made by optimizing the silicon (Si) content in order to improve flowability of an aluminum molten metal. In some instances, the aluminum alloy includes a total content of elements except for silicon (Si) and iron (Fe) not to exceed 0.3 wt %. Also provided is a heat sink for a battery using such an aluminum alloy for diecasting having improved thermal conductivity and castability. Provided herein is a heat sink that can be used for indirect cooling of a high voltage battery system for an environmentally-friendly vehicle, and a manufacturing method thereof.
Since electronic control of a vehicle is increasing and higher output of an electronic device is promoted, heat radiation has emerged as a problem. There is a need for materials with desirable heat radiation characteristics and properties.
Generally, an aluminum alloy can be applied to parts for diecasting. In some cases, an Al—Si alloy such as ADC3, ADC10, and ADC12, and an Al—Mg alloy such as ADC5 or ADC6 can be used. Although, these aluminum alloys have excellent strength, the have low thermal conductivity due to components added during the production of the alloy. As such, there are limitations to the use of these aluminum alloys for heat radiation parts.
For example with ADC10 and ACD12 alloys which are optimized for a diecasting method, their thermal conductivity is 98 W/(m·K), which corresponds to 43% of that of pure aluminum (230 W/(m·K)). Thus, there are problems with using such materials for manufacturing a housing requiring heat management or a heat sink.
Components such as silicon (Si) and copper (Cu), magnesium (Mg), iron (Fe), zinc (Zn) and nickel (Ni) can be regulated or adjusted in order to increase its thermal conductivity. A composition of the existing aluminum alloy is as shown in Table 1 below.
Specifically, the existing aluminum alloy material as shown in Table 1 has problems as follows.
In the case of an aluminum alloy material A that mainly regulates silicon (Si) and copper (Cu) components, many alloy elements are added in the process in order to improve flowability of a molten metal and seizure to a mold, such that thermal conductivity of the alloy is deteriorated. In particular, when the content of copper (Cu) component which is a main reinforcement material of the aluminum alloy, is excessively large, the thermal conductivity is decreased and hot shortness occurs during the diecasting method.
In the case of an aluminum alloy material B or C that regulates silicon (Si), magnesium (Mg), iron (Fe), boron (B) components, thermal conductivity is remarkably improved as compared to the material A. However, since the content of silicon (Si) component in material B or C is smaller than the reference level, flowability of a molten metal is significantly deteriorated. Accordingly, the material B or C may not be used in a diecasting method which is mainly used for vehicles.
Material D of Table 1 is an aluminum extruded material, and can have an excellent thermal conductivity of about 180 to 200 W/(m·K) by decreasing a content of zinc (Zn), copper (Cu), magnesium (Mg), etc. Unfortunately, material D can only be used in an extrusion process to manufacture a product, and the diecasting method may not be used. With such an extruded material, the material is 70% more expensive compared to a diecasting material. Therefore it is disadvantageous in terms of cost of parts, and due to characteristics of the extrusion process, the degree of freedom of design is significantly deteriorated and the design constraints are increased.
Accordingly, there is a need for aluminum alloy compositions for diecasting methods that have excellent thermal conductivity.
A high voltage battery used for an environmentally-friendly vehicle is an energy supply source that flows a large amount of current with hundreds of volts of high direct current voltage to drive a driving motor of a vehicle, and supplies power to electric parts for a vehicle. In the high voltage battery, a direct cooling method in which each battery cell is directly cooled using an air or a cooling water in order to control heat in the battery has been mainly used. Recently, an indirect cooling method in which a battery cell is cooled by mounting a heat sink and flowing a cooling fluid only on an upper part thereof in order to increase output efficiency per battery volume that affects capacity of the battery, has been developed and used.
For the indirect cooling method described in the related art, only a heat sink manufactured by forming a lower part of a portion that surface-contacts the battery cells using an aluminum plate, forming a portion that contacts a cooling fluid in a fin shape using an aluminum extruded material, and the like, and assembling them, respectively, has been developed and applied. Therefore, a complicated process of assembling the heat sink with the battery cell and again assembling plastic injection molded articles to form an appearance after manufacturing the heat sink needs to be performed.
An embodiment of the present invention is directed to a new aluminum alloy material that may be used as a material at the time of manufacturing an electronic part requiring heat radiation characteristics or part for a vehicle using a diecasting method.
Specifically, an embodiment of the present invention is directed to an aluminum alloy for diecasting to which a diecasting method having high degree of freedom of design by optimizing a content of silicon (Si) and iron (Fe) and a content of elements except for silicon (Si) and iron (Fe) may be applied, and of which thermal conductivity is high.
Another embodiment of the present invention is directed to a heat sink for a battery capable of performing insert injection molding of a plastic structure by integrally manufacturing a lower part contacting battery cells and an upper part contacting a cooling fluid using the aluminum alloy for diecasting by a diecasting method without a separate assembly process, and a manufacturing method thereof.
In accordance with an embodiment of the present invention, an aluminum alloy for diecasting contains about 10.0 wt % to about 12.0 wt % (e.g., about 10.0 wt %, 10.1 wt %, 10.2 wt %, 10.3 wt %, 10.4 wt %, 10.5 wt %, 10.6 wt %, 10.7 wt %, 10.8 wt %, 10.9 wt %, 11.0 wt %, 11.1 wt %, 11.2 wt %, 11.3 wt %, 11.4 wt %, 11.5 wt %, 11.6 wt %, 11.7 wt %, 11.8 wt %, 11.9 wt %, or about 12.0 wt %) of silicon (Si), about 0.5 wt % to about 0.8 wt % (e.g., about 0.5 wt %, 0.6 wt %, 0.7 wt %, or about 0.8 wt %) of iron (Fe), about 0.3 wt % or less (e.g., about 0.3 wt %, 0.28 wt %, 0.25 wt %, 0.2 wt %, 0.1 wt %, or less) of impurities, and remainder of aluminum (Al).
A term “impurities” mean materials except for silicon (Si), iron (Fe), and aluminum (Al) in the aluminum alloy, and the impurities preferably may include one or more elements selected from zinc (Zn), copper (Cu), manganese (Mn), magnesium (Mg), chromium (Cr), nickel (Ni), titanium (Ti), boron (B), and tin (Sn). Here, any impurities that may be used in the art may be used without particular limitation in addition to the above described impurities.
Thermal conductivity of the aluminum alloy for diecasting of which the contained materials have above described content range may be about 167 W/(m·K) or more (e.g., about 167 W/(m·K), 170. 175, 180, 185, 190, 200, 230, 250, 300, 500 W/(m·K), or more).
In accordance with another embodiment of the present invention, a heat sink for a battery includes: a radiation fin part 31 including a plurality of radiation fins 21 that radiate heat by contacting a cooling fluid; and a thin wall part 11 disposed at a lower end of the radiation fin part 31 and surface-contacting battery cells to transfer heat to the radiation fin 21 contacting the cooling fluid, in which fastening holes 50 for performing insert injection molding of a plastic structure are formed at both ends of the thin wall part 11, and the radiation fin part 31 and the thin wall part 11 are integrally manufactured using a single material by diecasting.
Two or more fastening holes 50 may be formed at one side end of the thin wall part, and preferably, two fastening holes may be formed.
The radiation fin part 31 may include the plurality of radiation fins formed to be spaced apart from each other at a predetermined distance in a direction orthogonal to a direction of a surface of the thin wall part 11 and be integrally formed on an upper end of the thin wall part 11.
The radiation fins may have a height of about 1.5 cm to about 3 cm (e.g., about 1.5 cm, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2.7, 2.8, 2.9 or about 3 cm), a thickness of from about 0.8 mm to about 5 mm (e.g., about 0.8 mm, 0.9 mm, 1 mm 1.1 mm, 1.2 mm, 1.3 mm, 1.4 mm, 1.5 mm, 1.6 mm, 1.7 mm, 1.8 mm, 1.9 mm, 2 mm, 2.1 mm, 2.2 mm, 2.3 mm, 2.4 mm, 2.5 mm, 2.6 mm, 2.7 mm, 2.8 mm, 2.9 mm, 3 mm, 3.1 mm, 3.2 mm, 3.3 mm, 3.4 mm, 3.5 mm, 3.6 mm, 3.7 mm, 3.8 mm, 3.9 mm, 4 mm, 4.1 mm, 4.2 mm, 4.3 mm, 4.4 mm, 4.5 mm, 4.6 mm, 4.7 mm, 4.8 mm, 4.9 mm, or about 5 mm) and a pitch of from about 2 mm to about 10 mm (e.g., about 2 mm, 3 mm 4 mm 5 mm, 6 mm, 7 mm 8 mm 9 mm, or about 10 mm).
The thin wall part may have a thickness of from about 0.8 mm to about 1.5 mm (e.g., about 0.8 mm, 0.9 mm, 1 mm 1.1 mm, 1.2 mm, 1.3 mm, 1.4 mm, 1.5 mm).
The single material forming the heat sink for a battery may be an aluminum alloy containing about 10.0 wt % to about 12.0 wt % (e.g., about 10.0 wt %, 10.1 wt %, 10.2 wt %, 10.3 wt %, 10.4 wt %, 10.5 wt %, 10.6 wt %, 10.7 wt %, 10.8 wt %, 10.9 wt %, 11.0 wt %, 11.1 wt %, 11.2 wt %, 11.3 wt %, 11.4 wt %, 11.5 wt %, 11.6 wt %, 11.7 wt %, 11.8 wt %, 11.9 wt %, or about 12.0 wt %) of silicon (Si), about 0.5 wt % to about 0.8 wt % (e.g., about 0.5 wt %, 0.6 wt %, 0.7 wt % or about 0.8 wt %) of iron (Fe), about 0.3 wt % or less (e.g., about 0.3 wt %, 0.28 wt %, 0.25 wt %, 0.2 wt %, 0.1 wt % or less) of impurities, and remainder of aluminum (Al), and the impurities may include one or more elements selected from zinc (Zn), copper (Cu), manganese (Mn), magnesium (Mg), chromium (Cr), nickel (Ni), titanium (Ti), boron (B), and tin (Sn).
Thermal conductivity of the heat sink for a battery may be about 190 W/(m·K) or more (e.g., about 190, 200, 210, 230, 250, 300, 350, 500 W/(m·K) or more).
In accordance with another embodiment of the present invention, a manufacturing method of a heat sink for a battery includes: a molten metal forming step of forming a molten metal by dissolving about 10.0 wt % to about 12.0 wt % (e.g., about 10.0 wt %, 10.1 wt %, 10.2 wt %, 10.3 wt %, 10.4 wt %, 10.5 wt %, 10.6 wt %, 10.7 wt %, 10.8 wt %, 10.9 wt %, 11.0 wt %, 11.1 wt %, 11.2 wt %, 11.3 wt %, 11.4 wt %, 11.5 wt %, 11.6 wt %, 11.7 wt %, 11.8 wt %, 11.9 wt %, or about 12.0 wt %) of silicon (Si), about 0.5 wt % to about 0.8 wt % (e.g., about 0.5 wt %, 0.6 wt %, 0.7 wt % or about 0.8 wt %) of iron (Fe), 0.3 wt % or less of impurities, and remainder of aluminum (Al); a diecasting step of injecting the molten metal into a diecasting mold to form the heat sink for a battery; and an aging heat treatment step of heat treating the heat sink for a battery for 6 hours after raising a temperature of the heat sink for a battery to from about 250° C. to about 350° C. (e.g., about 250° C., about 260° C., about 270° C., about 280° C., about 290° C., about 300° C., about 310° C., about 320° C., about 330° C., about 340° C., or about 350° C., and then slowly cooling the heat sink for a battery.
In the diecasting step, the molten metal is injected into the diecasting mold using a plunger, a pressurizing speed of the plunger may be divided into a first speed section and a second speed section having different pressurizing speeds, a pressurizing speed in the second speed section may be faster than that in the first speed section, and the pressurizing speed in the second speed section may be from about 3 m/s to about 3.5 m/s (e.g., about 3 m/s, 3.1 m/s, 3.2 m/s, 3.3 m/s, 3.4 m/s, or about 3.5 m/s).
If the speed in the second speed section is less than 3 m/s, the molten metal is not properly injected into the diecasting mold, such that insufficiently molded portions present, that is, a portion formed at a thin thickness is insufficiently molded, and if the speed in the second speed section is greater than 3.5 m/s, since the speed is high, air may be excessively mixed, thereby affecting the quality of products.
In the aging heat treatment step, a heating rate is faster than a cooling rate in terms of temperature change per unit time.
In the specification, it is to be noted that the terms “comprising”, “including”, or “adding”, and the like, are not construed as necessarily including several components or several steps described in the specification and some of the above components or steps may not be included or additional components or steps are construed may be further included.
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings, and the embodiments may be modified in various different ways by a person having ordinary skill in the art to which the present invention pertains, thus the present invention is not limited to the embodiments described herein.
A range of a content of composition of an aluminum alloy for diecasting according to the present invention is as shown in Table 2 below. A term “impurities” in Table 2 indicates a total content of elements except for aluminum (Al), silicon (Si), and iron (Fe).
Generally, in the aluminum alloy for diecasting, flowability of an aluminum molten metal is the most important factor. The flowability of the molten metal is changed depending on an added element of the aluminum alloy, and in particular, the flowability of the molten metal is determined depending on a content of silicon (Si).
Silicon (Si), which is a main component of the aluminum alloy for diecasting of the present invention, plays an important role of improving formability of a product as a result of improving the flowability of the aluminum molten metal, and it is preferable that a content of silicon (Si) is about 10.0 wt % to about 12.0 wt % (e.g., about 10.0 wt %, 10.1 wt %, 10.2 wt %, 10.3 wt %, 10.4 wt %, 10.5 wt %, 10.6 wt %, 10.7 wt %, 10.8 wt %, 10.9 wt %, 11.0 wt %, 11.1 wt %, 11.2 wt %, 11.3 wt %, 11.4 wt %, 11.5 wt %, 11.6 wt %, 11.7 wt %, 11.8 wt %, 11.9 wt %, or about 12.0 wt %) based on the total weight of the aluminum alloy.
When a content of silicon (Si) is less than 10 wt %, for example, a product manufactured using an aluminum alloy containing silicon of 8 wt % and iron (Fe) of 1.0 wt %, flowability of a molten metal is deteriorated, such that insufficiently molded portions may present in the product or a shape of the product may be deformed.
When the content of silicon (Si) is greater than 12.0 wt %, the flowability of the molten metal is excessively increased, such that an excessive amount of gas pockets occur. As a result, bubbles are generated in the product manufactured by diecasting, thereby causing a quality problem.
Iron (Fe), which is another main component of the aluminum alloy for diecasting of the present invention, is to remove seizure between the aluminum alloy and a diecasting mold at the time of taking the aluminum alloy out in the diecasting process. It is preferable that a content of iron (Fe) is about 0.5 wt % to about 0.8 wt % (e.g., about 0.5 wt %, 0.6 wt %, 0.7 wt %, or about 0.8 wt %) based on the total weight of the aluminum alloy. When the content of iron (Fe) is less than 0.5 wt %, since the content is small, the seizure between the diecasting mold and the aluminum alloy occurs, and when the content of iron (Fe) is greater than 0.8 wt %, since the content of iron (Fe) is large, corrosion resistance of the aluminum alloy is deteriorated.
In the aluminum alloy for diecasting of the present invention, a content of impurities which are elements except for aluminum (Al), silicon (Si), and iron (Fe) is about 0.3 wt % or less (e.g., about 0.3 wt %, 0.29 wt %, 0.28 wt %, 0.27 wt %, 0.26 wt %, 0.25 wt %, 0.24 wt %, 0.23 wt %, 0.22 wt %, 0.21 wt %, 0.2 wt %, 0.19 wt %, 0.18 wt %, 0.17 wt %, 0.16 wt %, 0.15 wt %, 0.14 wt %, 0.13 wt %, 0.12 wt %, 0.11 wt %, 0.1 wt %, 0.09 wt %, 0.08 wt %, 0.07 wt %, 0.06 wt %, 0.05 wt %, or less) based on the total weight of the aluminum alloy, and when the content of impurities is greater than 0.3 wt %, since the content of impurities is large, thermal conductivity is decreased.
Tables 3 and 4 show measurement results of thermal conductivity depending on the content of copper (cu) and magnesium as impurities, respectively.
As shown in Table 3, in Comparative Examples 1 and 2 in which the content of copper (Cu) as impurities is greater than 0.3%, it may be confirmed that both of the thermal conductivity at 25° C. and the thermal conductivity at 100° C. were less than 150 W/(m·K), which is lower than 169 W/(m·K) of the thermal conductivity at 25° C. and 170 W/(m·K) of the thermal conductivity at 100° C. in Example 1 in which the content of impurities is less than 0.3 wt %.
Further, as shown in Table 4, in Comparative Examples 3 and 4 in which the content of magnesium (Mg) as impurities is greater than 0.3%, both of the thermal conductivity at 25° C. and the thermal conductivity at 100° C. were less than 150 W/(m·K), similar to Comparative Examples 1 and 2 described above. The thermal conductivity of less than 150 W/(m·K) is much lower than 167 W/(m·K) of the thermal conductivity at 25° C. and 168 W/(m·K) of the thermal conductivity at 100° C. in Example 2.
That is, the aluminum alloy for diecasting of the present invention has thermal conductivity of about 167 W/(m·K) or more by containing the impurities in a content of 0.3 wt % or less.
Hereinafter, a heat sink for a battery using an aluminum alloy for diecasting and a manufacturing method thereof will be described in more detail through a detailed embodiment.
As shown in
As such, the existing assembly type heat sink is manufactured by forming the lower part 10 and the upper part 30 using different materials, that is, forming the lower part 10 using an aluminum plate and forming the upper part 30 in a fin shape using an aluminum extruded material, etc. that is not for diecasting, and assembling the lower part 10 and the upper part 30. Therefore, defect rate of the heat sink in a manufacturing process is increased, and in particular, heat resistance of the assembly part mechanically fastening the upper part and the lower part is increased, as a result, performance of the battery may be deteriorated. Further, when manufacturing the battery cell by assembling the heat sink, an additional process of separately manufacturing respective plastic structures and assembling the plastic structures is required.
As illustrated in
Specifically, in the heat sink for a battery of the present invention, the radiation fin part 31 includes the plurality of radiation fins 21 formed to be spaced apart from each other at a predetermined distance in a direction orthogonal to a direction of a surface of the thin wall part 11.
Since the radiation fins need to have a shape and arrangement suitable for heat radiation so as to radiate heat to the air or the cooling fluid well, the radiation fins 21 of the present invention preferably, have a height of from about 1.5 cm to about 3 cm (e.g., about 1.5 cm, 1.6 cm, 1.7 cm, 1.8 cm, 1.9 cm, 2.0 cm, 2.1 cm, 2.2 cm, 2.3 cm, 2.4 cm, 2.5 cm, 2.6 cm, 2.7 cm, 2.8 cm, 2.9 cm, or about 3 cm), a thickness of from about 0.8 mm to 5 mm (e.g., about 0.8 mm, 1, 2, 3, 4, or about 5 mm), and a pitch of from about 2 mm to about 10 mm (e.g., about 2 mm, 3, 4, 5, 6, 7, 8, 9, or about 10 mm). When the size and the pitch of the radiation fins 21 deviate from the above range, formability of diecasting is deteriorated and the structure suitable for radiation may not be achieved, such that the heat from the battery cells may not be smoothly radiated.
Further, the thin wall part 11 may have a thickness of from about 0.8 mm to about 1.5 mm (e.g., about 0.8 mm, 0.9 mm, 1 mm, 1.1 mm, 1.2 mm, 1.3 mm, 1.4 mm or about 1.5 mm), most preferably, 1.2 mm.
The thin wall part 11 serves to allow the heat sink to perform smooth radiation by surface-contacting the battery cells, and thus flatness of the surface of the thin wall part is important. If the thickness of the thin wall part is less than 0.8 mm, since the thickness is too thin, the flatness may be decreased. Further, since the heat sink is provided between the battery cells in the indirect cooling type battery module as in
The heat sink for a battery of the present invention is integrally formed using a single material. Here, the single material means the aluminum alloy for diecasting described above, the aluminum alloy containing from about 10.0 wt % to about 12.0 wt % (e.g., about 10.0 wt %, 10.1 wt %, 10.2 wt %, 10.3 wt %, 10.4 wt %, 10.5 wt %, 10.6 wt %, 10.7 wt %, 10.8 wt %, 10.9 wt %, 11.0 wt %, 11.1 wt %, 11.2 wt %, 11.3 wt %, 11.4 wt %, 11.5 wt %, 11.6 wt %, 11.7 wt %, 11.8 wt %, 11.9 wt %, or about 12.0 wt %) of silicon (Si), from about 0.5 wt % to about 0.8 wt % (e.g., about 0.5 wt %, 0.6 wt %, 0.7 wt % or about 0.8 wt %) of iron (Fe), from about 0.3 wt % or less (e.g., about 0.3 wt %, 0.29 wt %, 0.28 wt %, 0.27 wt %, 0.26 wt %, 0.25 wt %, 0.24 wt %, 0.23 wt %, 0.22 wt %, 0.21 wt %, 0.2 wt %, 0.19 wt %, 0.18 wt %, 0.17 wt %, 0.16 wt %, 0.15 wt %, 0.14 wt %, 0.13 wt %, 0.12 wt %, 0.11 wt %, 0.1 wt %, 0.09 wt %, 0.08 wt %, 0.07 wt %, 0.06 wt %, 0.05 wt % or less) of impurities, and remainder of aluminum (Al).
A manufacturing method of a heat sink for a battery of the present invention sequentially includes a molten metal forming step of forming a molten metal, a diecasting step, and an aging heat treatment step of heat-treating the heat sink for a battery formed through the diecasting step.
In the molten metal forming step, a molten metal is formed by dissolving an aluminum alloy. The molten metal is formed by dissolving an aluminum alloy containing from about 10.0 wt % to about 12.0 wt % (e.g., about 10.0 wt %, 10.1 wt %, 10.2 wt %, 10.3 wt %, 10.4 wt %, 10.5 wt %, 10.6 wt %, 10.7 wt %, 10.8 wt %, 10.9 wt %, 11.0 wt %, 11.1 wt %, 11.2 wt %, 11.3 wt %, 11.4 wt %, 11.5 wt %, 11.6 wt %, 11.7 wt %, 11.8 wt %, 11.9 wt %, or about 12.0 wt %) of silicon (Si), from about 0.5 wt % to from about 0.8 wt % (e.g., about 0.5 wt %, 0.6 wt %, 0.7 wt % or about 0.8 wt %) of iron (Fe), from about 0.3 wt % or less (e.g., about 0.3 wt %, 0.29 wt %, 0.28 wt %, 0.27 wt %, 0.26 wt %, 0.25 wt %, 0.24 wt %, 0.23 wt %, 0.22 wt %, 0.21 wt %, 0.2 wt %, 0.19 wt %, 0.18 wt %, 0.17 wt %, 0.16 wt %, 0.15 wt %, 0.14 wt %, 0.13 wt %, 0.12 wt %, 0.11 wt %, 0.1 wt %, 0.09 wt %, 0.08 wt %, 0.07 wt %, 0.06 wt %, 0.05 wt % or less) of impurities, and remainder of aluminum (Al). Here, it is preferable that a temperature of the molten metal is maintained at 740° C. to 760° C.
Next, in the diecasting step, a diecasting process of forming the heat sink for a battery which is a molded article of the aluminum alloy by injecting the molten metal into a diecasting mold is performed. First, the diecasting mold is preheated to a temperature of 190° C. to 240° C. in advance before injecting the molten metal. If a temperature of the mold is lower than 190° C., the molten metal is cooled such that injectability is deteriorated. On the contrary, if the temperature of the mold is higher than 240° C., since the temperature is too high, a significant amount of time is required to cool the molten metal, as a result, work time may be increased.
The molten metal is injected into the preheated diecasting mold using a cylinder rod, a piston, or a plunger, and preferably, the molten metal obtained by dissolving the aluminum alloy is put into an injection sleeve and injected into the diecasting mold using the plunger.
Here, when injecting the molten metal using the plunger, a pressurizing speed of the plunger includes a first speed section in which the pressurizing speed of the plunger is low and a second speed section in which the pressurizing speed of the plunger is high. First, in the first speed section of low speed, the plunger is moved to let the air in the injection sleeve out so that the molten metal is filled in the sleeve, and then in the second speed section of high speed, the molten metal is injected into the diecasting mold at high speed.
It is preferable that the speed in the first speed section is from about 0.1 m/s to about 0.4 m/s, and the speed in the first speed section is from about 3 m/s to about 3.5 m/s. Here, a point at which the first speed section is changed to the second speed section is set to from about 245 mm to about 255 mm (e.g., about 245 mm, 246 mm, 247 mm, 248 mm, 249 mm, 250 mm, 251 mm, 252 mm, 253 mm, 254 mm, or about 255 mm).
If the speed in the second speed section is less than 3 m/s, the molten metal is not properly injected into the diecasting mold, such that insufficiently molded portions present, that is, a portion formed at a thin thickness is insufficiently molded, and if the speed in the second speed section is greater than 3.5 m/s, since the speed is high, air may be excessively mixed, thereby affecting the quality of products.
After cooling the molted metal injected into the diecasting mold for a predetermined time, the integral heat sink for a battery is taken out by opening up the mold.
The aging heat treatment step that is T5 heat treatment (artificial aging) is performed on the heat sink for a battery taken out from the mold in order to improve thermal conductivity. Preferably, after raising the temperature of the heat sink for a battery to from about 250° C. to about 350° C., the heat sink for a battery is heat treated for 6 hours and then cooled to a predetermined temperature or lower. In this case, in performing the aging heat treatment, a heating rate is faster than a cooling rate in terms of temperature change per unit time.
In a case of performing the heat treatment at a temperature lower than 250° C. increase in thermal conductivity may be insufficient, on the contrary, In a case of performing the heat treatment at a high temperature of 350° C. or higher, due to characteristics of the diecasting method, bubbles in the product move to a surface of the product to make the surface uneven, or blister phenomenon in which blisters are generated occur. As a result, the product may not be used as a final product.
In the aging heat treatment step, the product is heated again relatively fast, maintained for 6 hours, and cooled relatively slow, thereby making the aluminum alloy be in a stable equilibrium state to improve thermal conductivity.
Although a result of thermal conductivity of the product after performing the aging heat treatment is not shown in the drawing, the thermal conductivity was measured as 190 W/(m·K) more, and it was confirmed that the thermal conductivity is remarkably improved through the aging heat treatment.
After the aging heat treatment step, the manufacturing method of an integral heat sink for a battery which is a final molded article may further include a step of integrally forming the thin wall part 11 of the heat sink for a battery and a plastic structure by the insert injection molding process.
As described above, the heat sink for a battery of the present invention is manufactured by integrally forming the radiation fin part and the thin wall part by the diecasting method and thus the process of separately assembling the parts is removed, and in manufacturing the battery cell, the plastic structure is integrally formed with the integral heat sink for a battery by insert injection molding, thereby significantly simplifying the manufacturing process of the heat sink.
As described above, in the aluminum alloy for diecasting according to the embodiment of the present invention, the content of silicon (Si) and the content of iron (Fe) are optimized and the total content of impurities which are elements except for silicon (Si), iron (Fe), and Aluminum (Al) is adjusted not to exceed 0.3 wt %. As a result, the aluminum alloy for diecasting of the present invention has thermal conductivity of minimum 167 W/(m·K) or more, that is, may improve thermal conductivity by 200%, as compared to ADC10 or ADC12 which is the existing general aluminum alloy for diecasting that is commercially available.
Further, even in a case in which diecasting is continuously performed 1,000 times or more by using the aluminum alloy for diecasting of the present invention, the problem of formability, seizure of product, or the like did not occur at all, and quality problems of the molded article such as insufficiently molded portions in the product or bubbles in the external surface did not occur. Therefore, it may be appreciated that the aluminum alloy for diecasting of the present invention satisfies the formability requirement of the aluminum alloy for diecasting.
Further, the heat sink for a battery of the present invention is integrally manufactured using a single material through the diecasting process to simplify the manufacturing process, and the shape of the radiation fin may be controlled in the diecasting mold, thereby easily changing the shape of the radiation fin for each optimal temperature of the battery. As a result, temperature control may be easily performed.
Further, in the manufacturing method of a heat sink for a battery of the present invention, the aging heat treatment is performed to stabilize the aluminum alloy, such that the thermal conductivity of the heat sink for a battery is remarkably improved to 190 W/(m·K) or more, thereby manufacturing the heat sink for a battery having excellent heat radiation characteristic.
In accordance with the embodiments of the present invention, the aluminum alloy for diecasting has thermal conductivity of minimum 165 W/(m·K), which corresponds to about 75% of thermal conductivity of pure aluminum. The aluminum alloy for diecasting has an effect of improving the thermal conductivity by 200% as compared to ADC10 or ADC12 which is the existing general aluminum alloy for diecasting that is commercially available.
In the case of manufacturing a heat sink or a case of parts requiring heat management using the aluminum alloy of the present invention, weight reduction is possible while maintaining the same performance, such that cost of the material is reduced, and accordingly, cost of the product may also be reduced.
The aluminum alloy for diecasting of the present invention may be molded to have a complicated shape using the diecasting method by adjusting a content of silicon (Si) and iron (Fe), that is, has improved castability as compared to the existing aluminum material having high thermal conductivity. Further, the aluminum alloy for diecasting of the present invention has an effect of increasing the life of the diecasting mold to a hundred thousand shots from fifty thousand shots of the existing aluminum material for diecasting.
In accordance with the embodiments of the present invention, the heat sink for a battery has an effect of remarkably decreasing defect rate as compared to the existing assembly type heat sink by removing the assembling process by integrally manufacturing the upper part and the lower part unlike the existing assembly type heat sink in which the upper part and the lower part having each function are separately manufactured and assembled.
Further, in accordance with the embodiments of the present invention, the heat sink for a battery may be continuously casted by using the diecasting method, and in the manufacturing process of the heat sink of the present invention, the insert injection molding of the plastic structure is possible, thereby having an effect of remarkably simplifying the overall manufacturing process of the high voltage battery system and significantly decreasing the manufacturing cost.
Further, the problem of heat resistance by the mechanical fastening that the existing assembly type heat sink has may be solved by integrally manufacturing the heat sink, thereby improving the performance of the high voltage battery.
Further, in accordance with the embodiments of the present invention, the heat sink for a battery is manufactured through the diecasting process, such that the shape of the radiation fin may be controlled in the diecasting mold, thereby easily changing the shape of the radiation fin for each optimal temperature of the battery.
The above described embodiments are provided only for a person having ordinary skill in the art to which the present invention pertains to easily practice the present invention, and the present invention is not limited to the above described embodiment and the accompanying drawings. Therefore, various substitutions, modifications, and alterations are possible, without departing from the scope and spirit of the present invention.