The present invention relates to a sulfur dioxide gas generating polymer or plastic articles formed by a multilayer coextrusion, not lamination. This coextrusion multilayer article can be used for film, sheets, liners, covers, pads, foams and bags, for preventing, retarding, controlling, delaying or killing microbiological contamination in foods, agricultural crops and botanicals.
Polymers and plastics are generally employed in agricultural product packaging to preserve desirable product traits such as freshness, taste, flavor, color and odor by functioning as a barrier against moisture, oxygen, carbon dioxide, ethylene, and odors. Inside the barrier an isolated, dynamic environment is created that changes with storage time and storage conditions, such as temperature. Products that contain high water content, such as melons, grapes, berries, meat, seafood, and dairy products, release trapped moisture that accumulates over time. Problematically, the packaged products are invariably contaminated by a residual, inoculated concentration of microbes or bioburden. The trapped high moisture atmosphere and availability of nutrients creates favorable conditions for rapid microbe growth and product spoilage.
Gases generating devices and compositions have been used during packing, transportation and storage of foods, agricultural crops and botanicals for protection from spoilage due to microbiological contamination from molds, fungus, viruses and bacteria. With the ever-increasing globalization of the food and agricultural industries, more products are being shipped greater distances than in the past. The result is extended transportation and storage times with the concomitant need for more effective preservation.
Sulfur dioxide gas has been found to be particularly well suited against mold and fungi and has been used extensively to control gray mould decay (Botrytis cineria sp) induced in packed grapes, berries, leeches, and other fresh produce as well as a proven antioxidant effectiveness against the browning process of green tissues present in fruit, vegetables and flowers.
The present invention is directed to a gas generating and gas releasing from a multilayer coextruded film. The present invention can provide a sulphur dioxide generator, which will maintain an acceptable sulphur dioxide concentration level inside a packaging container, a bag or liner for a period of weeks during shipping or for months if the agricultural crops and fresh produce are stored for late season sale.
The present invention is a multilayer coextrusion, not lamination, which provides a sulfur dioxide generator which includes two or more structural layers forming a film (≦15 mil thickness) or a sheet (≧15 mil thickness) of gas permeable material with an active substance incorporated in one or between them. The coextruded active substances includes a material dispersed therein which, in the presence of moisture, release sulphur dioxide gas.
The present invention is directed to a gas generating and gas releasing from a multilayer coextruded article consisting essentially of between 40% and 99.9% by weight of a polymer and between 0.1% and 70% by weight of a gas generating solid dispersed into the polymer matrix.
The present invention involves a multilayer coextruded article, which consists essentially of a multilayer polymeric film or sheet. The three layered film structure was conjoined by means of blown or cast film coextrusion (
The present invention involves a multilayer coextrued film, the inner layer of the article being an olefin, such as a low density polyethylene (LDPE) having a density range of 0.89 to 0.93. The LDPE allows water vapor into the active layer thus to generate sulphur dioxide gas. The LDPE is also permeable and allows sulphur dioxide gas to transfer into the packed agricultural crops and produce. The sulfur dioxide gas provides for preventing, retarding, controlling, delaying or killing microbiological contaminated foods, agricultural crops and botanicals.
The middle layer of the invented film or sheet consists of a polymeric mixture with a moisture activated sulphur dioxide gas generating precursor salt. This salt consist of a particle size range from 1 micron to less than 16 microns dispersed in a polymer said LDPE. These small particle size salts in the present of moisture, will produce a fast release rate of sulfur dioxide gas up to 150 ppm per hour from 0.1 to 4 days for fast kill of Botrytis Cinerea sp, molds, bacteria, and spores. These salts include: sodium sulfite, sodium metabisulfite, sodium bisulfite which disperse in a polymer said LDPE. In addition, a colorant or dye may be added for aesthetic, light selection or light reducing effects.
The third layer of the invented film or sheet consists of a polymeric mixture with a moisture activated sulfur dioxide gas generating precursor salt. This salt consist of a particle size range from 16 micron to 80 microns dispersed in a polymer said LDPE. These larger particle size salts, in the present of moisture, will produce a much slower and sustained release rate of sulfur dioxide gas ranging from 0.1 to 8 ppm per hour for a longer period of up to 75 days or more to suppress the growth of Botrytis Cinerea sp, molds, bacteria, and spores. These salts include: sodium sulfite, sodium metabisulfite, sodium bisulfite which disperse in a polymer said LDPE. In addition, a colorant or dye may be added for aesthetic, light selection or light reducing effects. See
In accordance with the present invention, a moisture activated gas releasing article has been made that comprises a polymer and a moisture activated solid component that is capable of generating and releasing a gas. The article provides antimicrobial protection of packaged agricultural products and is capable of sustained generation and release of a gas in the presence of moisture. The gas generally controls the growth of microorganisms thereby providing protection of agricultural products from those microorganisms during packing, transportation and storage.
In the first structural layer, the polymeric article of the invention comprises a polymer said low density polyethylene which has a density range of 0.89 to 0.93. A small percentage of processing aid can be added to the LDPE. The polymeric low density polyethylene film structure is permeable to moisture and sulphur dioxide gas. The generated gas is effective for permeating through into the agriculture product to control the growth of microorganisms.
In the second structural layer, the polymeric article of the invention comprises a polymer said low density polyethylene which has a density range of 0.89 to 0.93; and a dispersed solid component capable of generating a gas upon exposure to moisture. In this structural layer, it consists essentially of 40% to 99.9% by weight of a polymer and between 0.1% and 70% by weight of a gas generating solid with a particle size range from 1 micron to 15 microns which is dispersed in the polymer matrix. These salts are: for example, sodium sulfite, sodium metabisulfite, sodium bisulfite. In addition, a colorant or dye may be added for aesthetic, light selection or light reducing effects.
In the third structural layer, the polymeric article of the invention comprises a polymer said low density polyethylene which has a density range of 0.89 to 0.93. This structural layer, includes 40% to 99.9% by weight of a polymer and between 0.1% and 70% by weight of a gas generating solid with a particle size 16 microns to 80 microns which is dispersed in the polymer matrix. The larger particles in the polymeric matrix release sulfur dioxide gas in a much slower pace than the smaller particles, for example, for 75 days or more for continuous control the growth of microorganisms and moulds during shipping. (Storage conditions: −1° C. to +10° C., RH 80% to 99%)
A master batch was prepared by adding low density polyethylene (LPDE) and sodium metabisulfite directly into a polymer extruder at LDPE: Na2MB weight ratio ranges of 60:40 and 40:60. The master batch was compounded, extruded, cut by a vented twin screw extruder and cut into pellets. The extrusion conditions were maintained below 175° C. and above 110° C. 0.1% to 3% processing aids such as amides can be used as an internal and external lubricant.
The three layer film or sheet was prepared as follows: A first co-extruded inside layer containing 0% by weight of sodium metabisulfite was prepared by using a single screw extruder with all zones and die kept below 175° C. and above 110° C. by adding LPDE with a density of 0.89 to 0.93 LDPE. This co-extruded film or sheet was prepared using processes and equipment normally used in blown or cast film production (
A second co-extruded middle layer containing 15% to 18% by weight of sodium metabisulfite master batch with a particle size of 0.1 micron to 15 microns was prepared by a blown film production equipment.
A third co-extrusion film was prepared by using a blown film production equipment by adding a master batch containing a 5% to 40% by weight of sodium metabisulfite. The master batch is a blend of sodium metabisulfite with particle size from 16 micron to 80 microns into 60 to 95% LDPE.