Patent Application
20200040464
This invention relates to an aqueous solution and a method for preparing an organic protective coating on a Cr(III) conversion layer which is localized on (anodized) aluminium (alloy) to enhance corrosion protection. The composition is an aqueous solution which contains water, an organic film forming agent and a corrosion inhibitor, wherein the corrosion inhibitor comprises or consists of at least one 2-aryl-triazole. According to the method of the present invention, the composition is used for post-treating of a Cr(III) conversion layer on (anodized) aluminium (alloy). The invention further provides a modified Cr(III) conversion coating on (anodized) aluminium (alloy), which is producible or produced with the inventive method. The modified Cr(III) conversion coating according to the invention shows excellent corrosion protection, paint adhesion and electrical resistivity.
Chromate based conversion coatings are widely used for the protection of aluminium and aluminium alloys. They act as a protective coating against corrosion and also serve as a base for paint adhesion. Many solutions have already been developed. Nevertheless, these solutions do not always meet the requirements for corrosion protection. This is especially true for corrosion protection of aluminium alloys which are rich in an alloy metal which is sensitive to oxidation (e.g. Cu-rich Al-alloys). Said aluminium alloys are known to be difficult to protect against corrosion due to copper inclusions formed by the copper content. The use of a corrosion inhibitor helps to protect said alloys from pitting corrosion.
The possibility of the corrosion inhibition of an aluminium alloy metal, especially copper, has attracted many researchers. The best organic inhibitors known today to inhibit corrosion of copper as an aluminium alloy metal are the triazole compounds benzotriazole, tolyltriazole and thiazole compounds mercaptobenzothiazole, benzothiazole, and dimercaptothiadiazole. Said compounds were found to react with copper ions to give a complex by forming a protective film chemisorbed on the surface. pH of the film-forming solution is considered to be very important factor to obtain a good corrosion protection. It is assumed in the prior art that corrosion protection is maximal if the pH of the treatment solution having the corrosion inhibitor is in the alkaline range.
EP 1 571 238 discloses processes and compositions for producing aluminium surfaces free from chromium(VI) chromate coatings.
EP 1 848 841 discloses a composition and process for preparing chromium-zirconium coatings on metal substrates such as aluminium (alloy) substrates.
WO 2014/044806 discloses an aqueous solution for improving corrosion resistance of a Cr(III) conversion coating on aluminium (alloys) and anodized aluminium (alloys). Said solution has the disadvantage that a buffering agent is required in the solution to avoid precipitation of the solution caused by a drop in pH upon contact with an acidic trivalent chromium conversion coating.
Starting herefrom, it was the object of the present invention to provide an aqueous solution for improving corrosion resistance of a Cr(III) conversion coating on aluminium (alloy) and/or anodized aluminium (alloy) which is less sensitive to pH variation i.e. does not show precipitation upon contact with an acidic trivalent chromium conversion coating.
The object is solved by the Aqueous solution with the features of claim 1, the method according to claim 11 and the modified Cr(III) conversion coating according to claim 15. The dependent claims show advantageous embodiments thereof.
According to the invention, an aqueous solution for improving corrosion resistance of a Cr(III) conversion coating on aluminium (alloy) and/or anodized aluminium (alloy) is provided, comprising
a) a corrosion inhibitor;
b) an organic film forming agent;
c) water;
characterized in that the corrosion inhibitor comprises or consists of at least one 2-aryl-triazole.
The advantage of the inventive aqueous solution is that it is less sensitive to a pH shift when used on an acidic surface i.e. it does not show precipitation upon contact with an acidic trivalent chromium conversion coating. Since no precipitation occurs at the surface of the trivalent chromium conversion coating to be treated, the solution may act more homogeneously and effectively over the whole area of the surface. Therefore, the whole treatment of the surface is more effective. Additionally, the inventive aqueous solution allows the provision of a modified Cr(III) conversion coating on (anodized) aluminium (alloy) having excellent corrosion protection, paint adhesion and electrical resistivity. According to the ISO 9227 corrosion test, a corrosion protection of more than 168 h, in preferred embodiments even more than 216 hours without any pits on aluminium 2024 is achieved.
The inventive solution may be characterized in that the concentration of the at least one 2-aryl-triazole is 0.5 to 50 g/L, preferably 1 to 25 g/L, more preferably 2 to 10 g/L, particularly 3 to 5 g/L, based on the total mass of the solution.
Moreover, the corrosion inhibitor of the inventive solution may further comprise azole-based compounds (e.g. 2-aryl-alkyl-triazole) in addition to the at least one 2-aryl-triazole. Said additional azole-based compounds may further enhance corrosion resistance, especially pitting corrosion resistance. The further azole-based compounds may be present in a concentration of 0.1 to 15 g/L, preferably 0.5 to 10 g/L, more preferably 1 to 7 g/L, particularly 2 to 5 g/L, based on the total mass of the solution.
In a preferred embodiment of the invention, the corrosion inhibitor of the aqueous solution comprises or consists of a mixture of a 2-aryl-triazole with a 2-aryl-alkyl-triazole, preferably a mixture of a 2-aryl-triazole with a 2-arylalkyl-triazole selected from the group consisting of 2-aryl-1-alkyl-triazole, 2-aryl-3-alkyl-triazole, 2-aryl-4-alkyl-triazole, 2-aryl-5-alkyl-triazole and mixtures thereof.
The organic film forming agent may be selected from the group consisting of polymers comprising an acrylic group, preferably an acrylic group selected from the group consisting of acrylonitrile, methacrylonitrile, methyl acrylate, methyl methacrylate, acrylate, methacrylate, acrylamide, methacrylamide and combinations thereof. Polymers comprising an acrylic group as the organic film forming agent provoke the formation of a layer with good electrical conductivity and good paint adhesion. Said film forming agent helps to maintain the corrosion inhibitor close to the copper inclusions on the aluminium surface and thus increase its corrosion resistance.
The concentration of the organic film forming agent may be 1 to 100 g/L, preferably 2 to 50 g/L, more preferably 4 to 25 g/L, particularly 8 to 12 g/L, based on the total mass of the solution.
In a preferred embodiment, the aqueous solution further comprises a wetting agent, preferably a siloxane-based wetting agent, more preferably a polyether siloxane copolymer.
The wetting agent provokes that the aspect of the treated substrate and corrosion protection in the area of the edges of the substrate is improved.
The concentration of the wetting agent may be 0.1 to 20 g/L, preferably 0.2 to 10 g/L, more preferably 0.5 to 5 g/L, particularly 1 to 2 g/L, based on the total mass of the solution.
In a preferred embodiment of the invention, the solution does not comprise a compound having at least two hydroxy groups and/or does not comprise a compound having at least one carboxy group.
The pH of the aqueous solution may be pH 4 to 14, preferably pH 6 to 12, more preferably pH 7.5 to 11, particularly pH 8 to 10.
In a preferred embodiment, the aluminium alloy is an aluminium-copper alloy.
According to the invention, a method for providing a modified Cr(III)-conversion coating on aluminium (alloy) and/or anodized aluminium (alloy) having a Cr(III) conversion coating on the surface is provided. The method comprises the step of contacting the Cr(III)-conversion coating with the inventive aqueous solution.
The method may further comprise the step of contacting the Cr(III) conversion coating with an aqueous passivation solution, preferably an aqueous passivation solution comprising at least one 2-aryl-triazole, optionally at least one 2-aryl-triazole in a concentration of 0.5 to 50 g/L, preferably 1 to 25 g/L, more preferably 2 to 10 g/L, particularly 3 to 5 g/L, based on the total mass of the solution.
Before contacting with the inventive aqueous solution and/before contacting with a passivation solution, at least one of the following steps may be performed in the inventive method:
wherein preferably step iv) follows step iii), step iii) follows step ii) and step ii) follows step i).
After contacting with the inventive aqueous solution, at least one of the following steps may be performed in the inventive method:
wherein preferably step ii) is performed last.
In a particularly preferred embodiment, after contacting with the inventive aqueous solution, the modified Cr(III) conversion coating is dried and then again contacted with the inventive aqueous solution. Preferably, the modified Cr(III) conversion coating is dried after said second contact with the inventive aqueous solution. In this regard, under drying of the modified Cr(III) conversion coating, a drying of the inventive aqueous solution located on the modified Cr(III) conversion coating is understood. It was discovered that this kind of treatment effectuates that NSST corrosion resistance (according to ISO 9227) is at least 648 hours.
According to the invention, a modified Cr(III) conversion coating on aluminium (alloy) and/or anodized aluminium (alloy), producible or produced with the inventive method, is provided. In fact, the Applicant has found that the modified coating comprises at least trace amounts of 2-aryl-triazole and thus distinguishes from Cr(III) conversion coatings known in the prior art.
With reference to the following Figures and Examples, the subject according to the invention is intended to be explained in more detail without wishing to restrict said subject to the special embodiments shown here.
A conventional passivation solution is produced by mixing 100 ml of Lanthane 613.3 part A and 75 ml of part B (Coventya) with demineralized water to make up one liter of solution. The pH of said solution is adjusted to pH 4 (e.g. using 10% ammonia solution in water).
The special passivation solution is identical to the conventional passivation above with the exception that it comprises 4 g/L of a mixture of azoles. Specifically, the special passivation solution is produced by mixing 100 ml of Lanthane 613.3 part A and 75 ml of part B (Coventya) with 4 g/L of a mixture of azoles and demineralized water to make up one liter of solution. The pH of said solution is adjusted to pH 4 (e.g. using 10% ammonia solution in water).
The reference post-treatment solution is produced by mixing 2 g of mercaptobenzothiazole, 4 g of triethanolamine and 1 g of Mowiol 4-88® with demineralized water to make up one liter of solution. Said solution is stirred until all compounds are dissolved. Then, the pH is adjusted to pH 10.5 (e.g. using 10% H2SO4 in water).
The inventive post-treatment solution without a wetting agent is produced by mixing 10 g/L (dry content) of an acrylic modified polymer, 4 g/L of a mixture of azoles (2-aryl-triazole and 2-aryl-alkyl-triazole) with demineralized water to make up one liter of solution.
The inventive post-treatment solution is stable for at least 10 weeks. On the contrary, the reference post-treatment solution (according to Example 2) shows precipitation even after 5 days i.e. is less stable.
The inventive post-treatment solution comprising a wetting agent is produced by mixing 10 g/L (dry content) of an acrylic modified polymer, 4 g/L of a mixture of azoles (2-aryl-triazole and 2-aryl-alkyl-triazole) and 1.5 g/L of a wetting agent (siloxane based) with demineralized water to make up one liter of solution.
The method comprises the following steps:
Features of the Produced Protective Coatings
I.) Glow Discharge Optical Emission Spectrometry (GDOES) of the Protective Coatings
Modified Cr(III) conversion coatings were produced with the method of Example 5 and the two different inventive post-treatment solutions mentioned in Examples 3 and 4.
The obtained modified coatings had the following properties:
Importantly, both inventive solutions produced a coating having a significant content of carbon and sulfur.
II.) Corrosion Resistance of the Protective Coatings
Cr(III) conversion coatings produced with the method of Example 5 were exposed to NSST (according to ISO 9227).
In the case that the substrate aluminium 2024 was only treated with the conventional passivation solution (for recipe see Example 1) i.e. was not treated with a post-treatment solution, first pits were appearing even after 96 hours. In other words, it turned out that the addition of a post-treatment solution is necessary to reach at least 168 hours until first pits are appearing. The obtained result is illustrated in
In the case that the aluminium 2024 was treated with the conventional passivation solution (recipe see Example 1) and i) the first inventive post-treatment solution (recipe see Examples 3), or ii) the reference post-treatment solution (recipe see Example 2), the observed corrosion resistance was equal (pits appearing after approx. 216 hours; data not shown). However,
However, in the case that the aluminium 2024 was treated with the special passivation solution (recipe see Example 1) and the first inventive post-treatment solution (recipe see Examples 3), the second inventive post-treatment solution (recipe see Example 4) or the reference post-treatment solution (recipe see Example 2), the observed corrosion resistance was equal in all cases, but improved over the treatment with the conventional passivation solution (pits appearing only after approx. 264 hours; data not shown).
This result indicates that 2-aryl-triazole is effective in improving corrosion protection not only when present in the post-treatment solution, but also when present in the passivation solution.
II.) Aspect of the Protective Coatings
In the case that the conventional passivation solution (of Example 1) was used together with the reference post-treatment solution (of Example 2), the aspect of the protective coating was observed to be hazy.
On the contrary, in the case that the conventional passivation solution (of Example 1) was used together with an inventive post-treatment solution (of Example 3 or Example 4), the aspect of the protective coating was observed to be homogeneous.
IV.) Paint Adhesion Properties of the Protective Coatings
Aluminium 2024 panels were treated with passivation solution with or without post-treatment solution.
These panels were painted with solvent-based polyurethane primer (PAC 33) and top-coat (PU 66-8H) from PPG AEROSPACE.
Aluminum 2024 panels were prepared as usual with an immersion time in the TCP solution of about five minutes. Adhesion of primers to TCP coatings was evaluated against Alodine 1200, a chromate conversion coating, per MIL-DTL81706.
Ratings, per ASTM 3359, are based on a scale of 0 to 5, with 0 being the best rating. Results of these paint adhesion tests are shown in
V.) Electrical Contact Resistance of the Protective Coatings
The treatment has to allow maintenance of low electrical contact resistance in a corrosive environment. Tests were performed according to MIL DTL 81706 and recorded values are:
Electrical resistivity is still below reference.
According to MIL DTL 81706, the electrical resistivity must be <5 mΩ before Neutral Salt Spray Test and <10 mΩ after Neutral Salt Spray Test. The treatment according to the invention enables to stay within the targeted values.
The method comprises the following steps:
Corrosion Resistance of the Protective Coatings
Cr(III) conversion coatings produced with the method of Example 6 were exposed to NSST (according to ISO 9227).
In the case that the aluminium 2024 was treated with the solution of Example 4 according to the protocol of Example 6, no pit appeared even after 648 hours of NSS exposure (see
This result indicates that a twice treatment with the inventive post-treatment solution separated by a drying step very strongly improves corrosion protection.
| Number | Date | Country | Kind |
|---|---|---|---|
| 16192725.6 | Oct 2016 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2017/075444 | 10/6/2017 | WO | 00 |