Patent Grant
8545960
This application is a continuation-in-part of PCT Patent Application No. PCT/US06/60160, filed on Oct. 23, 2006, which claims the benefit of U.S. Provisional Patent Application No. 60/728,987, filed on Oct. 21, 2005, both of which are hereby incorporated by reference in their entirety.
The present invention relates generally to articles comprising protective sheets, as well as methods of making and using the same.
A variety of protective sheets and protective coatings can be selectively applied to protect exterior surfaces on a variety of articles. Often, protective sheets and protective coverings are selectively applied to an article's surface after the article is formed. Many such applications are intended to reduce abrasion or other wear on the underlying surface. Other applications are geared primarily toward maintaining or improving aesthetics or integrity of an underlying surface (e.g., when the underlying surface contains printed material thereon or when the surface contains aesthetically undesirable pinholes, bubbles, or other surface imperfections that can occur when, for example, producing molded articles). It is not surprising that there exists a need for protective sheets and protective coatings in a variety of applications.
Certain protective sheets and protective coatings, as well as related methods for making and using the same, are known. As an example, polyurethane “clearcoat” protective coatings have been applied to a variety of finished molded parts, such as plastic body panels, in order to bolster weathering performance, as well as scratch- and abrasion-resistance, without detrimentally affecting appearance of the underlying surface. Another example involves application of polyurethane sheets to automotive body panels for protection of the body panel against chipping or other damage caused by, for example, objects such as flying stones or debris. As another example, “leading edge tapes” have been applied to select portions of articles, such as helicopter blades and aircraft noses or wings, in order to protect underlying surfaces from scratch- and abrasion-resistance.
There are two widely used methods of applying gel coats or similar exterior protective coatings to articles. The first method involves spraying the gel coat onto an exterior surface of an article after the article is formed (e.g., by molding). The second method involves eliminating this subsequent processing (e.g., post-molding) step by pre-applying the gel coat to the interior surface of, for example, a mold where it can then be transferred to an exterior surface of the article formed therein. For example, see U.S. Pat. Nos. 4,081,578; 4,748,192; and 5,849,168. This method, which is one variation of “in-mold processing,” is sometimes referred to as in-mold declaration or in-mold labeling depending on the application and materials used.
While gel coats are capable of improving the aesthetics of surfaces to which they are applied, they are often not capable of imparting some or all of the desired performance properties. For example, gel coats are often too thin or too hard to provide substantial levels of abrasion resistance. Further, gel coats typically do not provide significant impact resistance when used on certain articles. After extended use, gel coats also have a tendency to crack, which enables water to penetrate into articles on which they are applied. Over time, such water penetration may lead to significant structural damage of the article. When the article is subjected to freeze-thaw cycling (e.g., as with many aerospace parts that undergo several freeze-thaw cycles in a single day of operation), premature structural failure is often more rapid, as any water trapped within the article will likely produce larger cracks and similar internal damage based on such freeze-thaw cycling.
In addition to their inability to often provide desired performance properties, use of gel coats typically decreases overall processing efficiency. For example, if the gel coat is spray-applied to a surface in a post-processing step, additional labor and manufacturing time is required in conjunction therewith. Even when applied in-mold, for example, typical gel coats require cure time after application to a mold surface and before actual molding of the article. Such cure time can take several hours, which is obviously undesirable from the perspective of processing efficiency.
While in-mold processing is otherwise generally more efficient than post-mold application of gel coats, if printed material (e.g., a textual or graphical decal) is applied to the surface of a finished article, a gel coat must then be conventionally spray-applied to that surface or a protective coating or protective sheet must generally be applied over the printed material as a post-processing step. This is often necessary even if a gel coat has already been applied to the surface in-mold.
The types of materials that can be applied as a gel coat are also limited, which is undesirable as it decreases flexibility in design and manufacture of articles. For example, many conventional gel coat materials are two-part compounds having a relatively short pot life, which requires that they be used within a few hours of compounding or discarded. When in-mold application of gel coats is desired, additional constraints must be considered. For example, availability of certain polymer matrix systems for in-mold processing, such as those based on epoxy thermoset resins used with carbon fiber reinforcements, is very limited.
It should be noted that materials other than gel coats have been applied “in-mold” and to different types of underlying surfaces. For example, multi-layer paint replacement film has been converted to a finished product through an in-mold decoration process. This process typically involves back molding of the film to form a finished article having the paint replacement film integrally adhered to the outer surface. In-mold processing has also been utilized to construct certain specialized sporting implements such as bicycle helmets, where a foam layer is in-mold bonded to the hard outer shell of the helmet. Nevertheless, application of exterior protective coverings to surfaces is in need of improvement.
To provide higher levels of abrasion resistance or impact resistance beyond what gel coats alone can provide, protective sheets have been added to the exterior surfaces of articles in addition to gel coats. As compared to a protective coating, such as a gel coat, a protective sheet is generally applied to a surface in its cured form. In contrast, a coating is generally applied to a surface to be protected in an uncured (e.g., solution) form, after which it is cured in-situ. While a sheet may be formed using conventional extrusion, casting, or coating technology, before the sheet is applied to a surface to be protected it is cured and/or formed.
Conventional protective sheets are often applied to a surface using a pressure sensitive adhesive. Many undesirable issues can arise, however, if the pressure sensitive adhesive is not adequately designed and formulated. For example, many pressure sensitive adhesives lack adequate bond strength to prevent edge lifting of protective sheets that are adhered to an underlying surface using the same. Protective sheets applied using existing technologies are typically not permanently bonded to the underlying surface. The durability of such constructions is often short-lived, as the adhesive bond often fails during repeated use, causing the protective sheet to lift from the surface. As another example, many conventional pressure sensitive adhesives are either repositionable and/or removable. This allows conventional protective sheets, which may lack adequate extensibility for easy application to a surface (especially irregular-shaped surfaces), to be more easily applied to surfaces. However, such pressure sensitive adhesives typically lack adequate permanency. In addition, often when a pressure sensitive adhesive is used for bonding a protective sheet to an underlying surface, a gel coat or other protective coating is often used in addition to the protective sheet (e.g., a coating is applied to an underlying surface before the protective sheet is applied).
In addition to the shortcomings associated with bonding of protective sheets to an underlying surface, application of protective sheets has proven to be otherwise difficult. For example, in addition to the bonding issues arising based on the often inadequately extensible nature of conventional protective sheets, it is often difficult to apply protective sheets to surfaces with complex shapes when relatively thick or multi-layer protective sheets are used. As a result, wrinkles often exist in protective sheets so applied. Even if uniformly applied to irregular surfaces initially, over time conventional protective sheets are prone to lifting from such surfaces. In any event, the way in which protective sheets are typically applied to such surfaces generally decreases processing efficiency.
While some benefits can be obtained from application of protective sheets and protective coatings according to known methods, such conventional methods often result in articles that still fail to adequately address important performance and processing considerations. Not only are performance property considerations important, but for the reasons stated above, aesthetics are also often another important consideration.
When attempting to address the myriad of important considerations, however, processing efficiency is often compromised. This is the case when, for example, multiple protective sheets and/or protective coatings (e.g., gel coats) are applied to a surface. In order to improve processing efficiency, it is desirable to minimize the number of protective sheets and protective coatings such as gel coats (especially those gel coats used primarily for aesthetic enhancement) that are applied to protect surfaces of underlying articles. For example, if gel coats could be eliminated, processing efficiency could improve both in terms of cost and time savings associated with the otherwise required additional processing steps associated with gel coating.
A wide variety of articles benefit from application of protective sheets according to the invention. Articles of the invention are useful in a range of indoor and outdoor applications—for example, the transportation, architectural and sporting goods industries. In certain embodiments of the invention, the article comprises at least a portion of a motorized vehicle (e.g., a bumper or side view mirror enclosure), at least a portion of an aerospace apparatus (e.g., a rotor blade for a helicopter), or at least a portion of a sporting implement (e.g., bicycles, skis, snowboards, and the like). Protective sheets of the invention have a chip resistance rating of at least “6B,” preferably better, as measured according to ASTM D3170 (SAE J400).
According to one aspect of the invention, an article comprises a protective sheet integrally bonded to at least one portion thereof. In one embodiment, the article has at least one exterior surface and the protective sheet covers at least a portion of that exterior surface. In another embodiment, the article is fully covered by the protective sheet.
According to another aspect of the invention, an article comprises an exterior protective sheet adhered to an underlying surface, wherein the article is essentially free of additional layers (e.g., an adhesive) between the protective sheet and the underlying surface. According to yet another aspect of the invention, an article comprises a protective sheet adhered to at least one exterior portion thereof, wherein the protective sheet is capable of providing all desired enhancements in performance and aesthetic properties of the article in one protective sheet component as compared to use of multiple protective sheet or protective coating components.
In an exemplary embodiment, at least a portion of the protective sheet is crosslinked with at least a portion of an underlying surface of the article. The protective sheet can also undergo thermolysis during cure of the article according to one aspect of the invention and depending on materials used for the various components.
Any suitable materials can be used for the protective sheet or to form the same. Preferably, the protective sheet is extensible. In an exemplary embodiment, the protective sheet comprises at least one elastomeric material. Protective sheets encompassed within the invention comprise any suitable chemistry and components to provide protective properties desired. For example, protective sheets can comprise (meth)acrylate, polyester, silicone, polyvinyl chloride, polyolefin (e.g., polyethylene, polypropylene, etc.), polyurethane, and/or fluorinated chemistries. In an exemplary embodiment, the protective sheet comprises at least one polyurethane-based layer.
Preferably, the protective sheet is visually clear. Thus, it is also preferred that the protective sheet consists essentially of non-composite material. According to further embodiments, the article comprises at least one of printed material and graphical material on at least one outwardly visible surface thereof.
Methods of the invention include those for applying protective sheets of the invention to a variety of articles. According to these methods, a protective sheet is applied to at least a portion of an exterior surface where protection is desired on an article. According to one embodiment of a method of the invention, at least one exterior surface of the article to be protected is integrally formed in the presence of the protective sheet.
One embodiment of a method of using a protective sheet to protect a molded surface comprises steps of: providing the protective sheet prior to forming the molded surface; and molding the surface in the presence of the protective sheet such that the molded surface is integrally formed with the protective sheet on at least a portion of at least one exterior surface thereof.
Another embodiment of a method of using a protective sheet to protect a molded surface comprises steps of: providing the protective sheet; forming the molded surface; and co-molding the protective sheet on at least a portion of the molded surface such that the protective sheet is integrally bonded with the molded surface.
The molded surface can be integrally formed, for example, with the protective sheet using an in-mold processing or insert-mold processing technique, such as an injection molding technique. In-mold and insert-mold processing for adherence of a protective sheet to an article's surface facilitates formation of new and improved articles. When formed in such a manner, beneficial properties associated with the protective sheet being positioned on an exterior surface of the article are maximized. For example, protective layers adhered to articles' surfaces using conventional methods such as spray coating a protective film using gel technology or otherwise adhering a protective film or sheet to a formed surface (e.g., using an adhesive, thermal bonding, or otherwise) are generally more prone to compromise beneficial protective properties or even fail as compared to those protective sheets integrally bonded to an article's surface. In addition, in-mold and insert-mold processing results in manufacturing efficiencies realized by, for example, elimination of process steps secondary to article formation as well as elimination of adhesive bonding materials otherwise required in many secondary applications.
The present invention is directed toward improved articles comprising a protective sheet on at least a portion of at least one exterior surface thereof. The surface underlying the protective sheet can comprise any suitable material or combinations thereof and may form any useful article. For example, the surface underlying at least a portion of the protective sheet can comprise a composite material as described in PCT Patent Application No. PCT/US06/60160 filed on Oct. 23, 2006. While certain advantages may be realized when at least a portion of the underlying surface comprises a composite material, the underlying surface may be any other suitable material in other embodiments of the invention.
Any suitable protective sheet can be applied to an article according to methods of the invention in order to result in improved articles. While a sheet material may be used primarily for aesthetic purposes (e.g., adding color to a surface) in certain applications, such a purpose or use does not exclude such sheets from being encompassed within the definition of protective sheets referenced throughout in describing the present invention. Preferred embodiments, however, are those associated with protective sheets that are visually clear. In this regard, an underlying surface to which the protective sheet is bonded can still be viewed despite the presence of the protective sheet imparting certain performance properties. Among other beneficial properties, the presence of the protective sheet enhances durability (e.g., abrasion resistance) of the article, as well as its impact resistance and fracture toughness in further embodiments.
For example, protective sheets of the invention have a chip resistance rating of at least “6B,” preferably better, as measured according to ASTM D3170 (SAE J400). According to this test method, an approximately 10-centimeter (4-inch) by 30-centimeter (12-inch) sample of protective sheet is mounted in back of a gravelometer, after which air pressure is used to project about 300 pieces of gravel at the protective sheet. The protective sheet is then removed and gently wiped with a clean cloth. Tape is applied to the test surface and then removed to pull off any loose fragments of the protective sheet. The appearance of the tested sample is then compared to standard transparencies supplied by SAE International to determine chipping ratings. Chipping ratings consist of one or more letter-number combinations. The letter designates the chip sizes being counted, and the number designates the number of chips of that size. For example, a rating of “B6” indicates the presence of 10-24 chips 1-3 millimeters in size.
In addition to enhanced performance properties associated with articles of the invention, processing efficiency is increased as compared to conventional articles and methods. According to exemplary embodiments, protective coatings (e.g., gel coats or similar protective coatings) are not needed to obtain desired properties and, thus, can be eliminated from articles of the invention. Such additional or inferior protective coatings are capable of being eliminated as aesthetic enhancement is typically not necessary in articles made according to the invention. As such, even if conventional gel coats are used within articles of the invention, aesthetics of the article would typically be essentially the same as those of comparable articles without the gel coat.
In essence, protective sheets of the invention and methods of their application are capable of providing all desired performance and aesthetic properties in one component and without requiring use of multiple protective sheets and/or multiple protective coatings in order to obtain comparable properties. By eliminating undesirable protective coatings and multiple protective layers, additional processing steps associated with conventional methods for protection of surfaces are likewise eliminated. Similarly, additional processing time associated therewith, such as when a gel coat is applied in-mold in a way that requires cure time after application to a mold surface and before actual molding of the article, is also eliminated.
Even when printed material is included on an exterior surface of an article, addition of a protective coating after application thereof to the surface is not required according to an exemplary embodiment of the invention. According to this embodiment, any printed material and/or graphical material desired to be placed on an exterior surface of an article is pre-printed onto or viewable within a protective sheet prior to its bonding to the underlying article. The protective sheet is then applied to at least a portion of a surface of an underlying article such that the printed material and/or graphical material is outwardly visible.
Articles comprising protective sheets according to the invention are useful in a range of indoor and outdoor applications—for example, the transportation, architectural and sporting goods industries. An exemplary embodiment of the invention relates to articles used in the automotive industry. Such articles include, for example, interior trim components (e.g., door handles, steering wheels, and gear shift knobs), internal mechanical components (e.g., drive shaft components), and exterior components (e.g., door panels, other body panels, roofs, fenders, hoods, side view mirror enclosures, and bumpers).
An exemplary embodiment of the invention relates to sporting implements and similar articles. Such articles include, for example, golf clubs, bicycle components (e.g., frames), hockey sticks, lacrosse sticks, skis, ski poles, fishing rods, tennis rackets, arrows, polo mallets, and bats. According to a preferred aspect of this embodiment, the portion of the surface where the protective sheet is applied is not the primary surface for impact by a ball, puck, or other object (i.e., the surface is not what may be commonly referred to as the “contact surface”). For example, when the article is a hockey stick, the protective sheet is preferably applied to the shaft as opposed to the blade. Similarly, when the article is a golf club, the protective sheet is preferably applied to the shaft as opposed to the club head. Likewise, when the article is a lacrosse stick, the protective sheet is preferably applied to the handle as opposed to the pocket. When the article is a baseball bat, the protective sheet is preferably applied to the handle as opposed to the barrel.
In certain applications, the presence of the protective sheet can mean the difference between having a usable piece of sporting equipment and/or one that is safe. For example, when a cross country skier's pole breaks during a race they must either forfeit the race or be lucky enough to be given another pole to use. As a further example, it is not uncommon to break several hockey sticks during a game. Each time conventional technology is used, the hockey stick has the potential to severely injure another person or the player as its shape can readily transform into that of a spear-like object when broken. By using articles of the present invention, the equipment may still be usable (e.g., as in the case of the cross country ski pole) or at least resist total failure for a longer period of time. In addition, when articles of the present invention are used, the equipment may be prevented from injuring somebody upon failure (e.g., as in the case of a splintered hockey stick).
In certain embodiments, advantages of the invention are maximized when the protective sheet is applied to substantially cover the entire underlying surface. That is, the protective sheet fully covers the underlying article. In comparison, partial coverage of an underlying article may not adequately contain or prevent breakage of the overall article in those applications. Thus, in an exemplary embodiment, the protective sheet is applied to fully cover the underlying article or an individual component thereof.
Performance benefits from the presence of the protective sheet are enhanced when the protective sheet is integrally bonded to the article. “Integrally bonded” refers to those materials with bonds formed between the protective sheet and underlying article that are essentially permanent in nature. Removal of an integrally bonded protective sheet typically requires more force than that required to separate the same protective sheet adhered using certain pressure sensitive adhesives (e.g., those pressure sensitive adhesives having low shear and low tack, removability, repositionability, or similar properties) that do not facilitate formation of permanent or durable bonds. Integrally bonded protective sheets are better able to contain underlying materials than conventionally adhered protective sheets due to the reduced chances that their bonds to underlying surfaces will fail.
According to the invention, at least one protective sheet is integrally bonded to at least a portion of at least one surface of an underlying article. Protective sheets of the invention are formed using any suitable method. In one embodiment, the protective sheet is generally planar. In exemplary embodiments, however, protective sheets are also pre-formed into a shape approximating the shape of the surface onto which it is to be adhered. This simplifies the process of adequately adhering the protective sheet to the surface and can be done, for example, by thermoforming or injection molding. Whatever the method used for its fabrication, the protective sheet is formed separately from formation of the exterior surface of the article to which it will be applied. Thus, for example, protective sheets of the invention do not require, and generally do not include, protective coatings formed by spray coating a surface of an article with a composition that forms a protective layer on the surface.
The protective sheet can be any suitable thickness. In one embodiment, protective sheets of the invention are about 50 μm (0.002 inch) to about 1.1 mm (0.045 inch) thick at their maximum thickness. In a further embodiment, protective sheets of the invention are about 80 μm (0.003 inch) to about 0.64 mm (0.025 inch) thick at their maximum thickness. In other embodiments, protective sheets of the invention are greater than 0.51 mm (20 mils), or even greater than about 2.54 mm (100 mils) thick at their maximum thickness. In yet other embodiments, protective sheets of the invention are thinner, ranging from about 0.15 mm (6 mils) to about 0.38 mm (15 mils) thick at their maximum thickness. It has been found that the use of relatively thin protective sheets imparts greater flexibility and conformability in many applications, particularly when applying the protective sheet to an irregular-shaped surface.
The protective sheet can be any suitable material and may include one or more layers. Protective sheets of the invention comprise at least a base layer and, optionally, topcoat or other layers. The use of multiple layers within a protective sheet imparts flexibility in design of protective sheets. While there may be protective sheets that do not involve multiple layers, but rather one layer, certain performance properties can often be better achieved when using a protective sheet comprising multiple layers.
In an exemplary embodiment, the protective sheet comprises one or more elastomeric materials. Elastomeric materials are preferably those polymeric materials exhibiting about 200% or greater elastic elongation. Elastomeric materials are preferred for use in the protective sheets of the invention because such materials are highly resilient and exhibit compressive recovery. Thus, elastomeric materials can enhance impact resistance, abrasion resistance, and other similar performance properties of surfaces and articles to which protective sheets comprising the same are applied. Further, elastomeric materials are generally highly extensible and conformable. Thus, when used in protective sheets of the invention, such materials ease application of such protective sheets to articles or molds of varying dimensions and shape. Exemplary elastomeric films include those based on polyurethane, ionomer, and fluoroelastomer chemistries. Extensible protective sheets are formed according to one aspect of this embodiment.
The terms “extensible” and “extensibility” refer to a material's ductility and its ability to be stretched and recover to essentially its original state after stretching. Extensible protective sheets are capable of recovering to their original state when stretched (i.e., elongated) up to about 125% of their initial length or more. Preferably, extensible protective sheets are capable of recovering to their original state when stretched up to about 150% of their initial length or more. According to one aspect of the invention, extensible protective sheets are capable of elongating more than 200% before breaking. Further preferable are extensible protective sheets that exhibit essentially no plastic deformation when stretched up to about 150% of their initial length.
According to one aspect of the invention, extensible protective sheets of the invention exhibit greater than about 210% elongation at break when tested according to the Tensile Testing Method described below. In a further embodiment, extensible protective sheets of the invention exhibit greater than about 260% elongation at break when tested according to the Tensile Testing Method described below. In a still further embodiment, extensible protective sheets of the invention exhibit greater than about 300% elongation at break when tested according to the Tensile Testing Method described below. In a further embodiment still, extensible protective sheets of the invention exhibit greater than about 350% elongation at break when tested according to the Tensile Testing Method described below.
According to another aspect of the invention, extensible protective sheets of the invention exhibit less than about 3% deformation after 25% elongation when tested according to the Recovery Testing Method described below. In a further embodiment, extensible protective sheets of the invention exhibit less than about 2% deformation after 25% elongation when tested according to the Recovery Testing Method described below. In a still further embodiment, extensible protective sheets of the invention exhibit less than about 1% deformation after 25% elongation when tested according to the Recovery Testing Method described below.
According to another aspect of the invention, extensible protective sheets of the invention exhibit less than about 8% deformation after 50% elongation when tested according to the Recovery Testing Method described below. In a further embodiment, extensible protective sheets of the invention exhibit less than about 5% deformation after 50% elongation when tested according to the Recovery Testing Method described below. In a still further embodiment, extensible protective sheets of the invention exhibit less than about 2% deformation after 50% elongation when tested according to the Recovery Testing Method described below.
According to another aspect of the invention, extensible protective sheets of the invention require a force of less than about 40 Newtons to elongate the sheet to 150% its initial length. In a further embodiment, extensible protective sheets of the invention require a force of less than about 30 Newtons to elongate the sheet to 150% its initial length. In yet a further embodiment, extensible protective sheets of the invention require a force of less than about 20 Newtons to elongate the sheet to 150% its initial length.
Protective sheets encompassed within the invention comprise any suitable chemistry and components to provide aesthetic and performance properties desired. For example, protective sheets can comprise (meth)acrylate, polyester, silicone, polyvinyl chloride, polyolefin (e.g., polyethylene, polypropylene, etc.), polyurethane, and/or fluorinated chemistries. In an exemplary embodiment, protective sheets of the invention are polyurethane-based in that they comprise at least one polyurethane-based layer.
For simplicity, the term “polyurethane” as used herein includes polymers containing urethane (also known as carbamate) linkages, urea linkages, or combinations thereof (i.e., in the case of poly(urethane-urea)s). Thus, polyurethanes of the invention contain at least urethane linkages and, optionally, urea linkages. In one embodiment, polyurethane-based layers of the invention are based on polyurethanes where the backbone has at least about 80% urethane and/or urea repeat linkages formed during their polymerization.
Polyurethane chemistry is well known to those of ordinary skill in the art. Polyurethane-based layers of the invention can contain polyurethane polymers of the same or different chemistries, the latter commonly understood to be a polymer blend. Polyurethanes generally comprise the reaction product of at least one isocyanate-reactive component, at least one isocyanate-functional component, and one or more other optional components such as emulsifiers and chain extending agents.
Components of polyurethanes are further described below, with reference to certain terms understood by those in the chemical arts as referring to certain hydrocarbon groups. Reference is also made throughout to polymeric versions thereof. In that case, the prefix “poly” is inserted in front of the name of the corresponding hydrocarbon group. Except where otherwise noted, such hydrocarbon groups, as used herein, may include one or more heteroatoms (e.g., oxygen, nitrogen, sulfur, or halogen atoms), as well as functional groups (e.g., oxime, ester, carbonate, amide, ether, urethane, urea, carbonyl groups, or mixtures thereof).
The term “aliphatic group” means a saturated or unsaturated, linear, branched, or cyclic hydrocarbon group. This term is used to encompass alkylene (e.g., oxyalkylene), aralkylene, and cycloalkylene groups, for example.
The term “alkylene group” means a saturated, linear or branched, divalent hydrocarbon group. Particularly preferred alkylene groups are oxyalkylene groups. The term “oxyalkylene group” means a saturated, linear or branched, divalent hydrocarbon group with a terminal oxygen atom. The term “aralkylene group” means a saturated, linear or branched, divalent hydrocarbon group containing at least one aromatic group. The term “cycloalkylene group” means a saturated, linear or branched, divalent hydrocarbon group containing at least one cyclic group. The term “oxycycloalkylene group” means a saturated, linear or branched, divalent hydrocarbon group containing at least one cyclic group and a terminal oxygen atom. The term “aromatic group” means a mononuclear aromatic hydrocarbon group or polynuclear aromatic hydrocarbon group. The term includes arylene groups. The term “arylene group” means a divalent aromatic group.
Any suitable method can be used for preparation of polyurethanes for use in polyurethane-based protective sheets of the invention. In one embodiment, the polyurethane is prepared and formed into a single layer using an extruder. The polyurethane can also be blown to form a single layer.
Many commercially available polyurethanes are available and suitable for use in preparing protective sheets of the invention. Extrusion grade polyurethanes can be used in certain embodiments of the invention. Extrusion grade polyurethanes include those available from Stevens Urethane of Easthampton, Mass. Aliphatic polyurethanes from Stevens Urethane, for example, those designated SS-1219-92 and SS-2219-92. Suitable polyurethanes are also available from Thermedics (Noveon, Inc.) of Wilmington, Mass., under the TECOFLEX trade designation (e.g., CLA-93AV) and from Bayer MaterialScience LLC of Pittsburgh, Pa., under the TEXIN trade designation (e.g., aliphatic ester-based polyurethane suitable as a base polymer for polyurethane-based layers of the invention is available under the trade designation, TEXIN DP7-3008). Polycaprolactone-based aliphatic polyurethane is available from Argotec, Inc. of Greenfield, Mass. under the trade designation, ARGOTEC 49510. Polyether-based aliphatic thermoplastic polyurethane is available from Argotec, Inc. of Greenfield, Mass. under the trade designations, ARGOTEC PE-399 and ARGOTEC PE-192. Similar polyurethanes are available from Stephens Urethane of Easthampton, Mass., under the trade designations, AG8451 and AG8320. Still further, similar polyurethanes are available from Deerfield Urethane, Inc. of Whately, Mass. (a Bayer MaterialScience company) under the trade designations Deerfield Urethane A4700 and Deerfield Urethane A4100. Polyester-based aliphatic polyurethanes are also suitable for use in the invention. Polycarbonate-based polyurethanes, such as those described in U.S. Pat. No. 4,476,293 are likewise suitable for use in the invention. In addition, U.S. Pat. Nos. 5,077,373 and 6,518,389 describe further suitable polyurethanes.
In another embodiment, polyurethane can be prepared and formed into a single layer using solution or dispersion chemistry and coating techniques known to those skilled in the art. Such a layer can be prepared by reacting components, including at least one isocyanate-reactive component, at least one isocyanate-functional component, and, optionally, at least one reactive emulsifying compound, to form an isocyanate-terminated polyurethane prepolymer. The polyurethane prepolymer can then be dispersed, and optionally chain-extended, in a dispersing medium to form a polyurethane-based dispersion that can be cast to form a layer of polyurethane. When polyurethane is prepared from an organic solventborne or waterborne system, once the solution or dispersion is formed, it is easily applied to a substrate and then dried to form a polyurethane layer. As known to those of ordinary skill in the art, drying can be carried out either at room temperature (i.e., about 20° C.) or at elevated temperatures (e.g., about 25° C. to about 150° C.). For example, drying can optionally include using forced air or a vacuum. This includes the drying of static-coated substrates in ovens, such as forced air and vacuum ovens, or drying of coated substrates that are continuously conveyed through chambers heated by forced air, high-intensity lamps, and the like. Drying may also be performed at reduced (i.e., less than ambient) pressure.
Any suitable isocyanate-reactive component can be used in this embodiment of the present invention. The isocyanate-reactive component contains at least one isocyanate-reactive material or mixtures thereof. As understood by one of ordinary skill in the art, an isocyanate-reactive material includes at least one active hydrogen. Those of ordinary skill in the polyurethane chemistry art will understand that a wide variety of materials are suitable for this component. For example, amines, thiols, and polyols are isocyanate-reactive materials.
It is preferred that the isocyanate-reactive material be a hydroxy-functional material. Polyols are the preferred hydroxy-functional material used in the present invention. Polyols provide urethane linkages when reacted with an isocyanate-functional component, such as a polyisocyanate.
Polyols, as opposed to monols, have at least two hydroxy-functional groups. Diols contribute to formation of relatively high molecular weight polymers without requiring crosslinking, such as is conventionally introduced by polyols having greater than two hydroxy-functional groups. Examples of polyols useful in the present invention include, but are not limited to, polyester polyols (e.g., lactone polyols) and the alkylene oxide (e.g., ethylene oxide; 1,2-epoxypropane; 1,2-epoxybutane; 2,3-epoxybutane; isobutylene oxide; and epichlorohydrin) adducts thereof, polyether polyols (e.g., polyoxyalkylene polyols, such as polypropylene oxide polyols, polyethylene oxide polyols, polypropylene oxide polyethylene oxide copolymer polyols, and polyoxytetramethylene polyols; polyoxycycloalkylene polyols; polythioethers; and alkylene oxide adducts thereof), polyalkylene polyols, polycarbonate polyols, mixtures thereof, and copolymers therefrom.
Polycarbonate-based polyurethanes are preferred according to one embodiment. It was found that this type of polyurethane chemistry easily facilitated obtainment of polyurethane-based protective sheets with properties desired. See U.S. Pat. No. 4,476,293 for a description of exemplary polycarbonate-based polyurethanes.
In one preferred embodiment, a polycarbonate diol is used to prepare polycarbonate-based polyurethane according to the invention. Although polyols containing more than two hydroxy-functional groups are generally less preferred than diols, certain higher functional polyols may also be used in the present invention. These higher functional polyols may be used alone, or in combination with other isocyanate-reactive materials, for the isocyanate-reactive component.
For broader formulation latitude, at least two isocyanate-reactive materials, such as polyols, may be used for the isocyanate-reactive component. As any suitable isocyanate-reactive component can be used to form the polyurethane, much latitude is provided in the overall polyurethane chemistry.
The isocyanate-reactive component is reacted with an isocyanate-functional component during formation of the polyurethane. The isocyanate-functional component may contain one isocyanate-functional material or mixtures thereof. Polyisocyanates, including derivatives thereof (e.g., ureas, biurets, allophanates, dimers and trimers of polyisocyanates, and mixtures thereof), (hereinafter collectively referred to as “polyisocyanates”) are the preferred isocyanate-functional materials for the isocyanate-functional component. Polyisocyanates have at least two isocyanate-functional groups and provide urethane linkages when reacted with the preferred hydroxy-functional isocyanate-reactive components. In one embodiment, polyisocyanates useful for preparing polyurethanes are one or a combination of any of the aliphatic or aromatic polyisocyanates commonly used to prepare polyurethanes.
Generally, diisocyanates are the preferred polyisocyanates. Useful diisocyanates include, but are not limited to, aromatic diisocyanates, aromatic-aliphatic diisocyanates, aliphatic diisocyanates, cycloaliphatic diisocyanates, and other compounds terminated by two isocyanate-functional groups (e.g., the diurethane of toluene-2,4-diisocyanate-terminated polypropylene oxide polyol).
Examples of preferred diisocyanates include the following: 2,6-toluene diisocyanate; 2,5-toluene diisocyanate; 2,4-toluene diisocyanate; phenylene diisocyanate; 5-chloro-2,4-toluene diisocyanate; 1-chloromethyl-2,4-diisocyanato benzene; xylylene diisocyanate; tetramethyl-xylylene diisocyanate; 1,4-diisocyanatobutane; 1,6-diisocyanatohexane; 1,12-diisocyanatododecane; 2-methyl-1,5-diisocyanatopentane; methylenedicyclohexylene-4,4′-diisocyanate; 3-isocyanatomethyl-3,5,5′-trimethylcyclohexyl isocyanate (isophorone diisocyanate); 2,2,4-trimethylhexyl diisocyanate; cyclohexylene-1,4-diisocyanate; hexamethylene-1,6-diisocyanate; tetramethylene-1,4-diisocyanate; cyclohexane-1,4-diisocyanate; naphthalene-1,5-diisocyanate; diphenylmethane-4,4′-diisocyanate; hexahydro xylylene diisocyanate; 1,4-benzene diisocyanate; 3,3′-dimethoxy-4,4′-diphenyl diisocyanate; phenylene diisocyanate; isophorone diisocyanate; polymethylene polyphenyl isocyanate; 4,4′-biphenylene diisocyanate; 4-isocyanatocyclohexyl-4′-isocyanatophenyl methane; and ρ-isocyanatomethyl phenyl isocyanate.
When preparing polyurethane dispersions for casting into layers of polyurethane, the isocyanate-reactive and isocyanate-functional components may optionally be reacted with at least one reactive emulsifying compound according to one embodiment of the invention. The reactive emulsifying compound contains at least one anionic-functional group, cationic-functional group, group that is capable of forming an anionic-functional group or cationic-functional group, or mixtures thereof. This compound acts as an internal emulsifier because it contains at least one ionizable group. Thus, these compounds are generally referred to as “reactive emulsifying compounds.”
Reactive emulsifying compounds are capable of reacting with at least one of the isocyanate-reactive and isocyanate-functional components to become incorporated into the polyurethane. Thus, the reactive emulsifying compound contains at least one, preferably at least two, isocyanate—or active hydrogen-reactive—(e.g., hydroxy-reactive) groups. Isocyanate- and hydroxy-reactive groups include, for example, isocyanate, hydroxyl, mercapto, and amine groups.
Preferably, the reactive emulsifying compound contains at least one anionic-functional group or group that is capable of forming such a group (i.e., an anion-forming group) when reacted with the isocyanate-reactive (e.g., polyol) and isocyanate-functional (e.g., polyisocyanate) components. The anionic-functional or anion-forming groups of the reactive emulsifying compound can be any suitable groups that contribute to ionization of the reactive emulsifying compound. For example, suitable groups include carboxylate, sulfate, sulfonate, phosphate, and similar groups. As an example, dimethylolpropionic acid (DMPA) is a useful reactive emulsifying compound. Furthermore, 2,2-dimethylolbutyric acid, dihydroxymaleic acid, and sulfopolyester diol are other useful reactive emulsifying compounds. Those of ordinary skill in the art will recognize that a wide variety of reactive emulsifying compounds are useful in preparing polyurethanes for the present invention.
One or more chain extenders can also be used in preparing polyurethanes of the invention. For example, such chain extenders can be any or a combination of the aliphatic polyols, aliphatic polyamines, or aromatic polyamines conventionally used to prepare polyurethanes.
Illustrative of aliphatic polyols useful as chain extenders include the following: 1,4-butanediol; ethylene glycol; 1,6-hexanediol; glycerine; trimethylolpropane; pentaerythritol; 1,4-cyclohexane dimethanol; and phenyl diethanolamine. Also note that diols such as hydroquinone bis(β-hydroxyethyl)ether; tetrachlorohydroquinone-1,4-bis(β-hydroxyethyl)ether; and tetrachlorohydroquinone-1,4-bis(β-hydroxyethyl)sulfide, even though they contain aromatic rings, are considered to be aliphatic polyols for purposes of the invention. Aliphatic diols of 2-10 carbon atoms are preferred. Especially preferred is 1,4-butanediol.
Illustrative of useful polyamines are one or a combination of the following: ρ,ρ′-methylene dianiline and complexes thereof with alkali metal chlorides, bromides, iodides, nitrites and nitrates; 4,4′-methylene bis(2-chloroaniline); dichlorobenzidine; piperazine; 2-methylpiperazine; oxydianiline; hydrazine; ethylenediamine; hexamethylenediamine; xylylenediamine; bis(ρ-aminocyclohexyl)methane; dimethyl ester of 4,4′-methylenedianthranilic acid; ρ-phenylenediamine; m-phenylenediamine; 4,4′-methylene bis(2-methoxyaniline); 4,4′-methylene bis(N-methylaniline); 2,4-toluenediamine; 2,6-toluenediamine; benzidine; 3,4′-dimethylbenzidine; 3,3′-dimethoxybenzidine; dianisidine; 1,3-propanediol bis(ρ-aminobenzoate); isophorone diamine; 1,2-bis(2′-aminophenylthio)ethane; 3,5-diethyl toluene-2,4-diamine; and 3,5-diethyl toluene-2,6-diamine. The amines preferred for use are 4,4′-methylene bis(2-chloroaniline); 1,3-propanediol bis(ρaminobenzoate); and ρ,ρ′-methylenedianiline and complexes thereof with alkali metal chlorides, bromides, iodides, nitrites and nitrates.
Any suitable additives can be present in protective sheets of the invention. Many different types of additives can be used and are readily available. For example, stabilizers, antioxidants, plasticizers, tackifiers, adhesion promoters (e.g., silanes, glycidyl methacrylate, and titanates), lubricants, colorants, pigments, dyes, polymeric additives (e.g., polyacetals, reinforcing copolymers, and polycaprolactone diols), and the like can be used in many embodiments of the invention. In certain embodiments, however, use of additives detracting from optical clarity of the protective sheet are minimized or eliminated. Such additives include, for example, colorants, pigments, fillers, and fiber- or other matrix-reinforcements typically present in composite materials. In an exemplary embodiment, the protective sheet would not be considered to be a composite material according to those skilled in the art.
According to another embodiment, polyurethane-based protective sheets of the invention comprise multiple layers (e.g., a carrier and a topcoat), at least one of which is polyurethane-based. According to one variation of this embodiment, the carrier and the topcoat layers are both polyurethane-based. In such an embodiment, the carrier preferably comprises a polyurethane-based layer as discussed above with respect to a single layer protective sheet of the invention. According to another variation of this embodiment, polyurethane-based protective sheets of the invention comprise a polyurethane-based topcoat and a carrier layer that may or may not be polyurethane-based.
When forming a protective sheet comprising a topcoat layer, the topcoat can be formed using any suitable method. In addition, the topcoat can be crosslinked or uncrosslinked. An uncrosslinked topcoat can be prepared from polyurethane-based layers discussed above. If crosslinking is desired, any suitable method can be used for the same. An exemplary discussion of crosslinked topcoats can be found in U.S. Pat. No. 6,383,644 and corresponding European Patent No. 1 004 608.
When applying the protective sheet to an article, particularly in applications where the articles and respective processing equipment have irregular-shaped or non-planar surfaces, extensibility of the protective sheet is important. Protective sheets described in PCT Patent Application No. PCT/US06/60171, entitled “Protective Sheets, Articles, and Methods,” which is incorporated herein by reference in its entirety, were found to be significantly more extensible than certain commercially available protective sheets having a crosslinked topcoat. Accordingly, in a further embodiment, protective sheets of the invention comprise an essentially uncrosslinked topcoat. In many applications where protective sheets are used, the potential benefits imparted by crosslinking an exterior layer were substantially outweighed by the significantly improved extensibility provided by protective sheets without a crosslinked exterior layer.
As discussed above, use of extensible protective sheets according to an exemplary embodiment of the invention imparts significant advantages, particularly when applying the protective sheet to irregular-shaped or non-planar surfaces. Further, use of extensible protective sheets in this manner better allows for full coverage of the article's outer surface with the protective sheet in certain embodiments of the invention. As noted above, full coverage can be beneficial for many applications in enhancing containment of the underlying article so as to increase safety and durability when using the article.
Several exemplary protective sheets applicable for use according to the invention are readily available on the market today and can be applied to the article without the additional use of a gel coat or similar protective coating. For example, Minnesota Mining & Manufacturing Co. (“3M”) in St. Paul, Minn., markets polyurethane-based sheet “Paint Protection Film” under the SCOTCHGARD product line. See also U.S. Pat. No. 6,383,644. As another example, Venture Tape Corp. in Rockland, Mass., markets such sheets (e.g., designated by product numbers 7510, 7512, and 7514) using the VENTURESHIELD trade designation. Avery Dennison in Strongsville, Ohio markets polyurethane products using the STONESHIELD trade designation. Protective sheets are available from entrotech, inc. of Columbus, Ohio under the ENTROFILM trade designations (e.g., entrofilm 843 and entrofilm 861) and others described in PCT Patent Application No. PCT/US06/60171, entitled “Protective Sheets, Articles, and Methods.”
According to the invention, a protective sheet is bonded to an underlying article using any suitable method. For example, the protective sheet can be adhered to an underlying article using an indirect bonding method. When indirectly bonded, the protective sheet is adhered to the underlying article using one or more additional layers therebetween. As another example, the protective sheet can be directly bonded to the exterior surface of an article. When directly bonded, the protective sheet is adhered to the underlying surface of the article without the use of any additional layers (e.g., adhesives, intermediate coatings, or tie layers) therebetween. In this embodiment, it is to be understood that the protective sheet itself preferably does not contain an outer adhesive layer positioned in contact with the underlying surface to which it is bonded according to the invention. For maximized process efficiency, direct bonding methods are preferred.
The protective sheet can be applied to at least a portion of the exterior surface of an article using in-mold, insert-mold, or co-mold processing techniques. The latter is sometimes referred to in terms of being a “reactive” molding technique.
In an exemplary embodiment, at least a portion of at least one exterior surface of an article to be protected is integrally formed in the presence of at least one protective sheet. “Integrally formed” refers to those exterior surfaces that are molded or otherwise fabricated in the presence of the protective sheet such that the two become integrally bonded during such formation.
When the article is molded, the protective sheet can be applied using in-mold, insert-mold, or co-mold processing techniques according to this exemplary embodiment. When formed in such a manner, beneficial properties associated with the protective sheet being positioned on an exterior surface of the article are maximized, as protective sheets and protective coatings adhered using other methods are generally more prone to failure. In addition, in-mold, insert-mold, and co-mold processing results in manufacturing efficiencies realized by, for example, elimination of processing steps secondary to article formation and often elimination of intermediate layers (e.g., those comprising adhesive bonding materials) and associated processing steps in many applications.
As discussed above, a wide variety of materials can be used for protective sheets of the invention. Extensible protective sheets, for example, are readily adapted for in-mold, insert-mold and co-mold processing techniques according to knowledge of those skilled in the art. Significant advantages are imparted when using such exemplary methods. For example, protective sheets applied using in-mold and insert-mold processing techniques provide processing efficiencies and improved performance properties arising from the improved integral bonding between the protective sheet and underlying surface as compared to otherwise adhering the protective sheet to the same surface after its formation. Integral bonds achieved with in-mold and insert-mold processing result in the protective sheet being less susceptible to shifting or sliding when an article comprising the same is in use.
Similar enhancements are obtained when protective sheets of the invention are co-molded with an article when applying a protective sheet to the outer surface thereof. Co-molding, sometimes referred to as reactive molding, refers to over-molding of an article with a protective sheet by applying the protective sheet to a molded article's surface and then further molding the article to sufficiently bond the protective sheet to the article's surface.
When applying the protective sheet to a non-planar or irregular-shaped surface of an article, it is not always necessary to completely and precisely cover the surface with the protective sheet. Rather, relatively small gaps in coverage (e.g., about 5 mm to about 10 mm) will often disappear after further molding of the article to sufficiently bond the protective sheet to the article's surface. For example, small gaps can disappear as a result of expansion of the protective sheet under heat and/or pressure of the molding process. Nevertheless, the protective sheet can overlap itself slightly (e.g., up to about 10 mm) in other embodiments without significantly affecting the resulting properties of the article comprising the protective sheet. In such a case, a self-adhesive bond can develop at the weld seam comprising the overlap. If desired, the weld seam of a co-molded article according to the invention can be hot-pressed (e.g., using a hot roller at a temperature of about 180° C.) to improve bonding at and appearance of the weld seam.
When co-molding the protective sheet to an underlying article, an adhesive may be included between the protective sheet and the underlying surface to facilitate adequate bond formation. According to one aspect of this embodiment, the adhesive is provided on the surface of the protective sheet to be bonded to the underlying article. Preferably, such an adhesive will be permanent in nature (e.g., such as that permanency provided by a thermoset adhesives).
Each suitable processing technique is susceptible to many variations as understood by those of ordinary skill in the art. For example, in-mold and insert-mold processing, which involve placement in a mold of a protective sheet to be integrally bonded with an article being formed within the mold, can be done using a variety of molding techniques. Such molding techniques include compression, bladder, vacuum bag, autoclave, injection molding, resin transfer molding (RTM), vacuum-assisted RTM, and other similar methods known to those of ordinary skill in the art.
With compression, bladder, vacuum bag, autoclave, and similar methods, a protective sheet is first positioned within a suitable mold. Material from which the article is to be formed is then positioned within the mold for curing into the desired shape. During such curing, which is often effected using heat and pressure, the protective sheet becomes integrally bonded to at least a portion of at least one surface of the article. According to a particularly preferred further embodiment, crosslinks form between the protective sheet and at least a portion of the underlying surface of the article during curing.
With injection molding, RTM, vacuum-assisted RTM, and similar methods, a protective sheet is placed within a mold. Material from which the article is to be formed is then injected into the mold to form an article of the invention. Those of ordinary skill in the art are readily familiar with injectable materials and techniques for their use in injection molding. The injectable material itself is generally heated to, for example, a semi-molten state for injection molding. For purposes of this invention, the term “semi-molten” means capable of flowing into the molding area. Prior to and during injection of the material, the protective sheet can be stabilized within the mold using any suitable method and apparatus, including the many methods associated with in-mold decoration. Such methods include those using gravity, air pressure, pins, tape, static electricity, vacuum, and/or other suitable means. In addition, release agents and other molding components can be used as readily understood by those skilled in the art.
Although not required, according to one variation of this embodiment, the protective sheet is heated prior to injecting the material into the mold and against the backside of the protective sheet. For example, one variation of this embodiment relates to insert-mold processing. During insert-mold processing, as compared to in-mold processing, the protective sheet is thermoformed into a three-dimensional shape prior to injection of the material. Typically, the protective sheet is shaped to approximate the contour of the interior surface of the mold into which it is placed for injection molding. In an exemplary embodiment, the thermoforming step occurs within the mold such that it does not require transfer prior to injection of the material. During in-mold processing, the protective sheet changes shape, if at all, upon injection molding of the material.
According to one aspect of this embodiment, any suitable injection molding apparatus can be used for molding. Typically, such molding apparatus have one or more orifices for injection of material into the mold. According to injection molding, RTM and similar methods, with the mold closed, uncured material (e.g., thermoset resin) is injected into the mold, after which it flows under heat and pressure while curing. Pressure from injecting material into the mold combined with the temperature within the mold and the surface of associated mold parts causes the material to fuse together with or bond to the interior surface of the protective sheet (i.e., it becomes integrally bonded).
An exemplary method of the invention comprises a bladder mold process. According to this embodiment, material for formation of an article and a protective sheet are arranged and then wrapped together around a bladder with a small mandrel inside the bladder. A heated mold is then placed over the wrapped bladder, the bladder is expanded to force the material against the mold, and the material forming the article is then cured in the mold. Curing times and temperatures depend on the specific materials used and are well known to those of skill in the art. Extensible protective sheets described herein are preferred for use in this embodiment, as such protective sheets are able to be efficiently and sufficiently wrapped around the bladder in such a process.
In another exemplary method of the invention, vacuum bag processing techniques are used to integrally bond protective sheets through in-mold processing. During vacuum bag processing, an uncured material for formation of the article is compacted against a mold surface to form an assembly. A vacuum is then pulled across the entire assembly and mold to remove excess air, uncured material, or other volatiles from the assembly. While the vacuum is being pulled, the mold is heated to cure the material within. According to a preferred embodiment, the vacuum itself provides all the pressure necessary to effect full cure of the material forming the article.
Exemplary embodiments and applications of the invention are described in the following non-limiting examples and related testing methods.
Tensile Testing Method
For tensile testing, samples were formed into standard tensile testing specimens according to ASTM D638-95 using designations for Type II measurements. Tensile testing was performed according to ASTM D638-95. The rate at which the jaws holding the specimen were pulled in a tensile manner was 1.0 millimeter/minute (0.04 inch/minute) to measure the elastic modulus of the sample, but increased to 300 millimeters/minute (11.8 inches/minute) to obtain the ultimate tensile strength and elongation data. Test data using this method is reported in Table 1.
Recovery Testing Method
For recovery testing, a generally rectangular sample having an initial length of 25 centimeters (10 inches) and width of 5 centimeters (2 inches) was prepared. The sample was stretched in tension until its length exceeded its initial length by a predetermined percentage (25% or 50%). After recovery equilibrium was obtained (approximately 5-10 minutes), the length of the relaxed sample was measured and the sample was qualitatively analyzed for defects or deformation. The change in length of the sample as compared to the initial length is reported as its “Percent Deformation” in Table 2. Note that values reported in Table 2 have a standard deviation of about plus/minus 0.6%.
Elongation Force Testing Method
Force required to elongate a generally rectangular sample having an initial length of 12.5 centimeters (5 inches) and width of 5 centimeters (2 inches) was measured using an IMASS SP2000 slip/peel tester (available from IMASS, Inc. of Accord, Mass.) operating at a speed of 30 centimeters/minute (12 inches/minute). Two forces were measured for each sample, those being that required to elongate the sample to 125% of its initial length and that required to elongate the sample to 150% of its initial length. The forces so measured are also reported in Table 2.
Weathering Testing Method
Where indicated, samples were tested for weathering resistance using a well-known QUV test method and weatherometer. The weathering conditions were as set forth in ASTM D4329.
An extensible polyurethane-based protective sheet was prepared such that the sheet comprised a carrier layer having a thickness of 150 microns, a topcoat layer having a thickness of 18 microns, and an adhesive layer having a thickness of 60 microns. The adhesive layer was adhered to the opposite side of the carrier layer from the topcoat layer. A standard release liner was positioned exterior to the adhesive layer, but was removed prior to testing.
To prepare the sheet, first a 98# polyethylene-coated kraft paper with silicone coated on one side was used as a release liner onto which the adhesive layer was formed. The adhesive layer was formed from an adhesive composition prepared by charging a closed vessel with initial components as follows: 20% by weight 2-ethyl hexyl acrylate, 5% by weight methyl acrylate, 1% by weight acrylic acid, 37% by weight ethyl acetate, 7% by weight isopropyl alcohol, 26.1% by weight toluene, and 3.75% by weight n-propanol. The weight percentages of each component were based on total weight of the reaction components, which also included 0.15% by weight benzoyl peroxide (98%) added in partial increments. To the initial components, 10% by weight of the benzoyl peroxide was first added. Then, the components were charged under a nitrogen atmosphere and using agitation. The vessel was heated at 80° C. until exotherm was reached. The exotherm was maintained by addition of the remaining benzoyl peroxide. After the benzoyl peroxide was depleted and the exotherm was complete, aluminum acetal acetonate was added to the polymerized solution in the amount of 0.4% by weight based on solid weight of the polymer.
This adhesive composition was coated onto the release liner and dried in a 14-zone oven, at 20 seconds per zone, with the zone temperatures set as follows: zone 1 (50° C.), zone 2 (60° C.), zone 3 (70° C.), zone 4 (80° C.), zone 5 (90° C.), zone 6 (90° C.), zones 7-10 (100° C.), and zones 11-14 (120° C.). With drying, the aluminum acetal acetonate functioned to crosslink the polymer. The thickness of the adhesive layer thus formed was 60 microns. The construction was then run through a chill stack to reduce the temperature to about 30° C.
A 150-micron-thick film of extruded aliphatic polyurethane, available from Stevens Urethane under the trade designation, SS-2219-92, was then provided and laminated to the exposed adhesive layer. This further construction was run through the 14-zone oven and then again chilled to about 30° C.
Meanwhile, an 18-micron-thick film for the topcoat layer was formed on a 76-micron thick (3-mil-thick) silicone-coated polyester carrier film. The film was formed by solution coating the polyurethane-based composition described below on the supporting carrier film. After the composition was coated on the carrier film, it was run through the 14-zone oven and then chilled to about 30° C.
The polyurethane-based composition was prepared by charging a closed vessel with 7.36% by weight of a hybrid linear hexane diol/1,6-polycarbonate polyester having terminal hydroxyl groups, 43.46% by weight toluene, 43.46% by weight isopropyl alcohol, and 0.03% by weight dibutyl tin laureate. The weight percentages of each component were based on total weight of the reaction components, which also included 5.68% by weight isophorone diisocyanate added later. The components were charged under a nitrogen atmosphere and using agitation. After the vessel was heated to 90° C., 5.68% by weight isophorone diisocyanate was continually added to the vessel through the resultant exotherm. After the exotherm was complete, the composition was maintained at 90° C. for one additional hour while still using agitation.
Once the topcoat layer was thus formed, it was thermally bonded to the exposed surface of the carrier layer. During thermal bonding, the carrier layer and the topcoat layer were contacted for about three seconds with application of heat 150° C. (300° F.) and 140 Pa (20 psi) pressure. Prior to testing, the release liner and carrier film were removed.
All of the individual components used in preparation of the protective sheet are readily available from a variety of chemical suppliers such as Aldrich (Milwaukee, Wis.) and others. For example, the isopropyl alcohol and toluene can be obtained from Shell Chemicals (Houston, Tex.).
Samples of the protective sheet were then tested according to the Tensile Testing Method, Recovery Testing Method, and Elongation Force Testing Method described above. Test data is reported in Table 1. Further, samples of the protective sheet were tested according to the Weathering Testing Method described above. After weathering for 500 hours, no visible yellowing was observed by the unaided human eye. Finally, samples of the protective sheet were tested for deglossing by placing them in an outside environment in the states of Florida and Arizona for approximately one year. After one year, no visible deglossing was observed by the unaided human eye.
For each example, a 150-μm (0.006-inch) thick film of a polycaprolactone-based, aliphatic thermoplastic polyurethane film (available from Argotec, Inc. of Greenfield, Mass.) is positioned as an outer layer on top of four stacked layers of prepreg carbon fiber fabric. The resulting 5-layer structure is then placed into a heated platen press for a period of about 45 minutes, at a temperature of about 120° C. (250° F.) and an applied pressure of about 0.34 MPa (50 psi). During this step, the resin composition within the prepreg is cured. The sample is then removed from the platen press and allowed to cool.
Any suitable epoxy resin composition can be used in this process. A number of commercial suppliers and published documents provide formulation guidelines for epoxy resin systems (e.g., “EPON® Resin Chemistry” published by Resolution Performance Products). Most Bisphenol-A and Bisphenol-F epoxy resins are expected to be suitable for use as the epoxy resin according to these Examples 2A-2C. Most amine-curing agents are expected to be suitable for use therein as well.
Resin Formulation 2A
As recommended in the company's data sheet for Amicure CG-1200 (an amine curing agent available from Air Products and Chemicals, Inc. of Allentown, Pa.), a suitable epoxy resin formulation is as follows:
Amicure CG-1200, in the amount of 4-15 phr (parts per hundred weight epoxy resin), is added to an epoxy resin having an epoxide equivalent weight (EEW) of 190. Numerous examples of Bisphenol-F and Bisphenol-A epoxy resins with an EEW of approximately 190 are commercially available, including for example, EPON Resin 828 (a Bisphenol-A epoxy resin available from Resolution Performance Products of Houston, Tex.).
Resin Formulation 2B
As recommended in the company's data sheet for Amicure UR (an amine curing agent available from Air Products and Chemicals, Inc. of Allentown, Pa.), a suitable epoxy resin formulation is as follows:
Amicure CG-1200 (an amine curing agent available from Air Products and Chemicals, Inc. of Allentown, Pa.), in the amount of 6 phr, is added to an epoxy resin having an EEW of 190. Numerous examples of Bisphenol-F and Bisphenol-A epoxy resins with an EEW of approximately 190 are commercially available, including for example, EPON Resin 828 (a Bisphenol-A epoxy resin available from Resolution Performance Products of Houston, Tex.). In addition, Amicure UR cure accelerator (a substituted urea-based accelerator available from Air Products and Chemicals, Inc. of Allentown, Pa.) is added in the amount of 2 phr.
Resin Formulation 2C
As recommended in the company's data sheet for Ancamine 2441 (a modified polyamine curing agent available from Air Products and Chemicals, Inc. of Allentown, Pa.), a suitable epoxy resin formulation is as follows:
Ancamine 2441 in the amount of 5 phr, is added to an epoxy resin having an EEW of 190. Numerous examples of Bisphenol-F and Bisphenol-A epoxy resins with an EEW of approximately 190 are commercially available, including for example, EPON Resin 828 (a Bisphenol-A epoxy resin available from Resolution Performance Products of Houston, Tex.). In addition, Amicure CG-1200 (an amine curing agent available from Air Products and Chemicals, Inc. of Allentown, Pa.), in the amount of 6 phr, is added to the epoxy resin.
Several layers of carbon fiber prepreg were prepared by hand-coating sufficient epoxy thermoset resin into a 12K woven carbon fiber fabric. The epoxy resin formulation was prepared based on 100 phr of EPON 863 (a Bisphenol-F epoxy resin available from Resolution Performance Products of Houston, Tex.), 22.4 phr of Ancamine 2441 (a modified polyamine curing agent available from Air Products and Chemicals, Inc. of Allentown, Pa.), and 5 phr of CAB-O-SIL TS-720 (a treated fumed silica available from Cabot Corporation of Billerica, Mass.). A protective sheet was directly bonded to the resulting epoxy-carbon fiber article using in-mold vacuum bag processing. The protective sheet consisted of a 150-μm (0.006-inch) thick film of a polycaprolactone-based, aliphatic thermoplastic polyurethane film (available from Argotec, Inc. of Greenfield, Mass. under the trade designation ARGOTEC 49510-6).
A flat aluminum plate was used as a vacuum bag mold surface. Prior to configuring a vacuum bag assembly thereon, the aluminum plate was cleaned and treated with the Waterworks Aerospace Release System available from Waterworks of East Ellijay, Ga. The vacuum bag assembly was constructed utilizing the following material components: Vacuum Bagging Film (a modified nylon blue vacuum bagging film available from The Composites Store, Inc. of Tehachapi, Calif.), Sealant Tape (available from The Composites Store, Inc. of Tehachapi, Calif. under the description “Yellow Super Seal Tacky Tape”), Breather Fabric (non-woven polyester fabric available from Richmond Aircraft Products, Inc. of Norwalk, Calif. under the trade designation, A 3000), Separator Release Film (perforated, violet FEP fluorocarbon release film available from Richmond Aircraft Products, Inc. of Norwalk, Calif. under the trade designation, A5000 Release Film), Bleeder Fabric (non-woven polyester fabric available from Richmond Aircraft Products, Inc. of Norwalk, Calif. under the trade designation, A 3000), and Peel Ply Release Film (PTFE-coated fiberglass fabric available from Airtech International, Inc. of Huntington Beach, Calif. under the trade designation, RELEASE EASE 234TFP).
The protective sheet was placed adjacent the aluminum plate. Then, four approximately 8-cm×13-cm (3-in×5-in) layers of the 12K carbon fiber prepreg were stacked on the protective sheet for processing in the vacuum bag assembly. After assembly of the vacuum bag system was complete, a vacuum was pulled on the prepreg stack for about 10 minutes to compress the various layers. While still pulling the vacuum, the entire assembly was placed into an oven at 120° C. (250° F.) for 60 minutes to cure the epoxy resin.
After cooling, the resulting carbon fiber composite articles were removed. Upon visual inspection, it was noted that the protective sheet was intimately bonded to the carbon fiber composite article. Surface finish of the protective sheet mirrored that of the aluminum plate.
Two layers of carbon fiber prepreg braid were prepared by hand coating sufficient epoxy thermoset resin into a 3K-braided carbon fiber sock. The epoxy resin formulation was prepared based on 100 phr of EPON 863 (a Bisphenol-F epoxy resin available from Resolution Performance Products of Houston, Tex.), 22.4 phr of Ancamine 2441 (a modified polyamine curing agent available from Air Products and Chemicals, Inc. of Allentown, Pa.), and 5 phr of CAB-O-SIL TS-720 (a treated fumed silica available from Cabot Corporation of Billerica, Mass.). A protective sheet was directly bonded to the resulting epoxy-carbon fiber composite article using a bladder molding process. The protective sheet consisted of a single layer of 0.35-mm (0.014-inch) aliphatic polyurethane film (available from Argotec, Inc. of Greenfield, Mass. under the trade designation ARGOTEC 49510-14).
The tubular cavity of a two-piece aluminum mold was used to define the outer surface of a lacrosse stick shaft to be formed from a composite material. The mold was approximately 81 centimeters (32 inches) in length and approximately 2.5 centimeters (1 inch) in diameter and was configured as an octagonal shape, which is common to lacrosse stick shafts. Prior to configuring the mold assembly, the protective sheet was applied to the tubular cavity, which was first coated with FEP release agent. An inflatable mandrel was constructed by fixturing a tubular latex bladder (available from Latex Technology Inc. of San Marcos, Calif.) over a steel tube attached to a supply of pressurized air. The prepreg braid was placed over the inflatable mandrel and the assembly was inserted into the mold cavity.
Pressurized air was applied to the inflatable mandrel causing the bladder to inflate and moving the prepreg braid into contact with the protective sheet against the mold surface. Pressure inside the bladder was increased to 0.17 MPa (25 psi) in order to compress the layers of prepreg braid and integrally bond the prepreg braid and the protective sheet. The mold was heated 5° C. per minute to 120° C., at which point it was held at 120° C. for 45 minutes to allow the epoxy resin to cure.
After cooling, the resulting carbon fiber composite lacrosse stick shaft was removed. Upon visual inspection, it was noted that the protective sheet was integrally bonded to the carbon fiber composite article. Surface finish of the protective sheet mirrored that of the aluminum mold.
Various modifications and alterations of the invention will become apparent to those skilled in the art without departing from the spirit and scope of the invention, which is defined by the accompanying claims. It should be noted that steps recited in any method claims below do not necessarily need to be performed in the order that they are recited. Those of ordinary skill in the art will recognize variations in performing the steps from the order in which they are recited.
| Number | Date | Country | Kind |
|---|---|---|---|
| PCT/US2006/060160 | Oct 2006 | WO | international |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US2007/067377 | 4/25/2007 | WO | 00 | 1/26/2009 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2008/051629 | 5/2/2008 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3296196 | Lamoreaux | Jan 1967 | A |
| 3463662 | Hodes et al. | Aug 1969 | A |
| 3523100 | Stein et al. | Aug 1970 | A |
| 3549583 | Nobuyoshi et al. | Dec 1970 | A |
| 3554951 | Blomeyer et al. | Jan 1971 | A |
| 3616198 | Saito | Oct 1971 | A |
| 3661672 | McQuade, Jr. | May 1972 | A |
| 3867350 | Pedain et al. | Feb 1975 | A |
| 4081578 | Van Essen et al. | Mar 1978 | A |
| 4092198 | Scher et al. | May 1978 | A |
| 4092199 | Ungar et al. | May 1978 | A |
| 4093766 | Scher et al. | Jun 1978 | A |
| 4101698 | Dunning et al. | Jul 1978 | A |
| 4154882 | Ungar et al. | May 1979 | A |
| 4207356 | Waugh | Jun 1980 | A |
| 4241140 | Ammons | Dec 1980 | A |
| 4269945 | Vanderhider | May 1981 | A |
| 4296156 | Lustig et al. | Oct 1981 | A |
| 4371686 | Yamamoto et al. | Feb 1983 | A |
| 4420525 | Parks | Dec 1983 | A |
| 4476293 | Robinson | Oct 1984 | A |
| 4550052 | Malek | Oct 1985 | A |
| 4657795 | Foret | Apr 1987 | A |
| 4748192 | Smith | May 1988 | A |
| 4751121 | Kuhnel et al. | Jun 1988 | A |
| 4774043 | Beckmann | Sep 1988 | A |
| 4810540 | Ellison et al. | Mar 1989 | A |
| 4900611 | Carroll | Feb 1990 | A |
| 4913760 | Benson et al. | Apr 1990 | A |
| 4919994 | Incremona et al. | Apr 1990 | A |
| 4933237 | Krenceski et al. | Jun 1990 | A |
| 4948654 | Brooks et al. | Aug 1990 | A |
| 5000903 | Matzinger et al. | Mar 1991 | A |
| 5034275 | Pearson et al. | Jul 1991 | A |
| 5055346 | Rohrbacher | Oct 1991 | A |
| 5070172 | Hirai et al. | Dec 1991 | A |
| 5077373 | Tsuda et al. | Dec 1991 | A |
| 5114514 | Landis | May 1992 | A |
| 5114789 | Reafler | May 1992 | A |
| 5203189 | Lovejoy et al. | Apr 1993 | A |
| 5215811 | Reafler et al. | Jun 1993 | A |
| 5219643 | Schmidt et al. | Jun 1993 | A |
| 5232527 | Vernhet et al. | Aug 1993 | A |
| 5242751 | Hartman | Sep 1993 | A |
| 5268215 | Krenceski et al. | Dec 1993 | A |
| 5288356 | Benefiel | Feb 1994 | A |
| 5306548 | Zabrocki et al. | Apr 1994 | A |
| 5310080 | Figge | May 1994 | A |
| 5334450 | Zabrocki et al. | Aug 1994 | A |
| 5391686 | Jadhav et al. | Feb 1995 | A |
| 5405675 | Sawka et al. | Apr 1995 | A |
| 5468532 | Ho et al. | Nov 1995 | A |
| 5486096 | Hertel et al. | Jan 1996 | A |
| 5518786 | Johnson et al. | May 1996 | A |
| 5556677 | Quigley et al. | Sep 1996 | A |
| 5562979 | Easterlow et al. | Oct 1996 | A |
| 5587230 | Lin et al. | Dec 1996 | A |
| 5604006 | Ponchaud et al. | Feb 1997 | A |
| 5620819 | Conforti et al. | Apr 1997 | A |
| 5688571 | Quigley et al. | Nov 1997 | A |
| 5707941 | Haberle | Jan 1998 | A |
| 5768285 | Griep et al. | Jun 1998 | A |
| 5770313 | Furumoto et al. | Jun 1998 | A |
| 5786285 | Walla et al. | Jul 1998 | A |
| 5849168 | Lutz | Dec 1998 | A |
| 5866257 | Schledjewski et al. | Feb 1999 | A |
| 5912081 | Negele et al. | Jun 1999 | A |
| 5912193 | Iwata et al. | Jun 1999 | A |
| 5912195 | Walla et al. | Jun 1999 | A |
| 5928778 | Takahashi et al. | Jul 1999 | A |
| 5955204 | Yamamoto et al. | Sep 1999 | A |
| 5965256 | Barrera | Oct 1999 | A |
| 5968444 | Yamamoto | Oct 1999 | A |
| 5985079 | Ellison | Nov 1999 | A |
| 6001906 | Golumbic | Dec 1999 | A |
| 6054208 | Rega et al. | Apr 2000 | A |
| 6132864 | Kiriazis et al. | Oct 2000 | A |
| 6153718 | Imashiro et al. | Nov 2000 | A |
| 6177189 | Rawlings et al. | Jan 2001 | B1 |
| 6254712 | Enlow et al. | Jul 2001 | B1 |
| 6319353 | Mussig | Nov 2001 | B1 |
| 6369186 | Branlard et al. | Apr 2002 | B1 |
| 6383644 | Fuchs | May 2002 | B2 |
| 6389602 | Alsaffar | May 2002 | B1 |
| 6436531 | Kollaja et al. | Aug 2002 | B1 |
| 6475616 | Dietz et al. | Nov 2002 | B1 |
| 6485836 | Reihs et al. | Nov 2002 | B2 |
| 6518359 | Clemens et al. | Feb 2003 | B1 |
| 6518389 | Kaufhold et al. | Feb 2003 | B1 |
| 6579601 | Kollaja et al. | Jun 2003 | B2 |
| 6592173 | Hardgrive et al. | Jul 2003 | B2 |
| 6602591 | Smith | Aug 2003 | B1 |
| 6607831 | Ho et al. | Aug 2003 | B2 |
| 6612944 | Bureau | Sep 2003 | B1 |
| 6624276 | Lamers et al. | Sep 2003 | B2 |
| 6627018 | O'Neill et al. | Sep 2003 | B1 |
| 6638467 | Yamamoto | Oct 2003 | B1 |
| 6642159 | Bhatnagar et al. | Nov 2003 | B1 |
| 6649003 | Spain et al. | Nov 2003 | B1 |
| 6649693 | Konishi et al. | Nov 2003 | B2 |
| 6651011 | Bache | Nov 2003 | B1 |
| 6659625 | Hanasaki | Dec 2003 | B2 |
| 6673428 | Reafler | Jan 2004 | B1 |
| 6677028 | Lasch et al. | Jan 2004 | B1 |
| 6680111 | Leibler et al. | Jan 2004 | B1 |
| 6682679 | Marentic et al. | Jan 2004 | B1 |
| 6709723 | Roys et al. | Mar 2004 | B2 |
| 6709748 | Ho et al. | Mar 2004 | B1 |
| 6713185 | Carlson et al. | Mar 2004 | B2 |
| 6723427 | Johnson et al. | Apr 2004 | B1 |
| 6723472 | Nakanishi et al. | Apr 2004 | B2 |
| 6730388 | MacQueen et al. | May 2004 | B2 |
| 6733870 | Enlow et al. | May 2004 | B2 |
| 6734273 | Onder | May 2004 | B2 |
| 6755757 | Sutherland | Jun 2004 | B2 |
| 6762243 | Stender et al. | Jul 2004 | B2 |
| 6770360 | Mientus et al. | Aug 2004 | B2 |
| 6790525 | Takeuchi et al. | Sep 2004 | B2 |
| 6790526 | Vargo et al. | Sep 2004 | B2 |
| 6797098 | Watanabe et al. | Sep 2004 | B2 |
| 6806212 | Fyfe | Oct 2004 | B2 |
| 6824834 | Schafheutle et al. | Nov 2004 | B2 |
| 6827895 | Yamamoto | Dec 2004 | B1 |
| 6835267 | Spain et al. | Dec 2004 | B1 |
| 6838130 | Spain et al. | Jan 2005 | B1 |
| 6852268 | Valyi et al. | Feb 2005 | B1 |
| 6852418 | Zurbig et al. | Feb 2005 | B1 |
| 6866383 | Naik et al. | Mar 2005 | B2 |
| 6869496 | Kollaja et al. | Mar 2005 | B1 |
| 6881856 | Tanaka et al. | Apr 2005 | B2 |
| 6890628 | Kerr | May 2005 | B2 |
| 6893596 | Haas et al. | May 2005 | B2 |
| 6908401 | Cheng | Jun 2005 | B2 |
| 6998084 | Horansky | Feb 2006 | B2 |
| 7005103 | Smith et al. | Feb 2006 | B2 |
| 7005794 | Watanabe et al. | Feb 2006 | B2 |
| 7011777 | Schmidt | Mar 2006 | B2 |
| 7048989 | Watkins et al. | May 2006 | B2 |
| 7108618 | Frischmon et al. | Sep 2006 | B2 |
| 7128669 | Blotteaux | Oct 2006 | B2 |
| 7141294 | Sakurai et al. | Nov 2006 | B2 |
| 7141303 | Clemens et al. | Nov 2006 | B2 |
| 7166249 | Abrams et al. | Jan 2007 | B2 |
| 7282533 | Kreitschmann et al. | Oct 2007 | B2 |
| 7316832 | Steinhardt et al. | Jan 2008 | B2 |
| 7931954 | Kobayashi et al. | Apr 2011 | B2 |
| 8117679 | Pierce | Feb 2012 | B2 |
| 20020006516 | Ito et al. | Jan 2002 | A1 |
| 20020061374 | O'Brien et al. | May 2002 | A1 |
| 20020157772 | Enlow et al. | Oct 2002 | A1 |
| 20020195910 | Hus et al. | Dec 2002 | A1 |
| 20030003282 | Roys et al. | Jan 2003 | A1 |
| 20030211334 | Jones | Nov 2003 | A1 |
| 20040048073 | Bacon | Mar 2004 | A1 |
| 20040071980 | McBain et al. | Apr 2004 | A1 |
| 20040096630 | Sakurazi et al. | May 2004 | A1 |
| 20040170793 | Linden et al. | Sep 2004 | A1 |
| 20040214007 | Brown et al. | Oct 2004 | A1 |
| 20050042431 | Wagenblast | Feb 2005 | A1 |
| 20050059309 | Tsotsis | Mar 2005 | A1 |
| 20050069698 | Eubanks et al. | Mar 2005 | A1 |
| 20050113194 | Pearson | May 2005 | A1 |
| 20050136205 | Stoppelmann et al. | Jun 2005 | A1 |
| 20050148404 | Ignatius | Jul 2005 | A1 |
| 20050156358 | Bellefleur et al. | Jul 2005 | A1 |
| 20050159060 | Shao | Jul 2005 | A1 |
| 20050164008 | Rukavina | Jul 2005 | A1 |
| 20050181203 | Rawlings et al. | Aug 2005 | A1 |
| 20050191490 | Ton-That et al. | Sep 2005 | A1 |
| 20050214559 | Minoda et al. | Sep 2005 | A1 |
| 20070036929 | Baird et al. | Feb 2007 | A1 |
| 20070047099 | Clemens et al. | Mar 2007 | A1 |
| 20070116933 | Kobayashi et al. | May 2007 | A1 |
| 20070178239 | Kestell et al. | Aug 2007 | A1 |
| 20080003406 | Steelman | Jan 2008 | A1 |
| 20080261014 | McGuire et al. | Oct 2008 | A1 |
| 20080286576 | McGuire | Nov 2008 | A1 |
| 20090186198 | McGuire | Jul 2009 | A1 |
| 20090292057 | Handa et al. | Nov 2009 | A1 |
| 20100059167 | McGuire | Mar 2010 | A1 |
| 20100062250 | Johnson et al. | Mar 2010 | A1 |
| 20110045306 | Johnson et al. | Feb 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 600 241 | Jul 1977 | DE |
| 197 15 871 | Jun 1998 | DE |
| 0978374 | Feb 2000 | EP |
| 1004608 | Oct 2004 | EP |
| 2 404 729 | Jan 2012 | EP |
| 2 463 093 | Jun 2012 | EP |
| 2 463 094 | Jun 2012 | EP |
| 2169228 | Jun 1990 | JP |
| 2000-260252 | Sep 2000 | JP |
| 2005335120 | Dec 2005 | JP |
| WO-9413465 | Jun 1994 | WO |
| WO-2007048141 | Apr 2007 | WO |
| WO-2007048145 | Apr 2007 | WO |
| WO-2007120188 | Oct 2007 | WO |
| WO-2009041964 | Apr 2009 | WO |
| Entry |
|---|
| “EPON Resins and Modifiers,” Resolution Performance Products SC:3059-01 (2002). |
| AircraftLog: Where Smart Solutions Take Flight, PPG Industries, Inc. (Huntsville, AL) (May 2005), pp. 10-11 and 16. |
| “CAB-O-SIL TS-720,” Cabot Corporation (Billerica, MA) PDS-141 (Jan. 2006). |
| “Aircraft Painting,” KLM Engineering & Maintenance, www.klm-em.com (Jun. 27, 2007). |
| Engineering EDGE, Air France KLM (Jan. 2006). |
| Umamaheswaran, Venkatakrishnan et al., “New Weatherable Film Technology to Eliminate Painting of Automotive Exteriors,” Society of Automotive Engineers: 2001-01-0443, (2001). |
| “Argotec 49510 Technical Data Sheet,” Argotec, Inc. (Greenfield, MA) (Oct. 2003). |
| “EPON Resin 863 Technical Data Sheet,” Hexion Specialty Chemicals (Houston, TX) RP:4041 (Jun. 2004). |
| “EPON Resin 862 Product Bulletin,” Resolution Performance Products (Houston, TX) RP:4048 (Mar. 2005). |
| “Epoxy Curing Agents and Modifiers: Amicure UR Curing Agent,” Air Products and Chemicals (Allentown, PA) Publication No. 125-9416.11. |
| “EPON Resin 828 Product Bulletin”, Resolution Performance Products (Houston, TX) RP:3075-01 (Apr. 2002). |
| “Blade Protection Kits Keep Helicopters in the Air,” EngineeringTalk (www.engineeringtalk.com/news/mmr/mmr102.html) (Sep. 16, 2005). |
| “EPON Resin Structural Reference Manual—EPON Resins—EPI-CURE Curing Agents—Heloxy Modifiers,” Resolution Performance Products (Houston, TX), pp. 3i to 3-6 (2001). |
| “3M Aircraft Belly Protective Tape 8641 Technical Data Sheet,” Minnesota Mining & Manufacturing Co. (St. Paul, MN) Publication No. 70/0703-7681-2 (Mar. 2007). |
| “3M Polyurethane Protective Tape 8674/8674DL Technical Data Sheet,” Minnesota Mining & Manufacturing Co. (St. Paul, MN) Publication No. 60/9700-0074-5 (Nov. 2005). |
| “3M Polyurethane Protective Tape 8672/8672 GB Technical Data Sheet,” Minnesota Mining & Manufacturing Co. (St. Paul, MN) Publication No. 78-9236-7045-5 (Nov. 2004). |
| “Improved Scotchgard Paint Protection Film Uses Latest 3M Technology,” 3M News: SEMA Show 2005, (Nov. 1, 2005). |
| “Ford Pressure Sensitive Performance Testing (Venture Tape) for Test Materials: 7510 and 7514,” ACT Laboratories, Inc. (Hillsdale, MI), published at: http://www.invisiblepatterns.com/pdf/AIN154314C.pdf, (Dec. 30, 2005). |
| “Paint Protection Film FAQ's,” previously published at: http://enprodistributing.com/products/protection/faq.htm, (Jul. 12, 2005). |
| “Scotchgard Paint Protection Film SGPF6 for Professional Applicators,” 3M Technical Data Sheet 75-3469-1065-8, Minnesota Mining & Manufacturing Co. (St. Paul, MN) (Apr. 2004). |
| “Scotchgard Paint Protection Film: Application Guide for Professional Applicators,” 3M Technical Update 75-3469-1102-9, Minnesota Mining & Manufacturing Co. (St. Paul, MN) (Apr. 2004). |
| “3M Paint Protection Film: A Clear Alternative to Vehicle Bras or Guards,” 3M Automotive Aftermarket Division 75-3467-9992-9, Minnesota Mining & Manufacturing Co. (St. Paul, MN) (2003). |
| “3M Paint Protection Film Builds Business through the SEMA Show,” 3M Holding Fast, 3M Automotive Division (St. Paul, MN), 1(25) (2002). |
| “Venture Shield Paint Protection 7510,” VentureTape (Rockland, MA), published at: http://www.venturetape.com/final/automotive—products.asp?id=609 (Jul. 12, 2005). |
| “Venture Shield—Paint Protection 7512”, VentureTape (Rockland, MA), published at: http://www.venturetape.com/final/automotive—products.asp?id=610 (Jul. 12, 2005). |
| “Test Report—Venture Shield 7510,” Bodycote Materials Testing Met-Chem Laboratory, published at: http://www.invisiblepatterns.com/pdf/067682.pdf, Letter Dated Jan. 14, 2004—Report No. 067682 (Jan. 14, 2003). |
| “Argotec Fills Industry Need with Thin, Aliphatic-Grade Polyurethane Films,” Argotec Press Release—www.argotecinc.com, (2006). |
| Number | Date | Country | |
|---|---|---|---|
| 20100068446 A1 | Mar 2010 | US |