The present invention relates to disperse dyes based on phenoxycarboxylic acid esters as coupling component, a process for the preparation of such dyes and to the use thereof in dyeing or printing semisynthetic and especially synthetic hydrophobic fibre materials, more especially textile materials.
Disperse azo dyes derived from substituted anilines as coupling component with ester groups in the side chain have been known for a long time and are used in dyeing hydrophobic fibre materials. It has, however, been found that the dyeings or prints obtained using the currently known dyes do not in all cases satisfy today's requirements, especially in respect of light fastness and fastness to washing. There is therefore a need for new dyes that especially have good washing fastness properties.
It has now been found, surprisingly, that the dyes according to the invention meet the criteria given hereinbefore to a considerable degree.
The present invention accordingly relates to disperse dyes that yield dyeings having a high degree of light fastness and fastness to washing and that, in addition, have good build-up characteristics both in the exhaust and thermosol processes and in textile printing.
The dyes according to the invention correspond to formula
wherein R1 and R2 are each independently of the other hydrogen, vinyl, allyl or C1-C6alkyl which is unsubstituted or substituted by cyano, carboxy, hydroxy, C1-C6alkoxy or C6-C24aryl,
R3 is hydrogen, C1-C6alkyl or C6-C24aryl,
R4 is hydrogen, C1-C6alkyl, 2-Cyano-C1-C6alkyl, 2-Alkoxy-C1-C6alkyl, 2-oxo-C1-C6alkyl or C6-C24aryl,
n is 0, 1 or 2, and
D denotes a radical of formula (2), (3), (4), (5), (6) or (7)
wherein
R5 is hydrogen, nitro, cyano or halogen,
R6 and R7 are each independently of the other hydrogen, nitro, cyano or halogen,
R8 and R9 are each independently of the other hydrogen, nitro, cyano or halogen,
R10 and R11 are each independently of the other nitro, cyano, trifluoromethyl, carboxy, C1-C6alkyl, C1-C6alkoxy, C1-C6acylamino or halogen,
R12 and R13 are each independently of the other hydrogen, nitro, cyano, trifluoromethyl, carboxy, C1-C6alkoxycarbonyl, C1-C6alkylsulfonyl, C1-C6alkylsulfonylamino, C1-C6acylamino or halogen,
R14 represents nitro, cyano or halogen,
R15 is C1-C6alkyl, and
R16 is nitro, cyano, trifluoromethyl, carboxy, C1-C6alkylsulfonyl, C1-C6alkylsulfonylamino, C1-C6acylamino or halogen.
Any radical denoting alkyl may be a straight-chain or branched alkyl radical.
Examples of alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, isopentyl, neopentyl and n-hexyl.
Substituted alkyl groups include, for example, 2-hydroxyethyl, 2-hydroxypropyl, 4-hydroxybutyl, 2-cyanoethyl, 2-cyanopropyl, 4-cyanobutyl, 2-methoxyethyl, 2-carboxyethyl and 4-methoxybutyl
C1-C6alkoxy may be, for example, methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, iso-butoxy, sec-butoxy, tert-butoxy, n-pentoxy, neopentoxy or n-hexoxy.
Any radical denoting halogen may be fluorine, chlorine or, preferably, bromine.
C6-C24Aryl groups are, for example, phenyl, tolyl, mesityl, isityl, naphthyl and anthryl.
Suitable C1-C6acylamino groups as radical R10, R11, R12, R13 or R17 are, for example, acetylamino, propionylamino and n-butyrylamino.
The dyes of formula (1) wherein n is 0 or 1, in particular 0, are preferred.
Preference is given to dyes of formula (1) wherein R1 and R2 are ethyl, benzyl or allyl.
R3 is preferably hydrogen.
R4 is preferably methyl.
Preference is given to dyes of formula (1) wherein n is 0, R3 is hydrogen and R4 is methyl.
Further preferred dyes of formula (1) are those wherein D is a radical of formula (2) as defined hereinbefore, wherein R5 is nitro.
Further preferred dyes of formula (1) are those wherein D is a radical of formula (3) as defined hereinbefore, wherein R6 and R7 are nitro.
Likewise, dyes of formula (1) are preferred, wherein D is a radical of formula (4) as defined hereinbefore, wherein R8 is nitro and R9 is hydrogen or bromine.
Furthermore, dyes of formula (1) are preferred, wherein D is a radical of formula (5) as defined hereinbefore, wherein R10 and R11 are each independently of the other nitro, cyano, trifluoromethyl, methoxy, chlorine or bromine.
Special preference is given to dyes of formula (1), wherein D is a radical of formula (5) as defined hereinbefore, wherein R12 is hydrogen or methoxycarbonyl.
Particularly preferred are dyes of formula (1), wherein D is a radical of formula (5) as defined hereinbefore, wherein R13 is nitro, cyano, methylsulfonyl or bromine.
Further preferred dyes of formula (1) are those wherein D is a radical of formula (6) as defined hereinbefore, wherein R14 represents cyano or bromine.
Moreover, dyes of formula (1) are preferred, wherein D is a radical of formula (7) as defined hereinbefore, wherein R16 is nitro or methylsulfonyl.
The present invention also relates to the process for the preparation of an azo dye of formula (I), which comprises diazotizing a compound of formula D-NH2, wherein D is as defined hereinbefore, according to a conventional method and then coupling the diazotized compound with a coupling component of formula (8)
wherein R1, R2, R3, R4 and n are as defined hereinbefore.
The diazotization of the compound of formula D-NH2 is carried out in a manner known per se, for example with sodium nitrite in an aqueous acidic medium, for example an aqueous hydrochloric acid medium or aqueous sulfuric acid medium. The diazotization can, however, also be carried out using other diazotizing agents, for example nitrosylsulfuric acid. An additional acid may be present in the reaction medium in the diazotization procedure, e.g. phosphoric acid, sulfuric acid, acetic acid, propionic acid, hydrochloric acid or a mixture of such acids, for example a mixture of propionic acid and acetic acid. The diazotization is advantageously carried out at temperatures from −10 to +30° C., e.g. from 0° C. to room temperature.
Coupling of the diazotized compound of formula D-NH2 to the coupling component of formula (8) is likewise carried out in known manner, for example in an aqueous acidic medium or aqueous organic medium, advantageously at temperatures from −10 to 30° C., especially below 10° C. The acid used may be, for example, hydrochloric acid, acetic acid, propionic acid, sulfuric acid or phosphoric acid.
The compounds of formula D-NH2 are known or can be prepared in a manner known per se.
The coupling components of formula (8) are likewise known or can be prepared in a manner known per se, for example by reacting 3-nitrophenol with a halogensubstituted carboxylic acid ester at pH>7, followed by reduction of the nitro compound to the corresponding amine, for example with tin, zinc or iron in hydrochloric acid or by hydration with Raney nickel, and, finally, reaction of the unsubstituted amine with alkyl chloride, allyl chloride or benzyl chloride.
The dyes according to the invention may be used for dyeing or printing semi-synthetic and especially synthetic hydrophobic fibre materials, more especially textile materials. Textile materials composed of blend fabrics that comprise such semi-synthetic or synthetic hydrophobic fibre materials can also be dyed or printed using the dyes according to the invention.
Semi-synthetic fibre materials that come into consideration are, especially, cellulose 2½-acetate and cellulose triacetate.
Synthetic hydrophobic fibre materials consist especially of linear, aromatic polyesters, for example those of terephthalic acid and glycols, especially ethylene glycol, or condensation products of terephthalic acid and 1,4-bis(hydroxymethyl)cyclohexane; of polycarbonates, e.g. those of α,α-dimethyl-4,4-dihydroxy-diphenylmethane and phosgene, and of fibres based on polyvinyl chloride or on polyamide.
The application of the dyes according to the invention to the fibre materials is effected in accordance with known dyeing methods. For example, polyester fibre materials are dyed in the exhaust process from an aqueous dispersion in the presence of customary anionic or non-ionic dispersants and, optionally, customary swelling agents (carriers) at temperatures of from 80 to 140° C. Cellulose 2½-acetate is dyed preferably at from 65 to 85° C. and cellulose triacetate at temperatures of from 65 to 115° C.
The dyes according to the invention will not colour wool and cotton present at the same time in the dyebath or will colour such materials only slightly (very good reservation) so that they can also be used satisfactorily in the dyeing of polyester/wool and polyester/cellulosic fibre blend fabrics.
The dyes according to the invention are suitable for dyeing in accordance with the thermosol process, in the exhaust process and for printing processes.
In such processes, the said fibre materials can be in a variety of processing forms, e.g. in the form of fibres, yarns or nonwoven, woven or knitted fabrics.
It is advantageous to convert the dyes according to the invention into a dye preparation prior to use. For this purpose, the dye is ground so that its particle size is on average from 0.1 to 10 microns. Grinding can be carried out in the presence of dispersants. For example, the dried dye is ground together with a dispersant or kneaded into a paste form together with a dispersant and then dried in vacuo or by atomisation. After adding water, the resulting preparations can be used to prepare printing pastes and dyebaths.
For printing, the customary thickeners will be used, e.g. modified or unmodified natural products, for example alginates, British gum, gum arabic, crystal gum, locust bean flour, tragacanth, carboxymethyl cellulose, hydroxyethyl cellulose, starch or synthetic products, for example polyacrylamides, polyacrylic acid or copolymers thereof, or polyvinyl alcohols.
The dyes according to the invention impart to the said materials, especially to polyester materials, level colour shades having very good in-use fastness properties such as, especially, good fastness to light, fastness to heat setting, fastness to pleating, fastness to chlorine, and wet fastness, e.g. fastness to water, to perspiration and to washing; the finished dyeings are further characterised by very good fastness to rubbing. Special emphasis should be given to the good fastness properties of the dyeings obtained with respect to perspiration and, especially, to washing.
The dyes according to the invention can also be used satisfactorily in producing mixed shades together with other dyes.
Furthermore, the dyes and dye mixtures according to the invention are also well suited to dyeing hydrophobic fibre materials from supercritical CO2.
The present invention relates to the above-mentioned use of the dyes according to the invention as well as to a process for the dyeing or printing of semi-synthetic or synthetic hydrophobic fibre materials, especially textile materials, in which process a dye according to the invention is applied to the said materials or incorporated into them. The said hydrophobic fibre materials are preferably textile polyester materials. Further substrates that can be treated by the process according to the invention and preferred process conditions can be found hereinbefore in the more detailed description of the use of the dyes according to the invention.
The invention relates also to hydrophobic fibre materials, preferably polyester textile materials, dyed or printed by the said process.
The dyes according to the invention are, in addition, suitable for modern reproduction processes, e.g. thermotransfer printing.
The Examples that follow serve to illustrate the invention. Parts therein are parts by weight and percentages are percentages by weight, unless otherwise indicated. Temperatures are given in degrees Celsius. The relationship between parts by weight and parts by volume is the same as between grams and cubic centimetres.
300 g of 3-nitrophenol are added to 800 ml of DMF. Then 240 g of sodium carbonate are added portionwise. Subsequently 270 g of chloroacetic acid methylester is added at 22° C. Then the mixture is stirred at 85° C. for six hours. After being cooled down to 25° C. it is given to 3 kg of water and 1 kg of ice. The resulting suspension is filtered off. The filter cake is washed with 300 g of water and dried in vacuum. Yield: 407 g.
30 g of 3-methoxycarbonylmethoxyaniline are given into 144 g of hydrochloric acid. Then 40 g of tin granulate and 140 ml of methanol are added. The temperature is held between 40 and 50° C. while cooling with a water bath. After one hour the reaction is complete. It is cooled down to 10° C. and filtered off from unreacted tin. While rapid stirring, a solution of 75 g sodium carbonate in 500 g of water is added whereupon a white suspension is obtained. Than 1000 ml of methanol are added while the temperature is kept between 10 and 15° C. with an ice bath. After stirring for half an hour the suspension is filtered. Methanol is removed from the filtrate in vacuum. The liquid residue is extracted three times with 150 ml ethyl acetate. The organic layer is dried with sodium sulfate and the solvent is removed in vacuum. Yield: 18 g.
22 g of 3-aminophenoxyacetic acid methylester are solved in 63 g allyl bromide. Subsequently, 10 g of sodium carbonate are added portionwise and the temperature is raised to 45° C. The reaction mixture is stirred at this temperature for 4.5 hours. The insoluble salt is filtered off and washed with 70 g of ethyl acetate. The combined filtrates are kept at 5° C. for 12 h. After the extraction with water, the organic phase is dried with sodium sulfate and the solvent is removed in vacuum (60° C., 28 mbar). Yield: 24 g (dark oil).
10 g of 3-aminophenoxyacetic acid methylester are solved in 19 g benzyl chloride. Subsequently, 14 g of sodium carbonate are added portionwise and the temperature is raised to 100° C. The reaction mixture is stirred at this temperature for 3 hours. The insoluble salt is filtered off and washed with 100 ml of ethyl acetate. The combined filtrates are kept at 5° C. for 12 h. After the extraction with water and brine, the organic phase is dried with sodium sulfate and the solvent is removed in vacuum (50° C., 10−2 mbar). Yield: 22 g (dark oil).
14 g of 3-aminophenoxyacetic acid methylester are solved in 20 ml DMF. Subsequently, 18 g of sodium carbonate are added portionwise, the temperature is raised to 50° C. and 38 g of diethyl sulfate are added. The reaction mixture is stirred at 60 to 65° C. for one hour. The insoluble salt is filtered off and washed with 75 g of ethyl acetate. After the extraction with brine, the organic phase is dried with sodium sulfate and the solvent is removed in vacuum (60° C., 80 mbar). Yield: 15 g (dark oil).
14 g of sulfuric acid (97%) are added to 11.5 g of ice. After the solution has cooled down to 20° C., 3.4 g of 2-amino-3-chlor-5-nitrobenzonitrile is added. Subsequently, 3.4 g of nitrosyl sulfuric acid (40% in sulfuric acid) are added while the reaction mixture is cooled. Then the mixture is stirred for two hours at 20° C. and cooled down to 5° C. before coupling.
A solution of the coupling component is prepared by addition of 4.6 g of sulfuric acid and 4.5 g of 3-diallylaminophenoxyacetic acid methylester to 50 ml water. Afterwards, 9.3 g of acetic acid, 2.6 g of a solution (10%) of sulfamic acid and 22 g of ice are added, followed by the addition of the solution of the diazonium salt. The temperature is held between 4 and 8° C. while adding 46 g of ice and afterwards the reaction mixture is allowed to grow warm to 20° C. It is stirred for 22 hours at room temperature, filtered and washed until it becomes neutral. The wet filter cake (32 g) is given to 57 g water. 137 mg of Surfynol 104E and acetic acid are added in an amount to adjust the pH value between 3 and 4. The mixture is stirred at 95° C. for six hours.
Subsequently, the hot solution is filtered off and the filter cake is dried in vacuum.
Yield: 5.8 g of the dye of formula (101);
wavelength of the absorption maximum λmax=558 nm
3.9 g of 2-amino-3,5-dinitrothiophene are dissolved in 30 g sulfuric acid (97%). Then 3.9 g of nitrosyl sulfuric acid (40% in sulfuric acid) are added at 0-5° C. The mixture is stirred for four hours at this temperature.
A solution of the coupling component is prepared by addition of 5.3 g of 3-diallylaminophenoxyacetic acid methylester and 5.5 g of sulfuric acid (97%) to 65 g of water. After cooling to 0° C., the diazonium salt solution is added at 0-5° C. within 30 minutes. The reaction mixture is stirred for 17 hours while it is allowed to warm to 15° C. Then it is filtered and washed with water until the filtrate becomes colorless. The wet filter cake (13 g) is given to 40 g water. 0.1 g of Surfynol 104E and acetic acid are added in an amount to adjust the pH value between 3 and 4. The mixture is stirred at 95° C. for one hour. Then the hot solution is filtered off and the filter cake is dried in vacuum.
Yield: 9 g of the dye of formula (102); λmax=640 nm
3.9 g of 3-amino-5-nitrobenzoisothiazol are dissolved in 15 g sulfuric acid (97%). Then 5.0 g of nitrosyl sulfuric acid (40% in sulfuric acid) are added at 0-5° C. The mixture is stirred for four hours at this temperature.
A solution of the coupling component is prepared by addition of 3.7 g of 3-diethylaminophenoxyacetic acid-methylester and 4.0 g of sulfuric acid (97%) to 45 g of water. After cooling to 0° C., the diazonium salt solution is added at 0-5° C. and at a pH value between 0.8 and 1.4 (addition of sodium acetate). The reaction mixture is stirred for 17 hours while it is allowed to grow warm to 15° C. Then it is filtered and washed with water until the filtrate becomes colorless. The wet filter cake (13 g) is given to 100 g water. 0.1 g of Surfynol 104E and acetic acid are added in an amount to adjust the pH value between 3 and 4. The mixture is stirred at 95° C. for one hour. Then the hot solution is filtered off and the filter cake is dried in vacuum.
Yield: 4 g. of the dye of formula (103); λmax=626 nm.
Analogously to Example I.1 the azo dyes listed in Table 1 can be prepared.
1 part by weight of the dye of formula (101) prepared in Example I.1 is milled together with four parts of a commercially available dispersing agent and 15 parts of water. Using that formulation, a 1% dyeing (based on the dye and the substrate) is produced on woven polyester by high temperature exhaust process at 130° C.
Test results: the light fastness of the dyeing is excellent as well as the results in the AATCC 61 and ISO 105 tests. The build up properties of the dye are very good.
Example II.1 is repeated by using the dyes of formulae (102)-(136) instead of the dye of formula (101). The build up properties of the dyes are very good and the dyeings exhibit good light fastness and very good results in the AATCC 61 and ISO 105 tests.
| Number | Date | Country | Kind |
|---|---|---|---|
| 08167141.4 | Oct 2008 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2009/062300 | 9/23/2009 | WO | 00 | 4/19/2011 |