Patent Application
20220041544
The present disclosure belongs to a technical field of adhesive materials, and specifically relates to an azobenzene derivative, a preparation method thereof, an azophenyl light control reversible adhesive, and a method of using the same.
Flexible displays have the characteristics of lightness and thinness, rollability, impact resistance, etc., and have a huge potential market in the field of portable electronic products. A liquid crystal display (referred to as LCD) and an organic light emitting display (referred to as OLCD) both can achieve flexible displays.
In the process of preparing flexible displays, a key technology for preparing flexible devices in the field of flexible display technology is how to separate the flexible substrate from the carrier substrate. In the prior art, mechanical lift-off or laser lift-off technology is usually used. The laser lift-off technology causes less damage to the flexible substrate, so it is widely used. In the laser lift-off technology, the flexible substrate is disposed on the glass substrate (that is, the glass substrate is used as the carrier substrate), and then the display components are prepared on the flexible substrate. After the preparation, the contact interface between the glass substrate and the flexible substrate is irradiated with a laser so as to separate the flexible substrate from the glass substrate.
When the laser irradiates the contact interface between the glass substrate and the flexible substrate, the energy may also be absorbed by the flexible substrate, causing the flexible substrate to ablate and release gas. Therefore, the flexible substrate expands partly and forms wrinkles after cooling, and even local stress is excessive and the flexible substrate is warped, causing product defects.
For solving the above technical problems, the present disclosure provides an azobenzene derivative, a preparation method thereof, an azophenyl light control reversible adhesive and a method of using the same.
In order to solve above technical problems, the present disclosure provides a technical solution which is:
an azobenzene derivative, having a molecular structure shown as below:
An azophenyl light control reversible adhesive, comprising abovementioned azobenzene derivative P1 and/or P2.
A method of using the abovementioned azophenyl light control reversible adhesive, comprising steps of:
SS1: coating an azophenyl light control reversible adhesive in a liquid state on a surface of a flexible substrate opposite to a glass substrate, so as to adhere the flexible substrate to the glass substrate, and then standing for a predetermined time;
SS2: forming display components on the flexible substrate;
SS3: irradiating the glass substrate with green light; and
SS2: applying opposite forces to the flexible substrate and the glass substrate, respectively, to separate the flexible substrate and the glass substrate.
In the present disclosure, the melting point of an azobenzene derivative P1 or P2 is modified commonly by alkyl chains and binaphthol to be slightly higher than room temperature. P1 and P2 in a liquid state may be cured spontaneously and quickly within 2 minutes and then exhibit an excellent bonding property after cured. The bonding strength can reach several megapascals to meet the requirements of subsequent processes. Under the irradiation of green light, the photothermal effect of the azobenzene derivative P1 or P2 causes the conversion from solid to liquid. After the irradiation of green light (under the same conditions of power and time, only green light (500-550 nm, 175 mW cm-2, 480 s-500 s) can achieve the conversion from solid to liquid of the azobenzene derivative P1 or P2), the azobenzene derivative P1 and P2 are heated to be melted and lose their bonding properties. This process is highly reversible. The heat in the process can be isolated on one side of the outer glass by the porous structure composed of ceramic fiber particles added. While heat cannot penetrate to one side of the panel, the middle layer peels off. This optical switch adhesive (azophenyl light control reversible adhesive) is easily soluble in common organic solvents, such as methylene chloride, easily cleaned and recovered, and can be recycled. The method is simple to operate and has low costs. The method may eliminate product defects caused by laser stripping, and can be used as a potential technology for stripping a flexible substrate.
In order to make the technical problems to be solved by the present disclosure, technical solutions, and beneficial effects clearer, the following further describes the present disclosure in detail with reference to the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are merely to explain the present disclosure, but not to limit the present disclosure.
In the present disclosure, the melting point of an azobenzene derivative P1 or P2 is modified commonly by alkyl chains and binaphthol to be slightly higher than room temperature. P1 and P2 in a liquid state may be cured spontaneously and quickly within 2 minutes and then exhibit an excellent bonding property after cured. The bonding strength can reach several megapascals to meet the requirements of subsequent processes. Under the irradiation of green light, the photothermal effect of the azobenzene derivative P1 or P2 causes the conversion from solid to liquid. After the irradiation of green light (under the same conditions of power and time, only green light (500-550 nm, 175 mW cm-2, 480 s-500 s) can achieve the conversion from solid to liquid of the azobenzene derivative P1 or P2), the azobenzene derivative P1 and P2 are heated to be melted and lose their bonding properties. This process is highly reversible. The heat in the process can be isolated on one side of the outer glass by the porous structure composed of ceramic fiber particles added. While heat cannot penetrate to one side of the panel, the middle layer peels off. This optical switch adhesive (azophenyl light control reversible adhesive) is easily soluble in common organic solvents such as methylene chloride, easy to clean and recover, and can be recycled. The method is simple to operate and has low cost. The method may eliminate product defects caused by laser stripping, and can be used as a potential technology for stripping a flexible substrate.
An azobenzene derivative, denoted as P1, having a molecular structure as below:
A preparation method of the azobenzene derivative P1 is as below: azobenzene, 3,4,5-tripentyloxybenzoic acid, 2,2′-dihydroxy-1,1′-binaphthol are provided with an amount ratio of 1:1:1; the above three raw materials are added into a reactor containing water to react together; the reactants are evenly stirred at 20° C. to react for 30 mins; the reaction mixture is then filtered (suction filtration) and dried; and an orange solid obtained is the azobenzene derivative P1. The melting point measured is 44° C.
The preparation method of the present disclosure is simple and low-cost. The reaction can take place at room temperature with water as the medium without catalyst, and the conversion rate of raw materials is as high as 85%-93%.
P1, as the optical switch adhesive (azophenyl light control reversible adhesive), is easily soluble in common organic solvents such as methylene chloride, easily cleaned and recovered, and can be recycled.
The preparation method of the azobenzene derivative P1 in this embodiment is as below: azobenzene, 3,4,5-tripentyloxybenzoic acid, 2,2′-dihydroxy-1,1′-binaphthol are provided with an amount ratio of 1:0.5:1.5; the above three raw materials are added into a reactor containing water to react together; the reactants are evenly stirred at 25° C. to react for 20 mins; the reaction mixture is then filtered (suction filtration) and dried; and an orange solid obtained is the azobenzene derivative P1.
The preparation method of the azobenzene derivative P1 in this embodiment is as below: azobenzene, 3,4,5-tripentyloxybenzoic acid, 2,2′-dihydroxy-1,1′-binaphthol are provided with an amount ratio of 1:1.5:0.5; the above three raw materials are added into a reactor containing water to react together; the reactants are evenly stirred at 30° C. to react for 25 mins; the reaction mixture is then filtered (suction filtration) and dried; and an orange solid obtained is the azobenzene derivative P1.
An azobenzene derivative, denoted as P2, having a molecular structure as below:
The preparation method of the azobenzene derivative P1 is as below: azobenzene, 3,4,5-tri(dodecyloxy)benzoic acid, 2,2′-dihydroxy-1,1′-binaphthol are provided with an amount ratio of 1:1:1; the above three raw materials are added into a reactor containing water to react together; the reactants are evenly stirred at 20° C. to react for 20 mins; the reaction mixture is then filtered (suction filtration) and dried; and an orange solid obtained is the azobenzene derivative P2.
The preparation method of the azobenzene derivative P1 in this embodiment is as below: azobenzene, 3,4,5-tri(dodecyloxy)benzoic acid, 2,2′-dihydroxy-1,1′-binaphthol are provided with an amount ratio of 1:0.5:1.5; the above three raw materials are added into a reactor containing water to react together; the reactants are evenly stirred at 25° C. to react for 30 mins; the reaction mixture is then filtered (suction filtration) and dried; and an orange solid obtained is the azobenzene derivative P2.
The preparation method of the azobenzene derivative P1 in this embodiment is as below: azobenzene, 3,4,5-tri(dodecyloxy)benzoic acid, 2,2′-dihydroxy-1,1′-binaphthol are provided with an amount ratio of 1:1.5:0.5; the above three raw materials are added into a reactor containing water to react together; the reactants are evenly stirred at 30° C. to react for 25 mins; the reaction mixture is then filtered (suction filtration) and dried; and an orange solid obtained is the azobenzene derivative P2
An azophenyl light control reversible adhesive comprises the azobenzene derivative P1 and/or P2 in any of Embodiments 1-6.
A method of using the azophenyl light control reversible adhesive comprises below steps of:
SS1: coating an azophenyl light control reversible adhesive in a liquid state on a surface of a flexible substrate opposite to a glass substrate, so as to adhere the flexible substrate to the glass substrate, and then standing for a predetermined time greater than or equal to 2 minutes, for example, 3 minutes, so as to make the azophenyl light control reversible adhesive to be cured quickly under room temperature;
SS2: forming display components on the flexible substrate;
SS3: irradiating the glass substrate with green light, wherein a time of irradiating with the green light is greater than or equal to 8 minutes, for example, 9 minutes, so as to allow the azophenyl light control reversible adhesive to convert from solid to liquid; and
SS2: applying opposite forces to the flexible substrate and the glass substrate, respectively, to separate the flexible substrate and the glass substrate.
The method is simple and low-cost. The azophenyl light control reversible adhesive is easily soluble in common organic solvents such as methylene chloride, easily cleaned and recovered, and can be recycled. It may eliminate product defects caused by laser stripping, and can be used as a potential technology for stripping a flexible substrate.
The azobenzene derivative P1 obtained in Embodiment 1 is placed at room temperature and irradiated with green light (500-550 nm, 175 mW cm-2) for 480 seconds. The state and temperature changes of the azobenzene derivative P1 are recorded. As shown in
The absorption spectra of 5 mg of azobenzene derivative P1 obtained in Embodiment 1 and 5 mg of azobenzene derivative P2 obtained in Embodiment 4 are measured to proof that the azobenzene derivative P1 and the azobenzene derivative P2 do have absorption within green light area as shown in
The azobenzene derivative P1 is coated on a surface of a flexible substrate opposite to a glass substrate, so as to adhere the flexible substrate to the glass substrate, and then stands for 2 minutes to cure. The cured P1 has a bonding strength reaching to 1.34 MPa as shown in
After irradiated with green light for 500 seconds, the azobenzene derivative P1 converts to liquid state and basically loses the bonding effect. When the irradiation is stopped, along with the release of heat, the liquid azobenzene derivative P1 quickly and spontaneously returns to the solid state within 2 minutes, and the bonding strength reaches to 1.32 MPa after the azobenzene derivative P1 is cured.
In the present disclosure, the melting point of an azobenzene derivative P1 or P2 is modified commonly by alkyl chains and binaphthol to be slightly higher than room temperature (44° C. and 53° C., respectively). P1 and P2 in liquid state may be cured spontaneously and quickly within 2 minutes and then exhibit an excellent bonding property after cured. The bonding strength can reach several megapascals to meet the requirements of subsequent processes. Under the irradiation of green light, the photothermal effect of the azobenzene derivative P1 or P2 causes the conversion from solid to liquid. After the irradiation of green light, the azobenzene derivative P1 and P2 are heated to be melted and lose their bonding properties. This process is highly reversible. The heat in the process can be isolated on one side of the outer glass by the porous structure composed of ceramic fiber particles added. While heat cannot penetrate to one side of the panel, the middle layer peels off.
The above descriptions are merely preferred embodiments of the present disclosure. For those of ordinary skill in the art, based on the idea of the present disclosure, many changes may be made in specific implementations and applications. These changes all belong to the protection scope of the present disclosure as long as these changes do not depart from the concept of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 202010787570.5 | Aug 2020 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2020/113756 | 9/7/2020 | WO | 00 |