The present invention generally relates to sensors composed of nanoscale structures, such as carbon nanotubes.
Materials technology has had a profound impact on the evolution of human civilization. In the 21st century, people are developing smart materials and smart sensors. Typically, materials employed for temperature and pressure sensing applications, such as polymers, exhibit both responses simultaneously, making it difficult to determine whether a change in temperature, pressure or both has occurred. More specifically, because temperature and pressure sensors composed of polymeric sensing elements respond simultaneously to both pressure and temperature it is difficult to determine what external environment has been applied to the sensor.
In one embodiment a sensor is provided that includes a first sensor element for measuring temperature and a second sensor element for measuring pressure. Broadly, the sensor includes a substrate, a first sensor element present on a first portion of the substrate composed of a first plurality nanostructures having a fixed number of electrical junctions, wherein changes in resistance or capacitance of the electrically interconnected carbon nanotubes is correlated to temperature measurements that are independent of pressure, and a second sensor element composed of a second plurality of nanostructures in which the number of junctions between the second plurality of nanostructures varies with changes in pressure that is applied to the second sensor element wherein resistance or capacitance changes in response to changes in the number of junctions between the second plurality of carbon nanotubes is correlated to a pressure measurement.
In one embodiment, a method of measuring temperature is provided that is independent of pressure. Broadly, the method may include providing a sensor element composed of a plurality of electrically interconnected nanostructures having a fixed number of junctions between each of the electrically interconnected nanostructures, applying a current through the electrically interconnected nanostructures, measuring electrical properties of the electrically interconnected nanostructures in response to an application of temperature to the sensor element, and correlating the electrical properties of the electrically interconnected nanostructures to temperature.
In one embodiment, a temperature sensor is provided that may be employed in the above described method of measuring temperature. Broadly, the temperature sensor may include a sensor element including a plurality of electrically interconnected carbon nanotubes having a fixed number of junctions between each of the electrically interconnected nanotubes, at least one electrical contact to the sensor element in electrical communication with the plurality of electrically interconnected carbon nanotubes, and a power source in connection with the at least one electrical contact providing a substantially constant current to the plurality of electrically interconnected carbon nanotubes, wherein resistance or capacitance of the electrically interconnected carbon nanotubes is correlated to temperature.
In another aspect, a temperature sensor is provided in which at least two carbon nanotubes are utilized in a thermocouple arrangement. Broadly, the temperature sensor includes a thermocouple body including a first carbon nanotube and a second carbon nanotube, the first carbon nanotube and the second carbon nanotubes having a junction at a first end of the thermocouple body, wherein the first carbon nanotube and the second carbon nanotube have dissimilar electrical properties, and a voltmeter in electrical communication with the first carbon nanotube and the second carbon nanotube, wherein the application of temperature to the first end of the thermocouple body produces a current in a circuit composed of the first carbon nanotube and the second carbon nanotube that is proportional to a temperature that is applied to the junction at the first end of the thermocouple body.
In another aspect, a method of measuring pressure is provided. Broadly, the method of measuring pressure includes providing a sensor element including a plurality of nanostructures; applying a current or voltage through the plurality of nanostructures; measuring electrical properties of the plurality of nanostructures in response to an application of pressure that increases or decreases a number of junctions in the plurality of nanostructures in the sensor element; and correlating the electrical properties of the plurality of nanostructures to pressure.
In one embodiment, a pressure sensor is provided that may be employed in the above-described method. Broadly, the pressure sensor includes a sensor element comprised of a plurality of vertically aligned carbon nanotubes fixed to a substrate, at least one electrical contact to the vertically aligned carbon nanotubes carbon nanotubes, and a power source in connection with the at least one electrical contact providing a substantially constant current to the plurality of vertically aligned carbon nanotubes carbon nanotubes, wherein resistance or capacitance of the electrically interconnected carbon nanotubes is correlated to pressure.
In another embodiment, a pressure sensor is provided that includes a plurality of flexible membranes each including electrically interconnected nanostructures, and a power source to the electrically interconnected nanostructures, wherein an external force applied to the pressure sensor deforms at least one of the plurality of flexible membranes into contact with an adjacent flexible membrane of the plurality of flexible membranes, in which changes in the electrical properties of the plurality of flexible membranes that results from the external force is correlated to a pressure value for the external force.
In another aspect, the present invention provides a sensor that includes a sensor element including a plurality of electrically interconnected nanostructures, a power supply to the plurality of electrically interconnected nanostructures, wherein the connectivity of the power supply to the electrically interconnected nanostructures provides a circuit, and a resonator in electrical communication with the circuit, in which electrical properties to the electrically interconnected nanostructures are varied by application of temperature or pressure to the pad, wherein changes in the electrical properties result in an impedance change in the circuit that produces a frequency response in the resonator, wherein the frequency response of the resonator is correlated to temperature or pressure.
The following detailed description, given by way of example and is not intended to limit the invention solely thereto, will best be appreciated in conjunction with the accompanying drawings, wherein like reference numerals denote like elements and parts, in which:
The present invention relates to the application of carbon nanotubes to temperature and pressure sensors, wherein the nature of the interconnection of the carbon nanotubes dictates the sensing characteristics of the sensor. The electrical properties, e.g., resistance, of carbon nanotubes have been determined to have a linear response to changes in temperature. In one example, by fixing the number of junctions between adjacent carbon nanotubes, the electrical pathway by which current travels through a plurality of electrically interconnected carbon nanotubes is held constant. By fixing the number electrical pathways through the plurality of electrically interconnected carbon nanotubes, the linearity of the electrical property response of the carbon nanotubes to variations in temperature may be realized so that temperature is measured independent of pressure.
In other embodiments of the present invention, the number of junctions may be varied in response to pressure. More specifically, when the number of junctions between adjacent carbon nanotubes that provide a plurality of electrically interconnected carbon nanotubes is not fixed, the application of pressure can increase the number of junctions to provide for an increase in the number of electrical pathways by which current travels through the electrically interconnected carbon nanotubes. Because, the decrease in resistance that results from the increased number of electrical pathways is at least one order of magnitude greater than the linear response of the electrical properties of the carbon nanotubes to temperature, the pressure may be measured independent of temperature.
Using the above principles, and by controlling the junction behavior between electrically interconnected carbon nanotubes, sensor elements may be provided in which temperature is measured independent of pressure and pressure is measured independent of temperature. Further, sensors can be provided that include a combination of temperature and pressure sensor elements, in which temperature sensor elements measure temperature independent of pressure, and pressure sensor elements measure pressure independent of temperature.
Detailed embodiments of the present invention are disclosed herein; however, it is to be understood that the disclosed embodiments are merely illustrative of the invention that may be embodied in various and alternative forms. In addition, each of the examples given in connection with the various embodiments of the invention are intended to be illustrative, and not restrictive. Further, the figures are not necessarily to scale, some features may be exaggerated to show details of particular components. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for teaching one skilled in the art to variously employ the present invention.
When describing the inventive structures and methods, the following terms have the following meanings, unless otherwise indicated.
As used herein a “sensor element” is the portion of a sensor that is exposed to a pressure or temperature to be measured.
As used herein a “nanostructure” is an object having at least one dimension between molecular and microscopic (micrometer-sized) dimension.
“Nanotube” as used herein is meant to denote one form of nanostructure having an aspect ratio of length to width greater than 10. The term “nanotube” includes single wall and multi-wall nanotubes unless specifically specified as distinct. In one embodiment, a carbon nanotube is at least one graphene layer wrapped into a cylinder. In one embodiment, a single wall carbon nanotube is a graphene rolled up into a seamless cylinder with diameter of the order of a nanometer. A multi-wall carbon nanotube is a plurality of graphene sheets rolled up into a seamless cylinder with diameter of the order of a nanometer.
“Electrical contact” means the electrically conductive connection from the plurality of electrically interconnected nanotubes to the circuit from which electrical properties are measured.
“Electrically interconnected” as used in conjunction with nanostructures means an electrically conductive pathway that is composed of at least two nanostructures that are engaged in electrical communication.
“Junction” with respect to nanostructures, e.g., nanotubes, means a point at which two nanostructures can transfer electrical charge from a first nanostructure to a second nanostructure in a plurality of electrically interconnected nanostructures.
“Electrically conductive”, “electrical communication”, and/or “electrically communicating” as used through the present disclosure means a material having a room temperature conductivity of greater than 10−8(Ω-m)−1.
“Linear” as used to describe the response in the electrical properties of the sensor element (having electrically interconnected carbon nanotubes therein) to changes in temperature means that a plot of the electrical properties of the sensor element, e.g., resistance or current, verses the temperature applied to the sensor element has a linear slope.
The term “independent” as used to describe the relationship between temperature and pressure in a sensor element that is measuring temperature means that there is substantially no change in the linear response of the electrical properties of the sensing element to changes in temperature by the application of pressure, so long as the application of pressure does not change the number of points of interconnection between the electrically interconnected carbon nanotubes in the sensor element.
A “matrix” is a medium between nanostructures that may be composed of a gas, liquid or solid.
For purposes of the description hereinafter, the terms “upper”, “lower”, “right”, “left, “vertical”, “horizontal”, “top”, “bottom”, “beneath”, “underlying”, “below”, “overlying” and derivatives thereof shall relate to the invention, as it is oriented in the drawing figures.
References in the specification to “one embodiment”, “an embodiment”, “an example embodiment”, etc., indicate that the embodiment described may include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described.
The present invention embodies the use of nanostructures, e.g., carbon nanotubes, such as nanotube mats, nanotube arrays, and composites thereof, as temperature and pressure sensors. In some examples, configurations of nanostructures, e.g., carbon nanotubes, such as nanotube mats, exhibit temperature sensing abilities, e.g., resistance as a function of temperature (resistance vs. temperature), with little to no pressure dependence, i.e., insensitive to pressure, so that temperature may be measured and sensed independent of pressure. In other embodiments, configurations of nanostructures are described that exhibit pressure sensing abilities, e.g., pressure as a function of temperature (pressure vs. temperature), with little to no temperature dependence, i.e., insensitive to temperature, so that pressure may be measured and sensed independent of temperature.
Although the following description is directed to temperature and pressure sensors having sensor elements composed of carbon nanotubes, the present invention is not limited thereto, as other nanostructures have been contemplated and are within the scope of the present invention. For example, the nanostructures that may be utilized in the sensor structures of the present invention include, but are not limited to: nanoribbons, such as carbon or ZnO nanoribbons; nanorods, such as ZnO nanorods doped with F, N, or In2O3 nanorods doped with Sn; or nanocylinders, such as single walled nanotubes, double wall nanotubes, few wall nanotubes, or multi-wall nanotubes. In one embodiment, the material of the nanostructures could be carbon and/or a metal oxide that is doped to increase conductivity, for example doped with small molecules or metal ions. Additionally, nanowires, nanotubes and nanoparticles have been considered as suitable materials to provide the temperature and pressure sensors that are disclosed herein.
In one embodiment, the electrically interconnected carbon nanotubes that are incorporated within the sensor element 10 are comprised of a mat of single or multi-wall carbon nanotubes. In one example, the electrically interconnected carbon nanotubes are provided by single wall carbon nanotube mats, as depicted in
It has been determined that the electrical resistivity of circuits formed using the above described carbon nanotube networks varies with changes in temperature. More specifically, in one embodiment, when a change in temperature is applied to a circuit that has been formed using a network of electrically interconnected carbon nanotubes a change in the resistivity of that circuit may be measure. For example, an oriented film of multiwall nanotubes may have a resistivity that is measured along the longest axis of the carbon nanotube of approximately 20 mΩ*cm or less at a temperature of 300 K, which has been measured to increase gradually in a linear manner with increasing temperature. By linear it is meant that when the resistivity is plotted as a function of temperature the slope of the line will be substantially equal to y=m(x)+b.
In one embodiment, the electrically interconnected carbon nanotubes have a temperature dependent resistivity that is defined by:
ρ(T)=αT+ρt exp (Tt/(T+Ts))
wherein ρ is the resistance in ohms/cm2, T is the temperature, α and ρt are temperature independent constants which incorporate geometric factors of the sample, Tt is the temperature corresponding to thermal voltage fluctuations which increase energy of electronic states above the activation energy, and Tt/Ts is the ratio defining the tunneling in the absence of thermal fluctuations. The expression αT represents the metallic conductivity, i.e., the conductivity of the carbon nanotubes 21, and the expression ρt exp (Tt/(T+Ts)) represents the barrier hoping conductivity that is measured at the nanotube bundle junctions 23 or nanotube defects.
Using the above temperature dependent resistivity characteristics of the electrically interconnected carbon nanotubes, a temperature sensor 100 may be provided in which a current is passed through a circuit containing the electrically interconnected carbon nanotubes, wherein changes in the resistivity that are measured from the electrically interconnected carbon nanotubes can be correlated to temperature.
One feature of carbon nanotube that contributes to the linear electrical property response to the application of temperature is that carbon nanotubes have a zero thermal expansion coefficient. Therefore, because the application of temperature does not result in a dimensional change of the carbon nanotubes, the junctions between the electrically interconnected carbon nanotubes are not affected by temperature variations.
In one aspect of the invention, due to the fixed number of junctions 23 between the plurality of electrically interconnected carbon nanotubes 21 in the sensor element 10, the temperature response that may be measured through electrical resistivity is independent of pressure. More specifically, because the electrically interconnected carbon nanotubes 21 have a fixed number of junctions 23, the electrically conductive pathways though the electrically interconnected carbon nanotubes 21 are not varied by changes in pressure. In embodiments of the invention in which the number of junctions 23 are not fixed, pressure changes can vary the number of junctions 23, which in turn changes the number of electrical pathways through the plurality of electrically interconnected carbon nanotubes 21, hence changing the resistivity of the plurality of electrically interconnected carbon nanotubes 21. Therefore, fixing the number of junctions 23 in the plurality of electrically interconnected carbon nanotubes 21 eliminates or at least minimizes the changes in electrical properties that typically result from pressure changes applied to the sensor element 10. Because the number of junctions 23 of the electrically interconnected carbon nanotubes 21 are fixed, the linear electrical property response of the plurality of electrically interconnected carbon nanotubes 21 to temperature can be measured without variation that results from the application of pressure, hence providing a sensor element 10 for measuring temperature that is insensitive to pressure. The thickness of the sensor element 10 of electrically interconnected carbon nanotubes is another factor that may contribute to the pressure independence of the temperature reading by providing a substantially fixed array of electrically interconnected carbon nanotubes. For example, a single layer of electrically interconnected carbon nanotubes on a substrate would be less susceptible to variations in electrical properties that result from pressure applications than multiple layers of electrically interconnected carbon nanotubes to the application of pressure, because a sensor element having a single layer of carbon nanotubes would eliminate the possibility of junctions formed by compressing the carbon nanotubes of the multiple layers into electrical contact in a manner that would increase the number of junctions between the carbon nanotubes. In one embodiment, the fixed nature of the bundles of carbon nanotubes may be aided by the introduction of a rigid matrix, such as a polymer having a shear modulus of 0.01 GPa at 300° K or greater, wherein in some examples the matrix material may have a shear modulus of 0.1 GPa at 300° K or greater.
The application of pressure to the sensor element 10 of a pressure independent temperature sensor 100 may result in a change in the value of the resistance for the electrically interconnected carbon nanotubes 21 that is no greater than variations in the resistance that occurs from experimental error, i.e., measurement error. Measurement error for the resistance may result from contact resistance within the measurement device or contact resistance from the measurement device to the sensor element 10. Variations from measurement error for the resistance of the sensor element 10 may be about 15.0% or less of the resistance being measured, more typically being less than 10.0%, and in some instances as low as 5.0% or less. Therefore, the application of pressure to the sensor element 10 of a pressure independent temperature sensor 100 may result in a change in the value of the resistance for the electrically interconnected carbon nanotubes 21 that is not greater than 10%. In an even further embodiment, the electrical properties of the sensing element that are correlated to a temperature value are not varied by a value greater than 5% by the application of a pressure. In yet another embodiment, the electrical properties of the sensing element that are correlated to a temperature value are not varied by a value greater than 0.5% by the application of a pressure.
In one embodiment, the thickness of the sensor element 10 may be greater than 20 nm. In one example, the thickness of the sensor element 10 of the electrically interconnected nanotubes 21 is no greater than 100 nm. In another embodiment, the thickness of the sensing element 10 that includes the pad 11 of the electrically connected nanotubes 21 ranges from about 20 nm to about 50 nm. In an even further embodiment, the thickness of the sensing element 10 of the electrically connected nanotubes 21 is less than 20 nm.
The carbon nanotubes 21 that provide the sensing element 10 typically have a high purity, i.e., have a low incidence of impurities. In one embodiment, the carbon nanotubes may have a high purity on the order of about 95% to about 99% carbon. In an even further embodiment, the carbon nanotubes have a high purity on the order of about 99% or greater.
The electrically interconnected carbon nanotubes having a fixed number of junctions may be provided by mat of carbon nanotubes, such as a mat of single wall carbon nanotubes. In one embodiment, a mat of single wall carbon nanotubes may be provided by laser vaporization. In one embodiment, the single wall carbon nanotubes are formed using laser vaporization in combination with a catalyst, such as a metal catalyst. In one embodiment, the catalyst is supported on a substrate, such as a graphite substrate, or the catalyst may be floating metal catalyst particles. In one embodiment, the metal catalyst may be composed of Fe, Ni, Co, Rh, Y or alloys and combinations thereof.
In one embodiment, laser vaporization includes a laser beam that impinges on a carbon (also referred to as graphite) target, such as a volume of a carbon containing feedstock gas, e.g., methane or carbon monoxide. In one embodiment, the laser used to vaporize the carbon target is a pulsed laser or is a continuous laser, wherein the carbon target is present in an oven at a temperature on the order of about 1200° C. In one embodiment, a pulsed laser has a light intensity on the order of about 100 kW/cm2, wherein a continuous laser has a light intensity on the order of about 12 kW/cm2. In one embodiment, the oven is filled with helium or argon gas in order to keep the pressure at 500 Torr.
In one embodiment, vapor plumes form, expand and cool. As the vaporized species cools, carbon molecules and atoms quickly condense to form larger clusters, which may include fullerenes. In one embodiment, the catalysts also begin to condense and attach to carbon clusters and prevent their closing into cage structures. Catalysts may open cage structures when they attach to them. In one embodiment, from these initial clusters, tubular molecules grow into single-wall carbon nanotubes until the catalyst particles become too large, or until conditions have cooled sufficiently that carbon no longer can diffuse through or over the surface of the catalyst particles. In one embodiment, the single-wall carbon nanotubes formed in this case are bundled together by van der waals forces to provide the network similar to that depicted in
The diameter of a single wall nanotube, as used in accordance with the present invention, typically ranges from about 1 nanometer to about 50 nanometers. In another embodiment, the diameter of a single wall nanotube ranges from about 1.2 nanometers to about 1.6 nanometers. In one embodiment the length of a single wall nanotube, as used in accordance with the present invention ranges from about 50 nanometers to about 10 microns. In another embodiment, the length of a single wall nanotube ranges from about 10 microns to about 20 millimeters. In one embodiment, the nanotubes used in accordance with the present invention have an aspect ratio of length to diameter on the order of approximately 200:1.
The carbon nanotubes produced by laser vaporization are typically formed in bundles. A bundle is a plurality of interconnected carbon nanotubes. In one example, a bundle of nanotubes contains on the order of 10,000 nanotubes or less. In another example, a bundle of nanotubes typically includes on the order of approximately 50 to approximately 5000 nanotubes. In one embodiment, a bundle of nanotubes has a diameter on the order of about 0.9 nm or greater.
The nanotubes comprise a majority of carbon typically being of high purity. In other examples, the nanotubes include a carbon content ranging from being greater than 50%, wherein a purification process is utilized to provide carbon nanotubes having of high purity, such as greater than 90% carbon. In one embodiment, the carbon nanotubes may be purified by a process that includes an acid treatment followed by an oxidation. In one embodiment, the acid treatment may include treatment and oxidation steps are provided by a dilute HNO3 reflux/air oxidation procedure.
In a following process step, the carbon nanotubes may be doped to adjust the conductivity of the carbon nanotubes. In one embodiment, n-type and p-type doping of carbon nanotubes is desirable to tune the conductivity of the carbon nanotubes for sensor applications. P-type denotes that the nanotube includes an excess of holes, i.e., positive charge carriers, wherein the nanotube may be doped with dopants to provide the excess of holes. N-type denotes that the nanotube includes an excess of electrons, i.e., negative charge carriers, wherein the nanotube may be doped with dopants to provide an excess of electrons.
In one embodiment, the carbon nanotubes become p-type following growth once exposed to the ambient air, wherein oxygen molecules are absorbed onto the carbon nanotube surface and through surface interactions alter the nanotube's electrical state rendering the nanotubes p-type conductivity. In another embodiment, exposure of the nanotube to potassium atoms may result in absorption of the potassium to the carbon nanotube, which dopes that region of the nanotube n-type. In a further embodiment, exposure of the carbon nanotube to fluorinated carboxylic acids and sulfonic acids produces a p-type conductivity carbon nanotube.
The nanotubes may be doped during production; purification processing, and/or post-processing. In one embodiment, the nanotubes may be doped during synthesis or by post processing through the use of gases, liquids, or solids, such as polymers, such as the polymers used in the polymer matrix. For example, post-growth doping nanotubes may be accomplished via deposition of dopant from vapor, liquid of solid phase in controlled atmosphere, vacuum or air. In one embodiment, deposition of dopants from vapor includes vapor gas absorption onto the carbon nanotubes. In one embodiment, deposition of dopants from liquid includes liquid dipping followed by a post treatment that may include heating and/or cooling. Examples of dopants may include, but at not limited to: nitric acid, thionyl chloride (SOCl2), triethylamine (Et3N), pyridine (C6H5N), orthodichlorobenzene or combinations thereof.
Although the above description is related to bundles of single or multi-wall carbon nanotubes, embodiments have been contemplated in which vertically aligned carbon nanotubes have been utilized in temperature sensors, so long as the vertically aligned carbon nanotubes are fixed in a rigid matrix so that the number of junctions that provide the electrical pathway though the sensor element 10 may be fixed.
Referring to
In one embodiment, the plurality of electrically interconnected carbon nanotubes may be positioned on the substrate 5 using a variety of deposition techniques that may include, but are not limited to: filtration of nanotubes from solutions onto filter paper and transferal to the substrate 5, spray deposition of solvated or suspended nanotubes, inkjetting, electrophoretic deposition onto substrates, electrospinning or a combination thereof.
In some embodiments, the plurality of electrically interconnected carbon nanotubes may be disposed within a matrix that may include, but is not limited to: insulating or conductive polymers, ceramics, metal powders and combinations thereof. The matrix may be employed to enhance or restrict conduction between the nanotubes themselves in the interconnected network. In one embodiment, the matrix may be composed of a polymer selected from the group including: but not limited to: poly(phenylene vinylene), polythiophenes, polypyridines, poly(pyridyl vinylenes), polyphenylenes and copolymers of these materials. In one embodiment, the polymer of the matrix may be a conjugated polymer. Conjugated polymers have a framework of alternating single and double carbon-carbon and/or carbon-nitrogen bonds or carbon-sulfur bonds. Single bonds are referred to as σ-bonds, and double bonds contain a σ-bond and a π-bond. Conjugated polymers have a σ-bond backbone of overlapping sp2 hybrid orbitals. The remaining out-of-plane pz orbitals on the carbon (or nitrogen) atoms overlap with neighboring pz orbitals to give π-bonds. When the sensor element 10 that is composed of the plurality of electrically interconnected carbon nanotubes further includes a polymer matrix, the nanotubes may be deposited atop the substrate 5 using spray deposition followed by spray deposition of the polymer matrix.
Still referring to
The power source to the sensor element 10 including the electrically interconnected carbon nanotubes can be an AC or DC power supply. In the embodiments of the invention in which the power source is a DC power supply, measurements of the resistance of the electrically interconnected carbon nanotubes are correlated to the temperature. In the embodiments of the invention in which the power source comprises an AC power supply, the capacitance of the electrically interconnected carbon nanotubes is measured and correlated to temperature. The power supply typically provides a constant value to provide a current through the electrically interconnected carbon nanotubes from which the voltage can be measured and in turn the resistance then determined.
In one embodiment, the above temperature sensor 100 is utilized in a method of measuring temperature that includes providing a sensor element 10 composed of a plurality of electrically interconnected carbon nanotubes 21 having a fixed number of junctions 23 between each of the electrically interconnected carbon nanotubes 21, applying a current through the electrically interconnected carbon nanotubes 21, measuring electrical properties of the electrically interconnected carbon nanotubes 21 in response to an application of temperature to the sensor element 10, and correlating the electrical properties of the electrically interconnected carbon nanotubes 21 to temperature. The electrical properties of the electrically interconnected carbon nanotubes 21 may be resistance or capacitance. The correlation of resistance or capacitance to temperature may be conducted using a computer.
In another aspect of the invention, carbon nanotubes may be configured to provide a temperature sensor having a thermocouple type arrangement. More specifically, in one embodiment, two dissimilar carbon nanotubes 200a, 200b are positioned to have at least one junction 210, as depicted by
An electric current flows in a closed circuit 300 of the two dissimilar carbon nanotubes 200a, 200b (hereafter referred to as a nanotube thermocouple circuit) when the junction 210 between the interconnected first carbon nanotube 200a and the second carbon nanotube 200b at the first end of the thermocouple body is subjected to a temperature change. In the nanotube thermocouple circuit, the current continues to flow as long as the junction 210 of the two dissimilar carbon nanotubes 200a, 200b is at a different temperature than the remaining portion of the first and second carbon nanotubes 200a, 200b. The magnitude and direction of the current depends on the temperature difference between the junction 210 and the remaining portion of the first and second carbon nanotubes 200a, 200b, and the properties of the first and second carbon nanotubes 200a, 200b. This effect is similar to the Seebeck effect that is utilized in temperature sensing using metal based thermocouples.
Any two dissimilar carbon nanotubes 200a, 200b can be used and the nanotube thermocouple circuit will generate a low voltage output that is proportional to the temperature difference between the junction 210 and the remaining portion of the first and second carbon nanotubes 200a, 200b. The term “dissimilar” as used to describe the carbon nanotubes utilized to provide the thermocouple type arrangement means that the electrical properties of the carbon nanotubes 200a, 200b in response to temperature change are not the same. In one embodiment, increasing or decreasing the number of defects that are present in the carbon nanotubes varies the electrical properties of the carbon nanotube so that a first carbon nanotube 200a is dissimilar from the second carbon nanotube 200b. Reducing the number of defects increases the conductivity of the carbon nanotubes. Therefore, the carbon nanotube having the reduced number of defects will have a lower resistance than the carbon nanotube having the greater number of defects. A carbon nanotube having a lesser degree of defects will have a lower resistance, and therefore be dissimilar than carbon nanotube having a greater degree of defects.
The number of defects that are present in a carbon nanotube may be decreased though an annealing process. Examples of annealing processes that can reduce the defects in the carbon nanotubes include annealing with pure methanol at 100° C. for a time period of approximately four hours; annealing at 1250° C. for four hours; and annealing at 2800° C. for four hours. Dissimilar carbon nanotubes may also be provided by different dopant types and concentrations within the carbon nanotubes and/or by different heat treatments of the carbon nanotubes.
For example, in one embodiment, dissimilar carbon nanotubes may be produced by varying the degree of oxygen adsorption that is present on the surface of the carbon nanotubes. For example, the concentration of oxygen that is adsorbed on the surface of the first carbon nanotube 200a may be reduced relative to the second carbon nanotube 200b by annealing the first carbon nanotube 200a in an argon containing atmosphere, wherein the anneal temperature may range from 100° C. to 1250° C.
One example of carbon nanotubes that are suitable for the first carbon nanotube 200a of the thermocouple body include carbon nanotubes doped with orthodichlorobenzene (ODCB). One example of carbon nanotubes that are suitable for the second carbon nanotube 200b of the thermocouple body include carbon nanotubes doped with thionyl chloride (or thionyl dichloride, SOCl2).
The junction 210 may be provided by physical contact between the first carbon nanotube 200a and the second carbon nanotube 200b. In one example, the junction 210 may further comprises a conductive weldment between the first carbon nanotube 200a and the second carbon nanotube 200b that is provided by electron beam or laser welding.
Electrical contacts 12 to each of the first and second carbon nanotubes 200a, 200b are present opposite the junction 210. The electrical contacts 12 to the first and second carbon nanotubes 200a, 200b of the thermocouple body are similar in function and composition as the electrical contacts 12 that are described above with reference to
A conventional voltmeter 230 may be electrically connected to the electrical contacts 12 to provide a circuit. Using the above described nanotube thermocouple circuit, temperatures ranging from about −200° C. to about +1200° C. may be measured with voltage increments corresponding to temperature changes on the order of about 41 μV/° C. In one embodiment, thermoelectric power generated by the carbon nanotubes 200a, 200b that provide the temperature sensor having the thermocouple arrangement may be used a power source.
In one embodiment, pressure sensitivity of the pressure sensor 110a is provided by flexibility of the vertically aligned carbon nanotubes 15 that are arranged in parallel and extend from a substantially rigid substrate 5, as depicted in
In one embodiment, the pressure sensor 110a may measure pressure values ranging from about 5 g/cm2 to about 4000 g/cm2. In another embodiment, the pressure sensor 110a may measure pressure values ranging from about 10 g/cm2 to about 1000 g/cm2. In a further embodiment, the pressure sensor 110a may measure pressure values ranging from about 50 g/cm2 to about 550 g/cm2. In an even further embodiment, the pressure sensor 110a may measure pressure values ranging from about 100 g/cm2 to about 150 g/cm2. It is noted that the above described ranges are provided for illustrative purposes and are not intended to limit the invention specifically thereto. For example, the pressure sensor 110a can measure any pressure, so long as the pressure does not diminish the structural integrity of the pressure sensor. By diminishing the structural integrity of the pressure sensor 110a it is meant that the pressure would sever the electrical connection of the vertically aligned carbon nanotubes 15 from the substrate 5.
Typically, the substrate 5 depicted in the embodiments of the invention that are consistent with
It is noted that the above described dimensions and pressures are provided for illustrative purposes only, since the range of pressures being measured by the structures described above may be modified by increasing or decreasing the dimensions separating the adjacent nanotubes 36 of the array of vertically aligned carbon nanotubes 15.
Referring to
Typically, the flexible substrate 29 has a shear modulus of less than about 1.5 GPa, typically ranging from about 1.0 GPa to about 0.5 GPa, and in some instances being as low as about 0.0005 GPa.
It is noted that the above described dimensions and pressures are provided for illustrative purposes only, since the range of pressures being measured by the structures described above may be modified by increasing or decreasing the dimensions separating the adjacent nanotubes of the vertically aligned carbon nanotubes 15 and/or by increasing or decreasing the shears modulus of the first skin 30 and/or second skin 35.
In one embodiment, the vertically-aligned nanotube arrays (VANTAs) that are utilized in the pressure sensors 100a, 100b that are depicted in
The patterned metal catalyst films are composed of a single layer or multilayers of thin metal films that are deposited by electron beam evaporation, sputtering, or chemical vapor deposition. In one embodiment, the metal catalyst film may include a transition metal including but not limited to Ni, Fe, or Co. In one embodiment, following deposition the metal catalyst film is patterned using photolithography and etch processes. The metal catalyst film may be patterned to provide dots patterns, pillars, stripes, and/or functional structures, such as sensor structures.
In one embodiment, the patterned metal catalyst film includes a buffer layer, e.g., Al, which is in contact with the substrate, and a metal catalyst, e.g., 0.2-1.0 nm of Fe formed atop the buffer layer. In one embodiment, the patterned metal catalyst film includes another metal layer, such as 0.2 nm of Mo.
The substrate including the pattered metal catalyst film is then placed inside a tube furnace and the temperature is raised under hydrogen and argon gas flow at various partial pressures. In one embodiment, hydrocarbon feedstocks may include other gases, such as acetylene with hydrogen and argon, or ethanol with hydrogen and argon, or methanol with hydrogen and argon, are passed over the patterned metal catalyst in a thermal chemical vapor deposition process, wherein carbon nanotubes grow from the patterned metal catalyst film. Following chemical vapor deposition, the method of forming vertically-aligned carbon nanotubes 15 may further include infiltration of the arrays with a polymer solution, followed by exfoliation of the film containing the vertically-aligned carbon nanotubes 15 by dissolution, peeling, and then physical exfoliation. In one embodiment, the carbon nanotubes produced in forming the vertically-aligned carbon nanotubes 15 may or may not be single wall carbon nanotubes (SWNTs).
In one embodiment, the vertically-aligned carbon nanotubes 15 may be infiltrated with polymer to maintain their alignment prior to the application of external pressure. Contrary to a network of carbon nanotubes, in which adjacent nanotubes are in electrical communication to provide a conductive path through the polymer matrix, adjacent vertically-aligned carbon nanotubes are parallel to one another. In one embodiment of the present invention, vertically-aligned carbon nanotubes 15 may be grown up to several millimeters in height or grown with limited heights of only one hundred nanometers with an accuracy of about 20 nm.
Referring to
In one embodiment, the power source to vertically aligned carbon nanotubes 15 is an AC or DC power supply. In the embodiments of the invention in which the power source is a DC power supply, measurements of the resistance of the electrically interconnected carbon nanotubes are correlated to the temperature. In the embodiments of the invention in which the power source comprises an AC power supply, the impedance of the electrically interconnected carbon nanotubes is measured and correlated to temperature. The power supply typically provides a constant value to provide a current through the electrically interconnected carbon nanotubes from which the voltage can be measured and in turn the resistance then determined. The correlation of resistance or impedance to temperature may be calibrated and calibration coefficients may used to correlate measured values to temperature.
It is noted that the above described dimensions and pressures are provided for illustrative purposes only, since the range of pressures being measured by the structures described above may be modified by increasing or decreasing the dimensions between the flexible membranes and by increasing or decreasing the shear modulus of the flexible membranes.
Referring to the pressure sensor 110c depicted in
In each of the embodiments depicted in
In another aspect, the present invention provides a sensor that includes a sensor element composed of a plurality of electrically interconnected nanostructures, a power supply to the plurality of electrically interconnected nanostructures, wherein the connectivity of the power supply to the electrically interconnected nanostructures provides a circuit, a resonator in electrical communication with the circuit, in which resistance to the electrically interconnected carbon nanotubes is varied by application of temperature or pressure to the pad, the changes in the resistance resulting in a reactive impedance of the circuit produces changes in a frequency response of the resonator, and a converter that correlates the changes in the frequency response of the resonator to temperature or pressure. A resonator is a device that exhibits resonance or resonant behavior, that is, it naturally oscillates at some frequencies, called its resonance frequencies with greater amplitude than others.
In one embodiment, the sensors of the present invention allow for simultaneous readings of pressure and temperatures while providing for wireless engagement to systems to which the pressure and temperature readings are transmitted. More specifically, in one example, because compression of the nanotubes in the array vertically aligned carbon nanotubes or mats of electrically interconnected carbon nanotubes changes their reactive capacitance and/or DC resistance, a patterned mat of electrically interconnected carbon nanotubes, or patterned network of vertically aligned carbon nanotubes, that forms an RF antennae may also function as the sensor element of a temperature and/or pressure sensor. For example, when the resistance of the film or coil that provides an RF antennae, which is produced by patterning an array of vertically aligned carbon nanotubes or patterning a mat of electrically interconnected carbon nanotubes, the frequency response of the RF resonator will change and can be remotely detectable.
The embodiments of the present invention provide specific sensing of pressure independent of temperature and specific sensing of temperature independent of pressure. The sensors described herein display a broad range of sensing and a high degree of linearity.
The following examples are provided to further illustrate aspects of the present invention and demonstrate some advantages that arise therefrom. It is not intended that the invention be limited to the specific examples disclosed.
Single wall carbon nanotubes were synthesized by laser vaporization and purified by dilute HNO3 reflux/air oxidation procedure. A conjugated polymer poly(2-methoxy-5-(2′-ethylhexyloxy)-1,4-phenylenevinylene) (MEHPPV) was provided having a molecular weight of 51,000 and a polydispersity of 1.1 for the matrix in which the single wall nanotubes were fixed to provide a pad of electrically interconnected carbon nanotubes. The polymer matrix and the single wall carbon nanotubes were mixed to formulate a composite material that was spin cast onto a polymeric substrate to provide the sensor element 10 of a temperature sensor 100, as depicted in
A 0.1 mA drive current was then applied to the sensor element including the electrically interconnected carbon nanotubes, while the sensor element was subjected to temperatures ranging from about 20° K to about 350° K. The resistance of the electrically interconnected carbon nanotubes was measured from the temperature sensor using a two point four wire configuration in a vacuum during the above described application of temperature and plotted to provide the linear temperature dependent resistivity (normalized to resistance at 300° K) that is depicted in
In each of the above examples, the linear temperature dependent resistivity of the temperature sensor did not appreciably change when subjected to pressure variations ranging from atmospheric pressure to 10−7 mmHg. Further, the linear temperature dependent resistivity of the temperature sensor did not change when subjected to static pressures as great as 200 g/5 mm.
The temperature sensors were exposed to temperatures ranging from 20° C. to 50° C., and static pressures ranging from 10 g/cm2 to 4,000 g/cm2. The static pressure was provided by applying a load ranging from 18 g to approximately 8,445 g to an area of the sensor element on the order approximately 2.05 cm2. While under the applied load, the temperature sensor was subjected to increasing temperature, wherein the electrical properties, i.e, resistance of the temperature sensor, was then measured and plotted in
The slope for the linear temperature dependent resistivity was then plotted in
Referring back to
The slope for the linear pressure response in the electrical properties, i.e, resistance, of the pressure sensor illustrated in
Temperature sensors having wireless properties that were produced from single wall nanotube (SWNT) mats that were either formed into an RF antenna using injetting, or by using patterning methods. The reactive capacitance and/or DC resistance of the RF antenna formed from the SWNT mat changes in response to temperature or pressure. This provides the RF antenna the ability to measure and transmit a wireless readout of pressure or temperature changes.
The temperature sensor can be used in a two frequency mixing model. The first frequency, which is smaller than critical frequency, may include information about temperature, and the second frequency, which is greater than the critical frequency, may include a bit (binary information) on whether the sensor reading is correct (bit=0). For example, if a high pressure and/or temperature, or other stimuli, damage or destroy the sensor, a reading of a non-zero slope at high frequency (bit≠0) will indicate such a condition.
While the present invention has been particularly shown and described with respect to the preferred embodiments thereof, it will be understood by those skilled in the art that the foregoing and other changes in forms of details may be made without departing from the spirit and scope of the present invention. It is therefore intended that the present invention not be limited to the exact forms and details described and illustrated, but fall within the scope of the appended claims.
This application is a divisional of U.S. patent application Ser. No. 12/547,562, filed Aug. 26, 2009 the entire content and disclosure of which is incorporated herein by reference.
This invention was made with government support under contract no. DE-AC05-00OR22725 awarded by the U.S. Department of Energy. The government has certain rights in the invention.