The present invention relates to a dielectric ceramic material. More particularly, the present invention relates to a dielectric ceramic material with properties suitable for use in applications such as UHF antennas where a proper combination of dielectric constant and loss factor is desirable.
Several different dielectric ceramic systems are of potential use in antennas for RF and Microwave Frequencies. The advantage of using dielectrics in microwave devices is size reduction of the antenna, which is due to the phenomenon that the length of electromagnetic wave in a medium is inversely proportional to square root of its dielectric constant (λ˜1/√K). The dielectric constant of most commercial microwave materials varies from ˜10 to 30-40 to 80-100 with maximal ten-fold size reduction of antenna or resonator being achieved in the latter case. Part of such materials are described in patents: U.S. Pat. No. 5,840,642 to Kim et al., U.S. Pat. No. 5,569,632 to Jung et al., KR20040051732, CN1519216, RU2167842; PCT published patent application WO9721642 to Suvorov et al.; JP3192606, JP3183657; U.S. Pat. No. 4,442,220 to Ouchi et al., all of which are herein incorporated by reference in their entirety.
However, even ten-fold size reduction is not sufficient for devices in the UHF domain (470 MHz to 870 MHz) where wavelength ranges from about 30 to 60 cm, which requires significant increase in dielectric constant of material. Materials with much higher dielectric constant (>1000) are based on ferroelectric systems, thus characterized by high dielectric losses and significant frequency dependence of properties at UHF. In order to form a viable UHF antenna a dielectric must have the correct combination of dielectric constant and loss factor to allow for the miniaturization of the antenna over the desired UHF frequency range 450 MHz to 900 MHz when combined with other components in the final antenna configuration. Dielectric ceramic with K in the range of 250 to 380, based on the Ag(Nb,Ta)O3 system is described in PCT published patent application WO9803446 to Valant et al., however these materials are very expensive, require oxygen atmosphere at sintering and exhibit relatively high dielectric losses at UHF.
What is needed is an improved dielectric material for use in UHF antennas and/or other applications.
Therefore, it is a primary object, feature, or advantage of the present invention to improve over the state of the art.
It is a further object, feature, or advantage of the present invention to provide an improved dielectric material suitable for use in UHF antennas.
A still further object, feature, or advantage of the present invention is to provide a ceramic dielectric material that does not require special atmosphere control during sintering.
Another object, feature, or advantage of the present invention is to provide a ceramic dielectric material that does not use expensive metals such as silver, niobium or tantalum.
Yet another object, feature, or advantage of the present invention is to provide a ceramic dielectric material that has a relatively high dielectric constant and a low dielectric loss.
One or more of these and/or other objects, features, or advantages of the present invention will become apparent from the specification and claims that follow.
A dielectric ceramic composition has a dielectric constant, K, of at least 200 and a dielectric loss, DF, of 0.0006 or less at 1 MHz. The dielectric ceramic composition may be formed by sintering by firing in air without a controlled atmosphere. The dielectric ceramic composition may have a major component of 92.49 to 97.5 wt. % containing 60.15 to 68.2 wt. % strontium titanate, 11.02 to 23.59 wt. % calcium titanate and 7.11 to 21.32 wt. % barium titanate; and a minor component of 2.50 to 7.51 wt. % containing 1.18 to 3.55 wt. % calcium zirconate, 0.50 to 1.54 wt. % bismuth trioxide, 0.2 to 0.59 wt. % zirconia, 0.02 to 0.07 wt. % manganese dioxide, 0.12 to 0.35 wt. % zinc oxide, 0.12 to 0.35 wt. % lead-free glass frit, 0.24 to 0.71 wt. % kaolin clay and 0.12 to 0.35 wt. % cerium oxide. The dielectric ceramic composition may be used in a broad band UHF antenna, in dielectric resonators, electrical filters, substrates, monolithic ceramic components, or otherwise.
A method of manufacturing includes providing a ceramic dielectric material consisting essentially of a major component of 92.49 to 97.5 wt. % containing 60.15 to 68.2 wt. % strontium titanate, 11.02 to 23.59 wt. % calcium titanate and 7.11 to 21.32 wt. % barium titanate, and a minor component of 2.50 to 7.51 wt. % containing 1.18 to 3.55 wt. % calcium zirconate, 0.50 to 1.54 wt. % bismuth trioxide, 0.2 to 0.59 wt. % zirconia, 0.02 to 0.07 wt. % manganese dioxide, 0.12 to 0.35 wt. % zinc oxide, 0.12 to 0.35 wt. % lead-free glass frit, 0.24 to 0.71 wt. % kaolin clay and 0.12 to 0.35 wt. % cerium oxide. The method further includes firing the ceramic dielectric material.
The invention described herein provides a ceramic formulation that when sintered into a ceramic substrate provides a material with high dielectric constant (>200) and low losses; <0.00060 @ 1 MHz). When combined with tuner circuit elements this substrate is an effective broad band UHF antenna. Furthermore, unlike the Ag(Nb,Ta)O3 system is described in PCT published patent application WO9803446 the invention herein does not require special atmosphere control during sintering nor does it use expensive metals such as silver, niobium or tantalum.
Following an extensive investigation of ceramic formulations in the SrTiO3—BaTiO3—CaTiO3 system a range of formulations was identified with the correct combination of properties for UHF broadband antennas. The compositions investigated are described in Table 1 below:
These ceramic compositions were formulated into ceramic slips and cast into substrates by methods well known in the art. After removal of organics in a bakeout process the final sintering was performed in air at temperatures 1270° C. and 1250° C. respectively, although other temperatures may be used. The dielectric properties were measured at 1 MHz and are shown in Table 2.
The dielectric constant (K) is very similar for the 2 different firing temperatures and there is a small variation in dielectric losses (DF). The temperature coefficient of capacitance (TCC) is similar for both firing temperatures. It is important to note that TCC for these compositions is very high compared to a Class 1 C0G multilayer capacitor formulation (±30ppm/° C. in the temperature range −55° C. to +125° C.) or a narrow band microwave antennas. In the case of the multilayer capacitor or narrow band microwave antenna stable properties with temperature are required to prevent a drift out of specification with temperature fluctuations. However, since these ceramics are used in a UHF antenna over a broad frequency band, temperature stability is less critical so higher TCC can be tolerated.
In order to form miniaturize the antenna whilst retaining low losses dielectric constant has to be maximized while retaining low losses.
The dielectric ceramic material may be used for other purposes in addition to use in UHF antennas. It may be used in dielectric resonators, filters, substrates for microelectronic circuits, or built-in to any number of types of electronic devices.
The present invention is not to be limited to the specific disclosure provided herein. The present invention contemplates variations in the formulation, the specific applications of the dielectric ceramic composition, the type of monolithic ceramic component incorporating the dielectric ceramic composition, the type of electronic device incorporating a UHF antenna, and other variations within the spirit and scope of the present invention.