Patent Application
20050029658
1. Field of the Invention
The present invention relates to a circuit board, and more specifically to a circuit board mounted with electronic parts including a semiconductor element to be used in a semiconductor device such as a power module.
2. Description of the Related Art
An example of a circuit board is disclosed in JP 06-310825 A. The circuit board according to this publication has an insulating layer and a Cu wiring layer, which are sequentially layered on a base plate formed of Al. A semiconductor element and other electronic parts are soldered to a surface of the Cu wiring layer in order to make the circuit board ready for use as a semiconductor device.
This circuit board exhibits high thermal conductivity and high dielectric strength, which are ensured by forming the insulating layer from two or more insulating resin layers different in filler content from one another.
Because the base plate of the circuit board is formed of Al having high thermal conductivity, heat generated in the electronic parts is transmitted through the Cu wiring layer and the insulating layer to the base plate and is then efficiently radiated from the base plate to the outside.
On the other hand, it is a known fact that the difference in thermal expansion coefficient between Al used to form the base plate and a semiconductor material such as Si used in the semiconductor element or other electronic parts is so large that a change in temperature of the circuit board causes thermal stress between the surface of the Cu wiring layer and the electronic parts. If the thermal stress is too great, the electronic parts might be warped and solder joining the electronic parts might be cracked.
In an attempt to ease this thermal stress, semiconductor devices for use in environments where the temperature fluctuates widely, for example, automobiles, is provided with a stress relieving member such as a heat spreader between the circuit board and the electronic parts.
However, interposing a stress relieving member causes an increase in number of parts that constitute the semiconductor device, which raises other problems including complication of the whole structure of the semiconductor device and an increase in manufacture cost.
The present invention has been made to solve the above problems, and an object of the present invention is therefore to provide a circuit board capable of, without using a stress relieving member, easing thermal stress that is generated between a wiring layer surface and electronic parts mounted to the surface.
A circuit board according to the present invention includes: a base plate; an insulating resin layer formed on a surface of the base plate; and a wiring layer formed on a surface of the insulating resin layer, the base plate being made of a material that is lower in thermal expansion coefficient than a material of the wiring layer to set the thermal expansion coefficient of a surface of the wiring layer lower than the thermal expansion coefficient of the material of the wiring layer.
With the thermal expansion coefficient of the surface of the wiring layer set lower than that of the material of the wiring layer, the difference in thermal expansion coefficient between the wiring layer surface and electronic parts mounted on the surface is reduced and accordingly thermal stress generated between the wiring layer surface and the electronic parts is eased.
A semiconductor device according to the present invention comprises the above circuit board and electronic parts mounted on the surface of the wiring layer of the circuit board.
An embodiment of the present invention will be described below with reference to the accompanying drawings.
The base plate 1 is made of the Al/SiC composite material which is obtained by pouring a melt of Al or a melt of an Al alloy containing Si into a mold filled with SiC powder and then casting to have a thermal expansion coefficient of 8.4×10−6/K. The insulating resin layer 2 is made of epoxy-based resin containing filler and having a glass transition temperature Tg of, for example, 152° C. The thermal expansion coefficient of Cu used to form the wiring layer 3 is 17.5×10−6/K, which makes the base plate 1 lower in thermal expansion coefficient than the wiring layer 3. The base plate 1 is 3 mm in thickness, the insulating resin layer 2 is 100 μm in thickness, and the wiring layer 3 is 100 μm in thickness.
It has been understood from a measurement with a strain gauge that the thermal expansion coefficient of a surface of the wiring layer 3 is about 9.2×10−6/K, and is lower than the thermal expansion coefficient of Cu constituting the wiring layer 3 (17.5×10−6/K).
It is understood from
For instance, when the base plate 1 is made of an Al/SiC composite material that has a thermal expansion coefficient of 8.4×10−6/K, a thermal expansion coefficient of the surface of the wiring layer 3 is about 13×10−6/K by setting the glass transition temperature Tg of the insulating resin layer 2 to 50° C., about 12×10−6/K by setting the glass transition temperature Tg of the insulating resin layer 2 to 90° C., and about 9×10−6/K by setting the glass transition temperature Tg of the insulating resin layer 2 to 152° C. Therefore, the thermal expansion coefficient of the surface of the wiring layer 3 can be set between 9×10−6/K and 13×10−6/K by choosing as the insulating resin layer 2 that has the glass transition temperature Tg of 50° C. to 152° C.
As described above, the thermal expansion coefficient of the surface of the wiring layer 3 can be set lower than the thermal expansion coefficient of the material of the wiring layer 3 by forming the base plate 1 from a material that is lower in thermal expansion coefficient than the wiring layer 3. Of various electronic parts such as the semiconductor element 5 mounted on the surface of the wiring layer 3, a chip resistor, a chip capacitor, and an Si semiconductor circuit chip, for example, have thermal expansion coefficients of about 7×10−6/K, 10×10−6/K, and 2.6×10−6/K, respectively. Setting the thermal expansion coefficient of the surface of the wiring layer 3 lower than 17.5×10−6/K, which is the thermal expansion coefficient of the material of the wiring layer 3, makes it possible to prevent, without using any stress relieving member, generation of a large thermal stress between the surface of the wiring layer 3 of the circuit board and the electronic parts including the semiconductor element 5 caused by a temperature change. Obtained as a result is a highly reliable semiconductor device which has no fear of warping the semiconductor element 5 or cracking the solder 4 even when used in automobiles and like other environments where the temperature fluctuates widely. In short, the solder reliability in a thermal shock cycle is improved. Another effect of eliminating the need for a heat spreader is a reduction in number of parts, which leads to simplification of the semiconductor device structure, fewer assembling steps, and less cost.
If resin having a specific glass transition temperature Tg is chosen for the insulating resin layer 2, the thermal expansion coefficient of the surface of the wiring layer 3 can be adjusted to suit the thermal expansion coefficient of the semiconductor element 5 and other electronic parts mounted to the surface of the wiring layer 3 without changing the material of the base plate 1. In other words, by setting the thermal expansion coefficient of the surface of the wiring layer 3 closer to the thermal expansion coefficient of the semiconductor element 5 mounted thereon, thermal stress generated between the surface of the wiring layer 3 and the semiconductor element 5 as one of electronic parts mounted on the surface of the wiring layer 3 can be eased more efficiently.
Furthermore, the circuit board can have excellent heat radiation characteristics if the base plate 1 is formed from an Al/SiC composite material that has as high thermal conductivity as pure Al. In addition, since no stress relieving member such as a heat spreader is needed, the overall heat resistance of the semiconductor device that is obtained by mounting the semiconductor element 5 and other electronic parts to the circuit board can be reduced.
Since the thermal expansion coefficient of the surface of the wiring layer 3 starts a rise at a point near the glass transition temperature Tg of the insulating resin layer 2 and continues to rise toward the thermal expansion coefficient of the material of the wiring layer 3 as the temperature of the surrounding is raised, it is preferable to set the glass transition temperature Tg of the insulating resin layer 2 higher than the upper limit of the temperature range in which the circuit board can be used. In automobiles, the temperature range in which a circuit board can be put into use is generally between −40° C. and 125° C. or between −55° C. and 150° C. Therefore, the glass transition temperature Tg of the insulating resin layer 2 is preferably set to 152° C., for example.
βs=0.0686*Dp+2.3578
As shown in
The result of an experiment proves that the thermal expansion coefficient of the surface of the wiring layer 3, namely, the thermal expansion coefficient βs (×10−6/K) of the portion to which the semiconductor element 5 is mounted is expressed as follows when βs<17.5×10−6/K is satisfied:
βs=−0.044·Tg+0.07*Dp+0.878*βb−0.3·Db
wherein Tg (° C.) represents the glass transition temperature of the insulating resin layer 2, Dp (μm) represents the thickness of the insulating resin layer 2, Db (mm) represents the thickness of the base plate 1, and βb (×10−6/K) represents the thermal expansion coefficient of the base plate 1.
The expression shows that the thermal expansion coefficient βs of the surface of the wiring layer 3 is lowered by increasing the glass transition temperature Tg of the insulating resin layer 2 or by reducing the thickness Dp of the insulating resin layer 2.
Although the wiring layer 3 is made of Cu in the embodiment described above, it may be formed of Al or Ni instead.
The material of the base plate 1 is not limited to an Al/SiC composite material having a thermal expansion coefficient of 8.4×10−6/K, and can be any other material as long as the thermal expansion coefficient of the base plate 1 is lower than the thermal expansion coefficient of the wiring layer 3.
As has been described, according to the present invention, a circuit board has a base plate, an insulating resin layer formed on a surface of the base plate, and a wiring layer formed on a surface of the insulating resin layer, and the thermal expansion coefficient of a surface of the wiring layer is set lower than the thermal expansion coefficient of the material of the wiring layer by employing a base plate material that is lower in thermal expansion coefficient than the material of the wiring layer, thus making it possible to ease, without the use of a stress relieving member, thermal stress generated between the surface of the wiring layer and electronic parts mounted on the wiring layer surface.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-206101 | Aug 2003 | JP | national |