Patent Application
20170259385
Field of the Invention
The present invention relates to a component of a turbomachine having wear-protected openings, boreholes or recesses, and also to a process for the production thereof.
Prior Art
In turbomachines and also stationary gas turbines or aviation engines, operating conditions prevail in part in the region of the flow passage during which aggressive media at very high temperatures are moved at high flow velocities so that the components are also exposed inter alia to severe vibrations. Accordingly, components in the region of the flow passage have to meet multifarious requirements under said circumstances and in particular need to have a high wear resistance to fretting. This is especially necessary in the region of openings, boreholes and recesses where a particularly high level of wear can become noticeable on account of the flow conditions.
Accordingly, it is necessary to especially protect such regions or to recondition such regions after a specified operating period.
For the protection of components in turbomachines, such as blade airfoils, it is already known to apply soldering materials, as is described for example in EP 1 685 923 A1, U.S. Pat. No. 8,342,386 B2, EP 1 219 375 A2, U.S. Pat. No. 7,343,676 B2, WO 2011/015192 A1, EP 0 673 292 B1, EP 2 774 710 A1 or JP-2005 305 492 A. However, for producing wear-protected openings or recesses or for repairing such molded components with wear-resistant materials, special requirements exist since the surfaces to be machined, such as the surfaces of turbine blades and the like, are not so easily accessible.
It is therefore the object of the present invention to provide a method for producing and/or repairing wear-protected openings, boreholes, recesses and the like of components of a turbomachine and especially of components of a flow passage boundary, and also to provide corresponding components which meet both the high demands for wear protection itself and for the resistance and adhesion of the applied wear protection and also to meet the requirements with regard to a simple and effective application.
This object is achieved by means of a method having the features of claim 1 and also by means of a component having the features of claim 13. Advantageous embodiments are the subject matter of the dependent claims.
For producing or repairing wear-stressed boreholes or openings on components of a turbomachine, especially of elements of a flow passage boundary, the invention proposes to create an at least two-layer, three-dimensional molded repair part which can be inserted into the borehole or opening and by means of a heat treatment can be bonded to a wall which encompasses the borehole or opening. The invention can correspondingly be used in the case of openings, boreholes or recesses which by an encompassing wall delimit and enclose a space, wherein a normal to the wall has a vector component which is oriented transversely to a central axis of the opening or recess or to an oppositely-disposed wall region.
According to the invention, the at least two-layer molded repair part can have one layer of an Ni-solder, wherein a second layer is formed from a mixture of an Ni-solder and hard material particles, wherein the hard material particles are formed from hard alloys on a base of cobalt and/or nickel, especially CoCrMo alloys, such as T800. The molded repair part can be designed so that an outer shape of the molded repair part at least partially corresponds to the inner shape of the borehole or opening to he repaired, that is to say the surface of the molded repair part corresponds at least partially to the shape of the wall which encompasses the opening or recess so that when the molded repair part is inserted into the recess or opening a flat abutment of the molded repair part against the wall boundary of the opening or recess comes about so that as a result of a corresponding heat treatment a good soldered bond is achieved between the molded repair part and the wall boundary of the opening or recess.
As a result of the at least two-layered design of the molded repair part with an outer Ni-solder layer, which when inserted into the recess or opening comes into contact with the wall which delimits the opening or recess, a good connection of the molded repair part to the wall of the opening or recess can be achieved. The at least second layer consisting of a mixture of Ni-solder and hard material particles (mixture layer), which after insertion of the molded repair part into the opening or recess constitutes the outer boundary of the opening or recess and therefore comes into contact with the media conducted in the flow system and/or with surfaces of adjacent components, a good wear protection can be provided. This is especially necessary since the mixture layer can have a high proportion of hard material particles in the form of hard alloys since as a result of the pure Ni-solder layer, which serves for connecting to the base material of the component to be protected, a particularly good abutment and adhesion and also bond with the component is made possible and therefore the mixture layer does not have to be matched to this requirement.
The molded repair part can be produced so that first of all a two-layer soldering tape or a soldering plate with an Ni-solder layer and a mixture layer of a mixture of Ni-solder and hard material particles is created, and then the corresponding two-layer soldering tape, by deep drawing or pressing into a die, is brought into the corresponding shape of a molded repair part.
The borehole, recess or opening, which is to be protected against wear by the application of the molded repair part, can be prepared by material machining and especially material removal for insertion of the molded repair part, wherein in this way not only the shape of the opening or recess can be matched to the outer shape of the molded repair part but also undesirable oxide layers or other foreign substances can be removed in order to ensure adhesion of the molded repair part to the base material of the component to be protected. The component to be protected can especially be formed by a nickel-based, or cobalt-based alloy, in which nickel or cobalt therefore form the primary alloy constituent. It can especially be superalloys with these primary alloy constituents which reach operating temperatures of over 55%, especially 80% or 90%, of their melting temperature and for example can be of monocrystalline design.
The mixture layer of the molded repair part can be constructed with a mixture of Ni-solder and hard material particles so that the layer has 20 to 60 wt. %, preferably 30 to 50 wt. %, extremely preferably 35 to 45 wt. %, especially 40 wt. % of hard particles.
The layer of Ni-solder preferably does not have hard material particles in order to ensure the best possible connection to the base material of the component to be protected.
The Ni-solder can be an alloy which has chromium, silicon and/or boron and also nickel, as the primary constituent, and unavoidable impurities.
In the case of the hard alloy for the hard material particles, it can he a Co—Mo—Cr—Si-alloy which especially comprises 16.5 to 18.5 wt. % chromium, 27 to 30 wt. % molybdenum, 3 to 3.8 wt. % silicon, up to 3 wt. % nickel and iron, up to 0.1 wt. % sulfur, nitrogen, oxygen and hydrocarbon in each case, and can have cobalt and unavoidable impurities as the remainder.
The heat treatment for bonding the molded repair part to the component to be protected can be carried out so that the whole component with the inserted molded repair part, or only one region of the component in which the molded repair part is inserted, is exposed to the heat treatment. The heat treatment can be carried out under vacuum conditions or under protective gas in order to avoid reactions of the component with the ambient atmosphere occurring during the heat treatment.
A drying process can be connected upstream of the heat treatment in which the applied solder with the hard material particles is air-dried at 50° to 80° Celsius, preferably at 60° to 70° Celsius, in order to expel for example binding agents which the soldering tape or the molded repair part can contain.
The heat treatment for carrying out the soldering process can be conducted within the temperature range of 1150° C. to 1200° C., especially 1170° C. to 1180° C., for 10 to 25 minutes, especially for 15 to 20 minutes.
The heating up process for heating to the solder temperature can already take place under vacuum conditions in common with the heat treatment in the case of the solder temperature, wherein the pressure can lie within the region of ≦10−3 mbar, preferably ≦10−4 mbar.
The heating up process to the solder temperature can be carried out continuously at constant or varying heating up rate, wherein the heating up rate can be selected within the range of 5° C. per minute to 30° C. per minute and especially within the range of 10° C. per minute to 20° C. per minute.
Alternatively or additionally, the component with the inserted molded repair part can also be held (aged) at one or more intermediate temperatures for a specific time during the heating up process in order to give the molded repair part sufficient time for example for the outgassing of binding agents. Therefore, intermediate ageings within the temperature range of 400° C. to 1100° C., for example at 450° C., 600° C. and/or 1050° C. for a time period of 5 to 40 minutes, especially 10 to 30 minutes, can be carried out.
A correspondingly produced component can for example be a turbine intermediate casing which constitutes the connecting passage between the high-pressure turbine and the low-pressure turbine of a turbomachine and is exposed to particularly high stresses.
In the attached drawings, in a purely schematic manner:
Further advantages, characteristics and features of the present invention become clear in the following detailed description of exemplary embodiments. However, the invention is not limited to these exemplary embodiments.
The layer 3 of nickel solder 4 and hard material particles 5 is composed in the depicted exemplary embodiment so that the layer 3 has about 60 wt. % Ni-solder 4 and 40 wt. % hard material particles in the form of a hard alloy on a base of cobalt.
The nickel solder, as used in the pure nickel-solder layer 2 and in the layer 3 with a mixture of nickel solder 4 and hard material particles 5, can be composed of 19 wt. % chromium, 10 wt. % silicon and remainder nickel and unavoidable impurities. In the case of the hard material alloy, it can be a cobalt-based alloy which can have 16.5-18.5 wt. % chromium, 27-30 wt. % molybdenum, 3-3.8 wt. % silicon, up to 3 wt. % nickel and iron, 0.080 wt. % carbon, 0.07 wt. % nitrogen, 0.05 wt. % oxygen, 0.03 wt. % phosphor and 0.03 wt. % sulfur and the remainder unavoidable impurities.
The soldering tape 1, which can be designed not only in tape form but also in plate form or in other suitable forms, can comprise the Ni-solder 4 and also the hard material particles 5 in powder form with a binding agent, such as a plastic, so that the soldering tape 1 or a corresponding soldering plate is deformable. Accordingly, a three-dimensionally formed molded repair part can be formed from the flat soldering tape 1, as is shown in
The corresponding molded repair part 15 can now be inserted into an opening or recess of a component 22, wherein the inner wall 21 of the component 22, which encompasses the opening or recess, is formed complementarily to at least a part of the surface of the conical molded repair part 15, wherein the complementary shape of the opening or recess of the component 22 can be achieved by means of corresponding material machining both of the opening or recess of the component 22 and of the molded repair part. It is particularly advantageous to prepare the opening or recess of the component 22 by material removal for insertion of a correspondingly formed molded repair part 15 since as a result of this not only the shapes are mutually adapted but also undesirable oxide layers or other foreign substances, which could impair connecting of the molded repair part 15 to the base material of the component 22, are removed from the inner wall 21 of the opening or recess of the component 22.
As a result, a wear-resistant coating with a high proportion of hard material particles 5 has been applied in an opening or recess 20 of a component 22 in a simple and reliable manner.
Although the present invention has been described in detail based on the exemplary embodiments, it is obvious to the person skilled in the art that the invention is not limited thereto but that rather modifications are possible in a way that individual features are omitted or other types of combinations of features are realized providing there is no departure from the scope of protection of the attached claims.