Patent Application
20110188037
1. Field of Invention
The present invention refers to a concentrator and locator device of a solute and to a method for concentrating and locating a solute present in a solution.
2. Related Art
Micro-structured surfaces are known having a geometry such as to reproduce the behaviour of lotus leaves, so as to exploit the known “Lotus Effect”.
Lotus leaves display a particular behaviour when they are wet by a liquid; the liquid forms into distinct droplets due to the micrometric corrugation of such surfaces. Such a milimetric corrugation creates high contact angles at the water—leaf surface—air interface. Consequently, the liquid tends to slide off from the surface without dampening it due to a reduced adhesion at the surface itself.
These surfaces are therefore typically used as self-cleaning surfaces since they have a hydrophobic behaviour.
It is often required to identify a solute present inside the solution. This is typically carried out by using, for example, optical devices based on UV (Ultraviolet) absorption, dynamic light scattering, infrared spectroscopes or devices which exploit chemical properties such as liquid or gas phase chromatography.
However, such devices have the drawback that, when the solution is very diluted, it is difficult to locate the solute, and it is thus necessary to perform an analysis on the entire solution, taking a long time before being able to identify the desired substance.
The purpose of the present invention is therefore that of proposing a concentrator and locator device of a solute and a method for concentrating and locating a solute in a small region of space, so as to allow the solute itself to be rapidly identified.
Briefly, the device according to an embodiment of the invention exploits the high contact angle which is formed between the surface of the device and the solute placed on it, and the super-hydrophobicity of such a surface, to detect, exploiting the principle of evaporation, molecules diluted in the solute up to attomolar (10−18 mols/litre) concentrations.
Further characteristics and advantages of embodiments of the invention shall become clear in the following detailed description, carried out purely as non-limiting example, with reference to the attached drawings, in which:
In
The microstructures 4, made for example from silicon or from photopolymers, are obtained through per se known deposition or lithography and attack processes.
The substrate 2 becomes super-hydrophobic thanks to the presence of such periodic micro-structures 4.
In a first variant of the invention, on the top 8 of the microstructures 4 an electroless deposition of noble metals is carried out, like for example silver or gold. An oxidation-reduction reaction of the noble metals is obtained which creates a continuous corrugated film of silver or gold on the top 8 of the microstructures 4.
In a second and third variant of the invention, nano-structures are formed on the top 8 of each lithographic micro-structure 4.
In particular, in the second variant of the invention a combination of high resolution electron beam lithography and electroless deposition of noble metals such as silver or gold is made. A reaction of oxidation-reduction of the noble metals is made which creates on the top 8 of the microstructures 4 a matrix shaped sub-frame making a checkerboard of nano-cylinders having a height comprised in the range 30-100 nm and a periodicity comprised in the range 35-125 nm. Such nano-cylinders have a diameter comprised in the range 30-100 nm and are arranged orthogonally with respect to the surface of the top 8.
In the third variant of the invention, instead of the nano-cylinders a plasmonic lens is made, or rather a linear chain (self-similar) comprising a plurality of nano-spheres, in particular three, having a diameter comprised in the range 10-100 nm.
Thereafter, some mono-layers of a predetermined material, preferably polytetrafluoroethylene (PTFE—also known as Teflon®, a registered trademark of DuPont), having an overall thickness comprised in the range 1-2 nm are deposed on the microstructures 4.
At this point, after having made the device 1, it is possible to use said device 1 to concentrate and locate a quantity of solute dissolved inside a solution.
The first operation 50 is to depose a drop of solution, preferably an inorganic solution or a protein suspension, at room temperature, on a device 1 of the type illustrated above, said drop having a spherical shape with a diameter comprised in the range 100 μm-3 mm. Such a drop positions itself on a group of microstructures 4, for example on an area defined by 50×50 microstructures 4, and remains still, suspended on the microstructures 4, thanks to the high contact angle existing between the drop and the microstructures 4 themselves. Preferably, such a contact angle is comprised in the range 160°-170°. Thanks to the presence of mono-layers of Teflon, the contact angle at the solution—micro-structures—air interface is thus increased with respect to the value which it would have without such monolayers.
In step 55 a predetermined length of time should be waited, for example 20 minutes; in such a length of time the solvent of the drop evaporates and the drop reduces in size maintaining its spherical shape. After the solvent has evaporated the drop reduces in size without however leaving solute residue on the microstructures 4, which it abandons due to its size reduction.
Moreover, the drop remains suspended on the microstructures 4 without penetrating between them, thanks to the high contact angle.
In step 60 the evaporation step is repeated thus progressively reducing the size of the drop, up until, for example, the drop has a diameter equal to 40 μm, maintaining the quantity of solute initially present in the drop unaltered but increasing its concentration by up to ten thousand times.
Such a drop with reduced diameter is deposed on a lower number of lithographic micro-structures 4, for example on four or eight microstructures 4, on an area 10 equal, for example, to 20 μm2.
When the drop reaches a predetermined minimum radius, for example equal to 40 μm, it collapses (step 65), or rather it spreads evenly upon the lithographic microstructures 4 of the area 10.
Thanks to this progressive reduction process of the size of the drop without losing solute, a solute concentration is obtained with respect to the initial drop, in particular a concentration equal to ten thousand times more. Moreover, the solute is located in a predetermined and very small area 10 of the device.
In step 70 the solute is detected, by scanning, for example, the area 10 with a
Raman or fluorescent microscope. The area 10 is illuminated with a microscope which sends a beam of laser light having a predetermined electric field towards said area 10 and the light reflected by the area 10 of the device 1 is analysed through diffraction gratings obtaining a reflection spectrum. By performing a spectroscopic analysis of the reflection spectrum the solute present in the drop is detected.
The corrugated film of gold or silver or the nano-structures made on the top 8 of the lithographic microstructures 4 in the area 10 amplify the local electric field, which then becomes greater than the electric field of the incident light, forming surface plasmons. In this way a very high detection sensitivity is reached, in particular even a single molecule of solute can be detected.
Alternatively, such a solute is a polluting chemical agent, for example a dioxin, and the device 1 according to an embodiment the invention is made on a packaging film. It is therefore possible to exploit the device 1 to detect, performing the aforementioned concentration and locating procedure operations, the presence of polluting substances on the packaging of food products, clothing items, etc.
Clearly, the principle of the invention remaining the same, the embodiments and the constructive details can be widely varied with respect to what has been described and illustrated purely as an example and not for limiting purposes, without for this reason departing from the scope of protection of the present invention defined by the attached claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| TO2008A000646 | Aug 2008 | IT | national |
This application is a U.S. National Stage Application of PCT/IB009/053763, filed Aug. 28, 2009, which designates the United States and claims the priority of Italian Patent Application No. TO2008A000646, filed on Aug. 29, 2008.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB09/53763 | 8/28/2009 | WO | 00 | 2/28/2011 |