This application is the U.S. National Stage filing under 35 U.S.C. 371 of International Application No. PCT/KR2020/011058, filed on Aug. 19, 2020, which claims priority to Korean Patent Application No. 10-2019-0100850, filed on Aug. 19, 2019 in Korean Intellectual Property Office, all of which are hereby incorporated by reference in their entirety.
The present invention relates to a cooling member, and more particularly, to a cooling member for a battery module and a battery module comprising the same.
The heat dissipation characteristic of a battery module is very important enough to influence the performance of the battery. Heat entry and exit are accompanied during charging and discharging of the battery, and the amount of heat generated at this time is proportional to the capacity of the unit cell, that is, the number of stacked unit cells. However, the heat generated during charging and discharging is released during the rest period, and the thicker the battery, the less the heat generated during discharging tends to be dissipated sufficiently during the resting period. As such, when the generated heat is accumulated in the battery, the temperature inside the battery rises, and as a result, the battery performance is deteriorated, and in severe cases, there is a risk of explosion. In particular, when the battery module is applied to a large-capacity secondary battery for driving a motor for an electric vacuum cleaner, electric scooter, or automobile, particularly as a main energy source for an electric vehicle, since it is charged and discharged with a large current, the temperature of the battery rises to a significant temperature by the heat generated inside the battery.
Meanwhile, electrical separation and flame-retardant characteristics are very important between each unit cell provided in the battery module. If electrical insulation and flame retardancy are not provided between unit cells, there is a risk of a large explosion or fire. In addition, if the flame is unintentionally transferred in a chain to components connected to each of the unit cells but not electrically connected to the unit cells, the fire may spread throughout the device or the device including the battery module, so electrical separation and flame retardancy are also very important between the components in the battery module and the unit cells. Therefore, in the case of components that are not intended to be electrically connected to the unit cells in the battery module, insulation of a certain level or higher is required to prevent electricity from being transmitted to other places even if the unit cells are leaking.
There may be a heat dissipation member for quickly dissipating heat generated from the unit cell to the outside among components that are not intended to be electrically connected to the unit cell in the battery module. As the number or capacity of the unit cells provided in the battery module increases, the amount of heat generated also increases, so the heat dissipation performance of the heat dissipation member is very important. For this reason, a conductive material such as aluminum, which is a material having high thermal conductivity through contact, may be considered as a heat dissipation member. However, while the heat dissipation member made of the conductive material has excellent thermal conductivity, there is a problem in that it is not electrically separated when in contact with the unit cell, that is, it does not have insulation.
Accordingly, in recent years, research has been actively conducted to construct a battery module by interposing an insulating member between a heat-dissipating member made of an unavoidably used conductive material and an insulating battery, but since the insulating member has no heat dissipation performance, there is a problem in that heat generated from the unit cell cannot be transferred to the heat dissipation member. In addition, even when an insulating member and a heat dissipation member are provided together to achieve insulation and heat dissipation at the same time, there is a problem in that heat transfer is not very easy due to the insulating effect due to the air layer existing at the interface between the insulating member and the unit cell, and the insulating member and the heat dissipating member.
Accordingly, there is an urgent need to research a cooling member that can rapidly transfer a large amount of heat generated from a plurality of unit cells to the outside and electrically separate the unit cells even when in contact with the unit cells due to excellent insulation.
The above information disclosed in this Background section is only for enhancement of understanding of the background of the invention and it may therefore contain information that does not form the prior art that is already known to a person of ordinary skill in the art.
The present invention has been devised in view of the above points, and is directed to providing a cooling member for a battery module capable of effectively transferring heat generated from a battery, which is a heat source, to the outside to cool the battery with better efficiency, and stably separating the battery electrically by the expression of excellent insulation properties; and a battery module including the same.
In addition, the present invention is directed to providing a cooling member for a battery module implemented such that a process of manufacturing the battery module by assembling the unit cell with the cooling member is very easy, and reworking thereof is also possible.
An exemplary embodiment of the present invention provides a cooling member for a battery module having a cooling plate in contact with a plurality of battery cells to transfer heat emitted from the battery cells to the outside, the cooling member for a battery module including a predetermined pattern formed to accommodate at least a portion of the outer surface of the battery cell on the main surface along the longitudinal direction, and an insulating heat dissipation layer covering part or all of an outer surface of the cooling plate so as to be interposed between the battery cell to be accommodated on the predetermined pattern and the cooling plate.
According to an embodiment of the present invention, the pattern may be formed by a cooling plate having a corrugated cross-section or an insulating heat dissipation layer having a corrugated cross-section.
In addition, the battery cell may have a cylindrical shape.
In addition, the cooling plate may have at least one moving passage through which a refrigerant flows therein.
In addition, the insulating heat dissipation layer may have a withstand voltage of 5 kV/mm or more.
In addition, the insulating heat dissipation layer may be a coating layer or a pad layer in which an insulating heat dissipation filler is dispersed in a silicon-based matrix.
In addition, the insulating heat dissipation layers may have a thickness of 300 to 5000 μm, more preferably 300 to 1000 μm, and still more preferably 300 to 500 μm. In addition, at this time, the insulating heat dissipation layer may have a Shore OO hardness of 35 to 50.
In addition, the insulating heat dissipation layer is a coating layer and may further include a silicone-based primer layer between the coating layer and the cooling plate, or the insulating heat dissipation layer is a pad layer and may further include a fixing member including an adhesive layer between the pad layer and the cooling plate to fix the pad layer to the cooling plate.
In addition, the cooling member may further include an insulating member provided in close contact with the insulating heat dissipation layer.
In addition, the present invention provides a battery module including the cooling member according to the present invention.
In addition, the present invention provides an electric vehicle including the cooling member according to the present invention.
The cooling member for a battery module according to the present invention effectively can transfer heat generated from the battery, which is a heat source, to the outside to cool a unit battery with better efficiency, and stably separate the battery electrically by the expression of excellent insulation properties, thereby minimizing explosion or fire.
In addition, a process of assembling the unit battery and the cooling member is very easy, and reworking thereof is also possible, such that the efficiency of the assembly process of the battery module can be significantly improved. Due to this, the cooling member for a battery module according to the present invention has great utility in large-capacity electrical components, and can be applied to various industries such as electric vehicles.
The above and other aspects, features, and advantages of the present invention will become more apparent to those of ordinary skill in the art by describing embodiments thereof in detail with reference to the accompanying drawings, in which:
Hereinafter, exemplary embodiments of the present invention will be described in detail so that those of ordinary skill in the art can readily implement the present invention with reference to the accompanying drawings. The present invention may be embodied in many different forms and is not limited to the embodiments set forth herein. In the drawings, parts unrelated to the description are omitted for clarity. Throughout the specification, like reference numerals denote like elements.
Referring to
The cooling member 100 includes a cooling plate 10 and an insulating heat dissipation layer 20 covering a part or all of the outer surface of the cooling plate 10.
The cooling plate 10 serves to transfer heat emitted from the battery cell 200 to other cooling components in the battery module 1000 or to a cooling device or cooling component other than the battery module. The shape of the cooling plate 10 is not limited in the case of an advantageous shape for contacting all of the plurality of battery cells 200 while maximizing the number of battery cells 200 provided in the allowed space of the battery module 1000. As an example, the cooling plate 10 may be a plate-shaped member having main surfaces 100A and 1008, and more specifically, may have a shape in which the cooling plate, which is a plate-shaped member having main surfaces 100A and 1008 as shown in
The length, width and thickness of the cooling plate 10 may be appropriately selected in consideration of the volume of the battery module, the number of allowed battery cells, the size of the battery, the presence or absence of a refrigerant moving channel therein, and the size of the moving channel, and thus the present invention is not particularly limited thereto.
In addition, the cooling plate 10 may be preferably made of a material having high thermal conductivity, and may be, for example, a metal or alloy known to have thermal conductivity, such as aluminum or copper. Alternatively, the cooling plate 10 may be a heat dissipation plastic having a thermal conductive heat dissipation filler in a polymer matrix. In this case, the polymer matrix may be a known thermoplastic resin. In addition, the thermal conductive heat dissipation filler may be a carbon-based heat dissipation filler including one or more selected from the group consisting of carbon nanotube such as single-walled carbon nanotube, double-walled carbon nanotube, and multi-walled carbon nanotube, graphene, graphene oxide, graphite, carbon black, and carbon-metal composite; a metal-based heat dissipation filler including such as aluminum, copper, and iron; and/or a ceramic-based heat dissipation filler including such as alumina, silicon, and boron nitride. Alternatively, the heat dissipation plastic may be formed of an electroconductive polymer compound.
In addition, the cooling plate 10 may have at least one moving passage 1 through which a refrigerant flows therein in order to more effectively dissipate heat generated in the battery cell 200. The refrigerant may be a known refrigerant, for example water or glycol. In addition, since the number and size of the moving passages 1 may be appropriately changed in consideration of the size of the cooling plate 10 and the desired heat conduction efficiency, the present invention is not particularly limited thereto. As an example, the width and thickness of the cooling plate 10 are determined according to the size of the cell, and there should be no problem in assembling the cell module. Two or more moving passages 1 provided therein may be designed to minimize the resistance of the flow of cooling water while maintaining vertical intervals.
Next, as shown in
In addition, due to the insulating heat dissipation layers 20 and 20′, an air layer may not be substantially included in the interface between the battery cell 200 and the cooling plate 10, and thus more improved heat transfer characteristics may be expressed. In addition, it is advantageous to effectively transfer heat from the battery cell 200 to the cooling plate 10 by increasing the close-contact characteristics and close-contact area between the battery cell 200 and the cooling plate 10. To this end, as shown in
The above-described insulating heat dissipation layers 20 and 20′ may have a form in which a heat dissipation filler 22 is dispersed in a polymer matrix 21.
The polymer matrix 21 may be a conventional polymer compound itself capable of forming a sheet having a predetermined thickness, or may be formed by crosslinking a polymer compound.
However, as shown in
In addition, if the polymer matrix 21 of the insulating heat dissipation layers 20 and 20′ is a material capable of expressing the above-described physical properties, there is no limitation. However, in the case of epoxy widely used as a general matrix, it is difficult to satisfy the above-described physical properties due to its high hardness, and it can be easily broken according to the vertical and horizontal movement of the battery cell 200, so it is not preferable as a polymer matrix material of the insulating heat dissipation layers 20 and 20′ according to the present invention. Preferably, the polymer matrix 21 may be made of a silicone-based material, an acrylic-based material, or the like, and more preferably a silicone-based material. Specifically, the polymer matrix 21 may be cross-linked by addition polymerization of polydimethylsiloxane containing a vinyl group at the terminal, which may be advantageous in achieving all of the above-described physical properties and realizing a coating layer having a uniform thickness.
In addition, for the heat dissipation filler 22, it is important for the expression of insulation properties to use a heat dissipation filler having a high resistance and/or dielectric constant among general heat dissipation fillers provided in the heat dissipation coating layer. As an example for this, for the heat dissipation filler 22, alumina, yttria, zirconia, aluminum nitride, boron nitride, silicon nitride, silicon carbide, single crystal silicon, etc. may be used.
In addition, the heat dissipation filler 22 may have an average particle diameter of 0.5 to 200 μm. However, according to an embodiment of the present invention, the heat dissipation filler may have an average particle diameter of 50 μm or less, and in another example, 20 to 40 μm. Here, the particle diameter of the heat dissipation filler is the diameter when the shape is spherical, and when the shape is polyhedral or irregular, it means the longest distance among the linear distances between two different points on the surface.
In addition, in order to increase the content in the insulating heat dissipation layers 20 and 20′ while minimizing the deterioration of the flexibility and compressive properties of the insulating heat dissipation layers 20 and 20′ due to the heat dissipation filler, the heat dissipation filler 22 may be designed as several particle diameter groups having different particle diameters. In addition, the heat dissipation filler may include a first heat dissipation filler having a particle diameter of 1 to 5 μm, a second heat dissipation filler having a particle diameter of 10 to 20 μm, and a third heat dissipation filler having a particle diameter of 25 to 40 μm, in a weight ratio of 1:1.5 to 3:3.5 to 5, and through this, the content in the insulating heat dissipation layer may be increased to 80% by weight or more, and it may be advantageous to achieve the desired effect.
In addition, the heat dissipation filler 22 may be contained 50 to 95% by weight, preferably 60 to 85% by weight, in the insulating heat dissipation layers 20 and 20′, thereby improving the heat dissipation characteristics while minimizing the deterioration of the insulation properties.
In addition, the insulating heat dissipation layers 20 and 20′ may have a thickness of 300 to 5000 μm, more preferably 300 to 1000 μm, and still more preferably 300 to 500 μm. If the thickness is less than 300 μm, after the battery cell 200 is accommodated in the pattern formed on the cooling members 100 and 100′, it may be difficult to express compressive properties for close contact with a large contact area, and there is concern about deterioration of insulation properties. In particular, a difference in the thickness of the insulating heat dissipation layer may be induced in the mountain portion and the valley portion of the pattern formed on the cooling plate 10, and since the thickness of the insulating heat dissipation layer formed in the mountain portion becomes thin, there may be a problem in insulating properties. In addition, if the thickness exceeds 5000 μm, thermal resistance increases, so it may be difficult to smoothly dissipate heat. In addition, it may be difficult to implement the corresponding thickness through coating on the pattern formed on the cooling plate 10, and it may not be easy to attach the pad layer to the pattern even after being implemented as a pad layer. In addition, it may be difficult to adhere without lifting in accordance with the shape of the pattern due to reduced flexibility. Preferably, it may be 1000 μm or less, and when it exceeds this, it may be very difficult to implement an insulating heat dissipation layer through coating. Accordingly, it can more preferably have a thickness of 300 to 500 μm in order that a predetermined thickness can be realized through the coating and the process is easy even when attaching, and in order to adhere to patterns of various shapes and to be fixed on the cooling plate.
More preferably, the insulating heat dissipation layer may have a thickness of 300 to 1000 μm and a shore hardness of 35 to 50, which may be advantageous in realizing an increased heat dissipation characteristic while ensuring an insulation property.
Describing the above-described insulating heat dissipation layer-forming composition for forming the insulating heat dissipation layers 20 and 20′, as an example, it may include polydimethylsiloxane containing a vinyl group, which is a silicone-based resin, at the terminal as a binder resin, alumina and a solvent as a heat dissipation filler, and may further contain a catalyst or curing agent necessary for curing. In addition, the viscosity may be 50,000 to 200,000 cPs, through which it is easy to form a coating layer having a thickness of 300 μm or more, and if the viscosity does not satisfy this, it may be difficult to form a coating layer having a thickness of 300 μm or more. In addition, it may be difficult to implement an insulating heat dissipation layer having a uniform thickness if the viscosity is low or high outside this.
Such an insulating heat dissipation layer-forming composition may form a coating layer preferably through impregnation during coating, but in the case of another method, it may be difficult to form an insulating heat dissipation layer having a thickness of 300 μm or more and having a uniform thickness regardless of a location on the cooling plate 10 having a bent pattern. The insulating heat dissipation layer-forming composition treated on the cooling plate 10 may be cured by, for example, heat, and curing conditions may be 10 to 30 minutes at 130 to 160° C. However, curing conditions can be appropriately changed in consideration of the type of binder resin used, and the like.
Meanwhile, as shown in
As shown in
Meanwhile, the fixing member 34 may have adhesive layers 31 and 33 on both sides of a support layer 32, and the support layer 32 guarantees the mechanical strength of the fixing member consisting only of an adhesive layer or a bonding layer and may be, for example, a PET film. The support layer 32 may have a thickness of 10 to 50 μm, for example, 25 μm. In addition, in the case of the adhesive layers 31 and 33 on both sides, the adhesive layer 31 in contact with the insulating heat dissipation layer 20′, which is a silicone pad layer, may be a silicone-based adhesive layer, and the adhesive layer 33 in contact with the cooling plate 10 may be an acrylic-based adhesive layer, and which may be advantageous in expressing more improved fixing properties to the cooling plate 10 on which the pattern is formed. In addition, pressure may be applied to the insulating heat dissipation layer 20′, which is a silicon pad layer, due to its close contact with the battery cell, and the silicone-based adhesive has an advantage in that the interface with the insulating heat dissipation layer 20′ may not lift even under the pressure applied to the insulating heat dissipation layer 20′ and maintain an attached state due to its excellent flexibility, compressive property, and elastic property. If an adhesive layer without flexibility and compressive property is used, even though the adhesive strength is excellent, when pressure is applied to the insulating heat dissipation layer 20′, there is a risk that the interface between the insulating heat dissipation layer 20′ and the adhesive layer may be lifted or damage such as cracks may occur in the adhesive layer.
When the insulating heat dissipation layer 20′ is an insulating tape, the thickness may be, for example, 50 μm to 2.5 mm, or 50 to 1000 μm, but it is not limited thereto.
Meanwhile, the cooling members 100 and 100′ described above may further include an insulating member to further improve insulating properties. Referring to
In addition, the above-described cooling members 100,100′,100″ may be in the form of a plate having a predetermined length along the longitudinal direction, or as shown in
The cooling members 100, 100′, 100″ having the above-described cooling plate 10 and the insulating heat dissipation layers 20 and 20′ have a predetermined pattern formed on the main surfaces 100A and 100B of the cooling members 100, 100′, 100″ along the longitudinal direction so that at least a portion of the outer surface of the battery cell 200 is accommodated and surface-contacted. The pattern may have a shape matching at least a portion of the outer surface of the battery cell 200, which has an advantage that it can be easily brought into close contact without an air layer between the battery cell 200 and the main surfaces 100A and 1006 of the cooling members 100, 100′, 100″.
Assuming the battery cell 200 is a cylindrical shape, the pattern may be derived from a cooling plate 10 of wavy cross-section as shown in
Meanwhile, the insulating heat dissipation layers 26 and 26′ shown in
In addition, the cooling plate 11 may also include at least one moving channel 2 through which a refrigerant may flow therein.
In addition, the insulating heat dissipation layers 26 and 26′ may be molded to have a corrugated cross-section, and may be, for example, a molding layer having a heat dissipation filler 28 in a polymer matrix 27. The molding layer is the same as the description of the insulating heat dissipation layer 20, which is the above-described coating layer, and thus a description thereof will be omitted.
The present invention may implement battery modules 1000, 2000 and 2000′ by surface-contacting a plurality of battery cells 200 and 210 on the cooling members 100,100′,100″,110 and 120 and on a predetermined pattern formed on the main surface of the cooling members 100,100′,100″,110 and 120. A known secondary battery may be used without limitation as the battery cells 200 and 210, and may be, for example, a lithium ion battery. The battery cells 200 and 210 may have an appropriate size in consideration of the desired electric capacity of the battery module. In addition, the shape of the battery cells 200 and 210 may be cylindrical, but is not limited thereto, and a known battery shape may be employed without limitation. In addition, the number of battery cells 200 and 210 provided in the battery modules 1000, 2000 and 2000′ may be appropriately changed in consideration of the electric capacity and volume of the battery modules 1000 and 2000, so the present invention is not limited thereto.
The present invention will be described in more detail through the following examples, but the following examples are not intended to limit the scope of the present invention, which should be construed to aid understanding of the present invention.
A corrugated pattern as shown in
The withstand voltage (breakdown voltage) of the insulating heat dissipation layer of the implemented cooling member was 6.5 kV/mm, the thermal conductivity was 1.5 W/mK, and the Shore OO hardness was 45. In this case, the Shore OO hardness was measured by implementing the same insulating heat dissipation layer-forming composition in the same way so that the final thickness was 400 μm on the release film, and then measuring the Shore OO hardness of the manufactured pad-type insulating heat dissipation layer.
It was prepared in the same manner as in Example 1, but without treating the insulating heat dissipation layer-forming composition on the cooling plate, a cooling member as shown in
A PTC element (0.4 A, 3.4 W), which is a heat source, was attached to the same position on one surface of the cooling member according to Example 1 and Comparative Example 1, and then a current was applied to generate heat, and after 1 hour, the temperature of one side (TC1) where the heat source is installed and the other side (TC2) were measured and shown in Table 1 below.
As can be seen from Table 1, the cooling member according to Example 1 provided with an insulating heat dissipation layer has a significantly lower temperature than Comparative Example 1 on the heat source side and the opposite side, and it can be seen that the cooling member according to Example 1 has very good heat dissipation characteristics through the small temperature difference between both sides of the cooling plate.
A flat cooling plate made of aluminum and having a width of 15 cm was prepared. A pattern in which mountains and valleys are alternately formed in the longitudinal direction as shown in
It was manufactured in the same manner as in Example 2, except that the thickness, hardness, and material of the insulating heat dissipation layer were changed as shown in Table 2 below to form a cooling member as shown in Table 2 below. In this case, Examples 5 to 6 increased the degree of curing in order to control the shore hardness, and specifically, the curing time was changed to 25 minutes and 45 minutes, respectively, to implement an insulating heat dissipation layer having a shore hardness of 50 and 60.
In this case, Example 7 uses the same type of heat dissipation filler in the same content as in Example 1, but an insulating heat dissipation layer-forming composition was prepared by mixing 3 parts by weight of a curing agent DICY and 200 parts by weight of methyl ethyl ketone as a solvent to 100 parts by weight of a bisphenol A epoxy component (Kukdo, YG-011) as a matrix forming component, and then was cured at 150° C. for 30 minutes.
In order to simply evaluate the heat dissipation characteristics of the heat generated by the cylindrical battery, a cylindrical aluminum conduit with a diameter of 10 cm and a length of 15 cm corresponding to the cylindrical battery was prepared. In order to heat the aluminum conduit, three PTC elements (0.4 A, 3.4 W), which are heat sources, were attached to the inner wall of the conduit at a distance from each other. After accommodating the prepared cylindrical aluminum conduit in any one of the valleys of one surface of the cooling member according to Examples 2 to 7, a current was applied to the PTC element to generate heat, and then after measuring the temperature of one surface of the cooling member on the side where the aluminum conduit was accommodated and the opposite surface, the temperature difference was calculated, and then the heat dissipation characteristics compared to Example 2 were examined by showing the temperature difference calculated in the other examples as relative percentages in Table 2 based on the temperature difference of Example 2 as 100%. If the heat dissipation characteristic is greater than 100%, it means that the temperature difference between one surface of the heat source side and the opposite surface is larger, and consequently, the heat dissipation characteristic in the thickness direction is worse than that of Example 2.
As can be seen in Table 2, when the thickness of the insulating heat dissipation layer decreases, the heat dissipation characteristics should be improved due to a decrease in thermal resistance, but in the case of Example 4 having a thickness of less than 300 μm even when the Shore OO hardness was the same as 45, the heat dissipation characteristics were significantly lowered compared to that of Example 3.
These results are expected as a result of a decrease in the amount of compressive deformation of the insulating heat dissipation layer due to the decrease in thickness, and thus the close-contact force or close-contact area between the outer surface of the cylindrical aluminum conduit and the insulating heat dissipation layer is reduced.
In addition, even when the thickness was the same as 400 μm, the heat dissipation characteristics were lowered when the shore hardness was increased to 50 and 60, respectively, and in particular, it can be seen that the heat dissipation characteristic of Example 6 was significantly lowered compared to Example 5.
On the other hand, in the case of Example 7 in which the material was changed to epoxy, the heat dissipation characteristic was significantly lower than that of Example 2.
Although exemplary embodiments of the present invention have been described above, the spirit of the present invention is not limited to the embodiments set forth herein. Those of ordinary skill in the art who understand the spirit of the present invention may easily propose other embodiments through supplement, change, removal, addition, etc. of elements within the same spirit, but the embodiments will be also within the scope of the present invention.
Number | Date | Country | Kind |
---|---|---|---|
10-2019-0100850 | Aug 2019 | KR | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/KR2020/011058 | 8/19/2020 | WO |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2021/034108 | 2/25/2021 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
20100104938 | Hermann | Apr 2010 | A1 |
20120050994 | Boday | Mar 2012 | A1 |
Number | Date | Country |
---|---|---|
109153868 | Jan 2019 | CN |
109563361 | Apr 2019 | CN |
109638374 | Apr 2019 | CN |
102015118605 | Jul 2017 | DE |
2019-075256 | May 2019 | JP |
10-2006-0034130 | Apr 2006 | KR |
1020060060808 | Jun 2006 | KR |
10-2007-0014658 | Feb 2007 | KR |
10-2013-0033597 | Apr 2013 | KR |
1020160105356 | Sep 2016 | KR |
10-2017-0142624 | Dec 2017 | KR |
101818922 | Jan 2018 | KR |
10-2018-0110382 | Oct 2018 | KR |
2016-067517 | May 2016 | WO |
Entry |
---|
Office Action for CN 202080059047.9 by China National Intellectual Property Administration dated Jul. 29, 2023. |
International Search Report dated on Dec. 1, 2020. |
Number | Date | Country | |
---|---|---|---|
20220302522 A1 | Sep 2022 | US |