Claims
- 1. A radiation sensitive emulsion comprised of a dispersing medium and silver iodochloride grains
- WHEREIN the silver iodochloride grains
- are comprised of three pairs of equidistantly spaced parallel {100} crystal faces and
- contain from 0.05 to 3 mole percent iodide, based on total silver, in a controlled, non-uniform iodide distribution forming
- a core containing at least 50 percent of total silver,
- surface shell, and
- a sub-surface shell that contains a maximum iodide concentration and provides, when the emulsion is exposed to 390 nm electromagnetic radiation at 10.degree. K., stimulated fluorescent emissions in the range of from 450 to 470 nm and at 500 nm, the stimulated fluorescent emission in the range of from 450 to 470 nm having a peak intensity more than twice the stimulated fluorescent emission intensity at 500 nm.
- 2. A radiation sensitive emulsion according to claim 1 wherein the grain size coefficient of variation of the silver iodochloride grains is less than 35 percent.
- 3. A radiation sensitive emulsion according to claim 2 wherein the grain size coefficient of variation of the silver iodochloride grains is less than 25 percent.
- 4. A radiation sensitive emulsion according to claim 1 wherein the silver iodochloride grains contain from 0.1 to 1.0 mole percent iodide, based on total silver.
- 5. A radiation sensitive emulsion according to claim 1 wherein the core contains at least 85 percent of total silver.
- 6. A radiation sensitive emulsion according to claim 1 wherein iodide forming the grains is excluded from the core of the grains.
- 7. A radiation sensitive emulsion according to claim 1 wherein the core accounts for at least 85 percent of total silver forming the grains.
- 8. A radiation sensitive emulsion according to claim 1 wherein the surface shell has a thickness of greater than 25 .ANG..
- 9. A radiation sensitive emulsion according to claim 1 wherein the surface shell is free of iodide as precipitated.
- 10. A radiation sensitive emulsion according to claim 1 wherein the silver iodochloride grains include tetradecahedral grains having {111} and {100} crystal faces.
- 11. A radiation sensitive emulsion according to claim 1 wherein the silver iodochloride grains contain a sensitivity enhancing dopant.
- 12. A radiation sensitive emulsion according to claim 1 wherein the silver iodochloride grains contain a contrast increasing dopant.
- 13. A radiation sensitive emulsion according to claim 1 wherein the silver iodochloride grains contain a reciprocity improving iridium dopant.
- 14. A radiation sensitive emulsion according to claim 1 wherein the emulsion contains a 5-mercaptotetrazole antifoggant.
- 15. A process of preparing a radiation sensitive silver iodochloride emulsion according to claim 1 comprising precipitating in a dispersing medium silver iodochloride grains wherein
- (a) grains accounting for at least 50 percent of total silver forming the silver iodochloride grains are grown in the dispersing medium,
- (b) while employing the grains as substrates for further grain growth, locating crystal lattice variances in the grains by the incorporation of iodide to form a first shell having a higher local iodide concentration than any other grain portion, and
- (c) precipitating silver chloride onto the surface of the grains formed in step (b) to create a surface shell separating the first shell from the surface of the completed grains.
- 16. A process according to claim 15 wherein iodide is introduced into the grains in a concentration up to 1.0 mole percent, based on total silver forming silver iodochloride grains.
- 17. A process according to claim 16 wherein iodide is introduced in step (b) in a concentration ranging from 0.1 to 0.6 mole percent, based on total silver forming silver iodochloride grains.
- 18. A process according to claim 15 wherein step (a) is completed prior to iodide introduction.
- 19. A process according to claim 15 wherein the grains provided in step (a) account for at least 85 percent of the total silver forming the silver iodochloride grains.
- 20. A process according to claim 15 wherein iodide introduction is completed prior to step (c).
- 21. A process according to claim 15 wherein iodide addition in step (b) is completed in less than 30 seconds.
- 22. A process according to claim 21 wherein iodide addition in step (b) is completed in less than 10 seconds.
- 23. A photographic print element according to claim 1 wherein the silver iodochloride grains include grains having at least one {111} crystal face.
Parent Case Info
This is a continuation-in-part of Applicants' patent application, U.S. Ser. No. 08/362,283, filed Dec. 22, 1994, now abandoned.
US Referenced Citations (14)
Foreign Referenced Citations (1)
Number |
Date |
Country |
0 295 439 |
Dec 1988 |
EPX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
362283 |
Dec 1994 |
|