The present invention relates to a curable silicone composition for die bonding use.
Curable silicone compositions are used to adhere optical semiconductor elements such as LEDs to supports comprising sapphire, for example. As examples of such curable silicone compositions, Patent Literature 1 and Patent Literature 2 propose curable silicone compositions comprising essentially linear or cyclic alkenyl group-containing organopolysiloxane, branched alkenyl group-containing organopolysiloxane, linear organopolysiloxane having hydrogen atoms bonded to silicon atoms in the molecular chain, branched organopolysiloxane having silicon atom-bonded hydrogen atoms, and a hydrosilylation reaction catalyst, and Patent Literature 3 proposes a curable silicone composition comprising linear organopolysiloxane having at least 2 alkenyl groups per molecule, branched organopolysiloxane having at least 2 alkenyl groups per molecule, branched organopolysiloxane having at least 2 silicon atom-bonded hydrogen atoms per molecule, and a hydrosilylation reaction catalyst.
However, in the die bonding of optical semiconductor elements such as LEDs, the adhesive layer is extremely thin, and it is known that even the curable silicone compositions described above are disadvantageous in that they do not afford adequate adhesive strength (die shear strength).
PATENT LITERATURE 1: Japanese Unexamined Patent Publication No. 2012-012433
PATENT LITERATURE 2: Japanese Unexamined Patent Publication No. 2012-012434
PATENT LITERATURE 3: Japanese Unexamined Patent Publication No. 2016-155967
Problems that the Invention is to Solve
The aim of the present invention is to provide a curable silicone composition for die bonding use, that can firmly adhere a semiconductor chip to a support.
The inventive curable silicone composition for die bonding use comprises at least
Component (A) preferably contains an organopolysiloxane resin comprising at least a siloxane unit represented by the formula R13 SiO1/2 (in the formula, R1 is an identical or different monovalent C1-12 hydrocarbon group having no aliphatic unsaturated bonds), a siloxane unit represented by the formula R12 R2SiO1/2 (in the formula, R1 is as described above, and R2 is a C2-12 alkenyl group), and a siloxane unit represented by the formula SiO4/2, wherein the molar ratio of the total amount of siloxane units represented by formula R13 SiO1/2 and siloxane units represented by formula R12R2SiO1/2, with respect to the siloxane unit represented by formula SiO4/2, is 0.5-1.6.
Component (B) is preferably an organopolysiloxane resin comprising at least a siloxane unit represented by the formula R43 SiO1/2 (in the formula, R4 is an identical or different monovalent C1-12 hydrocarbon group having no aliphatic unsaturated bonds), a siloxane unit represented by the formula R4 HSiO2/2 (in the formula, R4 is as described above), and a siloxane unit represented by the formula SiO4/2, wherein the molar ratio of the siloxane unit represented by formula R43SiO4/2 is 0.6-1.5 and the molar ratio of the siloxane unit represented by formula R4HSiO2/2 is 1.5-3 with respect to the siloxane unit represented by formula SiO4/2; or an organopolysiloxane comprising at least a siloxane unit represented by the formula R43SiO1/2 (in the formula, R4 is an identical or different monovalent C1-12 hydrocarbon group having no aliphatic unsaturated bonds) and a siloxane unit represented by the formula R4HSiO2/2 (in the formula, R4 is as described above), and having no siloxane unit represented by the formula SiO4/2.
Component (D) is preferably an alkyne alcohol and/or silylated alkyne alcohol.
Component (E) is preferably a reaction mixture comprising epoxy group-containing alkoxysilane and alkenyl group-containing diorganosiloxane oligomer having both molecular chain terminals silanol group-blocked.
The inventive composition preferably also contains (F) fumed silica having a BET specific surface area of 20-200 m 2/ g , at 1-20 parts by mass per 100 parts by mass of the total amount of components (A) and (B).
The inventive composition is preferably such that when cured it forms a cured product having a type D durometer hardness, as defined in JIS K 6253-1997, of at least 50.
Also, the inventive composition is preferably such that when cured it forms a cured product having a flexural strain, as defined in JIS K 7171-1994, of at least 10%.
The inventive composition is preferably a curable silicone composition for die bonding use, for adhering LED elements to substrates.
A feature of the inventive curable silicone composition for die bonding use is that it can firmly adhere a semiconductor chip to a support.
Component (A) is an organopolysiloxane having at least 2 alkenyl groups per molecule. Examples of the alkenyl groups are C2-12 alkenyl groups such as vinyl, allyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, undecenyl, and dodecenyl groups; they are preferably vinyl groups. Examples of the silicon atom-bonded groups (other than alkenyl groups) also present in component (A) are C1-12 alkyl groups such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, cert-butyl, pentyl, neopentyl, hexyl, cyclohexyl, heptyl, octyl, nonyl, decyl, undecyl and dodecyl groups; C6-12 aryl groups such as phenyl, tolyl, xylyl and naphthyl groups; benzyl group and C7-12 aralkyl groups such as phenethyl, and phenylpropyl groups; and groups obtained by substituting some or all of the hydrogen atoms in these groups with halogen atoms such as fluorine, chlorine or bromine atoms. It should be noted that a small amount of hydroxyl group or alkoxy group such as methoxy or ethoxy group may be bonded to the silicon atom in component (A), provided that this does not adversely affect the aim of the present invention.
There are no limitations relating to the molecular structure of component (A); for example, it can be linear, linear with some branching, cyclic, branched, or a three-dimensional network structure. Component (A) is a single organopolysiloxane having such a molecular structure, or a mixture of two or more organopolysiloxanes having these molecular structures; it preferably contains at least organopolysiloxane resin having a branched or three-dimensional network structure, because this can afford adequate adhesive strength (chip die shear strength), and it is particularly preferably a mixture of organopolysiloxane that is linear or linear with some branching, and organopolysiloxane resin having a branched or three-dimensional network structure.
Examples of linear organopolysiloxanes include dimethylpolysiloxane having both molecular chain terminals dimethylvinylsiloxy group-blocked; dimethylsiloxane-methylphenylsiloxane copolymer having both molecular chain terminals dimethylvinylsiloxy group-blocked; dimethylsiloxane-methylvinylsiloxane copolymer having both molecular chain terminals dimethylvinylsiloxy group-blocked; methylphenylpolysiloxane having both molecular chain terminals dimethylvinylsiloxy group-blocked; dimethylsiloxane-methylvinylsiloxane copolymer having both molecular chain terminals trimethylsiloxy group-blocked; dimethylsiloxane-methylvinylsiloxane-methylphenylsiloxane copolymer having both molecular chain terminals trimethylsiloxy group-blocked; and mixtures of 2 or more thereof.
Furthermore, examples of organopolysiloxane resins having a branched or three-dimensional structure include those comprising at least a siloxane unit represented by the formula R13SiO1/2, a siloxane unit represented by the formula R12R2SiO1/2 and a siloxane unit represented by the formula SiO4/2.
In the formulae, R1 are identical or different monovalent C1-12 hydrocarbon groups having no aliphatic unsaturated bonds, and R1 denote C1-12 alkyl groups, C6-12 aryl groups or C7-12 aralkyl groups as described above, and are preferably methyl groups.
Also, in the formula, R2 is a C2-12 alkenyl group, and denotes an alkenyl group as described above, and is preferably a vinyl group.
These organopolysiloxane resins comprise at least a siloxane unit represented by the formula R13SiO1/2, a siloxane unit represented by the formula R12R2SiO1/2 and a siloxane unit represented by the formula SiO4/2; and they may also contain a siloxane unit represented by the formula R1SiO3/2, provided that this does not adversely affect the aim of the present invention. Also, these organopolysiloxane resins may have hydroxyl groups or alkoxy groups bonded to silicon atoms within the molecule, provided that this does not adversely affect the aim of the present invention; the adhesiveness of the inventive composition can be improved by having polar groups such as hydroxyl groups and/or alkoxy groups, particularly hydroxyl groups, bonded to the silicon atoms in the molecule. It should be noted that the organopolysiloxane resin is preferably such that the molar ratio of the total amount of siloxane units represented by formula R13SiO1/2 and siloxane units represented by formula R12R2SiO1/2, with respect to the siloxane unit represented by formula SiO4/2, is preferably 0.5-1.6, or more preferably 0.6-1.5 or 0.6-1.4.
Examples of these organopolysiloxane resins are those represented by the average composition formulae below. In the formulae, Vi, Me and Ph represent vinyl group, methyl group and phenyl group, respectively.
(ViMe2SiO1/2)0.10(Me3SiO1/2)0.33(SiO4/2)0.57(HO1/2)0.03
(ViMe2SiO1/2)0.13(Me3SiO1/2)0.35(SiO4/2)0.52(HO1/2)0.02
(ViMePhSiO1/2)0.10(Me3SiO1/2)0.45(SiO4/2)0.43(HO1/2)0.03
(ViMe2SiO1/2)0.09(Me3SiO1/2)0.31 (SiO4/2)0.60(HO1/2)0.04
(ViMe2SiO1/2)0.10(Me3SiO1/2)0.40(SiO4/2)0.50(HO1/2)0.03
Component (A) preferably contains at least this type of organopolysiloxane resin, and there are no limitations with regard to the amount contained; it preferably constitutes 40-90% by mass of component (A), and more preferably the lower limit is 50% by mass or 60% by mass and the upper limit is 80% by mass or 70% by mass. This is because when the organopolysiloxane resin content is at or above the abovementioned lower limit, the cured product obtained on curing the inventive composition can be very hard and tough, and when it is at or below the abovementioned upper limit, the inventive composition does not become too viscous and its handleability is good.
It should be noted that in order to lower the viscosity of the inventive composition and increase the hardness and mechanical strength of the cured product obtained on curing the inventive composition, an organopolysiloxane resin having a high alkenyl group content and low relative viscosity, as represented by the average composition formulae below, may be used in component (A) in addition to the abovementioned organopolysiloxane resin.
(ViMe2SiO1/2)0.55(Me3SiO1/2)0.05(SiO4/2)0.40
(ViMe2SiO1/2)0.13(Me3SiO1/2)0.45(SiO4/2)0.40
Moreover, in order to lower the viscosity of the inventive composition and increase the hardness and mechanical strength of the cured product obtained on curing the inventive composition, component (A) preferably contains alkenyl group-containing cyclic organopolysiloxane. This cyclic organopolysiloxane is represented by the average unit formula.
(R32SiO2/2)
In the formula, R3 are identical or different monovalent C1-12 hydrocarbon groups; specific examples are C1-12 alkyl groups, C2-12 alkenyl groups, C6-12 aryl groups and C7-12 aralkyl groups as described above, and these groups wherein some or all of the hydrogen atoms are substituted with halogen atoms such as fluorine atoms, chlorine atoms or bromine atoms. At least two R3 per molecule are abovementioned alkenyl groups, preferably vinyl groups. Also, in the formula, n is an integer from 3-20, preferably an integer from 3-10.
Examples of these cyclic organopolysiloxanes are shown below. In the formulae, Vi and Me are as described above.
(MeViSiO2/2)3
(MeViSiO2/2)4
(MeViSiO2/2)5
There are no particular limitations regarding the amount of cyclic organopolysiloxane in component (A); for good mechanical strength of the cured product obtained on curing the inventive composition, the amount is preferably no more than 5% by mass, more preferably no more than 3% by mass, of component (A).
There are no particular limitations regarding the viscosity of component (A); for good workability of the inventive composition, the viscosity at 25° C. is 10-5,000,000 m Pa·s, or preferably 50-1,000,000 mPa·s.
Component (B) is an organopolysiloxane having, per molecule, at least 2 siloxane units represented by the formula RHSiO. In order for the scorch time (ts1) and the 90% vulcanization time [tc(90)] of the inventive composition to be within the abovementioned ranges, an organopolysiloxane having the abovementioned siloxane units must be used as component (B). In the formula, R is a monovalent C1-12 hydrocarbon group having no aliphatic unsaturated bonds; examples are C1-12 alkyl groups, C6-12 aryl groups and C7-12 aralkyl groups as described above, and these groups wherein some or all of the hydrogen atoms are substituted with halogen atoms such as fluorine atoms, chlorine atoms or bromine atoms; it is preferably a methyl group.
There are no particular limitations regarding the molecular structure of component (B); for example, it can be linear, linear with some branching, branched, cyclic, or a three-dimensional network structure. Component (B) may be a single organopolysiloxane having such a molecular structure, or a mixture of two or more organopolysiloxanes having such molecular structures.
Examples of organopolysiloxane resins of branched or three-dimensional network structure are those comprising at least a siloxane unit represented by the formula R43SiO1/2, a siloxane unit represented by the formula R4HSiO2/2 and a siloxane unit represented by the formula SiO4/2; it may contain a siloxane unit represented by the formula R42SO2/2 and/or a siloxane unit represented by the formula R4SiO3/2, provided that this does not adversely affect the aim of the present invention. Also, these organopolysiloxane resins may have hydroxyl groups or alkoxy groups bonded to silicon atoms within the molecule, provided that this does not adversely affect the aim of the present invention. In this organopolysiloxane resin, with respect to the siloxane unit represented by formula SiO4/2, the molar ratio of the siloxane unit represented by formula R43SiO1/2 is preferably 0.6-1.5, and the molar ratio of the siloxane unit represented by formula R4HSiO2/2 is preferably 1.5-3.
In the formulae, R4 are identical or different monovalent C1-12 hydrocarbon groups having no aliphatic unsaturated carbon bonds; examples are C1-12 alkyl groups, C6-12 aryl groups and C7-12 aralkyl groups as described above, and these groups wherein some or all of the hydrogen atoms are substituted with halogen atoms such as fluorine atoms, chlorine atoms or bromine atoms; preferably they are methyl groups.
The organopolysiloxane resins represented by the average unit formulae below are examples of these organopolysiloxane resins. In the formulae, Me is as described above.
(Me3SiO1/2)0.23(MeHSiO2/2)0.51(SiO4/2)0.26
(Me3SiO1/2)0.24(MeHSiO2/2)0.49(SiO4/2)0.27
(Me3SiO1/2)0.24(Me2SiO2/2)0.10(MeHSiO2/2)0.40(SiO4/2)0.26
Furthermore, examples of organopolysiloxanes that are linear, or linear with some branching, are those comprising at least a siloxane unit represented by the formula R43SiO1/2, and a siloxane unit represented by the formula R4HSiO2/2 and having no siloxane unit represented by SiO4/2; they may also contain siloxane units represented by the formula R42HSiO1/2, siloxane units represented by the formula R42SiO2/2 or siloxane units represented by the formula R4SiO3/2, provided that this does not adversely affect the aim of the present invention.
In the formulae, R4 are identical or different monovalent C1-12 hydrocarbon groups having no aliphatic unsaturated carbon bonds; examples are C1-12 alkyl groups, C6-12 aryl groups and C7-12 aralkyl groups as described above, and these groups wherein some or all of the hydrogen atoms are substituted with halogen atoms such as 5 fluorine atoms, chlorine atoms or bromine atoms; preferably they are methyl groups.
The organopolysiloxanes represented by the formulae below are examples of these organopolysiloxanes. In the formulae, Me and Ph are as described above.
Me3SiO (MeHSiO)35SiMe3
HMe2SiO (Me2SiO)36Si Me2H
Me3SiO (MeHSiO)80SiMe3
Me3SiO (Me2SiO)30(MeHSiO)30SiMe3
Me 2PhSiO (MeHSiO)35SiMe2Ph
There are no particular limitations regarding the weight average molecular weight (Mw) of component (B), and for good adhesive strength of the cured product obtained on curing the inventive composition it is preferably no lower than 6000, no lower than 8000 or no lower than 10,000.
The amount of component (B) is such that the silicon atom-bonded hydrogen atom content in component (B) is within 0.1-10 moles with respect to 1 mole of the total amount of alkenyl groups in component (A); for good hardness, mechanical properties and adhesiveness of the resulting cured product, it is preferably such that said amount is within 0.5-5 moles, or 0.5-3 moles.
Component (C) is a platinum-group metal hydrosilylation reaction catalyst for promoting hydrosilylation of the inventive composition. Examples of platinum-group metals include platinum, ruthenium, rhodium, palladium, and iridium, and platinum is preferred. Examples of platinum-group metal hydrosilylation reaction catalysts, as component (C), include platinum fine powder, platinum black, chloroplatinic acid, alcohol-modified chloroplatinic acid, chloroplatinic acid-diolefin complex, platinum-olefin complex, platinum bis(acetoacetate), platinum bis(acetylacetonate) and other platinum-carbonyl. complexes, chloroplatinic acid-divinyltetramethyldisiloxane complex, chloroplatinic acid-tetravinyltetramethylcyclotetrasiloxane complex and other chloroplatinic acid-alkenylsiloxane complexes, platinum-divinyltetramethyldisiloxane complex, platinum-tetravinyltetramethylcyclotetrasiloxane complex and other platinum-alkenylsiloxane complexes, and complexes of chloroplatinic acid and acetylene alcohol; for marked promotion of the hydrosilylation reaction, platinum-alkenylsiloxane complexes are preferred.
Examples of the alkenylsiloxanes are 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, alkenylsiloxane oligomers in which some of the methyl groups In these alkenylsiloxanes are substituted with ethyl or phenyl groups, or the like, and alkenylsiloxane oligomers in which the vinyl groups in the alkenylsiloxane are substituted with allyl or hexenyl groups, or the like. In particular, 1,3-divinyl-1,1,3,3-tetramethyldisiloxane is preferred for good stability of the platinum-alkenylsiloxane complex produced.
To improve the stability of the platinum-alkenylsiloxane complex, these platinum-alkenylsiloxane complexes are preferably dissolved in an alkenylsiloxane oligomer such as 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, 1,3-diallyl-1,1,3,3-tetramethyldisiloxane, 1,3-divinyl-1,3-dimethyl-1,3-diphenyldisiloxane, 1,3-divinyl-1,1,3,3-tetraphenyldisiloxane, or 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, or an organosiloxane oligomer such as dimethylsiloxane oligomer, and they are especially preferably dissolved in an alkenylsiloxane oligomer.
The amount of component (C) is such that, with respect to the total amount of components (A) and (B), the amount, in mass units, of platinum-based element in this component is at least 10 ppm, and preferably 10-500 ppm, 10-100 ppm or 10-50 ppm.
This is because when the component (C) content is at or above the lower limit of the abovementioned ranges, the curability . of the inventive composition is good, specifically, the curability at die bonding thicknesses of 10 μm and lower is good; and moreover, when said content is at or below the upper limit of the abovementioned ranges, problems such as coloration of the resulting cured product are unlikely to arise.
Component (D) is a hydrosilylation reaction inhibitor for extending the pot life and improving the storage stability of the inventive composition at room temperature. Examples of component (D) are alkyne alcohols such as 1-ethynylcyclohexan-1-ol, 2-methyl-3-butyn-2-ol, 3,5-dimethyl-l-hexyn-3-ol, 2-phenyl-3-butyn-2-ol; enyne compounds such as 3-methyl-3-penten-1-yne and 3,5-dimethyl-3-hexen-1-yne; silylated alkyne alcohols such as methyltris(1-methyl-1-phenyl-propyneoxy)silane, dimethylbis(1-methyl-1-phenyl-propyneoxy)silane, methyltris(1,1-dimethyl-propyneoxy)silane and dimethylbis(1,1-dimethyl-propyneoxy)silane; and benzotriazoles; it is preferably an alkyne alcohol and/or silylated alkyne alcohol.
The amount of component (D) is preferably 0.0001-5 parts by mass, 0.01-5 parts by mass, or 0.01-3 parts by mass per 100 parts by mass of the total amount of components (A) and (B). This is because when the component (D) content is at or above the lower limit of the abovementioned ranges, it is possible to sufficiently inhibit gelling or curing that can occur when component (A), component (B) and component (C) are mixed, and when it is at or below the upper limit of the abovementioned ranges, it does not markedly lower the vulcanization characteristics of the inventive composition.
It is possible to achieve a scorch time (ts1) of 20-60 seconds at the die bonding temperature, specified in JIS K 6300-2, and a 90% vulcanization time [tc(90)] of 300-500 seconds with respect to the maximum torque value up to a vulcanization time of 600 seconds, by adjusting the amount of component (C), and adjusting the proportion with component (D) and/or the amount of component (D), in the inventive composition.
Component (E) is an adhesiveness-bestowing agent for bestowing the inventive composition with adhesiveness. A commonly known adhesiveness-bestowing agent that can be blended into curable silicone compositions that are cured by a hydrosilylation reaction can be used as this adhesiveness-bestowing agent.
Examples of component (E) are alkoxysilanes such as vinyltrimethoxysilane, allyltrimethoxysilane, allyltriethoxysilane, hydrogen triethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, and 3-methacryloxypropyltriethoxysilane; reaction mixtures comprising an alkenyl group-containing diorganosiloxane oligomer having both molecular chain terminals silanol group-blocked, such as dimethylsiloxane-methylvinylsiloxane copolymer oligomer having both molecular chain terminals silanol group-blocked or methylvinylsiloxane oligomer having both molecular chain terminals silanol group-blocked, and an epoxy group-containing alkoxysilane such as 3-glycidoxypropyltrimethoxysilane or 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane; reaction mixtures comprising an abovementioned alkenyl group-containing diorganosiloxane oligomer having both molecular chain terminals silanol group-blocked and 3-methacryloxypropyltrimethoxysilane; reaction mixtures comprising an abovementioned epoxy group-containing alkoxysilane and 3-aminopropyltriethoxysilane; and tris(3-trimethoxysilylpropyl)isocyanurate; and it is preferably a reaction mixture comprising alkenyl group-containing diorganosiloxane oligomer having both molecular chain terminals silanol group-blocked and an epoxy group-containing alkoxysilane.
The amount of component (E) is 0.01-10 parts by mass, preferably 0.01-5 parts by mass, per 100 parts by mass of the total amount of components (A) and (B). This is because when the component (E) content is at or above the lower limit of the abovementioned ranges, it is possible to bestow the inventive composition with sufficient adhesiveness; and when it is at or below the upper limit of the abovementioned ranges, it is unlikely to cause discoloration of the cured product obtained on curing the inventive composition.
In order to improve the workability and adhesiveness of the inventive composition, it preferably contains (F) fumed silica having a BET specific surface area of 20-200 m 2/g. There are no particular limitations relating to the amount of component (F), and for good mechanical properties of the resulting cured product, it is preferably 1-20 parts by mass per 100 parts by mass of the total amount of components (A) and (B).
As optional components, in addition to component (F), inorganic filler such as silica, glass, alumina and zinc oxide; silicone rubber powder; powders of resins such as silicone resin and polymethacrylate resin; and heat-resistant agent, dye, pigment, flame retardant, solvent, etc., may also be incorporated into the inventive composition, provided that the aim of the present invention is not adversely affected.
The inventive composition is cured by heating, and for rapid curing it is preferably heated to 50-200° C.
The inventive composition is preferably cured to form a cured product having a type D durometer hardness, as defined in JIS K 6253-1997 “Hardness testing methods for rubber, vulcanized or thermoplastic”, of at least 50, and more preferably to form a cured product having a type D durometer hardness of 50-70. This is because when the hardness is 50 or higher, the cured product has sufficient cohesive force, and sufficient strength and adhesiveness can be achieved under conditions where the film thickness is 10 μm or less; and when the hardness is 70 or lower, the cured product has flexibility and sufficient adhesion can be achieved.
Also, the inventive composition is preferably cured to form a cured product having a flexural strain, as defined in JIS K 7171-1994 “Plastics—Determination of flexural properties”, of at least 10%. This is because when the flexural strain is 10% or higher, the cured product has flexibility and sufficient adhesion is achieved.
The inventive composition is such that at the die bonding temperature the scorch time (ts1) is 20-60 seconds, as measured by MDR (moving die rheometer), and the 90% vulcanization time [tc(90)] is 300-500 seconds; an example of a method for obtaining such a curable composition is to use as component (B) an organopolysiloxane having per molecule at least 2 siloxane units represented by the formula RHSiO, and to adjust the amount of component (C) or adjust the type and amount of component (D). It should be noted that the measurement by MDR is performed as stipulated in JIS K 6300-2 “Rubber, unvulcanized—Physical property—Part 2: Determination of cure characteristics with oscillating curemeters”, and the same applies to the definitions of the scorch time (ts1) and the 90% vulcanization time [tc(90)].
By achieving such curability, it is possible to realise sufficient curability at 150° C., which is the die bonding temperature usually adopted when using die bonding agent for LEDs having a film thickness of 10 μm or less. If the scorch time (ts1) and/or 90% vulcanization time [tc(90)] are below their abovementioned respective lower limits, curing proceeds too quickly and it is not possible to achieve sufficient adhesive strength, and if they are above their abovementioned respective upper limits, curing proceeds too slowly, such that sufficient curing cannot be achieved by curing for 2 hours at 150° C., which constitutes usual die bonding conditions.
The inventive curable silicone composition for die bonding use is described in more detail by means of examples and comparative examples. It should be noted that viscosity refers to the value at 25° C. In the examples and comparative examples, the following components were used to adjust the curable silicone compositions for die bonding use. In the formulae, Vi represents a vinyl group and Me represents a methyl group.
The following components were used as component (A).
HO(MeViSiO)2OH
and having a viscosity of 30 m Pa·s (vinyl content=30% by mass)
(Me2ViSiO1/2)0.55(Me3SiO1/2)0.05(SiO4/2)0.40
and having a viscosity of 300 m Pa·s (vinyl content=19.0% by mass)
(Me2ViSiO1/2)0.15(Me3SiO1/2)0.45(SiO4/2)0.40
and having a viscosity of 350 m Pa·s (vinyl content=5.1% by mass)
(Me2ViSiO1/2)0.09(Me3SiO1/2)0.43(SiO4/2)0.48(HO1/2)0.03
that is solid at room temperature (vinyl content=3.0% by mass)
(Me2ViSiO1/2)0.10(Me3SiO1/2)0.45(SO4/2)0.45(HO1/2)0.02
that is solid at room temperature (vinyl content=3.0% by mass)
The following components were used as component (B).
(Me3SiO1/2)0.23(MeHSiO2/2)0.51(SiO4/2)0.26
and having a viscosity of 2000 m Pa·s (weight average molecular weight=18,000, silicon atom-bonded hydrogen atom content=0.78% by mass)
(Me3SiO1/2)0.24(MeHSiO2/2)0.40(SiO2/2)0.27
and having a viscosity of 510 m Pa·s (weight average molecular weight=16,300, silicon atom-bonded hydrogen atom content=0.75% by mass)
Me3SiO (MeHSiO)36SiMe3
and having a viscosity of 10 m Pa·s (weight average molecular weight=8,800, silicon atom-bonded hydrogen atom content=1.6% by mass)
(HMe2SiO1/2)0.67(SiO4/2)0.33
and having a viscosity of 120 m Pa·s (weight average molecular weight=1310, silicon atom-bonded hydrogen atom content=0.95% by mass)
The following component was used as component (C).
The following components were used as component (D).
The following component was used as component (E).
The following component was used as component (F).
In the examples and comparative examples, the vulcanization characteristics of the curable silicone compositions for die bonding use and the properties of the cured products were measured as follows.
Measurement of Scorch Time ts1 and 90% Vulcanization Time tc(90)
These were measured by vulcanizing the curable silicone composition for die bonding use for 600 seconds at a common die bonding temperature (150° C.) in accordance with the method stipulated in JIS K 6300-2:2001 “Rubber, unvulcanized—Physical property—Part 2: Determination of cure characteristics with oscillating curemeters”, using a Curelastometer (Premier MDR manufactured by Alpha Technologies). It should be noted that measurement was started when 5 ml of the curable liquid silicone composition was placed on the lower die and the upper die was closed.
The measurements were performed using an R-type die for rubber, with an amplitude angle of 0.5°, a vibration frequency of 100/minute, and a torque range of up to 230 kgf·cm.
The curable silicone composition for die bonding use was press-molded at 150° C. for 2 hours to produce sheet-like cured product. The hardness of this sheet-like cured product was measured as stipulated in JIS K 6253-1997 “Hardness testing methods for rubber, vulcanized or thermoplastic” using a type D durometer.
The curable silicone composition for die bonding use was heated at 150° C. for 2 hours to produce the cured product. The flexural strain (%) of the cured product was found in accordance with the method stipulated in JIS K 7171-1994 “Plastics—Determination of flexural properties”.
The curable silicone composition for die bonding use was coated onto an LED substrate using a die bonder (AD830 PLUS, manufactured by ASM), then a 300 μ2 LED chip was placed thereon, and the resulting system was cured under curing conditions at 150° C. for 2 hours. The chip die strength was then measured using a die shear tester (DAGE 4000 Bondtester, manufactured by Nordson DAGE).
The curable silicone compositions for die bonding use were prepared in accordance with the compositions shown in Table 1 and Table 2. It should be noted that in Table 1 and Table 2, “SiH/Vi” represents the value of the total number of moles of silicon atom-bonded hydrogen atoms in component (B) per mole of the total amount of vinyl groups in component (A). The vulcanization characteristics of the curable silicone compositions and the properties of the cured products are also shown in Table 1 and Table 2.
The inventive composition can firmly adhere a semiconductor element to a support, and is therefore suitable as a die bonding agent for semiconductor elements such as light emitting diodes (LEDs), semiconductor lasers, photodiodes, phototransistors, solid-state imaging, light emitters and photoreceptors for photocouplers.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017-124377 | Jun 2017 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2018/023212 | 6/19/2018 | WO | 00 |