DIELECTRIC CERAMIC COMPOSITION AND CERAMIC ELECTRONIC COMPONENTS

Abstract
Provided is a dielectric ceramic composition including a first component and a second component, wherein the first component comprises an oxide of Ca of 0.00 mol % to 35.85 mol % an oxide of Sr of 0.00 mol % to 47.12 mol %, an oxide of Ba of 0.00 mol % to 51.22 mol %, an oxide of Ti of 0.00 mol % to 17.36 mol %, an oxide of Zr of 0.00 mol % to 17.36 mol %, an oxide of Sn of 0.00 mol % to 2.60 mol %, an oxide of Nb of 0.00 mol % to 35.32 mol %, an oxide of Ta of 0.00 mol % to 35.32 mol %, and an oxide of V of 0.00 mol % to 2.65 mol %, and the second component includes at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass and (b) an oxide of Cu and/or an oxide of Ru.
Description
TECHNICAL FIELD

The present invention relates to a dielectric ceramic composition and ceramic electronic components using the dielectric ceramic composition as a dielectric layer.


BACKGROUND ART

In recent years, requirements of electronic components that are operated under a high temperature environment exceeding 150° C. have increased year by year for devices mounted in a harsh temperature environment, such as an environment around an engine room of an automobile. In particular, in an automobile market in recent years, the use of electronic control for each function has rapidly progressed, aiming at improving safety and environmental performance. Consequently, the mounting ratio of electronic devices has been increased. Of these electronic devices, an electronic device mounted in an engine room is exposed to a harsh temperature environment and thus high heat resistance in addition to high reliability has been required for the electronic components.


Conventionally, as the ceramic electronic components satisfying such requirement such as capacitors, a ceramic composition exhibiting a paraelectricity (paraelectric material) such as calcium zirconate is used for a dielectric layer of the ceramic electronic components. However, the electronic components having a dielectric layer constituted by the paraelectric material have low relative dielectric constant of the ceramic composition and thus capacitors having high capacity cannot be obtained.


Barium titanate (BaTiO3) known as a representative ceramic composition for ceramic capacitors has a high relative dielectric constant. However, barium titanate has the peak of the relative dielectric constant at a characteristic temperature referred to as a ferroelectric transition temperature and the properties are rapidly lowered at 120° C. or more.


Therefore, the development of a dielectric ceramic composition having a high relative dielectric constant even in a high temperature environment (for example, 150° C. or more) has been desired.


In recent years, in the ceramic electronic components, a base metal such as nickel and copper is frequently used as a material for internal electrodes. In the case where the base metal is used as the internal electrode layer, the dielectric layer and the internal electrodes are co-fired. In order to prevent the base metal from oxidation during firing, the ceramic electronic components including the ceramic composition constituting the dielectric layer are fired under a reducing atmosphere.


Non-Patent Literature 1 has described a dielectric ceramic composition having a tungsten bronze structure represented by a general formula M2+6M4+2Nb8O30. In this Non-Patent Literature 1, in order to obtain experimental samples, the raw materials of the ceramic composition are mixed, and thereafter the materials are fired around 1,000° C. for 15 hours. The obtained product is ground, dried, and molded, and thereafter further sintered at 1,250° C. to 1,350° C. for 5 hours to 6 hours.


In Patent Literatures 1 to 11, the dielectric ceramic compositions having various tungsten bronze structures have been studied.


CITATION LIST
Non-Patent Literature



  • Non-Patent Literature 1: Mat. Res. Bull., Vol. 27 (1992), pp. 677-684; R. R. Neurgaonkar, J. G. Nelson and J. R. Oliver



Patent Literatures



  • Patent Literature 1: Japanese Patent Application Laid-open No. 2002-211975

  • Patent Literature 2: Japanese Patent Application Laid-open No. 2007-197277

  • Patent Literature 3: Japanese Patent Application Laid-open No. H11-043370

  • Patent Literature 4: Japanese Patent Application Laid-open No. 2000-169215

  • Patent Literature 5: Japanese Patent Application Laid-open No. 2008-189487

  • Patent Literature 6: WO 08/102608 Pamphlet

  • Patent Literature 7: WO 06/114914 Pamphlet

  • Patent Literature 8: Japanese Patent Application Laid-open No. 2013-180906

  • Patent Literature 9: Japanese Patent Application Laid-open No. 2013-180907

  • Patent Literature 10: Japanese Patent Application Laid-open No. 2013-180908

  • Patent Literature 11: Japanese Patent Application Laid-open No. 2012-169635



SUMMARY
Technical Problem

However, in Non-Patent Literature 1, although the properties of the dielectric ceramic composition itself having the tungsten bronze structure have been studied from the academic viewpoint, the applications of the dielectric ceramic composition are not considered at all. In other words, in Non-Patent Literature 1, the dielectric ceramic composition is fired in a laboratory under a normal environmental atmosphere. However, as a result of detailed study for the dielectric ceramic composition having the tungsten bronze structure represented by the general formula conducted by the inventors of the present invention, the inventors of the present invention have found that a dielectric ceramic composition having completely different properties from those of the dielectric ceramic composition reported in Non-Patent Literature 1 is obtained in the case where firing and sintering are performed under a reducing atmosphere that has been required for dielectric ceramic compositions in recent years.


In Patent Literatures 1 to 11, the dielectric ceramic compositions having the tungsten bronze structures have also been studied. However, in any of these Patent Literatures, dielectric ceramic compositions simultaneously exhibiting the effects of “being possible to be fired under a reducing atmosphere”, “providing sufficiently a high relative dielectric constant”, “having an excellent dielectric property in a wide temperature region”, and “having a small dielectric loss” have not been obtained.


In addition to the above-described performances, for the dielectric ceramic composition, a high insulation resistance value above a certain level (for example, about 40 MΩ at 200° C.) is required for electronic components using the dielectric ceramic composition.


Therefore, an object of the present invention is to provide a dielectric ceramic composition that can be fired under a reducing atmosphere, has a high relative dielectric constant, and, in the case where the dielectric ceramic composition is used as the dielectric layer of ceramic electronic components such as a laminated ceramic capacitor, has a small change in electrostatic capacity even under a high temperature environment, for example, under a condition of 150° C. to 200° C. and small dielectric losses at 25° C. and 200° C., and further can obtain a high insulation resistance value even at 200° C., and ceramic electronic components in which the dielectric ceramic composition is used as the dielectric layer.


Solution to Problem

The above-described problems are solved by the present invention described below.


Namely, the present invention (1) provides a dielectric ceramic composition comprising: a first component; and a second component, wherein


as a content ratio relative to a total number of moles of the first component when converted into following oxides, the first component comprises an oxide of Ca of 0.00 mol % to 35.85 mol % in terms of CaO, an oxide of Sr of 0.00 mol % to 47.12 mol % in terms of SrO, an oxide of Ba of 0.00 mol % to 51.22 mol % in terms of BaO, an oxide of Ti of 0.00 mol % to 17.36 mol % in terms of TiO2, an oxide of Zr of 0.00 mol % to 17.36 mol % in terms of ZrO2, an oxide of Sn of 0.00 mol % to 2.60 mol % in terms of SnO2, an oxide of Nb of 0.00 mol % to 35.32 mol % in terms of Nb2O5, an oxide of Ta of 0.00 mol % to 35.32 mol % in terms of Ta2O5, and an oxide of V of 0.00 mol % to 2.65 mol % in terms of V2O5;


the first component comprises at least one oxide selected from the oxide of Ca, the oxide of Sr, and the oxide of Ba, at least one oxide selected from the oxide of Ti and the oxide of Zr, and at least one oxide selected from the oxide of Nb and the oxide of Ta as essential components, and, a total content ratio of the oxide of Ca in terms of CaO, the oxide of Sr in terms of SrO, and the oxide of Ba in terms of BaO is 48.72 mol % to 51.22 mol %, a total content ratio of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 is 15.97 mol % to 17.36 mol %, and a total content ratio of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 is 31.42 mol % to 35.31 mol % relative to the total number of moles of the first component when converted into the oxides; and


as a content ratio relative to a total mass of the first component when converted into the oxides, the second component comprises at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass in terms of MnO and (b) one or both of an oxide of Cu and an oxide of Ru.


In addition, the present invention (2) provides a dielectric ceramic composition comprising: a first component; and a second component, wherein


as the first component, a compound represented by a following general formula (1):





AaM1bM2cOd  (1)


(in the formula (1), A is represented by a general formula (2):





Ba1-x-ySrxCay  (2)


(in the formula (2), 0≤x≤0.920 and 0≤y≤0.700); M1 is at least one element selected from Ti, Zr, and Sn; M2 is at least one element selected from Nb, Ta, and V; and 5.70≤a≤6.30, 1.90≤b≤2.10, 7.20≤c≤8.80, and 27.45≤d≤32.50) is included (with the proviso that, when Sn is included, a content ratio of the oxide of Sn in terms of SnO2 relative to a total number of moles of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 is 15.00 mol % or less and when V is included, a content ratio of the oxide of V in terms of V2O5 relative to a total number of moles of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 is 7.50 mol % or less); and


as a content ratio relative to a total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5, the second component comprises at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass in terms of MnO and (b) one or both of an oxide of Cu and an oxide of Ru.


In addition, the present invention (3) provides a dielectric ceramic composition comprising: a first component; and a second component, wherein


a compound represented by a following general formula (3):





α·Caη1M3θ1M4ϕ1Oω1-β·Srη2M3θ2M4ϕ2Oω2-γ·Baη3M3θ3M4ϕ3Oω3  (3)


(in the formula (3), η1, η2, and η3 are each independently values within a range of 5.70 to 6.30; θ1, θ2, and θ3 are each independently values within a range of 0.95 to 1.05; ϕ1, ϕ2, and ϕ3 are each independently values within a range of 0.90 to 1.10; ω1, ω2, and ω3 are each independently values within a range of 27.45 to 32.50; M3 is represented by a general formula (4):





Ti2-ρ-σZrρSnσ  (4)


(in the formula (4), 0≤ρ≤2.0 and 0≤σ≤0.3); M4 is represented by a general formula (5):





Nb8-π-ψTaπVψ  (5)


(in the formula (5), 0≤π≤8.0 and 0≤ψ≤0.6); and α, β, and γ satisfy α+β+γ=1.00), and when an arbitrary point in a ternary composition diagram is represented as (α, β, γ), the compound existing within a range surrounded by line segments linking a point A=(0.05, 0.95, 0.00), a point B=(0.70, 0.30, 0.00), a point C=(0.70, 0.00, 0.30), a point D=(0.00, 0.00, 1.00), and a point E=(0.00, 0.90, 0.10) is included as the first component, and


as a content ratio relative to a total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5, the second component comprises at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass in terms of MnO and (b) one or both of an oxide of Cu and an oxide of Ru.


In addition, the present invention (4) provides the dielectric ceramic composition of (3), wherein the first component is a compound existing within a range surrounded by line segments linking a point A′=(0.05, 0.95, 0.00), a point B′=(0.60, 0.40, 0.00), a point C′=(0.70, 0.20, 0.10), a point D′=(0.70, 0.10, 0.20), a point E′=(0.55, 0.00, 0.45), a point F′=(0.40, 0.00, 0.60), a point G′=(0.10, 0.10, 0.80), a point H′=(0.00, 0.00, 1.00), a point I′=(0.00, 0.40, 0.60) a point J′=(0.20, 0.40, 0.40), a point K′=(0.00, 0.70, 0.30), and a point L′=(0.00, 0.90, 0.10) in the ternary composition diagram.


In addition, the present invention (5) is the dielectric ceramic composition according to any one of (1) to (4), wherein, as the content ratio relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5, the second component comprises one or both of an oxide of Cu of 0.010% by mass or more and less than 0.080% by mass in terms of CuO and an oxide of Ru of 0.050% by mass or more and less than 0.300% by mass in terms of RuO2.


In addition, the present invention (6) provides the dielectric ceramic composition of any one of (1) to (5), wherein an oxide of D (D is at least one element selected from Li, Mg, Si, Cr, Al, Fe, Co, Ni, Zn, Ga, Ge, In, W, Mo, Y, Hf, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) is included as the second component.


In addition, the present invention (7) provides the dielectric ceramic composition of any one of (1) to (6), wherein the dielectric ceramic composition comprises a tungsten bronze type crystal phase.


In addition, the present invention (8) provides the dielectric ceramic composition of any one of (1) to (7), wherein the relative dielectric constant at 25° C. is 100.0 or more.


In addition, the present invention (9) provides the dielectric ceramic composition of any one of (1) to (8), wherein a change rate in electrostatic capacity is within a range of −20.0% to 5.0% in a temperature range of −55° C. to 200° C.


In addition, the present invention (10) provides the dielectric ceramic composition of any one of (1) to (9), wherein a dielectric loss (tan δ) at 25° C. is 10.0% or less and a dielectric loss (tan δ) at 200° C. is 10.0% or less.


In addition, the present invention (11) provides the dielectric ceramic composition of any one of (1) to (10), wherein an insulation resistance value at 200° C. is 40 MΩ or more and less than 100 MΩ.


In addition, the present invention (12) provides ceramic electronic components, wherein a dielectric layer formed of the dielectric ceramic composition as described in any one of (1) to (11); and an electrode layer comprising a base metal as a conductive component.


In addition, the present invention (13) provides the ceramic electronic components of (12), wherein the base metal is at least one metal selected from nickel and copper.


In addition, the present invention (14) provides the ceramic electronic components of (12) or (13), wherein a plurality of the dielectric layers and a plurality of the electrode layers are laminated.


Advantageous Effects of Invention

According to the present invention, the dielectric ceramic composition that can be fired under a reducing atmosphere, has a high relative dielectric constant, and, in the case where the dielectric ceramic composition is used as the dielectric layer of ceramic electronic components such as a laminated ceramic capacitor, has a small change in electrostatic capacity even under a high temperature condition of 150° C. to 200° C., a change rate in electrostatic capacity within a range of −50.0% to 50.0% (hereinafter, may be described as within ±50.0%) in a temperature range of −55° C. to 200° C., small dielectric losses at 25° C. and 200° C., and further can obtain a insulation resistance value at 200° C. of 40 MΩ or more, and the ceramic electronic components in which the dielectric ceramic composition is used as the dielectric layer can be provided.





BRIEF DESCRIPTION OF DRAWINGS


FIG. 1 is a triangle diagram illustrating the suitable composition range of the dielectric ceramic composition according to the present invention.



FIG. 2 is a triangle diagram illustrating the further suitable composition range of the dielectric ceramic composition according to the present invention.



FIG. 3 is a SEM image (10,000 times) of Reference Sample 8.



FIG. 4 is a SEM image (10,000 times) of Reference Sample 15.



FIG. 5 is a SEM image (10,000 times) of Reference Sample 66.



FIG. 6 is a graph illustrating trends of the change rates of the electrostatic capacity of Reference Samples 8, 15, and 66.



FIG. 7 is a graph illustrating trends of the change rates of the electrostatic capacity of Reference Samples 15 and 78.



FIG. 8 is a sectional view schematically illustrating a ceramic capacitor.



FIG. 9 is a chart illustrating the result of X-ray diffraction measurement of Reference Sample 15.





DESCRIPTION OF EMBODIMENTS

Hereinafter, the present invention will be described with reference to embodiments illustrated in drawings. In the present invention, in the description of a numerical range “Δ to □”, the values of Δ and □ are included unless otherwise noted.


(Ceramic Capacitor 1)


The ceramic capacitor 1 illustrated in FIG. 8 includes a laminated body 10 having a cuboid shape as a whole. The laminated body 10 is constituted with a plurality of laminated dielectric layers 3 and a plurality of internal electrodes 2a and 2b formed along different interfaces of the dielectric layers 3. The internal electrodes 2a and 2b are alternately arranged in the laminated body 10. Each of the internal electrodes 2a and 2b is electrically connected to an external electrode 4 at different edges of the laminated body 10. On the external electrode 4, a first plated layer made of copper or a nickel-copper alloy, or the like may be formed and a second plated layer made of solder or tin, or the like may be further formed on the first plated layer, if necessary.


As described above, the internal electrodes 2a and 2b are formed in a state where the internal electrodes overlap with each other in a laminated direction of the laminated body 10 and thus accumulate electrical charge between the adjacent internal electrodes 2a and 2b. The electrical connection of the internal electrodes 2a and 2b and the external electrode 4 allows the charge to be taken out.


(Internal Electrodes 2a and 2b)


In the present invention, the base metal is used as a conductive component for the internal electrodes 2a and 2b. As the base metal as the conductive component, pure metals such as nickel, copper, and aluminum and, in addition to these metals, alloys, mixtures, or composites including these metal components may be used. As the base metal as the conductive component, one metal selected from nickel and copper is particularly preferable. The internal electrodes 2a and 2b may include a conductive component in addition to the base metal and an inhibitor described below as long as the effects of the present invention are not impaired.


The internal electrodes 2a and 2b may be formed by any methods. Examples of the method include a method for forming the internal electrodes using a conductive paste obtained by kneading a metal powder including the base metal with a binder component. In the case where the conductive paste is used, a method for forming the internal electrodes by a printing method such as screen printing is particularly preferable as the method for forming the internal electrodes 2a and 2b. In the conductive paste, as what is called inhibitor for controlling sintering of the metal powder, a dielectric ceramic composition powder having the same components as the components in the dielectric ceramic composition according to the present invention described below may be included. In addition to the above method, the internal electrodes 2a and 2b may also be formed by known methods such as an ink-jet method, a vapor deposition method, and a plating method.


(Dielectric Layer 3)


The dielectric layer 3 is constituted of the dielectric ceramic composition according to the present invention described below, whereby the change in the electrostatic capacity is small even in a wide temperature region, in particular, in a high temperature region of around 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and both dielectric losses (tan δ) at 25° C. and 200° C. are 10.0% or less, while a high relative dielectric constant is being maintained. In addition, the dielectric ceramic composition according to the present invention has excellent reduction resistance and thus is less likely to be reduced and does not transform to a semiconductor even in the case where the base metal is used as the conductive component of the internal electrode and simultaneous firing is performed under a reducing atmosphere.


(Dielectric Ceramic Composition)


The dielectric ceramic composition according to the first embodiment of the present invention includes the first component and the second component, in which


as a content ratio relative to a total number of moles of the first component when converted into following oxides, the first component comprises an oxide of Ca of 0.00 mol % to 35.85 mol % in terms of CaO, an oxide of Sr of 0.00 mol % to 47.12 mol % in terms of SrO, an oxide of Ba of 0.00 mol % to 51.22 mol % in terms of BaO, an oxide of Ti of 0.00 mol % to 17.36 mol % in terms of TiO2, an oxide of Zr of 0.00 mol % to 17.36 mol % in terms of ZrO2, an oxide of Sn of 0.00 mol % to 2.60 mol % in terms of SnO2, an oxide of Nb of 0.00 mol % to 35.32 mol % in terms of Nb2O5, an oxide of Ta of 0.00 mol % to 35.32 mol % in terms of Ta2O5, and an oxide of V of 0.00 mol % to 2.65 mol % in terms of V2O5;


the first component comprises at least one oxide selected from the oxide of Ca, the oxide of Sr, and the oxide of Ba, at least one oxide selected from the oxide of Ti and the oxide of Zr, and at least one oxide selected from the oxide of Nb and the oxide of Ta as essential components, and a total content ratio of the oxide of Ca in terms of CaO, the oxide of Sr in terms of SrO, and the oxide of Ba in terms of BaO is 48.72 mol % to 51.22 mol %, a total content ratio of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 is 15.97 mol % to 17.36 mol %, and a total content ratio of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 is 31.42 mol % to 35.31 mol % relative to the total number of moles of the first component when converted into the oxides; and


as a content ratio relative to a total mass of the first component when converted into the oxides, the second component comprises at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass in terms of MnO and (b) one or both of an oxide of Cu and an oxide of Ru.


The dielectric ceramic composition according to the first embodiment of the present invention includes the first component and the second component. In the dielectric ceramic composition according to the first embodiment of the present invention, among oxides included in the dielectric ceramic composition, all oxides other than the oxides included as the first component are included as the second component.


The first component of the dielectric ceramic composition according to the first embodiment of the present invention comprises one or more oxides selected from the oxide of Ca, the oxide of Sr, and the oxide of Ba, one or more oxides selected from the oxide of Ti and the oxide of Zr, and one or more oxides selected from the oxide of Nb and the oxide of Ta as essential components and one or more oxides selected from the oxide of Sn and the oxide of V as optional components.


In the dielectric ceramic composition according to the first embodiment of the present invention, as a content ratio relative to a total number of moles of the first component when converted into the following oxides, the content of each of the oxides existing in the first component is an oxide of Ca of 0.00 mol % to 35.85 mol % in terms of CaO, an oxide of Sr of 0.00 mol % to 47.12 mol % in terms of SrO, an oxide of Ba of 0.00 mol % to 51.22 mol % in terms of BaO, an oxide of Ti of 0.00 mol % to 17.36 mol % in terms of TiO2, an oxide of Zr of 0.00 mol % to 17.36 mol % in terms of ZrO2, an oxide of Sn of 0.00 mol % to 2.60 mol % in terms of SnO2, an oxide of Nb of 0.00 mol % to 35.32 mol % in terms of Nb2O5, an oxide of Ta of 0.00 mol % to 35.32 mol % in terms of Ta2O5, and an oxide of V of 0.00 mol % to 2.65 mol % in terms of V2O5.


In the dielectric ceramic composition according to the first embodiment of the present invention, the total content ratio of the oxide of Ca in terms of CaO, the oxide of Sr in terms of SrO, and the oxide of Ba in terms of BaO relative to the total number of moles of the first component when converted into the above oxides is 48.72 mol % to 51.22 mol % and preferably 49.37 mol % to 50.62 mol %.


In the dielectric ceramic composition according to the first embodiment of the present invention, the total content ratio of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 relative to the total number of moles of the first component when converted into the above oxides is 15.97 mol % to 17.36 mol % and preferably 16.32 mol % to 17.01 mol %. In the case where the first component includes Sn, the content ratio of the oxide of Sn in terms of SnO2 relative to total number of moles of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 is 15.00 mol % or less.


In the dielectric ceramic composition according to the first embodiment of the present invention, the total content ratio of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 relative to the total number of moles of the first component when converted into the above oxides is 31.42 mol % to 35.31 mol % and preferably 32.20 mol % to 34.43 mol %. In the case where the first component includes V, the content ratio of the oxide of V in terms of V2O5 relative to total number of moles of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 is 7.50 mol % or less.


The dielectric ceramic composition according to the first embodiment of the present invention includes at least (a) component, that is, the oxide of Mn and (b) component, that is, the oxide of Cu, the oxide of Ru, or the oxide of Cu and the oxide of Ru as the second component. In other words, the dielectric ceramic composition according to the first embodiment of the present invention includes the oxide of Mn and one or both of the oxide of Cu and the oxide of Ru as the essential second component.


In the dielectric ceramic composition according to the first embodiment of the present invention, the content of the oxide of Mn is 0.005% by mass to 3.500% by mass, preferably 0.005% by mass to 2.000% by mass, and particularly preferably 0.010% by mass to 1.500% by mass in terms of MnO relative to the total mass of the first component when converted into the above oxides.


In the case where the dielectric ceramic composition according to the first embodiment of the present invention includes the oxide of Cu as the second component, the content of the oxide of Cu is preferably 0.010% by mass or more and less than 0.080% by mass, particularly preferably 0.020% by mass or more and less than 0.080% by mass, and more preferably 0.030% by mass or more and less than 0.080% by mass in terms of CuO relative to the total mass of the first component when converted into the above oxides.


In the case where the dielectric ceramic composition according to the first embodiment of the present invention includes the oxide of Ru as the second component, the content of the oxide of Ru is 0.050% by mass or more and less than 0.300% by mass, particularly preferably 0.100% by mass or more and less than 0.300% by mass, and more preferably 0.200% by mass or more and less than 0.300% by mass in terms of RuO2 relative to the total mass of the first component when converted into the above oxides.


The dielectric ceramic composition according to the first embodiment of the present invention includes the oxide of Mn having the above content as the second component, whereby in the case where the dielectric ceramic composition is used as a dielectric layer of the ceramic electronic components such as a laminated ceramic capacitor, the change in the electrostatic capacity is small even in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses (tan δ) at 25° C. and 200° C. are small.


The dielectric ceramic composition according to the first embodiment of the present invention, in which the content of the first component is determined to be the above content and the oxide of Mn is included in the above content as the second component, exhibits the effects in which the change in the electrostatic capacity is small in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses (tan δ) at 25° C. and 200° C. are small. In addition, the dielectric ceramic composition according to the first embodiment of the present invention, in which one or both of the oxide of Cu and the oxide of Ru are included as the second component, can provide the high insulation resistance value without significantly affecting the effects caused by determining the content of the first component to be the above content and including the oxide of Mn in the above content as the second component, that is, the effects in which the change in the electrostatic capacity is small in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses at 25° C. and 200° C. are small.


The dielectric ceramic composition according to the first embodiment of the present invention includes (a) the oxide of Mn and (b) any one or both of the oxide of Cu and the oxide of Ru and, in addition to the above components, the oxides (hereinafter, also described as a (c) component) other than the (a) component and the (b) component may be optionally included as the second component. The second component is added to the dielectric ceramic composition according to the present invention for the purpose of improving the reduction resistance and other properties. The ratio of total mass of the second component other than the (b) component in terms of the oxides (that is, the total mass of the (a) component and the (c) component) is preferably 10.000% by mass or less and particularly preferably 0.100% by mass to 5.500% by mass relative to the total mass of the first component when converted into the above oxides.


The optional component of the second component included in the dielectric ceramic composition according to the first embodiment of the present invention is preferably the oxides of D (D is at least one element selected from Li, Mg, Si, Cr, Al, Fe, Co, Ni, Zn, Ga, Ge, In, W, Mo, Y, Hf, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) and the oxide of Mg, the oxide of Si, and the oxide of Y are particularly preferable.


The mass of the oxide of D is a converted value of Li in terms of Li2O, Mg in terms of MgO, Si in terms of SiO2, Cr in terms of Cr2O3, Al in terms of Al2O3, Fe in terms of Fe2O3, Co in terms of CoO, Ni in terms of NiO, Zn in terms of ZnO, Ga in terms of Ga2O3, Ge in terms of GeO2, In in terms of In2O3, Win terms of WO3, Mo in terms of MoO3, Yin terms of Y2O3, Hf in terms of HfO2, La in terms of La2O3, Ce in terms of CeO2, Pr in terms of Pr6O11, Nd in terms of Nd2O3, Sm in terms of Sm2O3, Eu in terms of Eu2O3, Gd in terms of Gd2O3, Tb in terms of Tb4O7, Dy in terms of Dy2O3, Ho in terms of Ho2O3, Er in terms of Er2O3, Tm in terms of Tm2O3, Yb in terms of Yb2O3, or Lu in terms of Lu2O3.


The dielectric ceramic composition according to the first embodiment of the present invention preferably exhibits existence of the tungsten bronze type crystal phase when crystal structure analysis such as X-ray diffraction is performed. The average grain size of the dielectric ceramic composition according to the first embodiment of the present invention is preferably 5 or less and particularly preferably 3 μm or less.


The dielectric ceramic composition according to the second embodiment of the present invention includes the first component and the second component, in which


as the first component, a compound represented by a following general formula (1):





AaM1bM2cOd  (1)


(in the formula (1), A is represented by a general formula (2):





Ba1-x-ySrxCay  (2)


(in the formula (2), 0≤x≤0.920 and 0≤y≤0.700); M1 is at least one element selected from Ti, Zr, and Sn; M2 is at least one element selected from Nb, Ta, and V; and 5.70≤a≤6.30, 1.90≤b≤2.10, 7.20≤c≤8.80, and 27.45≤d≤32.50) is included (with the proviso that, when Sn is included, the content ratio of the oxide of Sn in terms of SnO2 relative to the total number of moles of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 is 15.00 mol % or less and when V is included, the content ratio of the oxide of V in terms of V2O5 relative to the total number of moles of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 is 7.50 mol % or less), and


as a content ratio relative to a total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5, the second component comprises at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass in terms of MnO and (b) one or both of an oxide of Cu and an oxide of Ru.


The dielectric ceramic composition according to the second embodiment of the present invention includes the first component and the second component. In the dielectric ceramic composition according to the second embodiment of the present invention, among oxides included in the dielectric ceramic composition, all oxides other than the oxides included as the first component are included as the second component.


In the dielectric ceramic composition according to the second embodiment of the present invention, the first component is a compound represented by the following general formula (1):





AaM1bM2cOd  (1).


In the general formula (1), A is represented by the general formula (2):





Ba1-x-ySrxCay  (2)


(in the formula (2), 0≤x≤0.920 and 0≤y≤0.700). In other words, A may be Ba alone, a combination of any of two of Ca, Sr, and Ba (Ca and Sr, Ca and Ba, or Sr and Ba), or a combination of Ca, Sr, and Ba.


In the general formula (1), M1 is at least one element selected from Ti, Zr, and Sn. Here, one or more elements selected from Ti and Zr are essential as M1. More specifically, M1 is Ti alone, Zr alone, a combination of Ti and Sn, a combination of Zr and Sn, a combination of Ti and Zr, or a combination of Ti, Zr, and Sn.


In the general formula (1), M2 is at least one element selected from Nb, Ta, and V. Here, one or more elements selected from Nb and Ta are essential as M2. More specifically, M2 is Nb alone, Ta alone, a combination of Nb and V, a combination of Ta and V, a combination of Nb and Ta, or a combination of Nb, Ta, and V.


In the general formula (1), a is in the range of 5.70≤a≤6.30, b is in the range of 1.90≤b≤2.10, c is in the range of 7.20≤c≤8.80, and d is in the range of 27.45≤d≤32.50.


In the case where the dielectric ceramic composition according to the second embodiment of the present invention includes Sn, the content ratio of the oxide of Sn in terms of SnO2 relative to total number of moles of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 is 15.00 mol % or less. In the case where the dielectric ceramic composition according to the second embodiment of the present invention includes V, the content ratio of the oxide of V in terms of V2O5 relative to total number of moles of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 is 7.50 mol % or less.


The dielectric ceramic composition according to the second embodiment of the present invention includes at least the (a) component, that is, the oxide of Mn and the (b) component, that is, the oxide of Cu, the oxide of Ru, or the oxide of Cu and the oxide of Ru as the second component. In other words, the dielectric ceramic composition according to the second embodiment of the present invention includes the oxide of Mn and one or both of the oxide of Cu and the oxide of Ru as the essential second component.


In the dielectric ceramic composition according to the second embodiment of the present invention, the content of the oxide of Mn is 0.005% by mass to 3.500% by mass, preferably 0.005% by mass to 2.000% by mass, and particularly preferably 0.010% by mass to 1.500% by mass in terms of MnO relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


In the case where the dielectric ceramic composition according to the second embodiment of the present invention includes the oxide of Cu as the second component, the content of the oxide of Cu is preferably 0.010% by mass or more and less than 0.080% by mass, particularly preferably 0.020% by mass or more and less than 0.080% by mass, and more preferably 0.030% by mass or more and less than 0.080% by mass in terms of CuO relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


In the case where the dielectric ceramic composition according to the second embodiment of the present invention includes the oxide of Ru as the second component, the content of the oxide of Ru is preferably 0.050% by mass or more and less than 0.300% by mass, particularly preferably 0.100% by mass or more and less than 0.300% by mass, and more preferably 0.200% by mass or more and less than 0.300% by mass in terms of RuO2 relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


The dielectric ceramic composition according to the second embodiment of the present invention includes the (a) component, that is, the oxide of Mn having the above content as the second component, whereby in the case where the dielectric ceramic composition is used as a dielectric layer of the ceramic electronic components such as a laminated ceramic capacitor, the change in the electrostatic capacity is small even in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses (tan δ) at 25° C. and 200° C. are small.


The dielectric ceramic composition according to the second embodiment of the present invention, in which the content of the first component is determined to be the above content and the oxide of Mn is included in the above content as the second component, exhibits the effects in which the change in the electrostatic capacity is small in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses (tan δ) at 25° C. and 200° C. are small. In addition, the dielectric ceramic composition according to the second embodiment of the present invention, in which one or both of the oxide of Cu and the oxide of Ru are included as the second component, can provide the high insulation resistance value without significantly affecting the effects caused by determining the content of the first component to be the above content and including the oxide of Mn in the above content as the second component, that is, the effects in which the change in the electrostatic capacity is small in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses at 25° C. and 200° C. are small.


The dielectric ceramic composition according to the second embodiment of the present invention includes (a) the oxide of Mn and (b) any one or both of the oxide of Cu and the oxide of Ru and, in addition to the above components, the oxides (hereinafter, also described as a (c) component) other than the oxides of the (a) component and the (b) component may be optionally included as the second component. The second component is added to the dielectric ceramic composition according to the present invention for the purpose of improving the reduction resistance and other properties. The total mass of the second component other than the (b) component in terms of the oxides (that is, the total mass of the (a) component and the (c) component) is preferably 10.000% by mass or less and particularly preferably 0.100% by mass to 5.500% by mass relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


The optional component of the second component included in the dielectric ceramic composition according to the second embodiment of the present invention is preferably the oxides of D (D is at least one element selected from Li, Mg, Si, Cr, Al, Fe, Co, Ni, Zn, Ga, Ge, In, W, Mo, Y, Hf, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) and the oxide of Mg, the oxide of Si, and the oxide of Y are particularly preferable.


The mass of the oxide of D is a converted value of Li in terms of Li2O, Mg in terms of MgO, Si in terms of SiO2, Cr in terms of Cr2O3, Al in terms of Al2O3, Fe in terms of Fe2O3, Co in terms of CoO, Ni in terms of NiO, Zn in terms of ZnO, Ga in terms of Ga2O3, Ge in terms of GeO2, In in terms of In2O3, Win terms of WO3, Mo in terms of MoO3, Yin terms of Y2O3, Hf in terms of HfO2, La in terms of La2O3, Ce in terms of CeO2, Pr in terms of Pr6O11, Nd in terms of Nd2O3, Sm in terms of Sm2O3, Eu in terms of Eu2O3, Gd in terms of Gd2O3, Tb in terms of Tb4O7, Dy in terms of Dy2O3, Ho in terms of Ho2O3, Er in terms of Er2O3, Tm in terms of Tm2O3, Yb in terms of Yb2O3, or Lu in terms of Lu2O3.


The dielectric ceramic composition according to the second embodiment of the present invention exhibits existence of the tungsten bronze type crystal phase when crystal structure analysis such as X-ray diffraction is performed. The average grain size thereof is preferably 5 or less and particularly preferably 3 μm or less.


The dielectric ceramic composition according to the third embodiment of the present invention includes the first component and the second component, in which


a compound represented by a following general formula (3):





α·Caη1M3θ1M4ϕ1-β·Srη2M3θ2M4ϕ2Oω2-γ·Baη3M3θ3M4ϕ3Oω3  (3)


(in the formula (3), η1, η2, and η3 are each independently values within a range of 5.70 to 6.30; θ1, θ2, and θ3 are each independently values within a range of 0.95 to 1.05; ϕ1, ϕ2, and ϕ3 are each independently values within a range of 0.90 to 1.10; ω1, ω2, and ω3 are each independently values within a range of 27.45 to 32.50; M3 is represented by a general formula (4):





Ti2-ρ-σZrρSnσ  (4)


(in the formula (4), 0≤p≤2.0 and 0≤σ≤0.3); M4 is represented by a general formula (5):





Nb8-π-ψTaπVψ  (5)


(in the formula (5), 0≤π≤8.0 and 0≤ψ≤0.6); and α, β, and γ satisfy α+β+γ=1.00), and when an arbitrary point in a ternary composition diagram is represented as (α, β, γ), the compound existing within a range surrounded by line segments linking a point A=(0.05, 0.95, 0.00), a point B=(0.70, 0.30, 0.00), a point C=(0.70, 0.00, 0.30), a point D=(0.00, 0.00, 1.00), and a point E=(0.00, 0.90, 0.10) is included as the first component; and


as a content ratio relative to a total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5, the second component comprises at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass in terms of MnO and (b) one or both of an oxide of Cu and an oxide of Ru.


The dielectric ceramic composition according to the third embodiment of the present invention includes the first component and the second component. In the dielectric ceramic composition according to the third embodiment of the present invention, among oxides included in the dielectric ceramic composition, all oxides other than the oxides included as the first component are included as the second component.


The first component of the dielectric ceramic composition according to the third embodiment of the present invention is a compound existing within the range surrounded by line segments linking a point A=(0.05, 0.95, 0.00), a point B=(0.70, 0.30, 0.00), a point C=(0.70, 0.00, 0.30), a point D=(0.00, 0.00, 1.00), and a point E=(0.00, 0.90, 0.10) (hereinafter, may also be described as a compound existing within the range surrounded by line segments linking the point A, the point B, the point C, the point D, and the point E on the ternary composition diagram illustrated in FIG. 1) when a point on the ternary composition diagram of Caη1M3θ1M4ϕ1Oω1-Srη2M3θ2M4ϕ2Oω2-Baη3M3θ3M4ϕ3Oω3 illustrated in FIG. 1 is represented by (α, β, γ) (here, α, β, and γ satisfy α+β+γ=1.00). The first component having the composition existing within the above range allows the relative dielectric constant at 25° C. to be 100.0 or more and thus exhibits ferroelectricity.


The first component of the dielectric ceramic composition according to the third embodiment of the present invention is preferably a compound existing within the range surrounded by line segments linking a point A′=(0.05, 0.95, 0.00), a point B′=(0.60, 0.40, 0.00), a point C′=(0.70, 0.20, 0.10), a point D′=(0.70, 0.10, 0.20), a point E′=(0.55, 0.00, 0.45), a point F′=(0.40, 0.00, 0.60), a point G′=(0.10, 0.10, 0.80), a point H′=(0.00, 0.00, 1.00), a point I′=(0.00, 0.40, 0.60) a point J′=(0.20, 0.40, 0.40), a point K′=(0.00, 0.70, 0.30), and a point L′=(0.00, 0.90, 0.10) (hereinafter, may also be described as a compound existing within the range surrounded by line segments linking the point A′, the point B′, the point C′, the point D′, the point E′, the point F′, the point G′, the point H′, the point I′, the point J′, the point K′, and the point L′ on the ternary composition diagram illustrated in FIG. 2) on the ternary composition diagram of Caη1M3θ1M4ϕ1Oω1-Srη2M3θ2M4ϕ2Oω2-Baη3M3θ3M4ϕ3Oω3 illustrated in FIG. 2. The first component having the composition existing within the above range is likely to provide the relative dielectric constant at 25° C. of 200 or more and thus exhibits ferroelectricity. The ternary composition diagram of “Caη1M3θ1M4ϕ1Oω1-Srη2M3θ2M4ϕ2Oω2-Baη3M3θ3M4ϕ3Oω3” illustrated in FIG. 2 is the same diagram as the ternary composition diagram of “Caη1M3θ1M4ϕ1Oω1-Srη2M3θ2M4ϕ2Oω2-Baη3M3θ3M4ϕ3Oω3” illustrated in FIG. 1.


Here, in the ternary composition diagram of “Caη1M3θ1M4ϕ1Oω1-Srη2M3θ2M4ϕ2Oω2-Baη3M3θ3M4ϕ3Oω3” according to the dielectric ceramic composition of the third embodiment of the present invention, η1, η2, and η3 are each independently values within the range of 5.70 to 6.30. θ1, θ2, and θ3 are each independently values within the range of 0.95 to 1.05. ω1, ω2, and ω3 are each independently values within the range of 0.90 to 1.10. ω1, ω2, and ω3 are each independently values within the range of 27.45 to 32.50. M3 is a general formula (4):





Ti2-ρ-σZrρSnσ  (4)


(in the formula (4), 0≤ρ≤2.0 and 0≤σ≤0.3). M4 is a general formula (5):





Nb8-π-ψTaπVψ  (5)


(in the formula (5), 0≤π≤8.0 and 0≤ψ≤0.6).


The dielectric ceramic composition according to the third embodiment of the present invention includes at least the (a) component, that is, the oxide of Mn and the (b) component, that is, the oxide of Cu, the oxide of Ru, or the oxide of Cu and the oxide of Ru as the second component. In other words, the dielectric ceramic composition according to the third embodiment of the present invention includes the oxide of Mn and one or both of the oxide of Cu and the oxide of Ru as the essential second component.


In the dielectric ceramic composition according to the third embodiment of the present invention, the content of the oxide of Mn is 0.005% by mass to 3.500% by mass, preferably 0.005% by mass to 2.000% by mass, and particularly preferably 0.010% by mass to 1.500% by mass in terms of MnO relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


In the case where the dielectric ceramic composition according to the third embodiment of the present invention includes the oxide of Cu as the second component, the content of the oxide of Cu is preferably 0.010% by mass or more and less than 0.080% by mass, particularly preferably 0.020% by mass or more and less than 0.080% by mass, and more preferably 0.030% by mass or more and less than 0.080% by mass in terms of CuO relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


In the case where the dielectric ceramic composition according to the third embodiment of the present invention includes the oxide of Ru as the second component, the content of the oxide of Ru is preferably 0.050% by mass or more and less than 0.300% by mass, particularly preferably 0.100% by mass or more and less than 0.300% by mass, and more preferably 0.200% by mass or more and less than 0.300% by mass in terms of RuO2 relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


The dielectric ceramic composition according to the third embodiment of the present invention includes the (a) component, that is, the oxide of Mn having the above content as the second component, whereby in the case where the dielectric ceramic composition is used as a dielectric layer of the ceramic electronic components such as a laminated ceramic capacitor, the change in the electrostatic capacity is small even in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses (tan δ) at 25° C. and 200° C. are small.


The dielectric ceramic composition according to the third embodiment of the present invention, in which the content of the first component is determined to be the above content and the oxide of Mn is included in the above content as the second component, exhibits the effects in which the change in the electrostatic capacity is small in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses (tan δ) at 25° C. and 200° C. are small. In addition, the dielectric ceramic composition according to the third embodiment of the present invention, in which one or both of the oxide of Cu and the oxide of Ru are included as the second component, can provide the high insulation resistance value under a high temperature environment without significantly affecting the effects caused by determining the content of the first component to be the above content and including the oxide of Mn in the above content as the second component, that is, the effects in which the change in the electrostatic capacity is small in a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity is within ±50.0% in a temperature range of −55° C. to 200° C., and the dielectric losses at 25° C. and 200° C. are small.


The dielectric ceramic composition according to the third embodiment of the present invention includes (a) the oxide of Mn and (b) any one or both of the oxide of Cu and the oxide of Ru and, in addition to the above components, the oxides (hereinafter, also described as a (c) component) other than the (a) component and the (b) component may be optionally included as the second component. The second component is added to the dielectric ceramic composition according to the present invention for the purpose of improving the reduction resistance and other properties. The total mass of the second component other than the (b) component in terms of the oxides (that is, the total mass of the (a) component and the (c) component) is preferably 10.000% by mass or less and particularly preferably 0.100% by mass to 5.500% by mass relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5.


The optional component of the second component included in the dielectric ceramic composition according to the third embodiment of the present invention is preferably the oxides of D (D is at least one element selected from Li, Mg, Si, Cr, Al, Fe, Co, Ni, Zn, Ga, Ge, In, W, Mo, Y, Hf, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) and the oxide of Mg, the oxide of Si, and the oxide of Y are particularly preferable.


The mass of the oxide of D is a converted value of Li in terms of Li2O, Mg in terms of MgO, Si in terms of SiO2, Cr in terms of Cr2O3, Al in terms of Al2O3, Fe in terms of Fe2O3, Co in terms of CoO, Ni in terms of NiO, Zn in terms of ZnO, Ga in terms of Ga2O3, Ge in terms of GeO2, In in terms of In2O3, Win terms of WO3, Mo in terms of MoO3, Yin terms of Y2O3, Hf in terms of HfO2, La in terms of La2O3, Ce in terms of CeO2, Pr in terms of Pr6O11, Nd in terms of Nd2O3, Sm in terms of Sm2O3, Eu in terms of Eu2O3, Gd in terms of Gd2O3, Tb in terms of Tb4O7, Dy in terms of Dy2O3, Ho in terms of Ho2O3, Er in terms of Er2O3, Tm in terms of Tm2O3, Yb in terms of Yb2O3, or Lu in terms of Lu2O3.


The dielectric ceramic composition according to the third embodiment of the present invention exhibits existence of the tungsten bronze type crystal phase when crystal structure analysis such as X-ray diffraction is performed. The average grain size thereof is preferably 5 μm or less and particularly preferably 3 μm or less.


In the dielectric ceramic composition according to the first embodiment of the present invention, the dielectric ceramic composition according to the second embodiment of the present invention, and the dielectric ceramic composition according to the third embodiment of the present invention, as the relative dielectric constant at 25° C. becomes higher, the dielectric ceramic composition becomes more preferable. The relative dielectric constant is 100.0 or more and preferably 200.0 or more, and depending on the composition, preferably 300.0 or more, further preferably 400.0 or more, and further preferably 500.0 or more.


In the dielectric ceramic composition according to the first embodiment of the present invention, the dielectric ceramic composition according to the second embodiment of the present invention, and the dielectric ceramic composition according to the third embodiment of the present invention, the change rate of the electrostatic capacity is within ±50.0% and preferably within the range of −33.0% to 22.0% in the temperature range of −55° C. to 200° C. In the present invention, the change rate of the electrostatic capacity refers to a value obtained by the method described below.


In the dielectric ceramic composition according to the first embodiment of the present invention, the dielectric ceramic composition according to the second embodiment of the present invention, and the dielectric ceramic composition according to the third embodiment of the present invention, the dielectric loss (tan δ) at 25° C. is 10.0% or less and the dielectric loss (tan δ) at 200° C. is 10.0% or less, which provides excellent high-frequency properties.


In the dielectric ceramic composition according to the first embodiment of the present invention, the dielectric ceramic composition according to the second embodiment of the present invention, and the dielectric ceramic composition according to the third embodiment of the present invention, the insulation resistance value at 200° C. is preferably 40 MΩ or more, and in particular, the insulation resistance value at 200° C. is preferably 40 MΩ or more and less than 100 MΩ.


In the dielectric ceramic composition according to the first embodiment of the present invention, the dielectric ceramic composition according to the second embodiment of the present invention, and the dielectric ceramic composition according to the third embodiment of the present invention, change in electrostatic capacity is small even under a high temperature condition of 150° C. to 200° C. and the change rate of the electrostatic capacity is within a range of −50.0% to 50.0%, preferably within a range of −33.0% to 22.0%, and particularly preferably −20.0% to 5.0% in a temperature range of −55° C. to 200° C. The dielectric ceramic composition according to the present invention is suitable for the electronic components for which the high insulation resistance value is required in addition to the small dielectric losses at 25° C. to 200° C.


The dielectric ceramic composition according to the first embodiment of the present invention, the dielectric ceramic composition according to the second embodiment of the present invention, and the dielectric ceramic composition according to the third embodiment of the present invention can be fired under a reducing atmosphere.


(External Electrode 4)


The external electrode 4 is formed by applying a conductive paste for the external electrode to the edge after the laminated body 10 is co-fired and firing the applied paste. The present invention, however, is not limited thereto. The external electrode 4 may also be formed by heat treatment using a paste including a thermosetting resin or a thermoplastic resin. The conductive component used for the conductive paste for the external electrode is not particularly limited. For example, pure metals such as nickel, copper, silver, palladium, platinum, and gold and, in addition to these metals, alloys, mixtures, or composites including these metal components may be used. As other additives, glass frit may be added to the conductive paste, if necessary. The external electrode 4 may also be co-fired together with the laminated body 10.


(Method for Producing Ceramic Capacitor 1)


The ceramic capacitor 1 is produced by known methods except using the dielectric ceramic composition according to the first embodiment of the present invention, the dielectric ceramic composition according to the second embodiment of the present invention, or the dielectric ceramic composition according to the third embodiment of the present invention. Hereinafter, one example will be described.


First, starting materials for forming the dielectric layer 3 are provided. Examples of the starting materials include oxides such as CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5, and carbonates and nitrates, or the like, which generate these oxides by firing.


These starting materials are weighed so as to be a target composition and mixed. The obtained mixture was calcinated at a temperature of about 700° C. to about 900° C. for about 3 hours to about 6 hours in the air. Subsequently, the obtained product is finely pulverized and the obtained dielectric raw material is used as the raw material for the first component.


In addition, a Mn compound such as MnO and MnCO3 as a Mn source, a Cu compound such as CuO, Cu2O, Cu(NO3)2, Cu(OH)2, and CuCO3 as a Cu source in the case where the oxide of Cu is included as the second component, a Ru compound such as RuO2, RuO4, Ru3(CO)12 as a Ru source in the case where the oxide of Ru is included as the second component, and compounds including Li, Mg, Si, Cr, Al, Fe, Co, Ni, Zn, Ga, Ge, In, W, Mo, Y, Hf, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu or the like, to be added, if necessary, are provided as a raw material for the second component.


Subsequently, the raw materials for the first component and the raw materials for the second component are kneaded and dispersed in an appropriate binder component to prepare a dielectric paste or a dielectric slurry. In the dielectric paste or the dielectric slurry, additives such as a plasticizer may be included, if necessary.


Subsequently, the obtained dielectric paste or dielectric slurry is formed into a sheet-like shape. Subsequently, a conductor pattern is formed using the conductive paste for the internal electrode described above on the surface of the obtained green sheet. This operation is repeated predetermined times to stack the sheets, which are pressed to be consolidated to yield an unfired laminated body (hereinafter, this laminated body is referred to as a green chip).


Subsequently, debinding is performed on the green chip, if necessary. The conditions for the debinding are not particularly limited. Examples of the conditions include heat treatment at a retention temperature of 180° C. to 400° C. for 1 hour to 3 hours.


Subsequently, the green chip is fired at about 1,150° C. to about 1,350° C. under a reducing atmosphere to provide a fired laminated body 10 (hereinafter, referred to as a sintered compact 10).


Thereafter, the sintered compact 10 is subjected to re-oxidation treatment (hereinafter, referred to as annealing), if necessary. The annealing conditions may be known conditions widely used in the art. For example, oxygen partial pressure at the time of annealing is preferably set to higher oxygen partial pressure than the oxygen partial pressure at the time of firing and the holding temperature is preferably set to 1,100° C. or less.


The sintered compact 10 obtained as described above is subjected to end polishing and thereafter the conductive paste for the external electrode is applied. The applied paste is fired to form the external electrode 4. The above-described plating layer is formed on the surface of the external electrode 4, if necessary.


Thus obtained ceramic capacitor 1 is implemented on, for example, a printed circuit board by, for example, soldering and used for various electronic devices and the like.


As described above, the embodiments of the present invention have described. The present invention, however, is not limited to the above-described embodiments at all and is used for various applications without departing from the scope of the present invention.


For example, although the ceramic capacitor has been described in the above description, the present invention is applicable for other ceramic electronic components such as an inductor and an actuator.


Hereinafter, the present invention will be described with reference to specific experimental examples. However, the present invention in not limited thereto. The compositions of the dielectric ceramic composition described below is presumed by the raw material composition (feed composition) and crystal structure analysis. The same applies in the present specification.


EXAMPLE

First, confirmation tests for determination of the content of the first component and the effect of addition of the oxide of Mn were conducted (Reference Samples 1 to 90 and Reference Samples 91 to 107).


Reference Example 1

(1) Preparation of Reference Samples 1 to 90 of Dielectric Ceramic Composition


As the starting materials of the first component, each powder of CaCO3, SrCO3, BaCO3, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5 was weighed so that the ratio of each powder in terms of the oxide was as listed in Table 1, Table 3, and Table 5 and the resultant mixture was wet-blended for 20 hours with pure water using a ball mill.


Subsequently, each of the blends was dried at 100° C. and thereafter calcinated at 750° C. to 900° C. for 3 hours in the air. The obtained product was similarly finely pulverized again with the ball mill to prepare the dielectric raw material for the first component.


As the second component, a mixture made by weighing and mixing 18.2 mg of MnCO3, 32 mg of MgO, 58.6 mg of SiO2, and 89.5 mg Y2O3 was provided and the mixture was used as the raw material for second component. Here, in Reference Sample 43, only three components of MnCO3, MgO, and Y2O3 excluding SiO2 were used as the raw materials for the second component. In Reference Sample 44, only three components of MnCO3, SiO2, and Y2O3 excluding MgO were used as the raw materials for the second component. In Reference Sample 45, only three components of MnCO3, MgO, and SiO2 excluding Y2O3 were used. In Reference Samples 78 and 79, only three components of MgO, SiO2, and Y2O3 excluding MnCO3 were used. Of the raw material for the second component, the amount of MnCO3 was changed to 0.404 mg in Reference Sample 41, the amount of MnCO3 was changed to 0.198 g in Reference Sample 42, and the amount of MnCO3 was changed to 2.055 g in Reference Sample 80.


A poly(vinyl alcohol) aqueous solution was prepared by charging ion-exchanged water and polyvinyl alcohol in a container so that the polyvinyl alcohol concentration was 6% by mass and mixing the resultant mixture at 90° C. for 1 hour.


Then, 25 g of each of the dielectric raw materials for the first component and the raw material for the second component having the above-described amount were mixed. The polyvinyl alcohol aqueous solution was added to the raw material mixture so that the concentration of the polyvinyl alcohol aqueous solution was 10% by mass relative to the resultant mixture and the resultant product was mixed and granulated in a mortar to prepare a granulated powder.


Furthermore, the obtained granulated powder was charged in a mold having a diameter of 14.0 mm and press-molded at a pressure of 1 ton/cm2 to provide a disk-shaped green compact.


Subsequently, the obtained green compact was fired in a reducing atmosphere to prepare a sintered compact. In this firing, the temperature increasing rate, the holding temperature, and the holding time were set to 300° C./h, 1,150° C. to 1,300° C., and two hours, respectively. As an atmosphere gas, moistened hydrogen/nitrogen mixture gas (hydrogen concentration 0.5%) was used and a wetter (wetter temperature 35° C.) was used for the moistening.


Subsequently, with respect to the obtained sintered compact, In—Ga electrodes having a diameter of 8 mm were applied to the two main surfaces of the sintered compact to provide a disk-shaped ceramic capacitor of respective Reference Samples 1 to 90.


(2) Analysis of Reference Samples 1 to 90 of Dielectric Ceramic Composition


With respect to the disk-shaped ceramic capacitors of corresponding Reference Samples 1 to 90 obtained as described above, each of the grain size, the crystal phase, the relative dielectric constant, the change rate of the electrostatic capacity, and the dielectric loss (tan δ) was analyzed. The results are listed in Table 2, Table 4, and Table 6.


<Grain Size>


The surface of each of the capacitor was observed using a scanning electron microscope (SEM). The average value of equivalent circle diameters determined from grain boundaries of randomly selected 20 crystal grains was determined to be the grain size. FIG. 3, FIG. 4, and FIG. 5 are SEM images of Reference Samples 8, 15, and 66, respectively.


<Crystal Phase>


The crystal phase was specified by X-ray diffraction measurement. As a representative example, the result of the X-ray diffraction measurement of Reference Sample 15 is illustrated in FIG. 9. The lower chart in FIG. 9 is a tungsten bronze type crystal phase serving as a reference and Reference Sample 15 was confirmed to include the tungsten bronze type crystal phase. The X-ray measurement results including other samples are listed in Table 2, Table 4, and Table 6. The sign “T” in the tables indicates that the existence of the tungsten bronze type crystal phase was confirmed.


<Relative Dielectric Constant>


With respect to each of the capacitors, an electrostatic capacity C was measured at a reference temperature of 25° C. using an LCR meter (4284A, manufactured by Agilent Technologies, Inc.) at a frequency of 1 kHz and a measurement voltage of 1 Vrms. Thereafter, the relative dielectric constant was calculated based on the thickness of the sintered compact, the effective electrode area, and the electrostatic capacity C obtained by the measurement result. The relative dielectric constant at a reference temperature of 200° C. was also calculated by the same manner.


A higher relative dielectric constant is preferable and thus the capacitor having a relative dielectric constant of 100.0 or more at 25° C. is determined to be excellent.


<Change Rate in Electrostatic Capacity>


The electrostatic capacity Ct at each temperature t in the temperature region of −55° C. to 200° C. was measured in the same conditions as the conditions of the relative dielectric constant measurement (4284A, manufactured by Agilent Technologies, Inc., frequency 1 kHz, and measurement voltage 1 Vrms). The change rate of the electrostatic capacity=((Ct−C25)/C25)×100(%) (hereinafter, the change rate of the electrostatic capacity may be described as ΔCt/C25) was calculated from the electrostatic capacity C25 at 25° C. used as the reference.


The change rate of the electrostatic capacity is preferably closer to 0 and is determined to be excellent when the change rate of the electrostatic capacity is within ±50.0%.


With respect to Reference Samples 8, 15, and 66, the trends of the change rate of the electrostatic capacity from −55° C. to 200° C. is illustrated in FIG. 6. In FIG. 6, the signs “x (cross)”, “◯ (circle)”, and “Δ (triangle)” refer to the change rate of the electrostatic capacities of Reference Sample 8, Reference Sample 15, and Reference Sample 66, respectively. With respect to Reference Samples 15 and 78, the trends of the change rate of the electrostatic capacity from −55° C. to 200° C. is illustrated in FIG. 7. In FIG. 7, the signs “◯ (circle)” and “Δ (tringle)” refer to the change rate of the electrostatic capacities of Reference Sample 15 and Reference Sample 78, respectively.


<Dielectric Loss (Tan δ)>


With respect to each of the capacitor samples, tan δ was measured using an LCR meter (4284A, manufactured by Agilent Technologies, Inc.) at a frequency of 1 kHz and a measurement voltage of 1 Vrms. At 25° C. and 200° C., tan δ is determined to be excellent when both of tan δ are 10.0% or less.











TABLE 1









Second component composition



in terms of oxides



[% by mass]









Total



content













First component composition in terms

Oxide

of


Sample
of oxides [mol %]
Dielectric ceramic
component
MnO
second




















name
CaO
SrO
BaO
TiO2
ZrO2
SnO2
Nb2O5
Ta2O5
V2O5
composition
species
content
component























Reference
33.33
0.00
16.67
16.67
0.00
0.00
33.33
0.00
0.00
Ca4Ba2Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 1










Si, Y


Reference
25.00
0.00
25.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca3Ba3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 2










Si, Y


Reference
16.67
0.00
33.33
16.67
0.00
0.00
33.33
0.00
0.00
Ca2Ba4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 3










Si, Y


Reference
4.17
0.00
45.83
16.67
0.00
0.00
33.33
0.00
0.00
Ca0.5Ba5.5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 4










Si, Y


Reference
0.00
0.00
50.00
16.67
0.00
0.00
33.33
0.00
0.00
Ba6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 5










Si, Y


Reference
16.67
8.33
25.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca2SrBa3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 6










Si, Y


Reference
0.00
8.33
41.67
16.67
0.00
0.00
33.33
0.00
0.00
SrBa5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 7










Si, Y


Reference
16.67
16.67
16.67
16.67
0.00
0.00
33.33
0.00
0.00
Ca2Sr2Ba2Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 8










Si, Y


Reference
7.33
21.33
21.33
16.67
0.00
0.00
33.33
0.00
0.00
Ca0.8Sr2.6Ba2.6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 9










Si, Y


Reference
0.00
25.00
25.00
16.67
0.00
0.00
33.33
0.00
0.00
Sr3Ba3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 10










Si, Y


Reference
33.33
16.67
0.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca4Sr2Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 11










Si, Y


Reference
8.33
33.33
8.33
16.67
0.00
0.00
33.33
0.00
0.00
CaSr4BaTi2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 12










Si, Y


Reference
0.00
37.50
12.50
16.67
0.00
0.00
33.33
0.00
0.00
Sr4.5Ba1.5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 13










Si, Y


Reference
8.33
41.67
0.00
16.67
0.00
0.00
33.33
0.00
0.00
CaSr5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 14










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca2Sr4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 15










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
32.50
0.80
0.00
Ca2Sr4Ti2Nb7.8Ta0.2O30
Mg, Mn,
0.0448
0.765


Sample 16










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
26.60
6.70
0.00
Ca2Sr4Ti2Nb6.4Ta1.6O30
Mg, Mn,
0.0448
0.765


Sample 17










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
20.00
13.33
0.00
Ca2Sr4Ti2Nb4.8Ta3.2O30
Mg, Mn,
0.0448
0.765


Sample 18










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
13.33
20.00
0.00
Ca2Sr4Ti2Nb3.2Ta4.8O30
Mg, Mn,
0.0448
0.765


Sample 19










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
6.67
26.67
0.00
Ca2Sr4Ti2Nb1.6Ta6.4O30
Mg, Mn,
0.0448
0.765


Sample 20










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
0.00
33.33
0.00
Ca2Sr4Ti2Ta8O30
Mg, Mn,
0.0448
0.765


Sample 21










Si, Y


Reference
16.67
33.33
0.00
15.00
1.67
0.00
33.33
0.00
0.00
Ca2Sr4Ti1.8Zr0.2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 22










Si, Y


Reference
16.67
33.33
0.00
13.33
3.33
0.00
33.33
0.00
0.00
Ca2Sr4Ti1.6Zr0.4Nb8O30
Mg, Mn,
0.0448
0.765


Sample 23










Si, Y


Reference
16.67
33.33
0.00
11.67
5.00
0.00
33.33
0.00
0.00
Ca2Sr4Ti1.4Zr0.6Nb8O30
Mg, Mn,
0.0448
0.765


Sample 24










Si, Y


Reference
16.67
33.33
0.00
10.00
6.67
0.00
33.33
0.00
0.00
Ca2Sr4Ti1.2Zr0.8Nb8O30
Mg, Mn,
0.0448
0.765


Sample 25










Si, Y


Reference
16.67
33.33
0.00
6.67
10.00
0.00
33.33
0.00
0.00
Ca2Sr4Ti0.8Zr1.2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 26










Si, Y


Reference
16.67
33.33
0.00
3.33
13.33
0.00
33.33
0.00
0.00
Ca2Sr4Ti0.4Zr1.6Nb8O30
Mg, Mn,
0.0448
0.765


Sample 27










Si, Y


Reference
16.67
33.33
0.00
0.00
16.67
0.00
33.33
0.00
0.00
Ca2Sr4Zr2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 28










Si, Y


Reference
16.67
33.33
0.00
16.50
0.00
0.17
33.33
0.00
0.00
Ca2Sr4Ti1.98Sn0.02Nb8O30
Mg, Mn,
0.0448
0.765


Sample 29










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.00
0.00
0.33
Ca2Sr4Ti2Nb7.96V0.04O30
Mg, Mn,
0.0448
0.765


Sample 30










Si, Y









In Table 1, Table 3, and Table 5, the composition in terms of the oxide of the first component is represented by mol % of each of the oxides in terms of the oxides listed in the tables relative to the total number of moles of each of the oxide components of the first component in terms of the oxides listed in the tables. The content of the Mn oxide is represented by % by mass of the Mn oxide in terms of MnO relative to the total mass of each of the oxide components of the first component in terms of the oxides listed in the tables. The total content of the oxides of the second component is represented by % by mass of the total of the oxides of the second component relative to the total mass of each of the oxide components of the first component in terms of the oxide listed in the tables.












TABLE 2









Change rate in
















Relative dielectric
electrostatic capacity
tan δ


Sample
Crystal
Grain size
constant
[%]
[%]















name
phase
[μm]
25° C.
200° C.
−55° C.
200° C.
25° C.
200° C.


















Reference
T
1.4
101.1
104.2
−17.2
3.1
3.9
7.4


Sample 1


Reference
T
0.8
214.2
252.1
−15.8
17.7
3.2
6.8


Sample 2


Reference
T
1.1
157.7
135.4
−15.4
−14.2
4.7
7.2


Sample 3


Reference
T
0.9
116.8
134.6
−9.6
15.2
3.7
7.8


Sample 4


Reference
T
0.9
992.6
637.6
−29.3
35.8
1.8
8.5


Sample 5


Reference
T
1.9
464.4
652.5
−30.0
40.5
2.6
4.5


Sample 6


Reference
T
1.8
249.4
202.2
9.8
−18.9
1.4
2.4


Sample 7


Reference
T
1.4
743.5
825.8
−23.9
11.1
2.2
8.8


Sample 8


Reference
T
0.8
146.0
153.5
7.9
5.2
1.7
3.7


Sample 9


Reference
T
0.9
141.4
131.0
−5.0
−7.4
5.6
8.5


Sample 10


Reference
T
0.8
116.3
112.5
2.3
16.0
3.3
6.8


Sample 11


Reference
T
1.9
567.9
591.3
−17.0
4.1
2.3
4.0


Sample 12


Reference
T
0.9
242.0
270.9
−30.8
21.8
2.4
8.6


Sample 13


Reference
T
2.0
464.8
567.6
−8.6
22.1
2.8
8.1


Sample 14


Reference
T
1.7
816.0
1,051.4
−12.3
28.9
3.0
0.8


Sample 15


Reference
T
2.5
437.6
525.3
−15.7
20.0
2.7
6.7


Sample 16


Reference
T
1.8
875.3
674.3
−16.4
−23.0
0.9
1.1


Sample 17


Reference
T
1.0
663.1
474.4
−7.4
−28.4
1.8
1.4


Sample 18


Reference
T
1.1
413.8
270.3
25.6
−34.7
0.2
1.6


Sample 19


Reference
T
1.4
315.8
229.2
34.5
−27.4
0.1
0.7


Sample 20


Reference
T
1.1
241.1
191.6
22.8
−20.5
0.3
0.9


Sample 21


Reference
T
2.9
495.6
607.4
−17.7
22.6
3.2
6.0


Sample 22


Reference
T
2.6
508.1
489.2
−17.5
−3.7
3.2
5.4


Sample 23


Reference
T
2.1
982.0
853.0
−23.1
−13.1
3.0
3.9


Sample 24


Reference
T
2.7
873.8
732.4
−16.6
−16.2
2.4
3.8


Sample 25


Reference
T
1.2
411.5
326.6
2.6
−20.6
1.1
2.8


Sample 26


Reference
T
1.6
832.5
691.9
−7.9
−16.9
0.9
3.5


Sample 27


Reference
T
1.2
320.9
247.3
1.9
−22.9
8.1
2.2


Sample 28


Reference
T
1.8
845.7
1,138.7
−23.9
34.6
3.2
2.8


Sample 29


Reference
T
2.0
882.3
1,192.6
−38.1
35.2
3.3
3.4


Sample 30

















TABLE 3








First component composition in terms of


Sample
oxides [mol %]
















name
CaO
SrO
BaO
TiO2
ZrO2
SnO2
Nb2O5
Ta2O5
V2O5





Reference
16.67
33.33
0.00
16.50
0.00
0.17
33.00
0.00
0.33


Sample 31


Reference
16.50
33.00
0.00
16.84
0.00
0.00
33.67
0.00
0.00


Sample 32


Reference
16.58
33.17
0.00
16.75
0.00
0.00
33.50
0.00
0.00


Sample 33


Reference
16.62
33.25
0.00
16.71
0.00
0.00
33.42
0.00
0.00


Sample 34


Reference
16.71
33.42
0.00
16.63
0.00
0.00
33.25
0.00
0.00


Sample 35


Reference
16.75
33.50
0.00
16.58
0.00
0.00
33.17
0.00
0.00


Sample 36


Reference
16.67
25.00
8.33
16.67
0.00
0.00
33.33
0.00
0.00


Sample 37


Reference
16.67
16.67
16.67
16.67
0.00
0.00
31.67
1.67
0.00


Sample 38


Reference
0.00
16.67
33.33
16.67
0.00
0.00
25.00
8.33
0.00


Sample 39


Reference
7.33
21.33
21.33
16.67
0.00
0.00
25.00
8.33
0.00


Sample 40


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 41


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 42


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 43


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 44


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 45


Reference
33.33
8.33
8.33
16.67
0.00
0.00
33.33
0.00
0.00


Sample 46


Reference
0.00
42.50
7.50
16.67
0.00
0.00
33.33
0.00
0.00


Sample 47


Reference
5.00
45.00
0.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 48


Reference
21.67
0.00
28.33
16.67
0.00
0.00
33.33
0.00
0.00


Sample 49


Reference
27.50
2.50
20.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 50


Reference
30.00
7.50
12.50
16.67
0.00
0.00
33.33
0.00
0.00


Sample 51


Reference
30.00
12.50
7.50
16.67
0.00
0.00
33.33
0.00
0.00


Sample 52


Reference
27.50
20.00
2.50
16.67
0.00
0.00
33.33
0.00
0.00


Sample 53


Reference
25.00
25.00
0.00
16.67
0.00
0.00
33.33
0.00
0.00


Sample 54


Reference
2.50
45.00
2.50
16.67
0.00
0.00
33.33
0.00
0.00


Sample 55


Reference
3.33
33.33
13.33
16.67
0.00
0.00
33.33
0.00
0.00


Sample 56


Reference
10.00
22.50
17.50
16.67
0.00
0.00
33.33
0.00
0.00


Sample 57


Reference
13.33
18.33
18.33
16.67
0.00
0.00
33.33
0.00
0.00


Sample 58


Reference
10.00
17.50
22.50
16.67
0.00
0.00
33.33
0.00
0.00


Sample 59


Reference
3.33
18.33
28.33
16.67
0.00
0.00
33.33
0.00
0.00


Sample 60
















Second component composition in





terms of oxides [% by mass]















Total






content




Oxide

of


Sample
Dielectric ceramic
component
MnO
second


name
composition
species
content
component





Reference
Ca2Sr4Ti1.98Sn0.02Nb7.96V0.04O30
Mg, Mn,
0.0448
0.765


Sample 31

Si, Y


Reference
Ca1.96Sr3.92Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 32

Si, Y


Reference
Ca1.98Sr3.96Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 33

Si, Y


Reference
Ca1.99Sr3.98Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 34

Si, Y


Reference
Ca2.01Sr4.02Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 35

Si, Y


Reference
Ca2.02Sr4.04Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 36

Si, Y


Reference
Ca2Sr3BaTi2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 37

Si, Y


Reference
Ca2Sr2BaTi2Nb7.6Ta0.4O30
Mg, Mn,
0.0448
0.765


Sample 38

Si, Y


Reference
Ca2Ba4Ti2Nb6Ta2O30
Mg, Mn,
0.0448
0.765


Sample 39

Si, Y


Reference
Ca0.8Sr2.6Ba2.6Ti2Nb6Ta2O30
Mg, Mn,
0.0448
0.765


Sample 40

Si, Y


Reference
Ca2Sr4Ti2Nb8O30
Mg, Mn,
0.0010
0.721


Sample 41

Si, Y


Reference
Ca2Sr4Ti2Nb8O30
Mg, Mn,
0.4873
1.213


Sample 42

Si, Y


Reference
Ca2Sr4Ti2Nb8O30
Mg, Mn,
0.0448
0.531


Sample 43

Y


Reference
Ca2Sr4Ti2Nb8O30
Mn, Si,
0.0448
0.637


Sample 44

Y


Reference
Ca2Sr4Ti2Nb8O30
Mg, Mn,
0.0448
0.407


Sample 45

Si


Reference
Ca4SrBaTi2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 46

Si, Y


Reference
Sr5.1Ba0.9Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 47

Si, Y


Reference
Ca0.6Sr5.4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 48

Si, Y


Reference
Ca2.6Ba3.4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 49

Si, Y


Reference
Ca3.3Sr0.3Ba2.4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 50

Si, Y


Reference
Ca3.6Sr0.9Ba1.5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 51

Si, Y


Reference
Ca3.6Sr1.5Ba0.9Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 52

Si, Y


Reference
Ca3.3Sr2.4Ba0.3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 53

Si, Y


Reference
Ca3Sr3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 54

Si, Y


Reference
Ca0.3Sr5.4Ba0.3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 55

Si, Y


Reference
Ca0.4Sr4Ba1.6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 56

Si, Y


Reference
Ca1.2Sr2.7Ba2.1Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 57

Si, Y


Reference
Ca1.6Sr2.2Ba2.2Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 58

Si, Y


Reference
Ca1.2Sr2.1Ba2.7Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 59

Si, Y


Reference
Ca0.4Sr2.2Ba3.4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 60

Si, Y



















TABLE 4









Change rate in
















Relative dielectric
electrostatic capacity
tan δ


Sample
Crystal
Grain size
constant
[%]
[%]















name
phase
[μm]
25° C.
200° C.
−55° C.
200° C.
25° C.
200° C.


















Reference
T
2.2
912.8
1,296.2
−43.3
42.0
3.6
4.8


Sample 31


Reference
T
1.8
551.8
734.6
−5.7
33.1
2.5
8.0


Sample 32


Reference
T
1.7
564.3
762.3
−6.0
35.1
2.6
7.4


Sample 33


Reference
T
1.8
532.9
730.5
−6.6
37.1
2.7
4.6


Sample 34


Reference
T
1.9
614.6
857.8
−5.7
39.6
2.4
6.0


Sample 35


Reference
T
1.8
596.3
822.6
−6.4
37.9
2.6
5.3


Sample 36


Reference
T
2.5
430.4
634.8
−14.4
47.5
1.9
6.8


Sample 37


Reference
T
0.9
637.1
707.6
−23.9
11.1
2.7
4.0


Sample 38


Reference
T
1.1
123.0
107.9
−15.3
−12.3
1.5
5.8


Sample 39


Reference
T
0.9
129.9
153.3
8.3
5.8
1.5
6.0


Sample 40


Reference
T
2.3
702.7
1,140.3
−5.7
42.3
2.3
8.6


Sample 41


Reference
T
2.6
200.4
206.2
−33.1
48.1
4.7
9.8


Sample 42


Reference
T
2.1
624.4
922.7
−3.9
47.8
2.1
6.8


Sample 43


Reference
T
2.3
630.8
1,161.1
−2.8
44.1
1.9
8.8


Sample 44


Reference
T
2.0
776.2
1,350.6
0.3
34.0
1.5
3.7


Sample 45


Reference
T
1.1
205.4
210.5
10.2
9.5
3.6
7.1


Sample 46


Reference
T
0.8
208.3
205.4
−21.9
10.6
2.6
8.9


Sample 47


Reference
T
2.1
294.8
397.6
−12.3
26.1
3.8
9.1


Sample 48


Reference
T
1.0
206.7
244.3
−13.4
−12.2
2.3
3.6


Sample 49


Reference
T
1.1
220.2
258.9
−12.9
13.7
2.1
3.1


Sample 50


Reference
T
1.3
231.4
270.1
−12.5
13.1
1.9
2.8


Sample 51


Reference
T
1.2
243.6
281.3
−11.4
12.8
1.7
2.5


Sample 52


Reference
T
0.9
201.3
206.5
−5.9
8.1
1.6
3.4


Sample 53


Reference
T
1.0
209.6
201.3
−6.6
−8.6
2.8
5.1


Sample 54


Reference
T
1.8
315.3
418.1
−10.5
20.2
3.2
8.1


Sample 55


Reference
T
1.4
401.4
435.2
−23.4
13.0
2.3
6.3


Sample 56


Reference
T
1.1
215.3
204.9
5.9
3.2
1.1
3.1


Sample 57


Reference
T
1.2
424.5
410.3
2.8
1.6
0.6
1.5


Sample 58


Reference
T
1.3
224.7
212.8
5.4
2.8
1.2
3.4


Sample 59


Reference
T
1.2
206.1
213.6
5.8
3.1
0.9
1.8


Sample 60


















TABLE 5









Second component composition in



terms of oxides [% by mass]









Total



content













First component composition in terms of

Oxide

of


Sample
oxides [mol %]
Dielectric ceramic
component
MnO
second




















name
CaO
SrO
BaO
TiO2
ZrO2
SnO2
Nb2O5
Ta2O5
V2O5
composition
species
content
component























Reference
0.00
17.50
32.50
16.67
0.00
0.00
33.33
0.00
0.00
Sr2.1Ba3.9Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 61










Si, Y


Reference
6.67
6.67
36.67
16.67
0.00
0.00
33.33
0.00
0.00
Ca0.8Sr0.8Ba4.4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 62










Si, Y


Reference
1.67
5.00
43.33
16.67
0.00
0.00
33.33
0.00
0.00
Ca0.2Sr0.6Ba5.2Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 63










Si, Y


Reference
17.50
2.50
30.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca2.1Sr0.3Ba3.6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 64










Si, Y


Reference
50.00
0.00
0.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 65










Si, Y


Reference
40.00
5.00
5.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca4.8Sr0.6Ba0.6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 66










Si, Y


Reference
0.00
50.00
0.00
16.67
0.00
0.00
33.33
0.00
0.00
Sr6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 67










Si, Y


Reference
0.00
0.00
50.00
0.00
0.00
0.00
50.00
0.00
0.00
BaNb2O6
Mg, Mn,
0.0448
0.765


Sample 68










Si, Y


Reference
0.00
50.00
0.00
0.00
0.00
0.00
50.00
0.00
0.00
SrNb2O6
Mg, Mn,
0.0448
0.765


Sample 69










Si, Y


Reference
50.00
0.00
0.00
0.00
0.00
0.00
50.00
0.00
0.00
CaNb2O6
Mg, Mn,
0.0448
0.765


Sample 70










Si, Y


Reference
0.00
0.00
48.28
17.24
0.00
0.00
34.48
0.00
0.00
Ba5.6Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 71










Si, Y


Reference
0.00
0.00
51.61
16.13
0.00
0.00
32.26
0.00
0.00
Ba6.4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 72










Si, Y


Reference
16.06
32.12
0.00
17.27
0.00
0.00
34.54
0.00
0.00
Ca1.86Sr3.72Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 73










Si, Y


Reference
17.12
34.41
0.00
16.16
0.00
0.00
32.31
0.00
0.00
Ca2.12Sr4.26Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 74










Si, Y


Reference
16.67
33.33
0.00
13.33
0.00
3.33
33.33
0.00
0.00
Ca2Sr4Ti1.6Sn0.4Nb8O30
Mg, Mn,
0.0448
0.765


Sample 75










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
30.00
0.00
3.33
Ca2Sr4Ti2Nb7.2V0.8O30
Mg, Mn,
0.0448
0.765


Sample 76










Si, Y


Reference
16.67
33.33
0.00
15.00
0.00
1.67
30.00
0.00
3.33
Ca2Sr4Ti1.8Sn0.2Nb7.2V0.8O30
Mg, Mn,
0.0448
0.765


Sample 77










Si, Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca2Sr4Ti2Nb8O30
Mg, Si,
0.0000
0.720


Sample 78










Y


Reference
16.67
16.67
16.67
16.67
0.00
0.00
33.33
0.00
0.00
Ca2Sr2Ba2Ti2Nb8O30
Mg, Si,
0.0000
0.720


Sample 79










Y


Reference
16.67
33.33
0.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca2Sr4Ti2Nb8O30
Mg, Mn,
5.0710
5.791


Sample 80










Si, Y


Reference
37.50
12.50
0.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca4.5Sr1.5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 81










Si, Y


Reference
37.50
0.00
12.50
16.67
0.00
0.00
33.33
0.00
0.00
Ca4.5Ba1.5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 82










Si, Y


Reference
0.00
47.50
2.50
16.67
0.00
0.00
33.33
0.00
0.00
Sr5.7Ba0.3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 83










Si, Y


Reference
36.67
6.67
6.67
16.67
0.00
0.00
33.33
0.00
0.00
Ca4.4Sr0.8Ba0.8Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 84










Si, Y


Reference
37.50
10.00
2.50
16.67
0.00
0.00
33.33
0.00
0.00
Ca4.5Sr1.2Ba0.3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 85










Si, Y


Reference
37.50
2.50
10.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca4.5Sr0.3Ba1.2Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 86










Si, Y


Reference
30.00
0.00
20.00
16.67
0.00
0.00
33.33
0.00
0.00
Ca3.6Ba2.4Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 87










Si, Y


Reference
6.67
1.67
41.67
16.67
0.00
0.00
33.33
0.00
0.00
Ca0.8Sr0.2Ba5Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 88










Si, Y


Reference
0.00
32.50
17.50
16.67
0.00
0.00
33.33
0.00
0.00
Sr3.9Ba2.1Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 89










Si, Y


Reference
0.00
22.50
27.50
16.67
0.00
0.00
33.33
0.00
0.00
Sr2.7Ba3.3Ti2Nb8O30
Mg, Mn,
0.0448
0.765


Sample 90










Si, Y



















TABLE 6









Change rate in
















Relative dielectric
electrostatic capacity
tan δ


Sample
Crystal
Grain size
constant
[%]
[%]















name
phase
[μm]
25° C.
200° C.
−55° C.
200° C.
25° C.
200° C.


















Reference
T
1.7
231.4
245.3
7.5
−16.4
1.1
2.1


Sample 61


Reference
T
1.8
238.2
215.4
12.6
−22.3
2.1
3.6


Sample 62


Reference
T
1.4
459.5
345.2
−19.7
26.5
1.5
4.4


Sample 63


Reference
T
1.5
311.1
394.4
−22.7
27.4
3.7
5.9


Sample 64


Reference
T
0.5
44.0
61.7
−18.9
40.3
5.1
10.9


Sample 65


Reference
T
0.6
135.1
244.5
−12.9
81.0
2.2
27.2


Sample 66


Reference
T
0.7
86.8
84.4
−12.9
−2.8
2.8
14.6


Sample 67


Reference
T
1.8
51.7
482.7
1.2
833.3
5.6
56.1


Sample 68


Reference
T
1.6
101.6
54.3
−52.2
−46.5
39.4
0.1


Sample 69


Reference
T
0.9
57.1
43.0
−24.6
−24.7
26.7
0.1


Sample 70


Reference
T
1.3
611.6
994.7
−6.6
62.6
2.1
18.8


Sample 71


Reference
T
1.2
715.3
997.4
−7.0
39.4
2.3
14.6


Sample 72


Reference
T
2.3
717.7
957.7
−6.2
33.4
2.5
11.7


Sample 73


Reference
T
3.1
525.0
757.2
−4.1
44.2
2.8
16.8


Sample 74


Reference
T
2.5
986.8
4,909.9
−23.7
397.5
3.7
84.3


Sample 75


Reference
T
2.4
2,555.1
N.D.
N. D.
N.D.
64.0
N. D.


Sample 76


Reference
T
4.1
1,269.0
2,886.4
−50.7
127.5
28.7
90.9


Sample 77


Reference
T
2.2
713.2
1,158.0
−5.4
62.4
2.8
18.9


Sample 78


Reference
T
1.9
310.4
335.2
−10.5
59.6
6.5
15.8


Sample 79


Reference
T
2.8
257.2
281.5
−15.7
62.3
9.8
12.1


Sample 80


Reference
T
0.7
125.2
183.4
−10.3
61.1
2.9
17.0


Sample 81


Reference
T
2.0
80.3
83.4
−19.1
30.2
4.6
10.1


Sample 82


Reference
T
0.8
94.8
92.4
−25.8
−4.9
5.6
21.5


Sample 83


Reference
T
0.7
102.5
133.6
−7.5
60.5
3.3
13.4


Sample 84


Reference
T
0.8
113.8
158.5
−8.6
60.8
3.1
15.2


Sample 85


Reference
T
1.4
90.4
108.5
−13.6
50.6
3.9
11.8


Sample 86


Reference
T
1.6
102.9
106.1
−22.9
6.1
4.1
7.7


Sample 87


Reference
T
1.1
180.1
189.8
−14.5
20.1
5.0
9.1


Sample 88


Reference
T
1.5
188.9
175.3
6.6
3.8
4.9
7.8


Sample 89


Reference
T
1.2
171.4
162.6
−4.5
−6.9
5.1
8.0


Sample 90









(3) Evaluation


From the above-described results, the samples existing within the range surrounded by the line segments of A-B-C-D-E in FIG. 1 had relative dielectric constants at 25° C. of 100.0 or more. In other words, it was confirmed that these samples had ferroelectricity. The samples existing within the range surrounded by the line segments of A-B-C-D-E in FIG. 1 also had change rates in electrostatic capacities of within ±50.0% in the temperature range of −55° C. to 200° C. and dielectric losses (tan δ) at 25° C. and 200° C. of 10.0% or less.


Furthermore, the samples existing within the range surrounded by the line segments of point A′-point B′-point C′-point D′-point E′-point F′-point G′-point Er-point I′-point J′-point K′-point L′ in FIG. 2 had relative dielectric constants at 25° C. of 200 or more.


Of these samples, the samples of Reference Sample Numbers 5, 8, 12, 15, 17, 18, 23 to 25, 27, 29 to 36, 38, 41, and 43 to 45 indicated relative dielectric constants of 500.0 or more and thus are particularly preferable.


The samples of Reference Sample Numbers 1 to 4, 7 to 13, 16 to 18, 23 to 28, 38 to 40, 46, 47, 49 to 62, and 87 to 90 indicated change rates in electrostatic capacities ΔCt/C25 in the temperature region of −55° C. to 200° C. of −33.0% to +22.0% and thus are particularly excellent in temperature properties.


In contrast to these samples, the samples of Reference Sample Numbers 65 to 86 did not provide excellent properties about one or more performances of the relative dielectric constant, the change rate of the electrostatic capacity, and tan δ.


As illustrated in FIG. 6, it is found that the change rate of the electrostatic capacity is within the range of −30.0% to 30.0% in the temperature range of −55° C. to 200° C. in the case where Reference Samples 8 and 15 are used, whereas the change rate of the electrostatic capacity is remarkably increased over around 150° C. in the case of Reference Sample 66.


Reference Sample 15 and Reference Sample 78 are samples that only has difference in the presence or absence of the oxide of Mn as the second component. As illustrated in FIG. 7, it is found that properties of both samples are significantly different.


Reference Example 2

The Reference Samples 91 to 107 were prepared in the same method as the method in Reference Sample 1 except that the raw materials for the first component described above were weighed so that the compositions in terms of the oxides were as listed in Table 7 and MnCO3 and SiO2 were weighed as the second component so that the compositions in terms of the oxides were as listed in Table 7. The disk-shaped ceramic capacitors corresponding to each of the samples were provided.


Thereafter, similar to Reference Example 1, the grain size, the crystal phase, the relative dielectric constant, the change rate of the electrostatic capacity, and the dielectric loss (tan δ) were measured. The results are listed in Table 8.


From these results, it is found that the samples having the Mn content in terms of MnO serving as the second component of less than 3.500% by mass relative to the total mass of the first component in terms of the oxides provide excellent results with respect to the relative dielectric constant, the change rate of the electrostatic capacity, and tan δ.











TABLE 7








First component composition in terms of



Sample
oxides [mol %]
Dielectric ceramic

















name
CaO
SrO
BaO
TiO2
ZrO2
SnO2
Nb2O5
Ta2O5
V2O5
composition





Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 91


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 92


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 93


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 94


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 95


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 96


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 97


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 98


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 99


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 100


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 101


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 102


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 103


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 104


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 105


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 106


Reference
12.50
33.30
4.16
15.03
1.67
0.00
29.97
3.33
0.00
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 107














Second component composition in




terms of oxides [% by mass]















Total






content




Oxide

of



Sample
component
MnO
second



name
species
content
component







Reference
Mn, Si
0.617
0.917



Sample 91



Reference
Mn, Si
0.9258
1.226



Sample 92



Reference
Mn, Si
1.2344
1.534



Sample 93



Reference
Mn, Si
3.0860
3.386



Sample 94



Reference
Mn, Si
3.3946
3.695



Sample 95



Reference
Mn, Si
3.6414
3.941



Sample 96



Reference
Mn, Si
0.9258
1.426



Sample 97



Reference
Mn, Si
1.2344
1.734



Sample 98



Reference
Mn, Si
3.0860
3.586



Sample 99



Reference
Mn, Si
3.3946
3.895



Sample 100



Reference
Mn, Si
3.6414
4.141



Sample 101



Reference
Mn, Si
0.6172
1.317



Sample 102



Reference
Mn, Si
0.9258
1.626



Sample 103



Reference
Mn, Si
1.2344
1.934



Sample 104



Reference
Mn, Si
3.0860
3.786



Sample 105



Reference
Mn, Si
3.3946
4.095



Sample 106



Reference
Mn, Si
3.6414
4.341



Sample 107










In Table 7, the composition in terms of the oxide of the first component is represented by mol % of each of the oxides in terms of the oxides listed in Table 7 relative to the total number of moles of each of the oxide components of the first component in terms of the oxides listed in Table 7. The content of the Mn oxide is represented by % by mass of the Mn oxide in terms of MnO relative to the total mass of each of the oxide components of the first component in terms of the oxides listed in Table 7. The total content of the oxides of the second component is represented by % by mass of the total of the oxides of the second component relative to the total mass of each of the oxide components of the first component in terms of the oxide listed in Table 7.












TABLE 8









Change rate in
















Relative dielectric
electrostatic capacity
tan δ


Sample
Crystal
Grain size
constant
[%]
[%]















name
phase
[μm]
25° C.
200° C.
−55° C.
200° C.
25° C.
200° C.


















Reference
T
1.5
965.7
932.3
−17.0
−3.5
1.5
1.6


Sample 91


Reference
T
1.8
953.9
921.4
−18.7
−3.4
1.3
5.2


Sample 92


Reference
T
1.5
886.3
687.2
−18.7
−22.5
4.0
1.6


Sample 93


Reference
T
1.6
869.5
750.6
−17.6
−13.7
1.8
5.6


Sample 94


Reference
T
1.8
842.6
631.8
−16.2
−20.3
2.2
8.3


Sample 95


Reference
T
2.0
767.1
582.4
−12.3
−27.9
2.8
12.4


Sample 96


Reference
T
2.5
981.3
935.7
−19.1
−4.6
1.5
2.4


Sample 97


Reference
T
2.2
1,011.8
985.1
−20.6
−2.6
2.0
2.1


Sample 98


Reference
T
1.6
805.1
713.3
−17.5
−11.4
1.2
6.3


Sample 99


Reference
T
1.5
738.6
573.3
−16.3
−18.2
2.3
9.5


Sample 100


Reference
T
1.3
627.8
446.6
−15.8
−30.7
2.7
15.8


Sample 101


Reference
T
1.3
988.6
952.3
−20.7
−3.7
2.3
1.2


Sample 102


Reference
T
3.5
973.5
924.6
−20.8
−5.0
2.1
2.3


Sample 103


Reference
T
4.4
972.1
921.3
−21.2
−5.2
1.8
1.9


Sample 104


Reference
T
4.5
804.0
717.7
−18.8
−10.7
2.1
7.1


Sample 105


Reference
T
4.8
725.2
586.3
−17.2
−16.9
2.6
9.8


Sample 106


Reference
T
5.1
584.7
488.1
−14.4
−29.3
2.9
17.2


Sample 107









From the above-described results, from comparison with the samples in which the content of the first component is out of the defined amount of the present invention or the samples in which the content of the oxide of Mn is out of the defined amount of the present invention, the samples in which the content of the first component is in the defined amount of the present invention, the content of the oxide of Mn is in the defined amount of the present invention, and the oxide of Cu and the oxide of Ru are not included exhibit effects of a small change in the electrostatic capacity even under a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity within the range of −50.0% to 50.0% in a temperature range of −55° C. to 200° C., and small dielectric losses at 25° C. and 200° C.


Example 1 and Comparative Example 1

(1) Preparation of Dielectric Ceramic Composition Samples 1 to 20


As the starting materials of the first component, each powder of CaCO3, SrCO3, BaCO3, TiO2, ZrO2, Nb2O5, and Ta2O5 was weighed so that the ratio of each powder in terms of the oxides was as listed in Table 9 and the resultant mixture was wet-blended for 20 hours with pure water using a ball mill.


Subsequently, each of the blends was dried at 100° C. and thereafter calcinated at 750° C. to 900° C. for 3 hours in the air. The obtained product was similarly finely pulverized again with the ball mill to prepare the dielectric raw material for the first component.


As the second component, a mixture made by weighing and mixing 41.2 mg of MnCO3, 72.2 mg of MgO, and 53.9 mg of SiO2 was provided and this mixture was used as the raw material for second component. Here, the raw material for second component was used in an amount of 1.3 times in each of Samples 1 to 6, 8, 9, 11, and 15 to 19. In Samples 8 to 11 and 15 to 20, in addition to the above-described raw materials, as the raw material for the second component, CuO was provided in 0.036% by mass to 0.680% by mass relative to the total mass of each of the oxides of the first component in terms of the oxides listed in the tables. In Samples 12 to 14, in addition to the above-described raw materials, as the raw material for the second component, RuO2 was provided in 0.100% by mass to 0.500% by mass relative to the total mass of each of the oxides of the first component in terms of the oxide listed in the tables.


A poly(vinyl alcohol) aqueous solution was prepared by charging ion-exchanged water and poly(vinyl alcohol) in a container so that the poly(vinyl alcohol) concentration was 6% by mass and mixing the resultant mixture at 90° C. for 1 hour.


Then, 25 g of each of the dielectric raw materials for the first component and the raw material for the second component having the above-described amount were mixed. The poly(vinyl alcohol) aqueous solution was added to the raw material mixture so that the concentration of the poly(vinyl alcohol) aqueous solution was 10% by mass relative to the resultant mixture and the resultant product was mixed and granulated in a mortar to prepare a granulated powder.


Furthermore, the obtained granulated powder was charged in a mold having a diameter of 14.0 mm and press-molded at a pressure of 1 ton/cm2 to provide a disk-shaped green compact.


Subsequently, the obtained green compact was fired in a reducing atmosphere to prepare a sintered compact. In this firing, the temperature increasing rate, the holding temperature, and the holding time were set to 300° C./h, 1,100° C. to 1,300° C., and two hours, respectively. As an atmosphere gas, moistened hydrogen/nitrogen mixture gas (hydrogen concentration 0.5%) was used and a wetter (wetter temperature 35° C.) was used for the moistening.


<Insulation Resistance Value>


For each of the capacitor samples, the insulation resistance value was measured using a digital ultra-high resistance meter/microammeter (8340A, manufactured by ADC CORPORATION) at an applied voltage of 200 V. The insulation resistance value was determined to be excellent when the insulation resistance value is 40 MΩ or more at 200° C.











TABLE 9








First component composition in terms of



Sample
oxides [mol %]
Dielectric ceramic















name
CaO
SrO
BaO
TiO2
ZrO2
Nb2O5
Ta2O5
composition





Sample 1
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 2
25.00
25.00
0.00
15.00
1.67
28.75
4.58
Ca3Sr3Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 3
0.00
5.00
45.00
15.00
1.67
28.75
4.58
Sr0.6Ba5.4Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 4
8.33
16.67
25.00
15.00
1.67
28.75
4.58
CaSr2Ba3Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 5
30.00
10.00
10.00
15.00
1.67
28.75
4.58
Ca3.6Sr1.2Ba1.2Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 6
0.00
42.50
7.50
15.00
1.67
28.75
4.58
Sr5.1Ba0.9Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 7
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 8
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 9
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 10
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 11
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 12
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 13
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 14
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30


Sample 15
25.00
25.00
0.00
15.00
1.67
28.75
4.58
Ca3Sr3Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 16
0.00
5.00
45.00
15.00
1.67
28.75
4.58
Sr0.6Ba5.4Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 17
8.33
16.67
25.00
15.00
1.67
28.75
4.58
CaSr2Ba3Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 18
30.00
10.00
10.00
15.00
1.67
28.75
4.58
Ca3.6Sr1.2Ba1.2Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 19
0.00
42.50
7.50
15.00
1.67
28.75
4.58
Sr5.1Ba0.9Ti1.8Zr0.2Nb6.9Ta1.1O30


Sample 20
12.50
33.33
4.17
15.00
1.67
30.00
3.33
Ca1.5Sr4Ba0.5Ti1.8Zr0.2Nb7.2Ta0.8O30














Second component composition in terms of




oxides [% by mass]



















Total








content




Oxide



of



Sample
component
MnO
CuO
RuO2
second



name
species
content
content
content
component







Sample 1
Mg, Mn,
0.132
0.000
0.000
0.991




Si



Sample 2
Mg, Mn,
0.132
0.000
0.000
0.991




Si



Sample 3
Mg, Mn,
0.132
0.000
0.000
0.991




Si



Sample 4
Mg, Mn,
0.132
0.000
0.000
0.991




Si



Sample 5
Mg, Mn,
0.132
0.000
0.000
0.991




Si



Sample 6
Mg, Mn,
0.132
0.000
0.000
0.991




Si



Sample 7
Mg, Mn,
0.102
0.000
0.000
0.762




Si



Sample 8
Mg, Mn,
0.132
0.036
0.000
1.027




Si, Cu



Sample 9
Mg, Mn,
0.132
0.045
0.000
1.036




Si, Cu



Sample 10
Mg, Mn,
0.102
0.050
0.000
0.812




Si, Cu



Sample 11
Mg, Mn,
0.132
0.054
0.000
1.045




Si, Cu



Sample 12
Mg, Mn,
0.102
0.000
0.100
0.862




Si, Ru



Sample 13
Mg, Mn,
0.102
0.000
0.200
0.962




Si, Ru



Sample 14
Mg, Mn,
0.102
0.000
0.500
1.262




Si, Ru



Sample 15
Mg, Mn,
0.132
0.677
0.000
1.667




Si, Cu



Sample 16
Mg, Mn,
0.132
0.677
0.000
1.667




Si, Cu



Sample 17
Mg, Mn,
0.132
0.677
0.000
1.667




Si, Cu



Sample 18
Mg, Mn,
0.132
0.677
0.000
1.667




Si, Cu



Sample 19
Mg, Mn,
0.132
0.677
0.000
1.667




Si, Cu



Sample 20
Mg, Mn,
0.102
0.100
0.000
0.862




Si, Cu










In Table 9, the composition in terms of the oxide of the first component is represented by mol % of each of the oxides in terms of the oxides listed in the tables relative to the total number of moles of each of the oxide components of the first component in terms of the oxides listed in Table 9. The content of the Mn oxide is represented by % by mass of the Mn oxide in terms of MnO relative to the total mass of each of the oxide components of the first component in terms of the oxides listed in Table 9. The content of the Cu oxide is represented by % by mass of the Cu oxide in terms of CuO relative to the total mass of each of the oxide components of the first component in terms of the oxides listed in Table 9. The content of the Ru oxide is represented by % by mass of the Ru oxide in terms of RuO2 relative to the total mass of each of the oxide components of the first component in terms of the oxides listed in Table 9. The total content of the oxides of the second component is represented by % by mass of the total of the oxides of the second component relative to the total mass of each of the oxide components of the first component in terms of the oxide listed in Table 9.














TABLE 10












Insulation



Change rate in


resistance












Relative dielectric
electrostatic capacity
tan δ
value


Sample
constant
[%]
[%]
[MΩ]














name
25° C.
200° C.
−55° C.
200° C.
25° C.
200° C.
200° C.

















Sample 1
865.5
923.9
−18.3
6.8
1.9
6.2
26


Sample 2
662.0
660.7
−22.7
−0.2
2.7
4.9
8.30


Sample 3
586.3
413.3
20.7
−29.5
0.8
2.4
35.7


Sample 4
1,061.9
601.9
−9.4
−43.3
0.9
4.2
14.7


Sample 5
511.0
453.3
−24.8
−11.3
2.2
5.0
8.62


Sample 6
1,234.2
680.1
2.0
−44.9
1.1
6.2
9.5


Sample 7
901.3
856.9
−29.2
−4.9
1.8
7.0
18


Sample 8
824.9
840.2
−16.3
1.9
1.1
3.6
64


Sample 9
798.7
818.2
−18.3
2.4
1.7
4.8
60


Sample 10
805.8
789.7
−17.9
−2.0
1.6
3.0
80


Sample 11
774.9
809.5
−17.9
4.5
1.6
6.1
40


Sample 12
663.0
677.7
−17.9
2.2
1.4
5.7
47


Sample 13
676.1
626.6
−19.1
−7.3
1.6
2.9
93


Sample 14
718.9
712.1
−20.0
−0.9
1.6
4.5
208


Sample 15
622.0
460.5
−27.2
−26.0
2.9
6.3
211


Sample 16
644.1
485.7
20.7
−24.6
0.7
7.0
309


Sample 17
1,115.0
634.1
−11.3
−43.1
1.3
4.8
277


Sample 18
606.8
460.3
−23.0
−24.1
3.2
3.6
189


Sample 19
1,178.6
648.1
4.9
−45.0
1.3
3.6
371


Sample 20
855.8
817.0
−14.8
−4.5
1.2
2.6
1,694









From the above-described results, it is confirmed that the content of the first component is in the defined amount of the present invention, the oxide of Mn is included in the defined amount of the present invention, and one or both of the oxide of Cu and the oxide of Ru are included, whereby a high relative dielectric constant at 25° C., a small change in the electrostatic capacity even under a high temperature condition of 150° C. to 200° C., the change rate of the electrostatic capacity within the range of −50.0% to 50.0% in a temperature range of −55° C. to 200° C., small dielectric losses at 25° C. and 200° C., and the high insulation resistance value at 200° C. can be achieved.


From the comparison with the Reference Samples in which the content of the first component is in the range of the defined amount of the present invention and the content of the oxide of Mn is in the defined amount of the present invention, but the oxide of Cu and the oxide of Ru are not included, it is found that the content of the first component is in the range of the defined amount of the present invention, the oxide of Mn is included in the range of the defined amount of the present invention, and one or both of the oxide of Cu and the oxide of Ru are included, whereby the insulation resistance value can be increased while the change in the electrostatic capacity is further smaller without significantly affecting action and effect on the relative dielectric constant, the change rate of the electrostatic capacity, and the dielectric loss.


In the above-described example, the single-plate type ceramic capacitors have been evaluated. For a laminated ceramic capacitor in which dielectric layers and internal electrodes are laminated, similar results can also be obtained.


REFERENCE CHARACTERS LIST






    • 1 Laminated Ceramic Capacitor


    • 2 Dielectric Layer


    • 3 Internal Electrode Layer


    • 4 External Electrode


    • 10 Laminated body




Claims
  • 1. A dielectric ceramic composition comprising: a first component; anda second component, whereinas a content ratio relative to a total number of moles of the first component when converted into following oxides, the first component comprises an oxide of Ca of 0.00 mol % to 35.85 mol % in terms of CaO, an oxide of Sr of 0.00 mol % to 47.12 mol % in terms of SrO, an oxide of Ba of 0.00 mol % to 51.22 mol % in terms of BaO, an oxide of Ti of 0.00 mol % to 17.36 mol % in terms of TiO2, an oxide of Zr of 0.00 mol % to 17.36 mol % in terms of ZrO2, an oxide of Sn of 0.00 mol % to 2.60 mol % in terms of SnO2, an oxide of Nb of 0.00 mol % to 35.32 mol % in terms of Nb2O5, an oxide of Ta of 0.00 mol % to 35.32 mol % in terms of Ta2O5, and an oxide of V of 0.00 mol % to 2.65 mol % in terms of V2O5;the first component comprises at least one oxide selected from the oxide of Ca, the oxide of Sr, and the oxide of Ba, at least one oxide selected from the oxide of Ti and the oxide of Zr, and at least one oxide selected from the oxide of Nb and the oxide of Ta as essential components, and a total content ratio of the oxide of Ca in terms of CaO, the oxide of Sr in terms of SrO, and the oxide of Ba in terms of BaO is 48.72 mol % to 51.22 mol %, a total content ratio of the oxide of Ti in terms of TiO2, the oxide of Zr in terms of ZrO2, and the oxide of Sn in terms of SnO2 is 15.97 mol % to 17.36 mol %, and a total content ratio of the oxide of Nb in terms of Nb2O5, the oxide of Ta in terms of Ta2O5, and the oxide of V in terms of V2O5 is 31.42 mol % to 35.31 mol % relative to the total number of moles of the first component when converted into the oxides; andas a content ratio relative to a total mass of the first component when converted into the oxides, the second component comprises at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass in terms of MnO and (b) one or both of an oxide of Cu and an oxide of Ru.
  • 2. A dielectric ceramic composition comprising: a first component; anda second component, whereinas the first component, a compound represented by a following general formula (1): AaM1bM2cOd  (1)
  • 3. A dielectric ceramic composition comprising: a first component; anda second component, whereina compound represented by a following general formula (3): α·Caη1M3θ1M4ϕ1Oω1-β·Srη2M3θ2M4ϕ2Oω2-γ·Baη3M3θ3M4ϕ3Oω3  (3)
  • 4. The dielectric ceramic composition according to claim 3, wherein the first component is a compound existing within a range surrounded by line segments linking a point A′=(0.05, 0.95, 0.00), a point B′=(0.60, 0.40, 0.00), a point C′=(0.70, 0.20, 0.10), a point D′=(0.70, 0.10, 0.20), a point E′=(0.55, 0.00, 0.45), a point F′=(0.40, 0.00, 0.60), a point G′=(0.10, 0.10, 0.80), a point H′=(0.00, 0.00, 1.00), a point I′=(0.00, 0.40, 0.60) a point J′=(0.20, 0.40, 0.40), a point K′=(0.00, 0.70, 0.30), and a point L′=(0.00, 0.90, 0.10) in the ternary composition diagram.
  • 5. The dielectric ceramic composition according to claim 1, wherein, as the content ratio relative to the total mass of the first component when the first component is converted into CaO, SrO, BaO, TiO2, ZrO2, SnO2, Nb2O5, Ta2O5, and V2O5, the second component comprises one or both of an oxide of Cu of 0.010% by mass or more and less than 0.080% by mass in terms of CuO and an oxide of Ru of 0.050% by mass or more and less than 0.300% by mass in terms of RuO2.
  • 6. The dielectric ceramic composition according to claim 1, wherein an oxide of D (D is at least one element selected from Li, Mg, Si, Cr, Al, Fe, Co, Ni, Zn, Ga, Ge, In, W, Mo, Y, Hf, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) is included as the second component.
  • 7. The dielectric ceramic composition according to claim 1, wherein the dielectric ceramic composition comprises a tungsten bronze type crystal phase.
  • 8. The dielectric ceramic composition according to claim 1, wherein relative dielectric constant at 25° C. is 100.0 or more.
  • 9. The dielectric ceramic composition according to claim 1, wherein a change rate in electrostatic capacity is within a range of −20.0% to 5.0% in a temperature range of −55° C. to 200° C.
  • 10. The dielectric ceramic composition according to claim 1, wherein a dielectric loss (tan δ) at 25° C. is 10.0% or less and a dielectric loss (tan δ) at 200° C. is 10.0% or less.
  • 11. The dielectric ceramic composition according to claim 1, wherein an insulation resistance value at 200° C. is 40 MΩ or more and less than 100 MΩ.
  • 12. A ceramic electronic component comprising: a dielectric layer formed of the dielectric ceramic composition as claimed in claim 1; andan electrode layer comprising a base metal as a conductive component.
  • 13. The ceramic electronic component according to claim 12, wherein the base metal is at least one metal selected from nickel and copper.
  • 14. The ceramic electronic component according to claim 12, wherein a plurality of the dielectric layers and a plurality of the electrode layers are laminated.
Priority Claims (1)
Number Date Country Kind
2018-076093 Apr 2018 JP national