Dielectric ceramic composition and dielectric ceramics

FIELD OF THE INVENTION

[0001] The present invention relates to a dielectric ceramic composition and a dielectric ceramics and, more particularly, to a dielectric ceramic composition and dielectric ceramics, which exhibits a relative dielectric constant of 8 to 22 in high-frequency regions such as microwaves and millimeter waves, and also have high mechanical strength and high-accuracy temperature coefficient as compared with conventional glass ceramics.

BACKGROUND OF THE INVENTION

[0002] Heretofore, dielectric ceramics have been widely used in dielectric resonators, dielectric substrate materials for MIC and waveguides that are used in high-frequency applications such as microwave and millimeter waves. With the recent development and spread of mobile communication including portable telephone, demand for dielectric ceramics as materials for electronic circuit boards and electronic parts has been increasing.

[0003] As a dielectric ceramic composition for electronic circuit boards and electronic parts, there have been developed so-called glass ceramics made of glass, which can be fired together with a high-conductive metal such as silver or copper, or a composite material of glass and ceramics.

[0004] For example, Unexamined Patent Publication (Kokai) No. 2001-348268 describes a dielectric ceramic composition comprising SiO2, CaO, MgO, B2O3 and Al2O3 which can be fired at the temperature of 1000° C. or lower and can be used in high-frequency parts.

[0005] Although the dielectric ceramic composition described in Unexamined Patent Publication (Kokai) No. 2001-348268 exhibits low dielectric loss, a temperature coefficient of electrostatic capacity increases because the dielectric ceramics has a large temperature coefficient of resonant frequency, and thus desired electric conductive characteristic can not be obtained according to service environment. Because of a low mechanical strength, cracking is likely to be caused by impact of an electronic equipment using the dielectric ceramics upon dropping.

SUMMARY OF THE INVENTION

[0006] A main object of the present invention is to provide a high-strength dielectric ceramic composition and a high-strength dielectric ceramics, which are suited for use in high-frequency parts and can control high-accuracy temperature characteristics.

[0007] Another object of the present invention is to provide a dielectric ceramic composition and a dielectric ceramics, which can prevent discoloration of a substrate upon firing together with a conductor or to color the substrate, thereby making it possible to reduce a rate of poor appearance.

[0008] The present invention has been completed based on such a fining that temperature characteristics of the resonant frequency can be improved and control of the desired dielectric constant and high strength can be achieved by using a dielectric ceramic composition comprising crystallized glass capable of depositing a diopside crystal, calcium titanate and/or strontium titanate and at least one kind selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3. The dielectric ceramic composition of the present invention comprises at least a crystallized glass powder capable of depositing a diopside crystal and a calcium titanate and/or a powdered strontium titanate.

[0009] Particularly, the dielectric ceramic composition of the present invention comprises:

[0010] (1) 30 to 90% by weight of a crystallized glass powder capable of depositing a diopside crystal,

[0011] (2) 1 to 40% by weight of a calcium titanate powder, a strontium titanate powder or a mixed powder, and

[0012] (3) 0 to 60% by weight of at least one kind selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3.

[0013] By using the mixture of various powders with such a composition, temperature characteristics of the resonant frequency of the dielectric ceramics formed after firing can be improved and control of the desired dielectric constant and high strength can be achieved.

[0014] Also it is preferred that a crystallized glass powder capable of depositing a diopside crystal, a calcium titanate powder, a strontium titanate powder, or a mixed powder of a calcium titanate powder and a strontium titanate powder used in the dielectric ceramic composition have a mean particle size of 3 μm or smaller in order to enhance the mechanical strength of the dielectric ceramics and to improve dielectric characteristics such as temperature coefficient of the resonant frequency.

[0015] The other dielectric ceramic composition of the present invention comprises:

[0016] [I] 100 parts by weight of a mixed powder comprising (1) 30 to 90% by weight of a crystallized glass powder capable of depositing a diopside crystal, (2) 1 to 40% by weight of a calcium titanate powder, a strontium titanate powder or a mixed powder thereof and (3) 0 to 60% by weight of at least one kind selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3, and

[0017] [II] 0.1 to 2.0 parts by weight of at least one kind of a powder (color tone modifier) selected from the group consisting of Fe2O3, Cr2O3, ZnO, CuO, Ag2O, Co3O4, MnO2, CeO2 and R2O3 (R represents a rare earth element).

[0018] By using the mixture of various powders with such a composition, temperature characteristics of the resonant frequency of the dielectric ceramics formed after firing can be improved and control of the desired dielectric constant and high strength can be achieved. Furthermore, it becomes possible to prevent discoloration of a substrate upon firing together with a conductor or to color the substrate, thereby making it possible to reduce a rate of poor appearance.

[0019] The dielectric ceramics of the present invention can be obtained by firing a preform (a green body) of a mixture of the dielectric ceramic composition at a temperature within a range from 850 to 1050° C., and a relative dielectric constant εr is within a range from 8 to 22 and a three-point bending strength is 250 MPa or larger, and a temperature coefficient of the resonant frequency is 0±60×10−6/° C.

[0020] Therefore, in dielectric substrate materials for MIC and electronic parts, in case of firing together with a conductor comprising Ag or Cu as a main component, the occurrence of warp and strain can be prevented and it becomes possible to design high-functional high-frequency circuit parts. Furthermore, when using dielectric ceramic composition containing the color tone modifier added therein, it becomes possible to prevent discoloration caused by a reducing action due to the conductor or to color the substrate.

[0021] In the dielectric ceramics of the present invention, the temperature coefficient of the electrostatic capacity is preferably 0±150×10−6/° C. Whereby, variation in the electrostatic capacity due to change in the temperature can be suppressed and temperature characteristics of the dielectric ceramics can be controlled with high accuracy.

[0022] Furthermore, in the ceramics after firing, at least diopside and/or a diopside solid solution and calcium titanate and/or strontium titanate preferably co-exist as a crystal phase. As described above, by allowing the crystal phase capable of changing the strength and the temperature coefficient of the dielectric ceramics to co-exist in the dielectric ceramics, the mechanical strength of the dielectric ceramics can be enhanced and also the relative dielectric constant and the temperature coefficient can be easily controlled.

[0023] The ceramics after firing preferably exhibits a thermal expansion coefficient as measured at room temperature to 400° C. of 8×10−6/° C. or higher. Whereby, the thermal expansion coefficient of the dielectric ceramics can be made to be closer to the thermal expansion coefficient of a glass epoxy resin used in a mother board and thus the mounting reliability to thermal shock can be improved.

BRIEF DESCRIPTION OF THE DRAWINGS

[0024]
FIG. 1 is a graph showing a powder X-ray diffraction pattern of a sample No. 1 according to Example 1 as the dielectric ceramics of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0025] It is important that the dielectric ceramic composition of the present invention contains a crystallized glass powder capable of depositing a diopside crystal and a calcium titanate powder, a strontium titanate powder or a mixed powder thereof and also contains at least one kind of a powder (filler component) selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3.

[0026] The diopside crystal is preferably used because of large relative dielectric constant, small dielectric loss and high strength in high frequency.

[0027] Calcium titanate and/or strontium titanate are used to compensate the temperature coefficient of the resonant frequency of the diopside crystal deposited in the dielectric ceramic composition. In case of using the diopside crystal alone, the temperature coefficient of the resonant frequency exhibits negative characteristics, while in case of using calcium titanate and/or strontium titanate alone, the temperature coefficient of the resonant frequency exhibits positive characteristics. Therefore, the diopside crystal is preferably used to control the temperature coefficient of the resonant frequency.

[0028] The filler components such as Al2O3 are preferably used in combination to improve the mechanical strength of the dielectric ceramics and to compensate temperature characteristics to the amount of calcium titanate.

[0029] To constitute the dielectric ceramic composition of the present invention, it is important that the dielectric ceramic composition comprises 30 to 90% by weight of a crystallized glass powder capable of depositing a diopside crystal, 1 to 40% by weight of a calcium titanate powder and 0 to 60% by weight of at least one kind of a powder selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3.

[0030] The amount of the crystallized glass powder capable of depositing a diopside crystal was defined within a range from 30 to 90% by weight by the following reason. That is, the amount of the crystallized glass powder is within the above range, a high-density dielectric ceramics can be formed at a temperature within a range from 850 to 1050° C. and it becomes possible to fire together with a conductor comprising Ag or Cu as a main component. When the amount of the crystallized glass powder is smaller than 30% by weight, the composition is not sintered at a temperature lower than 1050° C. and it becomes impossible to fire together with the conductor comprising Ag or Cu as a main component. On the other hand, when the amount exceeds 90% by weight, the mechanical strength is lowered and it becomes difficult to retain the shape in case glass is softened during the firing, resulting in poor dimensional accuracy of the wiring substrate. Therefore, the amount of the crystallized glass powder is more preferably within a range from 40 to 80% by weight in order to maintain sinterability, high strength and high dimensional accuracy.

[0031] The crystallized glass powder capable of depositing a diopside crystal preferably has a composition of 30 to 55% by weight of SiO2, 10 to 35% by weight of MgO and 24 to 40% by weight of CaO. Al2O3 may be contained alone or together with ZnO in the crystallized glass powder. It is desirable that the amount of Al2O3 is 4.5 to 15% by weight.

[0032] At least one kind selected from the group consisting of hardystonite, celsian, cordierite, anorthite, gahnite, willemite, spinel and mullite is preferably deposited from the glass powder, in addition to diopside, because high strength can be achieved.

[0033] The amount of the calcium titanate powder was defined within a range from 1 to 40% by weight by the following reason. That is, the diopside crystal, which has the temperature coefficient of the resonant frequency if of −63×10−6/° C. and exhibits negative characteristics, and the calcium titanate powder, which exhibits the temperature coefficient of the resonant frequency if of 840×10−6/° C. at a temperature within a range from 25 to 85° C., co-exist in the dielectric ceramics and both powders can compensate the temperature coefficient of the resonant frequency and control it within a range of 0±60×10−6/° C.

[0034] When the amount of the calcium titanate powder is smaller than 1% by weight, it becomes difficult to improve the relative dielectric constant of the dielectric ceramics and to control the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. On the other hand, when the amount exceeds 40% by weight, the temperature coefficient of the resonant frequency increases to the positive side and it becomes difficult in order to control the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. while maintaining the sinterability. Therefore, the amount of the calcium titanate powder is more preferably within a range from 3 to 30% by weight to control the temperature with high accuracy. As used herein, control of the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. means that the absolute value is 60×10−6/° C. or smaller.

[0035] The amount of the strontium titanate powder used in place of the calcium titanate powder was defined within a range from 1 to 40% by weight by the following reason. That is, the diopside crystal, which has the temperature coefficient of the resonant frequency τf of −63×10−6/° C. and exhibits negative characteristics, and the strontium titanate powder, which exhibits the temperature coefficient of the resonant frequency τf of 1670×10−6/° C. at a temperature within a range from 25 to 85° C., co-exist in the dielectric ceramics and both powders can compensate the temperature coefficient of the resonant frequency and control it within a range of 0±60×10−6/° C.

[0036] When the amount of the strontium titanate powder is smaller than 1% by weight, it becomes difficult to improve the relative dielectric constant of the dielectric ceramics and to control the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. On the other hand, when the amount exceeds 40% by weight, the temperature coefficient of the resonant frequency increases to the positive side and it becomes difficult in order to control the temperature coefficient of the resonant frequency within a range of 0±60×10−16/° C. while maintaining the sinterability. Therefore, the amount of the strontium titanate powder is more preferably within a range from 3 to 30% by weight to control the temperature with high accuracy. As used herein, control of the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. means that the absolute value is 60×10−6/° C. or smaller.

[0037] When using the mixed powder of calcium titanate and strontium titanate in place of calcium titanate or strontium titanate, The amount of the mixed powder was defined within a range from 1 to 40% by weight by the following reason. That is, the diopside crystal, which has the temperature coefficient of the resonant frequency τf of −63×10−6/° C. and exhibits negative characteristics, and the mixed powder in the state wherein two phase of calcium titanate and strontium titanate co-exist, which exhibits the temperature coefficient of the resonant frequency if within a range from 840×10−6 to 1670×10−6/° C. at a temperature within a range from 25 to 85° C., co-exist in the dielectric ceramics and both powders can compensate the temperature coefficient of the resonant frequency and control it within a range of 0±60×10−6/° C.

[0038] When the amount of the mixed powder of calcium titanate and strontium titanate is smaller than 1% by weight, it becomes difficult to improve the relative dielectric constant of the dielectric ceramics and to control the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. On the other hand, when the amount exceeds 40% by weight, the temperature coefficient of the resonant frequency increases to the positive side and it becomes difficult to control the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. while maintaining the sinterability. Therefore, the amount of the mixed powder of calcium titanate and strontium titanate is more preferably within a range from 3 to 30% by weight in order to control the temperature with high accuracy.

[0039] As used herein, control of the temperature coefficient of the resonant frequency within a range of 0±60×10−6/° C. means that the absolute value is 60×10−6/° C. or smaller.

[0040] The amount of at least one kind of a powder selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3 as the filler component was defined within a range from 0 to 60% by weight by the following reason. That is, when the amount exceeds 60% by weight, it becomes impossible to sinter at 1050° C. or lower. Particularly, the amount is preferably 50% by weight or smaller in view of the sinterability. As the filler component used herein, a combination of calcium titanate and/or strontium titanate wherein the temperature coefficient of the resonant frequency exhibits positive characteristics, TiO2 and BaTi4O9 wherein the temperature coefficient exhibits positive characteristics, and Al2O3, ZrO2, MgTiO3, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3 wherein the temperature coefficient of the resonant frequency exhibits negative characteristics is preferably selected and prepared to control the temperature coefficient of the resonant frequency to nearly zero. The amount of the filler component is more preferably within a range from 0.5 to 30% by weight.

[0041] In addition to the above compounds, the composition may contain V, Cr, Mo, W, Mn, Co, Ni, Cu, Ag, Ru, Cd and oxides thereof in the amount of 10% by weight or smaller as far as the strength is maintained and warp or strain of the substrate does not occur when fired together with the conductor.

[0042] The mean particle size of the powder, which serves as the filler component, is preferably within a range from 1 to 3.5 μm to control the sinterability and high strength of the ceramics and the temperature coefficient of the resonant frequency, and more preferably from 1.2 to 3 μm in order to improve the dispersibility to the crystallized glass powder capable of depositing a diopside crystal, the calcium titanate powder or the strontium titanate powder.

[0043] The method of producing a dielectric ceramics using the composition of the present invention will now be described. First, a glass powder having a mean particle size of 1 to 3 μm, a calcium titanate powder and/or a strontium titanate powder, each having a mean particle size of 1 to 3 μm, and at least one kind of a powder selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3 as a filler component are prepared.

[0044] The mean particle size of the crystallized glass powder capable of depositing a diopside crystal, the calcium titanate powder and/or the strontium titanate powder is preferably 3 μm or smaller because a high-density dielectric ceramics can be obtained by firing at a temperature within a range from 850 to 1050° C., and more preferably within a range from 1.5 to 2.5 μm because compensation of the temperature coefficient of the resonant frequency and high strength can be achieved.

[0045] As the combination of the calcium titanate powder and/or the strontium titanate powder and the filler component, a combination of calcium titanate and/or strontium titanate wherein the temperature coefficient of the resonant frequency exhibits positive characteristics, a group (TiO2 and BaTi4O9) wherein the temperature coefficient exhibits positive characteristics, and a group (Al2O3, ZrO2, MgTiO3, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3) wherein the temperature coefficient of the resonant frequency exhibits negative characteristics is preferably selected and prepared to control the temperature coefficient of the resonant frequency to nearly zero. Then, these raw powders are weighed and mixed in the above proportions in a ball mill using ZrO2 balls to obtain a ground mixture having a particle size of 2.0 μm or smaller.

[0046] The resulting mixed powder is formed into a preform of a predetermined shape by various known forming methods such as press forming method, doctor blade method, injection molding method or tape forming method. Among these methods, a doctor blade method and a tape forming method are particularly preferred for formation of a laminate.

[0047] The resulting preform is fired in an oxidizing atmosphere such as air or a non-oxidizing atmosphere such as nitrogen at a temperature of 850 to 1050° C. for 0.5 to 2 hours to obtain dielectric ceramics.

[0048] Metal salts such as hydroxide, carbonate and nitrate which produce the oxides when fired may be used as raw powders. The dielectric ceramic composition of the present invention may include inevitable impurities such as Fe, Hf, Sn, Nb, Na and K as far as they do not exert any adverse influence on characteristics and sinterability.

[0049] It is particularly preferred that diopside and/or a diopside solid solution deposited from the glass powder and granular calcium titanate and/or strontium titanate co-exist in the dielectric ceramics in order to control the temperature characteristics. When the diopside crystal and calcium titanate and/or strontium titanate are remained in the ceramics, high strength can be imparted to the dielectric ceramics.

[0050]
FIG. 1 is a graph showing a powder X-ray diffraction pattern of an example of a dielectric ceramics obtained by using calcium titanate as the dielectric ceramic composition of the present invention and Al2O3 as the filler and firing the composition. As shown in FIG. 1, there exist clear X-ray diffraction peaks which indicate crystal phases of the diopside crystal, calcium titanate, and Al2O3 added as the filler component. As is apparent from this fact, the diopside crystal, calcium titanate and the Al2O3 component co-exist in the dielectric ceramics. The other heterogenous phase may co-exist as far as it is a crystal phase which does not exert a drastic influence on the strength and dielectric characteristics. As a result of observation using an electron microscope, granular CaTiO3 and Al2O3 are uniformly dispersed.

[0051] When using the strontium titanate powder or a mixture of the calcium titanate powder and the strontium titanate powder as the filler in place of the calcium titanate powder, the same tendency is recognized.

[0052] In the dielectric ceramics of the present invention with the above constitution, Er can vary within a range from 8 to 22, the three-point bending strength of the ceramics can be controlled to 250 MPa or larger, the temperature coefficient of the resonant frequency can be controlled to 0±60×10−6/° C., particularly, 0±40×10−6/° C., and the temperature coefficient of the electrostatic capacity can be controlled to 0±150×10−6/° C., particularly 0±70×10−6/° C. Also the firing temperature can be controlled to a temperature within a range from 850 to 1050° C. which enables the composition to fire together with a conductor comprising Ag or Cu as a main component. Therefore, the occurrence of warp or strain can be suppressed even in case of firing together with the conductor.

[0053] In the dielectric ceramics of the present invention, the thermal expansion coefficient as measured at a temperature within a range from room temperature to 400° C. is preferably 8×10−6/° C. or larger, and more preferably within a range from 8.5×10−6 to 9.8×10−6/° C.

[0054] To constitute the other dielectric ceramics of the present invention, 0.1 to 2.0 parts by weight of at least one kind of a powder (II) selected from the group consisting of Fe2O3, Cr2O3, ZnO, CuO, Ag2O, Co3O4, MnO2, CeO2 and R2O3 (R represents a rare earth element) is further added to 100 parts by weight of a mixed powder (I) comprising 30 to 90% by weight of a crystallized glass powder capable of depositing a diopside crystal, 1 to 40% by weight in total of a calcium titanate powder and/or a strontium titanate powder and 0 to 60% by weight of at least one kind of a powder selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3.

[0055] At least one kind of the powder (II) selected from the group consisting of Fe2O3, Cr2O3, ZnO, CuO, Ag2O, Co3O4, MnO2, CeO2 and R2O3 (R represents a rare earth element) was added in the amount within a range from 0.1 to 2.0 parts by weight based on 100 parts by weight of the mixed powder (I) by the following reason. That is, these powders are added as the color tone modifier in order to suppress uneven coloring of the substrate by preventing discoloration of the diopside crystal phase due to a reducing action upon firing together with the conductor, or coloring the substrate while suppressing lowering and variation of the mechanical strength. When the amount exceeds 2.0 parts by weight, the mechanical strength is drastically lowered. On the other hand, when the amount is smaller than 0.1 parts by weight, the effect of preventing discoloration or coloring disappears. The amount is more preferably within a range from 0.1 to 1.0 parts by weight in order to prevent discoloration or to control the substrate by maintaining high mechanical strength. The particle size of these oxides is preferably 1.0 μm or smaller to exert the above effect more sufficiently.

[0056] In case of producing a dielectric ceramics using the dielectric ceramic composition of the present invention, first, a mixed powder comprising a diopside crystallized glass powder having a mean particle size of 2.0 μm, a calcium titanate powder and/or a strontium titanate powder, each having a mean particle size of 2.0 μm, and at least one kind of a powder selected from the group consisting of Al2O3, TiO2, ZrO2, MgTiO3, SrTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3 as a filler component and, furthermore, at least one kind of a powder selected from the group consisting of Fe2O3, Cr2O3, ZnO, CuO, Ag2O, Co3O4, MnO2, CeO2 and R2O3 (R represents a rare earth element) as a color tone modifier are prepared. Then, the resulting powders are mixed in the above proportion, formed and then fired in the same manner as described above to obtain a dielectric ceramics of the present invention.

EXAMPLES

Example 1

[0057] First, the following glass frits A and B were used as a glass frit which is a crystallized glass powder capable of depositing a diopside crystal, having a mean particle size of 2 μm.

[0058] Glass frit A: 45 wt % SiO2-25 wt % CaO-15 wt % MgO-10 wt % ZnO-5 wt % Al2O3

[0059] Glass frit B: 49 wt % SiO2-28 wt % CaO-18 wt % MgO-5 wt % Al2O3

[0060] As a filler, a CaTiO3 powder having a mean particle size of 2 μm and purity of 99% or higher and Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O7, Ca2Nb2O7, SrZrO3 and CaZrO3 powders each having a mean particle size of 2 μm were used. These respective components were weighed and mixed with water in proportions shown in Table 1 in wet process for 20 hours in a ball mill using ZrO2 balls to obtain a ground mixture having a particle size of 1.5 μm or smaller.

[0061] As Comparative Example, a crystallized glass powder incapable of depositing a diopside crystal (glass frit C: 50 wt % of SiO2-40 wt % of BaO-10 wt % of Al2O3) was used.

[0062] The ground mixture was formed into a preform of cylindrical shape in size of 5 mm×4 mm×50 mm as a sample for evaluation of a bending strength under a pressure of 100 MPa, fired under the conditions of a maximum temperature shown in Table 1 for one hour to obtain a sample in size of 4 mm×3 mm×40 mm. This sample was subjected to the measurement of a three-point bending strength at room temperature under the conditions of a cross head speed of 0.5 mm/min and a distance between the lower supports of 30 mm. The thermal expansion coefficient was measured by using an apparatus for measuring the thermal expansion coefficient. The results are shown in Table 2.

[0063] Also the above ground mixture was formed into a preform of cylindrical shape measuring 10 mm in diameter and 8 mm in height as a sample for evaluation of dielectric characteristics under a pressure of 100 MPa, fired under the conditions of a maximum temperature shown in Table 1 for one hour to obtain a sample measuring 8 mm in diameter and 6 mm in height.

[0064] With respect to the evaluation of dielectric characteristics, the relative dielectric constant εr of the sample was measured at frequency of 9 to 15 GHz using a dielectric circular cylinder resonator method, and the temperature coefficient τf of the resonant frequency was measured at a temperature within a range from −40 to 85° C. The results are shown in Table 2. τf [×10−6/° C.] in the table is a value as measured at a temperature within a range from 25 to 85° C. and is represented by the following equation:

τf=(1/f25° C.) (f85° C.−f25° C.)/(60° C.)×106

[0065] where f25° C. denotes the resonant frequency at 25° C. and f85° C. denotes the resonant frequency at 85° C. TCC in the table is a temperature coefficient of the electrostatic capacity and is represented by τf and the thermal expansion coefficient α according to the following equation:

TCC=−
2(α+τf)

[0066] where the thermal expansion coefficient α is a value measure at a temperature within a range from room temperature to 400° C.

[0067] The crystal phase in the dielectric ceramics was identified by X-ray diffraction. The results are shown in Table 2.

1TABLE 1GlassFiringCom-CT **Filler composition (wt. %) ***temp.No.ponentwt. %(wt. %)ALTiZrMTBTLTNTCNSZCZ° C. 1A601029100000000900 2A701019100000000900 3A65529010000000900 4A68724010000000900 5A72324001000000890 6A75520000000000850 7A6513100001110 000900 8A601550000010 10 001050 * 9 A6004000000000089010B6093010000000091011B7092000000000089012B8010900100000085013B6282901000001091014B5283900000000191015B7462000000000091016B6463000000000091017B5464000000000091018B5873500000000091019B5374000000000091020B4874500000000093021B5020200000010 0001000 22B454000000010 5001050 * 23 B955000000000085024B902800000000085025B3020400000010 0001050 * 26 B204040000000000Not fired* 27 B70030000000000900* 28 C601030000000000900* 29 B30565000000000Not fired* 30 B4045500000000001050 Sample numbers marked with * are not within the scope of the present invention. ** CT: CaTiO3 *** AL: Al2O3, Ti: TiO2, Zr: ZrO2, MT: MgTiO3, BT: BaTi4O9, LT: La2Ti2O7, NT: Nd2Ti2O7, CN: Ca2Nb2O7, SZ: SrZrO3, CZ: CaZrO3

[0068]

2

TABLE 2

Thermel
Characteristics

Bending
expansion
at 9 to 15 GHz

strength
coefficient ×

τ f ×
TCC ×
Crystal phase in

No.
MPa
10−6/° C.
ε r
10−6/° C.
10−6/° C.
dielectric ceramics **

1
251
8.5
10.0
18.8
−54.6
D, CT, H, AL, W, G

2
281
8.5
10.8
22.7
−62.4
D, CT, H, AL, W, G

3
274
8.5
9.4
−16.6
16.2
D, CT, H, AL, W

4
308
8.5
10.0
−2.2
−12.58
D, CT, H, AL, W

5
270
8.4
8.8
−35.1
53.4
D, CT, H, AL, W

6
265
8.5
9.3
−21.7
26.4
D, CT, H, AL, W

7
263
8.5
12.5
59.3
−135.6
D, CT, ST, H, AL, W

8
252
8.5
15.9
59.0
−135
D, CT, ST, H, AL,

W, NT, CN

* 9
276
8.4
8.1
−63.3
109.8
D, H, AL, W

10
322
9.3
10.1
3.9
−26.4
D, CT, AL, A

11
299
9.4
9.8
−1.1
−16.6
D, CT, AL

12
305
9.5
9.6
−2.1
−14.8
D, CT, AL

13
318
9.3
9.5
−12.3
6
D, CT, AL

14
360
8.9
9.4
−9.9
2
D, CT, AL

15
264
9.3
8.7
−31.4
44.2
D, CT, AL

16
364
9.3
9.0
−25.9
33.2
D, CT, AL

17
360
8.9
9.1
−26.3
34.8
D, CT, AL

18
342
9.2
9.4
−18.2
18
D, CT, AL

19
326
9
9.3
−14.3
10.6
D, CT, AL

20
308
8.9
8.7
−16
14.2
D, CT, AL

21
263
9.3
12.9
55
−128.6
D, CT, AL, NT, Co,

Sp

22
258
9.5
22
59.9
−138.8
D, CT, AL, NT, CN,

M

* 23
240
9.7
7.9
−69.0
118.6
D, CT

24
260
9.6
8
−58.0
96.8
D, CT, AL

25
280
9.2
13.4
59
−136.4
D, CT, AL, NT

* 26
Not evaluated due to
—
—
—
—

not fired

* 27
340
9
7.7
−67.7
117.4
D, AL

* 28
220
7
8.5
5.5
−25
CT, AL, Ce

* 29
Not evaluated due to
—
—
—
—

not fired

* 30
310
9.4
25
99.9
−218.6
D, CT, AL

Sample numbers marked with * are not within the scope of the present invention.

** D: Diopside, H: Hardystonite, Ce: Celsian, Co: Cordierite, G: Garnite, W: Willemite, Sp: Spinel, M: Mullite, CT: CaTiO3, ST: SrTiO3, AL: Al2O3, CN: Ca2Nb2O7, NT: Nd2Ti2O7, A: Anorthite

[0069] As is apparent from the results of Table 2, in the samples Nos. 1 to 8, 10 to 22, 24 and 25, any dielectric ceramic composition could be fired together with a low-resistance conductor such as Ag or Cu at a temperature within a range from 850 to 1050° C.

[0070] These samples had excellent dielectric characteristics as follows: the relative dielectric constant is 8 to 22, the three-point bending strength of the ceramics is 250 MPa or larger, the temperature coefficient of the resonant frequency is 0±60×10−6/° C., and the temperature coefficient of the electrostatic capacity is 0±150×10−6/° C. Particularly, in the sample wherein the temperature coefficient of the electrostatic capacity of the dielectric ceramics is controlled to 0+40×10−6/° C., the temperature coefficient of the electrostatic capacity was 0±70×10−6/° C.

[0071] On the other hand, in the samples Nos. 9, 23 and 26 to 30, which do not contain calcium titanate or contain the diopside crystallized glass powder and calcium titanate in the amount that is not within a scope of the present invention, the three-point bending strength was smaller than 250 MPa or the temperature coefficient of the resonant frequency was not within a range of 0±60×10−6/° C.

Example 2

[0072] In the same manner as in Example 1, except that a strontium titanate powder (purity: 99% or higher) having a mean particle size of 2 μm was used in place of the calcium titanate powder used as the raw powder in Example 1, a dielectric ceramics was produced and evaluated. The composition is shown in Table 3 and the evaluation results are shown in Table 4.

3TABLE 3GlassFiringCom-ST **Filler composition (wt. %) ***temp.No.ponentwt. %(wt. %)ALTiZrMTBTLTNTCNSZCZ° C.31A6093010000000090032A6552901000000090033A6363001000000090034A7222500100000089035A6512110001110 00090036A601370000010 10 001050 37B6093010000000091038B7092001000000089039B8010900100000085040B7262200000000091041B6273000000001091042B5274000000000191043B7452100000000091044B6553000000000091045B5553900000001091046B5364100000000091047B5464000000000091048B5020200000010 0001050 49B454000000010 5001050 * 50 B934300000000085051B6323500000000085052B3020400000010 0001050 * 53 B30565000000000Not fired* 54 B4045150000000001050 Sample numbers marked with * are not within the scope of the present invention. ** ST: SrTiO3 *** AL: Al2O3, Ti: TiO2, Zr: ZrO2, MT: MgTiO3, BT: BaTi4O9, LT: La2Ti2O7, NT: Nd2Ti2O7, CN: Ca2Nb2O7, SZ: SrZrO3, CZ: CaZrO3

[0073]

4

TABLE 4

Thermel
Characteristics

Bending
expansion
at 9 to 15 GHz

strength
coefficient ×

τ f ×
TCC ×
Crystal phase in

No.
MPa
10−6/° C.
ε r
10−6/° C.
10−6/° C.
dielectric ceramics **

31
250
8.7
10.1
53.6
−124.6
D, ST, H, AL, W, G

32
270
8.7
9.2
13.8
−45
D, ST, H, AL, W

33
305
8.7
9.8
23.8
−65
D, ST, H, AL, W

34
255
8.5
8.7
−16.1
15.2
D, ST, H, AL, W

35
250
8.7
12.1
55.0
−127.4
D, ST, H, AL, W, N

T, Ce

36
255
8.7
15.5
59.0
−135.4
D, ST, H, AL, W, N

T, CN

37
312
9.4
9.7
53.6
−126
D, ST, AL, A

38
305
9.5
9.4
53.6
−126.2
D, ST, AL

39
305
9.7
9.2
59.9
−139.2
D, ST, AL

40
305
9.4
9.9
23.8
−66.4
D, ST, AL

41
302
9.4
9.1
33.7
−86.2
D, ST, AL

42
255
9
8.9
33.7
−85.4
D, ST, AL

43
255
9.4
8.3
13.8
−46.4
D, ST, AL

44
350
9.4
8.6
13.8
−46.4
D, ST, AL

45
350
9
8.7.
13.8
−45.6
D, ST, AL

46
350
9.3
9.0
23.8
−66.2
D, ST, AL

47
350
9.1
8.9
23.8
−65.8
D, ST, AL

48
290
9.4
12.5
55
−128.8
D, CT, AL, NT, Co,

Sp

49
270
9.6
21.5
59.9
−139
D, CT, AL, NT, C

N, M

* 50
220
9.8
7.5
3.8
−27.2
D, ST

51
255
9.8
8
−16.4
13.2
D, ST, AL

52
255
9.3
13
59.0
−136.6
D, ST, AL, NT

* 53
Not evaluated due to
—
—
—
—

not fired

* 54
295
9.6
24.5
99.9
−219
D, ST, AL

Sample numbers marked with * are not within the scope of the present invention.

** D: Diopside, H: Hardystonite, Ce: Celsian, Co: Cordierite, G: Garnite, W: Willemite, Sp: Spinel, M: Mullite, CT: CaTiO3, ST: SrTiO3, AL: Al2O3, CN: Ca2Nb2O7, NT: Nd2Ti2O7, A: Anorthite

[0074] As is apparent from the results of Table 4, in the samples Nos. 31 to 49, 51 and 52 of the present invention, any dielectric ceramic composition could be fired together with a low-resistance conductor such as Ag or Cu at a temperature within a range from 850 to 1050° C.

[0075] These samples had excellent dielectric characteristics as follows: the relative dielectric constant is 8 to 21.5, the three-point bending strength of the ceramics is 250 MPa or larger, the temperature coefficient of the resonant frequency is within a range from −16.4×10−6/° C. to 59.9×10−6/° C., and the temperature coefficient of the electrostatic capacity is within a range from −139.2×10−6/° C. to 15.2×10−6/° C.

[0076] On the other hand, in the samples Nos. 50, 53 and 54 which contain the diopside crystallized glass powder and strontium titanate that is not within a scope of the present invention, sintering could not be conducted, or the three-point bending strength was smaller than 250 MPa or the temperature coefficient of the resonant frequency was not within a range of 0±60×10−6/° C.

Example 3

[0077] In the same manner as in Example 1, except that a mixed powder of a calcium titanate powder and a strontium titanate powder, each having a mean particle size of 2 μm and a purity of 99% or higher, was used in place of the calcium titanate powder used as the raw powder in Example 1, a dielectric ceramics was produced and evaluated. The composition is shown in Table 5 and the evaluation results are shown in Table 6.

5TABLE 5GlassFiringCom-CT **ST **Filler composition (wt. %) ***temp.No.ponentwt. %(wt. %)(wt. %)ALTiZrMTBTLTNTCNSZCZ° C.55B58343500000000090056B58163500000000090057B48120210000010 00090058B48139 20000010 00093059B7271200000010 00093060A60413500000000093061A554140000000000900** CT: CaTiO3, ST: SrTiO3 *** AL: Al2O3, Ti: TiO2, Zr: ZrO2, MT: MgTiO3, BT: BaTi4O9, LT: La2Ti2O7, NT: Nd2Ti2O7, CN: Ca2Nb2O7, SZ: SrZrO3, CZ: CaZrO3

[0078]

6

TABLE 6

Thermel
Characteristics

Bending
expansion
at 9 to 15 GHz

strength
coefficient ×

τ f ×
TCC ×
Crystal phase in

No.
MPa
10−6/° C.
ε r
10−6/° C.
10−6/° C.
dielectric ceramics **

55
290
9.3
9.0
−29.9
41.2
D, CT, H, AL, ST

56
277
9.4
8.9
−39.9
61
D, CT, H, AL, ST

57
260
9.5
15.0
−50.0
81
D, CT, H, AL, ST,

NT

58
260
9.5
21.0
−59.0
99
D, CT, H, AL, ST,

NT

59
309
9.3
9.3
−16.5
14.4
D, CT, ST, AL

60
268
8.5
9.1
−16.9
16.8
D, CT, ST, H, AL,

W

61
250
8.5
8.0
−20.9
24.8
D, CT, ST, H, AL,

W

** D: Diopside, H: Hardystonite, W: Willemite, ST: SrTiO3, AL: Al2O3, NT: Nd2Ti2O7

[0079] As is apparent from the results of Table 6, in the samples Nos. 55 to 61 of the present invention, any dielectric ceramic composition could be fired together with a low-resistance conductor such as Ag or Cu at a temperature within a range from 900 to 930° C.

[0080] These samples had excellent dielectric characteristics as follows: the relative dielectric constant is 8 to 21, the three-point bending strength of the ceramics is 250 MPa or larger, the temperature coefficient of the resonant frequency is within a range from −59×106/° C. to 16.5×10−6/° C., and the temperature coefficient of the electrostatic capacity is within a range from 14.4×10−6/° C. to 99×10−6/° C. Particularly, in the sample wherein the temperature coefficient of the electrostatic capacity of the dielectric ceramics is controlled to 0+40×10−6/° C., the temperature coefficient of the electrostatic capacity was 0+70×10−6/° C.

Example 4

[0081] First, a glass frit which is a crystallized glass powder capable of depositing a diopside crystal, CaTiO3, SrTiO3 and Al2O3, TiO2, ZrO2, MgTiO3, BaTi4O9, La2Ti2O7, Nd2Ti2O, Ca2Nb2O7, SrZrO3 and CaZrO3 powders, each having purity of 99% or higher, and Fe2O3, Cr2O3, ZnO, CuO, Ag2O, Co3O4, MnO2, CeO2 and R2O3 (R represents a rare earth element) were weighed and mixed with water in proportions shown in Tables 7 to 9 in wet process (medium: isopropyl alcohol) for 20 hours in a ball mill using ZrO2 balls to obtain a ground mixture having a particle size of 2.0 μm or smaller.

[0082] The following glass frits were used.

[0083] Glass frit D: 41 wt % SiO2-23 wt % CaO-15 wt % MgO-21 wt % ZnO

[0084] Glass frit E: 49 wt % SiO2-33 wt % CaO-18 wt % MgO

[0085] In the sample No. 89, the glass flit C was used as Comparative Example. Using the resulting mixture, a dielectric ceramics was produced and evaluated in the same manner as in Example 1. Discoloration and color tone of the dielectric ceramics were visually observed. The results are shown in Tables 10 to 12.

7TABLE 7GlassAdditive compositionCom-CT **Filler composition (wt. %) ***(parts by weight)No.ponentwt. %(wt. %)ALTiZrMTBTLTNTCNSZCZFe2O3Cr2O3ZnO62D6010291000000000.10063D7010191000000000.10.1064D655290100000000.10.10.165D687240100000000.10066D723240010000000.20067D755200000000000.20068D6513100001110 0000.10.5069D601550000010 10 000.110* 70 D600400000000000.10171E609301000000000.10072E709200000000000.10073E801091010000000.10074E626290100000100.10075E528390000000010.10076E746200000000000.10077E646300000000000.10078E546400000000000.10079E587350000000000.10080E537400000000000.50081E4874500000000010082E5020200000010 0001.50083E454000000010 500200* 84 E95500000000002.20085E90260000000000.10086E3020400000010 0000.100* 87 E2040400000000000.100* 88 E70030000000000000* 89 C601030000000000111* 90 E305650000000000.100* 91 E404550000000000.0500Additive composition(parts by weight)R2O3 (R representsFiringrare-earth element)temp.No.CuOAg2OCo3O4MnO2CeO2Y2O3La2O3Nd2O3Sm2O3Er2O3° C.620000000000900630000000000900640000000000900650.10000000009006600000000008906700000000008506800000000009006900000000001050 * 70 00000000008907110000000009107201000000008907300100000008507400001000009107500000100009107600000010009107700000001009107800000000109107900000000019108000000000009108100000000009308200000000001000 8300000000001050 * 84 00000000008508500000000008508600000000001050 * 87 0000000000Notfired* 88 0000000000900* 89 0000000000900* 90 0000000000Notfired* 91 00000000001050 Sample numbers marked with * are not within the scope of the present invention. ** CT: CaTiO3 *** AL: Al2O3 Ti: TiO2, Zr: ZrO2, MT: MgTiO3, BT: BaTi4O9, LT: La2Ti2O7, NT: Nd2AL, Ti2O7, CN: Ca2Nb2O7, SZ: SrZrO3, CZ: CaZrO3

[0086]

8

TABLE 8

Glass

Additive composition

Com-

ST **
Filler composition (wt. %) ***
(parts by weight)

No.
ponent
wt. %
(wt. %)
AL
Ti
Zr
MT
BT
LT
NT
CN
SZ
CZ
Fe2O3
Cr2O3
ZnO

92
D
60
9
30
1
0
0
0
0
0
0
0
0
0.1
0
0

93
D
65
5
30
0
1
0
0
0
0
0
0
0
0.1
0.1
0.1

94
D
63
6
29
0
1
0
0
0
0
0
0
0
0.1
0
0

95
D
72
2
25
0
0
1
0
0
0
0
0
0
0.2
0
0

96
D
65
12
11
0
0
0
1
1
10
0
0
0
0.1
0.5
0

97
D
60
13
7
0
0
0
0
0
10
10
0
0
0.1
1
0

* 98
D
60
0
40
0
0
0
0
0
0
0
0
0
0.1
0
1

99
E
60
9
30
1
0
0
0
0
0
0
0
0
0.1
0
0

100
E
70
9
20
0
1
0
0
0
0
0
0
0
0.1
0
0

101
E
80
10
9
0
0
1
0
0
0
0
0
0
0.1
0
0

102
E
72
6
21
0
0
0
0
0
0
0
0
0
0.1
0
0

103
E
62
7
30
0
0
0
0
0
0
0
1
0
0.1
0
0

104
E
52
7
40
0
0
0
0
0
0
0
0
1
0.1
0
0

105
E
74
5
21
0
0
0
0
0
0
0
0
0
0.1
0
0

106
E
65
5
30
0
0
0
0
0
0
0
0
0
0.1
0
0

107
E
55
5
40
0
0
0
0
0
0
0
1
0
0.1
0
0

108
E
53
6
36
0
0
0
0
0
0
0
0
0
0.1
0
0

109
E
54
6
40
0
0
0
0
0
0
0
0
0
0.5
0
0

110
E
50
20
20
0
0
0
0
0
10
0
0
0
1.5
0
0

111
E
45
40
0
0
0
0
0
0
10
5
0
0
2
0
0

* 112
E
93
4
0
0
0
0
0
0
0
0
0
0
2.2
0
0

113
E
63
2
9
0
0
0
0
0
0
0
0
0
0.1
0
0

114
E
30
20
40
0
0
0
0
0
10
0
0
0
0.1
0
0

* 115
E
30
5
65
0
0
0
0
0
0
0
0
0
0.1
0
0

* 116
E
40
45
5
0
0
0
0
0
0
0
0
0
0.05
0
0

Additive composition

(parts by weight)

R2O3 (R represents
Firing

rare-earth element)
temp.

No.
CuO
Ag2O
Co3O4
MnO2
CeO2
Y2O3
La2O3
Nd2O3
Sm2O3
Er2O3
° C.

92
0
0
0
0
0
0
0
0
0
0
900

93
0
0
0
0
0
0
0
0
0
0
900

94
0.1
0
0
0
0
0
0
0
0
0
900

95
0
0
0
0
0
0
0
0
0
0
890

96
0
0
0
0
0
0
0
0
0
0
900

97
0
0
0
0
0
0
0
0
0
0
1050

* 98
0
0
0
0
0
0
0
0
0
0
890

99
1
0
0
0
0
0
0
0
0
0
910

100
0
1
0
0
0
0
0
0
0
0
890

101
0
0
1
0
0
0
0
0
0
0
850

102
0
0
0
1
0
0
0
0
0
0
910

103
0
0
0
0
1
0
0
0
0
0
910

104
0
0
0
0
0
1
0
0
0
0
910

105
0
0
1
0
0
0
1
0
0
0
910

106
0
0
0
1
0
0
0
1
0
0
910

107
0
0
0
0
0
0
0
0
1
0
910

108
0
0
0
0
0
0
0
0
0
1
910

109
0
0
0
0
0
0
0
0
0
0
910

110
0
0
0
0
0
0
0
0
0
0
1050

111
0
0
0
0
0
0
0
0
0
0
1050

* 112
0
0
0
0
0
0
0
0
0
0
850

113
0
0
0
0
0
0
0
0
0
0
850

114
0
0
0
0
0
0
0
0
0
0
1050

* 115
0
0
0
0
0
0
0
0
0
0
Not

fired

* 116
0
0
0
0
0
0
0
0
0
0
1050

Sample numbers marked with * are not within the scope of the present invention.

** ST: SrTiO3

*** AL: Al2O3 Ti: TiO2, Zr: ZrO2, MT: MgTiO3, BT: BaTi4O9, LT: La2Ti2O7, NT: Nd2, Ti2O7, CN: Ca2Nb2O7, SZ: SrZrO3, CZ: CaZrO3

[0087]

9

TABLE 9

Glass

Additive composition

Com-

CT **
ST **
Filler composition (wt. %) ***
(parts by weight)

No.
ponent
wt. %
(wt. %)
(wt. %)
AL
Ti
Zr
MT
BT
LT
NT
CN
SZ
CZ
Fe2O3
Cr2O3
ZnO

117
E
58
5
2
35
0
0
0
0
0
0
0
0
0
0.1
0
0

118
E
58
3
4
35
0
0
0
0
0
0
0
0
0
0.1
0
0

119
E
58
1
6
35
0
0
0
0
0
0
0
0
0
0.1
0
0

120
E
48
1
20
21
0
0
0
0
0
10
0
0
0
0.1
0
0

121
E
48
1
39
2
0
0
0
0
0
10
0
0
0
0.1
0
0

122
E
72
7
1
20
0
0
0
0
0
10
0
0
0
0.1
0
0

123
D
60
4
1
35
0
0
0
0
0
0
0
0
0
0.1
0.1
0

124
D
55
4
1
40
0
0
0
0
0
0
0
0
0
0.1
0.2
0

R2O3 (R represents
Firing

rare-earth element)
temp.

No.
CuO
Ag2O
Co3O4
MnO2
CeO2
Y2O3
La2O3
Nd2O3
Sm2O3
Er2O3
° C.

117
0
0
0
0
0
0
0
0
0
0
900

118
0
0
0
0
0
0
0
0
0
0
900

119
0
0
0
0
0
0
0
0
0
0.5
900

120
0
0
0
0
0
0
0
0
0
0.5
930

121
0
0
0
0
0
0
0
0
0
0.5
930

122
0
0
0
0
0
0
0
0
0
0.5
930

123
0
0.1
0
0
0
0
0
0
0
0
900

124
0
0
0
0
0
0
0
0
0
0
900

** CT: CaTiO3, ST: SrTiO3

*** AL: Al2O3, Ti: TiO2, Zr: ZrO2, MT: MgTiO3, BT: BaTi4O9, LT: La2Ti2O7, NT: Nd2Ti2O7, CN: Ca2Nb2O7, SZ: SrZrO3, CZ: CaZrO3

[0088]

10

TABLE 10

Thermel
Characteristics

Bending
expansion
at 9 to 15 GHz
Coloration or

strength
coefficient ×

τ f ×
TCC ×
Prevention of
Color
Crystal phase in

No.
MPa
10−6/° C.
ε r
10−6/° C.
10−6/° C.
discoloration
tone
dielectric ceramics **

62
251
8.5
9.8
18.8
−54.6
Yes
Red
D, CT, H, AL, W, G

63
281
8.5
10.6
22.7
−62.4
Yes
Brown
D, CT, H, AL, W, G

64
274
8.5
9.2
−16.6
16.2
Yes
Brown
D, CT, H, AL, W

65
308
8.5
9.8
−2.2
−12.58
Yes
Brown
D, CT, H, AL, W

66
270
8.4
8.6
−35.1
53.4
Yes
Red
D, CT, H, AL, W

67
265
8.5
9.1
−21.7
26.4
Yes
Red
D, CT, H, AL, W

68
263
8.5
12.3
59.3
−135.6
Yes
Brown
D, CT, ST, H, AL, W

69
252
8.5
15.7
59.0
−135
Yes
Brown
D, CT, ST, H, AL, W,

NT, CN

* 70
276
8.4
7.9
−63.3
109.8
Yes
Brown
D, H, AL, W

71
322
9.3
9.9
3.9
−26.4
Yes
Brown
D, CT, AL, A

72
299
9.4
9.7
−1.1
−16.6
Yes
Brown
D, CT, AL

73
305
9.5
9.4
−2.1
−14.8
Yes
Brown
D, CT, AL

74
318
9.3
9.3
−12.3
6
Yes
Brown
D, CT, AL

75
360
8.9
9.2
−9.9
2
Yes
Red
D, CT, AL

76
264
9.3
8.5
−31.4
44.2
Yes
Red
D, CT, AL

77
364
9.3
8.8
−25.9
33.2
Yes
Red
D, CT, AL

78
360
8.9
8.9
−26.3
34.8
Yes
Red
D, CT, AL

79
342
9.2
9.2
−18.2
18
Yes
Red
D, CT, AL

80
326
9
9.1
−14.3
10.6
Yes
Red
D, CT, AL

81
308
8.9
8.5
−16
14.2
Yes
Red
D, CT, AL

82
263
9.3
12.7
55
−128.6
Yes
Red
D, CT, AL, NT, Co,

Sp

83
258
9.5
21.8
59.9
−138.8
Yes
Red
D, CT, AL, NT, CN,

M

* 84
240
9.7
7.7
−69.0
118.6
Yes
Red
D, CT

85
260
9.6
7.8
−58.0
96.8
Yes
Red
D, CT, AL

86
280
9.2
13.2
59
−136.4
Yes
Red
D, CT, AL, NT

* 87
Not evaluated due to
—
—
—
Yes
Red
—

not fired

* 88
340
9
7.7
−67.7
117.4
No
White
D, AL

* 89
220
7
8.3
5.5
−25
Yes
Brown
CT, AL, Ce

* 90
Not evaluated due to
—
—
—
Yes
Red
—

not fired

* 91
310
9.4
24.8
99.9
−218.6
No
White
D, CT, AL

Sample numbers marked with * are not within the scope of the present invention.

** D: Diopside, H: Hardystonite, Ce: Celsian, Co: Cordierite, G: Garnite, W: Willemite, Sp: Spinel, M: Mullit CT: CaTiO3, ST: SrTiO3, AL: Al2O3, CN: Ca2Nb2O7, NT: Nd2Ti2O7, A: Anorthite

[0089]

11

TABLE 11

Thermal
Characteristics

Bending
expansion
at 9 to 15 GHz
Coloration or

strength
coefficient ×

τ f ×
TCC ×
Prevention of
Color
Crystal phase in

No.
MPa
10−6/° C.
ε r
10−6/° C.
10−6/° C.
discoloration
tone
dielectric ceramics **

92
250
8.7
9.9
53.6
−124.6
Yes
Brown
D, ST, H, AL, W, G

93
270
8.7
9.0
13.8
−45
Yes
Brown
D, ST, H, AL, W

94
305
8.7
9.6
23.8
−65
Yes
Brown
D, ST, H, AL, W

95
255
8.5
8.5
−16.1
15.2
Yes
Red
D, ST, H, AL, W

96
250
8.7
11.9
55.0
−127.4
Yes
Brown
D, ST, H, AL, W,

NT, Ce

97
255
8.7
15.3
59.0
−135.4
Yes
Brown
D, ST, H, AL, W,

NT, CN

98
270
8.5
7.8
−36.0
55
Yes
Brown
D, H, AL, W

99
312
9.4
9.5
53.6
−126
Yes
Brown
D, ST, AL, A

100
305
9.5
9.2
53.6
−126.2
Yes
Brown
D, ST, AL

101
305
9.7
9.0
59.9
−139.2
Yes
Brown
D, ST, AL

102
305
9.4
9.7
23.8
−66.4
Yes
Brown
D, ST, AL

103
302
9.4
8.9
33.7
−86.2
Yes
Brown
D, ST, AL

104
255
9
8.7
33.7
−85.4
Yes
Red
D, ST, AL

105
255
9.4
8.1
13.8
−46.4
Yes
Red
D, ST, AL

106
350
9.4
8.4
13.8
−46.4
Yes
Red
D, ST, AL

107
350
9
8.5
13.8
−45.6
Yes
Red
D, ST, AL

108
350
9.3
8.8
23.8
−66.2
Yes
Red
D, ST, AL

109
350
9.1
8.7
23.8
−65.8
Yes
Red
D, ST, AL

110
290
9.4
12.3
55
−128.8
Yes
Red
D, CT, AL, NT, Co,

Sp

111
270
9.6
21.3
59.9
−139
Yes
Red
D, CT, AL, NT, CN,

M

* 112
220
9.8
7.3
3.8
−27.2
Yes
Red
D, ST

113
255
9.8
7.4
−16.4
13.2
Yes
Red
D, ST, AL

114
255
9.3
12.8
59.0
−136.6
Yes
Red
D, ST, AL, NT

* 115
Not evaluated due to
—
—
—
Yes
—
—

not fired

* 116
295
9.6
24.3
99.9
−219
No
—
D, ST, AL

Sample numbers marked with * are not within the scope of the present invention.

** D: Diopside, H: Hardystonite, Ce: Celsian, Co: Cordierite, G: Garnite, W: Willemite, Sp: Spinel, M: Mulli CT: CaTiO3, ST: SrTiO3, AL: Al2O3, CN: Ca2Nb2O7, NT: Nd2Ti2O7, A: Anorthite

[0090]

12

TABLE 12

Thermel
Characteristics

Bending
expansion
at 9 to 15 GHz
Coloration or

strength
coefficient ×

τ f ×
TCC ×
Prevention of
Color
Crystal phase in

No.
MPa
10−6/° C.
ε r
10−6/° C.
10−6/° C.
discoloration
tone
dielectric ceramics **

117
282
9.2
8.8
−19.9
21.4
Yes
Red
D, CT, H, AL, ST

118
290
9.3
8.8
−29.9
41.2
Yes
Red
D, CT, H, AL, ST

119
277
9.4
8.7
−39.9
61
Yes
Red
D, CT, H, AL, ST

120
260
9.5
14.8
−50.0
81
Yes
Red
D, CT, H, AL, ST, NT

121
260
9.5
20.8
−59.0
99
Yes
Red
D, CT, H, AL, ST, NT

122
309
9.3
9.1
−16.5
14.4
Yes
Red
D, CT, ST, AL

123
268
8.5
8.9
−16.9
16.8
Yes
Brown
D, CT, ST, H, AL, W

124
250
8.5
7.8
−20.9
24.8
Yes
Brown
D, CT, ST, H, AL, W

** D: Diopside, H: Hardystonite, W: Willemite, CT: CaTiO3, ST: SrTiO3, AL: Al2O3, NT: Nd2Ti2O7

[0091] As is apparent from the results of Tables 10 to 12, in the samples Nos. 62 to 69, 71 to 83, 85, 86, 92 to 97, 99 to 111, 113, 114 and 117 to 124 of the present invention wherein calcium titanate, strontium titanate or a mixture of calcium titanate and strontium titanate was used as the filler in the dielectric ceramic composition, any dielectric ceramic composition could be fired together with a low-resistance conductor such as Ag or Cu at a temperature within a range from 850 to 1050° C.

[0092] In spite of performing coloration, these samples had excellent dielectric characteristics as follows: the relative dielectric constant is 8 to 25, the three-point bending strength of the ceramics is 250 MPa or larger, the temperature coefficient of the resonant frequency is within a range of 0±60×10−6/° C., and the temperature coefficient of the electrostatic capacity is within a range of 0±150×10−6/° C.

[0093] On the other hand, in the samples Nos. 70, 84, 87 to 91, 98, 112, 115 and 116 which contain the diopside crystallized glass powder and filler component that is not within a scope of the present invention, the three-point bending strength was smaller than 250 MPa or the temperature coefficient τf of the resonant frequency was not within a range of 0±60×10−6/° C.

Number	Date	Country
2002-19016	Jan 2002	JP
2002-123057	Apr 2002	JP
2002-137578	May 2002	JP

Dielectric ceramic composition and dielectric ceramics

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Priority Claims (3)