This invention relates to single crystal growth in high pressure and high temperature autoclaves and in flux method production of piezoelectric crystals.
Industrial hydrothermal crystal growth and other methods for crystal growth are exceptionally time consuming and require the utilization of a great amount of resources, electricity and personnel, for proper operation. Generally, in laboratories and research and development teams, scientists have the tendency to prefer the most high-quality crystals possible. However, in industrial applications, a balance is required between performance, quality, and crystal growth time. In said industrial applications, the highest quality crystal possible is not necessarily required, therefore meaning that a new method of crystal growth is required to more perfectly strike this balance. It is possible to sacrifice some minor degree of quality to achieve a more economical growth time while still maintaining a working crystal. One existing way to increase the growth rate of hydrothermal crystals is to increase the temperature differential between the growth zone and the dissolving zone. However, this results in a product that is of lower quality than what can be produced via my invention. This invention is addressing another intrinsic property of the some of the crystals grown, in that their solubility is simply too low for standard hydrothermal conditions, like for example, crystals like Gallium Orthophosphate (GaPO4), Berlinite (A1PO4), Gallium Arsenate (GaAsO4) and other Quartz homeotypes. By shifting the nutrients to the seed with a sub-acoustic piezoelectric shaker, even with a nutrient that has low-solubility, the growth rate of the crystal is increased by a two to three-fold growth rate.
While it has been thought of to use a mechanical stirrer in the past, this method is both dangerous to use and cumbersome, making it impractical for use in high pressure and high temperature autoclaves. Furthermore, in the way that mechanical stirring is broadly applied, the action is in layman's terms “a back and forth action”. The dissolved nutrients are shifted both towards the crystal seed and away from it, making overall progress limited. How this can instead be corrected in my invention is through the use of sub-acoustic piezoelectric shakers that produce waveforms that can produce pulses to solely push the nutrients towards the seed and prevent material from shifting back to its original position. These waveforms can correspondingly be changed to suit the specific growth needs of the crystal being grown.
It is also especially important to note the secondary application of the invention that would serve both a useful and important role with very little further change. This is, to monitor the ‘health’ of the autoclave during crystal growth. No such similar idea has been put into practice or discussed before, limiting any discussion on prior art. To monitor the ‘health’ of the autoclave, a sensor can be affixed to the appropriate location. During the operation of both the autoclave and shaker, the sensor will collect consistent trending data received from the inside of the autoclave. This data can thereupon be read and analyzed for any alarming abnormalities. The sudden rupture of a high-pressure autoclave can produce an explosion that is an incredibly dangerous event that can result in the loss of assets, personnel, and investment. That is why, if any method exists that can prevent such a catastrophe, even if just shortly ahead of time, it is very important information to both current and prospective users of autoclaves for crystal growth. Some examples of sensors that can be used to monitor the health of the autoclave include accelerometers and acoustic microphones.
A dynamic mechanical movement of the nutrient in the direction of the seeds requires physical displacement of the molecules that are transported. The lower the frequency of such mechanical forces, the larger the displacement obtained. Therefore, it is preferable to use low frequencies in the level of sub-acoustic to acoustic frequencies, instead of ultrasonics or higher frequencies in the megahertz range due to the fact that they could be destructive to the crystal structure during its growth. Some researchers utilize sonochemistry to achieve faster chemical reactions, though not necessarily for achieving crystal growth, but instead to achieve higher yields of a chemical reaction in a disorganized structure, very much in contrast to the organized nature of crystals.
In accordance with one embodiment of my invention, a standard high-pressure, high-temperature autoclave used for crystal growth will have a piezoelectric shaker attached to enhance diffusional transport of nutrients to the growth zone. It is another improvement to the design to apply a sensor to the appropriate location to determine the health of the growth process and the apparatus. Also, it is also understandable that my method is applicable to high-temperature crystal growth via the flux method. In the same vein as the hydrothermal method, the flux method suffers from the same shortcoming of having an inefficient for industrial purposes process by which to shift nutrients to the crystal seed.
The foregoing and other objects, features, and advantages of my invention will be apparent from the following more particular description of a preferred embodiment of the invention, as illustrated in the accompanying drawings. The drawings are not necessarily made to scale, but instead are used to detail the nature and principle of the invention. The preferred embodiment(s) of the present invention is/are described in conjunction with the associated drawings in which like features are indicated with like reference numerals and in which
On one of the embodiments of my invention, a piezoelectric shaker 6 is located on the top of the autoclave 1 (
By utilizing, the apparatus as described above, a faster crystal growth rate can be achieved, to a level that the quality of the crystals is not compromised. As the industry stands today, the level of quality demanded results in growth periods for crystals that are entirely too long for proper industrial mass production and result in the atrocious wasting of valuable manpower, energy, and time. This embodiment can be used to grow just about any hydrothermal crystal from Quartz to Sapphire.
On another of the embodiments of my invention (
Because many of the crystals grown by autoclave 1 are piezoelectric and the shaker 6 used is piezoelectric, the resulting phenomena could be that a combination of ideal conditions will result in the growing crystals aligning with the signal with synergy, similar to the phenomena of swinging pendulums aligning over time at a particular resonant frequency. The net effect is an improved crystal structure and rate of growth accelerated by my invention.
The same approach utilized onto an autoclave can be applied to the flux method, as the piezocicctric shaker might be attached to the crucible and produce the same effects of accelerating the diffusional transfer of nutrient to the seeds. The flux method can be used to grow also Gallium ortho Phosphate and other crystals grown by the melt, or in a flux.
The foregoing description of the preferred embodiment of the invention has been presented for the purposes of illustration and description. While this invention has been particularly shown and described with reference to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit and scope of the invention in the following claims. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of the above teachings. It is intended that the scope of the invention be limited not with this detailed description, but rather by the claims appended hereto.