Patent Grant
7250088
The invention relates to an apparatus and a method for manufacturing a directionally solidified columnar grained article.
The directional solidification process is a version of investment casting in which a cavity resembling the desired finished piece is defined by a ceramic shell mold. The mold is placed on a cooling surface, preheated to a desired temperature in a high temperature environment, filled with a liquid alloy, and withdrawn from the high temperature environment into a lower temperature environment (defined by a vacuum or liquid coolant or cooling by other means) at a specific rate so as to induce solidification of the liquid alloy in a directional fashion, starting at the cooling plate. A casting furnace is known for example from U.S. Pat. No. 3,532,155, furnaces working with gas cooling are known from the U.S. Pat. No. 3,690,367 or the European patent application EP-A1-749,790, and a LMC furnace is described in U.S. Pat. No. 3,763,926.
Directionally solidified articles with a columnar grain structure contain a multitude of grains oriented within a certain controlled and generally narrow range of angles relative to the main direction of stress in the article during service. For example, the direction of centrifugal force in a turbine blade is considered along the main axis of the blade and runs from root to blade tip. The preferred direction of grain growth is always parallel to the direction of heat flow during directional solidification.
Due to the nature of the directional solidification process, this main axis of the component to be solidified is normally oriented vertically so that the grains naturally grow along the main stress axis. The cooling plate is oriented horizontally. This is described by Chandley in U.S. Pat. No. 3,248,764 and by VerSnyder in U.S. Pat. No. 3,260,505. In these disclosures, an open-ended “starter zone” incorporated into the bottom of the ceramic casting mould is placed directly over a chill plate.
When liquid alloy is poured into the ceramic shell mold, it impinges on the chill plate and solidification starts immediately, where many randomly oriented grains begin growing at the chill plate. In a “starter zone” which restricts growth to the direction parallel to the imposed thermal gradient and solidification direction (perpendicular to the advancing solid front—perpendicular also to the cooling plate), the grains growing most closely to the direction of heat flow (in this case, the vertical) will grow the fastest and crowd out those that have larger angles to this preferred direction.
At leaving the exit of the starter section there are typically many grains growing approximately in the same direction. In this sense, starter zones are grain selectors in that they impede the growth of grains of undesirable crystallographic orientations into the article to be manufactured. Typical starter zones consist simply of rectangular or angled blocks connected directly to the article to be solidified with a columnar grained structure. Typically the growth direction is vertical and the chill plate and induced isotherms (and solid front) are horizontal. For columnar grained articles, the starter block is connected directly to an article-defining cavity in the shell mold.
A modification of this is given by US 4,475,582, US 4,548,255 and US 4,180,119 in which a smaller starter block is used, at the top of which there is a helical “pig tail” type grain selector which is more effective than the vertically oriented starter—so much so that only one dendrite with an orientation very closely oriented to the vertical exits at the top of the helical selector and enters the article, thereby imparting the article with a single crystal grain structure. The helical selector, in effect, selects out the single best oriented dendrite or grain from those exiting the first starter which are generally vertically oriented but within a certain distribution of angles to the vertical. A less effective means of selecting a vertically oriented dendrite is with a simple thin and elongated growth section leading to the article-defining cavity, as disclosed by Bridgman in U.S. Pat. No. 1,793,672.
In both of the above cases (columnar grained and single crystal selectors) the selectors produce an array of grains or a single grain with random rotational orientations where the axis of rotation is equivalent to the direction of preferred growth (generally the vertical)—this is referred to as the secondary orientation. In many cases the random secondary orientation is not a problem for the design of a single crystal article (the well known advantages of a defined primary orientation are much more important) and hence many are cast with random secondary orientations. However in some cases there are definite advantages to growing a single crystal article having a defined secondary orientation.
For these cases there exist practices and disclosures for selecting grains with a controlled secondary orientation. These fall into two categories: using seed crystals (also described by Bridgman in U.S. Pat. No. 1,793,672) and using special grain selectors. Seed crystals are generally themselves small cylindrical single crystal castings fit into the bottom of the shell mold, and liquid metal filing the shell mold impinges on this rather than on a chill plate. If the seed crystal is properly used, solidification will start epitaxially at the seed-liquid interface, continuing desirable primary and secondary crystallographic orientations of the seed throughout the article-defining cavity.
These seed crystals are not without problems, being costly to produce and requiring special conditions during casting to produce the desired single grain in the article. To reduce the cost they are made small, but this also makes them difficult to handle and difficult to reuse. They constitute another handling operation for the shell mold and impose a holding chamber on the shell mold design. The cavities designed to contain the seeds must function precisely to avoid liquid metal leaking around the sides of the seeds which would nucleate new, randomly oriented grains. For this reason there are several disclosures for using single crystal selectors in addition to the seed in order to block out the continued growth of the random grains (see US 4,714,101, US 4,475,582). Finally, the small passage way containing the seeds and the passage from the seeds to the article-defining cavity in the shell mold almost completely eliminate any significant heat transfer through the metal to the cooling plate, thus slowing down solidification during the casting process. This increases the furnace time required to cast the part, and hence increases its cost.
Because of the problems associated with seeds there have also been disclosures of specially designed single crystal selectors which, by themselves, produce single grains with the desired primary vertical orientation and also a desired secondary orientation. For example, U.S. Pat. No. 3,580,324 discloses a selector with right angle bends and horizontal growth directions to select a secondary orientation. U.S. Pat. No. 5,062,468 discloses a selector design that produces dendrites which are almost always within +/−30° of the desired secondary orientation by using special horizontal growth sections. Numerous other disclosures are given for various means of selecting the secondary orientation of a single grain.
As discussed, there are sometimes advantages for controlling the secondary orientation of the grain for a single crystal article. For a columnar grained article, the random secondary orientation of the columnar grains with respect to the vertical has always been taken as unavoidable and is evidenced by the current standard practice of casting columnar grained articles with such grains of random secondary orientation. However, if it were to be desired to control the secondary orientation of these grains, seeds and selectors would still be the only possible means of achieving this. The same problems of seeds for single crystal articles would exist for seeds to be used for columnar grained castings—and would be much greater. The seeds, being composed of several individual single crystals and generally being much larger in surface area than seeds for single crystal articles would be very expensive. Fitting into the shell mold would be even more problematic. In fact, once a seed is going to be used, greater advantages in properties of the article and simplicity in seeding are maintained simply by using a single seed for the part. The multiple orientation seed is a contradiction in terms, since if all members in the seed were given the same orientation, a single crystal structure would result with the widely known superior properties over columnar grained articles.
It is object to the present invention to produce a novel structured columnar grained article, a method of producing it by means of a novel multiple grain selector and an apparatus for carrying out the method. The columnar grained article will have at least two columnar dendrites or grains having reduced secondary misorientation (compared to random) and may exhibit controlled secondary misorientation in a particular direction relative to some feature or dimension of the article. It is found that an array of growing dendrites can be used to select out a narrower than random distribution of secondary misorientations among several grains with nearly the same effectiveness as a specially designed single crystal selector does for a single grain.
The multiple grain selector consists of a portion of constrained growth in the main direction of heat flow during solidification (that is, the main direction of solidification) which acts to select grains with a desired primary orientation, and a portion which constrains the grains to grow at least partially in the horizontal (secondary) direction so that it is not possible for any grain or dendrite to grow from cooling plate to the article-defining cavity along a continuous path of purely vertical growth. The advantage of the novel structure is that it shows surprisingly stronger transverse properties (low cycle fatigue life, creep rupture life) than those in prior art columnar grained articles due to the reduced secondary misorientation of the columnar grained article.
This will be achieved for a relatively low incremental cost over the normal process and much lower costs in comparison to using multiple seeds or multiple single crystal selectors known from the state of the art.
Another advantage comes from the possibility of choosing a desired secondary orientation relative to the article or some feature of the article (not just the relative misorientation between adjacent grains or dendrites). For example, it may be preferred to center the distribution of secondary orientations around the main direction of transverse loading in the columnar grained article, so as to further maximise transverse lifetime.
A further advantage of this invention over the prior art of single crystal selectors is that the selectors disclosed herein are much larger and more robust than the smaller selector sections known in the state of the art, and Will not suffer from the fragility of the prior art selectors often leading to mold cracking during handling or casting.
A further advantage of the present invention over prior art selectors is that, due to the relatively large cross section of the multi-grain selector, there will still be a substantial amount of heat flow through the metal in the selector to the cooling plate. In some possible embodiments of the invention, with small selector chambers, there will not be a large difference in heat flow to the cooling plate compared to the prior art columnar grained casting processes. This will maintain rapid solidification at the start of casting and help to keep furnace-usage time costs to a minimum.
It will be understood that although the following drawings show relatively large sections for the sake of clarity, the practical use of this invention will minimize the entire selector section size as much as possible to minimize heat flow impacts.
a shows a cross section through a variant of the embodiment according to
b shows a cross section through a variant of the embodiment according to
a shows a variation of the embodiment according to
b shows a cross section through a variation of the embodiment according to
a shows a variation of a cross section through the embodiment of
b shows a variation of a cross section through the embodiment according to
The present invention relates to an apparatus and a method for manufacturing a directionally solidified columnar grained article and to the columnar grained article itself. As shown in
The columnar grained article 3 growing out of the selector section 1 has at least two columnar dendrites or grains having reduced secondary misorientation (compared to random) and may exhibit controlled secondary misorientation in a particular direction relative to some feature or dimension of the columnar grained article 3. It was found that an array of growing dendrites can be used to select out a narrower than random distribution of a secondary misorientations among several grains with nearly the same effectiveness as a specially designed single crystal selector section does for a single grain.
There is no upper limit to the dimensions of thickness X and length Y of primary selector section 5a although there is no significant benefit for Y being more than 50% longer than the overlying columnar grained article 3 dimension (airfoil chord, for example). The selector section 1 may have varying dimensions X and Y, may be irregularly shaped, or may take on any regular shape including curves or straight edged shapes. The selector section 1 may be shaped so as to conform in cross section some part of the columnar grained article 3 being cast, for example, the airfoil of a turbine blade. These basic design principles are applicable to all embodiments disclosed within the
A second embodiment of the invention is shown in
As shown in
The invention is not limited to the embodiment described herein. Any combination of designs of the above mentioned general embodiments may be used as such a multiple step secondary selector section using features taken from more than one design, or using the same selector section design twice. It is possible in any of the above mentioned designs of a selector section 1 that the functionality may be enhanced by the use of special high thermal conductivity or low thermal conductivity materials in any portion of the selector section 1 interior or on the selector section 1 to cooling plate 2 boundary or in conjunction with the shell mold on the selector section 1 surface. Furthermore in any of the above mentioned designs functionality can be enhanced by a locally or generally changing the surface emmissivity of the shell mold anywhere on the surface of the selector-defining cavities.
For all embodiments disclosed herein it is possible that a single mold for directional solidification contains a plurality of selector sections 1 and a plurality of columnar grained articles 3 in order to cast more than one columnar grained article 3 with reduced secondary misorientation simultaneously.
The resulting directionally solidified article has columnar-grained structure in which the columnar grains have a reduced amount of misorientation (compared to random) with respect to each other in the secondary orientation. This can be carried out in such a way that the direction around which the distribution of secondary orientations is centered is controlled with respect to some aspect or dimension of the columnar grained article 3 so as to achieve a desired effect. The distribution of secondary misorientations among the columnar grains of the columnar grained article 3 can be maintained within a maximum limit of approximately 30° or less, with a preferred range of 20° or less, with a most preferred range of 15° or less. The process can be carried out in such a way that the relative misorientations of the columnar grains is varied more or less in a continuous fashion along the transverse dimension of the columnar grained article 3. For example, the, 010. direction may be caused to be approximately perpendicular to the tangent of the airfoil surface at some height on a turbine blade or vane. The relative misorientation between the trailing edge grain and leading edge grain may in this case be quite large, approaching 45°.
In general the practice of using a multi-grain selector section 1 for the purpose of selecting, out a multitude of grains, only those that show a preferred orientation in approximately the same direction (primary) and with reduced rotational misorientation (secondary) with respect to each other where the axis of rotational misorientation is approximately the same as the preferred orientation of the grains. The selector section 1 can be positioned relative to the columnar grained article 3 so that the distribution of secondary orientations of the grains centers approximately around a desired secondary orientation.
The main advantage of this type of a multiple-grain selector section 1 and the resulting novel structure is the stronger transverse properties exhibited by the reduced misorientation columnar grained article. This will be achieved for a relatively low incremental cost over the normal process and much lower costs in comparison with multiple seeds or multiple single crystal selector section as known from the state of the art.
Another advantage comes from the possibility of choosing a desired secondary orientation (not just the relative misorientation between adjacent grains or dendrites). For example, it may be preferred to center the distribution of secondary orientations around the main direction of transverse loading in the columnar grained article, so as to further maximize transverse lifetime.
With some casting furnaces and mold cluster arrangements, it is advantageous to incline the selector section 1 and main cavity at an angle to the vertical (thereby inclining the primary direction of solidification to the vertical) in order to avoid certain casting defects. For this reason the entire selector section 5a, 5b, 5b1, 5b2 and the main cavity may be inclined at an angle to the vertical as illustrated in
A further advantage of this invention over the prior art of single crystal selector sections is that the selector sections disclosed herein are much larger and more robust than the smaller selector sections known in the art. Therefore the selector sections of the invention will not suffer from the fragility of the prior art selector sections often leading to mold cracking during handling or casting.
A further advantage of the present invention over prior art selector sections is that, due to the relatively large cross section of the multi-grain selector section, there will still be a substantial amount of heat flow through the metal in the selector, section to the cooling plate. In some possible embodiments of the invention, with small selector section chambers, there will not be a large difference in heat flow to the cooling plate compared to the prior art columnar grained casting processes. This will maintain rapid solidification and help to keep furnace-usage time costs to a minimum.
| Number | Date | Country | Kind |
|---|---|---|---|
| 99810724 | Aug 1999 | EP | regional |
This application is a divisional of application Ser. No. 09/382,630, filed on Aug. 25, 1999, now U.S. Pat. No. 6,568,456.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1793672 | Bridgman | Feb 1931 | A |
| 3248764 | Chandley | May 1966 | A |
| 3260505 | Ver Snyder | Jul 1966 | A |
| 3532155 | Kane et al. | Oct 1970 | A |
| 3536121 | Piearcey | Oct 1970 | A |
| 3580324 | Copley et al. | May 1971 | A |
| 3690367 | Daniels | Sep 1972 | A |
| 3763926 | Tschinkel et al. | Oct 1973 | A |
| 4180119 | Burd et al. | Dec 1979 | A |
| 4475582 | Giamei et al. | Oct 1984 | A |
| 4548255 | Reiner et al. | Oct 1985 | A |
| 4605452 | Gemma et al. | Aug 1986 | A |
| 4612969 | Burd et al. | Sep 1986 | A |
| 4714101 | Terkelsen | Dec 1987 | A |
| 5062468 | Monte et al. | Nov 1991 | A |
| 5161602 | Chang et al. | Nov 1992 | A |
| 5173255 | Ross et al. | Dec 1992 | A |
| 5275227 | Staub | Jan 1994 | A |
| 5611670 | Yoshinari et al. | Mar 1997 | A |
| 5803967 | Plano et al. | Sep 1998 | A |
| 5899257 | Alleweireldt et al. | May 1999 | A |
| 6217286 | Huang et al. | Apr 2001 | B1 |
| 6800148 | Frasier et al. | Oct 2004 | B2 |
| Number | Date | Country |
|---|---|---|
| 0082100 | Jun 1983 | EP |
| 749790 | Dec 1996 | EP |
| 2724857 | Mar 1996 | FR |
| 2734189 | Nov 1996 | FR |
| Number | Date | Country | |
|---|---|---|---|
| 20030188845 A1 | Oct 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09382630 | Aug 1999 | US |
| Child | 10355138 | US |