Patent Application
20240234432
The present invention relates to a display device including a circuit formed with a transistor, and a method for manufacturing the display device.
Various metal oxides exist and are used for a variety of applications. Indium oxide is a well-known material as a metal oxide and is used as a light-transmitting conductive material which is necessary for liquid crystal displays and the like.
Some metal oxides have semiconductor characteristics. As metal oxides having semiconductor characteristics, for example, there are tungsten oxide, tin oxide, indium oxide, zinc oxide, and the like, and a transistor in which a channel formation region is formed using such a metal oxide having semiconductor characteristics has been proposed (for example, see Patent Documents 1 to 4 and Non-Patent Document 1).
As metal oxides, multi-component oxides as well as single-component oxides are known. For example, InGaO3(ZnO)m (m is a natural number) having a homologous series is known as a multi-component oxide semiconductor including In, Ga, and Zn (see Non-Patent Documents 2 to 4).
In addition, it has been confirmed that an oxide semiconductor layer including such an In—Ga—Zn-based oxide can be used as a channel layer of a transistor (see Patent Document 5, and Non-Patent Documents 5 and 6).
An object of one embodiment of the present invention is to provide a transistor having favorable electric characteristics and high reliability, and a manufacturing method thereof. Another object is to provide a display device to which the transistor is applied and which has favorable display quality and high reliability.
One embodiment of the present invention is a display device in which a transistor including an oxide semiconductor layer is provided. An active matrix substrate of the display device includes a pixel portion and a driver circuit portion. A gate electrode is provided to overlap with a back channel portion of a transistor in at least the driver circuit portion. In manufacture of the transistor, the oxide semiconductor layer is subjected to heat treatment for dehydration or dehydrogenation. After the heat treatment, a protective insulating layer is formed using an insulating inorganic material containing oxygen so as to cover the oxide semiconductor layer.
Through the heat treatment, the carrier concentration is changed.
A transistor having favorable electric characteristics can be manufactured. In particular, a transistor whose threshold voltage is not easily shifted even when it is used for a long term and which has high reliability can be manufactured. With use of such a transistor in at least a driver circuit portion, the reliability of a display device can be improved.
FIGS. 24A1, 24A2, and 24B are diagrams illustrating display devices which are one embodiment of the present invention.
Embodiments and examples of the present invention will be described with reference to the drawings. However, the present invention is not limited to the description below, and those skilled in the art will appreciate that a variety of modifications can be made to the modes and details without departing from the spirit and scope of the present invention. Therefore, the present invention is not interpreted as being limited to the following description in the embodiments and examples. Note that, in all the drawings for explaining the embodiments and examples, the same portions or portions having the same functions are denoted by the same reference numerals, and the description thereof will be made only once.
Note that in Embodiments 1 to 4 which are described below, a transistor which is provided in at least a driver circuit portion of a display device which is one embodiment of the present invention will be described.
In this embodiment, a transistor that can be applied to a display device which is one embodiment of the present invention and a manufacturing method thereof will be described. In a display device which is one embodiment of the present invention, the transistor of this embodiment is provided in at least a driver circuit portion.
A transistor 471 is a bottom-gate transistor, and includes a first gate electrode layer 401, a gate insulating layer 402, an oxide semiconductor layer 403, and source and drain electrode layers 405 which are provided over a substrate 400. In addition, a first protective insulating layer 407 which is in contact with part of the oxide semiconductor layer 403 and covers the first gate electrode layer 401, the gate insulating layer 402, the oxide semiconductor layer 403, and the source and drain electrode layers 405 is included, and a second gate electrode layer 409 which is provided over the first protective insulating layer 407 and overlaps with the oxide semiconductor layer 403 is included. Note that the first protective insulating layer 407 can be referred to as a second gate insulating layer.
The oxide semiconductor layer 403 including a channel formation region may be formed using an oxide material having semiconductor characteristics. For example, an oxide semiconductor whose composition formula is represented by InMO3(ZnO)m (m>0) can be used, and particularly, an In—Ga—Zn—O-based oxide semiconductor is preferably used. Note that M represents one or more metal elements selected from Ga, Fe, Ni, Mn, or Co. As an example, M may be Ga or may include the above metal element in addition to Ga; for example, M may be Ga and Ni or Ga and Fe.
Note that in the above oxide semiconductor, a transition metal element such as Fe or Ni or an oxide of the transition metal may be contained in addition to a metal element contained as M.
In this specification, an oxide semiconductor including a material whose composition formula is represented by InMO3 (ZnO)m (m>0) where at least Ga is included as M is referred to as an In—Ga—Zn—O-based oxide semiconductor, and a thin film thereof is also referred to as an In—Ga—Zn—O-based non-single-crystal film.
As the oxide semiconductor applied to the oxide semiconductor layer 403, any of the following oxide semiconductors can be applied in addition to the above: an In—Sn—Zn—O-based oxide semiconductor; an In—Al—Zn—O-based oxide semiconductor; a Sn—Ga—Zn—O-based oxide semiconductor; an Al—Ga—Zn—O-based oxide semiconductor; a Sn—Al—Zn—O-based oxide semiconductor; an In—Zn—O-based oxide semiconductor; a Sn—Zn—O-based oxide semiconductor; an Al—Zn—O-based oxide semiconductor; an In—O-based oxide semiconductor; a Sn—O-based oxide semiconductor; and a Zn—O-based oxide semiconductor.
Further, silicon oxide may be included in the above oxide semiconductor.
The oxide semiconductor layer 403 can be formed in the following manner: at least after an oxide semiconductor film is formed, heat treatment (heat treatment for dehydration or dehydrogenation) through which impurities such as moisture (H2O) are reduced is performed to reduce the resistance of the oxide semiconductor film (the carrier concentration of the oxide semiconductor film is increased, preferably to 1×1018/cm3 or more); and the first protective insulating layer 407 is formed in contact with the oxide semiconductor film (or a processed oxide semiconductor layer) so that the resistance of the oxide semiconductor film is raised (the carrier concentration of the oxide semiconductor film is decreased, preferably to less than 1×1018/cm3, more preferably to 1×1014/cm3 or less). In such a manner, the oxide semiconductor layer 403 that can be used as the channel formation region can be formed.
Further, after the heat treatment for dehydration or dehydrogenation is performed so that impurities such as moisture are eliminated, the oxide semiconductor layer is preferably slowly cooled (gradually cooled) under an inert atmosphere. After the oxide semiconductor layer is subjected to heat treatment for dehydration or dehydrogenation and is slowly cooled, an insulating oxide film or the like is formed in contact with the oxide semiconductor layer; thus, the carrier concentration of the oxide semiconductor layer can be reduced. In such a manner, the reliability of the transistor 471 can be improved.
Further, impurities such as moisture which are present not only in the oxide semiconductor layer 403, but also in the gate insulating layer 402, at an interface between the oxide semiconductor layer 403 and a layer provided below and in contact with the oxide semiconductor layer 403 (i.e., an interface between the oxide semiconductor layer 403 and the gate insulating layer 402), and at an interface between the oxide semiconductor layer 403 and a layer provided over and in contact with the oxide semiconductor layer 403 (i.e., an interface between the oxide semiconductor layer 403 and the first protective insulating layer 407) are reduced.
The oxide semiconductor layer 403 includes a high-resistance oxide semiconductor region at least in a region which is in contact with an inorganic insulating film, and the high-resistance oxide semiconductor region can serve as a channel formation region.
Note that an In—Ga—Zn—O-based non-single-crystal film used for the oxide semiconductor layer 403 may be amorphous, microcrystalline, or polycrystalline. Although the “In—Ga—Zn—O-based non-single-crystal film” is given, the oxide semiconductor layer 403 may be an In—Ga—Zn—O-based single crystal film instead.
When the high-resistance oxide semiconductor region is used as a channel formation region, electric characteristics of the transistor can be stabilized and increase in off current or the like can be prevented.
The source and drain electrode layers 405 which are in contact with the oxide semiconductor layer 403 are preferably formed using a material including a metal with high oxygen affinity. It is preferable that the material including a metal with high oxygen affinity be one or more materials selected from titanium, aluminum, manganese, magnesium, zirconium, beryllium, or thorium.
When heat treatment is performed while the oxide semiconductor layer 403 and the metal layer with high oxygen affinity are in contact with each other, oxygen atoms move from the oxide semiconductor layer 403 to the metal layer, the carrier density in the vicinity of an interface is increased, and a low-resistance region is formed. The low-resistance region may be in a film shape having an interface.
Through the above steps, the transistor whose contact resistance is reduced and on current is increased can be manufactured.
First, the first gate electrode layer 401 is formed over the substrate 400 having an insulating surface. As the substrate 400 having an insulating surface, any glass substrate used in the electronics industry (also called an alkali-free glass substrate) such as an aluminosilicate glass substrate, an aluminoborosilicate glass substrate, or a barium borosilicate glass substrate, a plastic substrate with heat resistance which can withstand a process temperature in this manufacturing process, or the like can be used. When the substrate 400 having an insulating surface is a mother glass, any of the following sizes of the substrate can be used; the first generation (320 mm×400 mm), the second generation (400 mm×500 mm), the third generation (550 mm×650 mm), the fourth generation (680 mm×880 mm or 730 mm×920 mm), the fifth generation (1000 mm×1200 mm or 1100 mm×1250 mm), the sixth generation (1500 mm×1800 mm), the seventh generation (1900 mm×2200 mm), the eighth generation (2160 mm×2460 mm), the ninth generation (2400 mm×2800 mm or 2450 mm×3050 mm), the tenth generation (2950 mm×3400 mm), and the like.
Alternatively, as illustrated in
The first gate electrode layer 401 can be formed to have a single-layer structure or a stacked-layer structure using a metal material such as molybdenum, titanium, chromium, tantalum, tungsten, aluminum, copper, neodymium, or scandium or an alloy material containing any of these materials as its main component.
For example, as a two-layer structure of the first gate electrode layer 401, the following structures are preferable: a two-layer structure of an aluminum layer and a molybdenum layer stacked thereover, a two-layer structure of a copper layer and a molybdenum layer stacked thereover, a two-layer structure of a copper layer and a titanium nitride layer or a tantalum nitride layer stacked thereover, and a two-layer structure of a titanium nitride layer and a molybdenum layer. As a three-layer structure, a stack of a tungsten layer or a tungsten nitride layer, a layer of an alloy of aluminum and silicon or an alloy of aluminum and titanium, and a titanium nitride layer or a titanium layer is preferable.
After a conductive film is formed over the entire surface of the substrate 400, a photolithography step is performed. A resist mask is formed over the conductive film, and an unnecessary portion is removed by etching. In such a manner, the first gate electrode layer 401 is formed. The first gate electrode layer 401 serves as a wiring and an electrode (such as a gate wiring, a capacitor wiring, and a terminal electrode which include the first gate electrode layer 401).
Next, the gate insulating layer 402 is formed over the first gate electrode layer 401.
The gate insulating layer 402 can be formed to have a single-layer structure or a stacked-layer structure using a silicon oxide layer, a silicon nitride layer, a silicon oxynitride layer, or a silicon nitride oxide layer by a plasma CVD method, a sputtering method, or the like. For example, a silicon oxynitride layer may be formed using SiH4 and one or both of oxygen and nitrogen as a source gas by a plasma CVD method. Alternatively, dinitrogen monoxide may be used instead of oxygen and nitrogen.
Next, an oxide semiconductor film is formed over the gate insulating layer 402.
Note that before the oxide semiconductor film is formed by a sputtering method, dust or the like on a surface of the gate insulating layer 402 is preferably removed by reverse sputtering in which an argon gas is introduced and plasma is generated. The reverse sputtering refers to a method in which an RF power source is used for application of voltage to a substrate under an argon atmosphere and plasma is generated to expose an object to be processed (e.g., the substrate) to the plasma so that a surface of the object is modified. Note that nitrogen, helium, or the like may be used instead of an argon atmosphere. Alternatively, an argon atmosphere to which oxygen, dinitrogen monoxide, or the like is added may be used. Further alternatively, an argon atmosphere to which chlorine, methane tetrafluoride, or the like is added may be used.
The oxide semiconductor film is formed using an In—Ga—Zn—O-based metal oxide as a target by a sputtering method. The oxide semiconductor film can be formed by a sputtering method under a rare gas (e.g., argon) atmosphere, an oxygen atmosphere, or an atmosphere including a rare gas (e.g., argon) and oxygen.
Note that the gate insulating layer 402 and the oxide semiconductor film may be formed successively without exposure to air. By successive formation of the gate insulating layer 402 and the oxide semiconductor film without exposure to air, the interface between the gate insulating layer 402 and the oxide semiconductor film can be prevented from being contaminated by atmospheric components or impurities (such as moisture and hydrocarbon) floating in air, so that variation in characteristics of the transistors can be reduced.
Next, the oxide semiconductor film is processed into an island-shaped first oxide semiconductor layer 430 by a photolithography step (see
The first oxide semiconductor layer 430 is subjected to heat treatment under an inert gas (nitrogen or a rare gas such as helium, neon, or argon) atmosphere or reduced pressure, and is slowly cooled under an inert atmosphere, whereby a second oxide semiconductor layer 431 is formed (see
It is preferable that impurities such as moisture and hydrogen be not contained in nitrogen or a rare gas such as helium, neon, or argon in the heat treatment. Alternatively, the purity of nitrogen or a rare gas such as helium, neon, or argon introduced in a heat treatment apparatus is preferably 6 N (99.9999%) or higher, more preferably 7 N (99.99999%) or higher (that is, the concentration of the impurities is 1 ppm or lower, preferably 0.1 ppm or lower).
For the heat treatment, a method in which an electric furnace is used, a gas rapid thermal anneal (GRTA) method in which a heated gas is used, an instantaneous heating method such as a lamp rapid thermal anneal (LRTA) method in which lamp light is used, or the like can be used.
Here, the case where the first oxide semiconductor layer 430 is subjected to heat treatment in which an electric furnace is used will be described with reference to
The gas supply means 606 includes a gas supply source 611, a pressure adjusting valve 612, a mass flow controller 614, and a stop valve 615. In this embodiment, as illustrated in
In this embodiment, nitrogen or a rare gas is introduced into the chamber 602 from the gas supply source 611, so that the inside of the chamber 602 is in a nitrogen or a rare gas atmosphere. In the chamber 602 heated at greater than or equal to 200° C. and less than or equal to 600° C., preferably, greater than or equal to 400° C. and less than or equal to 600° C., the first oxide semiconductor layer 430 formed over the substrate 604 (the substrate 400 in
Alternatively, the chamber 602 in which the pressure is reduced by the evacuation means 607 is heated at greater than or equal to 200° ° C. and less than or equal to 600° C., preferably, greater than or equal to 400° C. and less than or equal to 600° C. In such a chamber 602, the first oxide semiconductor layer 430 formed over the substrate 604 (the substrate 400 in
Next, the heaters 603 are turned off, and the chamber 602 is slowly cooled (gradually cooled). By performance of heat treatment and slow cooling under an inert gas atmosphere or under reduced pressure, resistance of the first oxide semiconductor layer 430 is reduced (i.e., the carrier concentration is increased, preferably to 1×1018/cm3 or higher), so that a second oxide semiconductor layer 431 can be formed.
Through the heat treatment in the above-described manner, the reliability of the transistor formed later can be improved.
Note that in the case where heat treatment is performed under reduced pressure, an inert gas may be introduced into the chamber 602 after the heat treatment, so that the chamber 602 is to be under an atmospheric pressure, and then, cooling may be performed.
After the substrate 604 in the chamber 602 of the heating apparatus is cooled to about 300° C., the substrate 604 may be transferred into an atmosphere at room temperature. As a result, the cooling time of the substrate 604 can be shortened.
If the heating apparatus has a multi-chamber structure, heat treatment and cool treatment can be performed in chambers different from each other. For example, the first oxide semiconductor layer 430 over the substrate 604 (the substrate 400 in
The heat treatment of the first oxide semiconductor layer 430 under an inert gas atmosphere or reduced pressure may be performed on the oxide semiconductor film which has not yet been processed into the island-shaped first oxide semiconductor layer 430. In that case, after heat treatment of the oxide semiconductor film performed under an inert gas atmosphere or reduced pressure, slow cooling is performed to the temperature equal to or higher than room temperature and lower than 100° C. Then, the substrate 604 (the substrate 400 in
The first oxide semiconductor layer 430 which has been subjected to heat treatment under an inert gas atmosphere or reduced pressure is preferably in an amorphous state, but may be partly crystallized.
Next, a conductive film is formed over the gate insulating layer 402 and the second oxide semiconductor layer 431.
As a material for the conductive film, an element selected from aluminum, chromium, tantalum, titanium, molybdenum, or tungsten; an alloy containing any of the above metal elements as its main component; an alloy containing the above metal elements in combination; and the like can be given.
In the case where heat treatment is performed after formation of the conductive film, a conductive film having at least enough heat resistance to the heat treatment is used. For example, when the conductive film is formed using aluminum alone, there are disadvantages such as low resistance and a tendency to be corroded; therefore, the conductive film is formed using aluminum in combination with a conductive material having heat resistance. As the conductive material having heat resistance which is used in combination with aluminum, any of the following materials may be used: an element selected from titanium, tantalum, tungsten, molybdenum, chromium, neodymium, or scandium, an alloy containing any of the above metal elements as its main component, an alloy containing the above elements in combination, and a nitride containing any of the above elements as its main component.
The second oxide semiconductor layer 431 and the conductive film are etched, so that a third oxide semiconductor layer 432 and the source and drain electrode layers 405 (a source electrode 405a and a drain electrode 405b) are formed (see
Next, the first protective insulating layer 407 is formed in contact with the third oxide semiconductor layer 432. Moisture, hydrogen ions, OH−, and the like are reduced in the first protective insulating layer 407, (that is, moisture, hydrogen ions, OH−, and the like are not included in the first protective insulating layer 407, or almost none of them are included in the first protective insulating layer 407). The first protective insulating layer 407 can block entry of them from the outside. The first protective insulating layer 407 is formed using an insulating inorganic material containing oxygen, and specifically, silicon oxide, silicon oxynitride, or silicon nitride oxide is preferably used.
In this embodiment, as the first protective insulating layer 407, a 300-nm-thick silicon oxide film is formed by a sputtering method. The substrate temperature in formation of the silicon oxide film may be from room temperature to 300° C. or lower and in this embodiment, is 100° C. The formation of the silicon oxide film by a sputtering method can be performed under a rare gas (e.g., argon) atmosphere, an oxygen atmosphere, or an atmosphere of a mixed gas of a rare gas (e.g., argon) and oxygen. As a target, a silicon oxide target or a silicon target may be used. For example, with use of a silicon target, a silicon oxide film can be formed by a sputtering method under an atmosphere containing oxygen.
When the oxide semiconductor film is formed as the first protective insulating layer 407 by a sputtering method, a plasma CVD method, or the like to be in contact with the third oxide semiconductor layer 432, in the low-resistance third oxide semiconductor layer 432, at least a region in contact with the first protective insulating layer 407 has increased resistance ((i.e., the carrier concentration is reduced, preferably to lower than 1×1018/cm3). Thus, a high-resistance oxide semiconductor region can be formed.
During a manufacture process of the transistor, it is important to increase and decrease the carrier concentration in the third oxide semiconductor layer 432 through performance of heat treatment and slow cooling under an inert gas atmosphere (or reduced pressure), formation of an insulating oxide, and the like. The third oxide semiconductor layer 432 becomes the oxide semiconductor layer 403 having a high-resistance oxide semiconductor region (see
Next, after a conductive film is formed over the first protective insulating layer 407, a photolithography step is performed. A resist mask is formed over the conductive film, and an unnecessary portion is removed by etching, so that the second gate electrode layer 409 (including a wiring or the like which is formed using the same layer) is formed. When the second gate electrode layer 409 is selectively etched so as to have a top surface having a desired shape, the first protective insulating layer 407 can function as an etching stopper.
Note that in the case where the second gate electrode layer 409 is connected to the first gate electrode layer 401, an opening which exposes the first gate electrode layer 401 is formed in a predetermined portion of the first protective layer 407 before the conductive film which is to be the second gate electrode layer 409 is formed.
For the conductive film formed over the first protective insulating layer 407, a metal material (one or more of metal elements selected from aluminum, copper, titanium, tantalum, tungsten, molybdenum, chromium, neodymium, or scandium, or an alloy containing any of the elements as its main component) can be used. A film formed using any of them can have a light-blocking property when having a sufficient thickness. In such a manner, the oxide semiconductor layer 403 can be blocked from light.
In
Note that here, the transistor 471 may be subjected to heat treatment under a nitrogen atmosphere or an air atmosphere (in air). This heat treatment is preferably performed at a temperature of 300° C. or less, and the timing of the heat treatment is not particularly limited as long as it is performed after an insulating film which is to be the first protective insulating layer 407 is formed. For example, heat treatment is performed at 350° C. for one hour under a nitrogen atmosphere. If the heat treatment is performed, variation in electric characteristics of the transistor 471 can be reduced.
Through the above steps, the transistor 471 illustrated in
Note that the transistor used in this embodiment is not limited to the one of
In
The resin layer 408 covers the source and drain electrode layers 405 and the oxide semiconductor layer 403 having the thin region with the first protective insulating layer 407 provided therebetween. The resin layer 408 can be formed using, for example, a photosensitive or non-photosensitive organic material to have a thickness of 0.5 μm to 3 μm. As the photosensitive or non-photosensitive organic material used for the resin layer 408, polyimide, acrylic, polyamide, polyimideamide, resist, benzocyclobutene, or a stack of any of these materials is used. Here, a layer of photosensitive polyimide is formed by a coating method as the resin layer 408. After polyimide is applied to the entire surface, light exposure, development, and baking are performed, whereby the resin layer 408 of polyimide whose surface is plane and has a thickness of 1.5 μm is formed.
By provision of the resin layer 408, unevenness due to a structure of a transistor 471B can be reduced and the surface on which the second gate electrode layer 409 is formed can be planarized.
In
The base insulating layer 410 is formed using a silicon oxynitride layer, a silicon nitride oxide layer, a silicon nitride layer, or the like having a thickness of 50 nm to 200 nm. In the case where glass is used as the substrate 400, the base insulating layer 410 can prevent an impurity element (such as sodium) in a glass substrate from diffusing into a transistor 471C, in particular, can prevent such an impurity element from entering the oxide semiconductor layer 403. In addition, in the case where the base insulating layer 410 is provided, the substrate 400 can be prevented from being etched in the etching step for forming the first gate electrode layer 401C.
Note that in the transistor 471C, the relationship between the width of a first gate electrode layer 401C and that of a second gate electrode layer 409C are different from the relationship between the width of the first gate electrode layer and the second gate electrode layer of the transistor 471 or the transistor 471B. The length of the first gate electrode layer 401C in a channel length direction of the transistor 471C in
Note that in
Note that in
In
Note that in the above description, an example in which a two-tone photomask is used in a photolithography step is shown. When a resist mask including regions having different thicknesses (for example, two different thicknesses of a two-tone mask) is used, the number of resist masks can be reduced, so that the process can be simplified and cost can be reduced. Note that in this specification, a gray-tone photomask and a half-tone photomask are collectively referred to as a multi-tone mask, for convenience. Note that the multi-tone mask is not limited to a three-tone mask, and a four-tone mask or a mask having five or more tones may be used.
In the case of using a multi-tone mask, after the oxide semiconductor film and the conductive film are stacked, a resist mask including regions having different thicknesses is formed over the conductive film, and an oxide semiconductor layer having a thin region and source and drain electrode layers are formed with use of the resist mask. In this case, end portions of the source and drain electrode layers and end portions of the oxide semiconductor layer are generally aligned with each other, and side surfaces of the oxide semiconductor layer are exposed. Therefore, in the case where the first protective insulating layer 407 is formed, the side surfaces of the oxide semiconductor layer and the region (the thin region) of the oxide semiconductor layer which does not overlap with the source and drain electrode layers are in contact with the first protective insulating layer 407.
The channel formation region in the semiconductor layer included in the transistor of this embodiment is a high-resistance region; thus, electric characteristics of the transistor are stabilized and increase in off current can be prevented. Therefore, a display device including a transistor which has favorable electric characteristics and high reliability can be provided.
Note that this embodiment can be implemented in combination with any of other embodiments described in this specification as appropriate.
In this embodiment, a transistor that can be applied to a display device which is one embodiment of the present invention and that is different from the transistor of Embodiment 1 and a manufacturing method thereof will be described. In a display device which is one embodiment of the present invention, the transistor of this embodiment is provided in at least a driver circuit portion.
The n-type oxide semiconductor layers 404 having low resistance are provided between the oxide semiconductor layer 403 and the source and drain electrode layers 405, whereby the transistor 472 can operate more stably.
One example of a method for manufacturing the transistor 472 in
Note that steps in which the first gate electrode layer 401 is formed over the substrate 400 having an insulating surface, the gate insulating layer 402 covering the first gate electrode layer 401 is formed, and an oxide semiconductor film is formed are the same as those of Embodiment 1. Therefore, detailed description is omitted here and the same portions as those of
A first oxide semiconductor film 433 is formed over the gate insulating layer 402 as in Embodiment 1.
Next, a first n-type oxide semiconductor film 440 serving as source and drain regions is formed over the first oxide semiconductor film 433 (see
The first n-type oxide semiconductor film 440 may be formed using, for example, an oxynitride film containing indium, gallium, and zinc which is obtained by use of a metal oxide containing indium (In), gallium (Ga), and zinc (Zn) (In2O3:Ga2O3:ZnO=1:1:1) by a sputtering method under an atmosphere containing a nitrogen gas, an Al—Zn—O-based non-single-crystal film, or an Al—Zn—O-based non-single-crystal film containing nitrogen, i.e., an Al—Zn—O—N-based non-single-crystal film (also referred to as an AZON film).
Note that an In—Ga—Zn—O-based non-single-crystal film used in this embodiment may be amorphous, microcrystalline, or polycrystalline. Alternatively, it may be a single crystal. By change in the condition of film formation or composition ratio of a target in the above manner, crystalline states of the first oxide semiconductor film 433 and the first n-type oxide semiconductor film 440 can be changed.
Therefore, the crystalline states of the n-type oxide semiconductor layers which are to be source and drain regions and the oxide semiconductor layer 403 which forms a channel region may be different from each other depending on the condition of the formation of the oxide semiconductor film or the composition ratio of the target. For example, the n-type oxide semiconductor layers which are to be the source and drain regions may include micro crystals; the oxide semiconductor layer 403 may be amorphous; the n-type oxide semiconductor layers which are to be the source and drain regions may be amorphous; or the oxide semiconductor layer 403 may include micro crystals.
Note that the first oxide semiconductor film 433 and the first n-type oxide semiconductor film 440 may be formed successively without being exposed to air. Successive film formation without being exposed to air makes it possible to obtain each interface between stacked layers, which is not contaminated by atmospheric components or an impurity element floating in air, such as moisture, hydrocarbon, or the like. Therefore, variation in characteristics of the transistors can be reduced. Note that the gate insulating layer 402, the first oxide semiconductor film 433, and the first n-type oxide semiconductor film 440 may be formed successively.
Next, as in Embodiment 1, the first oxide semiconductor film 433 is subjected to heat treatment. By performance of heat treatment and slow cooling under an inert gas atmosphere or under reduced pressure, resistance of the first oxide semiconductor film 433 is reduced (i.e., the carrier concentration is increased, preferably to 1×1018/cm3 or higher), so that a low-resistance oxide semiconductor film (a second n-type oxide semiconductor film) can be formed.
The first oxide semiconductor film 433 is subjected to heat treatment under an inert gas (nitrogen or a rare gas such as helium, neon, or argon) atmosphere or reduced pressure. By the heat treatment under the above atmosphere on the first oxide semiconductor film 433, impurities such as hydrogen and moisture contained in the first oxide semiconductor film 433 can be removed.
It is preferable that impurities such as moisture and hydrogen be not contained in nitrogen or a rare gas such as helium, neon, or argon in the heat treatment. Alternatively, the purity of nitrogen or a rare gas such as helium, neon, or argon introduced in a heat treatment apparatus is preferably 6 N (99.9999%) or higher, more preferably 7 N (99.99999%) or higher (that is, the concentration of the impurities is 1 ppm or lower, preferably 0.1 ppm or lower).
In this embodiment, an electric furnace has a structure in which the temperature increases at greater than or equal to 0.1° C./min and less than or equal to 20° C./min, the atmosphere in the chamber is a nitrogen atmosphere or a rare gas atmosphere, and the temperature is set at greater than or equal to 200° ° C. and less than or equal to 600° C., preferably greater than or equal to 400° C. and less than or equal to 600° C. In such a manner, the first oxide semiconductor film 433 and the first n-type oxide semiconductor film 440 which are formed over the substrate are heated. Alternatively, the pressure is reduced by an evacuation means, and the temperature is set at greater than or equal to 200° C. and less than or equal to 600° C., preferably greater than or equal to 400° C. and less than or equal to 600° ° C. In such a manner, the first oxide semiconductor film 433 and the first n-type oxide semiconductor film 440 which are formed over the substrate are heated, so that a second oxide semiconductor film and a second n-type oxide semiconductor film are formed.
After the heat treatment, the heaters of the electric furnace are turned off, so that the chamber is slowly cooled (gradually cooled). Note that the electric furnace preferably has a structure in which the temperature decreases at greater than or equal to 0.1° C./min and less than or equal to 15° C./min.
Through the heat treatment in the above-described manner, the reliability of the transistor formed later can be improved.
Next, a resist mask (not shown) is formed over the second oxide semiconductor film and the second n-type oxide semiconductor film by a photolithography step, and the films are processed into an island-shaped second oxide semiconductor layer 431 and a second n-type oxide semiconductor layer 434 by an etching step (see
Note that here, the oxide semiconductor films are processed after the heat treatment; however, the heat treatment may be performed after the oxide semiconductor films are processed. Next, after the resist mask is removed, a conductive film is formed over the second n-type oxide semiconductor layer 434.
As a material for the conductive film, an element selected from aluminum, chromium, tantalum, titanium, molybdenum, or tungsten; an alloy containing any of the above metal elements as its component; an alloy containing the above metal elements in combination; and the like can be given.
If heat treatment is performed after formation of the conductive film, a conductive film having at least enough heat resistance to the heat treatment is used.
Next, a photolithography step is performed. A resist mask is formed over the conductive film, and the conductive film is etched, whereby the source and drain electrode layers 405 are formed. Note that the second n-type oxide semiconductor layer 434 in a region between source and drain electrodes which are formed by the source and drain electrode layers 405 (i.e., a back channel portion) is etched with use of the same resist mask, so that second n-type oxide semiconductor layers 437 which are to be source and drain regions are formed (see
Next, the first protective insulating layer 407 is formed using an inorganic insulating film containing oxygen, such as silicon oxide or silicon nitride oxide, in contact with the third oxide semiconductor layer 432. Here, as in Embodiment 1, a silicon oxide film having a thickness of 300 nm is formed by a sputtering method as the first protective insulating layer 407.
When the first protective insulating layer 407 is formed by a sputtering method, a plasma CVD method, or the like to be in contact with the low-resistance first oxide semiconductor layer 432 with use of silicon oxide, in the low-resistance third oxide semiconductor layer 432, at least a region in contact with the first protective insulating layer 407 has increased resistance (i.e., the carrier concentration is reduced, preferably to lower than 1×1018/cm3). Thus, a high-resistance oxide semiconductor region can be formed.
During a manufacture process of the transistor, it is important to increase and decrease the carrier concentration in the third oxide semiconductor layer 432 through performance of heat treatment and slow cooling under an inert gas atmosphere (or reduced pressure), formation of an insulating oxide, and the like. The third oxide semiconductor layer 432 becomes the oxide semiconductor layer 403 having a high-resistance oxide semiconductor region (see
Note that steps after formation of the first protective insulating layer 407 are the same as those of Embodiment 1. That is, the second gate electrode layer 409 is formed over the first protective insulating layer 407.
Note that a resin layer may be provided over the second gate electrode layer 409. By provision of the resin layer over the second gate electrode layer 409, unevenness due to a structure of the transistor 472 can be reduced and the element can be planarized.
Note that the transistor 472 may be subjected to heat treatment under a nitrogen atmosphere or an air atmosphere (in air). This heat treatment is preferably performed at a temperature of 300° C. or less, and the timing of the heat treatment is not particularly limited as long as it is performed after an insulating film which is to be the first protective insulating layer 407 is formed. For example, heat treatment is performed at 350° C. for one hour under a nitrogen atmosphere. If the heat treatment is performed, variation in electric characteristics of the transistor 472 can be reduced.
Through the above steps, the transistor 472 illustrated in
A transistor 472B in
The resin layer 408 covers the source and drain electrode layers 405 and the oxide semiconductor layer 403 having the thin region with the first protective insulating layer 407 provided therebetween. The resin layer 408 can be formed using a photosensitive or non-photosensitive organic material to have a thickness of 0.5 μm to 3 μm. As the photosensitive or non-photosensitive organic material used for the resin layer 408, polyimide, acrylic, polyamide, polyimideamide, resist, benzocyclobutene, or a stack of any of these materials is used. Here, a layer of photosensitive polyimide is formed by a coating method as the resin layer 408. After polyimide is applied to the entire surface, light exposure, development, and baking are performed, whereby the resin layer 408 of polyimide whose surface is plane and has a thickness of 1.5 μm is formed.
By provision of the resin layer 408, unevenness due to a structure of the transistor 472B can be reduced and the surface on which the second gate electrode layer 409 is formed can be planarized.
Note that as illustrated in
Note that even if the structure of
Note that in the case where parasitic capacitance does not become a problem because the portion in which the resin layer 408 and the first protective insulating layer 407 are stacked is sufficiently thick, the second gate electrode may be used as a common gate electrode which covers a plurality of transistors in the driver circuit and may have an area substantially the same or larger than the area of the driver circuit.
Note that in the above description, an example in which a two-tone photomask is used in a photolithography step is shown. When a resist mask including regions having different thicknesses (for example, two different thicknesses of a two-tone mask) is used, the number of resist masks can be reduced, so that the process can be simplified and cost can be reduced.
In the case of using a multi-tone mask, after the oxide semiconductor film of two stacked layers and the conductive film are stacked, a resist mask including regions having different thicknesses is formed over the conductive film, and an oxide semiconductor layer having a thin region and source and drain electrode layers are formed with use of the resist mask. In this case, end portions of the source and drain electrode layers and end portions of the oxide semiconductor layer are generally aligned with each other, and side surfaces of the oxide semiconductor layer are exposed. Therefore, in the case where the first protective insulating layer 407 is formed, the side surfaces and the region (the thin region) which does not overlap with the source and drain electrode layers of the oxide semiconductor layer are in contact with the first protective insulating layer 407.
The channel formation region in the semiconductor layer included in the transistor of this embodiment is a high-resistance region; thus, electric characteristics of the transistor are stabilized and increase in off current can be prevented. Therefore, a semiconductor device (a display device) including a transistor which has favorable electric characteristics and high reliability can be provided.
Note that this embodiment can be implemented in combination with any of other embodiments described in this specification as appropriate.
In this embodiment, a transistor that can be applied to a display device which is one embodiment of the present invention and that is different from the transistors of Embodiments 1 and 2 and a manufacturing method thereof will be described. In a display device which is one embodiment of the present invention, the transistor of this embodiment is provided in at least a driver circuit portion.
One example of a method for manufacturing the transistor 473 in
Note that steps in which the first gate electrode layer 401 is formed over the substrate 400 having an insulating surface, the gate insulating layer 402 covering the first gate electrode layer 401 is formed, and an oxide semiconductor film is formed are the same as those of Embodiment 1. Therefore, detailed description is omitted here and the same portions as those of
A first oxide semiconductor film is formed over the gate insulating layer 402 as in Embodiment 1.
Next, a photolithography step is performed. A resist mask is formed over the first oxide semiconductor film, and the first oxide semiconductor film is etched, so that an island-shaped oxide semiconductor layer 430 is formed. Note that etching here is not limited to wet etching and may be dry etching (see
Next, as in Embodiment 1, the first oxide semiconductor layer 430 is subjected to heat treatment. By performance of heat treatment and slow cooling under an inert gas atmosphere or under reduced pressure, resistance of the first oxide semiconductor layer 430 is reduced (i.e., the carrier concentration is increased, preferably to 1×1018/cm3 or higher), so that a low-resistance second oxide semiconductor layer 431 can be formed.
The first oxide semiconductor layer 430 is subjected to heat treatment under an inert gas (nitrogen or a rare gas such as helium, neon, or argon) atmosphere or reduced pressure. By the heat treatment under the above atmosphere on the first oxide semiconductor layer 430, impurities such as hydrogen and moisture contained in the first oxide semiconductor layer 430 can be removed.
It is preferable that impurities such as moisture and hydrogen be not contained in nitrogen or a rare gas such as helium, neon, or argon in the heat treatment. Alternatively, the purity of nitrogen or a rare gas such as helium, neon, or argon introduced in a heat treatment apparatus is preferably 6 N (99.9999%) or higher, more preferably 7 N (99.99999%) or higher (that is, the concentration of the impurities is 1 ppm or lower, preferably 0.1 ppm or lower).
In this embodiment, an electric furnace has a structure in which the temperature increases at greater than or equal to 0.1° C./min and less than or equal to 20° C./min, the atmosphere in the chamber is a nitrogen atmosphere or a rare gas atmosphere, and the temperature is set at greater than or equal to 200° C. and less than or equal to 600° C., preferably greater than or equal to 400° C. and less than or equal to 600° C. In such a manner, the first oxide semiconductor layer 430 which is formed over the substrate is heated in the heated chamber. Alternatively, the pressure is reduced by an evacuation means, and the temperature is set at greater than or equal to 200° C. and less than or equal to 600° C., preferably greater than or equal to 400° C. and less than or equal to 600° C. In such a manner, the first oxide semiconductor layer 430 which is formed over the substrate is heated, so that the second oxide semiconductor layer 431 is formed.
After the heat treatment, the heaters of the electric furnace are turned off, so that the chamber is slowly cooled (gradually cooled). Note that the electric furnace preferably has a structure in which the temperature decreases at greater than or equal to 0.1° C./min and less than or equal to 15° C./min.
Through the heat treatment in the above-described manner, the reliability of the transistor formed later can be improved.
Next, an insulating film which is to be a channel protective layer is formed in contact with the second oxide semiconductor layer 431. Moisture, hydrogen ions, OH−, and the like are reduced in the insulating film which is to be the channel protective layer and is formed in contact with the second oxide semiconductor layer, and are prevented from entering the insulating film from the outside. The insulating film is formed using an insulating inorganic material containing oxygen. Specifically, silicon oxide, silicon oxynitride, or silicon nitride oxide is used. That is, the insulating film which is to be the channel protective layer may be formed in a manner similar to formation of the first protective insulating layer 407 described in Embodiment 1.
In this embodiment, as the insulating film which is to be the channel protective layer, a 300-nm-thick silicon oxide film is formed by a sputtering method. The substrate temperature in film formation may be from room temperature to 300° C. or lower and in this embodiment, is 100° C. The formation of the silicon oxide film by a sputtering method can be performed under a rare gas (e.g., argon) atmosphere, an oxygen atmosphere, or an atmosphere of a mixed gas of a rare gas (e.g., argon) and oxygen. As a target, a silicon oxide target or a silicon target may be used. For example, with use of a silicon target, a silicon oxide film can be formed by a sputtering method under an atmosphere containing oxygen.
When the insulating film which is to be the channel protective layer is formed by a sputtering method, a plasma CVD method, or the like to be in contact with the second oxide semiconductor layer 431, in the low-resistance second oxide semiconductor layer 431, at least a region in contact with the insulating film which is to be the channel protective layer has increased resistance ((i.e., the carrier concentration is reduced, preferably to lower than 1×1018/cm3). Thus, a high-resistance oxide semiconductor region can be formed.
During a manufacture process of the transistor, it is important to increase and decrease the carrier concentration in the third oxide semiconductor layer through performance of heat treatment and slow cooling under an inert gas atmosphere (or reduced pressure), formation of an insulating oxide, and the like. The second oxide semiconductor layer 431 becomes the oxide semiconductor layer 403 having a high-resistance oxide semiconductor region.
Next, a photolithography step is performed. A resist mask is formed over the insulating film that is to be the channel protective layer, and an unnecessary portion is removed by etching, so that the channel protective layer 406 is formed. Note that the width of the first gate electrode layer 401 is preferably larger than that of the channel protective layer 406 (i.e., the length of the channel protective layer 406 in the channel length direction) (see
Next, after the resist mask is removed, a conductive film is formed over the second oxide semiconductor layer 431 and the channel protective layer 406.
As a material for the conductive film, an element selected from aluminum, chromium, tantalum, titanium, molybdenum, or tungsten; an alloy containing any of the above metal elements as its component; an alloy containing the above metal elements in combination; and the like can be given.
If heat treatment is performed after formation of the conductive film, a conductive film having at least enough heat resistance to the heat treatment is used.
Next, a photolithography step is performed. A resist mask is formed over the conductive film, and the conductive film is etched, whereby the source and drain electrode layers 405 (the source electrode 405a and a drain electrode 405b) are formed. In this etching, the channel protective layer 406 functions as an etching stopper of the oxide semiconductor layer 403. Therefore, the oxide semiconductor layer 403 is not etched.
Because of the structure in which the channel protective layer 406 is provided on and in contact with a channel formation region of the oxide semiconductor layer 403, damage to the channel formation region of the oxide semiconductor layer 403 (for example, reduction in film thickness due to plasma or an etchant in etching, or oxidation) in the manufacturing process can be prevented. Therefore, the reliability of the transistor 473 can be improved.
Next, the first protective insulating layer 407 is formed over the source and drain electrode layers 405 and the channel protective layer 406. Moisture, hydrogen ions, OH−, and the like are reduced in the first protective insulating layer 407, and are prevented from entering the first protective insulating layer 407 from the outside. The first protective insulating layer 407 is formed using an insulating inorganic material containing oxygen. Specifically, silicon oxide, silicon nitride, silicon oxynitride, silicon nitride oxide, aluminum oxide, aluminum nitride, magnesium oxide, yttrium oxide, hafnium oxide, or tantalum oxide can be given (see
Note that steps after formation of the first protective insulating layer 407 are the same as those of Embodiment 1. That is, the second gate electrode layer 409 is formed over the first protective insulating layer 407.
Note that a resin layer may be provided over the second gate electrode layer 409. By provision of the resin layer over the second gate electrode layer 409, unevenness due to a structure of the transistor 473 can be reduced and the element can be planarized.
Note that the transistor 473 may be subjected to heat treatment under a nitrogen atmosphere or an air atmosphere (in air). This heat treatment is performed at a temperature of 300° C. or less, and the timing of the heat treatment is not particularly limited as long as it is performed after the channel protective layer 406 is formed. For example, heat treatment is performed at 350° C. for one hour under a nitrogen atmosphere. If the heat treatment is performed, variation in electric characteristics of the transistor 473 can be reduced.
Through the above steps, the transistor 473 illustrated in
A transistor 473B in
The resin layer 408 covers the source and drain electrode layers 405 and the channel protective layer 406 with the first protective insulating layer 407 provided therebetween. The resin layer 408 can be formed using a photosensitive or non-photosensitive organic material to have a thickness of 0.5 μm to 3 μm. As the photosensitive or non-photosensitive organic material used for the resin layer 408, polyimide, acrylic, polyamide, polyimideamide, resist, benzocyclobutene, or a stack of any of these materials is used. Here, a layer of photosensitive polyimide is formed by a coating method as the resin layer 408. After polyimide is applied to the entire surface, light exposure, development, and baking are performed, whereby the resin layer 408 of polyimide whose surface is plane and has a thickness of 1.5 μm can be formed. By provision of the resin layer 408, unevenness due to a structure of the transistor 473B can be reduced and the surface on which the second gate electrode layer 409 is formed can be planarized.
Note that as illustrated in
Note that even if the structure of
Note that in the case where parasitic capacitance does not become a problem because the portion in which the resin layer 408 and the first protective insulating layer 407 are stacked is sufficiently thick, the second gate electrode may be used as a common gate electrode which covers a plurality of transistors in the driver circuit and may have an area substantially the same or larger than the area of the driver circuit.
The channel formation region in the semiconductor layer included in the transistor of this embodiment is a high-resistance region; thus, electric characteristics of the transistor are stabilized and increase in off current can be prevented. Therefore, a semiconductor device (a display device) including a transistor which has favorable electric characteristics and high reliability can be provided.
Note that this embodiment can be implemented in combination with any of other embodiments described in this specification as appropriate.
In this embodiment, a transistor that can be applied to a display device which is one embodiment of the present invention and that is different from the transistors of Embodiments 1 to 3 and a manufacturing method thereof will be described. In a display device which is one embodiment of the present invention, the transistor of this embodiment is provided in at least a driver circuit portion.
One example of a method for manufacturing the transistor 474 in
Note that steps in which the first gate electrode layer 401 is formed over the substrate 400 having an insulating surface, the gate insulating layer 402 covering the first gate electrode layer 401 is formed, and an oxide semiconductor film is formed are the same as those of Embodiment 3. Therefore, detailed description is omitted here and the same portions as those of
A first oxide semiconductor film 433 is formed over the gate insulating layer 402 as in Embodiment 1.
Next, as in Embodiment 1, the first oxide semiconductor film 433 is subjected to heat treatment. By performance of heat treatment and slow cooling under an inert gas atmosphere or under reduced pressure, resistance of the first oxide semiconductor film 433 is reduced (i.e., the carrier concentration is increased, preferably to 1×1018/cm3 or higher), so that a low-resistance second oxide semiconductor film can be formed.
The first oxide semiconductor film 433 is subjected to heat treatment under an inert gas (nitrogen or a rare gas such as helium, neon, or argon) atmosphere or reduced pressure. By the heat treatment under the above atmosphere on the first oxide semiconductor film 433, impurities such as hydrogen and moisture contained in the first oxide semiconductor film 433 can be removed.
It is preferable that impurities such as moisture and hydrogen be not contained in nitrogen or a rare gas such as helium, neon, or argon in the heat treatment. Alternatively, the purity of nitrogen or a rare gas such as helium, neon, or argon introduced in a heat treatment apparatus is preferably 6 N (99.9999%) or higher, more preferably 7 N (99.99999%) or higher (that is, the concentration of the impurities is 1 ppm or lower, preferably 0.1 ppm or lower).
In this embodiment, an electric furnace has a structure in which the temperature increases at greater than or equal to 0.1° C./min and less than or equal to 20° C./min, the atmosphere in the chamber is a nitrogen atmosphere or a rare gas atmosphere, and the temperature is set at greater than or equal to 200° C. and less than or equal to 600° C., preferably greater than or equal to 400° C. and less than or equal to 600° C. In such a manner, the first oxide semiconductor film 433 which is formed over the substrate is heated in the heated chamber.
After the heat treatment, the heaters of the electric furnace are turned off, so that the chamber is slowly cooled (gradually cooled). Note that the electric furnace preferably has a structure in which the temperature decreases at greater than or equal to 0.1° C./min and less than or equal to 15° C./min.
Through the heat treatment in the above-described manner, the reliability of the transistor formed later can be improved.
Next, an insulating film which is to be a channel protective layer is formed in contact with the second oxide semiconductor film. Moisture, hydrogen ions, OH−, and the like are reduced in the insulating film which is to be the channel protective layer and is formed in contact with the second oxide semiconductor film, and are prevented from entering the insulating film from the outside. The insulating film is formed using an insulating inorganic material containing oxygen. Specifically, a silicon oxide film or a silicon nitride oxide film is used.
In this embodiment, as the insulating film which is to be the channel protective layer, a 300-nm-thick silicon oxide film is formed by a sputtering method. The substrate temperature in film formation may be from room temperature to 300° C. or lower and in this embodiment, is 100° C. The formation of the silicon oxide film by a sputtering method can be performed under a rare gas (e.g., argon) atmosphere, an oxygen atmosphere, or an atmosphere of a mixed gas of a rare gas (e.g., argon) and oxygen. As a target, a silicon oxide target or a silicon target may be used. For example, with use of a silicon target, a silicon oxide film can be formed by a sputtering method under an atmosphere containing oxygen.
When the insulating film which is to be the channel protective layer is formed by a sputtering method, a plasma CVD method, or the like to be in contact with the second oxide semiconductor film, in the low-resistance second oxide semiconductor film, at least a region in contact with the insulating film which is to be the channel protective layer has increased resistance ((i.e., the carrier concentration is reduced, preferably to lower than 1×1018/cm3). Thus, a high-resistance oxide semiconductor region can be formed.
During a manufacture process of the transistor, it is important to increase and decrease the carrier concentration in the oxide semiconductor layer through performance of heat treatment and slow cooling under an inert gas atmosphere (or reduced pressure), formation of an insulating oxide, and the like. The second oxide semiconductor film becomes the third oxide semiconductor film having a high-resistance oxide semiconductor region.
Next, a photolithography step is performed. A resist mask is formed over the insulating film that is to be the channel protective layer, and an unnecessary portion is removed by etching, so that the channel protective layer 406 is formed. Note that the width of the first gate electrode layer 401 is preferably larger than that of the channel protective layer 406 (i.e., the length of the channel protective layer 406 in the channel length direction).
Next, an n-type oxide semiconductor film serving as source and drain regions is formed over the third oxide semiconductor film and the channel protective layer 406. The n-type oxide semiconductor film is formed using an oxide semiconductor film having lower resistance than the third oxide semiconductor film.
The n-type oxide semiconductor film may be formed using, for example, an oxynitride film containing indium, gallium, and zinc which is obtained by use of a metal oxide containing indium (In), gallium (Ga), and zinc (Zn) (In2O3:Ga2O3:ZnO=1:1:1) by a sputtering method under an atmosphere containing a nitrogen gas, an Al—Zn—O-based non-single-crystal film, or an Al—Zn—O-based non-single-crystal film containing nitrogen, i.e., an Al—Zn—O—N-based non-single-crystal film (also referred to as an AZON film).
Note that an In—Ga—Zn—O-based non-single-crystal film used in this embodiment may be amorphous, microcrystalline, or polycrystalline. Alternatively, the crystalline state is not limited thereto, and it may be a single crystal. By change in the condition of film formation or composition ratio of a target in the above manner, crystalline states of the third oxide semiconductor film and the n-type oxide semiconductor film can be changed.
Therefore, the crystalline states of the n-type oxide semiconductor film which is to be the source and drain regions and the third oxide semiconductor film which forms a channel region may be different from each other depending on the condition of the formation of the oxide semiconductor film or the composition ratio of the target. For example, the n-type oxide semiconductor film which is to be the source and drain regions may include micro crystals; the third oxide semiconductor film may be amorphous; the n-type oxide semiconductor film which is to be the source and drain regions may be amorphous; or the third oxide semiconductor film may include micro crystals.
Next, a photolithography step is performed. A resist mask is formed over the n-type oxide semiconductor film, and an unnecessary portion of the n-type oxide semiconductor film and the third oxide semiconductor film is removed by etching. In such a manner, the oxide semiconductor layer 403 is formed (see
Note that the photolithography step is not particularly limited to the above description, and the following manner may be alternatively employed: a resist mask is formed over the insulating film that is to be a channel protective layer; an unnecessary portion of the insulating film that is to be the channel protective layer and the third oxide semiconductor film is removed by etching; the resist mask is reduced; and an unnecessary portion of the insulating film that is to be the channel protective layer is further removed by etching. In such a manner, the channel protective layer 406 may be formed. In this case, the resist mask which is formed first over the insulating film that is to be the channel protective layer is preferably a resist mask which is formed using a multi-tone mask and is provided with regions having different thicknesses.
Next, after the resist mask is removed, a conductive film is formed over the n-type oxide semiconductor film.
As a material for the conductive film, an element selected from aluminum, chromium, tantalum, titanium, molybdenum, or tungsten; an alloy containing any of the above metal elements as its main component; an alloy containing the above metal elements in combination; and the like can be given.
If heat treatment is performed after formation of the conductive film, a conductive film having at least enough heat resistance to the heat treatment is used.
Next, a photolithography step is performed. A resist mask is formed over the conductive film, and the conductive film is etched, whereby the source and drain electrode layers 405 are formed.
Then, a region of the n-type oxide semiconductor film, which is between the source electrode and the drain electrode formed from the source and drain electrode layers 405, is removed by etching with use of the same resist mask, whereby the n-type oxide semiconductor layers 404 which are to be the source and drain regions are formed.
The n-type oxide semiconductor layers 404 having low resistance are provided between the oxide semiconductor layer 403 and the source and drain electrode layers 405, whereby the transistor 474 can operate more stably as compared with the case of using only metal wirings.
In this etching, the channel protective layer 406 functions as an etching stopper of the oxide semiconductor layer 403. Therefore, the oxide semiconductor layer 403 is not etched. The channel protective layer 406 is provided, so that damage to the channel formation region of the oxide semiconductor layer 403 (for example, reduction in film thickness due to plasma or an etchant in etching, or oxidation) in the manufacturing process can be prevented. Therefore, the reliability of the transistor 474 can be improved (see
Next, the first protective insulating layer 407 is formed over the source and drain electrode layers 405 and the channel protective layer 406 (see
Note that steps after formation of the first protective insulating layer 407 are the same as those of Embodiment 1. That is, the second gate electrode layer 409 is formed over the first protective insulating layer 407.
Note that a resin layer may be provided over the second gate electrode layer 409. By provision of the resin layer over the second gate electrode layer 409, unevenness due to a structure of the transistor 474 can be reduced and the element can be planarized.
Note that the transistor 474 may be subjected to heat treatment under a nitrogen atmosphere or an air atmosphere (in air). This heat treatment is performed at a temperature of 300° C. or less, and the timing of the heat treatment is not particularly limited as long as it is performed after the channel protective layer 406 is formed. For example, heat treatment is performed at 350° C. for one hour under a nitrogen atmosphere. If the heat treatment is performed, variation in electric characteristics of the transistor 474 can be reduced.
Through the above steps, the transistor 474 illustrated in
A transistor 474B in
The resin layer 408 covers the source and drain electrode layers 405 and the channel protective layer 406 with the first protective insulating layer 407 provided therebetween. The resin layer 408 can be formed using a photosensitive or non-photosensitive organic material to have a thickness of 0.5 μm to 3 μm. As the photosensitive or non-photosensitive organic material used for the resin layer 408, polyimide, acrylic, polyamide, polyimideamide, resist, benzocyclobutene, or a stack of any of these materials is used. Here, a layer of photosensitive polyimide is formed by a coating method as the resin layer 408. After polyimide is applied to the entire surface, light exposure, development, and baking are performed, whereby the resin layer 408 of polyimide whose surface is plane and has a thickness of 1.5 μm can be formed.
By provision of the resin layer 408, unevenness due to a structure of a transistor 474B can be reduced and the surface on which the second gate electrode layer 409 is formed can be planarized.
Note that as illustrated in
Note that even if the structure of
Note that in the case where parasitic capacitance does not become a problem because the portion in which the resin layer 408 and the first protective insulating layer 407 are stacked is sufficiently thick, the second gate electrode may be used as a common gate electrode which covers a plurality of transistors in the driver circuit and may have an area substantially the same or larger than the area of the driver circuit.
The channel formation region in the semiconductor layer included in the transistor of this embodiment is a high-resistance region; thus, electric characteristics of the transistor are stabilized and increase in off current can be prevented. Therefore, a semiconductor device (a display device) including a transistor which has favorable electric characteristics and high reliability can be provided.
Note that this embodiment can be implemented in combination with any of other embodiments described in this specification as appropriate.
In this embodiment, an example in which an inverter circuit in a driver circuit is formed using two n-channel transistors will be described. Transistors in
The driver circuit for driving a pixel portion is formed using an inverter circuit, a capacitor, a resistor, and the like. When two n-channel transistors are combined to form an inverter circuit, there are the following combinations: a combination of an enhancement type transistor and a depletion type transistor (hereinafter, a circuit formed by such a combination is referred to as an EDMOS circuit) and a combination of enhancement type transistors (hereinafter, a circuit formed by such a combination is referred to as an EEMOS circuit).
In
Further, over a first gate insulating layer 13 covering the first gate electrode 11 and the third gate electrode 42, an oxide semiconductor layer 16 and a second oxide semiconductor layer 47 are provided.
An electrode layer serving as a first terminal (a source electrode layer 15a) and an electrode layer serving as a second terminal (a drain electrode layer 15b) are provided over the oxide semiconductor layer 16. The electrode layer serving as the second terminal is directly connected to the third gate electrode 42 through a contact hole 44 formed in the first gate insulating layer 13. In addition, an electrode layer serving as a third terminal 411 is provided over the second oxide semiconductor layer 47.
The transistor 20 includes the first gate electrode 11, the first gate insulating layer 13 covering the first gate electrode 11, and the oxide semiconductor layer 16 overlapping with the first gate electrode 11 with the first gate insulating layer 13 between the first gate electrode 11 and the oxide semiconductor layer 16. The electrode layer serving as the first terminal (the source electrode layer 15a) is a power supply line to which negative voltage VDL is applied (a negative power supply line). This power supply line may be a power supply line with a ground potential (a ground potential power supply line). Note that in the inverter circuit, the electrode layer serving as the first terminal is the drain electrode layer and the electrode layer serving as the second terminal is the source electrode layer in some cases, depending on a potential of a wiring connected to the electrode layer serving as the second terminal (the drain electrode layer 15b).
The second transistor 43 includes the third gate electrode 42 and the second oxide semiconductor layer 47 overlapping with the third gate electrode 42 with the first gate insulating layer 13 between the third gate electrode 42 and the second oxide semiconductor layer 47. The third terminal 411 is a power supply line to which positive voltage VDH is applied (a positive power supply line). Note that in the inverter circuit, the electrode layer serving as the second terminal is the source electrode layer and the electrode layer serving as the third terminal 411 is the drain electrode layer in some cases, depending on a potential of a wiring connected to the electrode layer serving as the second terminal (the drain electrode layer 15b).
Here, a buffer layer 408a (also referred to as a source region or a drain region) is provided between the second oxide semiconductor layer 47 and the drain electrode layer 15b. A buffer layer 408b (also referred to as a drain region or a source region) is provided between the second oxide semiconductor layer 47 and the third terminal 411.
In this embodiment, in order that the transistor 20 can serve as an n-channel enhancement type transistor, a second gate insulating layer is provided over the oxide semiconductor layer 16 and a second gate electrode 19 is provided over the second gate insulating layer so that the threshold voltage of the transistor 20 is controlled by voltage applied to the second gate electrode 19.
Note that the example in which the electrode layer serving as the second terminal (the drain electrode layer 15b) is directly connected to the third gate electrode 42 through the contact hole 44 formed in the first gate insulating layer 13 is illustrated in
This embodiment can be implemented in combination with any of Embodiments 1 to 4 as appropriate.
In this embodiment, a display device which is one embodiment of the present invention will be described with reference to a block diagram, a circuit diagram, a waveform diagram showing potential changes of signals, a top view (a layout diagram), and the like.
An example of a block diagram of an active matrix liquid crystal display device is illustrated in
Note that although a mode in which the scan line driver circuit 802 and the signal line driver circuit 803 are formed over the substrate 800 is described here, part of the scan line driver circuit 802 may be mounted over an IC formed over another substrate. Further, part of the signal line driver circuit 803 may be mounted over an IC formed over another substrate. Still further, a plurality of scan line driver circuits 802 may be provided over the substrate 800.
The pixel portion 827 includes a plurality of pixels 828 arranged in a matrix. The pixel 828 includes a pixel transistor 829 connected to the scan line 823A, the control line 823B, and the signal line 824, a storage capacitor 830, and a pixel electrode 831.
The pixel structure here illustrates a case where one electrode of the storage capacitor 830 is connected to the pixel transistor 829 and the other electrode of the storage capacitor 830 is connected to a capacitor line 832. The pixel electrode 831 serves as one of electrodes which drive a display element (such as a liquid crystal element, a light-emitting element, or a contrast medium (electronic ink)). The other electrode (also referred to as a counter electrode) of the display element is connected to a common terminal 833. From the common terminal, a common potential is applied to the counter electrode of the display element.
The protective circuit 835 is provided between a wiring extended from the pixel portion 827 and the signal line input terminal 822. The protective circuit 835 is also provided between the scan line driver circuit 802 and the pixel portion 827. In this embodiment, the protective circuit 835 including a plurality of protective circuits is provided so that the pixel transistors 829 and the like are not broken when surge voltage due to static electricity or the like is applied to the scan line 823A, the control line 823B, the signal line 824, or the capacitor line 832. Accordingly, the protective circuits 835 are formed so that charge can be released into a common wiring when surge voltage is applied.
In this embodiment, an example in which one protective circuit is provided for each wiring in the vicinity of the signal line input terminals 822 is shown. However, the position of the protective circuits 835 and the number of protective circuits provided in the protective circuit 835 are not limited to the example.
The use of the transistor described in any of Embodiments 1 to 4 as the pixel transistor 829 allows the threshold voltage of the pixel transistor 829 to be controlled and/or on current of the transistor to be increased.
In
As shown in
Note that the waveform diagrams in
Note that, in the layout diagram of
In
By driving the pixel transistor 829 in a manner in which the waveform G1 and the waveform G2 are in the same potential as shown in
Note that the waveform diagram in
Note that, in the layout diagram of
As described above, by use of the transistor having the structure described in any one of Embodiments 1 to 4, the threshold voltage can be controlled to a favorable value while effects described in the above embodiments can be obtained.
Note that in this embodiment, what is illustrated in the drawing can be freely combined with or replaced with what is described in another embodiment as appropriate.
In this embodiment, a light-emitting display device to which the transistor including an oxide semiconductor layer described in any one of Embodiments 1 to 4 is applied will be described. Note that as an example of a display element included in the light-emitting display device of this embodiment, a light-emitting element utilizing electroluminescence is described. Light-emitting elements utilizing electroluminescence are classified according to whether a light emitting material is an organic compound or an inorganic compound. The former is referred to as an organic EL element and the latter is referred to as an inorganic EL element.
In an organic EL element, by application of voltage to a light-emitting element, electrons and holes are separately injected from a pair of electrodes into a layer containing a light-emitting organic compound, and current flows. The carriers (electrons and holes) are recombined, and thus, the light-emitting organic compound is excited. The light-emitting organic compound returns to a ground state from the excited state, thereby emitting light. Owing to such a mechanism, this light-emitting element is referred to as a current-excitation light-emitting element.
The inorganic EL elements are classified according to their element structures into a dispersion-type inorganic EL element and a thin-film inorganic EL element. A dispersion-type inorganic EL element has a light-emitting layer where particles of a light-emitting material are dispersed in a binder, and its light emission mechanism is donor-acceptor recombination type light emission that utilizes a donor level and an acceptor level. A thin-film inorganic EL element has a structure where a light-emitting layer is sandwiched between dielectric layers, which are further sandwiched between electrodes, and its light emission mechanism is localized type light emission that utilizes inner-shell electron transition of metal ions.
Note that description is made in this embodiment using an organic EL element as a light-emitting element.
A structure and an operation of the pixel in the light-emitting display device are described. In this example, one pixel includes two n-channel transistors each of which includes an oxide semiconductor layer (for example, an In—Ga—Zn—O-based non-single-crystal film) as a channel formation region.
A pixel 6400 includes a switching transistor 6401 (a first transistor), a driver transistor 6402 (a second transistor), a capacitor 6403, and a light-emitting element 6404. The switching transistor 6401 has a first gate electrode connected to a scan line 6406A, a second gate electrode connected to a control line 6406B, a first electrode (one of a source electrode and a drain electrode) connected to a signal line 6405, and a second electrode (the other of the source electrode and the drain electrode) connected to a gate of the driver transistor 6402. The driver transistor 6402 has a first gate electrode connected to a power supply line 6407 through the capacitor 6403, a second gate electrode connected to the control line 6406B, a first electrode connected to the power supply line 6407, and a second electrode connected to a first electrode (a pixel electrode) of the light-emitting element 6404. A second electrode of the light-emitting element 6404 corresponds to a common electrode 6408. The common electrode 6408 is electrically connected to a common potential line provided over the same substrate, and the connection portion may be used as a common connection portion.
Note that the second electrode (the common electrode 6408) of the light-emitting element 6404 is set to a low power supply potential. The low power supply potential is a potential smaller than a high power supply potential when the high power supply potential set to the power supply line 6407 is a reference. As the low power supply potential, GND, 0 V, or the like may be employed, for example. A potential difference between the high power supply potential and the low power supply potential is applied to the light-emitting element 6404 to make current flow through the light-emitting element 6404, so that the light-emitting element 6404 emits light. Thus, each of the potentials is set so that the potential difference between the high power supply potential and the low power supply potential is equal to or higher than the forward threshold voltage of the light-emitting element 6404.
Note that gate capacitance of the driver transistor 6402 may be used as a substitute for the capacitor 6403, so that the capacitor 6403 can be omitted. The gate capacitance of the driver transistor 6402 may be formed between the channel region and the gate electrode, for example.
In the case of analog grayscale driving, voltage equal to or higher than the sum of the forward voltage of the light-emitting element 6404 and the threshold voltage of the driver transistor 6402 is applied to the first gate of the driver transistor 6402. The forward voltage of the light-emitting element 6404 indicates a voltage at which a desired luminance is obtained, and includes at least forward threshold voltage. The video signal by which the driver transistor 6402 operates in a saturation region is input, so that current can be supplied to the light-emitting element 6404. In order to allow the driver transistor 6402 to operate in the saturation region, the potential of the power supply line 6407 is set higher than the potential of the first gate of the driver transistor 6402. When an analog video signal is used, current can be made to flow through the light-emitting element 6404 in accordance with the video signal and analog grayscale driving can be performed.
As shown in
Note that the switching transistor 6401 serves as a switch and a potential of the second gate is not always required to be controlled by the control line 6406B. That is, the control line 6406B may be connected to only the second gate of the driver transistor 6402.
Note that the pixel structure illustrated in
In the case of digital grayscale driving, a video signal is input to the gate of the driver transistor 6402 so that the driver transistor 6402 is either completely turned on or completely turned off. That is, the driver transistor 6402 operates in a linear region. Since the driver transistor 6402 operates in a linear region, the potential of the first gate of the driver transistor 6402 is set higher than the potential of the power supply line 6407. Note that voltage which is equal to or higher than the sum of the voltage of the power supply line and the Vth of the driver transistor 6402 is applied to the signal line 6405. In this case, the same structure as in
Next, structures of a light-emitting element will be described with reference to
In order to extract light emitted from the light-emitting element, at least one of an anode and a cathode should be transparent. There are the following structures of a light-emitting element which is formed over the same substrate as a transistor: a top-emission structure in which light is extracted through the surface opposite to the substrate, a bottom-emission structure in which light is extracted through the surface of the substrate, and a dual-emission structure in which light is extracted through the surface opposite to the substrate and the surface of the substrate. As illustrated in
A light-emitting element having a top-emission structure will be described with reference to
In
In
In addition, a partition 7006 formed of an insulating material is provided in order to prevent short circuit of the second gate electrode 7009 and the cathode 7003. The light-emitting layer 7004 is provided so as to overlap with both of part of the partition 7006 and part of the cathode 7003 which is not covered with the partition 7006.
The light-emitting layer 7004 may be formed using either a single layer or a stacked layer of a plurality of layers. When the light-emitting layer 7004 is formed using a stacked layer of a plurality of layers, an electron-injection layer, an electron-transport layer, a light-emitting layer, a hole-transport layer, and a hole-injection layer are sequentially stacked over the cathode 7003. It is not necessary to form all of these layers. The anode 7005 is formed using a light-transmitting conductive material such as a film of indium oxide including tungsten oxide, indium zinc oxide including tungsten oxide, indium oxide including titanium oxide, indium tin oxide including titanium oxide, indium tin oxide (hereinafter referred to as ITO), indium zinc oxide, or indium tin oxide to which silicon oxide is added.
The light-emitting element 7002 includes the cathode 7003, the anode 7005, and the light-emitting layer 7004 sandwiched between the cathode 7003 and the anode 7005. In the case of the pixel illustrated in
Next, a light-emitting element having a bottom-emission structure will be described with reference to
In
Similarly to the case of
In
The light-emitting element 7012 includes the cathode 7013, the anode 7015, and the light-emitting layer 7014 sandwiched between the cathode 7013 and the anode 7015. In the case of the pixel illustrated in
Next, a light-emitting element having a dual-emission structure will be described with reference to
The cathode 7023 of the light-emitting element 7022 is formed over a conductive film 7027 having a light-transmitting property which is electrically connected to the transistor 7021 via a connection electrode 7028, and a light-emitting layer 7024 and an anode 7025 are stacked in this order over the cathode 7023. For the cathode 7023, any of conductive materials which have a low work function can be used as in the case of
Similarly to the case of
The light-emitting element 7022 includes the cathode 7023, the anode 7025, and the light-emitting layer 7024 sandwiched between the cathode 7023 and the anode 7025. In the case of the pixel illustrated in
In
Although an organic EL element is described here as a light-emitting element, an inorganic EL element may be used as a light-emitting element.
Note that although the example in which a transistor (a driver transistor) which controls driving of a light-emitting element is connected to the light-emitting element is described in this embodiment, a transistor for controlling current may be connected between the driver transistor and the light-emitting element.
Next, the appearance and a cross section of a light-emitting display panel (also referred to as a light-emitting panel), which is one embodiment of the semiconductor device of the present invention, will be described with reference to
A sealant 4505 is provided so as to surround a pixel portion 4502, signal line driver circuits 4503a and 4503b, and scan line driver circuits 4504a and 4504b which are provided over a first substrate 4500. In addition, a second substrate 4506 is provided over the pixel portion 4502, the signal line driver circuits 4503a and 4503b, and the scan line driver circuits 4504a and 4504b. Accordingly, the pixel portion 4502, the signal line driver circuits 4503a and 4503b, and the scan line driver circuits 4504a and 4504b are sealed together with a filler 4503, by the first substrate 4500, the sealant 4505, and the second substrate 4506. It is preferable that a panel be packaged (sealed) with a protective film (such as a laminate film or an ultraviolet curable resin film) or a cover material with high air-tightness and little degasification so that the panel is not exposed to the outside air as described above.
The pixel portion 4502, the signal line driver circuits 4503a and 4503b, and the scan line driver circuits 4504a and 4504b formed over the first substrate 4500 each include a plurality of transistors, and a transistor 4510 included in the pixel portion 4502 and a transistor 4509 included in the signal line driver circuit 4503a are illustrated as an example in
Here, the transistors 4509 and 4510 include a Zn—O-based oxide semiconductor. In this embodiment, the transistors 4509 and 4510 are n-channel transistors. The transistors 4509 and 4510 are covered with a resin layer 4508 which is provided over the first protective layer 4507, and a second protective insulating layer 4514 which is provided over the resin layer 4508. Note that the second protective insulating layer 4514 formed using silicon nitride is formed to cover a top surface and side surfaces of the resin layer 4508. A second gate electrode 4522 is provided as a top layer of the transistor 4509, and a second gate electrode 4521 is provided as a top layer of the transistor 4510. The second gate electrodes 4521 and 4522 are formed from the same layer, and they each control the threshold voltage of the transistor, and function as a protective layer for the oxide semiconductor layer.
The width of the second gate electrode 4522 may be larger than that of the gate electrode of the transistor 4509 so that gate voltage can be applied to the entire oxide semiconductor layer. In the case where the second gate electrode 4522 is formed using a light-blocking conductive material, the oxide semiconductor layer of the transistor 4509 can be shielded from light. In the case where the second gate electrode 4522 is formed using a light-blocking conductive material, changes in electric characteristics of the transistor due to photosensitivity of the oxide semiconductor can be prevented and thus the transistor can operate stably.
The width of the second gate electrode 4521 is different from that of the second gate electrode 4522 and is smaller than that of the first gate electrode of the transistor 4510. When the width of the second gate electrode 4521 is made smaller than that of the first gate electrode of the transistor 4510, an area in which the second gate electrode 4521 overlaps with the source electrode or the drain electrode of the transistor 4510 is reduced, whereby parasitic capacitance can be reduced. The width of the second gate electrode 4521 is smaller than that of the oxide semiconductor layer of the transistor 4510; thus, the second gate electrode 4521 shields only part of the oxide semiconductor layer from light, but a second electrode layer 4513 is provided over the second gate electrode 4521. When the second electrode layer 4513 is formed using a light-blocking conductive material, the entire part of the oxide semiconductor layer can be shielded from light.
A first electrode layer 4517 that is a pixel electrode included in the light-emitting element 4511 is connected to a source electrode or a drain electrode of the transistor 4510. Note that the light-emitting element 4511 has a structure in which the first electrode layer 4517, an electroluminescent layer 4512, and the second electrode layer 4513 are stacked, but it is not limited to the structure. The structure of the light-emitting element 4511 can be changed as appropriate depending on the direction in which light is extracted from the light-emitting element 4511, or the like.
A partition wall 4520 is formed using an organic resin film, an inorganic insulating film, or organic polysiloxane. It is particularly preferable that the partition wall 4520 be formed using a photosensitive material and an opening be formed over the first electrode layer 4517 so that a sidewall of the opening is formed as an inclined surface with continuous curvature.
The electroluminescent layer 4512 may be formed using either a single layer or a stacked layer of a plurality of layers.
A protective film may be formed over the second electrode layer 4513 and the partition wall 4520 in order to prevent entry of oxygen, hydrogen, moisture, carbon dioxide, or the like into the light-emitting element 4511. As the protective film, a silicon nitride film, a silicon nitride oxide film, a DLC film, or the like can be formed.
A variety of signals and potentials are supplied to the signal line driver circuits 4503a and 4503b, the scan line driver circuits 4504a and 4504b, or the pixel portion 4502 from FPCs 4518a and 4518b.
In this embodiment, a connection terminal electrode 4515 and the first electrode layer 4517 which is included in the light-emitting element 4511 are formed from the same material and the same layer. A terminal electrode 4516 and the source and drain electrodes which are included in the transistors 4509 and 4510 are formed from the same material and the same layer. Note that a gate insulating layer 4501 of the transistors 4509 and 4510 is provided below the terminal electrode 4516
The connection terminal electrode 4515 is electrically connected to a terminal included in the FPC 4518a through an anisotropic conductive film 4519.
The second substrate 4506 located in the direction in which light is extracted from the light-emitting element 4511 needs to have a light-transmitting property. In that case, a light-transmitting substrate such as a glass plate, a plastic plate, a polyester film, or an acrylic film is used.
As the filler 4503, an ultraviolet curable resin or a thermosetting resin can be used, in addition to an inert gas such as nitrogen or argon. For example, PVC (polyvinyl chloride), acrylic, polyimide, an epoxy resin, a silicone resin, PVB (polyvinyl butyral), or EVA (ethylene vinyl acetate) can be used. Here, nitrogen is used for the filler 4503.
In addition, if needed, an optical film, such as a polarizing plate, a circularly polarizing plate (including an elliptically polarizing plate), a retardation plate (a quarter-wave plate or a half-wave plate), or a color filter, may be provided as appropriate on a light-emitting surface of the light-emitting element. Further, the polarizing plate or the circularly polarizing plate may be provided with an anti-reflection film. For example, anti-glare treatment by which reflected light can be diffused by projections and depressions on the surface so as to reduce the glare can be performed.
The signal line driver circuits 4503a and 4503b and the scan line driver circuits 4504a and 4504b may be provided using a single crystal semiconductor film or polycrystalline semiconductor film over another substrate. In addition, only the signal line driver circuits, or only the scan line driver circuits or part thereof may be separately formed over another substrate.
Through the above steps, a highly reliable light-emitting display device (display panel) as a semiconductor device can be manufactured.
This embodiment can be implemented in combination with any of the other embodiments as appropriate.
In this embodiment, a liquid crystal display device to which the transistor including an oxide semiconductor layer described in any one of Embodiments 1 to 4 is applied will be described. A liquid crystal display device having a display function can be manufactured using the transistors including an oxide semiconductor layer which are described in any one of Embodiments 1 to 4 not only in a driver circuit but also in a pixel portion. Further, part or whole of a driver circuit can be formed over the same substrate as a pixel portion, using the transistor, whereby a system-on-panel can be obtained.
The liquid crystal display device includes a liquid crystal element (a liquid crystal display element) as a display element.
In addition, the liquid crystal display device includes a panel in which a display element is sealed, and a module in which an IC and the like including a controller are mounted on the panel. The liquid crystal display device also includes one mode of an element substrate before the display element is completed in a manufacturing process of the liquid crystal display device, and the element substrate is provided with a means to supply current to the display element in each pixel. Specifically, the element substrate may be in a state after only a pixel electrode of the display element is formed, a state after a conductive film to be a pixel electrode is formed but before the conductive film is etched to be the pixel electrode, or any other states.
A liquid crystal display device in this specification refers to an image display device, a display device, or a light source (including a lighting device). Further, the liquid crystal display device also includes any of the following modules in its category: a module to which a connector such as a flexible printed circuit (FPC), a tape automated bonding (TAB) tape, or a tape carrier package (TCP) is attached; a module having a TAB tape or a TCP at the end of which a printed wiring board is provided; and a module in which an integrated circuit (IC) is directly mounted on a display element by a chip-on-glass (COG) method.
Next, the appearance and a cross section of a liquid crystal display panel, which is one embodiment of the liquid crystal display device of the present invention, will be described with reference to FIGS. 24A1, 24A2, and 24B. FIGS. 24A1 and 24A2 are top views of panels in which a liquid crystal element 4013 is sealed with a sealant 4005 between a first substrate 4001 and a second substrate 4006.
In FIGS. 24A1, 24A2, and 24B, the sealant 4005 is provided so as to surround a pixel portion 4002 and a scan line driver circuit 4004 which are provided over the first substrate 4001. The second substrate 4006 is provided over the pixel portion 4002 and the scan line driver circuit 4004. Therefore, the pixel portion 4002 and the scan line driver circuit 4004 are sealed together with a liquid crystal layer 4008, by the first substrate 4001, the sealant 4005, and the second substrate 4006. There is no particular limitation on the liquid crystal layer 4008 in this embodiment, but a liquid crystal material exhibiting a blue phase is used. A liquid crystal material exhibiting a blue phase has a short response time of one millisecond or less from the state of applying no voltage to the state of applying voltage, whereby short-time response is possible. The liquid crystal material exhibiting a blue phase includes a liquid crystal and a chiral agent. The chiral agent is employed to align the liquid crystal in a helical structure and to make the liquid crystal exhibit a blue phase. For example, a liquid crystal material into which a chiral agent is mixed at 5 wt % or more may be used for the liquid crystal layer. As the liquid crystal, a thermotropic liquid crystal, a low-molecular liquid crystal, a high-molecular liquid crystal, a ferroelectric liquid crystal, an anti-ferroelectric liquid crystal, or the like is used.
In FIG. 24A1, a signal line driver circuit 4003 that is formed using a single crystal semiconductor film or a polycrystalline semiconductor film over a substrate separately prepared is mounted in a region that is different from the region surrounded by the sealant 4005 over the first substrate 4001.
Note that FIG. 24A2 illustrates an example in which part of the signal line driver circuit is formed over the first substrate 4001. A signal line driver circuit 4003b is formed over the first substrate 4001, and a signal line driver circuit 4003a formed using a single crystal semiconductor film or a polycrystalline semiconductor film is mounted over a separately-prepared substrate.
Note that the connection method of a driver circuit which is separately formed is not particularly limited, and a COG method, a wire bonding method, a TAB method, or the like can be used. FIG. 24A1 illustrates an example in which the signal line driver circuit is mounted by a COG method, and FIG. 24A2 illustrates an example in which the signal line driver circuit is mounted by a TAB method.
The pixel portion 4002 and the scan line driver circuit 4004 which are provided over the first substrate 4001 include a plurality of transistors.
The transistors 4010 and 4011 are covered with the first protective insulating layer 4020, the resin layer 4021 which is the second protective insulating layer, and the third protective insulating layer 4022. The first protective insulating layer 4020 is provided over and in contact with the oxide semiconductor layers of the transistors 4010 and 4011 and a gate insulating layer 4019.
The resin layer 4021 which is the second protective insulating layer and serves as a planarizing insulating film can be formed from an organic material having heat resistance, such as polyimide, acrylic, benzocyclobutene, polyamide, or epoxy. Other than such organic materials, it is also possible to use a low-dielectric constant material (a low-k material), a siloxane-based resin, phosphosilicate glass (PSG), borophosphosilicate glass (BPSG), or the like. Note that the resin layer 4021 may be formed by stacking a plurality of insulating films formed of these materials. The resin layer 4021 is a light-transmitting resin layer and a photosensitive polyimide resin is used in this embodiment.
There is no particular limitation on the formation method of the insulating layer, and the following method can be employed depending on the material: a method such as a sputtering method, an SOG method, spin coating, dip coating, spray coating, or a droplet discharging method (e.g., ink jetting, screen printing, or offset printing), or with a tool (equipment) such as a doctor knife, a roll coater, a curtain coater, or a knife coater.
Note that the third protective insulating layer 4022 is provided to prevent entry of an impurity element (such as sodium) which floats in air, such as an organic substance, a metal substance, or water vapor, and which contaminates the oxide semiconductor layer, and the third protective insulating layer 4022 is preferably a dense film. The protective film may be formed using either a single layer or a stacked layer of a silicon oxide film, a silicon nitride film, a silicon oxynitride film, a silicon nitride oxide film, an aluminum oxide film, an aluminum nitride film, aluminum oxynitride film, and/or an aluminum nitride oxide film by a PCVD method or a sputtering method.
Further, the third protective insulating layer 4022 is formed using a silicon nitride film obtained under a low power condition by a plasma CVD method. Further, a base insulating layer 4007 which is formed using a silicon nitride film and the third protective insulating layer 4022 are in contact with each other outside the pixel portion to surround the resin layer 4021 which is the second protective insulating layer. Thus, the transistors 4010 and 4011 are encapsulated with silicon nitride films, whereby the reliability of the transistors 4010 and 4011 is improved.
A second gate electrode 4028 is formed over the first protective insulating layer 4020 and in a position overlapping with the oxide semiconductor layer of the transistor 4011. A second gate electrode 4029 is formed over the third protective insulating layer 4022 and in a position overlapping with the oxide semiconductor layer of the transistor 4010.
A pixel electrode layer 4030 and a common electrode layer 4031 are provided over the first substrate 4001, and the pixel electrode layer 4030 is electrically connected to the transistor 4010. The second gate electrodes 4028 and 4029 can have the same potential as the common electrode layer 4031. The second gate electrodes 4028 and 4029 are formed in the same step as the common electrode layer 4031. Further, if the second gate electrodes 4028 and 4029 are formed using a light-blocking material, they can also serve as light-blocking layers shielding the oxide semiconductor layers of the transistors 4011 and 4010 from light.
Alternatively, the second gate electrodes 4028 and 4029 can have a different potential from the common electrode layer 4031. In this case, a control line electrically connected to the second gate electrodes 4028 and 4029 is provided and the threshold voltage of each of the transistors 4011 and 4010 is controlled with a potential of the control line.
Note that the structures of the transistors are not limited to the above description, and the second gate electrodes 4028 and 4029 may be connected to the first gate electrode, or they may be in a floating state.
The liquid crystal element 4013 includes the pixel electrode layer 4030, the common electrode layer 4031, and the liquid crystal layer 4008. In this embodiment, a method is used in which grayscale is controlled by generating an electric field which is substantially parallel to a substrate (i.e., in a lateral direction) to move liquid crystal molecules in a plane parallel to the substrate. In such a method, an electrode structure used in an in plane switching (IPS) mode or a fringe field switching (FFS) mode can be used. Note that a polarizing plate 4032 and a polarizing plate 4033 are provided on the outer sides of the first substrate 4001 and the second substrate 4006, respectively.
For the first substrate 4001 and the second substrate 4006, a glass substrate, a plastic substrate, or the like having a light-transmitting property can be used. As the plastic substrate, a fiberglass-reinforced plastics (FRP) plate, a polyvinyl fluoride (PVF) film, a polyester film, or an acrylic resin film can be used. Moreover, a sheet in which aluminum foil is sandwiched between PVF films or polyester films can also be used.
A post spacer 4035 is obtained by selective etching of an insulating film and is provided in order to control the thickness (a cell gap) of the liquid crystal layer 4008. Note that the shape of the spacer is not limited thereto, and a spherical spacer may alternatively be used. The columnar post spacer 4035 is located to overlap with the second gate electrode 4029.
FIGS. 24A1, 24A2, and 24B illustrate examples of liquid crystal display devices in which a polarizing plate is provided on the outer side (the view side) of a substrate; however, the polarizing plate may be provided on the inner side of the substrate.
Furthermore, a light-blocking layer serving as a black matrix may be provided to an appropriate position. In FIGS. 24A1, 24A2, and 24B, a light-blocking layer 4034 is provided on the second substrate 4006 side so as to cover the transistors 4010 and 4011. By provision of the light-blocking layer 4034, contrast can be further improved and the transistor can operate stably.
When the light-blocking layer 4034 is provided, the intensity of incident light on the oxide semiconductor layers of the transistors can be attenuated; accordingly, electric characteristics of the transistors can be prevented from being varied due to photosensitivity of the oxide semiconductor layers and the transistors can operate stably.
The pixel electrode layer 4030, the common electrode layer 4031, and the second gate electrodes 4028 and 4029 can be formed from a light-transmitting conductive material such as indium oxide containing tungsten oxide, indium zinc oxide containing tungsten oxide, indium oxide containing titanium oxide, indium tin oxide containing titanium oxide, indium tin oxide (hereinafter referred to as ITO), indium zinc oxide, or indium tin oxide to which silicon oxide is added.
A conductive composition containing a conductive high molecule (also referred to as a conductive polymer) can also be used for the pixel electrode layer 4030, the common electrode layer 4031, and the second gate electrodes 4028 and 4029.
Note that a variety of signals and potentials are supplied to the signal line driver circuit 4003 which is formed separately, and the scan line driver circuit 4004 or the pixel portion 4002 from an FPC 4018.
Further, since the transistor is easily broken by static electricity and the like, a protective circuit for protecting the driver circuits is preferably provided over the same substrate for a gate line or a source line. The protective circuit is preferably formed using a nonlinear element in which an oxide semiconductor is used.
In FIGS. 24A1, 24A2, and 24B, a connection terminal electrode 4015 and the pixel electrode layer 4030 are formed from the same layer, and a terminal electrode 4016 and source and drain electrode layers of the transistors 4010 and 4011 are formed from the same layer.
The connection terminal electrode 4015 is electrically connected to a terminal included in the FPC 4018 through an anisotropic conductive film 4017.
FIGS. 24A1, 24A2, and 24B illustrate an example in which the signal line driver circuit 4003 is separately formed and mounted on the first substrate 4001; however, this embodiment is not limited to this structure. The scan line driver circuit may be formed separately and then mounted, or only part of the signal line driver circuit or part of the scan line driver circuit may be formed separately and then mounted.
In the case where color display is performed, for example, light-emitting diodes which emit light of plural colors may be arranged in a backlight portion. In the case of an RGB mode, a red light-emitting diode 2610R, a green light-emitting diode 2610G, and a blue light-emitting diode 2610B are disposed in each of the regions into which a display area of the liquid crystal display device is divided.
A polarizing plate 2606 is provided on the outer side of the counter substrate 2601, and a polarizing plate 2607 and an optical sheet 2613 are provided on the outer side of the element substrate 2600. A light source is formed using the red light-emitting diode 2610R, the green light-emitting diode 2610G, the blue light-emitting diode 2610B, and a reflective plate 2611. An LED control circuit 2614 provided for a circuit substrate 2612 is connected to a wiring circuit portion 2608 of the element substrate 2600 via a flexible wiring board 2609 and further includes an external circuit such as a control circuit or a power source circuit.
In this embodiment, an example in which LEDs are individually made to emit light by this LED control circuit 2614, so that a field-sequential liquid crystal display device is formed; however, an embodiment of the present invention is not limited thereto. A cold cathode tube or a white LED may be used as a light source of backlight, and a color filter may be provided.
Further, in this embodiment, an example of an electrode structure used in the IPS mode is described; however, there is no particularly limitation on the electrode structure mode. The following mode can be used: a TN (twisted nematic) mode, an MVA (multi-domain vertical alignment) mode, a PVA (patterned vertical alignment) mode, an ASM (axially symmetric aligned micro-cell) mode, an OCB (optical compensated birefringence) mode, an FLC (ferroelectric liquid crystal) mode, an AFLC (antiferroelectric liquid crystal) mode, or the like.
This embodiment can be implemented in combination with any of the other embodiments as appropriate.
In this embodiment, an example of an electronic paper will be described as a semiconductor device which includes a plurality of transistors including an oxide semiconductor layer.
The electronic paper of
The transistor 581 has a bottom-gate structure. A first electrode layer 587 is electrically connected to a source or drain electrode through an opening formed in a first protective insulating layer 584, a resin layer 585 which is a second protective insulating layer, and a third protective insulating layer 586. The first protective insulating layer 584 covers the transistor 581. A second gate electrode 582 is provided below and in contact with the resin layer 585 which is provided over the first protective insulating layer 584, and the third protective insulating layer 586 is provided to cover the second gate electrode 582. An oxide semiconductor layer of the transistor 581 is protected by the first protective insulating layer 584, the resin layer 585 which is the second protective insulating layer, the second gate electrode 582, and the third protective insulating layer 586.
Between the first electrode layer 587 and a second electrode layer 588, spherical particles 589 each having a black region 590a, a white region 590b, and a cavity 594 are provided. A space around the spherical particles 589 is filled with a filler 595 such as a resin (see
Further, instead of the twisting ball, an electrophoretic element can also be used. A microcapsule having a diameter of about 10 μm to 200 μm in which transparent liquid, positively charged white microparticles, and negatively charged black microparticles are encapsulated, is used. In the microcapsule which is provided between the first electrode layer and the second electrode layer, when a potential difference is generated between the first electrode layer and the second electrode layer, the white microparticles and the black microparticles move to opposite sides, so that white or black can be displayed. A display element using this principle is an electrophoretic display element and is called an electronic paper in general. The electrophoretic display element has higher reflectance than a liquid crystal display element, and thus, an auxiliary light is unnecessary, power consumption is low, and a display portion can be recognized in a dim place. In addition, even when power is not supplied to the display portion, an image which has been displayed once can be maintained. Accordingly, in the case where the electric paper has a structure in which a signal and electric power are wirelessly supplied from an electric wave source, a displayed image can be held even if a semiconductor device having a display function is distanced from the electric wave source.
By using the transistor manufactured by the process described in any one of Embodiments 1 to 4 as a switching element, an electronic paper can be manufactured as a semiconductor device at low cost. An electronic paper can be used for electronic devices of a variety of fields as long as they can display data. For example, an electronic paper can be applied to an electronic book (e-book) reader, a poster, an advertisement in a vehicle such as a train, displays of various cards such as a credit card, and the like. Examples of such electronic devices are illustrated in
A first display portion 2705 and a second display portion 2707 are incorporated in the first housing 2701 and the second housing 2703, respectively. The first display portion 2705 and the second display portion 2707 may be configured to display one image or different images. In the case where the first display portion 2705 and the second display portion 2707 display different images, for example, a display portion on the right side (the first display portion 2705 in
In the electronic book reader 2700 in
The electronic book reader 2700 may be configured to transmit and receive data by wireless communication. The structure can be employed in which desired book data or the like is purchased and downloaded from an electronic book server by wireless communication.
This embodiment can be implemented in combination with any of the other embodiments as appropriate.
A semiconductor device using the transistor described in any one of Embodiments 1 to 4 can be applied to a variety of electronic devices (including an amusement machine). Examples of electronic devices include a television set (also referred to as a television or a television receiver), a monitor of a computer or the like, a camera such as a digital camera or a digital video camera, a digital photo frame, a mobile phone handset (also referred to as a mobile phone or a mobile phone device), a portable game console, a portable information terminal, an audio reproducing device, a large-sized game machine such as a pachinko machine, and the like.
In the television set in
The television set illustrated in
Note that the television set illustrated in
When the display portion 1002 of the mobile phone handset 1000 illustrated in
There are mainly three screen modes of the display portion 1002. The first mode is a display mode mainly for displaying an image. The second mode is an input mode mainly for inputting data such as text. The third mode is a display-and-input mode which is a combination of the two modes, that is, a combination of the display mode and the input mode.
For example, in the case of making a call or texting, a text input mode mainly for inputting text is selected for the display portion 1002 so that text displayed on a screen can be inputted. In that case, it is preferable to display a keyboard or number buttons on almost all area of the screen of the display portion 1002.
When a detection device including a sensor for detecting inclination, such as a gyroscope or an acceleration sensor, is provided inside the mobile phone handset 1000, display on the screen of the display portion 1002 can be automatically changed by determining the orientation of the mobile phone handset 1000 (whether the mobile phone handset 1000 is placed horizontally or vertically for a landscape mode or a portrait mode).
The screen modes are changed by touching the display portion 1002 or using the operation buttons 1003 of the housing 1001. Alternatively, the screen modes may be changed depending on the kind of the image displayed on the display portion 1002. For example, when a signal of an image displayed on the display portion 1002 is the one of moving image data, the screen mode is changed to the display mode. When the signal is the one of text data, the screen mode is changed to the input mode.
Further, in the input mode, when input by touching the display portion 1002 is not performed for a certain period while a signal detected by the optical sensor in the display portion 1002 is detected, the screen mode may be controlled so as to be changed from the input mode to the display mode.
The display portion 1002 may function as an image sensor. For example, an image of a palm print, a fingerprint, or the like is taken when the display portion 1002 is touched with a palm or a finger, whereby personal identification can be performed. Further, by providing a backlight or a sensing light source which emits near-infrared light in the display portion 1002, an image of a finger vein, a palm vein, or the like can be taken.
The cellular phone in
This embodiment can be implemented in combination with any of the other embodiments as appropriate.
One of methods for examining reliability of transistors is a bias-temperature stress test (hereinafter, referred to as a BT test). The BT test is one kind of accelerated test and can evaluate change in characteristics, caused by long-term usage, of transistors in a short time. In particular, the amount of shift in threshold voltage of the transistor between before and after the BT test is an important indicator for examining reliability. Between before and after the BT test, the small amount of shift in threshold voltage means high reliability.
Specifically, the temperature of a substrate over which a transistor is formed (substrate temperature) is set at fixed temperature, a source and a drain of the transistor are set at the same potential, and a gate is supplied with potential different from those of the source and the drain for a certain period. The substrate temperature may be set as appropriate in accordance with the purpose of the test. A test in the case where potential applied to the gate is higher than potentials of the source and the drain is referred to as a +BT test, and a test in the case where potential applied to the gate is lower than potentials of the source and the drain is referred to as a −BT test.
The stress conditions for the BT test can be determined by setting the substrate temperature, electric field intensity applied to a gate insulating film, or a time period of application of electric field. The electric field intensity applied to a gate insulating film can be determined by dividing the potential difference between the gate potential and the source and drain potential by the thickness of the gate insulating film. For example, in the case where the electric field intensity applied to the 100-nm-thick gate insulating film is to be set to 2 MV/cm, the potential difference may be set to 20 V.
In this example, results of a BT test performed on three kinds of samples are described. The samples are subjected to heat treatment under a nitrogen atmosphere at 250° C., 350° C., and 450° C., which is performed before formation of a source and a drain in manufacture of a transistor.
Note that “voltage” generally indicates a difference between potentials of two points, and “potential” indicates a static electric energy (electrical potential energy) unit charge which is at a point in a static electric field has. However, in an electronic circuit, a difference between a potential at a certain point and a reference potential (e.g., a ground potential) is often referred to as the potential at a certain point. Thus, in the following description, when a difference between a potential at a certain point and a reference potential (e.g., a ground potential) is referred to as the potential at a certain point, the potential at a certain point means the voltage except for the case where definition is particularly given.
As the BT test, a +BT test and a −BT test were performed under such conditions that a substrate temperature was 150° C., an electric field intensity applied to a gate insulating film was 2 MV/cm, and a time period for application was one hour.
First, the +BT test is described. In order to measure initial characteristics of a transistor subjected to the BT test, a change in characteristics of the source-drain current (hereinafter, referred to as the drain current) was measured, under the conditions where the substrate temperature was set to 40° C., the voltage between a source and a drain (hereinafter, the drain voltage) was set to 10 V, and the voltage between a source and a gate (hereinafter, the gate voltage) was changed in the range of −20 V to +20 V. That is, Vg-Id characteristics were measured. Here, as a countermeasure against moisture-absorption onto surfaces of the samples, the substrate temperature was set to 40° C. However, the measurement may be performed at room temperature (25° C.) or lower if there is no particular problem.
Next, the substrate temperature was increased to 150° C., and then, the potentials of the source and the drain of the transistor were set to 0 V. After that, the voltage was applied to the gate so that the electric field intensity applied to the gate insulating film was 2 MV/cm. In this case, the thickness of the gate insulating film of the transistor was 100 nm. The gate was supplied with +20 V of voltage, and the gate supplied with the voltage was kept for one hour. Note that although the time period for voltage application was one hour here, the time period may be changed as appropriate in accordance with the purpose.
Next, the substrate temperature was lowered to 40° ° C. while the voltage was kept on being applied to the source, the drain, and the gate. If application of the voltage is stopped before the substrate temperature was completely lowered to 40° C., the transistor which has been damaged during the BT test is repaired by the influence of residual heat. Thus, lowering of the substrate temperature needs to be performed with application of the voltage. After the substrate temperature was lowered to 40° C., application of the voltage was terminated.
Then, the Vg-Id characteristics were measured under the conditions same as those for the measurement of the initial characteristics, so that the Vg-Id characteristics after the +BT test were obtained.
Next, the −BT test is described. The −BT test was performed with the procedure similar to the +BT test, but has a different point from the +BT test, in that the voltage applied to the gate after the substrate temperature is increased to 150° C. is set to −20 V.
In the BT test, it is important to use a transistor which has been never subjected to a BT test. For example, if a −BT test is performed with use of a transistor which has been once subjected to a +BT test, the results of the −BT test cannot be evaluated correctly due to influence of the +BT test which has been performed previously. Similarly, if the transistor which has been once subjected to a +BT test is used for another+BT test, the results cannot be evaluated correctly. However, the usage of the transistor is not limited to the above in the case where the BT test is performed repeatedly in consideration of such influence.
Note that in
Note that in each of
In terms of the amount of shift in the threshold voltage after the +BT test, it is found from
As can be seen from
As described in this example, according to one embodiment of the present invention, the reliability in both of the +BT test and the −BT test can be improved.
Note that the transistor having high reliability in the −BT test as described above is particularly useful for application to a driver circuit in a driver circuit portion of a display device.
In this example, heat treatment was performed on a plurality of samples under a nitrogen atmosphere at heat temperatures whose conditions were determined. Such a plurality of samples were measured with thermal desorption spectroscopy (hereinafter referred to as TDS). Measurement results are shown in
The TDS is used for detecting and identifying a gas component discharged or generated from the samples by a quadrupole mass analyzer; thus, a gas and a molecule discharged from surfaces and insides of the samples can be observed. Discharge or generation of gas from the samples occurs while the samples are heated and the temperature is rising in high vaccum. With use of a TDS (product name: 1024 amu QMS) manufactured by ESCO Ltd., under a condition where the rising temperature was at approximately 10° C./min, measurement was performed. At the beginning of the measurement, the pressure was 1×10−8 (Pa), and during the measurement, the pressure was at a degree of vacuum of about 1×10−7 (Pa).
In addition, from the graphs of
Note that even in the case where the sample which has been subjected to heat treatment at 450° ° C. under a nitrogen atmosphere is left at room temperature in an air atmosphere approximately for one week, discharge of moisture at 200° C. or higher was not observed. Thus, it is found that by performing heat treatment, the In—Ga—Zn—O-based non-single-crystal film becomes stable.
Further,
Next, measurements of the carrier concentration and Hall mobility are described.
From the results of
Moreover, H, O, OH, H2, O2, N, N2, and Ar, in addition to H2O, were each measured by TDS. The measurement resulted in that peaks of H, O, and OH were observed clearly but peaks of H2, O2, N, N2, and Ar were not observed. As samples of the above measurement, a structure where an In—Ga—Zn—O-based non-single-crystal film with an original thickness of 50 nm was formed over a glass substrate was used. The conditions of heat treatment were set as follows: heat treatment under a nitrogen atmosphere at 250° C. for an hour; that under a nitrogen atmosphere at 350° C. for an hour; that under a nitrogen atmosphere at 350° C. for ten hours; and that under a nitrogen atmosphere at 450° C. for an hour. As comparative samples, a structure in which heat treatment was not performed on an In—Ga—Zn—O-based non-single-crystal film and a structure including only a glass substrate were measured.
With respect to an oxide semiconductor layer including a region having high oxygen density and a region having low oxygen density, a phenomenon in which oxygen is diffused in accordance with heat treatment was simulated. The result thereof will be described with reference to
The layer 703 having low oxygen density was formed to have an amorphous structure including In atoms, Ga atoms, Zn atoms, and O atoms, where the numbers of In atoms, Ga atoms, and Zn atoms were each 15 and the number of O atoms was 54.
In addition, the layer 705 having high oxygen density was formed to have an amorphous structure including In atoms, Ga atoms, Zn atoms, and O atoms, where the numbers of In atoms, Ga atoms, and Zn atoms were each 15 and the number of O atoms was 66.
The density of the oxide semiconductor layer 701 was set to 5.9 g/cm3.
Next, the classical molecular dynamics (MD) simulation was performed on the oxide semiconductor layer 701 under conditions of NVT ensemble and a temperature of 250° C. The time step was set to 0.2 fs, and the total simulation time was set to 200 ps. In addition, Born-Mayer-Huggins potential was used for the potentials of metal-oxygen bonding and oxygen-oxygen bonding. Moreover, movement of atoms at an upper end portion and a lower end portion of the oxide semiconductor layer 701 was fixed.
The simulation results are shown in
The solid line 707 shows that the oxide semiconductor layer 701 has high oxygen densities in a region ranging from an interface between the layer 703 having low oxygen density and the layer 705 having high oxygen density to the layer 705 having high oxygen density. On the other hand, the dashed line 709 shows that the oxygen density is uniform in the layer 703 having low oxygen density and the layer 705 having high oxygen density.
From the above, when there is non-uniformity in the distribution of oxygen concentration as in the stack of the layer 703 having low oxygen density and the layer 705 having high oxygen density, it is found that the oxygen diffuses from where the oxygen density is higher to where the oxygen density is lower by heat treatment and thus the oxygen density becomes uniform.
That is, as described in Embodiment 1, since the oxygen density at the interface between the oxide semiconductor layer 403 and the first oxide insulating layer 407 is increased by formation of the first protective insulating layer 407 over the oxide semiconductor layer 403 with use of an insulating oxide, the oxygen diffuses to the oxide semiconductor layer 403 where the oxygen density is low and thus the oxide semiconductor layer 403 has higher resistance. As described above, the reliability of a transistor included in a display device which is one embodiment of the present invention can be improved.
This application is based on Japanese Patent Application serial no. 2009-159052 filed with Japan Patent Office on Jul. 3, 2009, the entire contents of which are hereby incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-159052 | Jul 2009 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 18129975 | Apr 2023 | US |
| Child | 18616403 | US | |
| Parent | 17573792 | Jan 2022 | US |
| Child | 18129975 | US | |
| Parent | 16923395 | Jul 2020 | US |
| Child | 17573792 | US | |
| Parent | 16270079 | Feb 2019 | US |
| Child | 16923395 | US | |
| Parent | 15827318 | Nov 2017 | US |
| Child | 16270079 | US | |
| Parent | 15096663 | Apr 2016 | US |
| Child | 15827318 | US | |
| Parent | 14804508 | Jul 2015 | US |
| Child | 15096663 | US | |
| Parent | 14228663 | Mar 2014 | US |
| Child | 14804508 | US | |
| Parent | 13632709 | Oct 2012 | US |
| Child | 14228663 | US | |
| Parent | 12828464 | Jul 2010 | US |
| Child | 13632709 | US |