Electrode for p-type gallium nitride-based semiconductors

Information

  • Patent Grant
  • 6734091
  • Patent Number
    6,734,091
  • Date Filed
    Friday, June 28, 2002
    22 years ago
  • Date Issued
    Tuesday, May 11, 2004
    20 years ago
Abstract
An improved electrode for a p-type gallium nitride based semiconductor material is disclosed that includes a layer of an oxidized metal and a first and a second layer of a metallic material. The electrode is formed by depositing three or more metallic layers over the p-type semiconductor layer such that at least one metallic layer is in contact with the p-type semiconductor layer. At least two of the metallic layers are then subjected to an annealing treatment in the presence of oxygen to oxidize at least one of the metallic layers to form a metal oxide. The electrodes provide good ohmic contacts to p-type gallium nitride-based semiconductor materials and, thus, lower the operating voltage of gallium nitride-based semiconductor devices.
Description




BACKGROUND OF THE INVENTION




Recently, much attention has been focused on GaN-based compound semiconductors (e.g., In


x


Al


y


Ga


1−x−y


N, wherein x+y≦1,0≦x≦1, and 0≦y≦1) for blue, green, and ultraviolet light emitting diode (LED) applications. One important reason is that GaN-based LEDs have been found to exhibit efficient light emission at room temperature.




In general, GaN-based LEDs comprise a multilayer structure in which n-type and p-type GaN-based semiconductor layers are stacked on a substrate (most commonly on a sapphire substrate with the n-type GaN-based semiconductor layer in contact with the substrate), and In


x


Ga


1−x


N/GaN multiple quantum well layers are sandwiched between the p-type and n-type GaN layers. A number of methods for growing the multilayer structure are known in the art, including metalorganic chemical vapor deposition (MOCVD), molecular beam epitaxy (MBE) and hydride vapor phase epitaxy (HVPE).




In general, p-type GaN-based semiconductor layers formed by growth methods, such as MOCVD, behave like a semi-insulating or high-resistive material. This is thought to result from hydrogen passivation caused by hydrogen that is present in the reaction chamber complexing with the p-type dopant and thus preventing the dopant from behaving as an active carrier. Typically, p-type GaN-based semiconductor materials are thermally annealed to activate the p-type carriers. However, even after thermal annealing, the resistivity of p-type GaN-based semiconductor materials remains relatively high making it difficult to form a satisfactory ohmic contact with the material. In addition, there are few metals with a high work function comparable to the band gap and electron affinity of gallium nitride and that will form a low resistance interface with gallium nitride. A good ohmic contact to gallium nitride is desirable because the performance of gallium nitride-based devices, such as the operating voltage is strongly influenced by the contact resistance.




Sapphire is generally used as the substrate for GaN-based LEDs because it is inexpensive and GaN-based semiconductor layers grown on a sapphire substrate are reasonably free of defects. However, sapphire is electrically insulative. Thus, electrodes cannot be mounted on the sapphire substrate, but must be formed directly on the n-type and p-type GaN-based semiconductor layers. In addition, since p-type GaN-based semiconductor layers have only moderate conductivity, a p-electrode typically is formed to cover substantially the entire surface of the p-type GaN-based semiconductor layer in a GaN-based LED in order to ensure uniform application of current to the entire layer and obtaining uniform light emission from the LED. However, this geometry requires that the light emitted by the LED be observed through the sapphire substrate or through a transparent p-electrode. Typically, light-transmitting electrodes transmit only 20 to 40% of the light emitted from the LED. Although sapphire has a high transmission coefficient, observation of the light emitted from the LED through the sapphire substrate requires a complicated packaging step. Thus, in order to decrease the cost of manufacture and increase the efficiency of GaN-based LEDs, it is desirable to develop p-electrodes that have improved light transmission.




SUMMARY OF THE INVENTION




The invention is an improved electrode for a p-type gallium nitride based semiconductor material that includes a layer of an oxidized metal and a first and a second layer of a metallic material. The first metallic layer has a first surface in contact with a p-type gallium nitride based semiconductor material and a second surface in contact with a first surface of the oxidized metal layer. The oxidized metal layer has a second surface in contact with a surface of the second metallic layer. Preferably, the electrode is light transmissive. In one embodiment, the oxidized metal layer is nickel oxide and the first and second metallic layers are gold.




The electrode of the invention can be used to form a semiconductor device, such as a light-emitting diode (LED) or a laser diode (LD). The semiconductor device includes a substrate having a first major surface. Over the first major surface of the substrate is a semiconductor device structure that includes an n-type gallium nitride-based semiconductor layer, and a p-type gallium nitride-based semiconductor layer over the n-type semiconductor layer. A first electrode is in electrical contact with the n-type semiconductor layer, and a second electrode in contact with the p-type semiconductor layer. The second electrode includes a layer of an oxidized metal and a first and a second layer of a metallic material. The first metallic layer has a first surface in contact with a p-type gallium nitride based semiconductor material and a second surface in contact with a first surface of the oxidized metal layer. The oxidized metal layer has a second surface in contact with a surface of the second metallic layer. Preferably, the second electrode is light transmissive and forms an ohmic contact with the p-type semiconductor layer. The oxidized metal layer includes metal oxides such as nickel oxide and zinc oxide. The oxidized metal layer is preferably nickel oxide. Typically, the layer of metallic material includes metals such as gold, nickel, palladium, platinum, silver, and combinations thereof. In one embodiment, the first and second metallic layers are substantially the same. Preferably, the first and second metallic layers are gold.




To prepare semiconductor devices utilizing the electrode of the invention, a substrate having a first major surface is provided, and a semiconductor device structure is provided over the first major surface of the substrate. The semiconductor device structure includes an n-type gallium nitride-based semiconductor layer and a p-type gallium nitride-based semiconductor layer over the n-type semiconductor layer. An electrode is formed that is in electrical contact with the n-type gallium nitride-based semiconductor layer. Three or more metallic layers are formed over the p-type semiconductor layer such that at least one metallic layer is in contact with the p-type semiconductor layer. At least two of the metallic layers are then subjected to an annealing treatment in the presence of oxygen to form an electrode in contact with the p-type gallium nitride-based semiconductor layer. Generally, the annealing treatment is conducted at a temperature that is about 400° C. or more but below the decomposition temperature of the GaN-based semiconductor layers. Preferably the annealing temperature is in the range of between about 400° C. and about 550° C. In one embodiment, the annealing treatment is preformed in an environment that includes oxygen and nitrogen. After the annealing treatment, the electrode formed is typically light transmissive. In one embodiment, prior to the annealing treatment, the electrode has a first metallic layer having a first surface is formed in contact with the p-type semiconductor layer, and a second metallic layer having a first surface is formed in contact with a second surface of the first metallic layer. After annealing the second metallic layer is substantially oxidized to a metal oxide. A third metallic layer is then formed in contact with a second surface of the metal oxide layer. Preferably, prior to the annealing treatment, the first metallic layer includes gold and the second metallic layer includes nickel. After annealing the second metallic layer is substantially oxidized to nickel oxide, and a third metallic layer is formed over the metal oxide. Preferably, the third metallic layer is gold. In another embodiment, prior to the annealing treatment, three metallic layers are formed over the p-type semiconductor material. The first metallic layer has a first surface in contact with the p-type semiconductor layer; the second metallic layer has a first surface in contact with a second surface of the first material; and the third metallic layer has a surface in contact with a second surface of the second metallic material. In one embodiment, the third metallic layer is substantially the same metallic material as the first metallic layer. In a preferred embodiment, the first and third layers include gold and the second layer includes nickel which is substantially oxidized to nickel oxide during the annealing treatment.




The electrodes of the invention form ohmic contacts with p-type GaN-based semiconductor materials and typically are more light transmissive than prior art electrodes used to form ohmic contacts with p-type GaN-based semiconductor materials which do not contain metal oxides.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a current-voltage curve for an electrode formed by the method described in Example 1.





FIG. 2

is a current-voltage curve for an electrode formed by the method described in Example 2.











DETAILED DESCRIPTION OF THE INVENTION




As used herein, a gallium nitride-based semiconductor material is a material having the formula In


x


Al


y


Ga


1−x−y


N, wherein x+y≦1, 0≦x≦1, and 0≦y≦1. Gallium nitride-based semiconductor material are usually grown by a vapor phase growth method such as metalorganic chemical vapor deposition (MOCVD or MOVPE, hydride chemical vapor deposition (HDCVD), or molecular beam epitaxy (MBE). Generally, a gallium nitride-based semiconductor material is an n-type material even when no n-type dopant is included in the material since nitrogen lattice vacancies are created during crystal growth. Thus, an n-type gallium nitride-based semiconductor material may not include an n-type dopant. However, an n-type gallium nitride-based semiconductor typically exhibits better conductivity when the material includes an n-type dopant. n-Type dopants for gallium nitride-based semiconductor materials include Group IV elements such as silicon, germanium and tin, and Group VI elements such as selenium, tellurium and sulfur.




A p-type gallium nitride-based semiconductor material is a gallium nitride-based semiconductor material that includes a p-type dopant. The p-type dopants (also called an acceptor) for gallium nitride-based semiconductor materials include Group II elements such as cadmium, zinc, beryllium, magnesium, calcium, strontium, and barium. Preferred p-type dopants are magnesium and zinc. Typically, during growth of the gallium nitride-based semiconductor material gaseous compounds containing hydrogen atoms are thermally decomposed to form the semiconductor material. The released hydrogen atoms, which are present mainly as protons, become trapped in the growing semiconductor material, and combine with p-type dopant inhibiting their acceptor function. To improve the conductivity of a p-type gallium nitride-based semiconductor material, the material may be placed in a high electric field, typically above 10,000 volts/cm for about 10 minutes or more. The protons trapped in the semiconductor material are drawn out of the material to the negative electrode, thereby activating the function of the p-type dopants (see U.S. patent application Ser. No. 10/127,345, the entire teachings of which are incorporated herein by reference). Alternatively, the conductivity of the p-type gallium nitride-based semiconductor material can be improved by annealing the material at a temperature above 600° C. in a nitrogen environment for 10 minutes or more (see U.S. Pat. No. 5,306,662, the entire teachings of which are incorporated herein by reference).




As described above, a gallium nitride-based semiconductor structure includes an p-type gallium nitride-based semiconductor layer and n-type gallium nitride-based semiconductor layer. The p-type gallium nitride-based semiconductor layer is generally grown over the n-type gallium nitride-based semiconductor layer. The n-type and p-type semiconductor layers can be in direct contact with each other or, alternatively, an active region can be sandwiched between the n-type and p-type gallium nitride-based semiconductor layers. An active region can have a single quantum-well structure or a multiple quantum-well structure. An active region having a single quantum-well structure has a single layer (i.e., the well layer) formed of a gallium nitride-based semiconductor material having a lower band-gap than the n-type and p-type gallium nitride-based semiconductor layers sandwiching it. An active region having a multiple quantum-well structure includes multiple well layers alternately stacked with multiple layers that have a higher band-gap than the well layers (i.e., barrier layers). The outer most layer of the active region closest to the n-type gallium nitride-based semiconductor layer is a well layer and has a smaller band-gap than the n-type gallium nitride-based semiconductor layer. The outer most layer of the active region closest to the p-type gallium nitride-based semiconductor layer may be a well layer or a barrier layer and may have a band-gap that is larger or smaller than the p-type gallium nitride-based semiconductor layer. Typically, the thickness of a well layer in a quantum-well structure is about 70 Å or less, and the barrier layers are about 150 Å or less. Generally, the well layers and barrier layers in a quantum-well structure are not intentionally doped.




The phrase “substantially light transmissive,” as used herein, with respect to an electrode means that the electrode transmits at least 1% of the light emitted from the gallium nitride-based semiconductor device therethrough. A light-transmitting electrode typically transmits at least about 40% of the light emitted from the gallium nitride-based semiconductor device. Preferably, a light-transmitting electrode transmits about 60% or more of the light emitted from the gallium nitride-based semiconductor device.




The phrase “substantially oxidized,” as used herein when referring to a metallic layer, means that at least about 60% of the metal forming the metallic layer has been oxidized to a metal oxide. In one embodiment, at least about 80% of the metal in the metallic layer is oxidized to a metal oxide. In another embodiment, at least about 95% of the metal in the metallic layer is oxidized to a metal oxide. In yet another embodiment, at least about 99% of the metal in the metallic layer is oxidized to a metal oxide.




The phrase “ohmic contact,” as used herein, refers to a region where two materials are in contact, which has the property that the current flowing through the region is proportional to the potential difference across the region.




To prepare electrodes of the invention, a first, second and third layer of a metallic material are deposited on a p-type gallium nitride-based material, such as p-type gallium nitride (p-GaN), by evaporation sublimation or other techniques known to those skilled in the art. The first metallic layer is deposited on the p-type gallium nitride-based material such that a first surface of the first metallic layer is in contact with the p-type gallium nitride-based material. Typically, the thickness of the first metallic layer is in the range of between about 5 Å and about 100 Å. The first metallic layer is a metal such as gold, platinum, palladium, silver or combination thereof. In a preferred embodiment, the first metallic layer is gold. A second metallic layer is deposited on the first metallic layer such that a first surface of the second metallic layer is in contact with a second surface of the first metallic layer. The thickness of the second metallic layer is in the range of between about 30 Å and about 500 Å. The second metallic layer is a metal such as nickel or zinc. Preferably, the second metallic layer is nickel. A third metallic layer is deposited on the second metallic layer such that a first surface of the third metallic layer is in contact with a second surface of the second metallic layer. The thickness of the third metallic layer is in the range of between about 10 Å and about 500 Å. The third metallic layer is a metal such as gold, platinum, palladium, silver or combination thereof. Preferably, the second metallic layer is gold.




In one embodiment, the first and the second layers are deposited on the p-type gallium nitride-based material and are annealed in the presence of oxygen before the third layer is deposited on the second layer. In another embodiment, the annealing step is done after deposition of the third layer. In either case, the second metallic layer is substantially oxidized to a metal oxide, such as nickel oxide or zinc oxide, during the annealing step. The metal oxide formed behaves as a p-type semiconductor (p-NiO or p-ZnO). During the annealing step, the metallic layers are heated to a temperature in the range of between about 400° C. and about 550° C. for about 30 seconds to about 1 hour. The amount of oxygen present in the annealing environment is greater than about 1% and may be as high as 100%. The annealing environment can be air or a controlled environment such as 65% oxygen/35% nitrogen. The annealing step may be preformed in a furnace, rapid thermal annealing, or on a hot plate.




It is believed that during the annealing process epitaxial layers, such as Au/p-NiO/Au/p-GaN layers, are formed by domain matching epitaxy where integral multiples of lattice planes match across the film-substrate interface. For example, epitaxial gold, which has a lattice constant of 0.408 nm, grown on top of p-type gallium nitride provides a template for the growth of nickel oxide, which has a lattice constant 0.417 nm, via lattice matching epitaxy. Nickel oxide can grow over the top of gold as well as laterally to contact p-type gallium nitride semiconductor layer, providing an ohmic contact to p-type gallium nitride.




EXAMPLE 1




An electrode was prepared by depositing a 25 Å thick layer of gold on a p-type gallium nitride semiconductor material. An 80 Å thick layer of nickel was deposited on the gold layer, then a 40 Å thick gold layer was deposited on the nickel layer. The metal layers were annealed at a temperature of 470° C. in a furnace in an environment that containing 65% oxygen and 35% nitrogen for 30 min.




A current-voltage (I-V) curve was plotted in FIG.


1


. The inset in

FIG. 1

shows the configuration used to measure the voltage between two metal pads. As can be seen from

FIG. 1

, the current-voltage curve is linear indicating that the electrode formed an ohmic contact with the p-type gallium nitride semiconductor material.




EXAMPLE 2




An electrode was prepared by depositing a 10 Å thick layer of gold on a p-type gallium nitride semiconductor material. An 50 Å thick layer of nickel was deposited on the gold layer, then a 50 Å thick gold layer was deposited on the nickel layer. The metal layers were annealed at a temperature of 520° C. in a furnace in an environment that containing 100% oxygen for 15 min.




A current-voltage (I-V) curve was plotted in FIG.


2


. The voltage was measured between two metal pads using the same configuration as shown in the inset in FIG.


1


. As can be seen from

FIG. 2

, the current-voltage curve is linear indicating that the electrode formed an ohmic contact with the p-type gallium nitride semiconductor material.




EQUIVALENTS




While this invention has been particularly shown and described with references to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the scope of the invention encompassed by the appended claims.



Claims
  • 1. A method for producing a semiconductor device comprising:providing a substrate having a first major surface; providing a semiconductor device structure over the first major surface of the substrate, the device structure comprising an n-type gallium nitride-based semiconductor layer, and a p-type gallium nitride-based semiconductor layer over the n-type semiconductor layer; forming an electrode in electrical contact with the n-type gallium nitride-based semiconductor layer; forming three or more metallic layers over the p-type semiconductor layer, wherein at least one of the metallic layers is in contact with the p-type semiconductor layer; and subjecting at least two of the metallic layers to an annealing treatment in the presence of oxygen to form an electrode in contact with the p-type gallium nitride-based semiconductor layer.
  • 2. The method of claim 1, wherein the annealing treatment is conducted at a temperature of about 400° C. or more.
  • 3. The method of claim 1, wherein prior to the annealing treatment, a first metallic layer having a first surface is in contact with the p-type semiconductor layer, and a second metallic layer having a first surface is in contact with a second surface of the first metallic layer.
  • 4. The method of claim 3, wherein prior to the annealing treatment, a surface of a third metallic layer is in contact with a second surface of the second metallic material.
  • 5. The method of claim 4, wherein the second metallic layer is nickel or zinc and the first and third metallic layers are, independently, selected from the group consisting of gold, palladium, nickel, platinum, silver and combinations thereof.
  • 6. The method of claim 5, wherein the second metallic layer is nickel which is substantially oxidized to nickel oxide during the annealing treatment.
  • 7. The method of claim 6, wherein the first and third metallic layers are the same material.
  • 8. The method of claim 7, wherein the first and third metallic materials are gold.
  • 9. The method of claim 3, wherein the annealing treatment oxidizes the second metallic layer to for a metal oxide.
  • 10. The method of claim 9, wherein after the annealing treatment, a surface of a third metallic layer is formed in contact with a second surface of the second metallic material which has been substantially oxidized to a metal oxide.
  • 11. The method of claim 10, wherein the second metallic layer is nickel and the metal oxide formed is nickel oxide.
  • 12. The method of claim 11, wherein the first and the third metallic layers are, independently, selected from the group consisting of gold, palladium, nickel, platinum, silver and combinations thereof.
  • 13. The method of claim 12, wherein the third metallic layer comprises substantially the same metallic material as the first metallic layer.
  • 14. The method of claim 13, wherein the first metallic layer and the third metallic layer comprises gold.
  • 15. The method of claim 1, wherein the electrode formed is substantially light transmissive.
  • 16. The method of claim 1, wherein the annealing treatment is preformed in an environment that includes nitrogen.
INCORPORATION BY REFERENCE

The entire teachings of the following applications are incorporated herein by reference: Ser. No. 10/187,466, “High-Power Light-Emitting Diode Structures,” by John C. C. Fan, Hong K. Choi, and Steve Tchang-Hun Oh, filed on even date herewith; Ser. No. 10/187,468, “Bonding Pad for Gallium Nitride-Based Light-Emitting Device,” by Tchang-Hun Oh, Hong K. Choi, Bor-Yeu Tsaur, and John C. C. Fan, filed on even date herewith; Ser. No. 10/389,750, “Light-Emitting Diode Device Geometry,” by John C. C. Fan, Hong K. Choi, Steven Oh, J. C. Chen, and Jagdish Narayan, filed on Jun. 17, 2002; and Ser. No. 60/393,008, “Domain Epitaxy for Thin Film Growth,” by Jagdish Narayan, filed on even date herewith.

US Referenced Citations (63)
Number Name Date Kind
4153905 Charmakadze et al. May 1979 A
4495514 Lawrence et al. Jan 1985 A
4670088 Tsaur et al. Jun 1987 A
4946548 Kotaki et al. Aug 1990 A
4966862 Edmond Oct 1990 A
5091333 Fan et al. Feb 1992 A
5210051 Carter, Jr. May 1993 A
5239188 Takeuchi et al. Aug 1993 A
5247533 Okazaki et al. Sep 1993 A
5272108 Kozawa Dec 1993 A
5278433 Manabe et al. Jan 1994 A
5281830 Kotaki et al. Jan 1994 A
5285078 Mimura et al. Feb 1994 A
5290393 Nakamura Mar 1994 A
5306662 Nakamura et al. Apr 1994 A
5323022 Glass et al. Jun 1994 A
5334277 Nakamura Aug 1994 A
5369289 Tamaki et al. Nov 1994 A
5383088 Chapple-Sokol et al. Jan 1995 A
5385862 Moustakas Jan 1995 A
5406123 Narayan Apr 1995 A
5408120 Manabe et al. Apr 1995 A
5433169 Nakamura Jul 1995 A
5468678 Nakamura et al. Nov 1995 A
5563422 Nakamura et al. Oct 1996 A
5578839 Nakamura et al. Nov 1996 A
5652434 Nakamura et al. Jul 1997 A
5686738 Moustakas Nov 1997 A
5733796 Manabe et al. Mar 1998 A
5734182 Nakamura et al. Mar 1998 A
5747832 Nakamura et al. May 1998 A
5751752 Shakuda May 1998 A
5767581 Nakamura et al. Jun 1998 A
5777350 Nakamura et al. Jul 1998 A
5828684 Van de Walle Oct 1998 A
5850410 Kuramata Dec 1998 A
5877558 Nakamura et al. Mar 1999 A
5880486 Nakamura et al. Mar 1999 A
5905276 Manabe et al. May 1999 A
5959307 Nakamura et al. Sep 1999 A
5998925 Shimizu et al. Dec 1999 A
6017774 Yuasa et al. Jan 2000 A
6051849 Davis et al. Apr 2000 A
6066861 Höhn et al. May 2000 A
6069440 Shimizu et al. May 2000 A
6078063 Nakamura et al. Jun 2000 A
6084899 Shakuda Jul 2000 A
6093965 Nakamura et al. Jul 2000 A
6115399 Shakuda Sep 2000 A
6153010 Kiyoku et al. Nov 2000 A
6172382 Nagahama et al. Jan 2001 B1
6204512 Nakamura et al. Mar 2001 B1
6215133 Nakamura et al. Apr 2001 B1
6245259 Höhn et al. Jun 2001 B1
6249012 Manabe et al. Jun 2001 B1
6287947 Ludowise et al. Sep 2001 B1
6337493 Tanizawa et al. Jan 2002 B1
6362017 Manabe et al. Mar 2002 B1
6475854 Narwankar et al. Nov 2002 B2
20010022367 Nakamura et al. Sep 2001 A1
20010030318 Nakamura et al. Oct 2001 A1
20020046693 Kiyoku et al. Apr 2002 A1
20020060326 Manabe et al. May 2002 A1
Foreign Referenced Citations (29)
Number Date Country
0 483 688 May 1992 EP
0 483 688 May 1992 EP
52028887 Mar 1977 JP
54-093380 Jul 1979 JP
59-228776 Dec 1984 JP
61-056474 Mar 1986 JP
2229475 Sep 1990 JP
02-229475 Sep 1990 JP
03-203388 Sep 1991 JP
03-218625 Sep 1991 JP
03-252177 Nov 1991 JP
04-068579 Mar 1992 JP
4209577 Jul 1992 JP
4236478 Aug 1992 JP
04-242985 Aug 1992 JP
05-243614 Sep 1993 JP
06-021511 Jan 1994 JP
06-177423 Jun 1994 JP
06-268259 Sep 1994 JP
8167735 Jun 1996 JP
8213692 Aug 1996 JP
8306643 Nov 1996 JP
8306958 Nov 1996 JP
8316527 Nov 1996 JP
9092880 Apr 1997 JP
9134881 May 1997 JP
9167857 Jun 1997 JP
11145513 May 1999 JP
WO 8800392 Jan 1988 WO
Non-Patent Literature Citations (43)
Entry
Foresi, J.S. and Moustakes, T.D., “Metal contacts to gallium nitride,” Appl. Phys. Lett. 62 (22): 2859-2861 (1993).
Nakamura, S., “InGaN blue—light—emitting diodes,” Journal of the Institute of Electronics, Information and Communication Engineers 76(9) :913-917 (1993) (Abstrat).
Akasaki, I. and Amano, H., “High efficiency UV and blue emitting devices preared by MOVPE and low energy electron beam irradiation treatment,” Physical Concepts of Materials for Novel Optoelectronic Device Applications, 1361:138-149 (1990).
Amano, H., et al., “P-Type Conduction in Mg-Doped GaN Treated with Low-Energy electron Beam Irradiation (LEEBI)”, Japanese Journal of Applied Physics 28 (12) :L2112-L2114 (1989).
Andreev, V.M., et al., “Luminescence Properties of i-n, i-n-and n-i-n Structures Made of Epitaxial Layers GaN/α-Al2O3,” Journal of Luminescence 35:9-16 (1986).
Boulou, M., et al., “Recombination Mechanisms in GaN:Zn,” Journal of Luminescence 18/19:767-770 (1979).
Casey, Jr., H.C. and Panish, M.B., “SLAB-Dielectric Waveguides,” in Heterostructure Lasers, (NY: Academic Press), pp. 32-35 (1978).
Foresi, J.S. amd Moustakes, T.D., “Metal Contacts to gallium nitride,” Appl. Phys. Lett. 62(22) :2589-2861 (1993).
Goldenberg, B., et al., “Ultraviolet and violet light-emitting GaN diodes grown by low-pressure metalorganic chemical vapor deposition,” Appl. Phys. Lett. 62(4) :381-383 (1993).
F. Goodenough, “Exotic Semiconductors Showcased at the IEDM,” Electronic Design, pp. 60, 62, 64-66, 68 (1994).
Hayashi, I., et al., “Junction Lasers Which Operate Continuously at Room Temperature,” Appl. Phys. Lett. 17(3) :109-111 (1970).
Jacob, G., et al., “GaN Electroluminscent Devices: Preparation and Studies,” Journal of Luminescence 17:263-282 (1978).
Jang, J.-S., et al., “High Quality Non-Alloyed Pt Ohmic Contacts to P-Type GaN Using Two-Step Surface Treatment,” MRS Internet J. Nitride Semiconductor Res. F99W10.4.
Kaminska, E., et al., “Ni/Si-Based Contacts to GaN: Thermally Activated Structural Transformations Leading to Ohmic Behavior,” MRS Internet J. Nitride Semicond. Res. 4S1, G9.9.
Kampen, T.U. and Mönch, W., “Metal Contacts on a-GaN,” MRS Internet J. Nitride Semicond. Res. 1(41).
Madar, R., “High Pressure Solution Growth of GaN+,” Journal of Crystal Growth 31:197-203 (1975).
Matsuoka, T., “Growth and Properties of a Wide-Gap Semiconductor InGaN,” Optoelectronics 5(1) :53-64 (1990).
T. Matsuoka, “Current status of GaN and related compounds as wide-gap semiconductors,” Journal of Crystal Growth 124:433-438 (1992).
Nakamura, S., et al., “High-power InGaN/GaN double-heterostructure violet light emitting diodes,” Appl. Phys. Lett. 62(19) :2390-2392 (1993).
Nakamura, S., et al., “P-GaN/N-InGaN/N-GaN Double-Heterostructure Blue-Light-Emitting Diodes,” Jpn. J. Appl. Phys. 32:L8-L11 (1993).
S. Nakamura, “Growth of InxGa(1−x)N compound semiconductors and high-power InGaN/AlGaN double heterostructure violet-light-emitting diodes,” Microelectronics Journal 25:651-659 (1994).
Nakamura, S., et al., “High-Power GaN P-N Junction Blue-Light-Emitting Diodes,” Japanese Journal of Applied Physics 30(12A) :L1998-L2001 (1991).
S. Nakamura, “InGaN/AlGaN Double-Heterostructure Blue LEDs,” Mat. Res. Soc. Symp. Proc. vol. 339:173-178 (1994).
Nakamura, S., et al., “Thermal Annealing Effects on P-type Mg-Doped GaN Films,” Jpn. J. Appl. Phys. 31:L139-L142 (1992).
S. Nakamura, “Zn-doped InGaN growth and InGaN/AlGaN double-heterostructure blue-light-emitting diodes,” Journal of Crystal Growth 145:911-917 (1994).
Nakamura, S., et al., “High-brightness InGaN/AlGaN double-heterostructure blue-green-light-emitting diodes,” J. Appl. Phys. 76(12) :8189-8191 (1994).
Nakamura, S., et al., “Cd-Doped InGaN Films Grown on GaN Films,” Jpn. J. Appl. Phys. 32:L338-L341 (1993).
S. Nakamura, “High-Power InGaN/AlGaN Double-Heterostructure Blue-Light-Emitting Diodes,” Int'l Electronic Devices Meeting 94:567-570 (1994).
Piotrowska, A., et al., “Ohmic Contacts to III-V Compound Semiconductors: A Review of Fabrication Techniques,” Solid-State Electronics 26(3) :179-197 (1983).
Sporken, R., et al., “XPS study of Au/GaN and Pt/GaN contacts,” MRS Internet J. Nitride Semiconductor Res. 2(23) (1997).
Venugopalan, H.S., et al., “Phase Formation and Morphology in Nickel and Nickel/Gold Contacts To Gallium Nitride,” MRS Internet Journal Nitride Semiconductor Research (1997) <URL:http://nsr.mij.mrs.org/MRS/S97-D/4.10>.
Zhou, L., et al., “Characteristics of Ti/Pt/Au Ohmic Contacts on p-type GaN/AlxGa1−xN Superlattices,” MRS Internet J. Nitride Semicond. Res. F99W10.3.
Dovidenko, K., et al., “Aluminum nitride films on different orientations of sapphire and silicon,” J. Appl. Phys. 79(5): 2439-2445, (1996).
Jain, S.C., et al., “Applied Physics Reviews/III—nitrides: Growth, characterization, and properties,” J. Appl. Phys. 87(3) : 965-1006, (2000).
Lin, Y.S., et al., “Dependence of composition fluctuation on indium content in InGaN/GaN multiple quantum wells,” Appl. Phys. Lett., 77(19) : 2988-2990, (2000).
Narukawa, Y., et al., “Dimensionality of excitons in laser-diode structures composed of InxGa1−xN multiple quantum wells,” Phys. Rev. B, 59(15) : 10283-10288, (1999).
Kawakami, Y., et al., “Dynamics of opitcal gain in InxGa1−xN multi-quantum well-based laser diodes,” Appl. Phys. Lett., 77(14) : 2151-2153, (2000).
Strite, S., and Morkoc, H., “GaN, A1N, and InN: A review,” J. Vac. Sci. Technol. B, 10(4) :1237-1266, (1992).
Hassan, K.M., et al., “Optical and structural studies of Ge nanocrystals embedded in AIN matrix fabricated by pulsed laser deposition,” Appl. Phys. Lett., 75(9) : 1222-1224, (1999).
Teng, C.W., et al., “Quantum Confinement of E1 and E2 transitions in Ge quantum dots embedded in an Al2O3 or an A1N matrix,” App. Phys. Lett., 76(1) : 43-45, (2000).
Narukawa, Y., et al., “Role of self-formed InGaN quantum dots for exciton localization in the purple laser diode emitting at 420 nm,” Appl. Phys. Lett., 70(8) : 981-983, (1997).
Nakamura, S., “The Roles of Structural Imperfections in InGaN-Based Blue Light-Emitting Diodes and Laser Diodes,” Science Magazine, 1-14, [retrieved online Aug. 8, 2000]. Retrieved from the Internet <URL: http://www.science.org/cgi/content/full/281/5379/956>.
Chichibu, S., et al., “Spatially resolved cathodoluminescence spectra of InGaN quantum wells,” App. Phys. Lett., 71(16) : 2346-2348, (1997).