Patent Grant
11351753
This application claims the priority of Japanese Patent Application No. 2016-130450, filed on Jun. 30, 2016, in the JPO (Japanese Patent Office). Further, this application is the National Phase Application of International Application No. PCT/JP2017/023734, filed on Jun. 28, 2017, which designates the United States and was published in Japan. Both of the priority documents are hereby incorporated by reference in their entireties.
The present invention relates to an electromagnetic wave transmissive metal member having a metallic luster and an electromagnetic wave transmissibility, an article using the electromagnetic wave transmissive metal member, and a production method for an electromagnetic wave transmissive metal film.
A metal member having both a metallic luster and an electromagnetic wave transmissibility is needed, for example, to decorate a cover member of a millimeter-wave radar mounted to a front end of an automotive vehicle such as a front grille, an emblem or a bumper.
The millimeter-wave radar is configured to transmit an electromagnetic wave having a millimeter waveband (frequency: about 77 GHz, wavelength: about 4 mm) forwardly with respect to the vehicle, and receive and analyze a reflected wave from a target so as to measure a distance or a direction with respect to the target, or the size of the target. A result of the measurement can be utilized for inter-vehicle distance measurement, automatic vehicle speed adjustment, automatic brake adjustment, etc. The front component of the vehicle to which the millimeter-wave radar is mounted is a portion constituting, so to say, the face of the vehicle, and having a great impact on a user. Thus, it is preferable to create a high-class appearance by a metallic lustrous front decoration. However, if the front component of the vehicle is made of a metal material, it will substantially preclude or hinder the millimeter-wave radar from emitting and receiving an electromagnetic wave. Therefore, in order to prevent hindering of the function of the millimeter-wave radar without spoiling an aesthetic appearance of the vehicle, there is a need for a metal member having both a metallic luster and an electromagnetic wave transmissibility. As one effective solution, there have been proposed some metal members in which a metal layer is discontinuously formed to provide an electromagnetic wave transmissibility by means of resulting discontinuous portions.
For example, in the following Patent Document 1, there is proposed a metal covering in which an indium film is formed on a surface of a substrate in an island pattern by a vacuum vapor deposition process. The indium film formed in an island pattern has a metallic luster, and allows an electromagnetic wave to be transmitted therethrough via gaps defined between adjacent ones of a plurality of islands.
Further, in the following Patent Document 2, there is proposed a method of producing a metal film-decorated sheet through heating treatment. This metal film-decorated sheet is obtained by: preparing a workpiece sheet which comprises a crack-inducing layer formed on a substrate sheet, and a metal film layer made of a specific metal material and formed in contact with the crack-inducing layer; and heating the workpiece sheet at a high temperature (120° C. to 200° C.) while imposing a given tension on the workpiece sheet, thereby forming a plurality of stringlike planar structures divided by cracks.
In the following Patent Document 3, heating treatment is utilized as with the Patent Document 2. In the Patent Document 3, an aluminum (Al) film formed on a resin substrate and a chromium film formed on the aluminum film are heated at a high temperature (120° C.) together with the resin substrate to form a laminate of the aluminum film and the chromium film into a discontinuous structure by means of thermal stress.
In the following Patent Document 4, heating treatment is also utilized. Here, an electroconductive film having a metallic luster is formed on a surface of a substrate by an electroless plating process, and then subjecting the electroconductive film to after-baking, thereby forming island-shaped microcracks for allowing an electromagnetic wave to be transmitted through the electroconductive film.
Although a metal member having an electromagnetic wave transmissibility at a level capable of withstanding practical use can be obtained by the technique proposed in the Patent Document 1, this technique leads to high production cost because indium is costly, as pointed out by many documents (e.g., the Patent Document 4).
On the other hand, the techniques proposed in the Patent Documents 2 to 4 using no indium are free from the problem with material cost. However, considerable investment in facility for performing the heating treatment is needed. Moreover, although it is only necessary to spend a relatively low material cost, an energy source for the heating is needed, resulting in high production cost. Further, the heating needs to be performed under detailed management of a heating temperature and a heating time. If the management is not properly performed, crack control becomes unstable, leading to problems such as the occurrence of variation in electromagnetic wave transmissibility property, and the occurrence of whitish haze in a resulting metallic lustrous member. Further, the heating is performed during the process of forming cracks. This can lead to a new problem that, due to a difference in linear expansion coefficient between the metal layer and the substrate, the laminate undesirably curls, resulting in deteriorated appearance of a resulting metallic lustrous member (see, for example, paragraph [0052] in the Patent Document 4).
The present invention has been made in view of solving the above conventional problems, and an object thereof is to provide: an electromagnetic wave transmissive metal member capable of being easily produced at a low production cost, with both a metallic luster and an electromagnetic wave transmissibility; an article using the electromagnetic wave transmissive metal member; and a production method for an electromagnetic wave transmissive metal film.
In order to solve the above problems, according to a first aspect of the present invention, there is provided an electromagnetic wave transmissive metal member comprising a metal layer and a crack layer, wherein the metal layer and the crack layer have, in their respective planes, a plurality of linear cracks extending substantially parallel to each other, and the linear cracks in the metal layer and the linear cracks in the crack layer penetrate through their respective layers in a thickness direction, and are continuous with each other in the thickness direction.
It is noted here that the term “linear” in the above “linear cracks” is added to distinguish them from the gaps or cracks in the conventional techniques, e.g., the island-shaped gaps described in the Patent Document 1, and definitely does not mean being completely linear. The term “linear cracks” encompasses all cracks having linearity at a level obtainable by the method defined in the appended claims, i.e., by “bending and stretching a multi-layered film in a longitudinal direction of the multi-layered film, in a state in which the multi-layered film is folded toward the side of an elongated substrate film along a cross direction intersecting the longitudinal direction”. Further, the term “substantially parallel” definitely does not mean being completely parallel, but encompasses any parallel degree enough to be usable in a millimeter-wave radar, a mobile phone, a smart phone, a tablet PC, a notebook PC, a refrigerator and the like as application targets of the present invention.
Preferably, in the electromagnetic wave transmissive metal member according to the first aspect of the present invention, an angle made by adjacent two of the linear cracks included in the plane of at least one of the metal layer and the crack layer is within the range of ±10°.
Preferably, in the electromagnetic wave transmissive metal member according to the first aspect of the present invention, 40% or more of angles, each of the angles being made by a respective one of a plurality of sets of two linear cracks which are arbitrarily selected from among a plurality of linear cracks included in a 400 μm□(400 μm-square (this will also be applied to the following)) plane of the metal layer or the crack layer are within the range of ±10°.
More preferably, in the above electromagnetic wave transmissive metal member, and as for the two linear cracks which are arbitrarily selected from among a plurality of linear cracks included in a 400 μm square-plane of the metal layer or the crack layer, 40% or more of the angles, each of the angles being made by the selected two linear cracks, are within the range of ±10°, and 40% or more of the angles are in the range of 80° to 100°.
In the electromagnetic wave transmissive metal member according to the first aspect of the present invention, 80% or more of the plurality of linear cracks included in a 400 μm square-plane of the metal layer or the crack layer, lie within the range of ±5° with respect to a reference straight line.
It is noted here that the “reference straight line” means a straight line set in the following manner. In a region between a first straight line having an arbitrarily-set given angle and a second straight line rotated with respect to the first straight line about an arbitrary point as an intersecting point with the first straight line, in a given direction by a given angle, a plurality of straight lines each passing through the arbitrary point are drawn one-by-one every time an angle with respect to the first straight line increases by a unit angle, and a total of lengths of linear cracks overlapping the plurality of straight lines and lines parallel to the plurality of straight lines (except the second straight line and lines parallel to the second straight line) is measured. This measurement is repeatedly performed over all 360° directions about the arbitrary point, in a plurality of the regions each having the given angle, to obtain a plurality of the totals, and a straight line located intermediate between a specific one of a plurality of sets of the first straight line and the second straight line is set as the “reference straight line”, wherein the specific set of the first straight line and the second straight line define a region having a largest value among the plurality of totals.
When the rate of the linear cracks lying within the range of ±5° with respect to the reference straight line is relatively large, it means that the linear cracks uniformly extend in a given direction. Thus, it can be considered that a good polarization property is obtained.
In the electromagnetic wave transmissive metal member according to the first aspect of the present invention, the linear cracks may be formed in the metal layer and the crack layer by bending and stretching a multi-layered film obtained by laminating the metal layer and the crack layer on a substrate film, in only one direction in a state in which the multi-layered film is folded toward the side of the substrate film. The term “one direction” here means that the direction of the bending and stretching is along only one direction, and includes a reciprocating feeding processing.
In the electromagnetic wave transmissive metal member according to the first aspect of the present invention, 70% or less of the plurality of linear cracks included in a 400 μm square-plane of the metal layer or the crack layer, lie within the range of ±5° with respect to a reference straight line.
When the rate of the linear cracks overlapping straight lines each having an angle falling within a given range, with respect to the reference straight line, is relatively small, it means that the linear cracks do not uniformly extend in a given direction. Thus, the polarization property deteriorates, whereas the transmissibility becomes better.
In the electromagnetic wave transmissive metal member according to the first aspect of the present invention, the linear cracks may be formed in the metal layer and the crack layer by bending and stretching a multi-layered film obtained by laminating the metal layer and the crack layer on a substrate film, in a plurality of directions in a state in which the multi-layered film is folded toward the side of the substrate film. The term “plurality of directions” here means that the direction of the bending and stretching is along a plurality of directions, and that the multi-layered film may be fed in respective reciprocating directions.
Preferably, in the electromagnetic wave transmissive metal member according to the first aspect of the present invention, each of the linear cracks has a length of 200 μm or more.
Preferably, in the electromagnetic wave transmissive metal member according to the first aspect of the present invention, each of the linear cracks generated in one of the metal layer and the crack layer located farther from a bending side when the metal layer and the crack layer are being bent with a given curvature has a width of 0.1 nm to 100 nm.
Preferably, in the electromagnetic wave transmissive metal member according to the first aspect of the present invention, a ratio of a thickness of the metal layer to a thickness of the crack layer is from 0.1 to 20, the metal layer has a thickness of 10 nm to 1000 nm, and/or the crack layer has a thickness of 5 nm to 5000 nm.
Preferably, in the electromagnetic wave transmissive metal member according to the first aspect of the present invention, the crack layer is made of a substance containing at least one selected from the group consisting of a metal having a Mohs hardness of 4 or more, an alloy comprising a primary component consisting of the metal, and ceramics.
More preferably, in the above electromagnetic wave transmissive metal member, the ceramics contains any of an oxide, a nitride, a carbide and an oxynitride of an element including at least one selected from the group consisting of a metal, silicon, and boron.
Preferably, in the electromagnetic wave transmissive metal member according to the first aspect of the present invention, the metal layer has a Mohs hardness of 1 to less than 4. More preferably, the metal layer contains either of at least one metal selected from the group consisting of Al, Cu, Ag, Au, and Zn, and an alloy comprising a primary component consisting of the metal.
According to a second aspect of the present invention, there is provided an electromagnetic wave transmissive metal film comprising the above electromagnetic wave transmissive metal member and a substrate film, or an electromagnetic wave transmissive metal member-equipped resin component comprising the above electromagnetic wave transmissive metal member and a molded resin substrate.
In order to solve the above problems, according to a third aspect of the present invention, there is provided a method of producing an electromagnetic wave transmissive metal film. The method comprises: forming linear cracks in a metal layer and a crack layer by bending and stretching a multi-layered film in a longitudinal direction of the multi-layered film, in a state in which the multi-layered film is folded toward the side of an elongated substrate film along a cross direction intersecting the longitudinal direction, the multi-layered film being made by laminating the metal layer and the crack layer on the substrate film.
The present invention can provide: an electromagnetic wave transmissive metal member capable of being easily produced at a low production cost, with both a metallic luster and an electromagnetic wave transmissibility; an article using the electromagnetic wave transmissive metal member; and a production method for an electromagnetic wave transmissive metal film.
With reference to the accompanying drawings, a preferred embodiment of the present invention will now be described. Although only the preferred embodiment of the present invention will be described in the following for the sake of convenience of explanation, it should be understood that the present invention is not limited thereto.
The metal member 1 comprises at least a metal layer 11 and a crack layer 12. Each of the metal films 3, 3A comprises the metal layer 11 and the crack layer 12, and further comprises at least a substrate film 10. The metal film 3 depicted in
In the metal member 1 or the metal film 3 or 3′, a linear crack 11′ and a linear crack 12′ are formed, respectively, in the metal layer 11 and the crack layer 12. The linear crack 11′ and the linear crack 12′ penetrate through respective ones of the metal layer 11 and the crack layer 12 in a thickness direction (the arrowed direction “a” in
With reference to
(1) First of all, a multi-layered film 20 is prepared in which a metal layer 11 and a crack layer 12 are laminated on an elongated substrate film 10, as depicted in
(2) Subsequently, the multi-layered film 20 is bent and stretched using the apparatus depicted in
As depicted in
(3) Although the metal film 3 can be used in the state depicted in
The electromagnetic wave transmissibility of the metal film can be finely adjusted by the widths “A” to “C” of the linear cracks, or a pitch between adjacent two linear cracks (as well depicted in
The metal member 1 can be obtained by transferring a metal member 1 formed during production of the metal film 3. Further, this metal member 1 may be transferred to a resin substrate (not depicted) to produce an electromagnetic wave transmissive metal member-equipped resin component comprising the metal member 1 and the resin substrate.
As the substrate film 10, it is possible to use a transparent film made of a homopolymer or copolymer of polyethylene terephthalate (PET), polyethylene naphthalate (PEN), polybutylene terephthalate, polyamide, polyvinyl chloride, polycarbonate (PC), cycloolefin polymer (COP), polystyrene, polypropylene (PP), polyethylene, polycycloolefin, polyurethane, polymethylmethacrylate (PMMA), or ABS. Such a transparent film is suited to the bending and stretching under tension, and has no influence on metallic luster and electromagnetic wave transmissibility. However, from a viewpoint of forming the metal layer 11 and the crack layer 12 thereon, the transparent film is capable of withstanding high temperatures during vapor deposition, sputtering or the like. Thus, among the above materials, e.g., polyethylene terephthalate, polyethylene naphthalate, polymethylmethacrylate, polycarbonate, cycloolefin polymer, ABS, polypropylene, and polyurethane are preferable. Among them, polyethylene terephthalate is particularly preferable, because it has a good balance between heat resistance and cost.
The substrate film 10 may be a single-layer film or may be a laminate film. The thickness thereof is preferably in the range of about 6 to 250 μm. With a view to enhancing adhesion with the metal layer 11 or the crack layer 12, it may be subjected to plasma processing.
The crack layer 12 is intended to induce, in the metal layer 11 which is continuous with the linear crack 12′, the linear crack 11′ during generation of the linear crack 12′, by means of a stress arising in the metal layer 11 disposed in contact with or adjacent to the crack layer 12. Thus, the crack layer 12 needs to be easy to enable the linear crack 12′ to be generated therein and to be capable of applying a sufficient stress to the metal layer 11.
For this reason, the thickness of the crack layer 12 is typically in the range of 5 nm to 5000 nm, preferably in the range of 10 to 1000 nm, more preferably in the range of 20 to 200 nm.
It is considered that a substance having a given hardness is breakable due to its relatively low breaking strength, as long as it has a moderately thin thickness. Thus, examples of a material suitable for the crack layer 12 include: a metal having a Mohs hardness of 4 or more, such as a metal including at least one selected from the group consisting of Cr, Ti, W, V, Nb, Mo, and Ni; and an alloy comprising a primary component consisting of the metal. For the same reason, a ceramics having an extremely high brittleness can be deemed as a material suitable for the crack layer 12. The ceramics may contain any of an oxide, a nitride, a carbide and an oxynitride of an element including at least one selected from the group consisting of a metal, silicon, and boron. Examples of the oxide here include AL2O3, ITO (tin-doped indium oxide), ZnO, TiO2, Nb2O5 and SiO2. Examples of the nitride include AlN, TiN, SiN and BN, and examples of the carbide include TiC and SiC. Here, ITO is a substance containing costly In. However, it is a mixture of In and other substances, and thereby a production cost thereof can be reduced as comparted to a case of using only In.
Mohs hardnesses of main metals are presented in the following Table 1.
The metal layer 11 needs to be capable of enabling the linear crack 11′ to be induced and generated therein by the linear crack 12′, as well as being capable of exhibiting a sufficient metallic luster. On the other hand, when the linear crack is generated therein, it needs to have a width enough to avoid spoiling the external appearance due to scattering or whitish haze. Thus, the metal layer 11 preferably has a hardness less than that of the metal contained in the crack later.
For this reason, a metal having a Mohs hardness of 1 to less than 4 is suitable as the metal layer 11. As one example, the metal layer 11 preferably contains either of at least one metal selected from the group consisting of Al, Cu, Ag, Au, and Zn, and an alloy comprising a primary component consisting of the metal. Particularly, from a viewpoint of stability and cost of a substance, Al, Cu and an alloy thereof is preferable.
In view of enabling the linear crack 11′ to be easily induced, the thickness of the metal layer 11 is typically in the range of 10 nm to 1000 nm, preferably in the range of 20 to 200 nm, more preferably in the range of 30 to 100 nm. This thickness is suited to forming a uniform film, and can provide a good appearance to a molded resin article as a final product. Further, considering the thickness and brittleness of each of the metal layer 11 and the crack layer 12, a ratio of the thickness of the metal layer to the thickness of the crack layer, i.e., the thickness of the metal layer/the thickness of the crack layer, is preferably in the range of 0.1 to 20, more preferably, in the range of 0.2 to 10. Further, for the same reason, the Mohs hardness of the metal layer 11 is preferably less than the Mohs hardness of the crack layer 12, and typically in the range of 1 to less than 4, preferably in the range of 2 to 3.5.
As is clear from
The linear cracks may be formed not only in one direction but also in a plurality of directions. For example, the multi-layered film is subjected to bending and stretching in the longitudinal direction “β” of the multi-layered film to form the linear cracks depicted in
Even though the linear cracks 11′, 12′, 15 are small in size, they can significantly increase a sheet resistance. As the sheet resistance becomes larger, an electromagnetic wave transmissivity attenuation rate becomes smaller, which provides a sufficient electromagnetic wave transmissibility to the metal film 3, 3′. The sheet resistance of the metal film 3, 3′ is typically equal to or greater than 100Ω/□, preferably equal to or greater than 200Ω/□, more preferably equal to or greater than 400Ω/□. Further, the electromagnetic wave transmissivity attenuation rate of the metal film 3, 3′ in this embodiment is typically equal to or less than −10 dB, preferably equal to or less than −5 dB, more preferably equal to or less than −1 dB.
The width of each of the linear cracks in the metal film 3, 3′ during the bending, more exactly, the width of each of the linear cracks 11′ (12′) in a layer located farther from the bending side, or in the metal layer 11 in the example of
Further, an angle, in the metal film 3, 3′, made by adjacent two of the linear cracks 11′, 12′, 15 included in the plane, is typically within the range of ±10°, preferably within the range of ±5°. This angular difference can be considered to mean that the linear cracks are substantially parallel to each other, in regard to, e.g., a millimeter-wave radar.
In a case where the linear cracks are formed in an approximately rectangular lattice pattern, 40% or more of angles, each of the angles being made by two linear cracks which are arbitrarily selected from among a plurality of linear cracks 11′, 12′, 15 included in an arbitrary 400 μm□ (square)-plane of the metal or crack layer, are typically within the range of ±10°, preferably within the range of ±5°, more preferably within the range of ±2°. Further, in a case where the linear cracks are formed in an approximately rectangular lattice pattern, 40% or more of the angles, each of the angles being made by two linear cracks which are arbitrarily selected from among a plurality of linear cracks 11′, 12′, 15 included in a 400 μm□-plane of the metal or crack layer, are typically within the range of ±10° (preferably within the range of ±5°, more preferably within the range of ±2°), and 40% or more of the angles are typically in the range of 80° (preferably 85° or less than 85°, more preferably 87° or more than 87°) to 100° (preferably 105° or less than 105°, more preferably 102° or less than 102°). Performance can be improved by suppressing an angular variation in the linear cracks as described above.
The length of each of the linear cracks 11′, 12′, 15′ in the metal film 3, 3′ is typically equal to or greater than 200 μm, preferably equal to or greater than 500 μm. For example, the wavelength of a signal to be emitted and received by a millimeter-wave radar is about 4 mm Thus, the above length is considered to be sufficient for use in a millimeter-wave radar.
The present invention will be more specifically described below by taking inventive examples and comparative examples. Various samples of the metal film were prepared, and evaluated in terms of visible light reflectance, surface resistance and microwave electric field transmission attenuation amount. The visible light reflectance is used for evaluation on metallic luster, and the surface resistance and the microwave electric field transmission attenuation amount are used for evaluation on electromagnetic wave transmissibility. A larger value of each of the visible light reflectance and the surface resistance is more desirable, and a smaller value of the microwave electric field transmission attenuation amount is more desirable.
Details of evaluation methods are as follows.
(1) Visible Light Reflectance
A reflectance at a measurement wavelength of 550 nm was measured using a spectrophotometer U4100 manufactured by Hitachi High Technologies Co., Ltd. As a reference value, the reflectance of an Al-deposited mirror was defined as a reflectance of 100%.
In order to have a sufficient metallic luster, the visible light reflectance need to be equal to or greater than 40%, preferably equal to or greater than 60%, more preferably equal to or greater than 70%. If the visible light reflectance is equal to or less than 40%, there is a problem that metallic luster significantly deteriorates, resulting in poor external appearance.
(2) Surface Resistance
The surface resistance was measured by an eddy-current measurement method in accordance with JIS-Z2316, using a non-contact type resistance measuring device NC-80MAP manufactured by Napson Corporation.
For example, the surface resistance needs to be equal to or greater than 100/□, preferably equal to or greater than 200Ω/□, more preferably equal to or greater than 400Ω/□. If the surface resistance is equal to or less than 100Ω/□, there is a problem that a sufficient electromagnetic wave transmissibility cannot be obtained.
(3) Microwave Electric Field Transmission Attenuation Amount
A microwave electric field transmission attenuation amount at 1 GHz was evaluated using a KEC method measurement and evaluation jig, and a spectral analyzer CXA signal Analyzer NA9000A manufactured by Agilent technologies Inc.
The microwave electric field transmission attenuation amount needs to be equal to or less than −10 dB, preferably, equal to or less than −5 dB, more preferably equal to or less than −1 dB. If the microwave electric field transmission attenuation amount is equal to or greater than −10 dB, there is a problem that 90% or more of an electromagnetic wave is shielded.
An electromagnetic wave transmissibility in a frequency band (76 to 80 GHz) of a millimeter-wave radar is correlated with an electromagnetic wave transmissibility in a microwave band (1 GHz), which exhibits a relatively low value. Thus, in this evaluation, the electromagnetic wave transmissibility in the microwave band (1 GHz) was used as an indicator.
A result of the evaluations is presented in the following Table 2. In the Table 2, the “upper” layer indicated in the field “Layer Configuration” means a layer located farther from the bending side (the side of the substrate film 10), while the “lower” layer means a layer located closer to the bending side. Further, in a case where only one of the metal and crack layers is provided, the presence and the absence of the metal or crack layer are denoted, respectively, by “yes” and “-” in the field “Layer Configuration”. In Inventive Example 1 and Comparative Example 1, no value is indicated in the field “Mohs Hardness”. This is simply because it was difficult to measure an accurate value of the Mohs hardness, but does not mean the Mohs hardness is small. A material for the crack layer has a Mohs hardness of at least 4 or more which is sufficiently greater than the Mohs hardness of a material for the metal layer.
This is an example in which the metal layer and the crack layer are arranged, respectively, as an upper layer and a lower layer. A PET film (thickness: 125 μm) manufactured by Mitsubishi Plastics, Inc. was used as a substrate film (which is equivalent to the substrate film 10 in
Subsequently, this multi-layered film was wound around a metal rod having a diameter of 6 mm while being folded toward the side of the substrate film, as previously described with reference to
In
In Inventive Example 1, a good result was obtained with regard to all of the visible light reflectance, the surface resistance, and the microwave electric field transmission attenuation amount. In other words, a metal film or a metal member having both a metallic luster and an electromagnetic wave transmissibility could be obtained.
This is an example in which the metal layer and the crack layer are arranged, respectively, as an upper layer and a lower layer, as with Inventive Example 1, except that the crack layer is made of alumina (Al2O3). The remaining conditions are the same as those in Inventive Example 1. For reference, the Mohs hardness of alumina is 9, whereas the Mohs hardness of aluminum (Al) used as a material for the metal layer is 2.5.
In this case, a metal film or a metal member having both a metallic luster and an electromagnetic wave transmissibility could be obtained.
This is an example in which the crack layer and the metal layer are arranged, respectively, as an upper layer and a lower layer, differently from Inventive Examples 1 and 2. Further, differently from Inventive Example 1, the crack layer was formed as a 45 nm-thick chromium (Cr) layer, and the metal layer was formed as a 20 nm-thick aluminum (Al) layer. The remaining conditions are the same as those in Inventive Example 1. For reference, the Mohs hardness of chromium is 8.5, whereas the Mohs hardness of aluminum is 2.5.
In this case, a metal film or a metal member having both a metallic luster and an electromagnetic wave transmissibility could be obtained.
Differently from Inventive Example 1, the multi-layered film was subjected to the bending and stretching processing in a plurality of directions, more specifically, subjected to the bending and stretching processing in the longitudinal direction “β” (see
In this case, a metal film or a metal member having both a metallic luster and an electromagnetic wave transmissibility could be obtained.
This is an example in which the metal layer and the crack layer are arranged, respectively, as an upper layer and a lower layer, as with Inventive Example 1. However, differently from Inventive Example 1, the bending and stretching processing was not performed. The remaining conditions are the same as those in Inventive Example 1.
In this case, a result regarding the electromagnetic wave transmissibility was insufficient, although a good result could be obtained with regard to the metallic luster.
This is an example in which the metal layer and the crack layer are arranged, respectively, as an upper layer and a lower layer, as with Inventive Example 1. The thickness of an aluminum (Al) layer as the upper layer was set to 70 nm, and an alumina (Al2O3) layer was used as the crack layer. Differently from Inventive Example 1, the bending and stretching processing was not performed. The remaining conditions are the same as those in Inventive Example 1.
In this case, a result regarding the electromagnetic wave transmissibility was insufficient, although a good result could be obtained with regard to the metallic luster.
This is an example in which the crack layer and the metal layer are arranged, respectively, as an upper layer and a lower layer, differently from Inventive Example 1. Further, differently from Inventive Example 1, the bending and stretching processing was not performed, and a 45 nm-thick chromium layer and a 20 nm-thick aluminum layer were used, respectively, as the crack layer and the metal layer. The remaining conditions are the same as those in Inventive Example 1.
In this case, a result regarding the electromagnetic wave transmissibility was insufficient, although a good result could be obtained with regard to the metallic luster.
This is an example in which the crack layer and the metal layer are arranged, respectively, as an upper layer and a lower layer, differently from Inventive Example 1. Further, differently from Inventive Example 1, a 45 nm-thick chromium layer and a 20 nm-thick aluminum layer were used, respectively, as the crack layer and the metal layer. Further, heating processing was performed, instead of performing the bending and stretching processing. The heating is based on operation of placing the metal film in an environment having a temperature of 120 degrees for 2 hours. The remaining conditions are the same as those in Inventive Example 1.
In this case, a result regarding the electromagnetic wave transmissibility was insufficient, although a good result could be obtained with regard to the metallic luster. Moreover, the metal film undesirably curled after the heating processing, resulting in difficulty in putting it to practical use.
These are examples in which only the metal layer is used, differently from Inventive Example 1. Further, the bending and stretching processing was not performed in Comparative Example 5, although it was performed in Comparative Example 6, as with Inventive Example 1. The remaining conditions are the same as those in Inventive Example 1.
In this case, a result regarding the electromagnetic wave transmissibility was insufficient, although a good result could be obtained with regard to the metallic luster.
These are examples in which only the crack layer is used, differently from Inventive Example 1. Further, differently from Inventive Example 1, a 50 nm-thick chromium layer was used as the crack layer. Further, the bending and stretching processing was not performed in Comparative Example 7, although it was performed in Comparative Example 8, as with Inventive Example 1. The remaining conditions are the same as those in Inventive Example 1.
In this case, a result regarding the metallic luster was insufficient because whitish haze occurred in an external surface, causing significant deterioration in the visible light reflectance, although a good result could be obtained with regard to the electromagnetic wave transmissibility was insufficient.
Various metal films were evaluated in terms of visible light reflectance, radio wave transmission attenuation amount, polarization degree, and crack ratio. The “visible light reflectance” is the same as the “visible light reflectance” in the aforementioned Inventive Example 1, etc., and the “radio wave transmission attenuation amount” is substantially equivalent to the “microwave electric field transmission attenuation amount” in the aforementioned Inventive Example 1, etc., and used for evaluation on electromagnetic wave transmissibility. The “polarization degree” is used for evaluation on polarization property obtained when linear cracks uniformly extend in a given direction. A larger value of the polarization degree means higher directionality of an electromagnetic wave. From a viewpoint of this directionality, a larger value of the polarization degree is more desirable. The “crack ratio” is correlated with the polarization degree. Thus, this was also added to evaluation items.
Details of evaluation methods are as follows.
(1) Visible Light Reflectance This item was measured by the same method using the same device as those in the aforementioned Inventive Example 1, etc.
(2) Radio Wave Transmission Attenuation Amount (Transmissivity)
A radio wave transmission attenuation amount at 76.5 GHz was evaluated using a transmission-reflection (return) attenuation measurement system LAF-26.5A manufactured by Keycom Corporation. The radio wave transmission attenuation amount is equivalent to the “microwave electric field transmission attenuation amount” in the aforementioned Inventive Example 1, etc. However, in this evaluation, microwave electric field transmission attenuation amounts of a “transmission axis” and a “blocking axis” were determined individually. The “microwave electric field transmission attenuation amount” in the aforementioned Inventive Example 1, etc., is substantially equivalent to the microwave electric field transmission attenuation amount of the “transmission axis”. The radio wave transmission attenuation amount of the “transmission axis” here means a radio wave transmission attenuation amount to be obtained when, in the above measurement system, a “polarization direction” of an electric field component of a receiving/emitting antenna is disposed to become perpendicular to a direction of a “linear crack serving as a reference line”. On the other hand, the radio wave transmission attenuation amount of the “blocking axis” here means a radio wave transmission attenuation amount to be obtained when, in the above measurement system, the “polarization direction” is disposed to become parallel to the direction of the “linear crack serving as a reference line”. In a case where the “polarization direction (polarization plane)” has an elliptical shape, a long axis thereof is used as the polarization direction. The “linear crack serving as a reference line” is defined as a linear crack along a “reference straight line” in “(4) Crack Ratio” as described later. The radio wave transmission attenuation amount of the “transmission axis” needs to be equal to or less than −10 dB, preferably equal to or less than −5 dB, more preferably equal to or less than −1 dB, as with the microwave electric field transmission attenuation amount” in the aforementioned Inventive Example 1, etc.
The “transmissivity” is a value which is not used for calculating the radio wave transmission attenuation amount but necessary for determining “(3). Polarization Degree” as described below, and can be determined by the following formula, using a value of the radio wave transmission attenuation amount.
Transmissivity (%)=10{circumflex over ( )}(−X/10)×100 (where X denotes the radio wave transmission attenuation amount (dB))
(3) Polarization Degree
The polarization degree is a value calculated as a ratio of the transmissivity (%) regarding the radio wave transmission attenuation amount of the “transmission axis” (hereinafter referred to as “T1”) to the transmissivity (%) regarding the radio wave transmission attenuation amount of the “blocking axis” (hereinafter referred to as “T2”), i.e., T1/T2. The polarization degree is appropriately adjusted according to the intended use. Generally, the polarization degree is preferably equal to or more than 1000, more preferably equal to or more than 2000, further preferably equal to or more than 4000.
(4) Crack Ratio
With reference to
First of all, with regard to the image in
Subsequently, the 90 values of the total length are summed up to obtain a final total length of the linear cracks (hereinafter referred to as “total length”).
Further, among the 90 values of the subtotal length, a region having the largest “subtotal length” (this region will hereinafter be referred to as “maximum region”) is extracted.
Further, a sum of lengths of linear cracks lying within the range of ±5° with respect to a straight line located intermediate between the first and second straight lines defining the maximum region (this straight line will hereinafter be referred to as “reference straight line”). More specifically, the subtotal length in the maximum region, a subtotal length in a first adjacent region rotated with respect to the maximum region in a given direction by 2°, a subtotal length in a second adjacent region further rotated with respect to the first adjacent region in the given direction by 2°, a subtotal length in a third adjacent region rotated with respect to the maximum region in a direction opposite to the given direction by 2° and a subtotal length in a fourth adjacent region further rotated with respect to the third adjacent region in the opposite direction by 2° are summed (this sum will hereinafter be referred to as “inclusive subtotal length”.
The “crack ratio” is a ratio of the “inclusive subtotal length” to the “total length”, i.e.,
Crack ratio (%)=Inclusive subtotal length (μm)/Total length (μm).
The crack ratio is correlated with the polarization degree. From a viewpoint of directionality, a larger value of the crack ratio is more desirable. Specifically, the crack ratio is preferably in the range of 80% to 100%, more preferably in the range of 90% to 100%, further preferably in the range of 95% to 100%, still further preferably in the range of 97% to 100%.
On the other hand, when the polarization degree and/or the crack ratio become larger, an electromagnetic wave is largely blocked, resulting in deterioration in the electromagnetic wave transmissibility. As above, the polarization degree and the electromagnetic wave transmissibility are in a trade-off relationship. Thus, from a viewpoint of the electromagnetic wave transmissibility, the polarization degree or the crack ratio is preferably set to a moderately small value. From the viewpoint of the electromagnetic wave transmissibility, the crack ratio is preferably equal to or less than 65%, more preferably equal to or less than 62%. Although a lower limit is not particularly limited, it is preferably equal to or greater than 30%, more preferably equal to or greater than 40%, further preferably equal to or greater than 50%, in view of a balance with the directionality.
A result of the evaluations is presented in the following Table 3. The items “Metal Layer”, “Crack Layer” and “Visible Light Reflectance” are the same as those described with reference to Table 2. In regard to conditions for the crack forming processing, the number of times of bending and the diameter of the metal rod around which the substrate film and others are wound are changed. In Inventive Examples 6 to 8, no value is indicated in the field “Mohs hardness”. This is simply because it was difficult to measure an accurate value of the Mohs hardness, but does not mean the Mohs hardness is small. A material for the crack layer has a Mohs hardness of at least 4 or more which is sufficiently greater than the Mohs hardness of a material for the metal layer. It should be noted that values of the polarization degree in Table 3 were calculated based on actual data, and do not exactly conform to values of T1/T2 in Table 3 because of significant figures (significant digits).
First of all, a multi-layered film having the same configuration as that in Inventive Example 2 was prepared in the same manner as that in Inventive Example 2. Subsequently, the multi-layered film was subjected to the bending and stretching processing using the 6 mm-diameter metal rod, as with Inventive Example 2. However, differently from Inventive Example 2, this bending and stretching processing was performed by repeating the reciprocating feeing in the longitudinal direction “β” 2 times. As a result, the same optical microscopic image as that presented in
In this case, regarding linear cracks included in a plane equivalent to the unit area (400 μm□) presented in
Further, good results were obtained with regard to the visible light reflectance and the radio wave transmission attenuation amount. That is, a metal film or a metal member having both a metallic luster and an electromagnetic wave transmissibility could be obtained.
Differently from Inventive Example 5, a 50 nm-thick STO (sulfated tin oxide) layer was used as the crack layer serving as a lower layer. Further, differently from Inventive Example 5, the bending and stretching processing was performed by repeating the reciprocating feeing in the longitudinal direction “β” “60 times”. The remaining conditions are the same as those in Inventive Example 5.
In this case, regarding linear cracks included in a plane equivalent to the unit area (400 μm□) presented in
Differently from Inventive Example 5, a 50 nm-thick AZO (aluminum-doped zinc oxide) layer was used as the crack layer serving as a lower layer. Further, differently from Inventive Example 5, the bending and stretching processing was performed by repeating the reciprocating feeing in the longitudinal direction “β” “60 times”. The remaining conditions are the same as those in Inventive Example 5.
In this case, regarding linear cracks included in a plane equivalent to the unit area (400 μm□) presented in
Differently from Inventive Example 5, a 50 nm-thick copper (Cu) layer was used as the metal layer serving as an upper layer, and a 50 nm-thick ITO layer was used as the crack layer serving as a lower layer. Here, ITO is a complex oxide in which SnO2 is contained in In2O3 in an amount of 10 wt %, as with Inventive Example 1. Further, differently from Inventive Example 5, the bending and stretching processing was performed by repeating the reciprocating feeing in the longitudinal direction “β” “60 times”. The remaining conditions are the same as those in Inventive Example 5.
In this case, regarding linear cracks included in a plane equivalent to the unit area (400 μm□) presented in
Differently from Inventive Example 5, the crack layer and the metal layer are arranged, respectively, as an upper layer and a lower layer. Although an aluminum (Al) layer was used as the metal layer as with Inventive Example 5, the thickness thereof was set to 20 μm. On the other hand, a 45 μm-thick chromium (Cr) layer was used as the crack layer, differently from Inventive Example 5. Regarding the bending and stretching processing, the reciprocating feeing was performed 2 times, as with Inventive Example 1. The remaining conditions are the same as those in Inventive Example 1. An image obtained by subjecting an optical microscopic image of a surface of a metal film produced in this Inventive Example 9 to binarization processing is provided as the aforementioned image in
In this case, regarding linear cracks included in a plane equivalent to the unit area (400 μm□) presented in
Differently from Inventive Example 5, the bending and stretching processing was not performed. The remaining conditions are the same as those in Inventive Example 5.
In this case, a result regarding the electromagnetic wave transmissibility was insufficient, although a good result could be obtained with regard to the metallic luster.
As is clear from the above Inventive Examples and Comparative Examples, a result satisfying both the metallic luster and the electromagnetic wave transmissibility could not be obtained by only one of the metal layer and the crack layer (Comparative Examples 5 to 8). Thus, it is necessary to provide at least both of the metal layer and the crack layer.
Further, even in the case where the metal layer and the crack layer are provided, a good result could not be obtained when the bending and stretching processing was not performed (Comparative Examples 1 to 3, 5, 7 and 9), or the heating processing was performed (Comparative Example 4).
Further, when the metal layer has a thickness greater than that of the crack layer (Inventive Example 1, Comparative Example 1, Inventive Example 2 and Comparative Example 2), a good result is less likely to be obtained, although it would depend on a difference in Mohs hardness therebetween.
Further, when forming linear cracks in a lattice pattern (gridiron pattern) by generating not only in the cross direction intersecting the longitudinal direction but also the longitudinal direction (Inventive Example 3), a result was obtained in which the electromagnetic wave transmissibility was further improved.
Further, it was proven that an excellent polarization property can be obtained (Inventive Examples 5 to 8), and, on the other hand, a good electromagnetic wave transmissibility can be obtained in the case where the polarization property is not so good (Inventive Example 9).
It should be understood that the present invention is not limited to the above examples, but may be appropriately modified and implemented without departing from the spirit and scope of the present invention as set forth in appended claims.
The metal film or the metal member of the present invention can be suitably used, for example, to decorate a cover member of a millimeter-wave radar mounted to a front end of an automotive vehicle such as a front grille, an emblem or a bumper. Further, it can be used as a radar cover such as a radome, or a polarized antenna for a base station or the like. However, it is to be understood that application targets of the present invention are not limited thereto but may include various other articles requiring both an aesthetic quality and an electromagnetic wave transmissibility, such as a mobile phone, a smart phone, a tablet PC, a notebook PC, and a refrigerator.
| Number | Date | Country | Kind |
|---|---|---|---|
| JP2016-130450 | Jun 2016 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2017/023734 | 6/28/2017 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2018/003847 | 1/4/2018 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6328358 | Berweiler | Dec 2001 | B1 |
| 8455086 | Inuduka et al. | Jun 2013 | B2 |
| 9305680 | Yamazaki | Apr 2016 | B2 |
| 20090297880 | Maruoka et al. | Dec 2009 | A1 |
| 20120076986 | Inuduka | Mar 2012 | A1 |
| 20130248091 | Inuduka et al. | Sep 2013 | A1 |
| 20160237549 | Hara et al. | Aug 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 101590706 | Dec 2009 | CN |
| 102483480 | May 2012 | CN |
| 2000-159039 | Jun 2000 | JP |
| 2003-69282 | Mar 2003 | JP |
| 2006-3909 | Jan 2006 | JP |
| 2009-286082 | Dec 2009 | JP |
| 2010-5999 | Jan 2010 | JP |
| 2011-163903 | Aug 2011 | JP |
| 2013-256104 | Dec 2013 | JP |
| 2013256104 | Dec 2013 | JP |
| 2016-144930 | Aug 2016 | JP |
| 10-2012-0023049 | Mar 2012 | KR |
| 2015050007 | Apr 2015 | WO |
| WO-2015050007 | Apr 2015 | WO |
| Entry |
|---|
| The extended European search report dated Jan. 22, 2020 for corresponding European Application No. 17820201.6. |
| International Search Report for corresponding international application PCT/JP2017/023734 dated Aug. 22, 2017. |
| Office Action issued for corresponding Chinese Patent Application No. 201780038483.6 dated Jul. 1, 2020 (Receipt Date: Jul. 31, 2020), along with an English translation. |
| Office Action issued for corresponding Japanese Patent Application No. 2018-525204 dated Apr. 1, 2021, along with an English machine translation. |
| Office Action issued for corresponding Korean Patent Application No. 10-2018-7037715 dated Sep. 27, 2021, along with an English machine translation. |
| Decision of Refusal dated Oct. 13, 2021, regarding the corresponding Japanese Patent Application No. 2018-525204, together with the English machine translation thereof. |
| Notice of Final Rejection dated Mar. 28, 2022 for corresponding Korean Patent Application No. 10-2018-7037715, along with an English machine translation. |