Patent Application
20190088817
The present invention relates to semiconductors, electronic devices and fabrication thereof. In particular, the present invention relates to altering the electrical and optical properties of semiconductors.
In semiconductor fabrication processes, the electrical properties of a semiconductor material, such as conductivity type, may be changed. Typically, semiconductors can be doped with a donor impurity to change their conductivity to n-type where there is an excess of electrons or doped with an acceptor impurity to change their conductivity to p-type where there is an excess of holes.
A semiconductor is considered a wide bandgap semiconductor when it has an electronic bandgap EG that is significantly larger than three electron volts (i.e., EG≥3 eV). Wide bandgap semiconductors formed from group III metal nitride materials, such as aluminum nitride (AlN) or aluminum-gallium nitride (AlxGa1-xN), are also known as refractory materials due to their high formation temperatures. It is to be understood the term group III metal refers to atoms selected from the boron group of the periodic table of elements. Of particular interest are the group III metal nitride materials, which can be typically doped with a donor impurity specie, such as a group-IV atom specie (e.g. silicon (Si)), to change the conductivity to n-type. Conversely, group III metal nitrides are doped with an acceptor impurity, such as a group-II atom specie (e.g., magnesium (Mg)), to change the conductivity to p-type. Semiconductors formed from group III metal nitride materials are used in the fabrication of electronic devices, such as high power transistors, and optical devices, such as light-emitting diodes (LEDs).
One problem with using group III metal nitride materials in devices, is that in conventional device-fabrication processes, it is difficult to achieve a high level of activated doping density in group III metal nitride materials that have a relatively high aluminum (Al) content, such as AlxGa1-xN, where x is greater than about 0.5. It is further found that electronic grade levels of activated p-type doping (NA≥1018 cm−3) are particularly difficult to obtain in all group III metal nitride semiconductors, which is exacerbated for high Al % films. High Al % films of AlxGa1-xN and AlyIn1-yN for the case of x≥0.6 and y≥0.7, respectively, suffer a transition in the energy ordering of the valence bands in the vicinity of the crystal momentum zone center (i.e., in the vicinity of the direct gap). This further complicates the achievement of high levels of activated holes for electronic and optoelectronic devices.
Co-deposition techniques are typically used to incorporate a selected dopant impurity into a bulk AlxGa1-xN material. However, these techniques often do not achieve the desired activated doping densities. Dopant impurities co-deposited during the epitaxial formation of a bulk group III nitride film tend to either segregate to the surface of the growing film or are not readily incorporated into substitutional metal lattice sites of the group III metal nitride crystal structure. Consequently, the impurity dopants are not optimally incorporated into the host group III metal nitride material. It is found experimentally, in order to achieve sufficient electrically activated dopant concentrations in group III metal nitride films, adding relatively high levels of impurity atom dopants during epitaxial layer formation, is required to compensate for the poor incorporation of the said impurity dopants—typically exceeding the solubility limit. There is yet a further fundamental trade-off in achieving simultaneously the goals of (i) high electrically activated dopant concentrations and (ii) high quality crystal structure films. That is, high incident fluxes of dopant species during co-deposition are required to incorporate at least a portion (typically ˜1-10%) of the available impurity atoms into the growing group III metal nitride film, which comes at the disadvantageous expense of reduced structural quality of the resulting group III metal nitride film.
There is yet a further fundamental limitation of conventional impurity atom doping in wide band gap semiconductors, and particularly for group III metal nitride semiconductors. Even if ideal substitutional doping of a group III metal site within the host crystal is achieved, the activation energy of the donor or acceptor Eact(D,A) is generally large, and thus at room temperature only a small portion of the available excess carriers are activated within the host.
Light emitting devices are typically based on the quantum mechanical recombination of opposite carrier types, namely electrons and holes, within a given spatial region of a fixed bandgap semiconductor material. The optical bandgap defining the said recombination region controls the emitted optical energy of a photon created by the conversion of energy of the electron and hole. The supply of electrons and holes are provided by p-type and n-type reservoirs and typically configured in the layered structure of a PIN diode. The PIN diode comprises a p-type layer (hole reservoir), an intrinsic layer and an n-type layer (electron reservoir). The recombination process occurs substantially within the intrinsic region and is generally formed as a not intentionally doped (NID) semiconductor. By appropriate electrical bias, electrons and holes are simultaneously injected into the intrinsic layer of the PIN diode. It is understood that PN junction diodes can also be used.
Furthermore, when group III metal nitride materials are used in conventional fabrication of ultraviolet (UV) LEDs, the UV LEDs are constructed using multiple layers of dissimilar compositions of selected group III metal nitrides forming so called heterostructures. In heterostructure UV PIN or PN LEDs, a wider bandgap group III metal nitride material is used to form at least one of a p-type region and an n-type region of the LED, and a narrower bandgap group III metal nitride material is used to form an active recombination region of the LED. The wider bandgap region is required so as to provide a low absorption coupling external to the device. That is, the photogenerated light must be able to escape from the internal region of the LED.
One problem with heterostructure UV LEDs, is that at any group III metal nitride heterojunction, for example, the interface between the wider bandgap and narrower bandgap group III metal nitride material, creates extremely large internal polarization fields, (such as spontaneous polarization fields and piezoelectric fields). These internal polarization fields interfere with the distribution and transport of charge carriers, such as electrons and holes, within the active region of the LED, and consequently the recombination of carriers is substantially reduced by the extremely large internal electric polarization fields which tend to inhibit the ideal spatial localization of electron and holes. In fact, the built in electric polarization fields tend to spatially separate the electron and hole wavefunctions in the recombination region. That is, the electronic spatial probability distributions (known by workers in the field as quantum mechanical wavefunctions) of the electrons and holes are not aligned and thus the so-called overlap integral is severely diminished and thus recombination is substantially reduced. The amount of light emitted from the LED is therefore substantially reduced compared to the equivalent case where internal electric polarization fields do not exist.
There is a pressing need to overcome the aforementioned limitation in conventional group III metal nitride light emitting devices. New approaches are needed for providing the desired conductivity type in group III metal nitride semiconductor materials having high Al-content such that the level of the impurity activation is high (i.e., NA,D>1018 cm−3) and new approaches are needed for enhancing light emission efficiency in UV LEDs.
In one form, although it need not be the only or indeed the broadest form, the invention resides in a superlattice. In particular, an engineered layered single crystal structure forming a superlattice. The superlattice provides p-type or n-type conductivity, and comprises alternating host layers and impurity layers, wherein:
Preferably, the semiconductor material is a group III metal nitride semiconductor material.
Suitably, a plurality of the impurity layers are donor impurity layers consisting essentially of a donor material and a plurality of the impurity layers are acceptor impurity layers consisting essentially of an acceptor material.
Suitably, the impurity layers alternate between donor impurity layers and acceptor impurity layers.
In another form, although it need not be the broadest form, the invention resides in an electronic device comprising:
Preferably, the electronic device is an ultraviolet light emitting diode or an ultraviolet light detector.
Suitably, the n-type superlattice and the p-type superlattice form a PN junction.
Suitably, electronic device further comprises an intrinsic region between the n-type superlattice and the p-type superlattice to form a PIN junction.
Suitably, the superlattice forms a layered PIN diode.
Suitably, the intrinsic region consists essentially of one or more group III metal nitride semiconductor materials.
Suitably, the intrinsic region has a bandgap that varies along a growth direction.
Suitably, the intrinsic region comprises at least one of the following: a pure group III metal nitride semiconductor material; a group III metal nitride semiconductor material including at least one crystal structure modifier, wherein the crystal structure modifier is selected from at least one of hydrogen (H), oxygen (O), carbon (C), rare-earth or lanthanide metal; and a not-intentionally doped (NID) group III metal nitride semiconductor material.
Suitably, a period and/or a duty cycle of the p-type superlattice and/or the n-type superlattice is such that the p-type superlattice and/or the n-type superlattice is transparent to a photon emission wavelength or a photon absorption wavelength of the intrinsic region.
Preferably, the electronic device further comprises a buffer region adjacent the n-type superlattice, the buffer region consisting essentially of AlN and/or GaN.
Suitably, the buffer region has a thickness of between about 1 nm to about 1 μm.
Suitably, the buffer region has a thickness of between 10 nm and about 1 μm, or more, preferably between 100 nm and 500 nm.
Suitably, the buffer region comprises a superlattice comprising alternating layers of AlN and GaN with a bulk composition equivalent to the group III metal nitride semiconductor material.
Suitably, the buffer region comprises a ternary bulk alloy composition of at least one of group III metal nitride semiconductor material with composition AlxGa1-xN, 0≤x≤1.
Suitably, the buffer region comprises a group III metal oxide of the form of: (AxB1-x)2O3, where A and B are selected from at least two of Al, In and Ga.
Preferably, the electronic device further comprises a substrate.
Preferably, a material for the substrate is selected from one of: a native group III metal nitride material, such as AlN or GaN, a metal oxide material, such as sapphire, magnesium oxide (MgO) or zinc-oxide (ZnO), silicon (Si), silicon-carbide (SiC), Calcium Fluoride (CaF2), a crystalline thin film semiconductor on amorphous glass, or a thin film crystalline semiconductor on metal.
Suitably, the electronic device comprises a buffer region between the n-type superlattice and the substrate.
Suitably, the electronic device comprises a buffer region between the p-type superlattice and the substrate.
Suitably, electronic device further comprises a p-type contact layer adjacent the p-type superlattice and a p-type contact formed on the p-type contact layer.
Suitably, the p-type contact is substantially reflective to an emission wavelength of the electronic device.
Suitably, the p-type contact comprises one or more windows or openings to enable light to leave the electronic device.
Suitably, the electronic device further comprises an n-type contact formed adjacent the n-type superlattice.
Suitably, the electronic device of further comprises an ohmic contact layer adjacent the substrate.
Suitably, the substrate and the ohmic contact layer comprise one or more windows or openings to enable light to leave the electronic device.
Suitably, the electronic device further comprises a passivation layer adjacent and perpendicular to the p-type superlattice and the n-type superlattice to isolate a conduction path.
Suitably, the passivation layer consists of a wide band gap material having a wider band gap than the group III metal nitride semiconductor material of the host layer.
Suitably, the passivation layer consists essentially of AlxOy, where 0<x≤2 and 0<y≤3.
Suitably, the n-type superlattice and/or the p-type superlattice is tensile strained or compressively strained.
Suitably, the n-type superlattice and/or the p-type superlattice has an electron wavefunction and a hole wavefunction, and peaks of the electron wavefunction are not spatially aligned with peaks of the hole wavefunction.
Suitably, the p-type superlattice and the n-type superlattice each comprise at least 10 host layers and at least 10 donor impurity layers or acceptor impurity layers.
Suitably, a period of the p-type superlattice and/or a period of the n-type superlattice is uniform.
Suitably, a period of the p-type superlattice and/or a period of the n-type superlattice is non-uniform.
Suitably, the host layers comprise non-intentionally doped group III metal nitride semiconductor material.
In another form, although it need not be the broadest form, the invention resides in a method of making a p-type or n-type superlattice via a film formation process, the method comprising the steps of:
Suitably, the desired number of layers is at least 10 host layers and at least 10 impurity layers.
Preferably, the film formation process is a vacuum deposition process, a molecular beam epitaxy process or a vapour phase deposition process.
Suitably, the film formation temperature is between about 200° C. and about 1200° C.
Suitably, the film formation temperature is between about 500° C. and about 850° C.
Suitably, the desired thickness of the superlattice is between about 50 nm and about 5 μm.
Suitably, the reaction chamber is sufficiently deficient of hydrogen (H), oxygen (O) and carbon (C) species so as to not impact the electronic or structural quality of the superlattice.
Suitably, the method comprises growth interruptions for nitrogen terminated surface preparation using excited molecular nitrogen species
Suitably, the host layers and the impurity layers have a predetermined crystal polarity.
Suitably, the predetermined crystal polarity is a substantially metal polar polarity or a nitrogen polarity along a growth direction.
Suitably, the group III metal in the group III metal nitride semiconductor material comprises at least about 50% Al by mol.
Suitably, the semiconductor material or group III metal nitride semiconductor material is selected from at least one of: aluminium nitride (AlN); aluminium gallium nitride (AlxGa1-xN) where 0<x<1; aluminium indium nitride (AlxIn1-xN) where 0<x<1; and aluminium gallium indium nitride (AlxGayIn1-x-yN) where 0<x<1, 0<y<1 and x+y<1.
Suitably, the donor material is selected from at least one of: silicon (Si); germanium (Ge); silicon-germanium (SixGe1-x) where 0<x<1; crystalline silicon-nitride (SixNy) where 0<x<3 and 0<y<4; crystalline germanium-nitride (GexNy) where 0<x<3 and 0<y<4; crystalline silicon-aluminium-gallium-nitride (Siu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0; and crystalline germanium-aluminium-gallium-nitride (Geu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0.
Suitably, the acceptor material is selected from at least one of: magnesium (Mg); zinc (Zn); carbon (C); crystalline magnesium-nitride (MgxNy) where x>0 and y>0; crystalline zinc-nitride (ZnxNy) where x>0 and y>0; magnesium-aluminium-gallium-nitride (Mgu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0; and zinc-aluminium-gallium-nitride (Znu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0.
Suitably, the donor material or the acceptor material comprises one or more of the atomic species in the Lanthanide series of the periodic table of elements.
Suitably, the donor material or the acceptor material comprises a majority of gadolinium (Gd).
Suitably, the donor material or the acceptor material is selected from crystalline lanthanide-nitride composition with formula LxNy, where L is at least one species of Lanthanide atom and N is nitrogen, where 0<x≤3 and 0<y≤2.
Suitably, the donor material or the acceptor material is a Gadolinium-nitride GdxNy, where 0<x≤3 and 0<y≤2.
Preferably, the superlattice comprises at least 10 host layers and at least 10 impurity layers.
Suitably, the host layers have a similar thickness to one another and/or the impurity layers have a similar thickness to one another.
Suitably, subsequent host layers have a substantially different thickness and/or subsequent impurity layers have a substantially different thickness.
Suitably, the host layers each have a thickness of between about 1 nm and about 25 nm.
Suitably, the host layers each have a thickness of at least one half of a monolayer and at most 10 monolayers.
Suitably, the impurity layers each have a thickness of between about 0.25 nm and about 2 nm.
Suitably, the impurity layers each have a thickness of at least one half of a monolayer and less than five monolayers.
Suitably, the impurity layers each have a thickness of at least one monolayer and less than or equal to two monolayers.
Suitably, each donor impurity layer and/or each acceptor impurity layer is a monolayer of atoms of the donor material or the acceptor material.
Suitably, the impurity layers each form a hexagonal crystal mesh and the host layers have a wurtzite crystal structure.
Suitably, the semiconductor material is silicene or graphene.
Suitably, the average spacing between atoms of the donor material or the acceptor material in the plane of the impurity layer is less than 1 nm.
Suitably, the average spacing between atoms of the donor material or the acceptor material in the plane of the impurity layer is about 0.1 nm.
Suitably, subsequent impurity layers are separated by a distance such that the electron and/or hole wavefunctions in the electronic potential wells induced by the atoms of the donor material or acceptor material spatially overlap.
The accompanying figures, where like reference numerals refer to identical or functionally similar elements throughout the separate views, together with the detailed description below, are incorporated in and form part of the specification, and serve to further illustrate embodiments of concepts that include the claimed invention, and explain various principles and advantages of those embodiments.
Skilled artisans will appreciate that elements in the figures are illustrated for simplicity and clarity and have not necessarily been drawn to scale. For example, the dimensions of some of the elements in the figures may be exaggerated relative to other elements to help to improve understanding of embodiments of the present invention.
The superlattice, electronic device and method components have been represented where appropriate by conventional symbols in the drawings, showing only those specific details that are pertinent to understanding the embodiments of the present invention so as not to obscure the disclosure with details that will be readily apparent to those of ordinary skill in the art having the benefit of the description herein.
According to one aspect, the invention resides in a superlattice providing p-type or n-type conductivity. The superlattice comprises alternating host layers and impurity layers. The host layers consist essentially of a semiconductor material, and the impurity layers consist essentially of a corresponding donor or acceptor material. For example, the host layers are formed of a not intentionally doped (NID) semiconductor material and the impurity layers are formed of one or more corresponding donor or acceptor materials. The superlattice can be formed via a film formation process as described further below with reference to
The superlattice can be considered to comprise a plurality of unit cells, each consisting of a host layer and an impurity layer. However, in alternative embodiments, the unit cells can comprise a host layer and two or more impurity layers. The electrical and optical properties of the superlattice can be changed by varying the period and the duty cycle of the unit cells. In preferred embodiments, the superlattice comprises unit cells having uniform periodicity. However, in alternative embodiments, the superlattice comprises unit cells having non-uniform periodicity. For example, the period is varied linearly along the superlattice by varying the thickness of the host layers and/or impurity layers.
The period of the superlattice is defined as the center-to-center spacing between adjacent impurity layers or impurity layers in adjacent unit cells. The duty cycle of each unit cell is defined as the ratio of the thickness of the host layer to the thickness of the impurity layer in the unit cell.
In preferred embodiments, the semiconductor material is a group III metal nitride semiconductor material. Particularly, the semiconductor material is a group III metal nitride semiconductor material wherein the group III metal in the group III metal nitride semiconductor material comprises at least about 50% Al by mol.
The superlattice exhibits several advantages over semiconductor materials doped via conventional methods. The superlattice obviates the need to co-deposit a dopant impurity during formation of the semiconductor material and substantially reduces or entirely eliminates the prior art problem of segregation of dopant impurities to the surface of the semiconductor material during the film formation process. The superlattice can also provide a relatively large excess of free carriers.
Where the host layers consist essentially of a group III metal nitride semiconductor material that has a high Al content, the superlattice achieves a high level of n-type or p-type conductivity and the activated carrier concentration does not significantly decrease with increasing Al content. Hence, the present invention can provide highly activated n-type or p-type conductivity in a group III metal nitride semiconductor with a high Al content.
The superlattice 115 comprises alternately formed host layers 120-n and impurity layers 130-n. As shown in the example in
In the embodiment shown in
With reference to the enlarged section shown in
In preferred embodiments, the host layers 120-n consist essentially of a Group III metal nitride semiconductor material. A Group III metal nitride semiconductor material consists of one or more Group III metals and nitrogen. For example, the semiconductor material can be selected from at least one of: aluminium nitride (AlN); aluminium gallium nitride (AlxGa1-xN) where 0<x<1; aluminium indium nitride (AlxIn1-xN) where 0<x<1; aluminium gallium indium nitride (AlxGayIn1-x-yN) where 0<x<1, 0<y<1 and x+y<1. In preferred embodiments, the one or more Group III metals comprise at least about 50% Al by mol.
In preferred embodiments, the impurity layers 130-n consist essentially of a donor material corresponding to the Group III metal nitride semiconductor material or an acceptor material corresponding to the Group III metal nitride semiconductor material. However, in some alternative embodiments, a plurality of the impurity layers are donor impurity layers consisting essentially of a donor material corresponding to the semiconductor material and a plurality of the impurity layers are acceptor impurity layers consisting essentially of an acceptor material corresponding to the semiconductor material. For example, impurity layers can alternate between donor impurity layers and acceptor impurity layers.
Where the impurity layers 130-n consist essentially of the donor material, the superlattice provides n-type conductivity. For example, the donor material can be selected from at least one of: silicon (Si); germanium (Ge); silicon-germanium (SixGe1-x) where 0<x<1; crystalline silicon-nitride (SixNy) where 0<x<3 and 0<y<4; crystalline germanium-nitride (GexNy) where 0<x<3 and 0<y<4; crystalline silicon-aluminium-gallium-nitride (Siu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0; and crystalline germanium-aluminium-gallium-nitride (Geu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0.
Where the impurity layers 130-n consist essentially of the acceptor material, the superlattice provides p-type conductivity. For example, the acceptor material can be selected from at least one of: magnesium (Mg); zinc (Zn); carbon (C); crystalline magnesium-nitride (MgxNy) where x>0 and y>0; crystalline zinc-nitride (ZnxNy) where x>0 and y>0; magnesium-aluminium-gallium-nitride (Mgu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0; and zinc-aluminium-gallium-nitride (Znu[AlxGa1-y]zNv) where u>0, x>0, 0<y<1, z>0 and v>0.
In some embodiments, the donor material or the acceptor material comprises one or more of the atomic species in the Lanthanide series of the periodic table of elements. For example, the donor material or the acceptor material can comprise a majority of Gadolinium (Gd). The donor material or the acceptor material can also be a crystalline lanthanide-nitride composition with formula LxNy where L is at least one species of Lanthanide atom and N is nitrogen, where 0<x≤3 and 0<y≤2. More preferably, the donor material or the acceptor material is a Gadolinium-nitride (GdxNy), where 0<x≤3 and 0<y≤2.
In some embodiments, the impurity layers 130-n each form a hexagonal crystal mesh and the host layers have a wurtzite crystal structure. In some embodiments, where the host layers have a wurtzite crystal structure the semiconductor material is silicene or graphene.
Each impurity layer 130-n interposed between adjacent host layers 120-n creates a sheet of spatially confined potential wells, which effectively creates a volume of n+-type or p+-type material in the superlattice 115. For example, a first sheet of potential wells is formed in the impurity layer 130-1 interposed between the host layer 120-1 and the host layer 120-2. A second sheet of potential wells is formed in the impurity layer 130-2 interposed between the host layer 120-2 and the host layer 120-3. A third sheet of potential wells is formed in the impurity layer 130-3 interposed between the host layer 120-3 and the host layer 120-4. The position and amplitude of the potential wells can be varied by varying the periodic spacing d1 of the impurity layers 130-n. The periodic spacing d1 is determined, for example, based on the bandgap of the semiconductor material used to form the host layers 120-n.
The periodic spacing d1 of the impurity layers 130-n can be varied by varying the thickness t2 of the host layers and/or the thickness t3 of the impurity layer. In preferred embodiments, the periodic spacing d1 of the impurity layers 130-n is between about 0.1 nm and about 10 nm.
In the embodiment shown in
A wavefunction is a probability amplitude in quantum mechanics that describes the quantum state of a particle and how it behaves. In some embodiments, the periodic spacing d1 of the impurity layers 130-n of the superlattice 115 is such that the electron wavefunctions Ψ in the potential wells induced by the atoms of the donor material or the acceptor material in subsequent impurity layers 130-n spatially overlap. Because the electron wavefunctions Ψ between the impurity layers 130-n overlap, a delocalized “sea” of electrons is formed. For example, if the host layers 120-n are formed of AlN and the periodic spacing d1 of the impurity layers 130-n is about 1 nm to 10 nm this will enable vertical propagation of electrons through the superlattice 115.
In preferred embodiments, the semiconductor material used to form the host layers 120-n is a wide bandgap material, such as AIN which has a bandgap of approximately 6 eV, and the donor or acceptor material used to form the impurity layers 130-n is an ultrathin narrow bandgap material, such as Si. Even though the bulk bandgap of single crystal Si is EG(Si)=1.1 eV, a continuous one monolayer thick Si film disposed across an N-terminated host surface is suitably bonded either side by N bonds and will act as a degenerate doping sheet. The charge deficit of the Si atoms provides a free electron to the crystal. Similarly, a one monolayer Mg sheet incorporated within an AlN host will generate an excess hole. The superlattice leads to higher carrier mobilities along a superlattice growth direction since the carriers are, on the average, more distant from the ionized impurity atom. Therefore, the mobility of the p-type or n-type superlattice is higher than the case of conventional homogeneous but random doping of a host semiconductor. The difference between the electronic bandgaps of the wide bandgap host material and the narrow band gap impurity material coupled with the large difference in electron affinities of each, effectively modulates the positions of the conduction-band and valence-band energies in the superlattice relative to the Fermi energy EFermi.
Donor impurity layers consisting essentially of the donor material effectively modulate the position of the conduction-band energies toward the Fermi energy EFermi and the position of the valence-band energies away from the Fermi energy EFermi. Donor impurity layers provide n+-type conductivity in localized regions by effectively pulling the lowest conduction band edge F below the Fermi energy EFermi. This is described further with reference to
Acceptor impurity layers effectively modulate the positions of the conduction-band energies away from the Fermi energy EFermi and the positions of the valence-band energies toward the Fermi energy EFermi. The acceptor impurity layers provide p+-type conductivity in localized regions by effectively moving the CH-valence-band edge closer to the Fermi energy EFermi. This is described further with reference to
The donor impurity layer induces a potential well, designated A. The energy-band diagram 200 shows the three lowest energy confined and quantized spatial electron wavefunctions ΨCn=1(z) and ΨCn=3(z) plotted relative to the lowest direct conduction band Γ (k=0, z). The energy-band diagram 200 shows that the peak of the ΨCn=1(z) wavefunction is localized to the induced potential well A. The base of the ΨCn=1(z) wavefunction lies below the Fermi energy EFermi in the host layers and peaks above the Fermi energy EFermi in the donor impurity layer forming a highly activated region in the donor impurity layer. This donor impurity layer therefore induces a degenerate electron concentration that extends along the plane of the donor impurity layer. This is to be compared to a single crystal host randomly doped by impurity atoms. In the case of random bulk doping the coupling between isolated impurity atom sites is typically too large to cause impurity wavefunction coupling. The doping density in random bulk doped crystals required to achieve impurity wavefunction coupling is greater than the solubility limit of the impurity within the host semiconductor. Therefore, the present method teaches the beneficial attribute of high effective impurity densities without structural compromise of the host semiconductor.
The energy-band diagram 250 shows the three lowest energy confined and quantized spatial electron wavefunctions ΨCn=1(z), ΨCn=2(z), and ΨCn=3(z) plotted relative to the conduction band Γ (k=0, z). The energy-band diagram 250 shows that the peaks of the electron wavefunctions ΨCn=1(z), ΨCn=2(z), and ΨCn=3(z) are localized to the induced potential wells A, B and C. The base of the ΨCn=1(z) wavefunction lies below the Fermi energy EFermi and forms highly activated regions in the donor impurity and host layers. The lowest lying quantization energies of the electron wavefunctions ΨCn=1(z), ΨCn=2(z), and ΨCn=3(z) all lie below the Fermi energy EFermi generating spatially localized electron states in the region 40<z<60 nm along the growth direction. The triple donor impurity layers, each of 1 nm width, thus form a highly activated and mobile donor concentration. It is understood that the high electron density induced extends in the plane of the layers substantially perpendicular to the growth direction z.
The three acceptor impurity layers induce the potential wells, designated A, B, and C, within each of the three valence bands CH (k=0, z), HH (k=0, z), and LH (k=0, z). The CH (k=0, z) valence band is the highest energy band. In the CH (k=0, z) valence band, the induced potential wells are shifted above the Fermi energy EFermi, providing pt-type conductivity in localized regions of the superlattice at the acceptor impurity layers.
The superlattices and portions of superlattices described above can provide a high level of n-type or p-type conductivity.
The optical and electrical properties of the superlattice can be altered by changing the period and/or the duty cycle of the unit cells. For example, the superlattice can be made transparent to a design wavelength of an electronic device enabling propagation of light from or to the electronic device through the superlattice. Short period and/or small spacings between impurity layers induce a so called type-II band structure wherein the conduction band minimum does not spatially coincide with the valence band maximum. Such superlattices with type-II real space band structure induce indirect energy-momentum dispersion and thus reduce optical absorption near the fundamental superlattice bandgap relative to the isolated bulk semiconductor material of the host layer.
That is, a superlattice can be engineered using the teachings herein to produce a type-II superlattice having a type-II band structure.
Furthermore, a superlattice comprising a high density of impurity species confined substantially to an impurity layer produces a large coupling between impurity atom wavefunctions within the plane of the impurity layer. Increasing the coupling between adjacent impurity atoms or species within the plane of the impurity layer reduces the activation energy Eact (SL) of the impurity compared to the sparse doping case wherein the same impurity species are randomly and sparsely substituted within a single crystal semiconductor host material having activation energy Eact(i:bulk).
This activation energy, lowered by the superlattice method, produces Eact(SL)<Eact(i:bulk), and therefore produces a higher active carrier density for a given operating temperature. This is particularly advantageous for wide band gap host semiconductors, such as in the host layer.
Such an electronic device is described below with reference to
According to another aspect, embodiments of the present invention relate to a method of making a superlattice via a film formation process. In preferred embodiments the superlattice is a p-type or n-type superlattice and made via a substantially two-dimensional thin film formation process. However, the method can also be used to make any of the superlattices described herein (for example superlattices for use in electronic devices having p-type and n-type regions and in some cases an intrinsic region). The film formation process can be, for example, a vacuum deposition process, a molecular beam epitaxy (MBE) process, a vapour phase deposition process, a chemical deposition process, or any other formation process that is capable of precisely forming layers of a given thickness in the range of 0.1 nm to 100 nm.
For example, the film formation process is an MBE process, the group III metal nitride semiconductor material is selected as a wideband gap semiconductor AlN and the donor material is selected as Si. A mechanical shutter is associated with each material source (e.g., Al, N, and Si). Each shutter is positioned in the beam path of the species that is emitted from the material source intersecting the line of sight of the beam between the source and the deposition plane of the substrate. The shutters are used to modulate the outputs of each material source species as a function of time for given calibrated arrival rates of source materials at the said deposition plane. When open, each shutter allows the corresponding species to impinge the deposition surface and participate in epitaxial layer growth. When closed, each shutter prevents the corresponding species from impinging the deposition surface and thus inhibits the respective species from being incorporated within a given film. A shutter-modulation process may be used to readily form atomically abrupt interfaces between the alternately disposed layers of the superlattice. The shutter sequences 150 for such a film formation process are shown in
At step 410, a substrate is prepared to have a surface of desired crystal symmetry and cleanliness devoid of disadvantageous impurities. The substrate is loaded into a reaction chamber, for example an MBE reaction chamber, and then the substrate is heated to a film formation temperature. In some embodiments, the film formation temperature is between about 200° C. and about 1200° C. In some embodiments, the film formation temperature is between about 500° C. and 850° C. In preferred embodiments, the reaction chamber is sufficiently deficient of water, hydrocarbons, hydrogen (H), oxygen (O) and carbon (C) species so as to not impact the electronic or structural quality of the superlattice.
At step 420, a first host layer 120-n consisting essentially of a group III metal nitride semiconductor material is formed via the film formation process on the prepared substrate 110. The host layer 120-n is formed to a thickness t2. For example, if the film formation process is MBE and the group III metal nitride semiconductor material is AlN, the shutters associated with the sources of elemental aluminum and excited molecular nitrogen are opened and a layer of AlN is formed. In this example, the source of elemental aluminum can be a conventional effusion cell and the source of excited molecular nitrogen species can be a plasma source. Other active-nitrogen sources can be used, for example ammonia and activated ammonia via a plasma.
At step 430, the formation of the first host layer 120-n is interrupted and a first impurity layer 130-n consisting essentially of a corresponding donor or acceptor material is formed using the film formation process. The impurity layer 130-n is formed to a thickness t3. In preferred embodiments, a first nitrogen terminated surface is formed on the first host layer prior to forming the first impurity layer and the first impurity layer 130-n is formed on the first nitrogen terminated surface. For example, if the film formation process is MBE, the group III metal nitride semiconductor material is AlN and the donor material is Si, the shutter associated with the aluminum source is closed and a layer of nitrogen species is deposited to form a nitrogen-terminated surface. The shutter associated with the active nitrogen species is then closed, a shutter associated with a source of Si is opened and the first impurity layer is formed atop the entire surface of the first host layer formed in step 420. In one example, the source of Si is an elemental silicon effusion cell comprising a pyrolytic boron nitride (PBN) crucible. In preferred embodiments, donor or acceptor material adatoms are chemisorbed and/or physisorbed on the nitrogen terminated surface and deposition is substantially self-limited by the available nitrogen bonds on the surface. In some embodiments, the surface is supersaturated with the donor or acceptor material and the donor or acceptor material is both physisorbed and chemisorbed. In one example, the deposited impurity layer is a monolayer of Si which ideally forms a reconstructed surface of the same symmetry type as the underlying surface of the host layer. For example, if the host layer is wurtzite AlN, then the impurity layer, being a monolayer of Si, can form a hexagonal mesh referred to herein as Silicene. In another example, one or more Si and N layers, being monolayered atomic planes, can be deposited along a growth direction with a stacking sequence of the form of —N—Si—N—Si— . . . —N.
At step 440, the formation of the first impurity layer 130-n is interrupted and a second host layer 120-n is formed using the film formation process. In preferred embodiments, a second nitrogen terminated surface is formed on the impurity layer prior to forming the second host layer 120-n. For example, if the film formation process is MBE, the group III metal nitride semiconductor material is AlN and the donor material is Si, the shutter associated with the Si source is closed, the shutter associated with the active nitrogen species is opened, and a layer of nitrogen species is deposited to form a nitrogen-terminated surface. The shutter associated with the aluminum source is then opened and the second host layer is formed using the film formation process. The thickness t2 of the host layer 120-n is based, for example, on the periodic spacing d1 between impurity layers 130-n and the thickness t3 of the impurity layers.
At step 450, it is determined whether the superlattice has reached a desired thickness t1. The desired thickness is defined along the growth direction, i.e. perpendicular to the plane of the layers. If the number of unit cells or impurity layers 130-n required to achieve the desired thickness t1 has been achieved, then the method 400 proceeds to step 470. However, if the superlattice has not reached a desired thickness or does not yet comprise a desired number of layers, the method 400 proceeds to step 460. In preferred embodiments, the desired number of layers is at least 10 host layers 120-n and at least 10 impurity layers 130-n and/or the desired thickness is between about 50 nm and about 5 μm. It is understood that a large number of periods can be deposited, such as of the order 100 or 1000.
At step 460, the formation of the second host layer is interrupted and a second impurity layer is formed using the film formation process. For example, if the film formation process is MBE, the group III metal nitride semiconductor material is AlN and the donor material is Si, the shutter associated with the aluminum source is closed and a layer of nitrogen species is deposited to the host layer to form a nitrogen-terminated surface. The shutter associated with the active nitrogen species is then closed, the shutter associated with the source of Si is opened and the second impurity layer is formed atop the entire surface of the host layer previously formed in step 440. The method 400 then returns to step 440.
When the desired thickness or desired number of layers of the superlattice has been achieved, at step 470, the film formation process is suspended and the structure comprising the substrate 110 and the superlattice is removed from the reaction chamber. For example, the material sources are deactivated, the reaction chamber is allowed to cool, and then the structure is removed from the reaction chamber.
In some embodiments, in steps 430 and 460 the impurity layers 130-n are single atomic layers or monolayers of donor or acceptor material. In some embodiments, the impurity layers 130-n are at least one monolayer and less than five monolayers of donor or acceptor material. In some embodiments, the impurity layers are at least one monolayer and less than or equal to two monolayers of donor or acceptor material.
In one example, a single atomic layer of Si or Mg can be formed to provide the superlattice with n-type or p-type conductivity, respectively. In another example, the impurity layers can be an impurity adatom matrix, such as 1 to 5 atomic layers of a single crystalline structure, such as SixNy where x>0 and y>0 or MgpNq p>0 and q>0. In yet another example, the impurity layers are alloys of Siu(AlxGa1-x)yNv or Mgu(AlxGa1-x)yNv, where x≥0, y≥0, u>0 and v≥0.
In some embodiments, the host layers 120-n and the impurity layers 130-n have a predetermined crystal polarity, such as a substantially metal polar polarity or a nitrogen polarity along a growth direction.
In some embodiments, the host layers 120-n and the impurity layers 130-n have a predetermined strain imposed by the impurity layer on to the host layer. For example, the superlattice can be engineered to have the host layers in a state of biaxial compression or biaxial tension relative to the buffer layer and substrate wherein the biaxial compression or biaxial tension is induced by the impurity layers. For example, an n-type superlattice formed using AlN host layers and Si impurity layers provides biaxial compression in the AlN host layer.
According to another aspect, the invention resides in an electronic device comprising an n-type superlattice providing n-type conductivity and a p-type superlattice providing p-type conductivity. For example, the electronic device can be a UV LED or a UV light detector. Particularly, the electronic device can be a UV LED operating in the optical wavelength range between 150 nm to 280 nm, and more preferably in the optical wavelength range between 190 nm to 250 nm.
The n-type superlattice comprises alternating host layers and donor impurity layers. The host layers of the n-type superlattice consist essentially of a group III metal nitride semiconductor material and the donor impurity layers consist essentially of a corresponding donor material. The p-type superlattice comprises alternating host layers and acceptor impurity layers. The host layers of the p-type superlattice consist essentially of the group III metal nitride semiconductor material and the acceptor impurity layers consist essentially of a corresponding acceptor material. The n-type superlattice and p-type superlattice can be the superlattice 115 described above, and the group III metal nitride semiconductor material, the donor material and/or the acceptor material can be the materials described in relation to the superlattice 115.
In some embodiments, the n-type superlattice and the p-type superlattice form a PN junction. In other embodiments, the electronic device further comprises an intrinsic region between the n-type superlattice and the p-type superlattice to form a PIN junction. Here the term “intrinsic region” has been used in line with convention and is not intended to suggest that the intrinsic region is always formed of a near pure semiconductor material. However, in some embodiments the intrinsic region is formed essentially of one or more not intentionally doped or pure semiconductor materials, particularly one or more semiconductor materials of the host layer.
In preferred embodiments, the electronic device can be considered to be a homojunction device because the same group III metal nitride semiconductor material is used throughout most or all of the electrical and optical layers of the electronic device. Because the same group III metal nitride semiconductor material is used throughout most or all of the electrical and optical layers of the electronic device, the refractive index is the same throughout these layers of the electronic device.
In preferred embodiments, a period and/or a duty cycle of the p-type superlattice and/or the n-type superlattice is such that the p-type superlattice and/or the n-type superlattice is transparent to a photon emission wavelength or a photon absorption wavelength of the intrinsic region or a depletion region of a PN junction. This enables light emitted from, or absorbed by the intrinsic region or the depletion region of the PN junction to efficiently enter or leave the device. Ideally, the depletion region is engineered for optimal optical generation probability by efficient recombination of injected electrons and holes from the respective n-type and p-type superlattice regions.
The substrate 510 has a thickness t4, which in preferred embodiments is between about 300 μm and about 1,000 μm. In preferred embodiments, the thickness t4 is chosen in proportion to a diameter of the substrate 510, such that the larger the diameter of the substrate, the larger the thickness t4.
In preferred embodiments, the substrate 510 is substantially transparent to a design wavelength of the electronic device. The design wavelength can be an emission wavelength of the electronic device 500 where the electronic device 500 is a UV LED or can be an absorption wavelength of the electronic device 500 where the electronic device 500 is an UV light detector. In preferred embodiments, the emission wavelength or the absorption wavelength is between 150 nm and 280 nm, and preferably between 190 nm and 250 nm. For example, the substrate 510 can be formed of a material that is substantially transparent to UV light, such as sapphire. In preferred embodiments, the material for the substrate can be selected from one of: a native group III metal nitride material, such as AlN or GaN, a metal oxide material, such as sapphire, magnesium oxide (MgO) or zinc-oxide (ZnO), silicon (Si), silicon-carbide (SiC), Calcium Fluoride (CaF2), a crystalline thin film semiconductor on amorphous glass, or a thin film crystalline semiconductor on metal.
In alternative embodiments, the substrate 510 is substantially non-transparent to the design wavelength of the electronic device 500. For example, the substrate 510 can be formed of a material that is substantially non-transparent to UV light, such as Si. The substrate 510 can be substantially insulating or substantially conductive. For example, the substrate 510 can be formed of Si (111) that has been doped to a high level of conductivity. In some embodiments, an optical access port can be optionally micro-machined or etched to enable efficient optical extraction using a through hole via technology used routinely in commercial CMOS processing.
The buffer region 520 has a thickness t5, which in preferred embodiments is between about 10 nm and about 1 μm and preferably between 100 nm and 500 nm. The buffer region 520 is formed sufficiently thick to have low defect density at a surface adjacent to the n-type superlattice 530. For example, the defect density of the buffer region 520 is about 108 cm−3 or less.
In preferred embodiments, the buffer region 520 consists essentially of AlN and/or GaN, preferably as bulk-like materials. In some embodiments, the buffer region comprises a ternary bulk alloy with composition AlxGa1-xN, 0≤x≤1. In some embodiments, the buffer region comprises a group III metal oxide of the form (AxB1-x)2O3, where A and B are selected from at least two of Al, In and Ga.
In some embodiments, the buffer region 520 comprises a buffer layer formed on a template layer, where the buffer layer consists essentially of the same group III metal nitride semiconductor material as host layers 532 of the n-type superlattice 530 and the p-type superlattice 550 and the template layer consists essentially of AlN.
In alternative embodiments, the buffer region 520 comprises a superlattice, such as a short-period superlattice, formed of alternating layers of AlN and GaN with a bulk composition equivalent to the group III metal nitride semiconductor material of the host layers 532. Such a superlattice structure can be used to further reduce the defect density in the buffer region 520 by introducing lateral strain energy to reduce threading dislocations.
The n-type superlattice 530 comprises alternating host layers 532 and donor impurity layers 534. The host layers 532 consist essentially of a group III metal nitride semiconductor material, for example, Al0.7Ga0.3N. The donor impurity layers 534 consist essentially of a corresponding donor material, for example, Si.
The p-type superlattice 550 comprises alternating host layers 532 and acceptor impurity layers 552. The host layers 532 of the p-type superlattice 550 consist essentially of the same group III metal nitride semiconductor material as the host layers 532 of n-type superlattice 530. The acceptor impurity layers 552 consist essentially of a corresponding acceptor material, for example, Mg.
The n-type superlattice 530 has a thickness t6 and the p-type superlattice 550 has a thickness t7. These thicknesses can be the thickness described above as thickness t1. The thicknesses t6 and t7 can be selected to substantially reduce parasitic absorption of light of the design wavelength of the electronic device 500. For example, Al0.7Ga0.3N has an emission wavelength of 220 nm.
An optical thickness of the n-type superlattice 530 can be determined from the refractive index of the group III metal nitride semiconductor material used to form the n-type superlattice 530. The optical thickness is selected for efficient extraction of light from the electronic device 500.
In some embodiments, the thickness t6 of the n-type superlattice 530 is selected to facilitate formation of an ohmic contact (not shown) on the electronic device 500. In some embodiments, the thickness t6 is at least about 250 nm to facilitate fabricating an ohmic contact using a selective mesa-etching process.
The host layers 532 of the n-type superlattice 530 and the p-type superlattice 550 have a thickness t9 and a thickness t11, respectively. These thicknesses can be the thickness described above as thickness t2. The donor impurity layers 534 have a thickness t10 and the acceptor impurity layers 552 have a thickness t12. These thicknesses can be the thickness described above as thickness t3.
The n-type superlattice 530 has a period d2 and the p-type superlattice 550 has a period d3. In preferred embodiments, period d2 and/or period d3 are based on the design wavelength of the electronic device 500. In the present embodiment, the period d2 and the period d3 are uniform. However, in alternative embodiments, period d2 and/or period d3 can be non-uniform. The periods d2 and d3 can be the period described above as period d1.
The n-type superlattice 530 can be considered to have a plurality of unit cells each consisting of a host layer 532 and a donor impurity layer 534. The p-type superlattice 550 can be considered to have a plurality of unit cells each consisting of a host layer 532 and an acceptor impurity layer 552. The optical properties of the n-type superlattice 530 and the p-type superlattice 550 can be selected by changing the period and/or duty cycle of the unit cells in the superlattice. In the present embodiment, the period d2 and the period d3 are the same. However, in alternative embodiments, period d2 and the period d3 can be different enabling different optical properties to be selected on either side of the intrinsic region 540.
In preferred embodiments, the intrinsic region 540 is the active region of electronic device 500 wherein electrons from the n-type superlattice 530 and holes from the p-type superlattice 550 recombine to emit photons. The intrinsic region 540 has a thickness t8, which in preferred embodiments is less than 500 nm, and is preferably about one half the emitted optical wavelength or an even multiple of the optical wavelength. The thickness t8 of the intrinsic region 540 is selected for efficient recombination of electrons from the n-type superlattice 530 and holes from the p-type superlattice 550.
In preferred embodiments, the intrinsic region 540 consists essentially of one or more group III metal nitride semiconductor materials. For example, the intrinsic region 540 can consist of the group III metal nitride semiconductor material used in the host layers 532 of the n-type superlattice and the p-type superlattice, for example Al0.7Ga0.3N, which has an emission wavelength of 220 nm. In some embodiments, the one or more group III metal nitride semiconductor materials are configured such that the intrinsic region 540 has a bandgap that varies along a growth direction.
For example, the intrinsic region 540 can comprise at least one of the following: a pure group III metal nitride semiconductor material; a group III metal nitride semiconductor material including at least one crystal structure modifier, wherein the crystal structure modifier is selected from at least one of: hydrogen (H), oxygen (O), carbon (C), rare-earth or lanthanide metal; and a not-intentionally doped (NID) group III metal nitride semiconductor material. The crystal structure modifier can produce a predetermined effect of at least one of: improving the material quality, altering the emission wavelength and altering the intrinsic strain state of the intrinsic region relative to the other regions of the superlattice.
In an alternative embodiment, the intrinsic region 540 comprises an impurity layer. The impurity layer consists essentially of: a donor material corresponding to the one or more group III metal nitride semiconductor materials of the intrinsic region; an acceptor material corresponding to the one or more group III metal nitride semiconductor materials of the intrinsic region; a compensated material comprising a donor material and an acceptor material corresponding to the one or more group III metal nitride semiconductor materials of the intrinsic region, such as Si and Mg; or a rare earth metal, such as Gd.
In some embodiments, the intrinsic region comprises an optical recombination superlattice. For example, the intrinsic region 540 can comprise a superlattice comprising a repeating unit cell of the following layers of material [host/Si/host/Gd/host/Mg], where host is a host semiconductor material, such as the group III metal nitride semiconductor material of the host layer.
In some embodiments, the optical recombination superlattice comprises host layers consisting essentially of a host semiconductor material and an impurity layer that is optically active. The impurity layer, for example, consists essentially of a material that is selected from a lanthanide species that is incorporated in a triply ionized state. The Lanthanide species within the optical recombination superlattice thus forms a prepared 4-f shell electronic manifold intrinsic to the Lanthanide atoms incorporated within the optical recombination superlattice. The 4-f electronic manifold of the triply ionized and atomically bonded Lanthanide specie is embedded on an electronic energy scale substantially within the bandgap energy of the host semiconductor material of the optical recombination superlattice.
Electrons and holes are injected into the optical recombination superlattice from the n-type and p-type superlattices, respectively, wherein the electrons and holes recombine transferring energy to the 4-f shell states of the Lanthanide specie in the impurity layer of the optical recombination superlattice and thus excite the said 4-f shell states. Relaxation of the excited 4f-shell states creates intense and sharp optical emission that is transmitted through the entire electronic device by virtue of the n-type and p-type superlattices being optically transparent.
In alternative embodiments, the intrinsic region 540 is omitted from the electronic device 500 shown in
The p-type contact 670 and the n-type contact 680 are formed using known photolithographic processes. The n-type contact 680 is formed via a photolithographic process, wherein a portion of each of the p-type contact 670, the p-type contact layer 660, the p-type superlattice 650, the intrinsic layer 640 and the n-type superlattice 630 are removed in order to expose a defined area on the n-type superlattice 630. A passivation layer 685 is formed to cover exposed edges of the n-type superlattice 630, the intrinsic layer 640, the p-type superlattice 650 and the p-type contact layer 660 to prevent undesired conduction paths from the n-type contact to the buffer region 620, the n-type superlattice 630, the intrinsic layer 640, the p-type superlattice 650 and the p-type contact layer 660. In preferred embodiments, the passivation layer 685 consists of a wide band gap material having a wider band gap than the group III metal nitride semiconductor material of the host layers in the n-type superlattice 630 and the p-type superlattice 650.
In one embodiment, the substrate 610 is a transparent insulating substrate formed of sapphire and the p-type contact layer 660 is formed of highly doped p-type GaN. The thickness of the p-type contact layer 660 is between about 25 nm and about 200 nm in one example, and is about 50 nm in another example. The p-type contact 670 is preferably reflective and electrically conductive. A portion of the p-type contact 670 can be formed using Al for highly optical reflective operation in the 190 nm to 280 nm wavelength region, and a portion of the p-type contact 670 can be formed of a not optically reflective material as an ohmic contact. In preferred embodiments, the n-type contact 680 is formed of titanium nitride (TiN) and/or Aluminium. The passivation layer 685 consists essentially of an aluminium oxide (AlxOy), where 0<x≤2 and 0<y≤3, or another material that is electrically insulating and suppresses surface leakage loss across the device
Light 690 that is emitted from the intrinsic layer 640 exits the LED device 600 vertically through the substrate 610 and also in the lateral direction. Because the p-type contact 670 can be engineered to be reflective, a portion of the light 690 that is emitted from the intrinsic layer 640 in the vertical direction through the p-type superlattice 650 can be reflected and exit the LED device 600 through the substrate 610 as reflected light 695.
The position of the intrinsic layer 640 within the electronic device 500 can be determined based on the design wavelength of the electronic device 500 as described hereinafter with reference to
In this example, the host layers of the p-type superlattice and the n-type superlattice are formed of AlN, the p-type contact layer 660 is formed of undoped GaN, and the p-type contact 670 is reflective and at least a portion of the p-type contact is formed of Al.
The absorption within the intrinsic region of externally applied light incident through the transparent substrate correlates in a reciprocal nature with the emission of light from the intrinsic region out through the substrate. Therefore, the greater the absorption at a wavelength within the intrinsic region, the more efficiently that wavelength of light will be emitted from the intrinsic region of the LED device out through the substrate.
The plot 700 therefore depicts the emission of light from or the absorption of light within the intrinsic region of the electronic device as a function of the vertical position of the intrinsic region and the wavelength of light emitted from the electronic device. The intrinsic layer is the electron-hole recombination (EHR) layer within the LED device. Each of the contour lines defines a degree of light absorption by the intrinsic layer relative to wavelength and position. The values associated with each contour line are in arbitrary units. The greater the value of the contour line, the higher the absorption of light.
Plot 700 shows that light with a wavelength of about 220 nm is minimally absorbed at point A if the intrinsic region is positioned at about 65 nm and maximally absorbed at point B if the intrinsic region is positioned at about 40 nm. Light of a wavelength of 220 nm will therefore be emitted more efficiently from the LED device if the intrinsic region is positioned at 40 nm than if the intrinsic region is positioned at 65 nm. This is a direct consequence of interference effects within a microcavity formed in the device. The microcavity is formed by the n-type and p-type superlattices, the reflective contact and the transparent buffer layer and substrate. The thickness of the buffer plays an important role in the optimal position of EHR region. The calculation presented uses the full real and imaginary optical constants as a function of wavelength for the materials stated. Such a design method improves the optical extraction efficiency of light emitting structures.
The substrate 810 is a non-transparent insulating substrate, consisting essentially of Si and the p-type contact 870 is patterned as a grid having a plurality of openings 872. Light 890 emitted from the intrinsic region 840 is emitted from the device through the openings 872. The light 890 emitted from the intrinsic region 840 also exits the LED device 800 in the lateral direction. “Laterally” or “lateral” refers to the direction substantially along the plane of the layers, while “vertically” or “vertical” refers to the direction substantially perpendicular or normal to the plane of the layers.
In some embodiments, the substrate 810 and the ohmic contact 882 comprise one or more windows or openings to enable light to leave the electronic device.
The energy band diagram 1000 shows a conduction band 1010 as a function of the distance z through the n-type superlattice. The thickness of each donor impurity layer is 1 nm, and the distance between each donor impurity layer is 5 nm. As can be seen in the diagram 1000, the donor impurity layers shift the position of the conduction band 1010 energy toward the Fermi energy EFermi and induce a series of 19 potential wells 1020.
Referring again to both
The energy band diagram 1100 shows a conduction band 1110 as a function of the distance z through the p-type superlattice. The thickness of each acceptor impurity layer is 1 nm, and the distance between each acceptor impurity layer is 5 nm. The acceptor impurity layers shift the position of the conduction band 1110 energy and induce a series of 19 potential wells 1120.
The energy band diagram 1200 shows a conduction band 1210 as a function of the distance z through the p-type superlattice. The thickness of each acceptor impurity layer is 1 nm, and the distance between each acceptor impurity layer is 5 nm. The impurity layers shift the position of the conduction band 1210 energy and induce a series of 19 potential wells 1220.
Referring again to the superlattice of
Similarly, in some embodiments of the devices comprising n-type superlattice and/or the p-type superlattices previously described, the peaks of the electron wavefunction are not spatially aligned with peaks of the hole wavefunction.
The electronic devices described herein have advantages over conventional heterojunction UV LEDs, in that they have improved light emission from the intrinsic layer or active region of the device. For example, the electronic devices of the present invention are homojunction devices and therefore devoid of the internal polarization fields that typically occur in heterojunction devices.
The superlattices can be designed to be transparent to the design wavelength of the electronic device to enable light to be emitted through the n-type or p-type semiconductor region while achieving a high level of n-type or p-type conductivity. Furthermore, the electrical (e.g., carrier concentration) and optical (e.g., optical transparency at the design wavelength) properties of the superlattices can be changed by varying the period and the duty cycle of the unit cells of the superlattice.
It should be appreciated that in the electronic devices shown herein the n-type and p-type superlattices and contacts may be swapped such that the p-type superlattice is grown first. However, a reason for growing the n-type superlattice first is that it is generally easier to grow an n-type superlattice on a substrate or buffer layer than a p-type superlattice.
In this specification, the term “superlattice” refers to a layered structure comprising a plurality of repeating unit cells including two or more layers, where the thickness of the layers in the unit cells is small enough that there is significant wavefunction penetration between corresponding layers of adjacent unit cells such that quantum tunnelling of electrons and/or holes can readily occur.
The reference to any prior art in this specification is not, and should not be taken as, an acknowledgement or any form of suggestion that the prior art forms part of the common general knowledge.
In this specification, the terms “comprise”, “comprises”, “comprising” or similar terms are intended to mean a non-exclusive inclusion, such that a system, method or apparatus that comprises a list of elements does not include those elements solely, but may well include other elements not listed.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2014902009 | May 2014 | AU | national |
| 2014902010 | May 2014 | AU | national |
This application is a continuation of U.S. patent application Ser. No. 15/594,015 filed May 12, 2017 and entitled “Electronic Devices Comprising N-Type and P-Type Superlattices”; which is a divisional of U.S. patent application Ser. No. 14/976,208 filed Dec. 21, 2015 and entitled “Electronic Devices Comprising N-Type and P-Type Superlattices”; which is a continuation of International Patent Application number PCT/IB2015/053179, filed Apr. 30, 2015; which claims priority from Australian Provisional Patent Application number 2014902010 filed on May 27, 2014 and entitled “Electronic Devices Comprising N-type and P-type Superlattices” and Australian Provisional Patent Application number 2014902009 filed on May 27, 2014 and entitled “N-type and P-type Superlattices and Fabrication Thereof” all of which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14976208 | Dec 2015 | US |
| Child | 15594015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15594015 | May 2017 | US |
| Child | 16182097 | US | |
| Parent | PCT/IB15/53179 | Apr 2015 | US |
| Child | 14976208 | US |