Claims
- 1. A method for producing an encapsulated toner for heat-and-pressure fixing, comprising the following steps (a) to (c):
- (a) dissolving a shell-forming resin comprising an amorphous polyester having an acid value of from 3 to 50 KOH mg/g as the main component in a mixture comprising a core material-constituuing monomer and a coloring agent;
- (b) dispersing the mixture obtained in step (a) comprising said amorphous polyester, said core material-constituting monomer, and said coloring agent, in an aqueous dispersant, and localizing said amorphous polyester on the surface of droplets comprising the core material-constituting monomer to give a polymerizable composition; and
- (c) polymerizing said core material-constituting monomer in the polymerizable composition obtained in step (b) to form a core material having a shell comprising the amorphous polyester covering the surface of the core material, thereby forming said encapsulated toner.
- 2. The method according to claim 1, wherein the amount of the amorphous polyester used is 3 to 50 parts by weight, based on 100 parts by weight of the core material.
- 3. A method for producing an encapsulated toner for heat-and-pressure fixing, comprising the following steps (a) to (c):
- (a) dissolving a shell-forming resin comprising an amorphous polyester having tertiary amine groups as the main component in a mixture comprising a core material-constituting monomer and a coloring agent, wherein said amorphous polyester having tertiary amine groups has an acid value of from 1 to 50 KOH mg/g;
- (b) dispersing the mixture obtained in step (a), comprising said amorphous polyester having tertiary amine groups, said core material-constituting monomer, and said coloring agent, in an aqueous dispersant, and localizing said amorphous polyester having tertiary amine groups on the surface of droplets comprising the core material constituting monomer to give a polymerizable composition; and
- (c) polymerizing said core material-constituting monomer in the polymerizable composition obtained in step (b) to form a core material having a shell comprising the amorphous polyester having tertiary amine groups covering the surface of the core material, thereby forming said encapsulated toner.
- 4. The method according to claim 3, wherein said amorphous polyester having tertiary amine groups is present in an amount of 3 to 50 parts by weight, based on 100 parts by weight of said core material.
Priority Claims (3)
Number |
Date |
Country |
Kind |
4-259088 |
Sep 1992 |
JPX |
|
5-77709 |
Mar 1993 |
JPX |
|
5-82611 |
Mar 1993 |
JPX |
|
Parent Case Info
This application is a continuation of application Ser. No. 08/110,965 filed on Aug. 24, 1993, now abandoned.
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
4016099 |
Wellman et al. |
Apr 1977 |
|
4814249 |
Oseto et al. |
Mar 1989 |
|
5035970 |
Hsieh et al. |
Jul 1991 |
|
5153093 |
Sacripante et al. |
Oct 1992 |
|
5264315 |
Tan et al. |
Nov 1993 |
|
Foreign Referenced Citations (13)
Number |
Date |
Country |
0533172 |
Mar 1993 |
EPX |
0536651 |
Apr 1993 |
EPX |
0552785 |
Jul 1993 |
EPX |
59-61843 |
Apr 1984 |
JPX |
63-128360 |
May 1988 |
JPX |
63-128361 |
May 1988 |
JPX |
63-281168 |
Nov 1988 |
JPX |
1-185652 |
Jul 1989 |
JPX |
2162355 |
Jun 1990 |
JPX |
4184358 |
Jul 1992 |
JPX |
4287051 |
Oct 1992 |
JPX |
5197203 |
Aug 1993 |
JPX |
2250103 |
May 1992 |
GBX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
110965 |
Aug 1993 |
|