Patent Application
20130133814
1. Field of the Invention
The present invention relates to a fabrication method of a color-changeable device, particularly to a fabrication method of an electrochromic device.
2. Description of the Related Art
Generally, a conventional electrochromic unit has a laminated structure, and at least one transparent electrode layer is layered on a side surface of the laminated structure. The conventional electrochromic unit generally further includes a couple of glass substrates. If the electrochromic unit is applied to a car-used mirror, one of the glass substrates is able to reflex light. A transparent conductive layer is layered on one side surface of the glass substrates. For example, indium tin oxide (ITO) layer is coating on the side surface. The glass substrates oppositely face to each other and the electrochromic layer is attached therebetween, to form an electrochromic unit. The electrochromic unit is electrically connected to a power source via the ITO layer.
When various driving voltages are respectively applied to the above conventional electrochromic unit, the color of the electrochromic unit will change according to one the corresponding driving voltage. However, the conventional electrochromic unit requires a higher driving voltage, performs with fewer color-levels and worse color contrast. Additionally, after a driving voltage is applied to the electrochromic device and then cut off, the color of the electrochromic device can just maintain for few hours (short-term color-changing memoryeffect). Besides, the electrochromic unit is generally applied to LCD, and thus requiring a higher driving voltage and being unable to maintain the appearance color. Furthermore, the transmittance of the electrochromic device for infrared is considerably high, thus infrared and harmful light cannot be sufficiently isolated.
An object of the present invention present is to provide a fabrication method of an electrochromic device. The light transmittance and appearance color of the electrochromic device can change according to various applied voltages, and infrared and harmful light can be isolated. Additionally, the electrochromic device of the present invention requires a lower driving voltage, performs with a better color contrast and a long-term color-changing memoryeffect.
To achieve this and other objects of the present invention, a fabrication method of an electrochromic device, including the steps of: (a) providing an upper substrate and a lower substrate, the upper substrate including an upper base layer and an upper transparent conductive layer, and the lower substrate including a lower base layer and a lower transparent conductive layer; (b) forming an ion storage layer on a surface of the upper transparent conductive layer and forming an electrochromic layer on a surface of the lower transparent conductive layer; (c) forming an electrolyte layer on a surface of the electrochromic layer; and (d) oppositely facing and combining the ion storage layer and the electrolyte layer.
According to the above-mentioned fabrication method of the electrochromic device, wherein the upper base layer and the lower base layer are made of glass, plastics or metal.
According to the above-mentioned fabrication method of the electrochromic device, wherein the metal is aluminum, chromium, silver or nickel.
According to the above-mentioned fabrication method of the electrochromic device, wherein the upper transparent conductive layer and the lower transparent conductive layer are layers of indium tin oxide (ITO), fluorine doped tin oxide (FTO), aluminum doped tin oxide (AZO) or gallium doped zinc oxide (GZO), nano-carbon material, conductive polymer or metal.
According to the above-mentioned fabrication method of the electrochromic device, wherein the ion storage layer and the electrochromic layer include transition metal oxide, intercalated compound and organic compound.
According to the above-mentioned fabrication method of the electrochromic device, wherein the ion storage layer and the electrochromic layer are formed by sputtering.
According to the above-mentioned fabrication method of the electrochromic device, wherein the transition metal oxide is WO3, NiOX, V2O5 or CuOx, the intercalated compound is Fe4[Fe(CN)6]3, and the organic compound is Poly(aniline) or viologen.
According to the above-mentioned fabrication method of the electrochromic device, wherein the electrolyte layer includes polymer, metal salt and additive.
According to the above-mentioned fabrication method of the electrochromic device, wherein the polymer is polymethyl methacrylate (PMMA), polyvinylidene difluoride (PVDF), polyvinyl chloride (PVC), polyethylene oxide (PEO), polyethylene terephthalate (PET), polyhydroxyethyl methacrylate (PHEMA), polyvinyl butyral (PVB) or ethylene vinyl acetate (EVA), the metal salt is lithium salt, silicate or potassium salt, and the additive is a carbonate-containing material.
According to the above-mentioned fabrication method of the electrochromic device, wherein step (c) includes steps of: coating an electrolyte material on a surface of the electrochromic layer to form a film; and carrying out a first drying process to dry the film to form the electrolyte layer.
According to the above-mentioned fabrication method of the electrochromic device, wherein the coating step is carried out by silkscreen printing, tape casting or roll to roll fabrication.
According to the above-mentioned fabrication method of the electrochromic device, wherein the first drying process sequentially includes three stages of: drying under 55-65° C. for 8-12 minutes, drying under 80-100° C. for 6-15 minutes, and drying under 110-130° C. for 8-12 minutes.
According to the above-mentioned fabrication method of the electrochromic device, wherein the fabrication method further includes a step of flatting the electrolyte layer after the first drying process.
According to the above-mentioned fabrication method of the electrochromic device, wherein the fabrication method further includes a step of disposing an assistant material between corresponding peripheries of the ion storage layer and the electrolyte layer after the first drying process, and a step of slantly gradually combining the ion storage layer and the electrolyte layer.
According to the above-mentioned fabrication method of the electrochromic device, wherein the assistant material is ester-containing solvent.
According to the above-mentioned fabrication method of the electrochromic device, wherein a second drying process is carried out so that the assistant material is melted to incorporate into the electrolyte layer, and the second drying process sequentially includes three stages of: drying under 55-65° C. for 8-12 minutes, drying under 80-100° C. for 6-15 minutes, and drying under 110-130° C. for 8-12 minutes.
According to the above-mentioned fabrication method of the electrochromic device, wherein the assistant material includes a spacer material, the spacer material is polymethyl methacrylate (PMMA) or silicon oxide, and the assistant material and the spacer material are in a weight ratio of 1:[100 to 1000000].
According to the above-mentioned fabrication method of the electrochromic device, wherein the fabrication method further includes a step of coating an UV adhesive on a periphery of the electrolyte layer.
According to the above-mentioned fabrication method of the electrochromic device, wherein the fabrication method further includes further include a step of coating an UV adhesive on peripheries of the stacked upper substrate, lower substrate, ion storage layer and electrolyte layer.
According to the above-mentioned fabrication method of the electrochromic device, wherein the fabrication method further includes a step of solidifying the UV adhesive.
The transmittance of the electrochromic device for visible light is about 15-70%, and the transmittance of the electrochromic device for infrared is lower than 3%. After a voltage is applied on the electrochromic device and then cut off, the color of the electrochromic device can maintain for 1-8 hours, so that infrared and harmful light can be isolated. Additionally, the electrochromic device of the present invention requires a lower driving voltage, performs with a better color contrast and a long-term color-changing memoryeffect.
The light transmittance and appearance color of the electrochromic device can change according to various applied voltages, and infrared and harmful light can be isolated. Additionally, the electrochromic device of the present invention requires a lower driving voltage, performs with a better color contrast and a long-term color-changing memoryeffect.
Other advantages and features of the present invention will be fully understood by reference to the following specification in conjunction with the accompanying drawings, in which like reference signs denote like components of structure.
The advantages and features of the present invention will be fully understood by reference to the following two examples in conjunction with the accompanying drawings.
As shown in
As shown in
The ion storage layer 16 and the electrochromic layer 18 include transition metal oxide, intercalated compound and organic compound. The transition metal oxide is WO3, NiOX, V2O5 or CuOx, the intercalated compound is Fe4[Fe(CN)6]3, and the organic compound is Poly(aniline) or viologen.
When a driving voltage is input the electrochromic device, changes of colors of the materials (transition metal oxide, intercalated compound and organic compound) in the electrochromic layer 18 are listed in the chart below. Reduction state (−) and oxidation state (+) represent the materials in the electrochromic layer 18 before and after their colors change, respectively.
As shown in
In this embodiment, step S13 includes steps of: coating an electrolyte material on a surface of the electrochromic layer 18 to form a film; and carrying out a first drying process to dry the film to form the electrolyte layer 20. The coating step is carried out by silkscreen printing, tape casting or roll to roll fabrication. In this embodiment, the first drying process sequentially includes three stages of: drying under 55-65° C. for 8-12 minutes, drying under 80-100° C. for 6-15 minutes, and drying under 110-130° C. for 8-12 minutes. Preferably, a step of flatting the electrolyte layer 20 is carried out after the first drying process, so as to uniform the uneven surface and periphery of the dried electrolyte layer 20.
As shown in FIGS. 1 and 5-6, in step S14, the ion storage layer 16 and the electrolyte layer 20 oppositely face to each other and are combined together. The ion storage layer 16 and the electrolyte layer 20 may, but not limited to, be combined together by roll-to-roll process.
In this embodiment, after the electrolyte layer 20 is flatted, a step of disposing an assistant material 22 between corresponding peripheries of the ion storage layer 16 and the electrolyte layer 20, and a step of slantly (for example, angled by an angle about 45 degrees) gradually combining the ion storage layer 16 and the electrolyte layer 20 by attaching. It is noted that the ion storage layer 16 and the electrolyte layer 20 may be combined together via face-to-face or other suitable processes. A second drying process is then carried out so that the assistant material 22 melted to incorporate into the electrolyte layer 20, so as to complete the combination of the ion storage layer 16 and the electrolyte layer 20.
The assistant material 22 may be ester-containing solvent or include a spacer material. The spacer material may be polymethyl methacrylate (PMMA) or silicon oxide, and the assistant material and the spacer material are in a weight ratio of 1:[100 to 1000000]. The assistant material 22 can enhance the combination strength of the ion storage layer 16 and the electrolyte layer 20, so as to improve the electron mobility between the ion storage layer 16 and the electrolyte layer 20, and lower the driving voltage of the electrochromic device. In this embodiment, the second drying process sequentially includes three stages: drying under 55-65° C. for 8-12 minutes, drying under 80-100° C. for 6-15 minutes, and drying under 110-130° C. for 8-12 minutes. Preferably, after step S14, a step of coating an UV adhesive on peripheries of the stacked the upper substrate 12, the lower substrate 14, the ion storage layer 16 and the electrolyte layer 20. A step of solidifying the UV adhesive is then carried out to form an UV adhesive frame. In this embodiment, the UV adhesive is solidified via irradiation of an UV light for about 30 seconds, wherein the wavelength of the UV light is about 315 nm. The UV adhesive frame can protect the upper substrate 12, the lower substrate 14, the ion storage layer 16 and the electrolyte layer 20.
It should be noted that the UV adhesive frame may be somewhat varied in an alternative embodiment. For example, before step S14, an UV adhesive is coated on a periphery of the electrolyte layer 20. A step of solidifying the UV adhesive is then carried out to form an UV adhesive frame. The UV adhesive frame can protect the ion storage layer 16 and the electrolyte layer 20 which are relatively important and weak in the electrochromic device.
For various driving voltages to drive the electrochromic device of the present invention, the lower the driving voltage the lighter color of the electrochromic device is; the higher the driving voltage the darker color of the electrochromic device is, The electrochromic device can present about 20 color-levels. The transmittance of the electrochromic device for visible light is about 15-70%, and the transmittance of the electrochromic device for infrared is lower than 3%. After a driving voltage is applied on the electrochromic device and then cut off, the color of the electrochromic device can maintain for 1-8 hours.
In sum, the light transmittance and appearance color of the electrochromic device can change according to various applied voltages, and infrared and harmful light can be isolated. Additionally, the electrochromic device of the present invention requires a lower driving voltage, performs with better color contrast and long-term color-changing memoryeffect.
Although particular embodiments of the invention have been described in detail for purposes of illustration, various modifications and enhancements may be made without departing from the spirit and scope of the invention. Accordingly, the invention is not to be limited except as by the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 100143098 | Nov 2011 | TW | national |