Claims
- 1. A composition consisting essentially of (a) from about 5 to about 55% by weight of at least one copolymer of ethylene with at least one .alpha.-olefin comonomer said comonomer containing from 4 to 10 carbon atoms, the ethylene content of said copolymer being from about 75 to about 98% by weight, the comonomer content of said copolymer being from about 2 to about 25% by weight, and the melt index of said copolymer being from about 0.1 to about 150; (b) from about 2 to about 12% by weight of at least one plasticizer selected from the group consisting of processing oils, epoxidized oils, polyesters, polyethers and polyether esters; and (c) from about 40 to about 90% by weight of filler.
- 2. The composition of claim 1 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 10 to about 35% by weight; (b) said plasticizer is present in an amount of from about 3 to about 10% by weight; and (c) said filler is present in an amount of from about 50 to about 85% by weight.
- 3. The composition of claim 2 wherein the .alpha.-olefin comonomer contains from 4 to 8 carbon atoms, the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 80 to about 96% by weight, the comonomer content is from about 4 to about 20% by weight, and the melt index of said copolymer is from about 0.5 to about 30.
- 4. The composition of claim 3 wherein said filler is selected from the group consisting of calcium carbonate, barium sulfate, hydrated alumina, clay, magnesium carbonate, calcium sulfate, silica, flyash, cement dust, wood flour, ground rice hulls and mixtures thereof.
- 5. The composition of claim 4 wherein said filler is selected from the group consisting of calcium carbonate, barium sulfate, hydrated alumina and mixtures thereof.
- 6. The composition of claim 4 wherein said plasticizer is selected from the group consisting of processing oils.
- 7. The composition of claim 6 wherein said processing oil is selected from the group consisting of naphthenic and paraffinic oils.
- 8. The composition of claim 5 wherein said plasticizer is a mixture of (.alpha.) processing oil and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 9. The composition of claim 8 wherein said processing oil is present in an amount of from about 50 to about 80 percent by weight.
- 10. The composition of claim 4 wherein said plasticizer is selected from the group consisting of polyesters.
- 11. The composition of claim 10 wherein said polyester is a liquid condensation product of (.alpha.) dibasic acid selected from the group consisting of saturated aliphatic dibasic acids and aromatic dibasic acids and (.beta.) polyol selected from the group consisting of aliphatic polyols and polyoxyalkylenepolyols.
- 12. The composition of claim 11 wherein greater than 50 percent by weight of the acid component of said polyester is selected from aliphatic dibasic acids and the polyol component is selected from aliphatic glycols.
- 13. The composition of claim 4 wherein said plasticizer is selected from the group consisting of polyethers.
- 14. The composition of claim 13 wherein said polyether is selected from polyols based on random and block copolymers of ethylene oxides or propylene oxides.
- 15. The composition of claim 4 wherein said plasticizer is selected from the group consisting of polyether esters.
- 16. The composition of claim 15 wherein said polyether ester is selected from esters of polyols based on polymers or copolymers of ethylene oxides or propylene oxides.
- 17. The composition of claim 4 wherein said plasticizer is selected from the group consisting of epoxidized oils.
- 18. The composition of claim 17 wherein said epoxidized oil is selected from the group consisting of epoxidized soybean oil and epoxidized linseed oil.
- 19. The composition of claim 4 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25 percent by weight; (b) said plasticizer is present in an amount of from about 4 to about 8 percent by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80 percent by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85 percent by weight.
- 20. The composition of claim 19 wherein the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94 percent by weight, the comonomoner content is from about 6 to about 16 percent by weight, and the melt index of said copolymer is from about 1 to about 10.
- 21. The composition of claim 20 wherein the comonomer is butene.
- 22. The composition of claim 20 wherein the comonomer is octene.
- 23. A sound deadening sheet prepared from a composition consisting essentially of (a) from about 5 to about 55% by weight of at least one copolymer of ethylene with at least one .alpha.-olefin comonomer said comonomer containing from 4 to 10 carbon atoms, the ethylene content of said copolymer being from about 75 to about 98% by weight, the comonomer content of said copolymer being from about 2 to about 25% by weight, and the melt index of said copolymer being from about 0.1 to about 150; (b) from about 2 to about 12% by weight of at least one plasticizer selected from the group consisting of processing oils, epoxidized oils, polyesters, polyethers and polyether esters; (c) from about 40 to about 90% by weight of filler; and (d) from 0 to about 27% by weight of elastomeric polymer.
- 24. The sound deadening sheet of claim 23 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 10 to about 35% by weight; (b) said plasticizer is present in an amount of from about 3 to about 10% by weight; (c) said filler is present in an amount of from about 50 to about 85% by weight and wherein the .alpha.-olefin comonomer contains from 4 to 8 carbon atoms, the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 80 to about 96% by weight, the comonomer content is from about 4 to about 20% by weight, the melt index of said copolymer is from about 0.5 to about 30 and wherein said filler is selected from the group consisting of calcium carbonate, barium sulfate, hydrated alumina, clay, magnesium carbonate, calcium sulfate, silica, flyash, cement dust, wood flour, ground rice hulls and mixtures thereof.
- 25. The sound deadening sheet of claim 24 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 26. The sound deadening sheet of claim 24 wherein said plasticizer is selected from the group consisting of polyesters and said polyester is a liquid condensation product of (.alpha.) dibasic acid selected from the group consisting of saturated aliphatic dibasic acids and aromatic dibasic acids and (.beta.) polyol selected from the group consisting of aliphatic polyols and polyoxyalkylenepolyols.
- 27. The sound deadening sheet of claim 24 wherein said plasticizer is selected from the group consisting of polyethers.
- 28. The sound deadening sheet of claim 24 wherein said plasticizer is selected from the group consisting of polyether esters.
- 29. The sound deadening sheet of claim 24 wherein said plasticizer is selected from the group consisting of epoxidized oils.
- 30. The sound deadening sheet of claim 24 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight.
- 31. The sound deadening sheet of claim 30 wherein the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is butene.
- 32. The sound deadening sheet of claim 31 wherein the comonomer is octene.
- 33. The sound deadening sheet of claim 24 wherein said elastomeric polymer is present in an amount of from about 1 to about 17% by weight and is selected from the group consisting of styrene-butadiene rubber, polyisobutylene, ethylene/propylene rubber, and terpolymer of ethylene, propylene and a diene monomer.
- 34. The sound deadening sheet of claim 33 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 35. The sound deadening sheet of claim 33 wherein said plasticizer is selected from the group consisting of polyesters, polyethers, polyether esters and epoxidized oils.
- 36. The sound deadening sheet of claim 33 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight and wherein the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is selected from the group consisting of butene and octene.
- 37. The sound deadening sheet of claim 33 wherein said elastomeric polymer is present in an amount of from about 2 to about 12% by weight and is selected from the group consisting of ethylene/propylene rubber and terpolymers of ethylene, propylene and a diene monomer, wherein the ethylene content is from about 20 to about 80% by weight and the diene content is from 0 to about 5% by weight, said dienes being selected from the group consisting of methylene norbornene, ethylidene norbornene, dicyclopentadiene and 1,4-hexadiene.
- 38. The sound deadening sheet of claim 37 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 39. The sound deadening sheet of claim 37 wherein said plasticizer is selected from the group consisting of polyesters, polyethers, polyether esters and epoxidized oils.
- 40. The sound deadening sheet of claim 37 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of fillers is from about 70 to about 85% by weight and wherein the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is selected from the group consisting of butene and octene.
- 41. A carpet having a backside coating prepared from a composition consisting essentially of (a) from about 5 to about 55% by weight of at least one copolymer of ethylene with at least one .alpha.-olefin comonomer said comonomer containing from 4 to 10 carbon atoms, the ethylene content of said copolymer being from about 75 to about 98% by weight, the comonomer content of said copolymer being from about 2 to about 25% by weight, and the melt index of said copolymer being from about 0.1 to about 150; (b) from about 2 to about 12% by weight of at least one plasticizer selected from the group consisting of processing oils, epoxidized oils, polyesters, polyethers and polyether esters; (c) from about 40 to about 90% by weight of filler; and (d) from 0 to about 27% by weight of elastomeric polymer.
- 42. The carpet of claim 41 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 10 to about 35% by weight; (b) said plasticizer is present in an amount of from about 3 to about 10% by weight; (c) said filler is present in an amount of from about 50 to about 85% by weight and wherein the .alpha.-olefin comonomer contains from 4 to 8 carbon atoms, the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 80 to about 96% by weight, the comonomer content is from about 4 to about 20% by weight, the melt index of said copolymer is from about 0.5 to about 30 and wherein said filler is selected from the group consisting of calcium carbonate, barium sulfate, hydrated alumina, clay, magnesium carbonate, calcium sulfate, silica, flyash, cement dust, wood flour, ground rice hulls and mixtures thereof.
- 43. The carpet of claim 42 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 44. The carpet of claim 42 wherein said plasticizer is selected from the group consisting of polyesters and said polyester is a liquid condensation product of (.alpha.) dibasic acid selected from the group consisting of saturated aliphatic dibasic acids and aromatic dibasic acids and (.beta.) polyol selected from the group consisting of aliphatic polyols and polyoxyalkylenepolyols.
- 45. The carpet of claim 42 wherein said plasticizer is selected from the group consisting of polyethers.
- 46. The carpet of claim 42 wherein said plasticizer is selected from the group consisting of polyether esters.
- 47. The carpet of claim 42 wherein said plasticizer is selected from the group consisting of epoxidized oils.
- 48. The carpet of claim 42 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight.
- 49. The carpet of claim 48 wherein the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is butene.
- 50. The carpet of claim 49 wherein the comonomer is octene.
- 51. The carpet of claim 42 wherein said elastomeric polymer is present in an amount of from about 1 to about 17% by weight and is selected from the group consisting of styrenebutadiene rubber, polyisobutylene, ethylene/propylene rubber, and terpolymer of ethylene, propylene and a diene monomer.
- 52. The carpet of claim 51 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 53. The carpet of claim 51 wherein said plasticizer is selected from the group consisting of polyesters, polyethers, polyether esters and epoxidized oils.
- 54. The carpet of claim 51 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight and the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is selected from the group consisting of butene and octene.
- 55. The carpet of claim 51 wherein said elastomeric polymer is present in an amount of from about 2 to about 12% by weight and is selected from the group consisting of ethylene/propylene rubber and terpolymers of ethylene, propylene and a diene monomer, wherein the ethylene content is from about 20 to about 80% by weight and the diene content is from 0 to about 5% by weight, said dienes being selected from the group consisting of methylene norbornene, ethylidene norbornene, dicyclopentadiene and 1,4-hexadiene.
- 56. The carpet of claim 55 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 57. The carpet of claim 55 wherein said plasticizer is selected from the group consisting of polyesters, polyethers, polyether esters and epoxidized oils.
- 58. The carpet of claim 55 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight and the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is selected from the group consisting of butene and octene.
- 59. An automotive carpet having a backside coating prepared from a composition consisting essentially of (a) from about 5 to about 55% by weight of at least one copolymer of ethylene with at least one .alpha.-olefin comonomer said comononer containing from 4 to 10 carbon atoms, the ethylene content of said copolymer being from about 75 to 98% by weight, the comonomer content of said copolymer being from about 2 to about 25% by weight, and the melt index of said copolymer being from about 0.1 to about 150; (b) from about 2 to about 12% by weight of at least one plasticizer selected from the group consisting of processing oils, epoxidized oils, polyesters, polyethers and polyether esters; (c) from about 40 to about 90% by weight of filler; and (d) from 0 to about 27% by weight of elastomeric polymer.
- 60. The automotive carpet of claim 59 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 10 to about 35% by weight; (b) said plasticizer is present in an amount of from about 3 to about 10% by weight; (c) said filler is present in an amount of from about 50 to about 85% by weight and wherein the .alpha.-olefin comonomer contains from 4 to 8 carbon atoms, the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 80 to about 96% by weight, the comonomer content is from about 4 to about 20% by weight, the melt index of said copolymer is from about 0.5 to about 30 and wherein said filler is selected from the group consisting of calcium carbonate, barium sulfate, hydrated alumina, clay, magnesium carbonate, calcium sulfate, silica, flyash, cement dust, wood flour, ground rice hulls and mixtures thereof.
- 61. The automotive carpet of claim 60 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oil and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 62. The automotive carpet of claim 60 wherein said plasticizer is selected from the group consisting of polyesters and said polyester is a liquid condensation product of (.alpha.) dibasic acid selected from the group consisting of saturated aliphatic dibasic acids and aromatic dibasic acids and (.beta.) polyol selected from the group consisting of aliphatic polyols and polyoxyalkylenepolyols.
- 63. The automotive carpet of claim 60 wherein said plasticizer is selected from the group consisting of polyethers.
- 64. The automotive carpet of claim 60 wherein said plasticizer is selected from the group consisting of polyether esters.
- 65. The automotive carpet of claim 60 wherein said plasticizer is selected from the group consisting of epoxidized oils.
- 66. The automotive carpet of claim 60 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight.
- 67. The automotive carpet of claim 66 wherein the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is butene.
- 68. The automotive carpet of claim 67 wherein the comonomer is octene.
- 69. The automotive carpet of claim 60 wherein said elastomeric polymer is present in an amount of from about 1 to about 17% by weight and is selected from the group consisting of styrene-butadiene rubber, polyisobutylene, ethylene/propylene rubber, and terpolymer of ethylene, propylene and a diene monomer.
- 70. The automotive carpet of claim 69 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (2) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 71. The automotive carpet of claim 69 wherein said plasticizer is selected from the group consisting of polyesters, polyethers, polyether esters and epoxidized oils.
- 72. The automotive carpet of claim 69 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight and the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is selected from the group consisting of butene and octene.
- 73. The automotive carpet of claim 69 wherein said elastomeric polymer is present in an amount of from about 2 to about 12% by weight and is selected from the group consisting of ethylene/propylene rubber and terpolymers of ethylene, propylene and a diene monomer, wherein the ethylene content is from about 20 to about 80% by weight and the diene content is from about 0 to about 5% by weight, said dienes being selected from the group consisting of methylene norbornene, ethylidene norbornene, dicyclopentadiene and 1,4-hexadiene.
- 74. The automotive carpet of claim 73 wherein said plasticizer is a mixture of (.alpha.) processing oil selected from the group consisting of naphthenic and paraffinic oils and (.beta.) epoxidized oil or polyester or polyether or polyether ester or any combination thereof, wherein said processing oil is present in an amount of from about 50 to about 95% by weight of said plasticizer.
- 75. The automotive carpet of claim 73 wherein said plasticizer is selected from the group consisting of polyesters, polyethers, polyether esters and epoxidized oils.
- 76. The automotive carpet of claim 73 wherein (a) said ethylene/.alpha.-olefin copolymer is present in an amount of from about 15 to about 25% by weight; (b) said plasticizer is present in an amount of from about 4 to about 8% by weight; and (c) when said filler is calcium carbonate or hydrated alumina the amount of filler is from about 65 to about 80% by weight, and when said filler is barium sulfate the amount of filler is from about 70 to about 85% by weight and the ethylene content of the ethylene/.alpha.-olefin copolymer is from about 84 to about 94% by weight, the comonomer content is from about 6 to about 16% by weight, the melt index of said copolymer is from about 1 to about 10 and wherein the comonomer is selected from the group consisting of butene and octene.
Parent Case Info
This application is a continuation-in-part of my copending application Ser. No. 176,783, filed Aug. 11, 1980, now abandoned.
US Referenced Citations (10)
Foreign Referenced Citations (3)
Number |
Date |
Country |
694890 |
Oct 1967 |
BEX |
2319431 |
Oct 1973 |
DEX |
53-42235 |
Sep 1978 |
JPX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
176783 |
Aug 1980 |
|