9726306
The present invention relates to pipe for conveying fluids and, in particular, to flexible, fiber reinforced pipe. The present invention also relates to a reinforcement tape for use to construct reinforced products.
Flexible pipes are needed for conveying fluids such as water, sour gas, carbon dioxide and hydrocarbons, some of which may be pressurized.
It is desirable that the pipe be flexible enough to be, for example, installed using a plough chute without collapsing or buckling, even in low temperature environments. The pipe should also be capable of containing high pressure flows under conditions of use, such as when buried, unrestrained and bent.
A flexible pipe has been invented for conveying fluids. A reinforcing tape has also been invented.
In accordance with one aspect of the present invention, there is provided a flexible pipe comprising: an inner liner formed as a tube and having an outer surface and an inner surface defining an inner diameter; a reinforcement layer bonded to the inner liner and including at least a first ply of reinforcing tape helically wrapped in a first helical direction about the inner tubular liner and a second ply of reinforcing tape helically wrapped about the first ply of reinforcing tape, the second ply of reinforcing tape helically wrapped in a second helical direction opposite to the first helical direction; and an outer jacket applied over and bonded to the reinforcement layer, the outer jacket formed of a thermoplastic.
In accordance with another aspect of the invention, there is provided a flexible pipe comprising: an inner liner formed as a tube and having an outer surface and an inner surface defining an inner diameter; a reinforcement layer applied about the inner liner and including at least a first ply of fiber reinforcements helically wrapped in a first helical direction about the inner liner and a second ply of fiber reinforcements helically wrapped about the first ply, the second ply helically wrapped in a second helical direction opposite to the first helical direction; and an outer jacket applied over the reinforcement layer, the inner liner, the reinforcement layer and the outer jacket each including a thermoplastic and the inner liner having an outer diameter and a wall thickness and an outer diameter to wall thickness ratio of 30:1 to 50:1.
In accordance with another aspect of the invention, there is provided a reinforcing tape comprising: a plurality of reinforcing fibers and a matrix about the plurality of reinforcing fibers to hold the reinforcing fibers in the form of a tape, the matrix including thermoplastic.
It is to be understood that other aspects of the present invention will become readily apparent to those skilled in the art from the following detailed description, wherein various embodiments of the invention are shown and described by way of illustration. As will be realized, the invention is capable for other and different embodiments and its several details are capable of modification in various other respects, all without departing from the spirit and scope of the present invention. Accordingly the drawings and detailed description are to be regarded as illustrative in nature and not as restrictive.
A further, detailed, description of the invention, briefly described above, will follow by reference to the following drawings of specific embodiments of the invention. These drawings depict only typical embodiments of the invention and are therefore not to be considered limiting of its scope. In the drawings:
The description that follows, and the embodiments described therein, are provided by way of illustration of an example, or examples, of particular embodiments of the principles of various aspects of the present invention. These examples are provided for the purposes of explanation, and not of limitation, of those principles and of the invention in its various aspects. In the description, similar parts are marked throughout the specification and the drawings with the same respective reference numerals. The drawings are not necessarily to scale and in some instances proportions may have been exaggerated in order more clearly to depict certain features.
A flexible pipe has been invented for conveying fluids. The pipe is flexible even when used in freezing temperature conditions such that it can be installed for example using a plough chute. The pipe can contain pressure when buried, unrestrained and bent. The pipe exhibits impact resistance under normal handling.
In one embodiment, a flexible pipe has been invented including: an inner liner having an inner surface and an outer surface; a reinforcement layer including at least a first ply of fiber reinforcements helically wrapped in a first helical direction about the inner tubular liner and a second ply of fiber reinforcements helically wrapped about the first ply, the second ply helically wrapped in a second helical direction opposite to the first helical direction, and an outer jacket applied over the reinforcement layer.
In one embodiment, the inner liner, the reinforcement layer and the outer jacket each contain a thermoplastic. The plys of reinforcements may include reinforcing fibers in a matrix containing thermoplastic and the inner liner and the outer jacket may each include at least one layer of a thermoplastic. The thermoplastic may have one or more of the following characteristics: (i) a softening temperature greater than 100° C., (ii) a brittleness temperature less than −60° C., (ii) a melt temperature of 120 to 300° C., (iii) a tensile strength of 16 to 100 MPa, (iv) an elongation to break of 100 to 1000%, (v) resistance to fatigue cracking when subjected to 1 million cycles at 1% strain, and (vi) a notched IZOD impact strength greater than 30 J/m. In one embodiment, the inner liner, the reinforcement layer and the outer jacket each contain the same type or compatible types of thermoplastic and that thermoplastic has all of the above noted attributes (i) to (vi) and are capable of becoming fused together.
The thermoplastic's low melt temperature offers a mold-ability that allows pipe components to be readily fused to other components, such as during construction or connection of a pipe to another pipe or to a coupling. For example, by forming parts of the same type of thermoplastic, they can be fused together when heated above the melt temperature of that thermoplastic.
The thermoplastic's low brittleness temperature and high elongation provide the pipe with a flexibility suitable for installation by ploughing into the ground.
The thermoplastic resistance to fatigue cracking enables the pipe to achieve fatigue performance of greater than 730,000 pressure cycles from atmospheric to maximum allowable pressure without leaking.
The thermoplastic impact strength allows the pipe to withstand a 125 J impact at −25° C., and retain sufficient strength to satisfy a 20 year maximum operating pressure for the pipe.
The thermoplastic has excellent chemical resistance, which makes the pipe suitable for conveyance of water, CO2, and gaseous and liquid hydrocarbons.
Examples of suitable thermoplastic types include polyamides, polyethylene and polypropylene.
In one embodiment, the plys are handled in the form of a tape.
Referring to
While the pipe may include a reinforcement layer with only two plies of reinforcing tape, the embodiment illustrated in
Pipe 8 may have various diameters such as of 50 to 600 mm (2 to 24 inches) inner diameter, but can even support larger diameters such as of 125 to 600 mm (5 to 24 inches) inner diameter with maximum operating internal pressure ranges from 50 to 500 bar. Generally, the inner diameter is between 125 to 300 mm at this operational pressure range.
While being formable as a large diameter composite pipe, the pipe retains useful properties such as being self supporting and flexible with good pressure containment and impact resistance. Pipe 8 may be formed in discrete lengths or may be formable into longer lengths, as by connecting a plurality of shorter length pipes end to end. The longer lengths may be spoolable for convenient handling.
The pipe may have a fully bonded construction. For example, in one embodiment, the reinforcement layer is fully bonded to inner liner 10 and to outer jacket 20 and each ply of tape in the reinforcement layer is bonded to the plies radially inwardly and radially outwardly of it. The reinforcement layer, therefore, may have a high inter-ply shear strength. Bonding may be achieved by thermoplastic melt fusion, which may include heating the materials to be contacted to a temperature above their melt temperature, bringing the materials into contact, and allowing the materials to cool at which time the contacted materials become fused together. In one embodiment, for example, a “thermoplastic tape placement” method may be employed whereby the thermoplastic tape and the substrate over which the tape is being applied are heated above their melting points. At the zone of contact, the tape is forced onto the substrate, for example, with a compaction roller. As a result of heat and pressure the tape and the substrate are fused together.
Inner liner 10 is tubular having an inner diameter defined by inner surface 12 that is open for the passage of fluids therethrough. The reinforcement layer is applied over outer surface 14 of the liner.
The liner is selected to act as a leak and permeation barrier. The liner should be formed of the most molecularly impervious polymer that meets acceptable material costs, as determined by a cost benefit analysis. Generally, the liner should be selected to minimize diffusion of gaseous components of the fluid being conveyed. As will be appreciated, the liner is selected to be substantially resistant to degradation by the fluid to be passed therethrough.
The liner is as thin as possible. In particular, liner 10 can be as thin as it can be manufactured, thus reducing weight and material cost, and improving the flexibility of the pipe. For example, bearing in mind that the pipe diameter may be relatively large, for example offered in diameters of about 6, 8, 10 or 12 inches, the liner may be less than less than 4 mm thick and may have an outside diameter to wall thickness ratio of 30:1 to 50:1. When the pipe is manufactured, the liner can be supported by an internal steel mandrel and, therefore, the liner is not required to support the loads induced by application of the outer layers such as during the winding process of reinforcing plies and the subsequent application of outer jacket 20.
As noted above, the liner includes a thermoplastic. In one embodiment, the liner includes a main tubular component formed of thermoplastic. Currently, polymers of greatest interest are polyamides, polypropylenes or polyethylenes such as high density polyethylene (HDPE). For petroleum operations, HDPE is particularly useful as it provides good chemical compatibility with many oilfield chemicals at a reasonable cost.
In some embodiments, the liner or a ply thereof is filled, for example, with amorphous clays, chopped glass or carbon fibers. These materials can enhance liner stability, for example, against low temperature cracking, against polymer creep for long term integrity and may enhance the initial strength of the liner following extrusion. The fibers can be aligned or random.
In some embodiments, the liner may be a tubular laminate including a plurality of tubular layers. A multi-layered liner can include, for example, more than one layer of the same material or of different materials. Particular layers may be selected to confer various performance characteristics to the liner. For example, one layer in a multi-layered liner may confer resistance to degradation by the fluid being conveyed, and another layer may confer resistance to permeation of gaseous components of the fluid being conveyed. In one embodiment, for example, to enhance resistance to gas permeation, a barrier layer may be employed. For example, a polymeric barrier layer of material with high permeation resistance to gas may be employed. Examples of permeation resistant materials are polyamides and ethylene vinyl alcohol. Such a material may be positioned adjacent inner surface 12.
While the liner may be formed in various ways, extrusion offers a simple and rapid means of production. A multi-layered liner may be made, for example, by coextrusion of the various layers, as is known in the art.
The reinforcement layer, including the number of plies of reinforcement tape, the nature of the tape and the construction, determines, for the most part, many of the operational parameters of the pipe including, for example, burst strength, pressure holding capability, flexibility, etc. For example, the number of tape plies can be selected to determine the pressure class of the pipe, with fewer plies offering a lower pressure holding pipe.
Generally there are at least two plies of tape in the reinforcing layer of the pipe, the plies of reinforcing tape are configured with one ply wound in a positive or clock-wise helical direction and the other ply wound in a negative or counter-clockwise helical direction. One or more further plies of reinforcing tape may be applied between the inner liner and the outer jacket. Generally, as shown, further plies of reinforcing tape are added in pairs with one of the pair of plies wrapped in a positive helical direction and the other of the pair of plies wrapped in a negative helical direction. In a four ply pipe, as shown for example, plies 16, 18, 22, 24 of reinforcing tape are configured with two plies wound in a positive or clock-wise helical direction and the other two plies wound in a negative or counter-clockwise helical direction. The plies generally alternate in their winding direction from inside to outside. A ply is one or more substantially continuous lengths of tape wound at the same angle and direction onto the underlying liner or tape ply.
The tape employed to form the plies can be configured in various ways from pipe to pipe and from ply to ply. In an embodiment as shown in
The reinforcing tape has a length much greater than its width w and the reinforcing fibers extend along the length of the tape to react loads along the length of the tape regardless of its orientation (i.e. when wrapped circumferentially, the tape reacts circumferential loads resulting from, for example, internal pressure). The fibers should also be resistant to degradation by chemicals, such as hydrocarbons and water, intended to be handled, or environmentally present, during use of the pipe. Suitable fibers include, for example, glass, carbon, nylon, polyester or aramid. For petroleum operations, glass fibers are of greatest interest due to the low cost and ability to carry the required loads. Elongation to failure of fiber glass is generally less than 3.0% and exhibit a filament strength greater than 1,600 MPa. Particularly useful glass fibers may be very straight and have low boron content of typically less than 1% by weight.
The tape includes 30 to 80% reinforcement fiber by weight, with 50 to 70% by weight fiber content being quite useful for embodiments employing glass fiber reinforcements.
The reinforcing tape includes a thermoplastic matrix. As noted above, the thermoplastic is selected to exhibit characteristics that ensure the flexibility and durability of the pipe. For example, the thermoplastic in one embodiment is HDPE. The reinforcing tape may further have a strength optimized by selection of the thermoplastic matrix composition. The tape's impact resistance may also be optimized by selection of the thermoplastic matrix composition.
To enhance the bonding of the matrix to the reinforcing fibers, the matrix may include a coupling agent. The inclusion of a coupling agent has been shown to increase the shear strength and the tensile strength of the tape. The coupling agent also assists the fusion of the reinforcement layer to the jacket and the liner. For example, the matrix of the reinforcing tape may include in excess of 5% by weight content coupling agent, with the most useful range determined to be between 8 and 20% by weight. An example of a suitable coupling agent for use with high density polyethylene is maleic anhydride grafted polyethylene. The inclusion of maleic anhydride grafted polyethylene to HDPE has shown to improve the shear strength and tensile strength of a thermoplastic reinforcement tape by 20% when the coupling agent content was increased from 5% to 18% by weight of the matrix.
The matrix composition tape may include additives to improve the impact resistance of the matrix and, therefore, the tape and the pipe. Specific to HDPE thermoplastic, impact modifier additives of particular interest are rubber, ethylene vinyl acetate (EVA), styrene butadiene styrene (SBS), styrene isoprene styrene (SIS), styrene ethylene butylene styrene (SEBS) and polyethylene such as medium density polyethylene. Such additives may be added in the range of 1 to 40% by weight of thermoplastic. SEBS, for example, may be added in the range of 3 to 13% by weight thermoplastic content. As another example, the medium density polyethylene may be added in the range of 10 to 30% by weight thermoplastic. A useful combination has been determined to be 7 to 10% SEBS and 16 to 18% medium density polyethylene, each by weight in HDPE. When compared to HDPE alone, a matrix containing 8% SEBS and 17% medium density polyethylene in HDPE increased the impact resistance of the matrix composition from 31 to 400 J/m (notched Izod).
An example of a suitable SEBS is Kraton™ G1657, which is a clear, linear triblock copolymer based on styrene and ethylene/butylene with a polystyrene content of about 13%. An example of a suitable medium density polyethylene is Nova™ RMs539U, which has a density of about 0.9 g/cc and in one embodiment has a density of 0.939 g/cc.
The thermoplastic matrix can contain both the coupling agent and the additive for improved impact resistance, as described above.
In one embodiment, the thermoplastic matrix has a high melt index of, for example, 9 to 60. The high melt index ensures adequate impregnation of the matrix into the reinforcing fibers. The tape void content should be no more than 5% and in one embodiment is no more than 3%.
The dimensions of the reinforcing tape may vary, but in one embodiment, they are selected for ease of manufacture. For example, the tape can be relatively thick and wide, for example, having a thickness t between its upper surface 103a and its lower surface 103b in the range 0.6 to 1.5 mm for example, 0.7 to 1.1 mm. The tape can have a width w of 25 to 40% or 30 to 35% of the pipe outer diameter to facilitate tape placement, meaning that for most large diameter embodiments the tape has a width of greater than 45 mm. The large thickness and width of the tape allows the pipe to be efficiently manufactured, for example, using a tape placement method.
The angle of winding of each ply 16, 18 is selected to maximize strength, primarily in the circumferential direction, but also to address axial loads. Winding angles of between about 8° and 86° can be used. In one embodiment, winding angles of between 40° and 70° are used, in one embodiment with winding angles of between 50° and 60°. In one embodiment, the plies of each pair are selected to have substantially equal load carrying capability. For example, the first and second plies can use similar tape, have substantially equal but opposite winding angles and be applied in substantially equal quantities.
Outer jacket 20 surrounds the reinforcement layer including plies 16 and 18, and in this embodiment plies 22 and 24, of tape. While the pipe will function to contain pressurized fluids without the outer jacket, it acts to protect the reinforcement layer from damage, as by cut, abrasion, and impact. In some embodiments, the outer jacket may also operate with a coupling to create a seal or to provide a pipe to pipe connection.
The outer jacket can be formed of any flexible material that can protect the reinforcing fibers to some degree and in this embodiment, capable of fusing to the underlying layer of the pipe. The outer jacket, in some embodiments, may also be selected to operate with the coupling system for pipe to pipe or ending fitting connections. As will be appreciated with consideration as to the intended use of the pipe, outer jacket 20 can be selected to be substantially resistant to degradation by environmental effects (i.e. ultraviolet light, weather, etc.) and by the chemicals that may come in contact with it. In this embodiment, as noted above, the outer jacket includes a thermoplastic and can be filled with reinforcements, if desired. Currently, the thermoplastic of greatest interest is a polyethylene, for example, HDPE.
As desired, the outer jacket can include or have attached thereto identifiers such as, for example, paint, coloration, bar-coding, chips, etc. or materials facilitating use or installation such as, for example, electrically conductive wire or survey locatable metal parts.
Outer jacket 20 may be coated with an insulation, if desired, for thermal insulation of environmental temperature to conduit temperature. Insulation may include polymers, foaming agents, etc.
Jacket 20 may be applied to the pipe in various ways. For example, the jacket materials can be applied as by extrusion, spraying, dipping, tape winding, shrink wrapping, braiding, etc. In one embodiment, the jacket is extruded onto the pipe. In another embodiment, a tape can be employed such as a HDPE tape, for example a neat (i.e. non-reinforced) or a low fiber content reinforced HDPE tape. The tape can be wound about the reinforcement layer using a tape placement method.
Pipe Production
With reference to
The liner can be formed in any desired way, with consideration as to the above noted description of the liner. In a preferred embodiment, the liner is produced by extrusion, providing continuous production thereof and is cut to desired lengths.
Winding can be accomplished by use of a winder that winds one or more lengths of tape in a helical fashion about the liner, as it is being advanced. The tape plys are wound about the liner while the liner is internally supported, if necessary. At least one length of tape is wound about the liner to form a first ply 16, which is in contact with and covers entirely the outer surface of the liner. Second ply 18 of tape is then wound about the first ply 16.
Further plys 22, 24 of reinforcing tape can be wound about second ply 18, as desired, as is shown. The winding direction is alternated with each subsequent ply. In addition, other layers can be applied such as coatings, etc. provided that they do not interfering with the ability of the fiber reinforcements to carry load, or otherwise significantly adversely effect the pipe performance.
Jacket 20 is then applied outwardly of the outer ply 24.
The ends of the pipe have sufficient integrity such that they can remain with the reinforcement layer exposed. Thus, an end cap ring may not be required.
However, if desired, an end cap can be installed on the pipe. For example, with reference to
In one embodiment, cap ring 230 may be formed of a thermoplastic material and may be connected to the pipe end face by fusion to the pipe liner 210, reinforcement layer 215 and jacket 220. Fusing may be achieved using various methods such as, for example, butt fusion. The thermoplastic may be of the same type as that used in the pipe construction. HDPE is an example of a typical material.
The cap ring outer and inner diameters may match those of the pipe. The length of the cap ring is variable, but is typically in the range of 10 to 50 mm in length.
As an alternative to a cap ring, a layer of thermoplastic material may be applied to the exposed end surface between and overlapping the pipe liner and the jacket. The layer of thermoplastic material may be applied in various ways, as by spray deposition, extrusion, dipping, etc. The layer may be relatively thin, for example, having a thickness of 1 to 2 mm.
As noted, to obtain long lengths of pipe, shorter length pipes may be connected end to end. Fittings may be connected to the end of a pipe in order to facilitate the construction of a pipeline. In some embodiments, the outer jacket may operate with a coupling to create a seal or to provide a pipe to pipe or pipe to fitting connections. For example, a coupling may be installed by fusion with the outer coating. In so doing, the outer coating, which includes thermoplastic, is heated to a temperature above the melting temperature of the thermoplastic and the coupling may be installed thereover. In one embodiment, the coupling may include a liner of compatible thermoplastic, which is also heated to at least the melting temperature, such that jacket 20 and the liner of the coupling fuse.
If an end cap is used, the cap ring outside diameter may be sealed to the inside diameter of the coupling, providing a seal from the pipe to the coupling. Where the end cap and the coupling liner contain thermoplastic, fusion may be employed, thereby enabling the formation of a seal between pipe inner liner 210, 230 cap ring and the coupling inner surface.
Pipe Performance
An implementation of a pipe has been constructed and tested. The pipe having a diameter of about 172 mm performed as shown in Table I:
The foregoing is simply an example of a pipe and is not intended to limit the scope of the invention.
It will be apparent that many other changes may be made to the illustrative embodiments, while falling within the scope of the invention and it is intended that all such changes be covered by the claims appended hereto.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2810424 | Swartswelter et al. | Oct 1957 | A |
| 2815043 | Kleiner et al. | Dec 1957 | A |
| 3117597 | Fritz et al. | Jan 1964 | A |
| 3235289 | Jones | Feb 1966 | A |
| 3481369 | Ganahi | Dec 1969 | A |
| 3536104 | Lejeune | Oct 1970 | A |
| 3604461 | Matthews et al. | Sep 1971 | A |
| 3905398 | Johansen et al. | Sep 1975 | A |
| 3948292 | Goto et al. | Apr 1976 | A |
| RE29112 | Carter | Jan 1977 | E |
| 4023835 | Ewing et al. | May 1977 | A |
| 4081302 | Drostholm et al. | Mar 1978 | A |
| 4147381 | Schwarz | Apr 1979 | A |
| 4173670 | VanAuken | Nov 1979 | A |
| 4224505 | Sturm | Sep 1980 | A |
| 4248062 | McLain et al. | Feb 1981 | A |
| 4257630 | Bartell et al. | Mar 1981 | A |
| 4273160 | Lowles | Jun 1981 | A |
| 4299082 | Tarantola | Nov 1981 | A |
| 4343333 | Keister | Aug 1982 | A |
| 4347090 | Anderson et al. | Aug 1982 | A |
| 4384595 | Washkewicz et al. | May 1983 | A |
| 4431034 | Abdullaev et al. | Feb 1984 | A |
| 4437616 | Magarian et al. | Mar 1984 | A |
| 4504086 | Carrow | Mar 1985 | A |
| 4514244 | Shaefer et al. | Apr 1985 | A |
| 4515737 | Karino et al. | May 1985 | A |
| 4601496 | Ulrich et al. | Jul 1986 | A |
| RE32230 | Satoh et al. | Aug 1986 | E |
| 4676276 | Fawley | Jun 1987 | A |
| 4770442 | Sichler | Sep 1988 | A |
| 4818318 | McMahon et al. | Apr 1989 | A |
| 4850395 | Briggs | Jul 1989 | A |
| 4860798 | Kovacs et al. | Aug 1989 | A |
| 4898212 | Searfoss et al. | Feb 1990 | A |
| 4927184 | Bourjot et al. | May 1990 | A |
| 5024252 | Ochsner | Jun 1991 | A |
| 5052444 | Messerly et al. | Oct 1991 | A |
| 5108135 | Mercado | Apr 1992 | A |
| 5125690 | Taylor et al. | Jun 1992 | A |
| 5127116 | Greig | Jul 1992 | A |
| 5163713 | Brettell et al. | Nov 1992 | A |
| 5228186 | Brettell et al. | Jul 1993 | A |
| 5252810 | Trosch et al. | Oct 1993 | A |
| 5261462 | Wolfe et al. | Nov 1993 | A |
| 5268050 | Azari | Dec 1993 | A |
| 5316046 | Igarashi et al. | May 1994 | A |
| 5338920 | Okusaka et al. | Aug 1994 | A |
| 5364130 | Thalmann | Nov 1994 | A |
| 5398974 | Mlzukawa et al. | Mar 1995 | A |
| 5407436 | Toft et al. | Apr 1995 | A |
| 5425981 | Bruning et al. | Jun 1995 | A |
| 5445191 | Green et al. | Aug 1995 | A |
| 5445848 | Venzi et al. | Aug 1995 | A |
| 5618065 | Akiyama | Apr 1997 | A |
| 5629062 | Ejiri et al. | May 1997 | A |
| 5674588 | Porfido et al. | Oct 1997 | A |
| 5788908 | Murakami | Aug 1998 | A |
| 5988689 | Lever | Nov 1999 | A |
| 6039084 | Martucci et al. | Mar 2000 | A |
| 6059319 | Wyke | May 2000 | A |
| 6109306 | Kleinert | Aug 2000 | A |
| 6112771 | Aoyagi et al. | Sep 2000 | A |
| 6164702 | Hauber et al. | Dec 2000 | A |
| 6406063 | Pfeiffer | Jun 2002 | B1 |
| 6478338 | Dalmolen et al. | Nov 2002 | B1 |
| 6497956 | Phillips et al. | Dec 2002 | B1 |
| 6656318 | Sabouraud et al. | Dec 2003 | B1 |
| 6670005 | Kimura et al. | Dec 2003 | B2 |
| 6716503 | Hauber | Apr 2004 | B1 |
| 6773773 | Hauber | Aug 2004 | B2 |
| 6804942 | Bryant | Oct 2004 | B2 |
| 6807988 | Powell et al. | Oct 2004 | B2 |
| 6844040 | Pabedinskas et al. | Jan 2005 | B2 |
| 6889716 | Lundberg et al. | May 2005 | B2 |
| 6893604 | Hauber | May 2005 | B2 |
| 6902205 | Bouey et al. | Jun 2005 | B2 |
| 7063118 | Hauber et al. | Jun 2006 | B2 |
| 7093620 | Dehennau et al. | Aug 2006 | B2 |
| 7166177 | Friedrich et al. | Jan 2007 | B2 |
| 7238400 | Gerez et al. | Jul 2007 | B2 |
| 7293590 | Martin | Nov 2007 | B2 |
| 7600537 | Bhatnagar et al. | Oct 2009 | B2 |
| 7781040 | Coyle | Aug 2010 | B2 |
| 7946629 | Conley et al. | May 2011 | B2 |
| 8042252 | Conley et al. | Oct 2011 | B2 |
| 8398119 | Kenworthy | Mar 2013 | B2 |
| 20020054968 | Hauber | May 2002 | A1 |
| 20020100516 | Powell et al. | Aug 2002 | A1 |
| 20020150752 | Debalme et al. | Oct 2002 | A1 |
| 20030026928 | Bryant | Feb 2003 | A1 |
| 20030039775 | Kong | Feb 2003 | A1 |
| 20030127147 | Van Dam et al. | Jul 2003 | A1 |
| 20030209312 | Hauber | Nov 2003 | A1 |
| 20040089405 | Friedrich et al. | May 2004 | A1 |
| 20040144440 | Bouey et al. | Jul 2004 | A1 |
| 20050143495 | Padareva | Jun 2005 | A1 |
| 20050183785 | Lundberg et al. | Aug 2005 | A1 |
| 20050189029 | Quigley et al. | Sep 2005 | A1 |
| 20050287326 | Schunke et al. | Dec 2005 | A1 |
| 20060127620 | Fisher | Jun 2006 | A1 |
| 20070028983 | Lord et al. | Feb 2007 | A1 |
| 20070062595 | Bhatnagar et al. | Mar 2007 | A1 |
| 20070200342 | Roberts-Moore et al. | Aug 2007 | A1 |
| 20070277895 | Zandiyeh | Dec 2007 | A1 |
| 20080036198 | Roberts-Moore et al. | Feb 2008 | A1 |
| 20080047657 | Jander | Feb 2008 | A1 |
| 20080185042 | Feechan et al. | Aug 2008 | A1 |
| 20080210329 | Quigley et al. | Sep 2008 | A1 |
| 20090011210 | Gao et al. | Jan 2009 | A1 |
| 20090097910 | Cloos et al. | Apr 2009 | A1 |
| 20100218839 | Conley et al. | Sep 2010 | A1 |
| 20100266789 | Conley et al. | Oct 2010 | A1 |
| 20100291342 | Jung et al. | Nov 2010 | A1 |
| 20110260354 | Ramli et al. | Oct 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 2513506 | Aug 2004 | CA |
| 2753024 | Sep 2010 | CA |
| 2268175 | Nov 1997 | CN |
| 0385731 | Sep 1990 | EP |
| 0750973 | Jan 1997 | EP |
| 0969236 | Jan 2000 | EP |
| 0972980 | Jan 2000 | EP |
| 1199447 | Jul 1970 | GB |
| 1263060 | Feb 1972 | GB |
| 1444560 | Aug 1976 | GB |
| 2003207077 | Jul 2003 | JP |
| WO 03086756 | Oct 2003 | WO |
| WO2011053141 | May 2011 | WO |
| Entry |
|---|
| A. G. Gibson, FRC '98, Consolidating New Applications, Seventh International Conference on Reinforced Composites, Conference Proceedings, Apr. 15-17, 1998, University of Houston Libraries. |
| Number | Date | Country | |
|---|---|---|---|
| 20130133775 A1 | May 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61560591 | Nov 2011 | US |