This disclosure relates to nanoparticle compositions that are stable under high salinity and high temperature conditions. This disclosure is also directed to methods of producing these nanoparticle compositions and their use for improved and enhanced oil recovery applications.
Current waterflood operations result in about an average of 50% recovery of original oil in place. In conventional surfactant-based enhanced oil recovery (EOR) applications, tremendous amounts of surfactants are used to mobilize or solubilize oil. This is primarily due to a significant portion of the surfactants injected being adsorbed onto the rock near the wellbore area or diffused into the water-filled small pores. In order to deliver a specific concentration of surfactants to a distant oil location, large concentrations of surfactants need to be injected to account for the surfactants lost by adsorption or diffusion into dead-end pores before reaching the target oil. One way to mitigate the loss of surfactants is to increase the amount of surfactants in water, either by increasing the concentration of a given slug size of surfactants or increasing the slug size of a given concentration of surfactants, to deliver enough surfactants to the oil/water interface. Other approaches use sacrificial chemicals to passivate the rock surface and minimize surfactant adsorption. Overall, the approaches fail to maintain a constant concentration of surfactant over an extended period in the formation. These techniques also increase the cost of current surfactant-enhanced oil recovery techniques.
Embodiments disclosed and described here address the shortcomings in the art such as lack of long term stability of EOR compositions under conditions of high salinity and high temperature. Embodiments include a nanosurfactant-containing composition suitable for injection into a hydrocarbon-bearing formation for enhanced recovery operations. In an embodiment, the EOR composition includes nanoparticles containing a sulfonate surfactant, a zwitterionic co-surfactant, and mineral oil. These nanosurfactants are delivered as aqueous compositions containing cations, such as sodium, calcium, magnesium, and potassium. The sulfonate surfactant and the zwitterionic co-surfactant form nanoparticles having a particle diameter ranging from about 10 nanometers (nm) to 100 nm. The nanoparticles are stable under high salinity and high temperature conditions. In certain embodiments, a substantial portion of the nanoparticles are stable for at least three months at temperatures of at least 100 degrees Celsius (° C.). The sulfonate surfactant can be selected from the group consisting of an alkyl sulfonate, an alkyl aryl sulfonate, and combinations thereof. In certain embodiments, the sulfonate surfactant is petroleum sulfonate. The zwitterionic co-surfactant can contain cocamidopropyl hydroxysultaine.
Embodiments disclosed and described here include methods for recovering hydrocarbons from a hydrocarbon-bearing formation. One such method includes introducing into the hydrocarbon-bearing formation a fluid containing nanoparticles. The nanoparticles are formed by mixing effective amounts of a sulfonate surfactant, a zwitterionic co-surfactant, and mineral oil. The method further includes driving the fluid through the hydrocarbon-bearing formation to displace hydrocarbons from the hydrocarbon-bearing formation; and recovering the displaced hydrocarbons. The sulfonate surfactant and the zwitterionic co-surfactant can form nanoparticles having a particle diameter ranging from about 10 nm to 100 nm. The nanoparticles are stable under high salinity and high temperature conditions. In certain embodiments, a substantial portion of the nanoparticles are stable for at least three months at temperatures of at least 100° C. The sulfonate surfactant can be selected from the group consisting of an alkyl sulfonate, an alkyl aryl sulfonate, and combinations thereof. The sulfonate surfactant can contain petroleum sulfonate. The zwitterionic co-surfactant can contain cocamidopropyl hydroxysultaine.
Embodiments disclosed and described here include methods for producing nanosurfactant-containing fluids suitable for injection into a hydrocarbon-bearing formation for enhanced recovery operations. One such method includes the steps of mixing a first aqueous mixture containing a sulfonate surfactant and a second aqueous mixture containing a zwitterionic co-surfactant in a reactor to form a third aqueous mixture. In the next step, a fourth aqueous mixture containing cations is mixed with the third aqueous mixture in the reactor to produce a fluid containing nanosurfactants with a particle diameter ranging from about 10 nm to 100 nm and containing the sulfonate surfactant and the zwitterionic co-surfactant. In certain embodiments, the first aqueous mixture containing the sulfonate surfactant further contains mineral oil and fresh water. The sulfonate surfactant can be selected from the group consisting of an alkyl sulfonate, an alkyl aryl sulfonate, and combinations thereof. The first aqueous mixture containing the sulfonate surfactant can further contain petroleum sulfonate, mineral oil, and fresh water. In certain embodiments, the second aqueous mixture is produced by mixing the zwitterionic co-surfactant in fresh water. In certain embodiments, the fourth aqueous mixture containing cations is sea water. The zwitterionic co-surfactant can contain cocamidopropyl hydroxysultaine. The petroleum sulfonate in the fluid containing nanosurfactants can range from 0.1 to 0.25 weight percent. The mineral oil in the fluid containing nanosurfactants can range from 0.002 to 0.02 weight percent. The zwitterionic co-surfactant in the fluid containing nanosurfactants can range from 0.1 to 0.2 weight percent.
Another method for producing nanosurfactant-containing fluids includes the steps of mixing a petroleum sulfonate surfactant, mineral oil, and a zwitterionic co-surfactant with fresh water in a reactor; introducing an aqueous salt solution to the reactor; and operating the reactor to produce nanoparticles containing the petroleum sulfonate surfactant, the mineral oil, and the zwitterionic co-surfactant and having a particle diameter ranging from about 10 nm to 100 nm. These nanoparticles are stable under high salinity and high temperature conditions. In certain embodiments, a substantial portion of the nanoparticles are stable for at least three months at temperatures of at least 100° C. The zwitterionic co-surfactant can contain cocamidopropyl hydroxysultaine.
Embodiments of the disclosure provide a method of producing a nanosurfactant composition suitable for injection into a hydrocarbon-bearing formation for enhanced oil recovery operations. The method includes the step of combining a sulfonate surfactant and an oil to form a first mixture. The method includes the step of combining the first mixture, a zwitterionic co-surfactant, and fresh water to form a second mixture. The method includes the step of combining the second mixture, a functionalized zwitterionic copolymer, and the fresh water to form a third mixture. The method includes the step of combining the third mixture and saline water to form the nanosurfactant composition. The saline water includes divalent cations. The nanosurfactant composition includes a nanoassembly. The nanoassembly has a hydrophobic interior and a hydrophilic exterior. The hydrophobic interior includes the sulfonate surfactant, a hydrophobic portion of the zwitterionic co-surfactant, and the oil. The hydrophilic exterior includes a hydrophilic portion of the zwitterionic co-surfactant interacting with the functionalized zwitterionic copolymer present in an aqueous environment. The hydrophilic portion of the zwitterionic co-surfactant stabilizes the nanoassembly by interacting with the divalent cations present in the saline water. The oil facilitates containment of the sulfonate surfactant in the hydrophobic interior of the nanoassembly.
In some embodiments, the nanoassembly has a diameter ranging between 10 nm and 100 nm. In some embodiments, the sulfonate surfactant is petroleum sulfonate. In some embodiments, the petroleum sulfonate includes an alkyl sulfonate, an alkyl aryl sulfonate, and combinations of the same. In some embodiments, the nanosurfactant composition has a sulfonate surfactant content ranging between 0.1 wt. % and 0.25 wt. %. In some embodiments, the zwitterionic co-surfactant is cocamidopropyl hydroxysultaine. In some embodiments, the nanosurfactant composition has a zwitterionic co-surfactant content ranging between 0.1 wt. % and 0.25 wt. %. In some embodiments, the functionalized zwitterionic copolymer has a first monomeric unit including a zwitterionic functional group. In some embodiments, the first monomeric unit includes 1-vinylimidazole. In some embodiments, the 1-vinylimidazole is functionalized with an alkyl sulfonate at an N3 position of the 1-vinylimidazole. In some embodiments, the functionalized zwitterionic copolymer has a second monomeric unit comprising a hydrophobic functional group. In some embodiments, the second monomeric unit includes styrene. In some embodiments, the second monomeric unit includes 4-methylstyrene. In some embodiments, the second monomeric unit includes 4-(trifluoromethyl)styrene. In some embodiments, the functionalized zwitterionic copolymer has the formula:
wherein n, x, and y are positive integers. In some embodiments, the oil is mineral oil. In some embodiments, the nanosurfactant composition has an oil content ranging between 0.002 wt. % and 0.02 wt. %. In some embodiments, the fresh water has a total dissolved solids concentration less than 3,000 ppm. In some embodiments, the saline water has a total dissolved solids concentration greater than 10,000 ppm.
Embodiments of the disclosure also provide a nanosurfactant composition suitable for injection into a hydrocarbon-bearing formation for enhanced oil recovery operations. The nanosurfactant composition includes a nanoassembly and an aqueous environment. The nanoassembly includes a hydrophobic interior and a hydrophilic exterior. The hydrophobic interior includes petroleum sulfonate, a hydrophobic portion of a zwitterionic co-surfactant, and mineral oil. The hydrophilic exterior includes a hydrophilic portion of the zwitterionic co-surfactant. The aqueous environment includes a functionalized zwitterionic copolymer and divalent cations. The hydrophilic portion of the zwitterionic co-surfactant is configured to interact with the functionalized zwitterionic copolymer present in the aqueous environment. The hydrophilic portion of the zwitterionic co-surfactant is configured to stabilize the nanoassembly by interacting with the divalent cations present in the aqueous environment. The mineral oil is configured to facilitate containment of the petroleum sulfonate in the hydrophobic interior of the nanoassembly.
In some embodiments, the nanoassembly has a diameter ranging between 10 nm and 100 nm. In some embodiments, the zwitterionic co-surfactant is cocamidopropyl hydroxysultaine. In some embodiments, the functionalized zwitterionic copolymer has a first monomeric unit including a zwitterionic functional group. In some embodiments, the first monomeric unit includes 1-vinylimidazole. In some embodiments, the 1-vinylimidazole is functionalized with an alkyl sulfonate at an N3 position of the 1-vinylimidazole. In some embodiments, the functionalized zwitterionic copolymer has a second monomeric unit including a hydrophobic functional group. In some embodiments, the second monomeric unit includes styrene. In some embodiments, the second monomeric unit includes 4-methylstyrene. In some embodiments, the second monomeric unit includes 4-(trifluoromethyl)styrene. In some embodiments, the functionalized zwitterionic copolymer has the formula:
wherein n, x, and y are positive integers.
Embodiments of the disclosure also provide a method for recovering hydrocarbons from a hydrocarbon-bearing formation. The method includes the step of introducing into the hydrocarbon-bearing formation a nanosurfactant composition. The nanosurfactant composition is formed by the step of combining a sulfonate surfactant and an oil to form a first mixture. The nanosurfactant composition is formed by the step of combining the first mixture, a zwitterionic co-surfactant, and fresh water to form a second mixture. The nanosurfactant composition is formed by the step of combining the second mixture, a functionalized zwitterionic copolymer, and the fresh water to form a third mixture. The nanosurfactant composition is formed by the step of combining the third mixture and saline water to form the nanosurfactant composition. The saline water includes divalent cations. The nanosurfactant composition includes a nanoassembly. The nanoassembly has a hydrophobic interior and a hydrophilic exterior. The hydrophobic interior includes the sulfonate surfactant, a hydrophobic portion of the zwitterionic co-surfactant, and the oil. The hydrophilic exterior includes a hydrophilic portion of the zwitterionic co-surfactant interacting with the functionalized zwitterionic copolymer present in an aqueous environment. The hydrophilic portion of the zwitterionic co-surfactant stabilizes the nanoassembly by interacting with the divalent cations present in the saline water. The oil facilitates containment of the sulfonate surfactant in the hydrophobic interior of the nanoassembly. The method includes the step of driving the nanosurfactant composition through the hydrocarbon-bearing formation to displace the hydrocarbons from the hydrocarbon-bearing formation. The nanoassembly reduces interfacial tension between the hydrocarbons and the saline water.
In some embodiments, the functionalized zwitterionic copolymer present in the aqueous environment screens a charged surface of the hydrophilic exterior of the nanoassembly from ions present on a surface of a carbonate-based rock present in the hydrocarbon-bearing formation. In some embodiments, the sulfonate surfactant is petroleum sulfonate. In some embodiments, the zwitterionic co-surfactant is cocamidopropyl hydroxysultaine. In some embodiments, the oil is mineral oil. In some embodiments, the functionalized zwitterionic copolymer has a first monomeric unit including a zwitterionic functional group. In some embodiments, the first monomeric unit includes 1-vinylimidazole. In some embodiments, the 1-vinylimidazole is functionalized with an alkyl sulfonate at an N3 position of the 1-vinylimidazole. In some embodiments, the functionalized zwitterionic copolymer has a second monomeric unit including a hydrophobic functional group. In some embodiments, the second monomeric unit includes styrene. In some embodiments, the second monomeric unit includes 4-methylstyrene. In some embodiments, the second monomeric unit includes 4-(trifluoromethyl)styrene. In some embodiments, the functionalized zwitterionic copolymer has the formula:
wherein n, x, and y are positive integers.
Embodiments of the disclosure also provide a method of providing a nanosurfactant composition suitable for injection into a hydrocarbon-bearing formation for enhanced oil recovery operations. The method includes the step of combining a sulfonate surfactant, an oil, and fresh water to form a first mixture. The method includes the step of combining a zwitterionic co-surfactant and the fresh water to form a second mixture. The method includes the step of combining a functionalized zwitterionic copolymer and the fresh water to form a third mixture. The method includes the step of combining the first mixture, the second mixture, and the third mixture to form a fourth mixture. The method includes the step of combining the fourth mixture and saline water to form the nanosurfactant composition. The saline water includes divalent cations. The nanosurfactant composition includes a nanoassembly. The nanoassembly has a hydrophobic interior and a hydrophilic exterior. The hydrophobic interior includes the sulfonate surfactant, a hydrophobic portion of the zwitterionic co-surfactant, and the oil. The hydrophilic exterior includes a hydrophilic portion of the zwitterionic co-surfactant interacting with the functionalized zwitterionic copolymer present in an aqueous environment. The hydrophilic portion of the zwitterionic co-surfactant stabilizes the nanoassembly by interacting with the divalent cations present in the saline water. The oil facilitates containment of the sulfonate surfactant in the hydrophobic interior of the nanoassembly.
Embodiments will be readily understood by the following detailed description in conjunction with the accompanying drawings. Embodiments are illustrated by way of example and not by way of limitation in the figures of the accompanying drawings.
Embodiments of this disclosure describe nanoparticle compositions that are stable under high salinity and high temperature conditions. More specifically, these compositions include petroleum sulfonate-based nanoparticles that are used for improved and enhanced oil recovery applications.
In the following description, numerous specific details are set forth in order to provide a thorough understanding of the various embodiments and reference is made to the accompanying drawings that form a part hereof. In other instances, well-known processes and methods may not be described in particular detail to refrain from unnecessarily obscuring the embodiments described here. Additionally, illustrations of embodiments here may omit certain features and/or details in order to not obscure the embodiments described here. Other embodiments may be utilized, and logical changes may be made without departing from the scope of the disclosure. Therefore, the following detailed description is not to be taken in a limiting sense.
The description may use the phrases “in certain embodiments,” “in an embodiment,” or “in embodiments,” which may each refer to one or more of the same or different embodiments. Furthermore, the terms “comprising,” “including,” “having,” and the like, as used with respect to embodiments of the present disclosure, are synonymous. As used here, the term “effective amount” refers to at least that amount of nanosurfactant or nanosurfactant components necessary to bring about a desired result, such as, for example, enhanced oil recovery or improved stability at high temperatures or improved stability for longer periods of time and at relatively high temperatures. The term salinity refers to the amount of total dissolved solids (TDS) in the water and is measured in parts per million (ppm). Water with a TDS concentration less than 3,000 ppm is considered fresh water. Water with a TDS concentration in excess of 10,000 ppm is considered saline. The term “high salinity conditions” refers to fluid conditions where the TDS concentration ranges from 30,000 ppm to 220,000 ppm. In certain embodiments, high salinity conditions include fluid conditions with the TDS concentration ranging from 60,000 ppm to 150,000 ppm. The term “high temperature conditions” refers to fluid or reservoir conditions where the temperature ranges from 75° C. to 150° C. In certain embodiments, high temperature conditions include fluid or reservoir conditions with the temperature ranging from 100° C. to 120° C.
Embodiments include nanosurfactant formulations and use of these formulations with long-term stability at high salinity and high temperature conditions. Nanosurfactants described here are nanoparticle compositions containing a sulfonate surfactant, a zwitterionic co-surfactant, and an oil. The nanosurfactants enable more economical oil recovery as compared to conventional surfactants by reducing the amount of surfactants lost by adsorption onto the rock surfaces. These compositions deliver surfactants more efficiently to the oil-water interfaces. Embodiments include aqueous suspensions of petroleum sulfonate-based nanoparticles with long-term stability at high salinity and high temperature conditions. These formulations contain small amounts of a class of zwitterionic co-surfactants (a surfactant with both anionic and cationic centers in the same molecule) that have no easily hydrolysable chemical bonds. These formulations are compatible with salty and hard water, in particular tolerant to high concentrations of sodium chloride and divalent cations. An example of a commercially-available zwitterionic surfactants used in these formulations is cocamidopropyl hydroxysultaine or betaine surfactants, such as SURFATEX CBS™, obtained from Surfactants International, LLC, headquartered in Allendale, N.J., USA; PETROSTEP® SB, PETROSTEP® CG-50, and Amphosol® CG-50 from Stepan, headquartered in Northfield, Ill., USA; and ColaTeric CBS-HP from Colonial Chemical Inc., headquartered in South Pittsburgh, Tenn. These formulations offer several advantages, such as colloidal and chemical stability at high salinity and high temperature for several months, substantial reduction of crude oil/seawater interfacial tension, ability to form an emulsion very rapidly upon contact with crude oil without any mechanical mixing. As demonstrated by experimental data from a lab-scale coreflooding setting, these formulations show appreciable increase in oil recovery beyond seawater flooding.
The formulations described here include sulfonates, mineral oil, and a class of co-surfactants that have no easily hydrolysable chemical bonds. For example, a nanosurfactant mixture was formulated using zwitterionic co-surfactants with petroleum sulfonate surfactants in the presence of mineral oil. The term “petroleum sulfonate” refers to a mixture containing sulfonated benzenoids (both alkyl aryl and aryl), and cycloaliphatic and paraffinic (alkyl) hydrocarbons in various ratios to one another depending on the nature of the source of the petroleum fraction. Petroleum sulfonates can include alkyl xylene sulfonates, alkyl aryl sulfonates, alpha-olefin sulfonates, and combinations thereof. An example of a commercially-available product that contains petroleum sulfonate is PETRONATE® EOR-2095 sodium sulfonate (EOR-2095) from Chemtura Corporation (headquartered in Philadelphia, Pa., USA) or PETRONATE® sodium sulfonates from Sonneborn LLC (headquartered in Parsippany, N.J., USA). Petroleum sulfonates are not stable by themselves in sea water. But, the formulation of zwitterionic co-surfactants with petroleum sulfonate surfactants in the presence of mineral oil was successfully operative in long-term stability tests in seawater and low salinity Arab-D water at 100° C. Seawater used in the experiments disclosed here has a TDS concentration of about 60,000 ppm. Low salinity Arab-D water has a TDS concentration of about 120,000 ppm. Certain alcohol ether sulfonates are not suitable for embodiments disclosed here as alcohol ether sulfonates do not combine with the zwitterionic co-surfactants to form the nanoparticles for cross well applications. Additional hydroxyl groups presented by the alcohol ether sulfonates increase material losses as they bind to calcium. In EOR fluids with seawater, the alcohol ether sulfonates bind preferentially to the carbonate rock instead of remaining available in the EOR fluid.
Embodiments disclosed here include compositions suitable for injection into a hydrocarbon-bearing formation for enhanced recovery operations. One such composition includes a sulfonate surfactant, a zwitterionic co-surfactant, and mineral oil.
In certain embodiments, the effective amounts of each of the sulfonate surfactant and the zwitterionic co-surfactant range from 0.1 to 0.9 wt % of the nanosurfactant mixture. In certain embodiments, the effective amounts of each of the sulfonate surfactant and the zwitterionic co-surfactant range from 0.1 to 0.5 wt % of the nanosurfactant mixture. In certain embodiments, the total amount of the sulfonate surfactant and the zwitterionic co-surfactant ranges from 0.2 to 1 wt % of the nanosurfactant mixture. In certain embodiments, the amount of mineral oil ranges from 0.002 wt %-0.02 wt % of the nanosurfactant mixture. In certain embodiments, the amount of mineral oil ranges from 0.002 wt %-0.01 wt % of the nanosurfactant mixture. In certain embodiments, the amount of mineral oil is approximately 0.005 wt % of the nanosurfactant mixture.
The wt % ratio of sulfonate/zwitterionic surfactants can range from 0.3 to 3. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.3 to 2.5. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.3 to 2.0. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.3 to 1.5. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.3 to 1.0. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.5 to 1.5. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.5 to 1. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.5 to 0.8. In certain embodiments, the wt % ratio of sulfonates/zwitterionic surfactants can range from 0.75 to 0.80.
Embodiments disclosed here include methods for recovering hydrocarbons from a hydrocarbon-bearing formation. One such method includes introducing into the hydrocarbon-bearing formation a fluid containing effective amounts of a sulfonate surfactant, a zwitterionic co-surfactant, and mineral oil; driving the fluid through the hydrocarbon-bearing formation to displace hydrocarbons from the hydrocarbon-bearing formation; and recovering the displaced hydrocarbons. The sulfonate surfactant and the zwitterionic co-surfactant can form nanoparticles having a particle diameter ranging from about 10 nm to 100 nm. In certain embodiments, the petroleum sulfonate-based nanoparticles in seawater-based formulations have particle diameters ranging from about 10 nm to 60 nm.
In an embodiment, a zwitterionic co-surfactant, such as cocamidopropyl hydroxysultaine, a petroleum sulfonate surfactant, such as sodium alkylbenzene sulfonates, and seawater were combined to form a colloidally and chemically stable formulation. Certain embodiments of these nanosurfactant formulations were colloidally and chemically stable for more than six months at 100° C. Stability refers to the ability of the particles to remain as part of the nanosurfactant composition without aggregating or displaying reduced sticking to the rock surfaces. Stability does not refer to the stability of the individual components. In certain embodiments, the seawater-crude oil IFT was reduced by two to three orders of magnitude. Certain embodiments showed reduced interfacial tension measured in milliNewtons per meter (mN/m) with crude oil at 90° C. and rapid formation of an emulsion at 100° C. without any mechanical mixing. Furthermore, in certain embodiments, the size of the formed nanoparticles was small (less than 50 nm) in comparison to pore diameters typically encountered in petroleum-bearing carbonate formations. The size of the nanoparticles was small and decreased to about 15 nm after increasing the temperature from 25° C. to 90° C. The size remained unchanged when the suspension is cooled back to 25° C. This indicates the enhanced stability of the formulation under oil reservoir conditions, and even when different temperatures are encountered in the reservoir.
When the surfactant molecules are formulated into nano-sized particles, the loss of surfactants is mitigated and the delivery of surfactants to the oil phase is enhanced. As illustrated in
When delivered as part of the nanoparticle composition, the surfactant is released in the presence of oil, otherwise it remains intact within the water phase. This approach is efficient and economical in delivering surfactants in targeted oil recovery applications. The nanoparticles are small enough to travel through the reservoir without straining. The sorption of these particles onto the rock matrix is not significant, and they are stable for periods of time exceeding their travel time to the oil-water interface. Flow of these aqueous nanoparticle compositions through the reservoir is different from the flow of foam compositions. These aqueous nanoparticle compositions easily permeate into low permeability zones, while the foam compositions do not have similar capability. Moreover, these aqueous nanoparticle compositions do not block the high permeability zones of a reservoir.
Previous surfactant formulations showed stability of about three to four days, and were thus deemed unsuitable for enhanced oil recovery applications. These prior surfactant formulations revealed instability and phase separation in the concentrated and seawater-diluted nanosurfactant suspensions even at room temperature (23-27° C.). Transmission electron microscopy (TEM) imaging indicated that the formed particles were present both as individual particles as well as linear (chain-like) aggregates up to 200 nm long. Both concentrated and seawater-diluted suspensions became more unstable at elevated temperatures (˜100° C.). Phase separation and aggregation were apparent after less than three days of exposure to 100° C. Noticeable precipitation was observed at greater seawater dilutions while separation of the oily petroleum sulfonate salts was apparent at lower dilutions. Samples with a median dilution showed a crossover between petroleum sulfonate separation and precipitation. Results also implied noticeable sorption of nanosurfactant components onto crushed rock grains at elevated temperatures and the formation of a significant number of aggregates in the supernatant after sorption.
Embodiments formulated using petroleum sulfonate surfactants, zwitterionic co-surfactants, and mineral oil with did not suffer from the disadvantages described in the prior paragraph. Due to the co-existence of immiscible components (oil and water) in the nanosurfactant solution, the configuration of nanosurfactants formed in seawater is fundamentally different than just a mixture (or a blend) of surfactant molecules. The nanosurfactants are emulsions of nano-sized oil droplets that contain the petroleum sulfonate. The droplets are in turn stabilized by the co-surfactant molecules, which are not easily hydrolyzed in seawater.
Embodiments disclosed here include methods for producing nanosurfactant compositions suitable for injection into a hydrocarbon-bearing formation for enhanced recovery operations. One such method includes the steps of mixing a sulfonate surfactant and a zwitterionic co-surfactant in the presence of freshwater or deionized water. In certain embodiments, the sulfonate surfactant contains 2 wt % to 20 wt % of mineral oil. If the sulfonate surfactant does not contain the required amount of mineral oil, then external mineral oil is added to the sulfonate surfactant. If required, the various fluids are diluted with freshwater or deionized water to the desired concentrations. The method further includes introducing an aqueous salt solution with cations to the reactor to the freshwater mixture of sulfonate surfactant and zwitterionic co-surfactant to produce a nanosurfactant composition containing nanoparticles with a particle diameter in a range of from about 10 nm to 100 nm and the sulfonate surfactant and the zwitterionic co-surfactant at about 0.2-1 wt %. These nanoparticles are stable under high salinity and high temperature conditions. A substantial portion of the nanoparticles is stable for at least three months at temperatures of at least 100° C. The sulfonate surfactant is selected from the group consisting of an alkyl sulfonate, an alkyl aryl sulfonate, and combinations thereof. In certain embodiments, the sulfonate surfactant is a petroleum sulfonate salt. In certain embodiments, the petroleum sulfonate nanoparticles in seawater-based formulations have particle diameters ranging from about 10 nm to 60 nm. In certain embodiments, the zwitterionic co-surfactant contains cocamidopropyl hydroxysultaine.
Another method of producing nanosurfactant compositions includes mixing the sulfonate surfactant with the zwitterionic co-surfactant in the presence of fresh water. The resulting mixture contains water in an amount ranging from 80 wt % to 98 wt % and the total amount of surfactants ranging from about 2 wt % to 20 wt %. After mixing the surfactants, water containing cations, such as seawater, is introduced to form nanosurfactant compositions with the total amount of surfactants ranging from about 0.2 wt % to 1 wt %. The cations include one or more of sodium, calcium, magnesium, and potassium. The cations-containing water has a TDS concentration ranging from 50,000 ppm-150,000 ppm. In certain embodiments, the nanosurfactant compositions contain 0.1 wt %-0.25 wt % of petroleum sulfonates, 0.002 wt %-0.02 wt % of mineral oil, and 0.1 wt %-0.2 wt % of a zwitterionic co-surfactant. These nanosurfactant compositions are stable under reservoir conditions. An example of reservoir conditions includes a TDS concentration ranging from 60,000 ppm to 150,000 ppm and a reservoir temperature ranging from 100° C. to 120° C.
These nanosurfactant compositions are different from the fracturing fluids that contain zwitterionic and ionic surfactants. The fracturing fluids contain 10 wt % to 20 wt % of the zwitterionic surfactants and the methods of production of these fracturing fluids do not permit the formation of the nanoparticles. As the fracturing fluids contain large amounts of surfactants to increase fluid viscosity, the fracturing fluids do not pass through the pores but instead fracture the rocks of the reservoir. Disclosed here are nanosurfactant compositions containing surfactants ranging from about 0.2 wt % to 1 wt % of the fluid used for improved or enhanced oil recovery. At this reduced concentration of surfactants, the fluid containing the nanosurfactants passes through the pores. The salts contained in the seawater force the surfactant and co-surfactant to form nanoparticles and stabilize these nanoparticles. The fluid containing the nanoparticles passes through the pores easily and delivers the active surfactants to mobilize oil and enhance recovery.
In some embodiments, the nanosurfactant composition includes oil-containing nanoassemblies. As shown in
Embodiments provide nanosurfactant compositions suitable for injection into a hydrocarbon-bearing formation for enhanced recovery operations. A non-limiting example nanosurfactant composition includes a sulfonate surfactant, a zwitterionic co-surfactant, a functionalized zwitterionic copolymer, mineral oil, and saline water.
In some embodiments, the nanosurfactant composition has a sulfonate surfactant content ranging between about 0.1 wt. % and about 0.25 wt. %. In some embodiments, the nanosurfactant composition has a zwitterionic co-surfactant content ranging between about 0.1 wt. % and about 0.25 wt. %. In some embodiments, the nanosurfactant composition has a cationic co-surfactant content ranging between about 0.005 wt. % and about 0.1 wt. %. In some embodiments, the nanosurfactant composition has an oil content ranging between about 0.002 wt. % and about 0.02 wt. %.
Embodiments include nanosurfactant compositions and use of these compositions with long-term stability at high salinity and high temperature conditions. The nanosurfactant compositions include nanoassemblies including a sulfonate surfactant, a zwitterionic co-surfactant, a functionalized zwitterionic copolymer, and an oil (such as mineral oil). The hydrophobic interior of the nanoassembly includes the mineral oil, the hydrophobic portion of the sulfonate surfactant, and the hydrophobic portion of the zwitterionic co-surfactant. In some embodiments, the hydrophilic portion of the sulfonate surfactant is located in the hydrophobic interior of the nanoassembly. The hydrophilic exterior of the nanoassembly includes the hydrophilic portion of the zwitterionic co-surfactant. In some embodiments, the functionalized zwitterionic copolymer is dissolved in the aqueous environment. In some embodiments, the functionalized zwitterionic copolymer interacts with the hydrophilic exterior of the nanoassembly. Without being bound by any theory, the functionalized zwitterionic copolymer screens the charged surface of the hydrophilic exterior of the nanoassembly from ions that may be present in the aqueous environment and from ions that may be present on the reservoir rock surface. Such nanosurfactant compositions are capable of reducing the overall dynamic retention on carbonate rock by greater than about 67% compared to nanosurfactant compositions that are in the absence of the functionalized zwitterionic copolymer. The zwitterionic co-surfactant is hydrolysis resistant.
In some embodiments, the sulfonate surfactant can include petroleum sulfonate. Petroleum sulfonate can include alkyl sulfonates, alkyl aryl sulfonate, alkyl xylene sulfonate, and alpha-olefin sulfonates, and combinations of the same. Non-limiting examples of a commercially-available product that contains petroleum sulfonate include PETRONATE® EOR-2095 sodium sulfonates and PETRONATE® HL/L sodium sulfonates.
In some embodiments, the zwitterionic co-surfactant can include cocamidopropyl hydroxysultaine or betaine-based surfactants. The molecular structure of cocamidopropyl hydroxysultaine (or N,N-dimethyl-N-(3-cocamidopropyl)-3-ammonio-2-hydroxypropylsulfonate) is shown in Formula (I):
where n is a positive integer ranging from 1 to 20. Non-limiting examples of a commercially available product that contains cocamidopropyl hydroxysultaine or betaine-based surfactants include SURFATEX CBS™, PETROSTEP® SB, PETROSTEP® CG-50, Amphosol® CG-50, and ColaTeric CBS-HP.
In some embodiments, the functionalized zwitterionic copolymer can include a first monomeric unit and a second monomeric unit. The functionalized zwitterionic copolymer can be amphiphilic. The first monomeric unit can include hydrophilic functional groups. The first monomeric unit can include cationic, anionic, zwitterionic, or amphoteric functional groups. In at least one embodiment, the first monomeric unit includes a zwitterionic functional group. As a non-limiting example, the first monomeric unit can include a vinylimidazole unit. The vinylimidazole unit can be 1-vinylimidazole where the vinyl group forms a covalent bond at the N1 position of the imidazole unit. The 1-vinylimidazole unit can be further functionalized with an alkyl sulfonate unit forming a covalent bond at the N3 position of the imidazole unit. In this manner, the sulfonate group exhibits a negative charge and the N3 of the imidazole unit exhibits a positive charge, resulting in a zwitterionic monomeric unit. The second monomeric unit can include hydrophobic functional groups. As a non-limiting example, the second monomeric unit can include a styrene unit. The styrene unit can be an alkylstyrene such as methylstyrene. The methylstyrene can be 4-methylstyrene. One or more hydrogen atoms of the methyl group forming the 4-methylstyrene can be substituted with one or more halogen atoms such as fluorine, chlorine, bromine, and iodine. In at least one embodiment, the second monomeric unit includes 4-(trifluoromethyl)styrene, which is a fluoro monomeric unit. In some embodiment, the second monomeric unit can include an acrylate unit. The acrylate unit can be an alkyl acrylate. Non-limiting examples of the alkyl group forming the alkyl acrylate-based second monomeric unit include —CH2CH3, —CH(CH3)2, and —C(CH3)3. One or more hydrogen atoms of the alkyl group forming the alkyl acrylate-based second monomeric unit can be substituted with one or more halogen atoms such as fluorine, chlorine, bromine, and iodine. Non-limiting examples of a fluoroalkyl group forming a fluoroalkyl acrylate-based second monomeric unit include —CH2CF3, —CH(CF3)2, and —C(CF3)3.
In at least one embodiment, the molecular structure of the functionalized zwitterionic copolymer is shown in Formula (II):
where n, x, and y are positive integers. The first monomeric unit (that is, the zwitterionic monomeric unit) includes 1-vinylimidazole functionalized with a n-propyl sulfonate at the N3 position of the imidazole unit. The second monomeric unit (that is, the fluoro monomeric unit) includes 4-(trifluoromethyl)styrene.
Advantageously, the zwitterionic monomeric units and the fluoro monomeric units of the functionalized zwitterionic copolymer allow the nanoassembly to exhibit an overall charge less anionic than in the absence of either of the zwitterionic monomeric units or the fluoro monomeric units, or both. In this manner, the interactions between the nanoassembly and the carbonate rock surface can be reduced. Advantageously, the trifluromethyl groups of the functionalized zwitterionic copolymer that can be present on the surface of the nanoassembly can form repulsive dipole interactions against the carbonate rock surface, preventing the nanoassembly from being adsorbed or absorbed to the carbonate rock surface.
In an example embodiment of the method, the petroleum sulfonate and the mineral oil are combined to form a first mixture. Subsequently, the first mixture, the zwitterionic co-surfactant, and fresh water are combined to form a second mixture. The second mixture, the functionalized zwitterionic copolymer, and additional fresh water are combined to form a third mixture. Thereafter, the third mixture and saline water are combined to form the nanosurfactant composition. The saline water includes divalent cations where the hydrophilic position of the zwitterionic co-surfactant interacts with the divalent cations present in the aqueous environment to stabilize the nanoassembly. The mineral oil facilitates the containment of the petroleum sulfonate in the hydrophobic interior of the nanoassembly. The functionalized zwitterionic copolymer present in the aqueous environment is configured to screen the charged surface of the hydrophilic exterior of the nanoassembly from ions present in the aqueous environment and from ions that may be present on the reservoir rock surface.
In an example embodiment of the method, the petroleum sulfonate, the mineral oil, and fresh water are combined to form a first mixture. The zwitterionic co-surfactant and fresh water are combined to form a second mixture. The functionalized zwitterionic copolymer and fresh water are combined to form a third mixture. Subsequently, the first mixture, the second mixture, and the third mixture are combined to form a fourth mixture. Thereafter, the fourth mixture and saline water are combined to form the nanosurfactant composition. The saline water includes divalent cations where the hydrophilic position of the zwitterionic co-surfactant interacts with the divalent cations present in the aqueous environment to stabilize the nanoassembly. The mineral oil facilitates the containment of the petroleum sulfonate in the hydrophobic interior of the nanoassembly. The functionalized zwitterionic copolymer present in the aqueous environment is configured to screen the charged surface of the hydrophilic exterior of the nanoassembly from ions present in the aqueous environment and from ions that may be present on the reservoir rock surface.
In an example embodiment of the method, the nanosurfactant composition is introduced into a hydrocarbon-bearing formation. The hydrocarbon-bearing formation can include carbonate-based rocks. The nanosurfactant composition is driven through the hydrocarbon-bearing formation such that the nanoassembly makes contact with and displaces hydrocarbons from the formation by reducing the interfacial tension between the hydrocarbons and the saline water included in the nanosurfactant composition. The functionalized zwitterionic copolymer present in the aqueous environment is configured to screen the charged surface of the hydrophilic exterior of the nanoassembly from ions present on the carbonate-based rock surface.
Examples of certain embodiments are provided here to facilitate a better understanding of the nanosurfactant compositions and methods of production of the nano surfactant compositions for use in enhanced oil recovery.
Experiments were conducted to evaluate performance of a petroleum sulfonate surfactant (EOR-2095) in combination with specific zwitterionic co-surfactants. Four zwitterionic co-surfactants were tested. Amphosol® LB is a mild amphoteric surfactant, containing lauramidopropyl betaine & myristamidopropyl betaine. PETROSTEP® CG-50 contains cocamidopropyl betaines. PETROSTEP® SB contains cocoamidopropyl hydroxysultaine. SURFATEX CBS™ contains cocamidopropyl hydroxysultaine. The qualitative results of these zwitterionic co-surfactants with EOR-2095 were analyzed by stability tests. Two co-surfactants—PETROSTEP® SB and SURFATEX® CBS (STRX)—were chosen for further experimentation with different sulfonates (EOR-095, BIOSOFT S101®, NACCANOL 90G®, G-3300®, ENORDET O342®, ENORDET O352®, ENORDET O242®). These surfactant and co-surfactant formulations were evalutated in seawater as well as in low salinity Arab-D brine. The stability and properties of the nanosurfactant compositions are dependent on type of the sulfonates used as the core of the nanostructured entity. The properties of the nanosurfactants are affected by factors such as co-surfactant type, salt concentration, type of petroleum sulfonate/alternative, oil content, and amount. Based on these tests, EOR-2095 and SURFATEX® CBS were selected for conducting further analysis.
Provided below in Table 1 is an example of the composition of the synthetic seawater. The different compounds were added in grams as shown in Table 1 to make one liter of synthetic seawater.
Cryo-TEM was used to study the morphology of the nanosurfactant samples. About 20 microliters (μL) of the nanosurfactant mixture samples were deposited without dilution onto copper C-flat holey carbon grids (Product code: CF-1.2/1.3-4C-T-50 from Electron Microscopy Sciences). The samples were blotted and frozen on a Gatan CP3 Cryoplunge in liquid ethane cooled with liquid nitrogen. Samples were mounted on the autoloader of an FEI Tecnai Arctica Field Emission Cryo-TEM (available at Center of Nanoscale Systems, Harvard University, Cambridge, Mass., USA). Low electron dose images were taken under 200 kilovolts accelerating voltage. As shown in
The stability of the nanosurfactant suspensions was tested in seawater at elevated temperatures (100° C.) for more than four months. Nanosurfactant samples were placed in cylindrical pressure tubes with air-tight Teflon lids. The tubes were sealed tightly and incubated in the oven at 100° C. The stability of these samples was checked and photographed over different periods of time.
Dynamic Light Scattering (DLS) analysis was used to measure changes in size of the nanosurfactant particles and aggregation behavior with increasing temperature and upon cooling back to room temperature. Different dilutions of about 3 mL nanosurfactant solutions in seawater (none, 1:3, 1:5, 1:7, 1:15) were placed in capped quartz cuvettes. The temperature was increased uniformly from 25° C. to 90° C. at 5° C. increments with a 15-minute equilibration time at each temperature prior to measuring the particle size. For each temperature, the particle size was taken as an average of five measurements of 90 seconds each. At the end of the heating cycle, measurements were repeated for the cooling process from 90° C. to 25° C. with all other parameters being the same.
One of the most important characteristics that determine the efficiency of a surfactant treatment in EOR is the IFT reduction. The IFT between crude oil and an aqueous solution (i.e. nanosurfactant-containing fluid) was measured using a spinning drop interfacial tensiometer (M6500). The solution to be tested was filled in a capillary tube and a drop of filtered UTMN crude oil (from Uthmaniyah oil field) was spun at ˜4000 revolutions per minute (rpm) at 90° C. The diameter of the oil droplet was recorded every 5 minutes for around 30 minutes and used to calculate the IFT based on known density deference, temperature, speed, and the drop diameter. The IFT is calculated as:
IFT Measurements for Nanosurfactant Samples
The IFT was measured for nanosurfactant samples and for fluids containing the zwitterionic co-surfactant alone. Table 2 and
Additionally, interfacial tension evaluation was conducted after the nanosurfactant composition was kept in the oven for more than 4 months at 100° C. About 5 mL of the sample was taken from the tube and the rest of the sample was sealed tightly and returned to the oven. The results were compared with the IFT values for the same sample that was measured previously before being incubated in the oven. Table 3 and
More IFT evaluations were conducted using different dilutions of the zwitterionic co-surfactant alone and the nanosurfactant composition. These samples were prepared by mixing components as shown in Table 4, and their IFT was measured. For the nanosurfactant composition, the previously prepared stock solution was diluted with seawater and used. On the other hand, for the zwitterionic co-surfactant samples, a new solution was prepared by adding 10 mL deionized water to the 4 wt % STRX original solution followed by 100 mL seawater. This co-surfactant solution was used as a stock for IFT and phase behavior experiments.
The results are summarized in
Further IFT measurements were obtained for the zwitterionic co-surfactant alone and the nanosurfactant composition containing the same amount of zwitterionic co-surfactant with different amounts of petroleum sulfonate. In order to realize the effect of the EOR-2095 concentration on the IFT values, samples with different zwitterionic co-surfactant/EOR-2095 ratios were prepared according to Table 5, where the volume of the zwitterionic co-surfactant solution was held constant in all the samples while varying the amount of EOR-2095.
Initially, the samples were prepared for IFT tests by mixing petroleum sulfonate and seawater first, then the zwitterionic co-surfactant was added. The mixtures appeared cloudy, indicating the formation of precipitates. So the measurements were repeated by first mixing the zwitterionic co-surfactant with petroleum sulfonate prepared in fresh water, followed by mixing with seawater. Only half of the samples were prepared for repeating the IFT (
To evaluate the role of mineral oil on IFT, a clear brown solution of EOR-2095 (2.5 wt %) was formed by mixing 2 g of oil-free petroleum sulfonate with 19.5 mL of deionized water. Mineral oil was intentionally removed from EOR-2095. The sample was sonicated using a probe sonicator for few minutes followed by using the ultrasonic bath for around 40 minutes with heating the sample at 60° C. This oil-free petroleum sulfonate (2.5 wt %) was used with the zwitterionic co-surfactant (4 wt %) and seawater to prepare two samples with the ratios 1:1:10 and 1:1.25:10 for petroleum sulfonate:the zwitterionic co-surfactant:seawater. The IFT was measured for theses samples for around 30 minutes and compared to the IFT for the zwitterionic co-surfactant-nanosurfactant (stock). Table 7 and
The presence of mineral oil improves the IFT performance of the nanosurfactant by approximately 4-5 times. Mineral oil facilitates the formation of nano-emulsion droplets and containment of the petroleum sulfonates. Also, this suggests that doping the petroleum sulfonates with different types and amounts of oil may play an important role.
An experiment was done using two different filtration options to address a concern about how much the soluble fraction of the petroleum sulfonate affects the IFT value with crude oil. About 10 mL of the 5 wt % EOR-2095 was mixed with 12.5 mL deionized water and 100 mL seawater. Sample was set for an hour and precipitated chunks were filtered by a filter paper under vacuum and IFT was measured for this supernatant. The other part of the sample was further filtered using a 0.22 μm syringe filter, then IFT was measured again. Table 8 and
IFT for Seawater and the Zwitterionic Co-Surfactant using Petroleum Sulfonates/Oil
A solution of 5 wt % petroleum sulfonates was prepared by mixing 50 g of EOR-2095 with 950 mL deionized water, as shown in
Phase behavior experiments were conducted on samples of the zwitterionic co-surfactant alone and the nanosurfactant composition. The experimental results were recorded by visual inspection with the use of UV light (365 nm). About 5 mL from each sample was placed into a pressure tube and sealed tightly to avoid any fluid loss. From each sample, two tubes were prepared; one with the addition of oil and the other without any oil. UTMN crude oil was used and was added gently to the surface of the sample, as shown in
Comparing the tubes containing the nanosurfactant mixture in contact with crude oil with those containing the co-surfactant alone in contact with crude oil, it can be seen that the samples with the nanosurfactant mixture are much darker, indicating improved formation of oil-in-water emulsions. Comparing the tubes containing the nanosurfactant mixture in contact with crude oil with those containing the co-surfactant alone, but containing no oil indicates that the more pronounced blue light emitted from the nanosurfactant mixture is due to the petroleum sulfonate. When they get in contact with crude oil, samples of the nanosurfactant composition and the fluid with the zwitterionic co-surfactant alone exchange some components with the crude oil into the aqueous phase, with the nanosurfactant composition being more efficient in enhancing that exchange. The above observations further support the ability of the nanosurfactant formulation to enhance the interaction of seawater with crude oil and form oil-in-water emulsions, thus improving recovery.
Further phase behavior experiments were conducted to examine the interaction of the zwitterionic co-surfactant and seawater with the petroleum sulfonates and oil.
Static sorption tests were conducted to evaluate the nanosurfactant solution with zwitterionic co-surfactant (˜0.2 wt % total active ingredients) and the zwitterionic co-surfactant alone (˜0.1 wt % STRX). Briefly, outcrop Arab-D rock was crushed as fine as possible and sieved to isolate the fraction passing through mesh size 40 and retained mesh size 100. In two 15 mL pressure tubes, about 4.0 g of crushed rock was added with 10 mL of the nanosurfactant mixture. In another two 15 mL pressure tubes, 4.0 g of crushed rock was added with 10 mL of the zwitterionic co-surfactant solution alone. The control samples were separate tubes of 10 mL of the nanosurfactant solution and 10 mL of the zwitterionic co-surfactant solution. Tubes were shaken 10 times and placed in the oven for 24 hours at 100° C. Samples were removed from the oven and 3 mL from the supernatant were collected in centrifuge tubes. Samples were centrifuged for 30 minutes at 3000 rpm, and about 2 mL of the supernatant (uppermost layer) was collected from each centrifuge tube into separate clean test tubes. NMR measurements were done on the supernatant samples. As shown in
To quantify the loss of surfactants due to adsorption, three 10 mL aliquots of zwitterionic co-surfactant alone (0.2 wt % in synthetic seawater) and three 10 mL aliquots of the nanosurfactant mixture (0.2 wt % of active ingredients) were placed in 15 mL screwcap tubes. Then, powdered Arab-D outcrop rock (4.00 g, 40-100 mesh fraction) was added to the two tubes containing the zwitterionic co-surfactant alone and two tubes containing the nanosurfactant mixture. The tubes were sealed, vigorously shaken and placed in an oven maintained at 100° C. for 24 hours. Following the heating step, the tubes were cooled to room temperature and 3 mL aliquots of the supernatants were withdrawn. The aliquots were placed in disposable polyethylene centrifuge test tubes and centrifuged at 3000 rpm for 30 minutes. Aliquots of the resulting supernatants (0.9 mL) were withdrawn using an Eppendorf micropipette and mixed with a standard solution of maleic acid (0.1 mL, 0.10 g of maleic acid in 11.08 g of D2O) as an internal reference in scintillation vials. Then about 0.7 mL aliquots of the mixed solutions were transferred to the NMR tubes for measurements. The 1H-NMR spectra were measured on Bruker Avance spectrometer operating at 400 MHz. To suppress the water peak, each spectrum was induced with an excitation sculpting pulse sequence using the standard (zgespg) program from the Bruker pulse library. A 4000 Hz acquisition window centered at the peak of the water signal (about 4.7 ppm) was used and 64 scans were collected for each sample with a 3 second delay between the scans. The integral of maleic acid (sharp singlet at 6.45 ppm) was given the value of 1000 for every sample and the other integrals were referenced to it. As shown in
NMR results in
In studies using the nanosurfactant mixture with zwitterionic co-surfactant as shown in
In order to assess the effects of mineral oil on the stability and functionality of the nanosurfactant composition (STRX-NS), a set of stability experiments and IFT measurements were conducted following the same procedures and conditions described in the previous sections.
As shown in
Several sorption tests were also conducted in which total organic carbon was used to quantify the amount of total carbon lost by sorption to the rock. For the nanosurfactant formulation containing the zwitterionic co-surfactant, the tests showed a total carbon loss of 0.88 mg/g after contact with the rock for 14 days at 100° C. This number corresponds to 13% loss of the total mineral oil introduced to the rock that aligns with the NMR results.
The nanosurfactant formulation containing the zwitterionic co-surfactant was subjected to further evaluation of oil recovery using several core plugs (17) from Arab-D reservoir. Routine core analysis was conducted and the petrophysical parameters, such as dimensions, porosity, permeability and pore volume were measured. For the first composite, three core plugs were selected based on their permeability, computed tomography (CT) scan and NMR data. The plugs were arranged as shown in
The experimental instrumentation 2800 includes a delta pressure module 2807, capable of delivering low delta pressure, or medium delta pressure, or high delta pressure, and in fluid communication with the core sample holder 2806. The experimental instrumentation 2800 also includes an air inlet 2808 and a water inlet 2809 that are supplied to a confining pressure module 2810. This module 2810 is in fluid communication with the core sample holder 2806. Effluent from the core sample holder 2806 is supplied to a sample analysis module 2811. Not shown in the figure are separators, back-pressure modulators, filters, pressure and temperature sensors, valves, pumps, heating elements and cooling elements that are in fluid communication with various components of the experimental instrumentation 2800 and are known to one of ordinary skill in the art.
About 20 core plugs with known air permeability (kair)>50 milliDarcy)) were selected. These plugs were cleaned and dried and their dry parameters were measured (kair, weight, porosity, density). These plugs were saturated with seawater and their wet weight and brine permeability (kw) were measured. Effluent water samples leaving the plugs were subjected to geochemistry analysis (every 4 pore volumes (PV)). Aliquots were provided to an external laboratory for IFT and micromodel experiments and for later imbibition tests. The saturated volumes were calculated and NMR (T2) on seawater-saturated samples were conducted. Core plugs were then saturated with dead UTMN crude oil (4-5 PVs). Samples were centrifuged if needed. The volume of water was measured and the initial water saturation (Swi) was calculated. The plugs were weighed and the volume of oil was calculated. NMR (T2) on oil-saturated plugs was conducted at Swi. The effluent oil samples were processed for IFT and micromodel experiments. These plugs were then age-saturated with oil at 90° C. and 1000 psi. Then, the NMR (T2) analysis of the aged samples was conducted. Three sets of core plug composites (3 plugs each) were assembled and dynamic coreflooding was run on two sets of composite core plugs using seawater until reaching residual oil saturation, Sor. Two core plugs were flooded with nanosurfactant composition, one at Swi, and one at Sor. NMR was conducted on plugs after the dynamic coreflood tests.
A functionalized zwitterionic copolymer was formulated by the following process. 2 g (equivalent to 21.25 mmol) of 1-vinyl imidazole, 0.406 g (equivalent to 2.36 mmol) of 4-trifluoromethylsytrene), 0.0388 g of 1 mol % (equivalent to 0.236 mmol) azobisisobutyronitrile (AIBN), and 5 mL of dimethyl sulfoxide (DMSO) were combined in a Schlenk tube with a magnetic stir bar. The reaction mixture was degassed using freeze-pump-thaw cycling for three cycles, sealed under a static inert atmosphere, and stirred at 60° C. for about 4 days. The resulting light yellow viscous mixture was cooled and diluted by adding methanol. The mixture was twice precipitated using acetone then dried overnight to produce a precursor copolymer poly(vinyl imidazole-co-4-trifluoromethylstyrene) (0.95:0.05), which was a clear hard light yellow solid. 1.2 g (equivalent to 10.6 mmol of the imidazole moieties) of the precursor copolymer dissolved in methanol and 1.555 g (equivalent to 12.75 mmol, which is about 1.2 times the magnitude than that of the imidazole moieties) of 1,3-propane sultone were combined. The reaction mixture was refluxed overnight under an inert atmosphere. The resulting functionalized zwitterionic copolymer was precipitated and filtered out. The resulting functionalized zwitterionic copolymer was twice washed with a mixture of 1:1 mixture of methanol and diethyl ether, and dried under vacuum to yield a light yellow solid.
A sample nanosurfactant composition, including the petroleum sulfonate, the zwitterionic co-surfactant, and the functionalized zwitterionic copolymer (formulated by the process shown in Example 8), and the mineral oil, was formulated by the following process. A PETRONATE® HL/L sodium sulfonate mixture (Sonneborn LLC, Parsippany, N.J.) was used as the source for the petroleum sulfonate and the oil. The petroleum sulfonate mixture had a sulfonate content ranging between 61 wt. % and 63 wt. %. The mixture had an oil content ranging between 31 wt. % and 35 wt. %. A 5 wt. % petroleum sulfonate mixture was prepared by mixing 80 g of the PETRONATE® HL/L sodium sulfonate mixture with 900 mL of deionized water and adjusting the volume to 1,000 mL with additional deionized water. A 4 wt. % aqueous zwitterionic co-surfactant solution was prepared by dissolving 91 g of the STRX co-surfactant (containing cocamidopropyl hydroxysultaine) in 900 mL of deionized water and adjusting the volume to 1,000 mL with additional deionized water once the dissolution was complete. A 5 wt. % aqueous functionalized zwitterionic copolymer solution was prepared by dissolving 50 g of the functionalized zwitterionic copolymer formulated in Example 8 in 900 mL of deionized water and adjusting the volume to 1000 mL with additional deionized water once the dissolution was complete. About 10 mL of the 5 wt. % petroleum sulfonate mixture, about 15 mL of the 4 wt. % aqueous zwitterionic co-surfactant solution, and about 10 mL of the 5 wt. % aqueous functionalized zwitterionic copolymer solution were vigorously mixed to form a suspension. About 530 mL of the synthetic seawater (as shown for example in Table 1, having a TDS concentration ranging between 57,000 ppm and 120,000 ppm) and about 35 mL of the suspension were vigorously mixed to form the sample nanosurfactant composition including the nanoassemblies. The sample nanosurfactant composition had a petroleum sulfonate content of about 0.1 wt. %. The sample nanosurfactant composition had a zwitterionic co-surfactant content of about 0.12 wt. %. The sample nanosurfactant composition had a functionalized zwitterionic copolymer content of about 0.1 wt. %. The sample nanosurfactant composition had an oil content ranging between about 0.002 wt. % and about 0.02 wt. %. The sample nanosurfactant composition had an organic content of about 0.32 wt. %.
A control nanosurfactant composition was also formulated using the above process but in the absence of the functionalized zwitterionic copolymer. The functionalized zwitterionic copolymer solution was substituted with an identical volume of deionized water. The control nanosurfactant composition had a nanoassembly content of about 0.2 wt. %.
The dynamic retention of the nanosurfactant compositions of Example 9 in carbonates was studied by flooding a limestone core plug. The composition of the effluent was determined by total organic carbon (TOC) analysis. The core plug had a 1.5 inch diameter and a 3 inch length. Limestone was used as a carbonate source. The permeability of the core plug was about 200 milliDarcy. The pore volume of the core plug was about 12.5 mL. The core plug was set in a vertical, bottom-to-top configuration. Temperature of the core plug was maintained at about 93° C. Twelve pore volumes of the sample nanosurfactant composition were injected into the core plug at an injection flow rate of about 0.5 mL/min, a core pressure of about 3,200 psi, and a confining pressure of about 4,200 psi. Subsequently, 35 pore volumes of the synthetic seawater were injected into the core plug. The core flooding experiment was repeated using the control nanosurfactant composition.
Ranges may be expressed here as from about one particular value and to about another particular value. Where the range of values is described or referenced here, the interval encompasses each intervening value between the upper limit and the lower limit as well as the upper limit and the lower limit and includes smaller ranges of the interval subject to any specific exclusion provided. Where a method comprising two or more defined steps is recited or referenced here, the defined steps can be carried out in any order or simultaneously except where the context excludes that possibility. While various embodiments have been described in detail for the purpose of illustration, they are not to be construed as limiting, but are intended to cover all the changes and modifications within the spirit and scope thereof.
This application is a continuation-in-part application of U.S. patent application Ser. No. 15/917,097, filed on Mar. 9, 2018, which claims the benefit of and priority to U.S. Provisional Application Ser. No. 62/469,414, filed on Mar. 9, 2017; all of the above-referenced applications are incorporated by reference in their entireties into this application.
Number | Name | Date | Kind |
---|---|---|---|
3939911 | Maddox et al. | Feb 1976 | A |
4008165 | Maddox et al. | Feb 1977 | A |
4017405 | Holm | Apr 1977 | A |
4018278 | Shupe | Apr 1977 | A |
4066124 | Carlin | Jan 1978 | A |
4088189 | Shupe | May 1978 | A |
4094798 | Tate et al. | Jun 1978 | A |
4110228 | Tyler et al. | Aug 1978 | A |
4110229 | Carlin et al. | Aug 1978 | A |
4120358 | Kalfoglou | Oct 1978 | A |
4154301 | Carlin et al. | May 1979 | A |
4194565 | Kalfoglou | Mar 1980 | A |
4296812 | Kalfoglou | Oct 1981 | A |
4318816 | Schievelbein | Mar 1982 | A |
4667740 | Maddox, Jr. | May 1987 | A |
5074385 | Tanino et al. | Dec 1991 | A |
5203411 | Dawe et al. | Apr 1993 | A |
5360558 | Pakulski et al. | Nov 1994 | A |
5736496 | Durbut et al. | Apr 1998 | A |
6302209 | Thompson, Sr. | Oct 2001 | B1 |
7094738 | Patal et al. | Aug 2006 | B2 |
7104327 | Harris et al. | Sep 2006 | B2 |
7932214 | Zamora et al. | Apr 2011 | B2 |
7939470 | Wagle et al. | May 2011 | B1 |
8252729 | Zhang | Aug 2012 | B2 |
8403044 | Hutchison et al. | Mar 2013 | B2 |
8637622 | Monin et al. | Jan 2014 | B2 |
8946132 | Chang et al. | Feb 2015 | B2 |
8969261 | Talingting Pabalan et al. | Mar 2015 | B2 |
8985206 | Morvan et al. | Mar 2015 | B2 |
9321955 | Hill et al. | Apr 2016 | B2 |
9512704 | Dawson et al. | Dec 2016 | B2 |
9951264 | Penny et al. | Apr 2018 | B2 |
10059872 | Janak et al. | Aug 2018 | B2 |
10190036 | Hernandez-Altamirano et al. | Jan 2019 | B2 |
20120095111 | Findley et al. | Apr 2012 | A1 |
20120285694 | Morvan et al. | Nov 2012 | A1 |
20130292121 | Penny et al. | Nov 2013 | A1 |
20150107832 | Dewolf et al. | Apr 2015 | A1 |
20150183979 | Pabalan et al. | Jul 2015 | A1 |
20160003018 | Saboowala | Jan 2016 | A1 |
20160075932 | Silveira | Mar 2016 | A1 |
20160076348 | Fernandez-Ibanez et al. | Mar 2016 | A1 |
20160160113 | Nguyen et al. | Jun 2016 | A1 |
20160186546 | Dawson et al. | Jun 2016 | A1 |
20160194550 | Hill et al. | Jul 2016 | A1 |
20160251568 | Do et al. | Sep 2016 | A1 |
20160257879 | Huang et al. | Sep 2016 | A1 |
20160290104 | Nelson et al. | Oct 2016 | A1 |
20170044423 | Weerasooriya et al. | Feb 2017 | A1 |
20170198193 | Rebolledo et al. | Jul 2017 | A1 |
20180134941 | Saboowala et al. | May 2018 | A1 |
20180346798 | Abdel-Fattah | Jun 2018 | A1 |
20180273830 | Hernandez Altamirano et al. | Sep 2018 | A1 |
20190169492 | Hill et al. | Jun 2019 | A1 |
20190330518 | Dai et al. | Oct 2019 | A1 |
20190345373 | Favero | Nov 2019 | A1 |
Number | Date | Country |
---|---|---|
103421481 | Dec 2013 | CN |
104419395 | Mar 2015 | CN |
105971571 | Sep 2016 | CN |
1201720 | May 2002 | EP |
2465911 | Jun 2012 | EP |
2001377 | Jan 1979 | GB |
2015135777 | Sep 2015 | WO |
2018209716 | Nov 2018 | WO |
2019195604 | Oct 2019 | WO |
Entry |
---|
“Safety Assessment of Alkyl Betaines as Used in Cosmetics”, Cosmetic Ingredient Review Final Report, 2014, pp. 23. |
“Safety Assessment of Alkyl Sultaines as Used in Cosmetics”, Tentative Report for Public Comment, 2017, pp. 21. |
Ahmed et al., “Empirical Modeling of the Viscosity of Supercritical Carbon Dioxide Foam Fracturing Fluid under Different Downhole Conditions”, Energies, 2018, pp. 1-16. |
Gizzatov et al., “Nanofluid of Petroleum Sulfonate Nanocapsules for Enhanced Oil Recovery in High-Temperature and High-Salinity Reseervoirs”, Energy & Fuels 33 (2019) pp. 11567-11573. |
He et al., “Brine-Soluble Zwitterionic Copolymers with Tunable Adsorption onRocks”, Applied Materials & Interfaces, 2020, pp. 13568-13574. |
International Search Report and Written Opinion for International Application No. PCT/US2018/021647; report dated Aug. 8, 2018; 16 pages. |
Li, et al, : “Synergism in mixed zwitterionic-anionic surfactant solutions and the aggregation numbers of the mixed micelles” Colloids and Surfaces A: Physiochemicaland Engineering Aspects, vol. 145, No. 1-3, pp. 167-174, Dec. 1998. |
Negin et al., “Most common surfactants employed in chemical enhanced oilrecovery”, Petroleum, 2017, pp. 197-211. |
Rosen, et al,“Synergism in binary mixtures of surfactants 12. Mixtures containing surfactants with two hydrophilic and two or three hydrophobicgroups”;Colloids and Surfaces A: Physiochemicaland Engineering Aspects; vol. 88, No. 1; pp. 1-11; Aug. 1994. |
Syed et al., “Influence of lauryl betaine on aqueous solution stability, foamability and foam stability”, Journal of Petroleum Exploration and Production Technology, 2019, pp. 2659-2665. |
Alzobaidi et al., “Continuous flow synthesis of petroleum sulfonates from crude oil and formulation into nano-surfactants for cost efficient oil mobilization”, Society of Petroleum Engineers, 2018, pp. 1-9. |
Singh et al., “Foams with wettability-altering capabilities for oil-wet carbonates: A synergistic approach”, Society of Petroleum Engineers, 2016, pp. 1-14. |
Number | Date | Country | |
---|---|---|---|
20200369947 A1 | Nov 2020 | US |
Number | Date | Country | |
---|---|---|---|
62469414 | Mar 2017 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 15917097 | Mar 2018 | US |
Child | 16990498 | US |