This invention relates generally to the field of metal-component fabrication and repair, and more particularly to the formation of oxide dispersion strengthened (ODS) alloys.
Oxide dispersion strengthened (ODS) alloys possess superior properties for high temperature applications; especially ODS alloys formed of superalloy materials. ODS alloys are distinguished from conventional alloys by the presence of dispersoids of fine particles and by an elongated grain shape which generally develops during a recrystallization heat treatment and/or hot and cold working. This particular grain structure enhances the high temperature deformation characteristics of ODS alloys by inhibiting the accumulation of inter-granular damage. As result of this and other properties, components fabricated from ODS alloys exhibit improved high-temperature creep strength and improved oxidation resistance as compared to conventional alloys.
The term “superalloy” is used herein as is understood in the art to describe a highly corrosion and oxidation resistant alloy that exhibits excellent mechanical strength and resistance to creep at high temperatures, as well as good surface stability. Superalloys typically include a base alloying element of nickel, cobalt or nickel-iron. Examples of superalloys include alloys sold under the trademarks and brand names Hastelloy, Inconel alloys (e.g., IN 700, IN 738, IN 792, IN 939), Rene alloys (e.g., Rene N5, Rene 80, Rene 142), Haynes alloys, Mar M, CM 247, CM 247 LC, C 263, 718, X-750, ECY 768, 282, X45, PWA 1483 and CMSX (e.g., CMSX-4, CMSX-8, CMSX-10) single crystal alloys.
ODS alloys, especially superalloys, are very difficult to weld and repair by conventional techniques (e.g., gas tungsten arc welding, laser welding, electron beam welding, etc.). Such fusion welding causes significant loss of strength. The alloys are furthermore difficult and uneconomical to process by less traditional processes such as friction welding.
ODS alloys are manufactured by mechanically alloying mixtures of powders. For example, metal powder such as alloys of iron aluminide, iron chromium, iron-chromium-aluminum, nickel chromium, or nickel aluminide, and oxides such as yttria (Y2O3) or alumina (Al2O3) are impacted in a ball mill. Shearing and smearing of the powders produces a fine mixture. A sealed container of the powder is then hot isostatically pressed and hot formed into a desired shape. High temperature heat treatment then provides stress relief and enlarges the grain size. Extraordinary strength is achievable with ODS materials. However, ODS processing is slow, expensive and provides limited control of part geometry. In addition, joining or repair of ODS parts is very difficult. Conventional arc and energy beam processes cause the fine oxide particles to segregate or coalesce, which degrades the result. Nickel based ODS superalloys are especially difficult to cold work and recrystallize.
Additional challenges associated with ODS alloys involve general shaping and joining of these materials. Shaping and joining techniques which preserve the microstructure and intrinsic strength of ODS alloys are severely limited, which often curtails their ability to be incorporated into high-temperature, load-bearing structures. For example, excessive heating of ODS alloys can cause the oxide to coalesce, leading to agglomeration such that the oxide dispersoids may no longer be effective in resisting slip at the grain boundaries. Melting of ODS alloys also results in “slagging off” of the oxide dispersoids reducing their strengthening ability. Since most ODS alloys derive their strength from an elongated grain structure, such disruption of the grain structure reduces strength.
The invention is explained in the following description in view of the drawings that show:
The substrate 23 may be made of an oxide dispersion strengthened (ODS) alloy with dispersoids 38A, and the ODS deposit 32 may be formed of material matching the substrate for buildup or repair, or the deposit 32 may be formed of material different than substrate for substrate surface enhancement. ODS cladding, layering, or welding may be applied to a substrate that is or is not ODS. In another embodiment, the substrate may be replaced with a fugitive or removable support surface for additive manufacturing that builds a component by successive ODS layering starting with a first layer on the support surface.
Particles of the metal oxide 34 may contain at least one metal oxide having a higher melting point than the filler alloy of the electrode 22. Exemplary metal oxides include oxides of aluminum, calcium, cerium, chromium, cobalt, hafnium, lanthanum, magnesium, nickel, silicon, titanium, tantalum, thorium, yttrium and zirconium. Mixtures of oxide particles containing different metal oxides and/or having different particle sizes may be used, or the oxide particles may be changed over time as the deposition progresses in space. The oxide particles may be directed 33 into the melt pool 26 from above as shown with nozzle 36. Alternately, not shown, they may be injected directly into the melt pool 26 from below its surface via a refractory nozzle to avoid contact with the atmosphere.
Excessive heating of the oxide can lead to coalescence and slagging of dispersoids 30B, adversely affecting the oxide distribution in the ODS deposit. Optimal size, shape and distribution of the dispersoids 30B may be attained in part by adjusting the alloy melting energy by adjusting the intensity of the arc and the on-off dwell proportions of the arc. The power and dwell times of the arc may be controlled so that the melt pool meets or exceeds the melting point of the filler alloy of the electrode 22 and the substrate, but does not reach the melting point of the oxide particles. This prevents oxide coalescence and slagging.
The distribution of the dispersoids 38B in the ODS alloy deposit 32 may be controlled by altering the velocity and concentration of particles of the oxide material 34 injected into the melt pool 26. Increasing the velocity or concentration of the oxide particles fired into the melt pool increases the proportion of dispersoids in the resulting deposit 32. Increasing velocity can also provide a more uniform distribution when the melt pool is especially viscous.
Herein, cold metal transfer and pulsed arc welding are illustrated as exemplary. Alternate technologies that can provide the alloy melting energy include pulsed gas metal arc welding, pulsed gas tungsten arc welding, pulsed tip tungsten inert gas welding (pulsed tip TIG), and pulsed energy beams, including for example a laser beam, a particle beam, a charged-particle beam, a molecular beam, etc. The cold metal transfer process is advantageous because of its mechanical mixing of the melt pool by rapid repetitive dipping of the electrode tip, high deposit control and relatively low heat. In addition to welding and cladding, it can form an extensive variety of additive deposition forms and wall growth directions. Tip tungsten inert gas welding may also be advantageous because of superimposed mechanical oscillation of feed wire helping to agitate the molten weld pool and promote oxide distribution therein. The on/off switching of the alloy melting energy described herein includes in some embodiments switching between a first energy level (on) and a second energy level (off) that is less than 50% of the first energy level.
Embodiments of the present disclosure enable the formation and repair of ODS superalloy components. However the invention is not confined to such materials and may also be applied to other ODS materials.
While various embodiments of the present invention have been shown and described herein, it will be obvious that such embodiments are provided by way of example only. Numerous variations, changes and substitutions may be made without departing from the invention herein. Accordingly, it is intended that the invention be limited only by the spirit and scope of the appended claims.
Number | Name | Date | Kind |
---|---|---|---|
4261764 | Narayan | Apr 1981 | A |
4595820 | Richardson | Jun 1986 | A |
4803334 | Burke | Feb 1989 | A |
5067986 | Fried et al. | Nov 1991 | A |
5449435 | Funkhouser et al. | Sep 1995 | A |
20080311420 | Zillmer et al. | Dec 2008 | A1 |
20110103961 | Glover et al. | May 2011 | A1 |
20120325779 | Yelistratov | Dec 2012 | A1 |
20130299470 | Park | Nov 2013 | A1 |
20150093279 | Kington et al. | Apr 2015 | A1 |
Number | Date | Country |
---|---|---|
2826655 | Nov 2012 | CA |
2218660 | Nov 1989 | GB |
Entry |
---|
Molian, P.A., et al., “Laser Welding of Oxide Dispersion-Strengthened Alloy MA754,” Journal of Materials Science, 1992, 27, 2687-94. |
Z. Feng, Z. Yu, D. Hoelzer, M. A. Sokolov, and L. T. Tan; “Friction Stir Welding of ODS Steels and Advanced Ferritic Structural Steels”; Oak Ridge National Laboratory, Fusion Reactor Materials Program; DOE/ER-0313/54, vol. 54, pp. 51-60; Jun. 30, 2013. |
Number | Date | Country | |
---|---|---|---|
20170080508 A1 | Mar 2017 | US |