Patent Application
20070095469
This invention relates to the formation of self-assembled monolayers (SAMs). In a preferred embodiment, the invention relates to the formation of SAMs in microcontact printing and, more particularly, b a new class of ink molecules for the formation of SAMs in microcontact printing, and their use therein.
Patterning a metal over a substrate is a common need and important process in modern technology, and is applied, for example, in microelectronics and display manufacturing. This patterning usually requires the vacuum deposition of a metal over the entire surface of a substrate and its selective removal using photolithography and etching techniques.
Microcontact printing is a technique for forming patterns of organic monolayers with micrometer and submicron lateral dimensions. It offers experimental simplicity and flexibility in forming certain types of patterns by printing molecules from a stamp onto a substrate. So far, most of the prior art relies on the remarkable ability of long chain alkanethiols to form self-assembled monolayers on, for example, gold or other metals. These patterns can act as nanometer-thin resists by protecting the supporting metal from corrosion by appropriately formulated etchants, or can allow for the selective placement of fluids on hydrophilic regions of the printed pattern. Patterns of SAMs having lateral dimensions that can be less than 1 micrometer can be formed by printing them on a metal substrate using an elastomeric “stamp”. The stamp is fabricated by moulding, for example, a silicone elastomer using a master (or mould) prepared using photolithography or using other techniques such as electron-beam lithography. For an effective transfer of the ink molecules to the substrate, often low modulus polymer materials, such as PDMS (polydimethylsiloxanes) are used for the stamp. There are, however, in principle no restrictions with respect to the stamp material.
U.S. Pat. No. 5,512,131 describes a method of patterning a material surface in which an elastomeric stamp having a stamping surface is loaded with a SAM forming species having a functional group selected to bind to a particular material, and the stamping surface is placed against a surface of the material and is removed to leave a SAM of the species according to the stamping surface pattern of the stamp. Additional stamping steps may be subsequently effected to produce any of a variety of SAM patterns on the surface. Additionally, portions of the material surface that are not coated with a stamped SAM pattern may be filled in with another SAM-forming species. Alternatively, portions that are not covered by a SAM layer may be etched or plated.
Patterning of a surface is also disclosed in EP-B-0 784 543, which describes a process for producing lithographic features in a substrate layer, comprising the steps of lowering a stamp carrying a reactant onto a substrate, confining the subsequent reaction to the desired pattern, lifting the stamp and removing the debris of the reaction from the substrate. The stamp may carry the pattern to be etched or depressions corresponding to the pattern.
Thus, microcontact printing is a soft lithographic patterning technique that has the inherent potential for the easy, fast and cheap reproduction of structured surfaces and electronic circuits with medium to high resolution.
The four main steps of a microcontact process are (with reference to
As explained above, printing of higher alkanethiols as ink molecules onto gold and other metal surfaces was one of the first techniques developed for SAMs of deprotonated thiolates on the surface resembling the pattern of the stamp.
The driving force for the formation of the SAM is the strong interaction of the polar thiolate head groups with the gold atoms (or atoms of other metals) in the uppermost surface layer, on the one hand, and the intermolecular (hydrophobic) van der Waals interaction between the apolar tail groups in the SAM, on the other hand. The combination of these two interactions resulted in a well ordered SAM of high stability against mechanical, physical or chemical attack.
It is known that the thiol molecules of ink solutions bind to the metal surface of the substrate during microcontact printing in their deprotonated form, as thiolates:
RSH→RS−+H+ (1)
At the same time, oxidation of the gold surface atoms occurs:
[M]surface+→[M(+)]surface+e− (2)
to allow formation of a strong bond between a sulphide group and a positively charged gold species in the uppermost metal layer:
RS−+[M(+)]surface→RS(−)−[M(+)]surface (3)
The oxidizing species that takes up the electron released by the metal surface is the hydrogen ion that disassociates from the alkanethiol (equations 1 and 2):
H++e−→½H2(↑) (4)
Combination of equations 1 to 4 results in the overall reaction:
RSH+[M]surface→RS(−)−[M(+)]surface+½H2(↑) (5)
The above prior art reaction scheme is further illustrated in
An identical mechanism can be formulated for other sulphur-functionalised molecular species that have been used as ink molecules for microcontact printing, such as thio- or dithiocarboxylic acids (RCSOH, RCS2H) and sulfinic acids (RSO2H), all of them bearing an S—H terminal functional group.
In fact, various ink molecules are in wide-spread use in the field of microcontact printing, such as alkanethiols (RSH), dialkyldisulfides (RSSR), dialkylsulfides (R2S) and multi-functional alkanethiols (X(—R—SH)n, n=1-6). Recently proposed ink molecules for printing on noble metal surfaces are 2-mono- and 2,2di-substituted propane-1,3dithiols (R1R2C((CH2)SH)2), thiocarboxylic acids (RCOSH) and dithiocarboxylic acids (RCS2H). For example, International Patent Application No. WO 02/071151 A1 describes a method of microcontact printing in which a dithiocarboxylic acid is used as the ink molecule in the formation of a SAM. In all these cases, it is the formal reduction of protons and the release of dihydrogen that are necessary to counterbalance the surface oxidation during the adsorption process.
One problem, however, in the application of microcontact printing to the patterning of metals is the limited number of suitable classes of ink molecules that are currently available and also the stability of these currently available inks during storage. This allows only limited variability in the development of tailor-made microcontact printing technologies, in particular as low shelf life times of ink solutions can hamper the applicability of these inks.
We have now devised an improved arrangement, and in a particular preferred embodiment the present invention can provide improved ink compositions for microcontact printing, which alleviates the problems associated with prior art ink compositions as discussed above.
There is provided by the present invention, therefore, a method of forming a SAM on at least one surface of a substrate by application to said surface of a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane so as to form a SAM prepared therefrom on said surface.
More particularly, there is provided by the present invention a method of forming a SAM on at least one surface of a substrate by application to said surface of a compound of formula (I) so as to form a SAM prepared therefrom on said surface
where X can represent either
or
wherein
one of R1 and R2 can represent hydrogen and at least one of R1 and R2 independently represents a hydrocarbon or halogenated hydrocarbon containing group, optionally provided with a selected functionality that can bind a selected biological or chemical species, or at least one of R1 and R2 can comprise a selected biological or chemical species directly or indirectly attached to the 1,3-dithiacyclopentane ring of a compound of formula (I), which selected biological or chemical species is such as to be suitable for immobilization to said surface further to binding of the 1,3-dithiacyclopentane ring, or a derivative thereof, to said surface; and
R3, R4, R5 and R6, are selected from the group consisting of hydrogen, halogen, —Ra, —ORa, —SRa, —NRaRb, wherein Ra and Rb can independently represent hydrocarbon which includes straight chained, branched and cyclic aliphatic and aromatic groups; or (i) R3 and R4, and/or (ii) R5 and R6, together respectively represent ═O.
The term hydrocarbon as used herein can denote straight-chained, branched and cyclic aliphatic and aromatic groups, and can typically include alkyl, alkenyl, alkynyl, cycloalkyl, cycloalkylalkyl, aryl, arylalkyl, arylalkenyl and arylalkynyl. The term “hydrocarbon containing group” also allows for the presence of atoms other than carbon and hydrogen, typically for example, oxygen and/or nitrogen. For example, one or more methylene oxide, or ethylene oxide, moieties may be present in the hydrocarbon containing group; alkylated amino groups may also be useful.
According to a first preferred embodiment of the present invention, X represents
and as such a method according to the present invention employs compounds of formula (Ia)
where R1 to R6 are substantially as hereinbefore defined.
According to a second preferred embodiment of the present invention, X represents
and as such a method according to the present invention employs compounds of formula (Ib)
again where R1 to R6 are substantially as hereinbefore defined.
Suitably, R1 represents hydrogen and R2 represents a hydrocarbon or halogenated hydrocarbon containing group. The term hydrocarbon as explained above can denote straight-chained, branched and cyclic aliphatic and aromatic groups, and can typically include alkyl, alkenyl, alkynyl, cycloalkyl, cycloalkylalkyl, aryl, arylalkyl, arylalkenyl and arylalkynyl. Suitably, the hydrocarbon groups can contain up to 35 carbon atoms, typically up to 30 carbon atoms, and more typically up to 20 carbon atoms. Corresponding halogenated hydrocarbons can also be employed, especially fluorinated hydrocarbons. In a preferred case where R2 represents a fluorinated alkyl group, this can be represented by the general formula F(CF2)k(CH2)l, where k is typically an integer having a value between 1 and 30 and l is an integer having a value of between 0 and 6. More preferably, k is an integer of between 5 and 20, and particularly between 8 and 18. It is of course recognized that although the above are given as preferred ranges for the values of k and l, the particular choice of k and l will depend on the purpose to which the surface to be treated is to be put. It will also be appreciated that the term “hydrocarbon containing group” also allows for the presence of atoms other than carbon and hydrogen, typically O or N, as explained above.
The above hydrocarbon groups can also be further substituted by substituents well known in the art, such as C1-6alkyl, phenyl, C1-6haloalkyl, hydroxy, C1-6alkoxy, C1-6alkoxyalkyl, C1-6alkoxyC1-6alkoxy, aryloxy, keto, C2-6alkoxycarbonyl, C2-6alkoxycarbonylC1-6alkyl, C2-6alkylcarbonyloxy, arylcarbonyloxy, arylcarbonyl, amino, mono- or di-(C1-6)alkylamino, or any other suitable substituents known in the art. In particular, for example in the case where R1 represent hydrogen and R2 represents phenyl, this phenyl group can be further substituted by phenylcarbonyloxy where the phenyl group of the above substituent may itself be further substituted by an alkyl group or other suitable substituent.
Preferred dithiacyclopentanes for use according to the present invention can be where R1 represents hydrogen and R2 represents alkyl, or aryl, which in turn may be further substituted, for example, by an arylcarbonyloxy substituent as referred to above. In a preferred embodiment, R1 represents hydrogen and R2 represents an alkyl group of up to 30 carbon atoms, and more typically up to 20 carbon atoms, and more preferably R2 represents —(CH2)16CH3. In an alternative preferred embodiment, R1 represent hydrogen and R2 represents phenyl, which may be further substituted by (alkyl substituted) phenylcarbonyloxy-, and more preferably R2 can represent the following substituent
In a further preferred embodiment of the present invention, it can be preferred that R1 represents hydrogen and R2 represents a hydrocarbon or halogenated hydrocarbon containing group, provided with a selected functionality that can bind a selected biological or chemical species. Suitably, a selected functionality is provided whereby one or more polymers, dendrimers or biomolecules can be bound by the 1,3-dithiacyclopentanes employed according to the present invention and thus be adsorbed onto the surface of a substrate. In particular, the present invention can allow biomolecules to be adsorbed onto the surface of a metal substrate, such as a coinage metal, such as gold, by binding of such biomolecules to 1,3-dithiacyclopentanes as employed in the present invention. Biomolecules that can be bound to a metal surface according to the present invention can include, for example, proteins, nucleic acids, antibodies, sugars, other carbohydrates and the like. Suitably, one of R1 or R2 can be provided with an amino acid functionality so as to facilitate binding of one or more biomolecules to a selected substrate, and suitably one of R1 or R2 can represent the following substituent
where X can represent a hydrocarbon containing group as hereinbefore described for R1 or R2, and more preferably can represent an alkylene linker, such as —(CH2)m—, where m is typically 1 to 6, or arylene linker, such as —(CH2)n(p-C6H4)(CH2)o—, where n and o can independently represent an integer of 0 to 3.
Alternatively, at least one of R1 and R2 can comprise a selected biological or chemical species directly or indirectly attached to the 1,3-dithiacyclopentane ring of a compound of formula (I), which selected biological or chemical species is such as to be suitable for immobilization to said surface further to binding of the 1,3-dithiacyclopentane ring, or a derivative thereof, to said surface. As such, the dithiacyclopentane functionality is inherent in the structure of the biological or chemical species to be immobilized, with the biological or chemical species either directly attached to the 1,3-dithiacyclopentane ring or indirectly attached thereto, for example by a hydrocarbon or halogenated hydrocarbon containing group substantially as hereinbefore described. For example, a selected peptide or protein could be modified to bear an amino acid as represented by the above formula and as such this could be present as a part of the polypeptide backbone. A “derivative” of the 1,3-dithiacyclopentane ring as referred to above for binding to the substrate surface can typically comprise an intermediate open chain structure obtained further to a redox reaction with the substrate surface (typically a metal), which can be further illustrated by reference to equations (6) and (7) and also FIGS. 3 to 7.
As referred to above, R3, R4, R5 and R6, are selected from the group consisting of hydrogen, halogen, —Ra, —ORa, —SRa, —NRaRb, wherein Ra and Rb can independently represent a hydrocarbon which includes straight chained, branched and cyclic aliphatic and aromatic groups; or (i) R3 and R4, and/or (ii) R5 and R6, together respectively represent ═O. More suitably, R3, R4, R5 and R6, are selected from the group consisting of hydrogen, fluoro, chloro, —Rc, —ORc, —SRc and —NRcRd, where Rc and Rd can represent C1-6alkyl or C2-6alkenyl. Each of R3, R4, R5 and R6, can, therefore, represent hydrogen. Alternatively, each of R3, R4, R5 and R6, can represent halogen, in particular fluoro. A further alternative is where R3 and R4 together represent ═O, and R5 and R6 together represent ═O, whereby the compounds for use according to the present invention include 1,3-dithiolane-4,5-diones.
It will be appreciated from the above that various combinations of the above described substituents X, and R1 to R6, may be employed in 1,3-dithiacyclopentanes according to the present invention, and as such bind to a metal substrate. For example, for substituents R1 and R2, these may be directly bound to the 1,3-dithiacyclopentane ring and binding of such 1,3-dithiacyclopentanes to a metal substrate as achieved by a method according to the present invention can be, for example, as illustrated in
For substituents R3 to R6, it may be preferred that each of R3 to R6 represents hydrogen substantially as hereinbefore described, as for example, specifically illustrated by
Specific 1,3-dithiacyclopentanes for use in methods according to the present invention include the following
It will be appreciated that certain 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentanes employed in a method according to the present invention are known compounds. However, certain 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentanes are novel per se and as such form a further aspect of the present invention. More particularly, the present invention further provides a compound of formula (Ic) (which is a subgroup of compounds of formula (Ia)
where R1c represents hydrogen, R2c represents C16-25alkyl and R3, R4, R5 and R6 are substantially as hereinbefore described. A particularly preferred compounds as provided by the present invention is
Typically a method according to the present invention can comprise providing a first SAM on a surface of a substrate by application of a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane substantially as hereinbefore described, and further providing a second material to the substrate. The second material can be provided as a SAM selectively formed in areas of the substrate surface substantially uncovered by the first SAM. The 1,3-dithiacyclopentane of the first SAM can be chemically distinct from the molecular species of the second SAM. For example, the first SAM may comprise a hydrophilic monolayer whereas the second SAM may comprise a hydrophobic monolayer. Alternatively, the second material can be a metal or other material, selectively applied to areas of the substrate surface substantially resembling the pattern of the first SAM, with suitable application techniques including electroless deposition of a metal from solution and other suitable techniques known in the art.
SAMs provided according to the present invention can be formed by suitable techniques known in the art, for example by adsorption from solution; or from a gas phase, or may be applied by use of a stamping step employing a flat unstructured stamp or may be applied by a microcontact printing technique which is generally preferred for the provision of at least a first SAM as referred to above.
A preferred embodiment of the invention, therefore, is directed to the provision of a SAM by microcontact printing and there is provided by the present invention, therefore, a method of microcontact printing, comprising printing a pattern on a surface of a substrate, where the pattern includes exposed regions and SAM protected regions, wherein the SAM is formed by application to at least one surface of the substrate of a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane, wherein the substituent at the 2 position facilitates formation of the SAM on the substrate.
Preferably, a method according to the present invention comprises providing a patterned stamp defining the required pattern of said patterned layer; and bringing a patterned stamp loaded with an ink into contact with the surface of said substrate, said patterned stamp being arranged to deliver said ink to the contacted areas of the surface of said substrate; wherein said ink comprises a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane, wherein the substituent at the 2 position facilitates formation of the SAM on the substrate.
The proposed new inks for use in a method according to the present invention have the effect of improving the binding process of sulphur-containing species to metal surfaces. In the case where the leaving molecule is ethylene as illustrated in
R1R2C(SCH2)2+2[M]surface→R1R2C(S(−)−[M(+)]surface)2+CH2═CH2(↑) (6)
In this case, the 1,2-ethylene group inherent in the dithiolane molecule is the oxidising species:
RS—CH2—CH2—SR+2e−→CH2═CH2(↑)+2RS− (7)
Since the released ethylene product is a less strong reductant than dihydrogen, the oxidation of the metal surface is easier and the formation of a respective monolayer occurs more readily.
1,3-dithiacyclopentanes as employed according to the present invention also provide improved stability of the formed monolayer because the ink molecule may form two possible bonds with the supporting metal surface (see FIGS. 3 to 7) instead of only one in the case of the simple alkanethiols of the prior art (see
A further disadvantage associated with the standard alkanethiol ink solutions of the prior art is that such solutions are known to be very unstable against air oxidation due to the oxidation sensitivity of the thiol head groups, causing slow decomposition of these solutions and the formation of insoluble solids.
Once such decomposition has occurred, the solutions are no longer usable. Thus, it is a significant advantage of 1,3-dithiacyclopentanes employed according to the present invention, in that they provide a significantly increased stability against air oxidation.
Typically, a stamp employed in a method according to the present invention includes at least one indentation, or relief pattern, contiguous with a stamping surface defining a first stamping pattern. The stamp can be formed from a polymeric material. Polymeric materials suitable for use in fabrication of a stamp include linear or branched backbones, and may be crosslinked or noncrosslinked, depending on the particular polymer and the degree of formability desired of the stamp. A variety of elastomeric polymeric materials are suitable for such fabrication, especially polymers of the general class of silicone polymers, epoxy polymers and acrylate polymers. Examples of silicone elastomers suitable for use as a stamp include the chlorosilanes. A particularly preferred silicone elastomer is polydimethylsiloxane.
A substrate on which is printed a pattern by use of a method according to the present invention typically comprises a metal substrate, or at least a surface of the substrate on which the pattern is printed comprises a metal, which can suitably be selected from the group consisting of gold, silver, copper, cadmium, zinc, palladium, platinum, mercury, lead, iron, chromium, manganese, tungsten and any alloys of the above. Preferably the substrate, or at least a surface of the substrate on which the pattern is printed, comprises gold.
The present invention also comprises an ink composition for use in microcontact printing, wherein the composition comprises a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane, wherein the substituent at the 2 position facilitates formation of the SAM on a substrate substantially as hereinbefore described, together with a solvent suitable for dissolving the 1,3-dithiacyclopentane.
Suitably, the concentration of 1,3-dithiacyclopentane in a solvent of a composition as provided by the present invention should be selected so as to be low enough that the 1,3-dithiacyclopentane is well-absorbed into a stamping surface of a selected stamp, and high enough that a well defined SAM may be transferred to a substrate surface without blurring. Typically, a 1,3-dithiacyclopentane will be transferred to a stamping surface in a solvent at a concentration of less than 100 mM, preferably from about 1.0 to 10.0 mM. Any organic solvent within which a 1,3-dithiacyclopentane suitable for use according to the present invention dissolves and which may be absorbed by a stamping surface is suitable. In such selection, if the stamping surface employed is relatively polar, then a relatively polar and/or protic solvent may be advantageously chosen. If a stamping surface employed is relatively non-polar, a relatively non-polar solvent may advantageously be chosen. For example, toluene, ethanol, THF, acetone, isooctane, diethylether and the like may be employed. When a siloxane polymer is selected for fabrication of a stamp for use in a method according to the present invention, and in particular a stamping surface thereof, ethanol is a preferred solvent.
The present invention also provides use of a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane, wherein the substituent at the 2 position facilitates formation of the SAM on a substrate substantially as hereinbefore described, as an ink for use in microcontact printing.
The present invention also provides use of a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane, wherein the substituent at the 2 position facilitates formation of the SAM on a substrate substantially as hereinbefore described, in the manufacture of an ink composition for use in microcontact printing, which use comprises dissolving said 1,3-dithiacyclopentane in a solvent suitable for transferring said 1,3-dithiacyclopentane to a stamping surface. A suitable solvent is substantially as hereinbefore described.
The present invention also provides a method of preparing an ink composition for use in microcontact printing, which method comprises dissolving a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane, wherein the substituent at the 2 position facilitates formation of the SAM on a substrate substantially as hereinbefore described, in a solvent suitable for transferring said 1,3-dithiacyclopentane to a stamping surface. A suitable solvent is again substantially as hereinbefore described.
There is also provided a kit for use in microcontact printing, which kit comprises an ink composition substantially as herein before described; a stamp substantially as hereinbefore described for transferring said 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane of said ink composition to a substrate; and a substrate substantially as hereinbefore described suitable for receiving said 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane of said ink composition from said stamp.
The present invention still further provides a patterned substrate prepared in accordance with techniques substantially as hereinbefore described. More particularly, the pattern is applied by contacting the substrate with an ink composition comprising a 1,3-dithiacyclopentane substantially as hereinbefore described. The present invention, therefore, provides a substrate provided with a pattern on at least one surface thereof, wherein the pattern includes exposed regions and SAM protected regions, wherein the SAM is formed by application to the surface of a 2-mono-, or 2,2-disubstituted 1,3-dithiacyclopentane, wherein the substituent at the 2 position facilitates formation of the SAM on the substrate substantially as hereinbefore described.
SAM protected regions of a substrate provided according to the present invention desirably exhibit a high stability against etching solutions, and as such exhibit applicability as an etch resist. There is also provided by the present invention a method of etching a substrate, which method comprises providing a SAM to a substrate substantially as hereinbefore described, and subsequently contacting the thus patterned substrate with an etching solution so as to achieve etching in the exposed regions of the substrate not protected by the previously applied SAM. The patterned substrates as provided by the present invention also exhibit applicability in the immobilization of selected chemical and biological materials to the substrate, and as such may also find applicability for use in biochip arrays and biosensors.
1,3-Dithiolanes as employed according to the present invention are typically synthesized through the reaction of carbonyl compounds (aldehydes or ketones) with 1,2-ethanedithiol (1,2-dimercaptoethane) or derivatives thereof, as, for instance, described in U.S. Pat. No. 4,075,228, U.S. Pat. No. 4,096,155, U.S. Pat. No. 4,125,539, or J. March “Advanced Organic Chemistry”, 4th Ed., John Wiley & Soris, New York (1992), pp 893-895.
The present invention will now be further illustrated by the following Figures and Experimental, which do not limit the scope of the invention in any way.
Experimental
Benzoic acid 4-methyl-4-(1,3-dithiolan-2-yl-)phenyl ester was purchased from the following company: SPECS and BIOSPECS B.V., Fleminglaan 16, Rijswijk 2289 CP, The Netherlands.
Commercially available 1-octadecanol with pyridinium chlorochromate gave 1-octadecanal as described in the following experimental. Treatment with 1,2-ethanedithiol then yielded the desired product, 2-heptadecyl-1,3-dithiolane.
A lukewarm solution of octadecanol (33.0 g, 0.122 mol) in 300 mL dichloromethane was added over a few minutes to a mixture of pyridinium chlorochromate (40.0 g, 0.186 mol) and 150 mL dichloromethane. The mixture was stirred for 2 h at RT, then 400 mL heptane was added. After stirring for 10 minutes the solution was decanted from the solid and chromatographed on 150 g silicagel using the dichloromethane/heptane mixture as the eluent. The colorless eluate was rotary evaporated to give the aldehyde as a solidifying oil. NMR (CDCl3): δ 0.9 (t, 3H), 1.2-1.5 (m, 28H), 1.7 (m, 2H), 2.45 (m, 2H), 9.8 (t, 1H).
The aldehyde obtained above was stirred for 2 h with 300 mL dichloromethane, 20 mL 1,2-ethanedithiol, and 2 mL BF3-etherate. Most of the solvent was removed by rotary evaporation and to the residue there was added heptane containing a little toluene. Chromotography over 100 g silicagel using heptane (with a little toluene) as the eluent gave the crude product which was purified by Kugelrohr distillation (this left a higher boiling impurity behind), followed by recrystallization from 200 mL heptane to give the product (34.04 g, 98.95 mmol, 81% overall yield). NMR (CDCl3): δ 0.95 (t, 3H), 1.1-1.6 (m, 30H), 1.9 (m, 2H), 3.3 (m, 4H), 4.55 (t, 1H).
Printing Process
Substrates were regular silicium wafers with an about 500 nm thick layer of silicium oxide (thermal oxide). On top of this a 2.5 nm thick layer of titanium was sputtered followed by a 17.5 nm thick gold layer. The uppermost gold surface was rinsed with water, ethanol, and n-heptane and treated with an argon plasma (0.25 mbar, 300 W) for 5 min prior to printing.
A regular poly(dimethylsiloxane) (PDMS) stamp with a size of about 1×2 cm2 was used. It was inked with the ink solution at least one hour before printing. This means, that the stamp was immersed in a respective ink solution and stored therein for one hour. The ink solution was a clear and colorless, 2 millimolar solution of 2-heptadecyl-1,3-dithiolane in ethanol. Immediately prior to printing the stamp was taken out of the ink solution and thoroughly rinsed with ethanol to remove all excess ink solution and subsequently dried in a stream of nitrogen for about one minute to remove all ethanol from the surface and from the topmost layer of the stamp material.
The so prepared stamp was brought in contact with the cleaned substrate. Intimate contact over the entire surface was assured by optical inspection. The stamp was removed again after 15 seconds.
Subsequently the printed substrates were developed by wet chemical etching. Thus the monolayer was transferred in the printing step so as to provide a resist, protecting the underlaying gold layer in the printed regions, but allowing undisturbed etching in the not printed regions. Etching was performed by immersing the printed substrates in an etching solution comprising potassium hydroxide (1.0M), potassium thiosulfate (0.1M), potassium ferricyanide (0.01M), potassium ferrocyanide (0.001M), water as the solvent and 1-octanol at half saturation at room temperature without special precautions. It was removed after all the gold was etched away in the not protected regions and a clear pattern was visible. The time necessary was about 7 minutes in the indicated etching solution.
A substrate with a top gold layer as described above was prepared for patterning according to the described procedure.
A PDMS stamp was inked and employed for stamping onto the substrate as described in Example 1, except that a 2 mM solution of benzoic acid 4-methyl-4-(1,3-dithiolan-2-yl-)phenyl ester in ethanol was used as the ink.
Subsequently the substrate was etched at room temperature in a solution containing potassium hydroxide (1.0M), potassium thiosulfate (0.1M), potassium ferricyanide (0.01M), and potassium ferrocyanide (0.001M) for 7 minutes to develop a clear pattern in the gold layer as described in Example 1.
A substrate with a top gold layer as described in Example 1 was prepared for patterning according to the described procedure.
A PDMS stamp was inked with a 2 mM solution of benzoic acid 4-methyl-4-(1,3-dithiolan-2-yl-)phenyl ester in ethanol and further washed and dried as described in Example 1.
The substrate was printed with the so prepared stamp as described before. Development of the pattern was performed via wet chemical etching in an aqueous etching bath of the following composition: 1.0M thiourea, 0.01M ferric sulfate, and 0.01M sulphuric acid. A clear pattern was obtained after an etching time of about 80 seconds at room temperature.
Substrates (1×2 cm2) with a composition as described in Example 1 were cleaned according to the procedure described above.
A solution of 2-heptadecyl-1,3-dithiolane in ethanol (2 mM) was prepared. The cleaned substrates were immersed in this solution half way, thus one half of the substrates was in contact with the solution and the other half remained outside the solution in the ambient. The substrates were again removed after 30 minutes, washed with ethanol and dried in a stream of nitrogen.
Subsequently the substrates were fully immersed at room temperature in a freshly prepared etching solution containing potassium hydroxide (1.0M), potassium thiosulfate (0.1M), potassium ferricyanide (0.01M), potassium ferrocyanide (0.001M), and n-octanol at half saturation. Samples were again removed from the etching solution after 9, 20, 45, or 80 minutes. In all cases a clear contrast was observed between the two halves of the substrates. The gold layer was completely etched away in the areas that had not been in contact with the dithiolane solution and was virtually unchanged in those areas that had been in contact with the dithiolane solution.
Inspection of the samples by optical microscopy revealed no difference between the sample that had been etched for 10, 20, and 45 minutes. The samples etched for 80 minutes showed some local microscopic defects, indicating a beginning breakdown of the protective self-assembled monolayer.
It should be noted that the above-mentioned embodiments illustrate rather than limit the invention, and that those skilled in the art will be capable: of designing many alternative embodiments without departing from the scope of the invention as defined by the appended claims. In the claims, any reference signs placed in parentheses shall not be construed as limiting the claims. The word “comprising” and “comprises”, and the like, does not exclude the presence of elements or steps other than those listed in any claim or the specification as a whole. The singular reference of an element does not exclude the plural reference of such elements and vice-versa. The invention may be implemented by means of hardware comprising several distinct elements, and by means of a suitably programmed computer. In a device claim enumerating several means, several of these means may be embodied by one and the same item of hardware. The mere fact that certain measures are recited in mutually different dependent claims does not indicate that a combination of these measures cannot be used to advantage.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0326904.0 | Nov 2003 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB04/52448 | 11/16/2004 | WO | 5/18/2006 |
