The present invention relates to a gamma radiation source containing 75Se, and in particular to a source for use in gamma radiography. Such a source has application, for example, in nondestructive testing, industrial gauging, densitometry and materials analysis in industry, research and medicine.
In the past, 75Se sources have been made by encapsulating elemental 74Se target material inside a welded metal target capsule. This is irradiated in a high flux reactor to convert some of the 74Se to 75Se. Typically, target capsules are made of low-activating metals, such as aluminum, titanium, vanadium and their alloys. Other expensive metals and alloys are also possible. The use of these metals ensures that impurity gamma rays arising from the activation of the target capsule are minimized. The 75Se is typically located within a cylindrical cavity inside the target capsule in the form of a pressed pellet or cast bead. To achieve good performance in radiography applications it is necessary for the focal spot size to be as small as possible and the activity to be as high as possible. This is achieved by irradiating in a very high neutron flux and by using very highly isotopically enriched 74Se target material, typically >95% enrichment.
After the irradiation, the activated target capsule is welded into one or more outer metal capsules to provide a leak-free source, which is free from external radioactive contamination.
Elemental selenium is chemically and physically volatile. It melts at 220° C. and boils at 680° C. It reacts with many metals, which might be suitable as low-activating capsule materials at temperatures above about 400° C., this includes titanium, vanadium and aluminum and their alloys. Selenium may react explosively with aluminum. This means that careful choice of target capsule material is required and the temperature of the target capsule during irradiation must be kept below about 400° C. to prevent the selenium reacting with, and corroding the target capsule wall. If this occurred, it would increase the focal spot size, distort the focal spot shape and reduce the wall thickness and strength of the target capsule.
An object of the present invention is to provide a source having a selenium target composition, which overcomes or ameliorates one or more of the problems associated with the use of elemental selenium, specifically the problems of achieving a thermally stable, non-volatile, non-reactive, high density, stable selenium target which nevertheless contains a very high density of selenium, comparable with the elemental form of the material.
The invention provides; in one of its aspects, a gamma radiation source comprising selenium-75 or a precursor therefore, wherein the selenium is provided in the form of one or more thermally stable compounds, alloys, or mixed metal phases with one or more metals (hereinafter referred to as acceptable metals or an acceptable metal) the neutron irradiation of which does not produce products capable of sustained emission of radiation which would unacceptably interfere with the gamma radiation of selenium-75.
Thus, for example, an acceptable metal, such as vanadium or rhodium, is activated but has no interfering gamma radiation. Molybdenum produces molybdenum-99 which does have interfering gamma radiation, but is very short lived and is therefore also an acceptable metal. Again, Thorium produces palladium-233 having a 27 day half life, but the gamma radiation of palladium-233 is 300-340 KeV which is very similar to selenium-75 and therefore acceptable.
Preferably, the said acceptable metal or metals is from the group comprising vanadium, molybdenum, rhodium, niobium, thorium, titanium, nickel, lead, bismuth, platinum, palladium, aluminum, or mixtures thereof. More preferably, the said acceptable metal or metals comprises one or a mixture of vanadium or molybdenum or rhodium.
Preferably, the selenium is provided in the form of a pellet or bead of a compound of formula MxSey where y/x is in the range 1-3 and M is one or a mixture of two or more of the said acceptable metals.
The preferred range for y/x is 1.5-2.5. More preferably, y/x is 2.
Preferably, the pellet or bead comprises VSe2 or MoSe2 or Rh2Se5.
Conveniently, elemental selenium is included in intimate admixture with the said compound, alloy or mixed metal phase to act as a binder therefore, in particular to facilitate formation of a dense, pore free pellet or bead.
For the safe containment of the active constituents, the pellet or bead is contained within a sealed, welded, metal capsule
Preferably, the pellet or bead is formed to have a spherical or pseudo-spherical focal spot geometry.
The invention provides, in another of its aspects, a method of manufacturing a gamma radiation source comprising mixing selenium-74 and one or a mixture of metals from the group comprising vanadium, molybdenum, rhodium, niobium, thorium, titanium, nickel, lead, bismuth, platinum, palladium, aluminum, in appropriate proportions for the desired product compound, and heating the mixture to cause the constituents to inter-react and subsequently subjecting the reaction product to irradiation to convert at least a proportion of the selenium-74 to selenium-75.
A specific method and construction of a gamma radiation source embodying the invention will now be described by way of example with reference to the drawings filed herewith, in which:
Referring to
The modified assembly shown in
The pellet composition is a metal selenide compound (in which part or all may be regarded as an intimate mixture of metal particles and elemental selenium) having the composition MxSey in which M is an acceptable metal, which minimizes unwanted impurity gamma rays. Examples of suitable acceptable metals include, but are not limited to vanadium, molybdenum, rhodium, niobium, thorium, titanium, nickel, lead, bismuth, platinum, palladium, aluminum. The most preferred metals are molybdenum, vanadium and rhodium which produce especially dense metal-selenium phases, which are rich in selenium. “x” and “y” in the chemical formula can have any values depending on the valence state of the metal, but the highest selenium density is achieved when the ratio of y/x is in the range 1-3, more preferably 1.5-2.5, most preferably 2. Examples of suitable metal-selenium target materials are as follows:
Metal-selenium pellet compositions can be prepared by a variety of methods. The method found to be most convenient, which gives rise to minimal process losses is to weigh out and mix a known quantity of enriched 74Se powder with a calculated quantity of powdered metal, and to heat the mixture in an inert, sealed container, such as a flame sealed glass ampoule, gradually increasing the temperature over several hours to the reaction temperature and then holding that temperature for several more hours. For example, the reaction temperature for the reaction between 74Se powder and vanadium powder is in the range 450° C.-550° C. In a specific example, a mixture of vanadium and selenium powders in the ratio one part vanadium to 1.9 parts enriched selenium-74 was heated in an evacuated flame sealed quartz ampoule, first at 550C. for 4 hours and then at 800C. for 100 hours. The product VSe.19 was pressed into half octagonal section pellets 11a and 11b of the form shown in FIG. 4.
Cylindrical pellets or beads can be prepared by several methods. For example, powder can be cold-pressed, hot-pressed or sintered to form cylindrical, spherical or pseudo-spherical geometries. These can be inserted into the target capsule, or cast or pressed in-situ. The capsule is then welded and leak tested prior to irradiation. Metal-selenium pellet compositions may consist of a pure metal selenide compound such as VSe2, or a mixture of compounds such as VSe2, MoSe2, MoSe3, or more complex phases obtained by reacting such mixtures together at high temperature. The composition may contain some metal powder and elemental selenium. Excess elemental selenium may be purposefully added as a bonding agent to bond metal selenide particles together to form pore free, high density pellets or beads. Pellets, which are made of mixtures, such as VSe2+VSe+Se, or MoSe2+MoSe3+Se may react or sinter together within the target capsule, either during a special annealing process prior to irradiation, or during the irradiation itself, as follows:
VSe+Se=VSe2 and MoSe2+Se=MoSe3
One advantage of using metal selenide phases is that the thermal and physical stability of the materials enables unencapsulated pellets and beads to be irradiated, in-principle. This can provide significant cost advantages by reducing the amount of reactor space, which is wasted by the presence of the low activating target capsules.
The invention is not restricted to the details of the foregoing examples.
| Number | Date | Country | Kind |
|---|---|---|---|
| 9909531 | Apr 1999 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCTGB00/01549 | 4/20/2000 | WO | 00 | 10/22/2001 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO0065608 | 11/2/2000 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3655348 | Bither, Jr. | Apr 1972 | A |
| 3791867 | Broadhead et al. | Feb 1974 | A |
| 3952030 | Chambers et al. | Apr 1976 | A |
| 4030886 | Bayly et al. | Jun 1977 | A |
| 4202976 | Bayly et al. | May 1980 | A |
| 4647386 | Jamison | Mar 1987 | A |
| 4654281 | Anderman et al. | Mar 1987 | A |
| 4738318 | Boettcher et al. | Apr 1988 | A |
| Number | Date | Country |
|---|---|---|
| WO 9424546 | Oct 1994 | WO |