Patent Application
20100151612
1. Field of the Invention
The present invention relates to a method for producing a semiconductor device which method includes growing an n-layer and a p-layer of a group III-V semiconductor on a growth substrate, bonding an electrode layer on the p-layer to a support substrate by use of solder, and removing the growth substrate through the laser lift-off process; and to a semiconductor device produced through the method. More particularly, the present invention relates to a method for producing a semiconductor device so as to prevent short circuit between side surfaces of a p-layer and an n-layer, and to a semiconductor device structure produced through the method.
2. Background Art
In general, sapphire, which is chemically and thermally stable, has been employed as a substrate for the growth of a group III nitride semiconductor. However, since sapphire has no electrical conductivity, current cannot flow in a vertical direction of a semiconductor stacked structure including a sapphire substrate. Furthermore, sapphire has no clear cleavage plane, making dicing of a semiconductor structure on a sapphire substrate difficult. In addition, sapphire exhibits low thermal conductivity, and inhibits radiation of heat from a semiconductor device. In a semiconductor device including a semiconductor layer and a sapphire substrate, external quantum efficiency is low due to total reflection at the interface between the semiconductor layer and the substrate, or confinement of light in the semiconductor layer. Meanwhile, one conceivable technique for improving light extraction efficiency is forming irregularities on a light extraction surface. However, a sapphire substrate encounters difficulty in such a processing.
One technique known to solve such a problem is the laser lift-off process, which is used for separation and removal of a sapphire substrate through laser beam radiation.
Japanese Patent Application Laid-Open (kokai) No. 2005-333130 discloses a method in which a group 111 nitride semiconductor device is formed on a sapphire substrate; grooves are formed in the device through etching for separating the device region into chips; each chip is provided with electrodes; and each group III nitride semiconductor device grown on the sapphire substrate is bonded to a support substrate, followed by the laser lift-off process. Japanese Patent Application Laid-Open (kokai) No. 2005-333130 describes that cracking in the group III nitride semiconductor device—which would otherwise be caused by thermal expansion of gas remaining in the grooves through laser beam radiation—can be prevented by filling the grooves with a dielectric material for elimination of gas.
Japanese Kohyo Patent Publication No. 2005-522873 discloses a method in which grooves are filled with a photoresist; and, instead of bonding between a group III nitride semiconductor device and a support substrate, a metal layer is formed on the group III nitride semiconductor device, followed by the laser lift-off process. This patent document describes that grooves are filled with a photoresist for the purpose of preventing a metal from entering the grooves during formation of a layer of the metal.
Japanese Patent Application Laid-Open (kokai) No. 2006-135321 discloses a method in which a protective film of, for example, SiO2 or Al2O3, and a seed metal film are formed on inclined side surfaces of a semiconductor device; and a metal layer is formed on grooves and the semiconductor device, followed by the laser lift-off process.
Meanwhile, Japanese Patent Application Laid-Open (kokai) Nos. 2004-95640 and 2006-261179 disclose a semiconductor device having a high-resistance device-isolating area, which is formed through ion implantation into a Group III nitride semiconductor.
When the method disclosed in Japanese Kohyo Patent Publication No. 2005-522873 is employed, resist remains in a Group III nitride semiconductor light-emitting device after the lift-off process. Therefore, such a device may have poor reliability after a subsequent mounting step including a high-temperature treatment (e.g., reflowing).
The method disclosed in Japanese Patent Application Laid-Open (kokai) No. 2006-135321 poses a problem in that, since a sapphire substrate (growth substrate) and a protective film are strongly bonded to each other, exfoliation occurs in the protective film during separation of the sapphire substrate, leading to cracking in a semiconductor device. This method also poses a problem in that a metal layer formed on the semiconductor device must be cut during dicing.
In the method disclosed in Japanese Patent Application Laid-Open (kokai) No. 2005-333130, since electrodes are formed before the grooves are filled with a dielectric material, a metal element constituting the electrodes may be deposited on a side surface of a semiconductor device, resulting in current leakage or short circuit. In addition, the formed dielectric film may be mechanically damaged during the laser lift-off process.
In view of the foregoing, an object of the present invention is to realize a Group III-V semiconductor device of a new structure, which device is bonded to a conductive support substrate and in which current leakage or short circuit is prevented at a side surface of the device. Another object of the invention is to provide a method for producing the semiconductor device.
Accordingly, in a first aspect of the present invention, there is provided a Group III-V semiconductor device bonded to a conductive support substrate, which device has a side surface whose surface layer has a high-resistance region formed through ion implantation.
No particular limitation is imposed on the atomic species used in ion implantation, and any atoms may be implanted, so long as the atoms are difficult to electrically activate. Examples of such atoms include nitrogen, arsenic, and phosphorus. The implanted ion concentration of the high-resistance region is preferably 1×1018 to 1×1022/cm3. When the concentration is lower than 1×1018/cm3, high resistance cannot be attained, whereas when the concentration is higher than 1×1022/cm3, crystallinity of the semiconductor is excessively impaired. Needless to say, both cases are not preferred.
The support substrate and the semiconductor device may be bonded to each other by means of a low-melting-point metal layer formed of a eutectic metal layer (e.g., an Au—Sn layer, an Au—Si layer, an Ag—Sn—Cu layer, or an Sn—Bi layer); or by means of a non-solder layer of Au, Sn, or Cu (although such a metal is not a low-melting-point metal).
The support substrate is formed of a conductive substrate such as an Si substrate, a GaAs substrate, a Cu substrate, or a Cu—W substrate. The support substrate may be formed through directly plating a semiconductor device with a metal such as Cu.
A second aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to the first aspect, wherein the semiconductor device is bonded to the support substrate by means of a low-melting-point metal layer.
A third aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to the second aspect, wherein the low-melting-point metal layer comprises at least one selected from a group consisting of Au—Sn, Au—Si, Ag—Sn—Cu, and Sn—Bi.
A fourth aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to the first aspect, wherein the semiconductor device is bonded to the support substrate by means of a non-solder layer.
A fifth aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to the fourth aspect, wherein the non-solder layer comprises at least one selected from a group consisting of Au, Sn, and Cu.
A sixth aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to any of the first to fifth aspects, wherein the semiconductor device is formed into an inverted tapered structure in which the device has a cross-sectional area gradually decreasing toward the support substrate.
A seventh aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to any of the first to fifth aspects, wherein the semiconductor device has a p-electrode bonded to the support substrate, and the p-electrode is formed on the entire top surface of the support substrate.
The p-electrode is preferably made of a metal having high optical reflectance and low contact resistance; for example, Ag, Rh, Pt, Ru, or an alloy containing such a metal as a primary component. Alternatively, the p-electrode may be made of, for example, Ni, an Ni alloy, or an Au alloy; or may be formed of a composite layer including a transparent electrode film (e.g., ITO film) and a highly reflective metal film.
An eighth aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to any of the first to sixth aspects, wherein the semiconductor has a top surface whose surface layer has, at least in the vicinity of the side surface, a high-resistance region formed through ion implantation.
A ninth aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to any of the first to sixth aspects, wherein the semiconductor has a top surface having thereon, at least in the vicinity of the side surface, an insulating film formed of a dielectric material.
In the eighth and ninth aspects of the invention, the top surface of a semiconductor device refers to a surface of the semiconductor device opposite the surface which is bonded to the support substrate. When the semiconductor device is a Group III nitride semiconductor device, the top surface is generally an n-layer surface, which serves as a light extraction surface when the device is a light-emitting device. The expression “in the vicinity of a side surface” refers to a portion of the top surface extending from the side surface to the inside and having a width 5% to 10% the width of the top surface. The high-resistance region or insulating film may be formed on the entire top surface of the semiconductor device other than the electrode-forming region(s).
A tenth aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to any of the first to ninth aspects, wherein the support substrate is formed through plating.
An eleventh aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to any of the first to tenth aspects, wherein the semiconductor device is a Group III nitride semiconductor device.
A twelfth aspect of the present invention is drawn to a specific embodiment of the semiconductor device according to any of the first to eleventh aspects, wherein the semiconductor device is a light-emitting device.
In a thirteenth aspect of the present invention, there is provided a method for producing a Group III-V semiconductor device, the method comprising:
forming, on a base, a plurality of semiconductor devices isolated from one another;
forming, through ion implantation, a high-resistance region in a surface layer of a side surface of each semiconductor device;
after formation of the high-resistance region, forming a p-electrode and a low-melting-point metal diffusion prevention layer on the top surface of the semiconductor device;
bonding the semiconductor device to a conductive support substrate via a low-melting-point metal layer; and
removing the base through the laser lift-off process.
The low-melting-point metal diffusion prevention layer may be formed of, for example, a Ti/Ni-containing multi-layer film (e.g., Ti/Ni/Au film), or a W/Pt-containing multi-layer film (e.g., W/Pt/Au film), and is provided for preventing diffusion therethrough of a metal constituting the low-melting-point metal layer. The low-melting-point metal diffusion prevention layer also prevents diffusion of an electrode material such as a metal of high optical reflectance (e.g., Ag).
The step of forming a plurality of semiconductor devices isolated from one another does not mean that the semiconductor devices are isolated with a base, but means that the semiconductor layer is divided into semiconductor device regions which are on a non-isolated, single base. For example, a semiconductor layer is epitaxially grown on a base, and a predetermined region of the layer is dry-etched. The p-electrode and low-melting-point metal diffusion prevention layer may be formed through the lift-off process.
The ion implantation dose is preferably 1×1010 to 1×1018/cm2. When the dose falls within this range, the implanted ion concentration of the high-resistance region can be adjusted to 1×1018 to 1×1022/cm3.
In the laser-lift-off process, a base is irradiated with a laser beam, to thereby melt the bonding interface between the base and the semiconductor layer, followed by removing the base.
A fourteenth aspect of the present invention is drawn to a specific embodiment of the production method according to the thirteenth aspect, wherein the side surface of the semiconductor device is formed to be inclined so that the device has a cross-sectional area gradually increasing toward the base, and ion implantation is performed along a direction normal to the main plane of the base.
A fifteenth aspect of the present invention is drawn to a specific embodiment of the production method according to the thirteenth or fourteenth aspect, wherein ion implantation is performed along a direction normal to the main plane of the base at an acceleration voltage which allows the implanted ions to reach the base.
A sixteenth aspect of the present invention is drawn to a specific embodiment of the production method according to the thirteenth or fourteenth aspect, wherein the method includes, after removal of the base, performing ion implantation into a portion of the surface of the semiconductor device which surface has previously bonded to the base, the portion being in the vicinity of the side surface.
A seventeenth of the present invention is drawn to a specific embodiment of the production method according to the thirteenth or fourteenth aspect, wherein the method includes, after removal of the base, forming an n-electrode on the surface of the semiconductor device which surface has previously bonded to the base, and performing ion implantation into the surface of the semiconductor device through the n-electrode, which serves as a mask.
An eighteenth aspect of the present invention is drawn to a specific embodiment of the production method according to the thirteenth or fourteenth aspect, wherein the method includes, after removal of the base, forming a dielectric material insulating film on a portion of the surface of the semiconductor device which surface has previously bonded to the base, the portion being in the vicinity of the side surface.
In a nineteenth aspect of the present invention, there is provided a method for producing a Group III-V semiconductor device, the method comprising:
forming a Group III-V semiconductor layer on a base;
forming a high-resistance region in a surface layer of a predetermined portion of the top surface of the semiconductor layer through ion implantation at an acceleration voltage which allows the implanted ions to reach the base;
dividing the semiconductor layer, through the high-resistance region, into semiconductor devices isolated from one another;
after formation of the high-resistance region, forming a p-electrode and a low-melting-point metal diffusion prevention layer on the top surface of each semiconductor device;
bonding the semiconductor device to a conductive support substrate via a low-melting-point metal layer; and
removing the base through the laser lift-off process.
The p-electrode and low-melting-point metal diffusion prevention layer may be formed solely on the top surface of each semiconductor device, or may be formed on the entire semiconductor layer without being patterned.
A twentieth aspect of the present invention is drawn to a specific embodiment of the production method according to the fifteenth or nineteenth aspect, wherein ion implantation is performed at a plurality of times at different acceleration voltages.
In a twenty-first aspect of the present invention, there is provided a method for producing a Group III-V semiconductor device, the method comprising:
forming a Group III-V semiconductor layer on a base;
forming a first high-resistance region in a surface layer of a predetermined portion of the top surface of the semiconductor layer through ion implantation at an acceleration voltage which does not allow the implanted ions to reach the base;
after formation of the first high-resistance region, forming a p-electrode and a low-melting-point metal diffusion prevention layer on the top surface of the semiconductor layer;
bonding the semiconductor device to a conductive support substrate via a low-melting-point metal layer;
removing the base through the laser lift-off process; and
forming, in addition to the first high-resistance region, a second high-resistance region in a surface layer of a predetermined portion of the surface of the semiconductor layer which surface has previously bonded to the base, the portion corresponding to the first high-resistance region, through ion implantation at an acceleration voltage which allows the implanted ions to reach the first high-resistance region; and
dividing the semiconductor layer, through the first and second high-resistance regions, into semiconductor devices isolated from one another.
In the twenty-first aspect, the p-electrode and low-melting-point metal diffusion prevention layer may be patterned on the top surface of the semiconductor layer serving as semiconductor device regions, or may be formed on the entire top surface of the semiconductor layer without being patterned.
After the steps of the nineteenth or twenty-first aspects, the high-resistance region(s) may be dry-etched, to thereby physically separate the semiconductor layer into device regions, and individual semiconductor devices may be produced through dicing. Alternatively, the semiconductor layer and the base may be directly diced, to thereby produce individual semiconductor devices.
A twenty-second aspect of the present invention is drawn to a specific embodiment of the production method according to any of the thirteenth to twenty-first aspects, wherein the low-melting-point metal layer comprises at least one selected from a group consisting of Au—Sn, Au—Si, Ag—Sn—Cu, and Sn—Bi.
A twenty-third aspect of the present invention is drawn to a specific embodiment of the production method according to any of the thirteenth to twenty-second aspects, wherein the semiconductor device is a Group III nitride semiconductor device.
A twenty-fourth aspect of the present invention is drawn to a specific embodiment of the production method according to any of the thirteenth to twenty-third aspects, wherein the semiconductor device is a light-emitting device.
According to the first to twelfth aspects of the invention, the semiconductor device has a side surface whose surface layer has a high-resistance region formed through ion implantation. Therefore, even though an insulating film of another material is not provided, current leakage or short circuit at the side surface can be prevented.
Particularly in the eighth or ninth aspect, the semiconductor has a top surface provided with a high-resistance region or an insulating film. Therefore, current leakage or short circuit can be also prevented at the top surface.
According to the thirteenth aspect, a side surface whose surface layer has a high-resistance region formed through ion implantation is produced. Therefore, even though an insulating film of another material is not provided, a semiconductor device in which current leakage or short circuit at the side surface is prevented can be produced.
According to the fourteenth aspect, the side surface of the semiconductor device is formed to be inclined. Therefore, ion implantation can be performed along a direction normal to the main plane of the base. Thus, a semiconductor device in which current leakage or short circuit at the side surface is prevented can be produced in a more simple manner.
According to the fifteenth to eighteenth aspects, the top surface of the semiconductor device is provided with a high-resistance region produced through ion implantation or with an insulating film. Therefore, a semiconductor device in which current leakage or short circuit is also prevented at the top surface can be produced.
According to the nineteenth or twenty-first aspect, after formation of p-electrodes, semiconductor devices are physically isolated at centers of high-resistance regions. Therefore, the side surface of each semiconductor device is covered with the high-resistance region at the time of physical isolation, whereby a metal constituting a p-electrode does not deposit on the side surface.
According to the twentieth aspect, ion implantation is performed at a plurality of times at different acceleration voltages. Therefore, the implanted ion concentration becomes uniform in the depth direction, and a high-resistance region having uniformity in the depth direction can be formed.
According to the twenty-first aspect, two-step ion implantation is performed to a first surface and to a second surface, to thereby form a high-resistance region. Thus, acceleration voltage during ion implantation can be reduced.
Various other objects, features, and many of the attendant advantages of the present invention will be readily appreciated as the same becomes better understood with reference to the following detailed description of the preferred embodiments when considered in connection with the accompanying drawings, in which:
By reference to the drawings, specific embodiments of the present invention will next be described. However, the present invention is not limited to the embodiments.
With reference to
The p-electrode 102 may be formed from a metal having high optical reflectance and low contact resistance; for example, Ag, Rh, Pt, Ru, or an alloy containing such a metal as a primary component. Alternatively, the p-electrode may be made of, for example, Ni, an Ni alloy, or an Au alloy; or may be formed of a composite layer including a transparent electrode film (e.g., ITO film) and a highly reflective metal film. The low-melting-point metal diffusion prevention layer 103 is formed of, for example, a Ti/Ni-containing multi-layer film (e.g., Ti/Ni/Au film), or a W/Pt-containing multi-layer film (e.g., W/Pt/Au film). The low-melting-point metal layers 105, 106 may be formed of a eutectic metal layer (e.g., an Au—Sn layer, an Au—Si layer, an Ag—Sn—Cu layer, or an Sn—Bi layer); or may be formed of, for example, a layer of Au, Sn, or Cu (although such a metal is not a low-melting-point metal). The n-electrode 108 is formed from Ti/Al or a similar material. The support substrate 107 may be a conductive substrate formed from, for example, Si, GaAs, Cu, or Cu—W.
The light-emitting device 100 operates such that the top surface of the semiconductor layer 101 (n-electrode 108 side) serves as a light extraction plane 101a. Since high-resistance regions 110, 111 are formed on the semiconductor layer 101, current leakage or short circuit is prevented at the side surface of the semiconductor layer 101 and a region of the top surface in the vicinity of the side surface.
By reference to
Firstly, a semiconductor layer 101 is epitaxially grown on a sapphire base 112 (
Subsequently, a predetermined region of the semiconductor layer 101 is dry-etched until the sapphire base 112 is exposed, to thereby separate the semiconductor layer 101 into individual devices. Through dry etching, each semiconductor layer portion 101 is formed to be inclined so that the cross-sectional area gradually increases from the p-layer toward the sapphire base 112, to thereby form grooves 120 (
Except for the side surface, the semiconductor layer 101 is covered with a resist film, and nitrogen ions are implanted along the direction normal to the sapphire base 112 to the side surface of the semiconductor layer 101 through the resist film, which serves as a mask. Through bombardment of nitrogen ions with atoms constituting the semiconductor layer 101, the crystal structure of the layer is partially destructed. As a result, a high-resistance region 110 is formed in a surface layer of the side surface of the semiconductor layer 101. Thereafter, the resist film is removed (
The semiconductor layer 101 is formed into a tapered structure, since a sample of a non-tapered (vertical) or an inverted tapered structure must be tilted for attaining ion implantation into the side surface, which is cumbersome and not advantageous.
The ion implantation dose is preferably 1010 to 1018/cm2, which corresponds to an excess nitrogen density of 1018 to 1022/cm3. When the dose is in excess of 1018/cm2, crystallinity of the semiconductor is excessively impaired, whereas when the dose is lower than 101°/cm2, high resistance cannot be attained. Both cases are not preferred. Ion implantation is performed at an acceleration voltage of 120 keV. As a result, the high-resistance region 110 is formed to a layer thickness of 300 nm. The high-resistance region 110 preferably has a thickness of 50 to 1,000 nm. When the thickness is 50 nm or less, the effect of preventing current leakage or short circuit cannot be attained, whereas when the thickness is 1,000 nm or more, a long period of time is required for completing ion implantation.
Other than nitrogen, impurities such as arsenic and phosphorus, which are difficult to electrically activate may be employed as ion species to be implanted.
After formation of the high-resistance layer 110, a p-electrode 102 and a low-melting-point metal diffusion prevention layer 103 are formed on the top surface of the semiconductor layer 101, and a low-melting-point metal layer 105 is formed on the low-melting-point metal diffusion prevention layer 103 (
Next, a support substrate 107 is bonded to the low-melting-point metal layer 105 via a low-melting-point metal layer 106, which is formed on the top surface of the support substrate 107 (
Through the laser lift-off technique, the sapphire base 112 is irradiated with a laser beam, to thereby remove the sapphire base 112 (
Subsequently, ion implantation is performed to a portion of the surface of the semiconductor layer 101 which surface has previously bonded to the sapphire base 112 (light extraction surface 101a) and which is in the vicinity of the side surface (i.e., extending from the side surface to the inside and having a width 5% to 10% the width of the top surface), whereby a high-resistance region 111 is formed (
On the light extraction surface 101a, a lattice-form n-electrode 108 is formed (
Next, steps of producing the light-emitting device 200 will be described. The steps of producing the light-emitting device 200 are the same as those of producing the light-emitting device 100, except that the step shown in
Similar to Embodiment 1, a p-electrode 102, a low-melting-point metal diffusion prevention layer 103, and a low-melting-point metal layer 105 are formed, a support substrate 107 is bonded to a low-melting-point metal layer 105 via a low-melting-point metal layer 106, and a sapphire base 112 is removed through the laser lift-off technique (
The acceleration voltage during ion implantation is 120 keV in Embodiment 1 and 1.2 MeV in Embodiment 2. However, the acceleration voltage is not limited to these values. When ion implantation is performed at an acceleration voltage which does not allow the implanted ions to reach the sapphire base 112, ion implantation is performed in a manner of Embodiment 1, whereas when ion implantation is performed at an acceleration voltage which allows the implanted ions to reach the sapphire base 112, ion implantation is performed in a manner of Embodiment 2.
$77
Steps of producing the light-emitting device 300 will be described. The steps of producing the light-emitting device 300 are the same as those of producing the light-emitting device 100 of Embodiment 1, except that the steps shown in
Similar to the high-resistance region 111 of the light-emitting device 100, current leakage or a similar phenomenon at a portion of the top surface of the semiconductor layer 401 in the vicinity of the side surface is prevented by virtue of the insulating film 411.
Other than SiO2, the insulating film 411 may be formed from, for example, Si3N4, ZrO2, NbO, or Al2O3.
By reference to
Firstly, in a manner similar to that of Embodiment 1, the semiconductor layer 501 is epitaxially grown on a sapphire base 112 (
Subsequently, a resist film is formed on a predetermined region of the semiconductor layer 501, and nitrogen ions are implanted along the direction normal to the sapphire base 112 through the resist film, which serves as a mask, to thereby form the high-resistance region 510. Thereafter, the resist film is removed (
On a portion of the semiconductor layer 501 other than the high-resistance region 510, a p-electrode 102 and a low-melting-point metal diffusion prevention layer 103 are formed through the lift-off process. A low-melting-point metal layer 105 is formed on the low-melting-point metal diffusion prevention layer 103 (
Next, the support substrate 107 is bonded to the low-melting-point metal layer 105 via a low-melting-point metal layer 106, which is formed on the top surface of the support substrate 107 (
The sapphire base 112 is removed through the laser lift-off technique (
Subsequently, the high-resistance region 510 is dry-etched into a tapered structure in which the device has a cross-sectional area gradually increasing toward the support substrate 107, to thereby form a groove 520 and physically separate the semiconductor layer into device regions (
Then, a n-electrode 108 is patterned into a lattice form, and the light-emitting device 500 shown in
By reference to
Firstly, similar to Embodiment 1, a semiconductor layer 701 is epitaxially grown on a sapphire base 112. Similar to the step of Embodiment 5 shown in
Subsequently, similar to a production step of Embodiment 6, a p-electrode 602, a low-melting-point metal diffusion prevention layer 603, and a low-melting-point metal layer 605 are formed on the entire top surface of a support substrate 107 (
Subsequently, ion implantation is performed once to a portion of the surface 701a of the semiconductor layer 701 which surface has previously bonded to the sapphire base 112, the portion being opposite the high-resistance region 710, at such an acceleration voltage that allows the implanted nitrogen ions to reach the high-resistance region 710. Similar to the aforementioned cases, the region to which ions are not implanted is covered with a resist film serving as a mask, and the resist film is removed after ion implantation. Through ion implantation, the high-resistance region 713 is formed. The semiconductor layer 701 is separated by the high-resistance regions 710, 713, to thereby isolate individual device regions (
An advantage of the aforementioned two-step ion implantation resides in that no such a high acceleration voltage that allows the implanted ions to reach the sapphire base 112 is required (Embodiments 2, 5, and 6). Briefly, the minimum required acceleration voltage can be reduced. When single-step ion implantation is performed to a layer having a thickness of 4 μm, an acceleration voltage of 1.2 MeV is required to cause nitrogen ions to reach the sapphire base 112. However, when two-step ion implantation of Embodiment 7 is performed, the acceleration voltage may be such a value that allows nitrogen ions to reach the half depth of the semiconductor layer. Specifically, when the layer thickness is 4 μm, the required acceleration voltage is 800 keV. Thereafter, the high-resistance regions 710, 713 are dry-etched to be inclined so as to form a tapered structure in which the device has a cross-sectional area gradually increasing toward the support substrate 107, to thereby form a groove 720, whereby the semiconductor layer is physically separated into individual device regions (
Thereafter, an n-electrode 108 is patterned to a lattice form. Through cutting along the groove 720 of the support substrate 107 together with the p-electrode 602, low-melting-point metal diffusion prevention layer 603, low-melting-point metal layer 605, and a low-melting-point metal layer 106, the light-emitting device 700 shown in
The two-step ion implantation technique for reducing the required acceleration voltage performed in Embodiment 7 may be applied to Embodiment 5.
In Embodiments 5 to 7, a high-resistance region is dry-etched to physically separate the region as shown in
In Embodiments 5 to 7, a p-electrode, a low-melting-point metal diffusion prevention layer, and a low-melting-point metal layer are formed before physical device isolation. Therefore, a metal constituting the electrode or the layers is not deposited on a side surface of the semiconductor device during formation of the electrode and the layers.
The above Embodiments are given for producing light-emitting devices. However, the present invention is not limited to a light-emitting device and encompasses any semiconductor devices which are produced through the laser lift-off technique. The invention is not limited to a Group III nitride semiconductor device and is applicable to Group III-V semiconductor (e.g., GaAs or GaP) devices. No particular limitation is imposed on the shape of the n-electrode, and any shape such as lattice or stripe may be employed, so long as light extraction through the top surface is not inhibited.
In the above Embodiments, the support substrate is bonded to the semiconductor structure. However, the support substrate may be formed through directly plating a semiconductor layer with a metal such as Cu.
As described hereinabove, a semiconductor device in which current leakage or short circuit is prevented at a side surface of the device can be produced.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2007-069266 | Mar 2007 | JP | national |
The present Application is a Divisional Application of U.S. patent application Ser. No. 12/076,234, filed on Mar. 14, 2008, which is based on and claims priority from Japanese Patent Application No. 2007-069266, filed on Mar. 16, 2007, the entire contents of which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12076234 | Mar 2008 | US |
| Child | 12656970 | US |