Hemocompatible polymer systems and related devices

Abstract

A polymer system and device with a hemocompatible film or coated polymers is provided, the polymer system comprises an organic phase and an aqueous phase, the organic phase comprises polymerizable monomers and at least one initiator and the aqueous phase comprises at least one dispersing agent, at least one free radical inhibitor and at least one buffering agent, the organic phase is immiscible in the aqueous phase, and the dispersing agent forms a hemocompatible surface on the polymer, and the device comprises a housing for containing the polymer system.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a hemocompatible surface coated polymer system comprising an organic phase and an aqueous phase. More specifically, the present invention relates to polymer having organic and aqueous phases, where the organic phase comprises polymerizable monomers and at least one initiator and the aqueous phase comprises at least one dispersing agent, at least one free radical inhibitor and at least one buffering agent, and the organic phase is immiscible in the aqueous phase, and the dispersing agent forms a hemocompatible surface on the polymer. The invention further provides for additional dispersants and devices and apparati containing the hemocompatible polymers.

2. Description of Related Art

It has been known and practiced in the art of suspension polymerization to manufacture polymers with a hemocompatible coating using a two-step process. In the first step of the two-step process, polymeric beads are manufactured by polymerizing monomer droplets using suspension polymerization. In the second step of the process, a hemocompatibilizing film is applied onto the exterior surface of the polymer to provide the hemocompatible coating. Unlike the prior art, the polymers of the present invention have aqueous and organic phases where the organic phase is immiscible in the aqueous phase, and the dispersing agent used in the aqueous phase forms a hemocompatible surface on the polymer.

SUMMARY OF THE INVENTION

The present invention provides for hemocompatible coated polymer system comprising an organic phase and an aqueous phase. In one embodiment, the organic phase comprises polymerizable monomers and at least one initiator and the aqueous phase comprises at least one dispersing agent, at least one free radical inhibitor and at least one buffering agent. In another embodiment, the organic phase of the system of the present invention is immiscible in the aqueous phase, and the dispersing agent forms a hemocompatible surface on the polymer.

In still another embodiment, the monomer is a monofunctional monomer, and the monofunctional monomer is selected from a group consisting of styrene, ethylstyrene, acrylonitrile, butyl methacrylate, octyl methacrylate, butyl acrylate, octyl acrylate, cetyl methacrylate, cetyl acrylate, ethyl methacrylate, ethyl acrylate, vinyltoluene, vinylnaphthalene, vinylbenzyl alcohol, vinylformamide, methyl methacrylate, methyl acrylate and mixtures thereof.

In yet another embodiment, the monomer is a polyfunctional monomer, and the polyfunctional monomer is selected from a group consisting of divinylbenzene, trivinylbenzene, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, pentaerythritol diacrylate, pentaerythritol triiacrylate, pentaerythritol tetraacrylate, dipentaerythritol dimethacrylate, dipentaerythritol trimethacrylate, dipentaerythritol tetramethacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, divinylformamide and mixtures thereof.

In still yet another embodiment, the initiator of the system of the present invention is selected from a group consisting of diacyl peroxides, ketone peroxides, peroxyesters, dialkyl peroxides, peroxyketals, azoalkylnitriles, peroxydicarbonates and mixtures thereof. In a further embodiment, the dispersing agent is selected from a group consisting of poly(N-vinylpyrrolidinone), hydroxyethyl cellulose, hydroxypopyl cellulose, poly(hydroxyethyl methacrylate), poly(hydroxyethyl acrylate), poly(hydroxypropyl methacrylate), poly(hydroxypropyl acrylate), poly(dimethylaminoethyl methacrylate), poly-(dimethylaminoethyl acrylate), poly(diethylamimoethyl methacrylate), poly-(diethylaminoethyl acrylate), poly(vinyl alcohol), salts of poly(methacrylic acid), and salts of poly(acrylic acid) and mixtures thereof.

In still a further embodiment, the free radical inhibitor is selected from a group consisting of p-nitrosophenoxide salts, sodium nitrite, N-hydroxy-N-methylglucamine, N-nitroso-N-methylglucamine and mixtures thereof. In yet a further embodiment, the buffering agent is selected from a group consisting of carbonate salts, bicarbonate salts, boric acid salts, salts of phosphoric acid and mixtures thereof. In still yet a further embodiment, the organic phase further comprises at least one porogen, and the porogen is selected from a group consisting of aliphatic hydrocarbons, dialkyl ketones, aliphatic carbinols and mixtures thereof. In another further embodiment, the polymer is a porous polymer.

In still another further embodiment, the present invention relates to a hemocompatible surface coated polymer system comprising an organic phase and an aqueous phase, the system being manufactured by a method comprising: forming the organic phase comprising polymerizable monomers and at least one initiator; forming the aqueous phase comprising at least one dispersant agent, at least one free radical inhibitor, and at least one buffering agent; dispersing the organic phase into the aqueous phase to thereby form organic phase droplets; and polymerizing the organic phase droplets coated with the dispersing agent to thereby form the hemocompatible surface coating on the polymer. In yet another further embodiment, the polymerization of the organic phase is formed by heating a mixture of the organic and aqueous phases.

In still yet another further embodiment, the present invention relates to a method of manufacturing a hemocompatible surface coated polymer system comprising an organic phase and an aqueous phase, the method comprising: forming the organic phase comprising polymerizable monomers and at least one initiator; forming the aqueous phase comprising at least one dispersant agent, at least one free radical inhibitor, and at least one buffering agent; dispersing the organic phase into the aqueous phase by agitation to form a suspension of organic droplets; and polymerizing the organic phase by heating the suspension of the organic phase droplets coated with the dispersing agent to thereby form the hemocompatible surface coating on the polymer.

In another embodiment, the present invention relates to a polymer with a hemocompatible coating comprising at least one crosslinking agent for making the polymer and at least one dispersing agent whereby the dispersing agent forms a hemocompatible surface on the polymer.

In another embodiment, the biocompatibilizing polymer comprises poly(N-vinylpyrrolidinone). In still another embodiment, the biocompatibilizing polymer is selected from a group consisting of poly(hydroxyethyl methacrylate), poly(hydroxyethyl acrylate), poly(dimethylaminoethyl methacrylate), salts of poly(acrylic acid), salts of poly(methacrylic acid), poly(diethylaminoethyl methacrylate), poly(hydroxypropyl methacrylate), poly(hydroxypropyl acrylate), poly(N-vinylpyrrolidinone), poly(vinyl alcohol) and mixtures thereof. In another embodiment, the salts may be sodium and potassium salts and in still another embodiment, the salts are water-soluble salts.

In yet another embodiment, the dispersing agent is selected from a group consisting of hydroxyethyl cellulose, hydroxypopyl cellulose, poly(hydroxyethyl methacrylate), poly(hydroxyethyl acrylate), poly(hydroxypropyl methacrylate), poly(hydroxypropyl acrylate), poly(dimethylaminoethyl methacrylate), poly(dimethylaminoethyl acrylate), poly(diethylamimoethyl methacrylate), poly(diethylaminoethyl acrylate), poly(vinyl alcohol), salts of poly(methacrylic acid), and salts of poly(acrylic acid) and mix thereof.

In still another embodiment, the crosslinking agent is selected from a group consisting of divinylbenzene, trivinylbenzene, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythrital tetra-, tri-, and dimethacrylates, pentaerythritol tetra-, tri- and diacrylates, dipentaerythritol tetra, tri-, and dimethacrylates, dipentaerythritol tetra-, tri-, and diacrylates, divinylformamide, and mixtures thereof.

In still yet another embodiment, the crosslinking agent comprises divinylbenzene. In a further embodiment, the crosslinking agent comprises trivinylcylohexane. In yet a further embodiment, the crosslinking agent comprises trivinylbenzene.

In still a further embodiment, the crosslinking agent comprises copolymers of divinylbenzene with comonomers being selected from a group consisting of styrene, ethylstyrene, acrylonitrile, butyl methacrylate, octyl methacrylate, butyl acrylate, octyl acrylate, cetyl methacrylate, cetyl acrylate, ethyl methacrylate, ethyl acrylate, vinyltoluene, vinylnaphthalene, vinylbenzyl alcohol, vinylformamide, methyl methacrylate, methyl acrylate and mixtures thereof.

In still yet a further embodiment, the polymer with the hemocompatible surface is a porous polymer. In another further embodiment, the polymer with the hemocompatible surface is an ion exchange polymer. In a further embodiment, the polymer is an affinity polymer. In yet another further embodiment, the biocompatibilizing polymer becomes grafted to the surface of the polymer to provide a polymer with the hemocompatible surface. For purposes of this invention, the term “grafting” is defined as chemically bonded with potential entanglement such that the dispersing agent is physically restricted from leaving the surface of the polymer.

In another embodiment, the present invention relates to a polymer manufactured by a process comprising: simultaneously polymerizing and coating with at least one crosslinking agent for making the polymer and using at least one dispersing agent to form a hemocompatible coated polymer.

For purposes of this invention, the term “hemocompatibility” is defined as a condition whereby a material, when placed in contact with whole blood and blood components or physiological fluids, results in clinically acceptable physiological changes. In another embodiment, the dispersing agent is a biocompatibilizing polymer. A “biocompatibilizing polymer” is defined as a polymer, which forms a surface over a non-biocompatible material, making the polymeric system compatible with physiological fluids and tissues. The term “crosslinking agent” is defined as a linking agent such as a polyfunctional monomer that links two or more polymer chains or segments of the same polymer chain together. The term “dispersing agent” is defined as a substance that imparts a stabilizing effect upon a finely divided array of immiscible particles suspended in a fluidizing medium. The immiscible particles can be a solid, liquid or gas and the fluidizing medium can be a liquid or a gas.

In another embodiment, the crosslinking agent is polymerized with at least one vinyl monomer. In a further embodiment, the dispersing agent forms a hemocompatible coating on a surface of the polymer. In yet a further embodiment, the coating of the polymer is equivalent to the surface of the polymer.

In still a further embodiment, the polymer is processed in non-pyrogenic water. For purposes of this invention, “non-pyrogenic” shall be defined by U.S.P. 25, Monograph (151) Pyrogenic Test, U.S. Pharmacopeia National Formulary.

In still yet another embodiment, the polymer of the present invention is prepared by suspension polymerization. For purposes of the invention, suspension polymerization is defined as the polymerization of monomer droplets dispersed in an immiscible liquid. Based upon an Elemental Analysis of the Polymer's Surface by X-Ray Photoelectron Spectroscopy (XPS), the dispersing agent becomes chemically grafting onto the surface of the polymer as the monomer droplets are transformed into polymeric beads. Polymers coated with poly(N-vinylpyrrolidinone) have been found to be biocompatible and hemocompatible. The hemocompatible polymers of the present invention pass the Lee White clotting tests and the tests for the hemolysis of red blood cells.

In another embodiment, the polymer of the present invention is a porous polymer. The term “porous polymer” is defined as a polymer particle having an internal pore structure with a porosity resulting from voids or holes throughout the polymer matrix. In still another embodiment, the polymer is an ion exchange resin or polymer. An ion exchange resin or polymer is a resin or polymer carrying ionogenic groups that are capable of exchanging ions or of sequestering ions. The ion exchange polymers of the present invention are beneficial when used with blood for removing and isolating varying ions and ionogenic molecules.

In still yet another embodiment, the present invention relates to a polymer with a hemocompatibilizing surface coating. In a further embodiment, the coated polymer is manufactured by a one step process comprising: simultaneously coating and polymerizing monomer droplets in a suspension polymerization procedure with at least one dispersing agent having encapsulated the droplets with a hemocompatible coating to thereby form a polymer with a hemocompatible surface-coating grafted onto the surface of the polymer beads.

In another embodiment, the present invention relates to a method of manufacturing a biocompatible and hemocompatible surface coated polymer. In still another embodiment, the method comprises: polymerizing monomer droplets comprising at least one crosslinking agent and simultaneously coating the resulting polymer beads using at least one dispersing agent to form a biocompatible surface coated polymer. In still another embodiment, the coated polymers are hemocompatible. In yet another embodiment, the polymer is formed using a suspension polymerization procedure. In another embodiment, the polymer is formed using an emulsion polymerization procedure followed by growing the particles with additional monomer feed.

In still another embodiment, the present invention relates to an application of use whereby the hemocompatible surface coated polymers of the present invention are utilized for medical applications. In another embodiment, the hemocompatible polymers of the present invention may be used to isolate and/or remove target substances from blood and physiological fluids and for specific treatments. In a further embodiment, the hemocompatible polymers of the present invention may be used in preserving organs. In yet another embodiment, the present invention relates to an apparatus for isolating blood components and for purifying blood using the hemocompatible surface coated polymers of the present invention. In one embodiment, the apparatus comprises a cartridge containing the hemocompatible polymers of the present invention.

In yet a further embodiment, the present invention relates to a polymer with a hemocompatible surface coating, the polymer being manufactured by a method comprising: polymerizing monomer droplets comprising at least one crosslinking agent to form a polymer and developing a surface coating on the polymer by using at least one dispersing agent carrying hydroxyl groups followed by a reaction of hydroxyl groups with a vinyl monomer or polymer to thereby form the hemocompatible surface coating on the polymer.

In still yet a further embodiment, the present invention also relates to a method of manufacturing a hemocompatible surface coated polymer using a one step process, the method comprising: polymerizing monomer droplets comprising at least one crosslinking agent to form a polymer and developing a surface coating on the polymer by using at least one dispersing agent carrying hydroxyl groups followed by a reaction of hydroxyl groups with a vinyl monomer or polymer to thereby form the hemocompatible surface coating on the polymer.

In another embodiment, the present invention relates to a polymer having a hemocompatible-coated surface, the polymer being manufactured by a two-step process comprising: polymerizing monomer droplets comprising at least one crosslinking agent and at least one dispersing agent to form a polymer; and coating the surface of the polymer by crosslinking a monovinyl monomer and a polyfunctional monomer mixture over the surface of the polymer bead to thereby form the hemocompatible coating on the surface of the polymer.

In a further embodiment, the present invention relates to a method comprising: polymerizing monomer droplets comprising at least one crosslinking agent and at least one dispersing agent to form a polymer; and coating the surface of the polymer by crosslinking a monovinyl monomer and a polyfunctional monomer mixture over the surface of the polymer bead to thereby form the hemocompatible coating on the surface of the polymer.

In another embodiment, the present invention relates to a hemocompatible system comprising an organic phase and an aqueous phase, wherein the organic phase composed of the polymerizable monomers and the porogen are dispersed into a slurry of droplets by agitation throughout the aqueous phase which is formulated to effect the stability of the droplets by the water-miscible dispersant and to quench polymer growth in the aqueous phase by carrying a water-soluble free radical inhibitor.

In a further embodiment, the present invention provides for a hemocompatible-coated polymer comprising at least one crosslinking agent and at least one dispersing agent whereby said dispersing agent forms a hemocompatible surface on said polymer, said dispersing agent is selected from a group consisting of heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof, said crosslinking agent is selected from a group consisting of divinylbene, trivinylbenne, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythrital dimethacrylate, pentaerythrital trimethacrylate, pentaerythrital tetramethacrylate, pentaerythritol diacrylate, pentaerythritol triiacrylate, pentaerythritol tetraacrylate, dipentaerythritol dimethacrylate, dipentaerythritol trimethacrylate, dipentaerythritol tetramethacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, divinylformamide and mixtures thereof, said polymer being developed simultaneously with the formation of the coating, wherein said dispersing agent gets chemically bound to said surface of said polymer.

In still a further embodiment, the present invention relates to a biocompatible coated polymer manufactured by a method comprising: polymerizing monomer droplets comprising at least one crosslinking agent to form a polymer and coating said resulting polymer using at least one dispersing agent to thereby form a biocompatible coated polymer, said dispersant being placed on said monomer droplets before polymerization, said dispersing agent is selected from a group consisting of heparin, albumin, carrageenen, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tagacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof, wherein said dispersing agent gets chemically bound to said surface of said polymer.

In another embodiment, the invention provides for a hemocompatible surface coated polymer system comprising an organic phase and an aqueous phase, said organic phase comprising polymerizable monomers and at least one initiator and said aqueous phase comprising at least one dispersing agent, at least one free radical inhibitor and at least one buffering agent, said organic phase being immiscible in said aqueous phase, wherein the organic phase forms a polymer, and wherein said dispersing agent in the aqueous phase forms a hemocompatible surface on said polymer said dispersing agent is selected from a group consisting of heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic Acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof.

In another further embodiment, the invention relates to a containment device for housing hemocompatible polymers, said device comprising a housing with an entrance and an exit, said hemocompatible polymers being situated within said housing of said device, hemocompatible-coated polymer comprising at least one crosslinking agent and at least one dispersing agent whereby said dispersing agent forms a hemocompatible surface on said polymer.

In still another embodiment, the dispersing agent in the device is selected from a group consisting of hydroxyethyl cellulose, hydroxypopyl cellulose, poly(hydroxyethyl methacrylate), poly(hydroxyethyl acrylate), poly(hydroxypropyl methacrylate), poly(hydroxypropyl acrylate), poly (dimethylaminoethyl methacrylate), poly-(dimethylaminoethyl acrylate), poly(diethylamimoethyl methacrylate), poly-(diethylaminoethyl acrylate), poly(vinyl alcohol), poly(N-vinylpyrrolidinone), salts of poly(methacrylic acid), and salts of poly(acrylic acid), heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMMEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof.

In yet another embodiment, the crosslinking agent in the device is selected from a group consisting of divinylbenzene, trivinylbenzene, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythrital dimethacrylate, pentaerythrital trimethacrylate, pentaerythrital tetramethacrylate, pentaerythritol diacrylate, pentaerythritol triiacrylate, penta erythritol tetraacrylate, dipentaerythritol dimethacrylate, dipentaerythritol trimethacrylate, dipentaerythritol tetramethacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, divinylformamide and mixtures thereof.

In still yet another embodiment, the device further comprises a polycarbonate canister with two polycarbonate end caps with male leur blood connectors, two polypropylene port plugs, two silicone O-rings and two screen assemblies designed to retain said polymers within said canister.

In a further embodiment, the apparatus for containing hemocompatible polymers, said apparatus comprising a housing and a hemocompatible surface coated polymer system situated within said housing, said system comprising an organic phase and an aqueous phase, said organic phase comprising polymerizable monomers and at least one initiator and said aqueous phase comprising at least one dispersing agent, at least one free radical inhibitor and at least one buffering agent, said organic phase being immiscible in said aqueous phase, wherein the organic phase forms a polymer, and wherein said dispersing agent in the aqueous phase forms a hemocompatible surface on said polymer said dispersing agent is selected from a group consisting of hydroxyethyl cellulose, hydroxypopyl cellulose, poly(hydroxyethyl methacrylate), poly(hydroxyethyl acrylate), poly(hydroxypropyl methacrylate), poly(hydroxypropyl acrylate), poly(dimethylaminoethyl methacrylate), poly-(dimethylaminoethyl acrylate), poly(diethylamimoethyl methacrylate), poly-(diethylaminoethyl acrylate), poly(vinyl alcohol), poly(N-vinylpyrrolidinone), salts of poly(methacrylic acid), and salts of poly(acrylic acid), heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof.

In another further embodiment, the apparatus further comprises a polycarbonate canister with two polycarbonate end caps with male leur blood connectors, two polypropylene port plugs, two silicone O-rings and two screen assemblies designed to retain said polymers within said canister.

DETAILED DESCRIPTION OF THE INVENTION

As required, detailed embodiments of the present invention are disclosed herein; however, it is to be understood that the disclosed embodiments are merely exemplary of the invention that may be embodied in various forms. The figures are not necessary to scale, some features may be exaggerated to show details of particular components. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a basis for the claims and as a representative basis for teaching one skilled in the art to variously employ the present invention.

The specific example below will enable the invention to be better understood. However, they are given merely by way of guidance and do not imply any limitation.

The specific example below will enable the invention to be better understood. However, they are given merely by way of guidance and do not imply any limitation.

EXAMPLE 1

The first polymer synthesis was targeted at an aqueous to organic volume ratio of 1.0. Table 1 below illustrates the targeted dispersion mixture designed for Example 1 using a fifty (50) liter reaction.

TABLE 1
Dispersion Mixture Desires for 50 Liters
Aqueous/Organic Volume Ratio     1.0
Volume of Organic Phase, ml      25,000.0
Volume of Aqueous Phase, ml      25,000.0
Density of Organic Phase, g/ml   0.83490
Weight of Organic Phase, g       20,872.5
Density of Aqueous Phase, g/ml   1.005
Weight of Aqueous Phase, g       25,125.0
Polymerizable Monomers, DVB plus EVB, g 8766.45
Total Volume of Organic & Aqueous Phases, ml 50,000.0
Total Weight of Organic & Aqueous Phases, g 45,997.5

The procedure for the polymerization in Example 1 is initiated by the preparation of an aqueous phase and an organic phase. Table 2 and 3 below illustrate the components of the aqueous phase composition for the polymer synthesis by weight percent (%) and by quantity of the components in grams (g), respectively.

TABLE 2
Aqueous Phase Composition
Ultrapure Water, wt. %           98.089
Water from Aqueous 45% Solution of Poly(N- 0.611
vinylpyrrolidinone), wt. %
Poly(N-vinylpyrrolidinone) Pure, wt. % 0.500
Sodium Carbonate, wt. %          0.500
Sodium Nitrite, wt. %            0.300

Other dispersants, such as poly(vinyl alcohol) have been used as a substitute for the poly(N-vinylpyrrolidinone).

TABLE 3
Aqueous Phase Charges
Ultrapure Water, g               24,644.83
Water from Aqueous 45% Solution of Poly(N- (153.542)
vinylpyrrolidinone), g
Poly(N-vinylpyrrolidinone) Pure, g (125.625)
Aqueous Poly(N-vinylpyrrolidinone) Solution, 45 wt. %, g 279.167
Sodium Carbonate, g              125.625
Sodium Nitrite, g                75.375
Weights in parenthesis are part of other charged
materials
Total Weight of Aqueous Phase, g 25,124.997

Table 4 and 5 illustrate the components of the organic phase composition for the polymer synthesis by weight percent (5) and by quantity of the components in grams (g), respectively.

TABLE 4
Organic Phase Composition
Divinylbenzene (DVB), wt. %      26.998
Ethylvinylbenzene (EVB), wt. %   15.0024
Inerts, wt. %                    0.41567
Toluene, wt. %                   27.134
Isooctane, wt. %                 30.450
Benzoyl Peroxide, wt. % of polymerizable monomers 1.03

Other immiscible porogens such as isooctane, cyclohexane and nonane have been substituted, both singularly and in combination with one another, for the mixture of toluene and isooctane.

TABLE 5
Organic Phase Charges
Divinylbenzene, Pure, g          (5635.069)
Ethylvinylbenzene, Pure, g       (3131.381)
Commercial DVB, Dow 63.5%, g     8853.211
Inerts, g                        (86.761)
Toluene, g                       5663.613
Isooctane, g                     6355.676
Weights in parenthesis are part of commercial DVB
Total Weight of Organic Phase, g (excluding BPO) 20,872.50
Benzoyl Peroxide, BPO, Pure, g   90.294
75 weight percent BPO, g         120.393
97 weight oercent BPO, g         93.087

Upon preparation of the aqueous and organic phases, the aqueous phase is introduced into the reactor. The reactor is set at an agitation rate sufficient to produce droplet slurry throughout the reaction volume. The aqueous phase is then heated to 65 degrees Celsius with agitation and a nitrogen sweep through the headspace in order to displace oxygen from the reactor space. The organic phase is then introduced into the reactor by pouring or pumping the organic phase onto the aqueous phase under agitation at a stirring rate of at least 86 revolutions per minute. The droplet dispersion is then stirred at 86 revolutions per minute for at least fifteen (15) minutes to set the droplet size and allow the droplet slurry to equilibrate as the temperature is raised from about 65 degrees to about 70 degrees Celsius. Once the droplet dispersion is homogenous throughout the reaction volume, the slurry is then heated to about 75 plus or minus 2.0 degrees Celsius and held at that temperature for ten (10) hours.

The slurry is cooled to about 70 degrees Celsius and the stirrer is turned off, and the polymer beads are allowed to collect at the top of the fluid bed. The mother liquor is then removed from the bottom of the reactor via a pump until the bead bed approaches within about one (1) inch from the bottom of the reactor. The mother liquor is discarded.

A sufficient amount of ultrapure water at ambient temperature is added to fluidize the bead bed and the slurry is heated to 60%. The quantity of water needed to wash the beads will be approximately one (1) bed volume or about 25 liters of water. Upon adding the water, the stirrer is then restarted and agitated at a stir rate of 106 revolutions per minute for about thirty (30) minutes while being heated to 60%. The stirring is stopped and the beads are allowed to collect at the top of the fluid bed.

The liquor is then drained from the bottom of the reactor via a pump until the bead bed approaches within about one (1) inch from the bottom of the reactor. The wash liquor is discarded. The beads are then washed with the 60 degree Celsius ultrapure water for at least five (5) washes or until the bulk fluid is transparent and free of junk polymer (a clear liquor is achieved). The water-wet bead slurry is transferred to a column that is fitted with a solid-liquid separator at the bottom of the column. The separator may be a mesh or screen made from Teflon, nylon, polypropylene, stainless steel, or glass with pore openings in the size from about 100 to about 300 microns.

The porogen mixture is displaced from the beads by a downflow treatment with ten (10) bed volumes of isopropyl alcohol at a flow rate of one (1) bed volume per hour. The isopropyl alcohol is displaced from the beads with water at a downflow treatment with ten (10) bed volumes of ultrapure water (pyrogen and endotoxin free) at a flow rate of one (1) bed volume per hour. The polymer beads are then transferred from the column into plastic containers for transport to the thermal steam-flux cleaner.

Alternatively, the porogen is displaced from the beads by a thermal-gas-flux treatment in which the porogen filled beads are heated from about 150 degrees to about 180 degrees Celsius under an upflow gas flux for approximately six (6) hours. The hot gas flux can be either super heated stream or hot nitrogen gas. The dried, cleaned, porogen free beads are wetted out with an aqueous solution of isopropyl alcohol in water for further handling prior to being packed into containers.

EXAMPLE 2

Other experimental procedures were conducted to make the polymeric beads manufactured by similar polymerization procedures described in Example 1 and under the variations identified in the Table of Inputs (Table 6) with the resulting responses tabulated in the Tables of responses (Table 7). Tables 6 & 7 are set forth below:

TABLE 6
Experimental Program: Input
	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
LDM	02-001	02-004	02-006	02-008	02-010	02-012	02-015	02-016
Organic Phase Composition
Monomer (DVB & EVB) Wt. %	42.0	42.0	42.0	42.0	40.7	50.0	40.0	40.0
Porogen Wt. %	58.0	58.0	58.0	58.0	59.3	50.0	60.0	60.0
Porogen/Monomer Ratio	1.3810	1.3810	1.3810	1.3810	1.457	1.000	1.500	1.500
Benzoyl Peroxide (BPO) Wt. %	1.03	1.03	1.03	1.03	1.03	1.03	1.03	1.03
Porogen Composition
Isooctane, Wt. %	52.5	52.5	52.5	52.5	53.5	60.0	99.327	99.327
Toluene, Wt. %	46.769	46.769	46.769	46.769	45.81	38.99	0	0
Inerts, Wt %	0.731	0.731	0.731	0.731	0.693	1.010	0.6734	0.6734
Toluene, plus Inerts, Wt. %	47.5	47.5	47.5	47.5	46.5	40.0	—	—
Isooctane/Toluene plus Inerts	1.105	1.105	1.105	1.105	1.1505	1.500	—	—
Ratio
Aquoeus Phase Composition
Sodium Carbonte, Wt. %	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500
Sodium Nitrite, Wt. %	0.300	0.300	0.300	0.300	0.300	0.300	0.300	0.300
Poly (N-Vinylpyrrolidione),	0.500	0.500	0.450	0.400	0.400	0.400	0.100	0.400
Wt. %
PVP K 30, 45-55 Kdaltons,	0	0	0	0	0	0	0	0
Wt. %
PVP K 60, 400-500 Kdaltons,	0.500	0.500	0.450	0.400	0.400	0.400	0.100	0.400
Wt. %
Poly (Vinyl alcohol), Wt. %	0.01	0.01	0.05	0.100	0.100	0.100	0.400	0.100
Molecular Size, Kdaltons	88.0	88.0	95.0	95.0	95.0	95.0	95.0	95.0
Amount Hydrolized, %	85	85	95	95	95	95	95	95
Aqueous/Organic Phase	0.9	0.9	0.9	0.9	0.9	0.9	0.9	0.9
Volume Ratio
	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
LDM	02-017	02-022	02-025	02-028	02-029	02-030	02-031	02-032
Organic Phase Composition
Monomer (DVB & EVB) Wt. %	45.0	45.0	45.0	45.0	45.0	45.0	45.0	45.0
Porogen Wt. %	55.0	55.0	55.0	55.0	55.0	55.0	55.0	55.0
Porogen/Monomer Ratio	1.222	1.222	1.222	1.222	1.222	1.222	1.222	1.222
Benzoyl Peroxide (BPO) Wt. %	1.03	1.03	1.03	1.03	1.03	1.03	1.03	1.03
Porogen Composition
Isooctane. Wt. %	99.174	99.174	99.274	99.274	99.274	99.274	99.274	99.274
Toluene, Wt. %	0	0	0	0	0	0	0	0
Inerts, Wt %	0.826	0.826	0.726	0.726	0.726	0.726	0.726	0.726
Toluene, plus Inerts, Wt. %	—	—	—	—	—	—	—	—
Isooctane/Toluene plus Inerts	—	—	—	—	—	—	—	—
Ratio
Aquoeus Phase Composition
Sodium Carbonte, Wt. %	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500
Sodium Nitrite, Wt. %	0.300	0.300	0.300	0.300	0.300	0.300	0.300	0.300
Poly (N-Vinylpyrrolidione),	0.500	0.500	1.000	0.700	0.900	1.000	1.000	1.500
Wt. %
PVP K 30, 45-55 Kdaltons,	0	0.250	1.000	0.700	0.900	1.000	1.000	1.500
Wt. %
PVP K 60, 400-500 Kdaltons,	0.500	0.250	0	0	0	0	0	0
Wt. %
Poly (Vinyl alcohol), Wt. %	0	0	0	0	0	0	0	0
Molecular Size, Kdaltons	—	—	—	—	—	—	—	—
Amount Hydrolized, %	—	—	—	—	—	—	—	—
Aqueous/Organic Phase	0.9	1.1	1.1	1.2	1.2	1.145	1.2	1.2
Volume Ratio
	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
LDM	02-033	02-034	02-036	02-038	02-040	02-042	02-044	02-047
Organic Phase Composition
Monomer (DVB & EVB) Wt. %	50.0	55.0	55.0	55.0	55.0	55.0	55.0	55.0
Porogen Wt. %	50.0	45.0	45.0	45.0	45.0	45.0	45.0	45.0
Porogen/Monomer Ratio	1.000	0.8182	0.8182	0.8182	0.8182	0.8182	0.8182	0.8182
Benzoyl Peroxide (BPO) Wt. %	1.03	1.03	1.03	1.03	1.03	1.03	1.03	1.03
Porogen Composition
Isooctane. Wt. %	99.112	98.915	98.915	98.915	98.915	98.915	98.915	98.915
Toluene, Wt. %	0	0	0	0	0	0	0	0
Inerts, Wt %	0.8878	1.085	1.085	1.085	1.085	1.085	1.085	1.085
Toluene, plus Inerts, Wt. %	—	—	—	—	—	—	—	—
Isooctane/Toluene plus Inerts	—	—	—	—	—	—	—	—
Ratio
Aquoeus Phase Composition
Sodium Carbonte, Wt. %	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.300
Sodium Nitrite, Wt. %	0.300	0.300	0.300	0.300	0.300	0.300	0.300	0.300
Poly (N-Vinylpyrrolidione),	1.000	0.500	1.300	1.100	1.000	0.200	0.300	0.010
Wt. %
PVP K 30, 45-55 Kdaltons,	0.9	0	1.000	1.000	0.800	0	0	0.010
Wt. %
PVP K 60, 400-500 Kdaltons,	0.100	0.500	0.300	0.100	0.200	0.200	0.300	0
Wt. %
Poly (Vinyl alcohol), Wt. %	0	0	0	0	0	0	0	0.250
Molecular Size, Kdaltons	—	—	—	—	—	—	—	95
Amount Hydrolized, %	—	—	—	—	—	—	—	95
Natrosol Plus, Wt. %								0
Aqueous/Organic Phase	1.1	1.1	1.0	1.0	1.0	1.0	1.0	1.0
Volume Ratio
	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
LDM	02-049	02-050	02-052	02-054	02-055	02-059	02-061	02-073
Organic Phase Composition
Monomer (DVB & EVB) Wt. %	55.0	55.0	55.0	55.0	55.0	55.0	55.0	55.0
Porogen Wt. %	45.0	45.0	45.0	45.0	45.0	45.0	45.0	45.0
Porogen/Monomer Ratio	0.8182	0.8182	0.8182	0.8182	0.8182	0.8182	0.8182	0.8182
Benzoyl Peroxide (BPO) Wt. %	1.03	1.03	1.03	1.03	1.03	1.03	1.03	1.03
Porogen Composition
Isooctane. Wt. %	98.915	98.915	98.915	98.915	98.915	98.915	98.915	98.915
Toluene, Wt. %	0	0	0	0	0	0	0	0
Inerts, Wt %	1.085	1.085	1.085	1.085	1.085	1.085	1.085	1.085
Toluene, plus Inerts, Wt. %	—	—	—	—	—	—	—	—
Isooctane/Toluene plus Inerts	—	—	—	—	—	—	—	—
Ratio
Aquoeus Phase Composition
Sodium Carbonte, Wt. %	0.100	0.500	0.500	0.500	0.500	0.500	0.500	0.500
Sodium Nitrite, Wt. %	0.100	0.300	0.300	0.300	0.300	0.300	0.300	0.300
Poly (N-Vinylpyrrolidione),	0.010	0	0.05	0	0	0	0	0
Wt. %
PVP K 30, 45-55 Kdaltons,	0.010	0	0.05	0	0	0	0	0
Wt. %
PVP K 60, 400-500 Kdaltons,	0	0	0	0	0	0	0	0
Wt. %
Poly (Vinyl alcohol), Wt. %	0.400	0	0	0	0	0	0.300	0.300
Molecular Size, Kdaltons	95	—	—	—	—	170	170	170
Amount Hydrolized, %	95	—	—	—	—	88	88	88
Natrosol Plus, Wt. %	0	0.500	0.300	0.300	0.300	0	0	0
Aqueous/Organic Phase	1.0	1.0	1.0	1.0	1.0	1.0	1.0	1.0
Volume Ratio
		Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
	LDM	02-074	02-075	02-079	02-082	02-083	02-086
	Organic Phase Composition
	Monomer (DVB & EVB) Wt. %	55.0	55.0	55.0	55.0	55.0	55.0
	Porogen Wt. %	45.0	45.0	45.0	45.0	45.0	45.0
	Porogen/Monomer Ratio	0.8182	0.8182	0.8182	0.8182	0.8182	0.8182
	Benzoyl Peroxide (BPO) Wt. %	1.03	1.03	1.03	1.03	1.03	1.03
	Porogen Composition
	Isooctane. Wt. %	98.915	98.915	98.915	98.915	98.915	98.915
	Toluene, Wt. %	0	0	0	0	0	0
	Inerts, Wt %	1.085	1.085	1.085	1.085	1.085	1.085
	Toluene, plus Inerts, Wt. %	—	—	—	—	—	—
	Isooctane/Toluene plus Inerts	—	—	—	—	—	—
	Ratio
	Aquoeus Phase Composition
	Sodium Carbonte, Wt. %	0.500	0.500	0.500	0.500	0.500	0.500
	Sodium Nitrite, Wt. %	0.300	0.300	0.300	0.300	0.300	0.300
	Poly (N-Vinylpyrrolidione),	0	0	0	0	0	0
	Wt. %
	PVP K 30, 45-55 Kdaltons,	0	0	0	0	0	0
	Wt. %
	PVP K 60, 400-500 Kdaltons,	0	0	0	0	0	0
	Wt. %
	Poly (Vinyl alcohol), Wt. %	0.300	0.300	0.300	0.300	0.300	0.3
	Molecular Size, Kdaltons	170	170	170	170	88	170
	Amount Hydrolized, %	88	88	88	88	85	88
	Natrosol Plus, Wt. %	0	0.05	0	0	0	0
	Aqueous/Organic Phase	1.0	1.0	1.0	1.0	1.0	1.0
	Volume Ratio

TABLE 7
Experimental Programs: Response
	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
LDM	02-001	02-004	02-006	02-008	02-010	02-017	02-025
Surface Characteristics
SEM; description (smooth, nodes	nodes,	nodes,	nodes,	nodes,	nodes,	no nodes,	no nodes,
present, open or closed pore	closed	closed	closed	closed	closed	open	open
structure)
Internal Pore Stucture (Dry Beads)
BET Surfrace Area, S, m2g−1	563.5	652.8	615.7	614.4	661.4	520.9	540.0
Porosity, Pwt in ml · g−1	0.9210	1.5370	1.53085	1.7245	1.7722	1.1241	1.3899
Pore modes greater than 100 Å	150	250, 400	250	430	490	250, 390, 495	320, 440
diameter from Desorption			500	550		640, 920	550, 750
Isotherm. List each						1400, 1900	1200, 2900
Pore modes range in Å greater	100-250	100-500	100-600	100-700	100-600	100-2300	100-2900
than 100 Å diameter, Desorption
Isotherm.
Cytochrome C Sorption
Static Assesment 500 mg/Liter Conc.
Mg Cyto C sorbed/g dry polymer	15.2	43.35	42.95	63.05	79.7	135.0	155.8
at 3 hr contact
% of Cyto C removed from solution	19.42	53.80	51.46	66.22	73.78	82.64	82.49
at 3 hr contact
Serum Albumin Sorption
% removed from solution with						6.1	4.15
a concentration of 35,000 mg/l
of serum albumin
Mg BSA (or HSA) sorbed/g dry						681.6	488.22
polymer at 3 hr contact
Coating Assesment
ESCA Measurements for Surface Components, Atom Fraction on surface
C	0.8702	0.8722	0.8917	0.8881	0.8855	0.8613	0.8520
O	0.0784	0.0758	0.0682	0.0729	0.0860	0.1106	0.1480
N	0.0514	0.0520	0.0401	0.0390	0.0284	0.0281	none
							detected
	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
LDM	02-034	02-036	02-038	02-040	02-044	02-054	02-055A
Surface Characteristics
SEM; description (smooth, nodes	no nodes,	no nodes,	nodes,	nodes,	nodes,	nodes,	nodes,
present, open or closed pore	open	open	closed	closed	closed	closed	closed
structure)
Internal Pore Stucture (Dry Beads)
BET Surfrace Area, S, m2g−1	537.2	556.6	556.6	549.6	545.4	536.8	525.2
Porosity, Pwt in ml · g−1	1.9069	1.9588	1.8754	1.8356	1.6420	1.6567	1.6957
Pore modes greater than 100 Å	380, 490	210, 280	210, 280,	300; 390;	250; 310;	280; 350;	290; 390;
diameter from Desorption	620, 930	380, 500,	380 500,	500; 650;	450; 550;	460; 600;	500; 640;
Isotherm. List each		650	650, 930	950	790; 1200	810; 1900	990
Pore modes range in Å greater	100-1600	100-1600	100-1600	100-1600	100-2000	100-2900	100-1700
than 100 Å diameter, Desorption
Isotherm.
Cytochrome C Sorption
Static Assesment 500 mg/Liter Conc.
Mg Cyto C sorbed/g dry polymer	86.6	82.0	54.8	57.7	61.7	73.9	57.8
at 3 hr contact
% of Cyto C removed from solution	85.12	85.26	57.82	61.43	65.55	79.83	63.63
at 3 hr contact
Serum Albumin Sorption
% removed from solution with	4.38		4.9	3.07	4.12
a concentration of 35,000 mg/l
of serum albumin
Mg BSA (or HSA) sorbed/g dry	301.46		311.96	192.10	257.96
polymer at 3 hr contact
Coating Assesment
ESCA Measurements for Surface Components, Atom Fraction on surface
C	0.8981	0.8682	0.8901	0.8586	0.8748	0.8238	0.7924
O	0.0778	0.0935	0.0771	0.0982	0.0897	0.1745	0.2076
N	0.0241	0.0383	0.0328	0.0432	0.355	none	none
						detected	detected
		Sample ID	Sample ID	Sample ID	Sample ID	Sample ID
	LDM	02-075	02-079	02-082	02-083	02-086
	Surface Characteristics
	SEM; description (smooth, nodes	nodes,		nodes,
	present, open or closed pore	closed		closed
	structure)
	Internal Pore Stucture (Dry Beads)
	BET Surfrace Area, S, m2g−1	531.5		528.9
	Porosity, Pwt in ml · g−1	1.5232		1.3708
	Pore modes greater than 100 Å	200; 310;		210; 280;
	diameter from Desorption	410; 530;		380; 490;
	Isotherm. List each	740; 900;		620; 900;
		1200		1300
	Pore modes range in Å greater	100-2400		100-2400
	than 100 Å diameter, Desorption
	Isotherm.
	Cytochrome C Sorption
	Static Assesment 500 mg/Liter Conc.
	Mg Cyto C sorbed/g dry polymer	32.8		61.1
	at 3 hr contact
	% of Cyto C removed from solution	39.00		74.89
	at 3 hr contact
	Serum Albumin Sorption
	% removed from solution with
	a concentration of 35,000 mg/l
	of serum albumin
	Mg BSA (or HSA) sorbed/g dry
	polymer at 3 hr contact
	Coating Assesment
	ESCA Measurements for Surface Components, Atom Fraction on surface
	C	0.8441		0.8830
	O	0.1559		0.1170
	N	none		none
		detected		detected

Numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the attendant claims attached hereto, this invention may be practiced otherwise than as specifically disclosed herein.

Claims

1. A hemocompatible-coated polymer comprising at least one crosslinking agent and at least one dispersing agent whereby said dispersing agent forms a hemocompatible surface on said polymer, said dispersing agent is selected from a group consisting of heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic Acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mix thereof, said crosslinking agent is selected from a group consisting of divinylbenzene, trivinylbenzene, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythrital dimethacrylate, pentaerythrital trimethacrylate, pentaerythrital tetramethacrylate, pentaerythritol diacrylate, penta erythritol triiacrylate, pentaerythritol tetraacrylate, dipentaerythritol dimethacrylate, dipentaerythritol trimethacrylate, dipentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, divinylformamide and mixtures thereof, said polymer being developed simultaneously with the formation of the coating, wherein said dispersing agent gets chemically bound to said surface of said polymer.

2. The polymer of claim 1 wherein said dispersing agent comprises a biocompatibilizing polymer.

3. The polymer of claim 2 wherein said biocompatibilizing polymer comprises poly(N-vinylpyrrolidinone).

4. The polymer of claim 1 wherein said polymer comprises copolymers of divinylbenzene with comonomers being selected from a group consisting of styrene, ethylstyrene, acrylonitrile, butyl methacrylate, octyl methacrylate, butyl acrylate, octyl acrylate, cetyl methacrylate, cetyl acrylate, ethyl methacrylate, ethyl acrylate, vinyltoluene, vinylnaphthalene, vinylbenzyl alcohol, vinylformamide, methyl methacrylate, methyl acrylate and mixtures thereof.

5. The polymer of claim 1 wherein said hemocompatible surfaced polymer is a porous polymer.

6. The polymer of claim 1 wherein said hemocompatible surfaced polymer is an ion exchange polymer.

7. The polymer of claim 2 wherein said biocompatibilizing polymer becomes grafted to the surface of said polymer to provide said hemocompatible surfaced polymer.

8. A biocompatible coated polymer manufactured by a method comprising: polymerizing monomer droplets comprising at least one crosslinking agent to form a polymer and coating said resulting polymer using at least one dispersing agent to thereby form a biocompatible coated polymer, said dispersant being placed on said monomer droplets before polymerization, said dispersing agent is selected from a group consisting of heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof, wherein said dispersing agent gets chemically bound to said surface of said polymer.

9. The polymer of claim 8 wherein said crosslinking agent is polymerized with at least one vinyl monomer.

10. The polymer of claim 8 wherein said dispersing agent forms a hemocompatible coating on the surface of said polymer.

11. The polymer of claim 8 wherein said dispersing agent comprises a biocompatibilizing polymer.

12. The polymer of claim 8 wherein said crosslinking agent is selected from a group consisting of diviylbenzene, trivinylbenzene, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythrital dimethacrylate, pentaerythrital trimethacrylate, pentaerythrital tetramethacrylate, pentaerythritol diacrylate, pentaerythritol triiacrylate, pentaerythritol tetraacrylate, dipentaerythritol dimethacrylate, dipentaerythritol trimethacrylate, dipentaerythritol tetramethacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, divinylformamide and mixtures thereof.

13. The polymer of claim 8 wherein said polymer comprises copolymers of divinylbenzene with comonomers being selected from a group consisting of styrene, ethylstyrene, acrylonitrile, butyl methacrylate, octyl methacrylate, butyl acrylate, octyl acrylate, cetyl methacrylate, cetyl acrylate, ethyl methacrylate, ethyl acrylate, vinyltoluene, vinylnaphthalene, vinylbenzyl alcohol, vinylformamide and mixtures thereof.

14. The polymer of claim 8 wherein said hemocompatible coated polymer is a porous polymer.

15. The polymer of claim 8 wherein said hemocompatible coated polymer is an ion exchange polymer.

16. The polymer of claim 8 wherein said dispersing agent comprises a biocompatibilizing polymer, said biocompatibilizing polymer becomes grafted to the surface of said polymer to provide said hemocompatible coated polymer.

17. The polymer of claim 14 wherein said polymer is processed in non-pyrogenic water.

18. A hemocompatible surface coated polymer system comprising an organic phase and an aqueous phase, said organic phase comprising polymerizable monomers and at least one initiator and said aqueous phase comprising at least one dispersing agent, at least one free radical inhibitor and at least one buffering agent, said organic phase being immiscible in said aqueous phase, wherein the organic phase forms a polymer, and wherein said dispersing agent in the aqueous phase forms a hemocompatible surface on said polymer said dispersing agent is selected from a group consisting of heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof.

19. The system of claim 18 wherein one of said monomer is a monofunctional monomer, said monofunctional monomer is selected from a group consisting of styrene, ethylstyrene, acrylonitrile, butyl methacrylate, octyl methacrylate, butyl acrylate, octyl acrylate, cetyl methacrylate, cetyl acrylate, ethyl methacrylate, ethyl acrylate, vinyltoluene, vinylnaphthalene, vinylbenzyl alcohol, vinylformamide, methyl methacrylate, methyl acrylate and mixtures thereof.

20. The system of claim 18 wherein one of said monomer is a polyfunctional monomer, said polyfunctional monomer is selected from a group consisting of divinylbenzene, trivinylbenzene, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, pentaerythritol diacrylate, pentaerythritol triiacrylate, pentaerythritol tetraacrylate, dipentaerythritol dimethacrylate, dipentaerythritol trimethacrylate, dipentaerythritol tetramethacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, divinylformamide and mixtures thereof.

21. The system of claim 18 wherein said initiator is selected from a group consisting of diacyl peroxides, ketone peroxides, peroxyesters, dialkyl peroxides, peroxyketals, azoalkylnitriles, peroxydicarbonates and mixtures thereof.

22. The system of claim 18 wherein said free radical inhibitor is selected from a group consisting of p-nitrosophenoxide salts, sodium nitrite, N-hydroxy-N-methylglucamine, N-nitroso-N-methylglucamine and mixtures thereof.

23. The system of claim 18 wherein said buffering agent is selected from a group consisting of carbonate salts, bicarbonate salts, boric acid salts, salts of phosphoric acid and mixtures thereof.

24. The system of claim 18 wherein said organic phase further comprises at least one porogen, said porogen being selected from a group consisting of aliphatic hydrocarbons, dialkyl ketones, aliphatic carbinols and mixtures thereof.

25. A containment device for housing hemocompatible polymers, said device comprising a housing with an entrance and an exit, said hemocompatible polymers being situated within said housing of said device, hemocompatible-coated polymer comprising at least one crosslinking agent and at least one dispersing agent whereby said dispersing agent forms a hemocompatible surface on said polymer.

26. The device of claim 25 wherein said dispersing agent is selected from a group consisting of hydroxyethyl cellulose, hydroxypopyl cellulose, poly(hydroxyethyl methacrylate), poly(hydroxyethyl acrylate), poly(hydroxypropyl methacrylate), poly(hydroxypropyl acrylate), poly(dimethylaminoethyl methacrylate), poly-dimethylaminoethyl acrylate), poly(diethylamimoethyl methacrylate), poly-(diethylaminoethyl acrylate), poly(vinyl alcohol), poly(N-vinylpyrrolidinone), salts of poly(methacrylic acid), and salts of poly(acrylic acid), heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof.

27. The device of claim 25 wherein said crosslinking agent is selected from a group consisting of divinylbenzene, trivinylbenzene, divinylnaphthalene, trivinylcyclohexane, divinylsulfone, trimethylolpropane trimethacrylate, trimethylolpropane dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane diacrylate, pentaerythrital dimethacrylate, pentaerythrital trimethacrylate, pentaerythrital tetramethacrylate, pentaerythritol diacrylate, pentaerythritol triiacrylate, pentaerythritol tetraacrylate, dipentaerythritol dimethacrylate, dipentaerythritol trimethacrylate, dipentaerythritol tetramethacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, divinylformamide and mixtures thereof.

28. The device of claim 25 wherein said device further comprises a polycarbonate canister with two polycarbonate end caps with male leur blood connectors, two polypropylene port plugs, two silicone O-rings and two screen assemblies designed to retain said polymers within said canister.

29. An apparatus for containing hemocompatible polymers, said apparatus comprising a housing and a hemocompatible surface coated polymer system situated within said housing, said system comprising an organic phase and an aqueous phase, said organic phase comprising polymerizable monomers and at least one initiator and said aqueous phase comprising at least one dispersing agent, at least one free radical inhibitor and at least one buffering agent, said organic phase being immiscible in said aqueous phase, wherein the organic phase forms a polymer, and wherein said dispersing agent in the aqueous phase forms a hemocompatible surface on said polymer said dispersing agent is selected from a group consisting of hydroxyethyl cellulose, hydroxypopyl cellulose, poly(hydroxyethyl methacrylate), poly(hydroxyethyl acrylate), poly(hydroxypropyl methacrylate), poly(hydroxypropyl acrylate), poly(dimethylaminoethyl methacrylate), poly-(dimethylaminoethyl acrylate), poly(diethylamimoethyl methacrylate), poly-(diethylaminoethyl acrylate), poly(vinyl alcohol), poly(N-vinylpyrrolidinone), salts of poly(methacrylic acid), and salts of poly(acrylic acid), heparin, albumin, carrageenan, konjac flour (glucomannan), guar gum (galactomannan), xanthan gum (polysaccharide of mannose, glucose, and glucuronic acid), gum arabic, gum tragacanth, locust bean gum, karaya gum, salts of carboxymethylcellulose, salts of carboxyethylcellulose, hydrophobically modified hydroxyethylcellulose (Natrosol Plus HMHEC, Grade 330), salts of hyaluronic acid, salts of poly(maleic acid), salts of poly(maleic acid-co-acrylic acid), salts of poly(maleic acid-co-methacrylic acid), salts of poly(itaconic acid), Type B gelatin, poly(ethylene oxide), poly(propylene oxide), poly(acrylamide), poly(methacrylamide), salts of poly(acrylamide-co-acrylic acid), salts of poly(acrylamide-co-methacrylic acid), salts of poly(methacrylamide-co-acrylic acid), salts of poly(methacrylamide-co-methacrylic acid) and mixtures thereof.

30. The apparatus of claim 29 wherein said apparatus further comprises a polycarbonate canister with two polycarbonate end caps with male leur blood connectors, two polypropylene port plugs, two silicone O-rings and two screen assemblies designed to retain said polymers within said canister.