Patent Application
20050152090
The present invention relates to capacitors comprising an inert porous shaped body onto which a first electrically conductive layer, a second layer of barium titanate and a further electrically conductive layer have been applied.
Capacitors perform many tasks in information technology and electric energy engineering. There has in recent times been a search for capacitors which have a high energy density and can perform the task of batteries or be used for covering short-term high load requirements.
Electrochemica Acta 45 (2000), 2483 to 2498, discloses electrochemical or double-layer capacitors. These devices, also known as supercapacitors or ultracapacitors, store electric energy in two capacitors which are connected in series and each have an electric double layer which is formed between the two electrodes and the ions in the electrolyte. The distance in which charge separation occurs is only a few Angstrom. As electrolytes, use is made of highly porous carbon having internal surface areas of up to 2500 m2/g. As indicated by the capacitor formula
C=E0·E·A/d
where C is the capacitance, E0 is the absolute dielectric constant, E is the dielectric constant of the dielectric, A is the area of the capacitor and d is the distance between the electrodes, capacitances of up to 100 farad/cm3 are possible at large areas A and small spacings d.
Such double-layer capacitors (supercapacitors) at present achieve energy densities of from 3 to 7 Wh/kg or Wh/liter, which are far below the energy densities of conventional batteries (lithium ion batteries achieve from 150 to 200 Wh/kg). This is due to the maximum possible voltage loading being restricted to about 3.5 V by the electrochemical stability of the electrolyte.
On the other hand, there is a type of capacitor which operates at high voltages, namely ceramic capacitors comprising dielectrics based on barium titanate.
Ceramic capacitors which comprise dielectrics based on barium titanate and operate at high working voltages because of the high dielectric breakdown resistance of the titanates of up to 200 V/0.1 μm are known from the prior art. However, ceramic capacitors have relatively low capacitances.
It is an object of the present invention to remedy the abovementioned disadvantages.
We have found that this object is achieved by new and improved capacitors which comprise an inert porous shaped body onto which a first electrically conductive layer, a second layer of barium titanate and a further electrically conductive layer have been applied.
The capacitors of the present invention can be produced as follows:
An inert porous shaped body can, in a first step, be provided with a first electrically conductive layer and this can be provided with a contact. A second layer of barium titanate can be applied on top of the first layer and, finally, another electrically conductive layer can be applied on top of this titanate layer and be provided with a contact. The capacitors obtained in this way can be hermetically sealed, e.g. encapsulated, except for the electric contacts.
Suitable porous shaped bodies are in general catalyst support materials, for example those based on metal oxides such as aluminum oxide, silicon dioxide, titanium dioxide, zirconium dioxide, chromium oxide or mixtures thereof, preferably aluminum oxide, silicon dioxide, titanium dioxide, zirconium dioxide or mixtures thereof, particularly preferably aluminum oxide, zirconium dioxide or mixtures thereof, or carbides, preferably silicon carbide, having a BET-surface area of from 0.1 to 20 m2/g, preferably from 0.5 to 10 m2/g, particularly preferably from 1 to 5 m2/g, a pore content of from 10 to 90% by volume, preferably from 30 to 85% by volume, particularly preferably from 50 to 80% by volume, and pore sizes of from 0.01 to 100 μm, preferably from 0.1 to 30 μm, particularly preferably from 1 to 10 μm.
The shaped bodies can have any shapes, for example rings, pellets, stars, wagon wheels, honeycombs, preferably cuboids, cylinders, rectangles or boxes of generally any size (diameter, longest edge length). In the case of capacitors for information technology, for example, the size is generally in the range from 1 to 10 mm. Larger dimensions are necessary in energy engineering.
To produce the first conductive layer on the shaped body, metals such as copper, nickel, chromium or mixtures thereof can be applied in any layer thickness, generally from 10 nm to 1000 nm, preferably from 50 nm to 500 nm, particularly preferably from 100 nm to 200 nm.
The application of the electrically conductive layer to the shaped body can be carried out using all known methods such as vapor deposition, sputtering or electroless plating, preferably electroless plating. In electroless plating, the shaped bodies are infiltrated or impregnated with suitable, commercially available plating liquids and heated to temperatures below 100° C. to deposit the metal. After metal deposition, the liquid, usually water, can be removed at elevated temperatures and, if desired, under reduced pressure.
It is also possible, for example in the case of iron or nickel, to produce the first conductive layer by heating the shaped bodies in iron carbonyl or nickel carbonyl vapors. In the case of iron, the shaped bodies can be heated to from about 150 to 200° C., and in the case of nickel to from 50 to 100° C.
In a preferred embodiment, the shaped bodies can be heated to elevated temperatures of from 50 to 100° C. in an inert atmosphere (e.g. nitrogen or argon) to produce a homogeneous metal layer. It may be advantageous to apply crystallization nuclei, e.g. nuclei based on platinum metals, likewise by impregnation with suitable liquids (see above).
Finally, the first metal layer can be provided with a contact. This can be carried out, for example, by soldering a metal foil onto an area of the metal-coated shaped body (production of the first electrode).
A dielectric can then be applied on top of the initially produced electrode. This is advantageously carried out using dispersions of crystalline titanate particles having sizes of less than 10 nm in alcohols. Such dispersions can be prepared by reaction of titanium alkoxides with barium hydroxides or strontium hydroxides in alcoholic solution as described in the German application No.: 102 21 499.9 (O.Z. 0050/53537).
The shaped body can be infiltrated or impregnated with such a dispersion which may contain from 5 to 60% by weight, preferably from 10 to 40% by weight, of titanate particles, followed by removal of the alcohol by increasing the temperature to 30-100° C., preferably 50-80° C., and, if desired, reducing the ambient pressure to deposit the titanium particles on the first electrode.
To produce a homogeneous, dense layer of the dielectric, the shaped bodies can be heated to from 700 to 1200° C., preferably from 900 to 1100° C., in an inert gas atmosphere so that the titanate particles sinter together to form a dense film.
To increase the layer thickness, the impregnation with the titanate dispersion and the sintering can be repeated a number of times. The layer thickness is generally from 10 to 1000 nm, preferably from 20 to 500 nm, particularly preferably from 100 to 300 nm.
Finally, a second electrode layer can be applied in a manner analogous to that employed for the first.
After the second electrode layer has been applied, this can be provided with a contact on the side opposite the first contact, thus producing the capacitor. The latter can be hermetically encapsulated to protect it and for the purposes of insulation.
The capacitors of the present invention are suitable as smoothing capacitors or energy storing capacitors or phase shift capacitors in electric energy engineering and as coupling capacitors, filter capacitors or miniature energy storage capacitors in information technology.
The capacitors of the present invention may be illustrated as follows:
A specific surface area (BET surface area) of the porous shaped body of 2 m2/g and a barium titanate layer thickness of 0.1 μm at a relative dielectric constant of 5000 (“The Effect of Grain Size on the Dielectric Properties of Barium Titanate Ceramic”, A. J. Bell and A. J. Moulson, in Electrical Ceramics, British Ceramic Proceedings No. 36, October 1985, pages 57-65) gives a capacitance calculated according to the formula on page 1, line 29, of about 1 farad/cm3. Such a capacitor can be charged to a voltage of 200 V, and its energy density is then 20 000 Ws/cm3 or approximately 5.5 kWh/liter.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102 21 498.0 | May 2002 | DE | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP03/04928 | 5/12/2003 | WO |