High performance thermoplastic compositions with improved melt flow properties

Information

  • Patent Grant
  • 6673872
  • Patent Number
    6,673,872
  • Date Filed
    Wednesday, May 17, 2000
    24 years ago
  • Date Issued
    Tuesday, January 6, 2004
    20 years ago
Abstract
A high performance thermoplastic polymer composition having improved melt flow properties, comprising a thermoplastic polymer resin and a low intrinsic viscosity poly(arylene ether). Preferred thermoplastic polymers are poly(imide) polymers.
Description




BACKGROUND OF THE INVENTION




High performance thermoplastic polymers such as poly(etherimide)s have been used to fabricate parts for numerous applications. Each application requires particular tensile and flexural properties, impact strength, heat distortion temperature (HDT), and resistance to warp. For example, U.S. Pat. No. 4,455,410 provides a poly(etherimide)-poly(phenylene sulfide) blend having good flexural strength characteristics. U.S. Pat. No. 3,983,093 provides poly(etherimide) compositions that have improved solvent resistance and are suitable for use in preparing films, molding compounds, coatings, and the like.




These thermoplastic polymers are characterized by a high glass transition temperature, usually above about 180° C., which makes them suitable for use in applications that require exposure to high temperatures. A drawback of these materials is that they exhibit poor melt flow properties, which makes processing difficult. Injection molding of thermoplastic polymers, for instance, is more easily performed with a thermoplastic resin that has a higher melt volume rate (MVR). Good melt flow properties are necessary to achieve fast molding cycles and to permit molding of complex parts. At the same time, mechanical properties such as impact strength and ductility must be maintained in order to pass product specifications.




U.S. Pat. No. 4,431,779 to White et al. discloses blends of polyetherimide and polyphenylene ether which exhibit good impact strength as well as good mechanical properties. White et al. focus on the comparability of polyphenylene ethers with polyetherimide, teaching that homogenous blends and non-uniform products may result. However, if amorphous polymers are employed, they are compatible and transparent films may be cast. The compatibility of the polyphenylene ethers to polyetherimide lessens as the quantity of aliphatic groups in the polymer increases. Although White et al. discuss polypheneylene ether polymers, they fail to teach the effects of such polymers and polymer blends on melt flow characteristics.




There accordingly remains a need in the art for thermoplastic polymers with improved melt flow properties, without the consequent loss of other desirable characteristics in the finished product.




BRIEF SUMMARY OF THE INVENTION




The above-described needs are met by a high performance, thermoplastic polymer composition having improved melt flow properties, comprising a high Tg, thermoplastic polymer resin and a poly(arylene ether) having a low intrinsic viscosity, preferably less than about 0.25 deciliters per gram (dl/g). Addition of low intrinsic viscosity poly(arylene ether)s generally have no or minimal detrimental effects on other physical properties of the thermoplastic polymer compositions.




DETAILED DESCRIPTION OF THE INVENTION




Addition of a poly(arylene ether) having a low intrinsic viscosity (IV) to high performance, high Tg, amorphous thermoplastic polymers provides highly improved melt flow properties to such polymers, without causing degradation of important mechanical properties such as impact strength and ductility. Other optional additives may also be used in the compositions to obtain other desired polymer properties.




Suitable high performance, high Tg thermoplastic polymer resins are known in the art, and typically have glass transition temperatures (Tg) of about 170° C. or greater, with about 200° C. or greater preferred. Exemplary resins include poly(imide), poly(sulfone), poly(ether sulfone), and other polymers.




Useful thermoplastic poly(imide) resins have the general formula (I):











wherein a is more than 1, typically about 10 to about 1,000 or more, and more preferably about 10 to about 500; and V is a tetravalent linker without limitation, as long as the linker does not impede synthesis or use of the polyimide. Suitable linkers include but are not limited to: (a) substituted or unsubstituted, saturated, unsaturated or aromatic monocyclic and polycyclic groups having about 5 to about 50 carbon atoms, (b) substituted or unsubstituted, linear or branched, saturated or unsaturated alkyl groups having 1 to about 30 carbon atoms; or combinations comprising at least one of the foregoing. Suitable substitutions and/or linkers include, but are not limited to, ethers, epoxides, amides, esters, and combinations comprising at least one of the foregoing. Preferred linkers include but are not limited to tetravalent aromatic radicals of formula (II), such as:











wherein W is a divalent moiety selected from the group consisting of —O—, —S—, —C(O)—, —SO


2


—, C


y


H


2y


—, C


y


H


2y-2


— (y being an integer from 1 to 10), and halogenated derivatives thereof, including perfluoroalkylene groups, or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions, and wherein Z includes, but is not limited, to divalent radicals of formula (III):











R in formula (I) includes but is not limited to substituted or unsubstituted divalent organic radicals such as: (a) aromatic hydrocarbon radicals having about 6 to about 20 carbon atoms and halogenated derivatives thereof; (b) straight or branched chain alkylene radicals having about 2 to about 20 carbon atoms; (c) cycloalkylene radicals having about 3 to about 20 carbon atoms, or (d) divalent radicals of the general formula (IV):











wherein Q includes but is not limited to a divalent moiety selected from the group consisting of —O—, —S—, —C(O) —, —SO


2


—, C


y


H


2y


—, C


y


H


2y-2


— (y being an integer from 1 to 10), and halogenated derivatives thereof, including perfluoroalkylene groups.




Preferred classes of poly(imide) polymers include poly(amide imide) polymers and poly(etherimide) polymers, particularly those poly(etherimide) polymers known in the art which are melt processable, such as those whose preparation and properties are described in U.S. Pat. Nos. 3,803,085 and 3,905,942, each of which is incorporated herein by reference.




Preferred poly(etherimide) resins comprise more than 1, typically about 10 to about 1000 or more, and more preferably about 10 to about 500 structural units, of the formula (V):











wherein T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions, and wherein Z includes, but is not limited, to divalent radicals of formula (III) as defined above.




In one embodiment, the poly(etherimide) may be a copolymer which, in addition to the etherimide units described above, further contains poly(imide) structural units of the formula (VI):











wherein R is as previously defined for formula (I) and M includes, but is not limited to, radicals of formula (VII):











The poly(etherimide) can be prepared by any of the methods known to those skilled in the art, including the reaction of an aromatic bis(ether anhydride) of the formula (VIII):











with an organic diamine of the formula (IX):




 H


2


N—R—NH


2


  (IX)




wherein T and R are defined as described above in formulas (I) and (IV).




Examples of specific aromatic bis(ether anhydride)s and organic diamines are disclosed, for example, in U.S. Pat. Nos. 3,972,902 and 4,455,410, which are incorporated herein by reference. Illustrative examples of aromatic bis(ether anhydride)s of formula (VIII) include: 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride (i.e., the dianhydride of bisphenol-A); 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)benzophenone dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride; 2,2-bis[4-(2,3-dicarboxyphenoxy)phenyl]propane dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)benzophenone dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfone dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl-2,2-propane dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl ether dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)benzophenone dianhydride and 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride, as well as various mixtures comprising at least one of the foregoing aromatic bis(ether anhydride)s.




The bis(ether anhydride)s can be prepared by the hydrolysis, followed by dehydration, of the reaction product of a nitro substituted phenyl dinitrile with a metal salt of dihydric phenol compound in the presence of a dipolar, aprotic solvent. A preferred class of aromatic bis(ether anhydride)s included by formula (VIII) above includes, but is not limited to, compounds wherein T is of the formula (X):











and the ether linkages, for example, are preferably in the 3,3′, 3,4′, 4,3′, or 4,4′ positions, and mixtures comprising at least one of the foregoing linkages, and where Q is as defined above.




Many diamino compound may be employed. Examples of suitable compounds are ethylenediamine, propylenediamine, trimethylenediamine, diethylenetriamine, triethylenetetramine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, nonamethylenediamine, decamethylenediamine, 1,12-dodecanediamine, 1,18-octadecanediamine, 3-methylheptamethylenediamine, 4,4-dimethylheptamethylenediamine, 4-methylnonamethylenediamine, 5-methylnonamethylenediamine, 2,5-dimethylhexamethylenediamine, 2,5-dimethylheptamethylenediamine, 2,2-dimethylpropylenediamine, N-methyl-bis (3-aminopropyl) amine, 3-methoxyhexamethylenediamine, 1,2-bis(3-aminopropoxy) ethane, bis(3-aminopropyl)sulfide, 1,4-cyclohexanediamine, bis-(4-aminocyclohexyl) methane, m-phenylenediamine, p-phenylenediamine, 2,4-diaminotoluene, 2,6-diaminotoluene, m-xylylenediamine, p-xylylenediamine, 2-methyl-4,6-diethyl-1,3-phenylene-diamine, 5-methyl-4,6-diethyl-1,3-phenylene-diamine, benzidine, 3,3′-dimethylbenzidine, 3,3′-dimethoxybenzidine, 1,5-diaminonaphthalene, bis(4-aminophenyl) methane, bis(2-chloro-4-amino-3,5-diethylphenyl) methane, bis(4-aminophenyl) propane, 2,4-bis(b-amino-t-butyl)toluene, bis(p-b-amino-t-butylphenyl) ether, bis(p-b-methyl-o-aminophenyl)benzene, bis(p-b-methyl-o-aminopentyl) benzene, 1,3-diamino-4-isopropylbenzene, bis(4-aminophenyl) sulfide, bis (4-aminophenyl) sulfone, bis(4-aminophenyl) ether, and 1,3-bis(3-aminopropyl) tetramethyldisiloxane. Mixtures comprising at least one of these compounds may also be present. The preferred diamino compounds are aromatic diamines, especially m- and p-phenylenediamine, hexamethylenediamnine, aliphatic diamines, and mixtures comprising at least one of the foregoing diamines.




In a particularly preferred embodiment, the poly(etherimide) resin comprises structural units according to formula (V) wherein each R is independently p-phenylene or m-phenylene or a mixture comprising at least one of the foregoing Rs, and T is a divalent radical of the formula (XI):











Included among the many methods of making the poly(imide)s, particularly poly(etherimide) polymers, are those disclosed in U.S. Pat. Nos. 3,847,867, 3,814,869, 3,850,885, 3,852,242, 3,855,178, 3,983,093, and 4,443,591. These patents are incorporated herein by reference for the purpose of teaching, by way of illustration, general and specific methods for preparing polyimides.




In general, the reactions can be carried out employing well-known solvents, e.g., o-dichlorobenzene, m-cresol/toluene and the like, to effect a reaction between the anhydride of formula (VIII) and the diamine of formula (IX), at temperatures of about 100° C. to about 250° C. Alternatively, the poly(etherimide) can be prepared by melt polymerization of aromatic bis(ether anhydride)s (VIII) and diamines (IX) by heating a mixture of the starting materials to elevated temperatures with concurrent stirring. Generally, melt polymerizations employ temperatures of about 200° C. to about 400° C. Chain stoppers and branching agents may also be employed in the reaction. When polyetherimide/polyimide copolymers are employed, a dianhydride, such as pyromellitic dianhydride, is used in combination with the bis(ether anhydride). The poly(etherimide) resins can optionally be prepared from reaction of an aromatic bis(ether anhydride) with an organic diamine in which the diamine is present in the reaction mixture at no more than about 0.2 molar excess, and preferably less than about 0.2 molar excess. Under such conditions the poly(etherimide) resin has less than about 15 microequivalents per gram (μeq/g) acid titratable groups, and preferably less than about 10 μeq/g acid titratable groups, as shown by titration with chloroform solution with a solution of 33 weight percent (wt %) hydrobromic acid in glacial acetic acid. Acid-titratable groups are essentially due to amine end-groups in the poly(etherimide) resin.




Generally, useful poly(etherimide) resins have a melt flow rate of about 1.0 to about 200 grams per ten minutes (“g/10 min”), as measured by American Society for Testing Materials (“ASTM”) D1238 at 337° C., using a 6.6 kilogram (“kg”) weight. In a preferred embodiment, the polyetherimide resin has a weight average molecular weight (Mw) of about 10,000 to about 150,000 grams per mole (“g/mole”), as measured by gel permeation chromatography, using a polystyrene standard. Such polyetherimide resins typically have an intrinsic viscosity greater than about 0.2 deciliters per gram (“dl/g”), preferably about 0.35 to about 0.7 dl/g measured in m-cresol at 25° C. Some such polyetherimides include, but are not limited to ULTEM® 1000 (number average molecular weight (Mn) 21,000; weight average molecular weight (Mw) 54,000; dispersity 2.5), ULTEM® 1010 (Mn 19,000; Mw 47,000; dispersity 2.5), ULTEM® 1040 (Mn 12,000; Mw 34,000-35,000; dispersity 2.9), or mixtures comprising at least one of the foregoing polyetherimides.




Poly(sulfone) polymers are derivatives of polysulfides and have more than one, typically more than 10 repeating units of the formula —Ar—SO


2


—. Preferred resins polysulfones are amorphous resins with high resistivity and dielectric strength. Polysulfones have high resistance to thermo oxidative conditions, and hydrolytic stability, making them suitable for appliances, electronic components, aircraft interior parts, and biological and medical devices.




The term “sulfone polymer”, as used herein, is intended to encompass those sulfone polymers featuring the sulfone group. Such materials are well known and are described in a number of places including, but not limited to: U.S. Pat. No. 4,080,403, U.S. Pat. No. 3,642,946; Modern Plastics Encyclopedia, 1977-78, pp. 108, 110-11 and 112; Kirk-Othmer Encyclopedia of Chemical Technology, Second Edition, Vol. 16, pp. 272-281 (1968); and Handbook of Plastics and Elastomers, C. A. Harper, ed., McGraw-Hill, Inc., 1975 pp. 1-69 and 1-95 to 96; all of which are incorporated herein by reference. Representative polymers of this type include poly(sulfone), poly(ether sulfone), poly(phenyl sulfone) and the like, as well as mixtures comprising at least one of the foregoing poly(sulfone)s. Commercially available sulfone polymers include those sold under the following trademarks: UDEL, RADEL A, RADEL R (commercially available from BP Amoco) and VICTREX (commercially available from ICI Americas, Inc.).




Suitable poly(arylene ether) polymers are those having low intrinsic viscosities. Poly(arylene ether) polymers are known, comprising a plurality of structural units of the formula (XII):











wherein for each structural unit, each Q


1


is independently halogen, primary or secondary lower alkyl (e.g., alkyl containing up to 7 carbon atoms), phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q


2


is independently hydrogen, halogen, primary or secondary lower alkyl phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined for Q


1


. Preferably, each Q


1


is alkyl or phenyl, especially C


1-4


alkyl, and each Q


2


is hydrogen. Meanwhile, n is less than 50, with less than about 40 preferred, and about 10 to about 25 especially preferred.




Both homopolymer and copolymer poly(arylene ether) resins may be used. The preferred homopolymers are those containing 2,6-dimethylphenylene ether units. Suitable copolymers include random copolymers containing, for example, such units in combination with 2,3,6-trimethyl-1,4-phenylene ether units or copolymers derived from copolymerization of 2,6-dimethylphenol with 2,3,6-trimethylphenol. Also included are poly(arylene ether)-containing moieties prepared by grafting vinyl monomers or polymers such as polystyrenes, as well as coupled poly(arylene ether) in which coupling agents such as low molecular weight polycarbonates, quinones, heterocycles and formals undergo reaction in known manner with the hydroxy groups of two poly(arylene ether) chains to produce a higher molecular weight polymer. Combinations of any of the above may also be used.




The poly(arylene ether) generally has a number average molecular weight of less than 6,000, with about 1,200 to about 4,800 preferred, and about 1,200 to about 3,000 especially preferred, as determined by gel permeation chromatography. Effective improvement in melt flow properties is generally achieved by use of poly(arylene ether) resins wherein the intrinsic viscosity (IV) of the resin is below 0.30 deciliters per gram (dl/g), preferably up to 10 about 0.25 dl/g, more preferably up to about 0.20 dl/g, and most preferably about 0.10 to about 0.15 dl/g (all measured in chloroform at 25° C.).




The poly(arylene ether) ether polymers suitable for use in this invention may be prepared by any number of processes known in the art from corresponding phenols or reactive derivatives thereof. Poly(arylene ether) resins are typically prepared by the oxidative coupling of at least one monohydroxy aromatic compound such as 2,6-xylenol or 2,3,6-trimethylphenol. Catalysts systems are generally employed for such coupling and contain at least one heavy metal compound such as copper, manganese, or cobalt compounds, usually in combination with various other materials. Catalyst systems containing a copper compound are usually combinations of cuprous or cupric ions, halide (e.g., chloride, bromide, or iodide) ions and at least one amine such as cuprous chloride-trimethylamine. Catalyst systems which contain manganese compounds are generally alkaline systems in which divalent manganese is combined with such anions as halide, alkoxide or phenoxide. Most often, the manganese is present as a complex with one or more complexing and/or chelating agents such as dialkylamines, alkylenediamines, o-hydroxy aromatic aldehydes, o-hydroxyazo compounds and o-hydroxyaryl oximes. Examples of manganese containing catalysts include manganese chloride-and manganese chloride-sodium methylate. Suitable cobalt type catalyst systems contain cobalt salts and an amine.




Examples of catalyst systems and methods for preparing poly(arylene ether) resins are set forth in U.S. Pat. Nos. 3,306,874, 3,306,875, 3,914,266 and 4,028,341 (Hay), 3,257,357 and 3,257,358 (Stamatoff), 4,935,472 and 4,806,297 (S. B. Brown et al.) and 4,806,602 (White et al.).




In general, the molecular weight of the poly(arylene ether) resins can be controlled by controlling the reaction time, the reaction temperature and the amount of catalyst. Long reaction times provide a higher average number of repeating units and a higher intrinsic viscosity. At some point, a desired molecular weight (intrinsic viscosity) is obtained and the reaction terminated by conventional means. For example, in the case of reaction systems which make use of a complex metal catalysts, the polymerization reaction may be terminated by adding an acid, e.g., hydrochloric acid, sulfuric acid and the like or a base e.g., potassium hydroxide and the like and the product is separated from the catalyst by filtration, precipitation or other suitable means as taught by Hay in U.S. Pat. No. 3,306,875. The ultra low intrinsic viscosity poly(arylene ether) resin may be recovered from the reaction solution used in the synthesis of higher molecular weight resins after the higher molecular weight resins have been separated.




It is preferable to employ ultra low IV poly(arylene ether) resin that is not recovered from a reaction solution by precipitation in a non-solvent. The solids recovered by these techniques are too fine and light, i.e. have an unacceptably low bulk density, to properly feed into processing equipment. It is preferable to employ ultra low LV poly(arylene ether) resin that is recovered from the reaction solution as a solid mass or in the form of an agglomerate having a size of at least 100 μm; preferably of a size greater than


1


mm. Agglomerates can be formed by spray drying the reaction solution. The ultra low IV poly(arylene ether) resin can be recovered as a solid mass in conventional equipment where the solvent is stripped off at elevated temperatures. This can be accomplished in conventional vented extruders, or vacuum/vented extruders, as such described in U.S. Pat. No. 5,204,410, or film evaporators, such as described in U.S. Pat. Nos. 5,419,810 and 5,256,250. The reaction solution may be concentrated as described in U.S. Pat. No. 4,692,482 to facilitate the removal of solvent performed by this equipment and minimize the exposure of the ultra low viscosity poly(arylene ether) resin to thermal stress. Forming a solid mass enables the ultra low viscosity poly(arylene ether) to be pelletized to a conventional pellet size of about 3 millimeters (mm) or any desired size. The ultra low LV poly(arylene ether) is preferably of a conventional pellet size so that it can be easily handled in feed hoppers for the equipment used to form the poly(arylene ether) blend with the high Tg amorphous thermoplastic polymer resin, and optionally additives. Preferably, this is accomplished with minimal thermal stress so that the formation of impurities is not a problem, as is taught in U.S. patent application Ser. No. 09/547,648, which is incorporated herein by reference.




Particularly useful poly(arylene ether) polymers are those which comprise molecules having at least one aminoalkyl-containing end group. The aminoalkyl radical is typically located in an ortho position to the hydroxy group. Products containing such end groups may be obtained by incorporating an appropriate primary or secondary monoamine such as di-n-butylamine or dimethylamine as one of the constituents of the oxidative coupling reaction mixture. Also frequently present are 4-hydroxybiphenyl end groups, typically obtained from reaction mixtures in which a by-product diphenoquinone is present, especially in a copper-halide-secondary or tertiary amine system. A substantial proportion of the polymer molecules, typically constituting as much as about 90 wt % of the polymer, may contain at least one of the aminoalkyl-containing and 4-hydroxybiphenyl end groups.




The high performance, thermoplastic polymer compositions having improved melt flow properties may optionally comprise various other additives known in the art. Exemplary additives include antioxidants, for example organophosphites such as tris(nonyl-phenyl)phosphite, tris(2,4-di-t-butylphenyl)phosphite, bis(2,4-di-t-butylphenyl)pentaerythritol diphosphite and distearyl pentaerythritol diphosphite; alkylated monophenols, polyphenols and alkylated reaction products of polyphenols with dienes, such as tetrakis{methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)}methane and octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate; butylated reaction products of para-cresol and dicyclopentadiene; alkylated hydroquinones; hydroxylated thiodiphenyl ethers; alkylidene-bisphenols; benzyl compounds; esters of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of beta-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of thioalkyl or thioaryl compounds, such as, distearylthiopropionate, dilaurylthiopropionate, and ditridecylthiodipropionate; and amides of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid.




Additives, i.e. fillers and reinforcing agents, are also known, such as, for example, conductive materials (such as metal flakes, metal particles, metal fibers, metal coated glass flakes, metal coated micas, carbon fibers, metal coated micas, carbon fibers, carbon nanotubes, metal coated fibers, and the like), silicates, titanium dioxide, ceramics, glass in the form of continuous glass fibers, spheres, particles, flaked glass, milled glass, fiber glass (especially chopped fiber glass), and mixtures comprising at least one of the foregoing glasses, carbon black, graphite, calcium carbonate, talc, and mica, and mixtures comprising at least one of the foregoing fillers and reinforcing agents. Other additives include mold release agents, compatibilizers, UV absorbers, anti-drip agents, stabilizers such as light stabilizers and others, lubricants, plasticizers, pigments, dyes, colorants, anti-static agents, blowing agents, flame retardants, impact modifiers, crystallization nucleators, and the like, as well as mixtures comprising at least one of the foregoing additives.




In the present high performance, thermoplastic polymer compositions, the high Tg amorphous thermoplastic resin component may be present in an amount of about 40 wt % to about 99.9 weight percent (wt %) of the total composition, with about 50 wt % to about 99 wt % preferred, and about 70 wt % to about 95 wt % especially preferred, with the remainder comprising a quantity of the low intrinsic viscosity poly(arylene ether). The effective quantity of low intrinsic viscosity poly(arylene ether) will vary depending on the properties of the high Tg thermoplastic resin component and any additional components (if present), and is readily determined by one of ordinary skill in the art. Such quantities will generally be in up to about 50 wt % based on the total composition, with about 0.1 to about 50 wt % preferred, about 1 to about 40 wt % more preferred, with about 5 wt % to about 30 wt % especially preferred. The thermoplastic polymer composition can further comprise about 0.1 wt % to about 50 wt % additives (e.g., fillers, reinforcing agents, etc.), with about 5 wt % to about 40 wt % preferred, and about 15 wt % to about 30 wt % especially preferred.




The preparation of the high performance, thermoplastic polymer compositions is normally achieved by merely blending the components under conditions suitable for the formation of an intimate blend. Such conditions may include solution blending or melt mixing in single or twin screw type extruders, mixing bowl, roll, kneader, or similar mixing devices that can apply a shear to the components. Twin screw extruders are often preferred due to their more intensive mixing capability over single screw extruders. It is often advantageous to apply a vacuum to the blend through at least one vent port in the extruder to remove volatile components in the composition.




Meanwhile, the blend is preferably sufficiently heated such that the components are in the molten phase, thereby enabling intimate mixing. Typically, temperatures up to about 350° C. can be employed, with about 250° C. to about 350° C. preferred.




The blended, high performance, thermoplastic polymer compositions can be molded into useful articles, such as, for example, heat resistant containers, by a variety of means such as, for example, injection molding, compression molding, thermoforming, and blow molding, among others conventionally known in the art. All patents cited are incorporated herein by reference.




The invention will be further described by the following examples, which are meant to be illustrative, not limiting.











EXAMPLES




TABLE 1: Control 1 and Examples 1 and 2; Control 2 and Examples 3-5




All formulations were compounded in a 25 millimeter (mm) Werner & Pfleiderer co-rotating twin screw extruder operating at a temperature of 360° C., and a speed of 300 rpm. The extrudate was quenched in a water bath and pelletized.




The pellets were dried for a minimum of 4 hours at 135° C. then injection molded into various test specimens using a 130 ton Stork injection molding machine with a melt temperature of 360° C. and a mold temperature of 140° C. The physical and mechanical properties of these formulations are reported in Table 1. Details of the test procedures are described in the experimental section that follows.




For Control 1 and Examples 1 and 2, the formulations were prepared with 0, 1, and 4 parts, respectively, of low IV (0.12 dl/g) PPO® SA120 (poly(phenylene ether) commercially available from GE Plastics, Pittsfield, Mass.) in ULTEM®1000 (polyetherimide commercially available from GE Plastics, Pittsfield, Mass.). Examples 1 and 2, which contain the low IV PPO®, have significantly better melt flow than the Control 1 without any loss in either the tensile or impact properties. The melt flow increases with SA120 PPO® content.




The formulations for Control 2, and Examples 3-5 were prepared using a lower molecular weight polyetherimide resin, ULTEM® 1010, with 0, 1, 3 and 5 parts of low IV PPO® SA120, respectively. Once again, the flow improves with increasing levels of low IV PPO® resin without a loss in either the tensile or impact properties.




















TABLE 1











Control






Control










1




1




2




2




3




4




5































Component













ULTEM ® 1010







100




99




97




95






(wt %)






ULTEM ® 1000




100




99




96






(wt %)






PPO ® SA120





1




4





1




3




5






0.12 IV (wt %)












Properties



















MVR, 360° C./5 kg




20.4




21.7




27.6




40.4




40.2




46.3




51






(cc/10 min)






Plate-plate MV,




1152




903




563




697




609




539




493






360° C.






Tensile Modulus




3345




3271




3248




3334




3333




3329




3331






(MPa)






Tensile Yield




114




114




112




109




110




112




111






Stress (MPa)






Tensile




11




23




13




5




8




13




8






Elongation (%)






Izod Notched




4.8




5.2




4.9




4.8




4.9




4.7




5.1






Impact (kJ/m


2


)














TABLE 2: Control 3, Comparative Example 1, and Example 6




Two formulations were prepared with 30 parts of 0.48 IV PPO® (Comp. 1) or 0.12 IV PPO® SA120 (Example 6) in a polyetherimide resin of ULTEM® 1010. An unfilled polyetherimide resin was included as a control (Control 3). All formulations were compounded and molded into test specimens consistent with the procedures outlined in the examples from Table 1.




Test data in Table 2 indicates that the use of low IV PPO® in place of the 0.48 IV PPO® resulted in a significant improvement in flow. Although there is a decrease in the tensile and impact properties with the use of low IV PPO® at these high loadings, the properties are suitable for a variety of applications.

















TABLE 2











Units




Control 3




Comp 1




6




























Component










ULTEM ® 1010




wt %




100




70




70






PPO ® 803, 0.48 IV




wt %









30











PPO ® SA120, 0.12 IV




wt %














30












Properties
















MVR, 295° C./10 kg




cc/10




0.5




8




60







min






Tensile Modulus




MPa




3300




3000




3200






Tensile Yield Stress




MPa




116




93




46






Tensile Elongation




%




16




5




1






Izod Unnotched




kJ/m


2






60




51




8






Impact






Vicat-B




° C.




213




209




196














TABLE 3: Control 4, Comparative Examples 2-4, and Examples 7-9




Polyetherimide formulations containing 20 parts of chopped glass fiber with 0, 3, 5, and 7 parts of either a 0.46 IV PPO® or 0.12 IV PPO® SA120 were dry blended and compounded in a 2.5 inch Egan single screw extruder operating at a temperature of 360° C. and 100 rpm. The glass fiber was fed in the feed throat. The extrudate was quenched in a water bath and pelletized.




The pellets were dried for a minimum of 4 hours at 140° C. before molding into various ASTM test specimens using a 150 ton Newbury injection molding machine at a melt temperature of 360° C. and a mold temperature of 140° C. The results of the various physical and mechanical properties are reported in Table 3. Details of the test procedures follow the tabulated data.




As determined by capillary rheometry and melt flow rate (MFR), the formulations containing the low IV PPO® SA120, Examples 8, 9 and 10, have significantly better flow than the formulations made with the higher IV PPO®. Also, there is no loss in tensile properties or HDT values with loadings up to 5 wt %. In Example 10, there is a reduction in tensile strength and elongation, but the properties are sufficient for a variety of applications.




















TABLE 3











Control





Comp





Comp





Comp







4




7




2




8




3




9




4































Component













ULTEM ® 1010 (wt %)




80




77




77




75




75




73




73






PPO ® SA120, 0.12 IV (wt %)





3





5





7






PPO ® 646 0.46 IV (wt %)






3





5





7






Glass (wt %)




20




20




20




20




20




20




20












Properties



















Capillary MV, 337° C. @




245




186




233




127




222




86




215






5120 s


−1


(Pa-s)






MFR 337° C./6.6 kg




13.5




14.4




12.4




16.6




12.6




23.3




12.7






(cc/10 min)






Tensile Modulus (Kpsi)




926




950




1024




1110




1010




1224




1006






Tensile Yield Stress (Kpsi)




21




21




21.4




19.1




20.6




12.8




19.7






Tensile Elongation (%)




3.6




3




3




2.2




3




1.4




2.9






HDT (° C.)




209




209




210




208




210




208




210






UL 94, V-0 Thickness (mils)




16




16





16





16














TABLE 4: Control 5 and Examples 10-12




Polyetherimide formulations containing 30 parts chopped glass fibers with 0, 1, 3, and 5 parts, respectively, of low IV PPO® SA120 were compounded and molded at 380° C. using similar procedures outlined in Table 1. The glass fibers were side fed into the 28 mm WP extruder. Data from Examples 10-12 show an improvement in flow without a significant loss in mechanical or impact performance when compared to Control 5.


















TABLE 4












Control










Units




5




10




11




12





























Component











ULTEM ® 1010




wt %




70




69




67




65






PPO ® SA120, 0.12 IV




wt %









1




3




5






Glass




wt %




30




30




30




30












Properties

















MVR, 360° C./5 kg




cc/10




15.8




16.9




20.3




20.3







min






Tensile Modulus




MPa




9533




9518




9366




9754






Tensile Yield Stress




MPa




162




161




154




149






Tensile Elongation




%




3.2




3.2




2.8




2.4






Izod Unnotched




kJ/m


2






43




42




39




38






Impact














TABLE 5: Control 6, Comparative Example 5 and Example 13




Polyetherimide formulations containing 30 parts chopped glass fibers with 21 parts of either 0.48 IV PPO (Comp 5) or low IV PPO® SA120 (Example 13) were compounded and molded according to the procedures 10 outlined in Table 1 & 4. Example 13, which contains the low IV PPO® SA120, flows significantly better than either the control or the formulation containing the higher IV PPO®. However, at high loadings, there is a decrease in the tensile, impact, and HDT performance but the properties are still suitable for certain applications.

















TABLE 5











Units




Control 6




Comp 5




13




























Component










ULTEM ® 1010




wt %




70




49




49






PPO ® 803, 0.48 IV




wt %









21











PPO ® SA120, 0.12 IV




wt %














21






Glass




wt %




30




30




30












Properties
















MVR, 295° C./10 kg




cc/10 min




0.5




2




23






Tensile Modulus




Mpa




10100




9400




8700






Tensile Yield Stress




Mpa




157




124




73






Tensile Elongation




%




3




2




1






Izod Unnotched




kJ/m


2






60




16




10






Impact






Vicat-B




° C.




214




214




203














TABLE 6: Control 7 and Examples 14-16




In Tables 6-8, three polysulfones obtained from BP Amoco were studied: Udel® (polysulfone) grade P1700, RadelA® (polyethersulfone) grade A200, and RadelR® (polyphenylsulfone) grade R5000. Formulations were dry mixed and then melt compounded in a Werner and Pfleiderer 28 mm co-rotating twin screw extruder at temperatures corresponding to 360° C., 375° C., and 400° C. for blends with Udel, RadelA, and RadelR, respectively. The pelletized materials were dried overnight at 120° C. before injection molding into parts for mechanical testing. Injection molding was performed in a 30-ton Engel molding machine at melt temperatures of 340° C. and a mold temperature of 95° C. Room temperature notched Izod impact strength, and tensile yield strength were then measured.




Polysulfone formulations containing 0, 2, 5, and 10 parts of low IV PPO® SA120 were compounded and molded according to the procedures outlined above. As compared to Control 7, Examples 14-16 demonstrate that the addition of the low IV PPO® SA120 results in a significant improvement in melt flow without a significant reduction in either mechanical strength or impact properties.


















TABLE 6












Control










Units




7




14




15




16





























Component











Udel P1700




wt %




100




98




95




90






PPO ® SA120, 0.12 IV




wt %




0




2




5




10












Properties

















Capillary Viscosity,




Pa-s




455




427




234




84






360° C. @ 1000 s−1






Tensile Yield Strength




Kpsi




10.2




10.3




10.4




10.6






Notched Izod @ 23° C.




Ft-lb/in




1.2




1.1




0.9




0.8














TABLE 7: Control 8 and Examples 17-19.




Polyethersulfone formulations containing 0, 2, 5, and 10 parts of low IV PPO® SA120 were compounded and molded using the procedures outlined for Table 6. As compared to Control 8, formulations containing low IV PPO have lower melt viscosities while maintaining their mechanical and impact properties.


















TABLE 7












Control










Units




8




17




18




19





























Component











Radel A, A200




wt %




100




98




95




90






PPO ® SA120, 0.12 IV




wt %




0




2




5




10












Properties

















Capillary Viscosity,




Pa-s




322




204




90




38






360° C. @ 1000 s


−1








Tensile Yield Strength




Kpsi




11.3




11.3




11.4











Notched Izod @ 23° C.




Ft-lb/in




1.7




1.3




0.9



















TABLE 8: Control 9 and Examples 20 and 21




Formulations containing 0, 2, and 5 parts of low IV PPO® SA120 in polyphenylsulfone were compounded and molded using the procedures described in Table 6. As seen in Table 8, the addition of low IV PPO in the formulation reduces the melt viscosity while retaining the excellent tensile strength and impact properties of polyphenylsulfone.

















TABLE 8












Control









Units




9




20




21




























Component










Radel R, R5000




wt %




100




98




95






PPO ® SA120, 0.12 IV




wt %




0




2




5












Properties
















Capillary Viscosity,




Pa-s




460




439




160






360° C. @ 1000 s


−1








Tensile Yield Strength




Kpsi




11.1




10.7











Notched Izod @ 23° C.




Ft-lb/in




15.7




12.8



















EXPERIMENTAL




The poly(imide) resins employed were ULTEM® 1000—1000 with a weight-average molecular weight of 63,000 g/mol, and ULTEM® 1010-1000 with a weight-average molecular weight of 53,000 g/mol, while the poly(arylene ether) resins employed were PPO® 803 with an intrinsic viscosity (IV) of 0.48 dl/g, PPO® 646 with an IV of 0.46 dl/g, and PPO® SA120 with an IV of 0.12 dl/g, all commercially available from G. E. Plastics, Pittsfield, Mass. PPO® SA120 is poly (2,6-dimethyl-1,4-phenylene) ether in a pelletized form with an average size of approximately ⅙ inches (3 mm) after recovery from a reaction solution with a vented extruder. Three polysulfones obtained from Amoco were studied: Udel® (polysulfone) grade P1700, Radel A® (polyethersulfone) grade A200, and Radel R® (polyphenylsulfone) grade R5000. The chopped glass fiber that was used is G-filament glass (⅛ inches) sized with silane coupling agent available from Owens Corning.




Melt volume rate (MVR) was determined according to ISO 1133, using a Zwick capillary rheometer at either 295° C. or 360° C. A Tinius Olsen capillary rheometer with a 6.6 kg load was used to determine the melt flow rate (MFR) according to ASTM 1238. Mechanical properties were determined according to ISO 527, ISO 180, ASTM 638, and ASTM 790 standards. Plate-plate melt viscosity (MV) was determined at 360° C. using a Rheometrics Dynamic Rheometer, while the capillary MV was performed at 337° C. with a Rheometrics Capillary Rheometer. Viscosity measurements on the formulations containing the various polysulfones were made by capillary rheometry using a Goettfert Rheograph model 2002 equipped with a 12 mm diameter piston and a 30/1 L/D capillary die operated at 360° C. The molecular weights of the ULTEM® resins were determined by gel permeation chromatography (GPC) using chloroform as a solvent. Intrinsic viscosity (IV) is measured in chloroform at 25° C. in units of deciliters/gram (dl/g). ISO 306 or ASTM 648 was used to measure deformation under load as a function of temperature of a thermoplastic part. The temperature at which the part deforms according to the ISO norm is defined as the Vicat temperature and is defined as the heat distortion temperature (HDT) under the ASTM standard, in ° C. Tests for flame retardancy were performed according to UL-94 protocol for a VO rating using 20 test bars of the polyphenylene ether formulations with the dimensions: 5 inches by 0.5 inches by 1.5 mm.




The compositions made in the above examples were tested for flammability using a flame retardant testing tool which provides a prediction of the likelihood that a particular UL standard, such as UL-94 will be passed. The UL-94 protocol calls for bar-shaped specimens of dimensions 5 inches (12.7 cm)×0.5 inches (1.3 cm) width×the desired normal thickness, UL-94 ratings being specified for a particular thickness. A flame having an inner cone of height 0.75 inches (1.9 cm) is applied to each specimen so that a distance of 0.375 inches (1.0 cm) separates the lower end of the specimen from base of the flame. The flame is held in that position for 10 seconds and then removed. A bum time is defined as the time required for the flame issuing from the specimen to disappear. If burning of the specimen ceases within 30 seconds, the flame is reapplied for an additional 10 seconds. The criteria for V-0, V-1, and V-2 ratings are listed below in Table 9.












TABLE 9











Vertical Flame Class Requirements















94V-0




94V-1




94V-2


















Individual burn time (seconds)




≦10




≦30




≦30






Total burn time (seconds)




≦50




 ≦250




 ≦250






(5 specimens)






Glowing time (seconds) (individual




≦30




≦60




≦60






specimen)






Drip particles that ignite cotton




NO




NO




YES











“≦” means less than or equal to.













For a V-0 rating, no individual burn times, from the first or second application may exceed 10 seconds. The total of the bum times for any five specimens may not exceed 50 seconds. Drip particles that ignite a piece of cotton gauze situated below the specimen are not allowed. The values listed in Table 3 represent the minimum thickness for all 20 samples passing the V-0 criteria.




Each of the tables represents a single experiment. For each example in a given table the compounding/molding/testing conditions were the same.




In each set of experiments, a reference lacking a poly(arylene ether) was included. Each set of data shows the improvement in flow as reflected by measurement of MVR, MFR, Plate—Plate NW, or capillary Mv upon addition of a low IV poly(arylene ether) (PPO® SA120) to the formulation.




The above examples demonstrate the improved melt flow of high performance thermoplastic polymers that have a poly(arylene ether) (for example, polyphenylene ether), component. No significant loss of molecular weight, tensile properties, heat resistance, or impact strength occurred with the addition of the polyphenylene ether.




While preferred embodiments have been shown and described, various modifications and substitutions may be made thereto without departing from the spirit and scope of the invention. Accordingly, it is to be understood that the present invention has been described by way of illustration and not limitation.



Claims
  • 1. A thermoplastic resin composition, comprising, based upon the total weight of the compositionabout 40 wt % to about 99.9 wt % of a high Tg amorphous thermoplastic polymer resin wherein the high Tg amorphous thermoplastic polymer resin is selected from the group consisting of poly (imide) polymers, poly(amide imide) polymers, poly(sulfone) polymers, poly(ether sulfone) polymers, poly(etherimide) polymers, and combinations of the foregoing high Tg amorphous thermoplastic polymer resins; and about 0.1 wt % to about 50 wt % of an unfunctionalized poly(arylene ether) having an intrinsic viscosity of about 0.10 to about 0.15 dl/g, as measured in chloroform at 25° C.
  • 2. A thermoplastic resin composition as in claim 1, comprising about 50 wt % to about 99 wt % of the high Tg amorphous thermoplastic polymer resin and about 1.0 wt % to about 40 wt % of the poly(arylene ether).
  • 3. A thermoplastic resin composition as in claim 2, comprising about 70 wt % to about 95 wt % of the high Tg amorphous thermoplastic polymer resin and about 5 wt % to about 30 wt % of the poly(arylene ether).
  • 4. A thermoplastic resin composition as in claim 1, wherein the poly(arylene ether) comprises a plurality of structural units of the formula XII): wherein each Q1 is independently a halogen, primary or secondary lower alkyl, phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; each Q2 is independently a hydrogen, halogen, primary or secondary lower alkyl, having from one to four carbon atoms, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and n is less than 50.
  • 5. A thermoplastic resin composition as in claim 4, wherein n is less than about 40.
  • 6. A thermoplastic resin composition as in claim 5, wherein n is about 10 to about 25.
  • 7. A thermoplastic resin composition as in claim 4, wherein each Q1 is C1-4 alkyl or phenyl, and Q2 is hydrogen.
  • 8. A thermoplastic resin composition as in claim 7, wherein the poly(arylene ether) is a poly(2,6-dimethyl-1,4-phenyleneoxide).
  • 9. A thermoplastic resin composition as in claim 4, wherein the poly(arylene ether) is a homopolymer comprising 2,6-dimethylphenylene ether units, copolymers comprising 2,6-dimethylphenylene ether and 2,3,6-trimethyl-1,4-phenylene ether units, or copolymers derived from copolymerization of 2,6-dimethylphenol with 2,3,6-trimethyl phenol.
  • 10. A thermoplastic resin composition as in claim 1, wherein the poly(imide) comprises the structural units of the formula (I): whereina is more than 1; V is a tetravalent linker selected from the group consisting of (a) substituted or unsubstituted, saturated, unsaturated or aromatic monocyclic and polycyclic groups having about 5 to about 50 carbon atoms, (b) substituted or unsubstituted, linear or branched, saturated or unsaturated alkyl groups having 1 to about 30 carbon atoms, and (c) combinations thereof, wherein the substitutions are ethers, epoxides, amides, esters, or combinations comprising at least one of the foregoing tetravalent linkers; and R is a divalent organic radical selected from the group consisting of (a) aromatic hydrocarbon radicals having about 6 to about 20 carbon atoms or halogenated derivatives thereof, (b) straight or branched chain alkylene radicals having about 2 to about 20 carbon atoms; (c) cycloalkylene radicals having about 3 to about 20 carbon atoms, and (d) divalent radicals of the formula (IV): wherein Q is a divalent moiety selected from the group consisting of —O—, —S—, —C(O)—, —SO2, CyH2y-2— and halogenated derivatives thereof, wherein y is an integer from 1 to 10.
  • 11. A thermoplastic resin composition as in claim 10, wherein a is about 10 to about 1000.
  • 12. A thermoplastic resin composition as in claim 10, wherein a is about 10 to about 500.
  • 13. A thermoplastic resin composition as in claim 10, wherein V is selected from the group consisting of the tetravalent aromatic radicals of formula (II): and halogenated derivatives of tetravalent aromatic radicals of formula (II), wherein W is a divalent moiety selected from the group consisting of —O—, —S—, —C(O)—, —SO2—, CyH2y, CyH2y-2—, and halogenated derivatives thereof, wherein y is an integer from 1 to 10, and a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions, and wherein Z is selected from the group consisting of divalent radicals of formula (III):
  • 14. A thermoplastic resin composition as in claim 1, wherein the poly(etherimide) polymer comprises structural units of the formula (V): wherein T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions; and wherein Z is one or more of the divalent radicals of formula (III):  and R is a divalent organic radical selected from the group consisting of (a) aromatic hydrocarbon radicals having about 6 to about 20 carbon atoms or halogenated derivatives thereof (b) straight or branched chain alkylene radicals having about 2 to about 20 carbon atoms; (c) cycloalicylene radicals having about 3 to about 20 carbon atoms, and (d) divalent radicals of the formula (IV): wherein Q is a divalent moiety selected from the group consisting of —O—, —S—, —C(O)—, —SO2—, CyH2y—, CyH2y-2—, and halogenated derivatives thereof, wherein y is an integer from 1 to 10.
  • 15. A thermoplastic resin composition as in claim 14, wherein the poly(etherimide) further comprises the polyimide structural units of the formula (VI): wherein R is a substituted or unsubstituted divalent organic radical selected from the group consisting of (a) aromatic hydrocarbon radicals having about 6 to about 20 carbon atoms or halogenated derivatives thereof, (b) straight or branched chain alkylene radicals having about 2 to about 20 carbon atoms; (c) cycloalkylene radicals having about 3 to about 20 carbon atoms, and (d) divalent radicals of the general formula (IV): wherein Q is a divalent moiety selected from the group consisting of —O—, —S—, —C(O)—, —SO2—, CyH2y—, CyH2y-2—, and halogenated derivatives thereof, wherein y is an integer from 1 to 5; and wherein M is one or more of the radicals of formula (VII):
  • 16. A thermoplastic resin composition as in claim 14, wherein the R is independently p-phenylene, m-phenylene, or a mixture comprising at least one of the foregoing Rs and T is a divalent radical of the formula (XI):
  • 17. A thermoplastic rosin composition as in claim 1, wherein the poly(imide) is prepared by reaction of a first material selected from the group consisting of 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl ether dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)benzophenone dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride, 2,2-bis[4-(2,3-dicarboxyphenoxy)phenyl]propane dianhydride, 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl ether dianhydride, 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfide dianhydride, 4,4′-bis(2,3-dicarboxyphenoxy)benzophenone dianhydride, 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfone dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl-2,2-propane dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl ether dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride, 4-(23-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)benzophenone dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride, and mixtures comprising at least one of the foregoing first materials, with a second material selected from the group consisting of ethylenediamine, propylenediamine, trimethylenediamine, diethylenetriamine, triethylenetetramine, hexamethylenediarmne, heptamethylenediamine, octamethylenediarnine, nonamethylenediamine, decamethylenediamine, 1,12-dodecanediamine, 1,18-octadecanediamine, 3-methylheotamethylenediamine, 4,4-dimethylheptamethylenediamine, 4-methylnonamethylenediamine, 5-methylnonamethylenediamine, 2,5-dimethylhexamethylenediamine, 2,5-dimethylheptamethylenediamine, 2,2-dimethylpropylenediamine, N-methyl-bis (3-aminopropyl) amine, 3-methoxyhexamethylenediamine, 1,2-bis(3-aminopropoxy) ethane, bis(3-aminopropyl) sulfide, 1.4-cyclohexanediamine, bis-(4-aminocyclohexyl) methane, m-phenylenediamine, p-phenylenediamine, 2,4-diaminotoluene, 2,6-diaminotoluene, m-xylylenediamine, p-xylylenediamine, 2-methyl-4,6-diethyl-1,3-phenylenediamine, 5-methyl-4,6-diethyl-1,3-phenylene-diamine, benzidine, 3,3′-dimethylbenzidine, 3,3′-dimethoxybenzidine, 1,5-diaminonaphthalene, bis(4-aminophenyl) methane, bis(2-chloro-4-amino-3,5-diethyiphenyl) methane, bis(4-aminophenyl) propane, 2,4-bis(b-amino-t-butyl) toluene, bis(p-b-ammo-t-butylphenyl) ether, bis(p-b-methyl-o-aminophenyl) benzene, bis(p-b-methyl-o-aminopentyl) benzene, ., 3-diamino-4-isopropylbenzene, bis(4-aminophenyl) sulfide, bis (4-aminophenyl) sulfone, bis(4-aminophenyl) ether, 1,3-bis(3-aminopropyl) tetramethyldisiloxane, and mixtures comprising at least one of the foregoing second materials.
  • 18. A thermoplastic resin composition as in claim 17, wherein the poly(etherimide) is prepared by reaction of aromatic dianhydrides selected from the group consisting of pyromellitic dianhydride, 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride, and mixtures comprising at least one of the foregoing dianhydrides, with diamines selected from the group consisting of aliphatic diamines, hexamethylenediamine, 1,3-bis(3-aminopropyl)tetramethyldisiloxane, m-phenylenediamine, p-phenylenediamine, or mixtures comprising at least one of the foregoing diamines.
  • 19. A thermoplastic resin composition as in claim 1, wherein the high Tg amorphous thermoplastic polymer has a Tg of about 170° C or greater.
  • 20. A thermoplastic resin composition as in claim 19, wherein the high Tg amorphous thermoplastic polymer has a Tg of about 200° C. or greater.
  • 21. A thermoplastic resin composition as in claim 1, wherein the poly(arylene ether) was recovered from a reaction solution as a solid mass and granulated or pelletized to a desired size or is recovered from a reaction solution as an agglomerate with an average particle size greater than 100 μm.
  • 22. A thermoplastic resin composition as in claim 1, wherein the poly(arylene ether) was recovered from a reaction solution of the poly(arylene ether) as a solid mass by evaporating solvent from said reaction solution in a film evaporator, cooling the recovered poly(arylene ether) to form a solid and granulating or pelletizing the solid.
  • 23. A thermoplastic resin composition as in claim 1, wherein the poly(arylene ether) is recovered from a reaction solution of the poly(arylene ether) as a solid mass by evaporating solvent from said reaction solution with a vented extruder and extruding the poly(arylene ether), cooling the extruded poly(arylene ether) to from a solid and granulating or pelletizing the solid.
  • 24. A thermoplastic resin composition comprising, based upon the total weight of the composition, about 0.1 wt % to about 50 wt % of an unfunctionalized poly(arylene ether) having an intrinsic viscosity of about 0.10 to about 0.15 dug, as measured in chloroform at 25° C, wherein the poly(arylene ether) polymer comprises a plurality of structural units of the formula (XII): wherein each Q1 is independently a halogen, primary or secondary lower alkyl having from one to four carbon atoms, phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; each Q2 is independently a hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydracarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and n is less than 50; and about 40 wt % to about 99.9 wt % of a high Tg amorphous thermoplastic polymer resin, wherein the high Tg amorphous thermoplastic polymer resin comprises structural units of the formula (V): wherein T is —O— or a group of the formula —O—Z—O— wherein the divalent bonds of the —O— or the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′positions; and wherein Z is one or more of the divalent radicals of formula (III):  and R is a divalent organic radical selected from the group consisting of (a) aromatic hydrocarbon radicals having about 6 to about 20 carbon atoms or halogenated derivatives thereof, (b) straight or branched chain alkylene radicals having about 2 to about 20 carbon atoms; (c) cycloalkylene radicals having about 3 to about 20 carbon atoms, and (d) divalent radicals of the formula (IV): wherein Q is a divalent moiety selected from the group consisting of —O—, —S—, —C(O)—, —SO2—, CyH2y—, CyH2y-2—, and halogenated derivatives thereof wherein y is an integer from 1 to 10.
  • 25. A thermoplastic resin composition as in claim 24, comprising about 50 wt % to about 99 wt % of the high Tg amorphous thermoplastic polymer resin and about 1 wt % to about 40 wt % of the poly(arylene ether).
  • 26. A thermoplastic resin composition as in claim 25, comprising about 70 wt % to about 95 wt % of the high Tg amorphous thermoplastic polymer resin and about 5 wt % to about 30 wt % of the poly(arylene ether).
  • 27. A thermoplastic resin composition as in claim 24, wherein each Q1 is C1-4 alkyl or phenyl, and Q2 is hydrogen.
  • 28. A thermoplastic resin composition as in claim 24, wherein the high Tg amorphous thermoplastic resin further comprises poly(imide) structural units of the formula (VI): wherein R is a substituted or unsubstituted divalent organic radical selected from the group consisting of (a) aromatic hydrocarbon radicals having about 6 to about 20 carbon atoms or halogenated derivatives thereof, (b) straight or branched chain alkylene radicals having about 2 to about 20 carbon atoms; (c) cycloalkylene radicals having about 3 to about 20 carbon atoms, and (d) divalent radicals of the general formula (IV): wherein Q is a divalent moiety selected from the group consisting of —O—, —S—, —C(O)—, —SO2—, CyH2y—, CyH2y-2—, and halogenated derivatives thereof, wherein y is an integer from 1 to 10; and M is one or more of the radicals of formula (VII):
  • 29. A thermoplastic resin composition as in claim 24, wherein the high Tg amorphous thermoplastic polymers are prepared by reaction of a first material selected from the group consisting of 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl ether dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)benzophenone dianhydride, 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride, 2,2-bis[4-(2,3-dicarboxyphenoxy)phenyl]propane dianhydride, 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl ether dianhydride, 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfide dianhydride, 4,4-bis(2,3-dicarboxyphenoxy)benzophenone dianhydride, 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfone dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl-2,2-propane dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl ether dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)benzophenone dianhydride, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride, and mixtures comprising at least one of the foregoing first materials, with a second material selected from the group consisting of ethylenediamine, propylenediamine, trimethylenediamine, diethylenetriamine, triethylenetetramine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, nonamethylenediamine, decamethylenediamine, 1,12-dodecanediamine, 1,18-octadecanediamine, 3-methylheptamethylenediamine, 4,4-dimethylheptamethylenediamine, 4-methylnonamethylenediamine, 5-methylnonamethylenediamine, 2,5-dimethylhexamethylenediamine, 2,5-dimethylheptamethylenediamine, 2,2-dimethylpropylenediamine, N-methyl-bis (3-aminopropyl) amine, 3-methoxyhexamethylenediamine, 1,2-bis(3-aminopropoxy) ethane, bis(3-aminopropyl) sulfide, 1,4-cyclohexanediamine, bis-(4-aminocyclohexyl) methane, m-phenylenediamine, p-phenylenediamine, 2,4-diaminotoluene, 2,6-diaminotoluene, m-xylylenediamine, p-xylylenediamine, 2-methyl-4,6-diethyl-1,3-phenylenediamine, 5-methyl-4,6-diethyl-1,3-phenylene-diamine, benzidine, 3,3′-dimethylbenzidine, 3,3′-dimethoxybenzidine, 1,5-diaminonaphthalene, bis(4-aminophenyl) methane, bis(2-chloro-4-amino-3,5-diethylphenyl) methane, bis(4-aminophenyl) propane, 2,4-bis(b-amino-t-butyl) toluene, bis(p-b-amino-t-butylphenyl) ether, bis(p-b-methyl-o-aminophenyl) benzene, bis(p-b-methyl-o-aminopentyl) benzene, 1,3-diamino-4-isopropylbenzene, bis(4-aminophenyl) sulfide, bis (4-aminophenyl) sulfone, bis(4-aminophenyl) ether, 1,3-bis(3-aminopropyl) tetramethyldisiloxane, and mixtures comprising at least one of the foregoing second materials.
  • 30. A thermoplastic resin composition as in claim 29, wherein the high Tg amorphous thermoplastic polymers are prepared by reaction of aromatic dianhydrides selected from the group consisting of pyromellitic dianhydride, 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride, and mixtures comprising at least one of the foregoing dianhydrides, with diamines selected from the group consisting of aliphatic diamines, hexamethylenediamine, 1,3-bis(3-aminopropyl) tetramethyldisiloxane, m-phenylenediamine, p-phenylenediamine, or mixtures comprising at least one of the foregoing diamines.
  • 31. A method of preparing a thermoplastic resin composition comprising:melt mixing about 40 wt % to about 99.9 wt % of a high Tg amorphous thermoplastic polymer resin selected from the group consisting of poly (imide) polymers, poly(sulfone) polymers, and combinations of the foregoing high Tg amorphous thermoplastic polymer resins and about 0.1 wt % to about 50 wt % of an unfunctionalized poly(arylene ether) having an intrinsic viscosity/of about 0.10 to about 0.15 dl/g, as measured in chloroform at 25° C., to form a mixture; and molding the mixture.
  • 32. A thermoplastic resin composition, comprising the reaction product of, based upon the total weight of the composition:about 40 wt % to about 99.9 wt % of a high Tg amorphous thermoplastic polymer resin selected from the group consisting of poly (imide) polymers, poly(sulfone) polymers, and combinations of the foregoing high Tg amorphous thermoplastic polymer resins; and about 0.1 wt % to about 50 wt % of an unfunctionalized poly(arylene ether) having an intrinsic viscosity of about 0.10 to about 0.15 dl/g, as measured in chloroform at 25° C.
  • 33. A thermoplastic resin composition as in claim 32, wherein the poly(arylene ether) was recovered from a reaction solution as a solid mass and granulated or pelletized to a desired size or is recovered from a reaction solution as an agglomerate with an average particle size greater than 10 μm.
  • 34. A thermoplastic resin composition as in claim 32, wherein the poly(arylene ether) was recovered from a reaction solution of the poly(arylene ether) as a solid mass by evaporating solvent from said reaction solution in a film evaporator, cooling the recovered poly(arylene ether) to form a solid and granulating or pelletizing the solid.
  • 35. A thermoplastic resin composition as in claim 32, wherein the poly(arylene ether) is recovered from a reaction solution of the poly(arylene ether) as a solid mass by evaporating solvent from said reaction solution with a vented extruder and extruding the poly(arylene ether), cooling the extruded poly(arylene ether) to from a solid and granulating or pelletizing the solid.
US Referenced Citations (50)
Number Name Date Kind
3257357 Stamatoff Jun 1966 A
3257358 Stamatoff Jun 1966 A
3306874 Hay Feb 1967 A
3306875 Hay Feb 1967 A
3642946 Grabowski Feb 1972 A
3803085 Takehoshi et al. Apr 1974 A
3814869 De Luca Jun 1974 A
3847867 Health et al. Nov 1974 A
3850885 Scotia et al. Nov 1974 A
3852242 White Dec 1974 A
3855178 White et al. Dec 1974 A
3905942 Takekoshi et al. Sep 1975 A
3914266 Hay Oct 1975 A
3972902 Heath et al. Aug 1976 A
3983093 Williams, III et al. Sep 1976 A
4028341 Hay Jun 1977 A
4042551 Kruse Aug 1977 A
4076929 Dohany Feb 1978 A
4080403 Gergen et al. Mar 1978 A
4135009 Mercurio Jan 1979 A
4151151 Isley Apr 1979 A
4293670 Robeson et al. Oct 1981 A
4385146 Axelrod May 1983 A
4431779 White et al. Feb 1984 A
4443591 Schmidt et al. Apr 1984 A
4455410 Giles, Jr. Jun 1984 A
4481325 Giles, Jr. Nov 1984 A
4515921 Witman May 1985 A
4515924 Brooks et al. May 1985 A
4588806 Aycock et al. May 1986 A
4663378 Allen May 1987 A
4692482 Lohrengel Sep 1987 A
4737546 Liu et al. Apr 1988 A
4778855 Boutni et al. Oct 1988 A
4806297 Brown et al. Feb 1989 A
4806602 White et al. Feb 1989 A
4822830 Adkins Apr 1989 A
4935472 Brown et al. Jun 1990 A
4942206 White et al. Jul 1990 A
4981890 Schleifstein Jan 1991 A
5081185 Haaf et al. Jan 1992 A
5095060 Haaf Mar 1992 A
5204410 Banevicius et al. Apr 1993 A
5256250 Pelzer Oct 1993 A
5272248 Pratt et al. Dec 1993 A
5376714 Yates Dec 1994 A
5376724 Bailly et al. Dec 1994 A
5419810 Van Der Piepen et al. May 1995 A
6166137 Brown et al. Dec 2000 A
6211327 Braat et al. Apr 2001 B1
Foreign Referenced Citations (2)
Number Date Country
0049191 Sep 1981 EP
0823457 Aug 1997 EP
Non-Patent Literature Citations (2)
Entry
McKenna, L.A., Modern Plastics Encyclopedia “Sulfone Polymers” pp. 108, 110-112, (1977-78).
Handbook of Plastics and Elastomers, C.A. Harper, ed., McGraw-Hill, Inc., (1975) pp. 1-69, 1-95 to 96.