High-precision method and apparatus for evaluating creep damage

Abstract

The present invention provides a high-precision method for evaluating creep damage of high tension heat resistant steel used in high temperature exposing apparatuses comprising comparing particle size behavior varying with creep damage progress of crystal grains having a crystal orientation difference of about 2 degrees or more, preferably 3 degrees or more at an evaluated part on the basis of a working curve or a working map prepared in advance by looking for the relation of grain sizes to creep damage extents, and also provides a high-precision apparatus for evaluating creep damage of high tension heat resistant steel used in high temperature exposing apparatuses comprising a measuring means for measuring particle size variation behavior of crystal grains or sub grains having a crystal orientation difference of about 2 degrees or more with regard to a specimen at the evaluated part of high tension heat resistant steel and a working curve or a working map prepared in advance by looking for the relation of the grain sizes with respect to the creep damage extents (including creep damage rates) at every level of loaded stress wherein a creep damage extent is evaluated by comparing the grain size variation behavior measured by the measuring means with a working curve or a working map selected on the basis of a loaded stress.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a method and an apparatus for evaluating an extent of the creep damage of high-tension heat resistant steel used for such as a power plant with precision and for short time.

[0003] 2. Description of the Related Art

[0004] Since thermal power plants in Japan had been constructed intensively for about ten years from 1955 to 1965, over half of the total plants have been operated for more than 100,000 hours. In order to operate the plants safely hereafter, a precise life evaluation is needed for the proper maintenance. A destructive test has been hitherto used as a most reliable evaluation method. The problem was the method consumed much time and cost in comparison to other methods. Recently, a more convenient method such as a metallographical evaluation method is applied instead of the destructive test.

[0005] High-tension ferritic steel or austenite stainless steel is used in recent high-pressure steam power plants. The metallographical method has not been applied to these steels because a structural change owning to the creep damage is little. Hence, evaluation methods for creep damage such as a method by convenient hardness measurement have been proposed.

[0006] For instance, the applicant of the present invention disclosed a method for evaluating the rest of the life of ferritic heat resistant steel in Japanese laid open patent publication P1990-248860A. The method comprises the steps of measuring a hardness of both the part influenced by welding heat and a base metal, preparing a working curve chart denoting a relation of creep damage extents of the parts influenced by welding heat with respect to the hardness differences between the parts influenced by welding heat and the base metal, and finding the creep damage extent by applying a hardness difference between the measuring part influenced by welding heat and the base metal to the working curve.

[0007] However, a problem of the accuracy of evaluating the creep damage by the above method still remains because the hardness varies with the factors such as accuracy of the hardness measurement, heat treatment, or aging, besides creep damage.

SUMMARY OF THE INVENTION

[0008] In view of the prior problems, the present invention provides a method and an apparatus for evaluating precisely and in a short period of time the creep damage of the parts influenced by welding heat of base metal and a welded joint of heat resistant steel used in a high temperature exposing apparatuses of thermal power plants and etc., specifically of such heat resistant steels as ferric steel based on two phases structure of ferrite and pearlite, high tension heat resistant ferritc steel based on a martensitic structure or austenitic stainless steel.

[0009] Recently, instruments and studies for metallographic analysis have advanced so that a microstructure change caused by a creep damage of a high tension heat resistant steel that is beginning to be used in power plants can be analyzed.

[0010] A microstructure of a heat resistant steel consists essentially of old austenitic grains having a large crystal orientation difference between adjacent crystals and comparatively small sub grains together with the old austenitic grains, the sub grains having a crystal orientation difference of about 2 degrees or more or preferably 3 degrees or more between adjacent crystals. The inventor of the present invention found that a time-saving and precise creep damage evaluation can be performed by comparing a behavior of these crystal grains increasing or decreasing in size on the basis of a working curve or a working map prepared in advance by looking for the relation of the grain sizes with respect to the creep damage extents. Hence, an aspect of the present invention is that creep damage can be evaluated by a change in an average grain size of crystal grains having a crystal orientation difference of about 2 degrees or more, preferably 3 degrees or more; to put it more simply, without distinguishing old austenitic grains from sub grains, a change of the smallest grain size measurement observed with a conventional instrument (e.g. EBSP) can evaluate creep damage by applying the observed grain size to a working curve.

[0011] More specifically, to evaluate creep damage of base metal, which is used in high temperature apparatuses, of ferritic steel and austenitic stainless steel having two phases structure of ferrite and pearlite, a part influenced by welding heat of ferritic heat resistant steel based on a tempered martensitic structure or a tempered bainite structure and having a fine grain region therein, or a part influenced by welding heat of austenitic stainless steel having a coarse grain region, crystal grains or sub grains having a crystal orientation difference of about 2 degrees or more, preferably 3 degrees or more at the evaluated part are preferably compared in terms of particle size variation more preferably average particle size behavior, which decreases with creep damage progress, on the basis of a working curve or a working map prepared in advance by looking for the relation of the grain sizes with respect to the creep damage extents.

[0012] To evaluate creep damage of a coarse grain region of a base metal of ferritic steel, a coarse grain region influenced by welding heat of ferritic heat resistant steel having a tempered martensitic structure or a tempered bainite structure or a coarse grain region influenced by welding heat of ferritic steel having two phases structure of ferrite and pearlite, crystal grains or sub grains having a crystal orientation difference of about 2 degrees or more, preferably 3 degrees or more at an evaluated part are preferably compared in terms of particle size variation more preferably average particle size behavior, which decreases with creep damage progress, on the basis of a working curve or a working map prepared in advance by looking for the relation of the grain sizes with respect to the creep damage extents.

[0013] Ordinary crystal grains, which mean old austenitic grains, are observed in all heat resistant steel. The grain cluster is referred to as a large obliquity grain cluster. The crystal orientation difference of the adjacent crystals is said to be approximately 20 degrees. The sub crystal grains are referred to as a region of a small obliquity grain cluster unlike with old austenitic grains. The crystal orientation difference of the adjacent crystals is as very small as 1-3 degrees. Therefore, the grain cluster is so unstable that the cluster is apt to migrate by creep strain. The sub crystal grains whose grain size is smaller than that of old austenitic grains exist in old austenitic grains. It is often the case that the sub crystal grains do not exist until heat treatment. There are many fine lath structures of rod shape surrounded by small obliquity grain clusters in material having a tempered martensitic structure or a tempered bainite structure. According to the present invention, since the lath structures are also surrounded by sub crystal grain clusters, an average grain size is determined by taking into account of the lath structures to evaluate creep damage.

[0014] The relation between average grain size and creep damage extent is affected by stress though the effect of temperature is small. It is preferable to find in advance the relation between creep damage rates corresponding to each stress loaded to a creep damage evaluation part and average grain size.

[0015] Therefore, a plurality of curved lines denoting the relation between creep damage rate and average grain size should be drawn at many levels of stress to formulate a series of maps, that is a 3D map made by stacking a plurality of graphical drawings shown in FIG. 6 for a plurality levels of stress. In order to evaluate creep damage, a curved line in one of drawings is preferably selected for the corresponding stress or two curved lines in FIG. 6(A) and FIG. 6(B) are preferably interpolated to find a curved line of the corresponding stress.

[0016] Further according to the present invention, the map is substantially a set of working curves of creep damage extent vs. sub crystal grain size prepared for each prescribed stress. A curved line is selected from the working curves of the map or a curved line is made by interpolating two curved lines with regard to a loaded stress of an evaluated part. The creep damage of the part is found from thus sought curved line.

[0017] Another aspect of the present invention relates to an apparatus for evaluating creep damage, with which the invention is effectively carried out. The apparatus comprises a measuring means for measuring particle size variation behavior of crystal grains or sub grains having a crystal orientation difference of about 2 degrees or more, preferably 3 degrees or more with regard to a specimen at an evaluated part of high tension heat resistant steel and a working curve or a working map prepared in advance by looking for the relation of the grain sizes with respect to the creep damage extents (including creep damage rates) at every level of loaded stress wherein a creep damage extent is capably evaluated by comparing the grain size variation behavior measured by the measuring means with a working curve or a working map selected on the basis of a loaded stress.

[0018] In this case, it is preferable that, with the measuring means, an electron beam is irradiated on said specimen, from whom TEM-Kikuchi pattern appears by the irradiation, the pattern being taken into a TV camera coated with phosphoric acid on its surface to observe and analyze it. The map is preferably a 3D map made by stacking a plurality of working curve charts denoting a relation of creep damage extents and average grain sizes for a plurality of prescribed levels of stress.

BRIEF DESCRIPTION OF DRAWINGS

[0019] In the accompanying drawings:

[0020] In FIG. 1, the upper drawing denotes a U groove form before welding and the lower drawing denotes a welding condition of joint welding by multi layer laminate welding;

[0021] FIG. 2(A) and FIG. 2(B) show a test specimen form and a method for cutting the same from a welding part;

[0022] FIG. 3 shows an apparatus for observing and analyzing crystal orientation pattern by known EBSP method;

[0023] FIG. 4 is a pattern diagram showing a crystal structure change of crystal grains or sub grains accompanying creep damage with regard to base metal of STBA24 and heat SUSTP347H, a part influenced by welding heat of heat STBA28 (a fine grain region) and a part influenced by welding heat of SUSTP347H (a coarse grain region);

[0024] FIG. 5 is a pattern diagram showing a crystal grain change of a part influenced by welding heat of STBA24 (a coarse grain region), and a crystal grain change of base metal and a part influenced by welding heat of heat STBA28 (a coarse grain region);

[0025] FIG. 6(A) is a graph chart showing a relation between grain size changes of sub grains and creep damage rates regarding base metal and FIG. 6(B) regards joint welding part;

[0026] FIG. 7 is a flow chart showing the steps of finding a creep damage rate from the orientation difference and the grain size change of base metal and a part influenced by welding heat,

[0027] FIG. 8 is a tables showing creep damage rates of various test specimens;

[0028] FIG. 9 is a table showing crystal orientation differences and average grain sizes in base material; and

[0029] FIG. 10 is a table showing crystal orientation differences and average grain sizes in heat STBA28.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0030] The invention will now be described below in detail by way of example with reference to the accompanying drawings. It should be understood, however, that the description herein of specific embodiments such as to the dimensions, the kinds of material, the configurations and the relative disposals of the elemental parts is not intended to limit the invention to the particular forms disclosed but the intention is to disclose for the sake of example unless otherwise specifically described.

[0031] Now in the following, the steps of creep damage evaluation according to the present invention are explained in the order of events.

[0032] First of all, base metal of steel tubes of heat exchanging boilers for thermal power plant boilers were used for test specimens. More specifically, materials are two kinds of ferritic steels and one kind of austenite stainless steel, details being described as follows.

[0033] 1. Ferritic steel

[0034] 1A. Ferritic steel based on two phases structure of ferrite and pearlite, JIS STBA24*(2.25Cr-1Mo) φ50.8×t9.5 mm.

[0035] 1B. High tension heat resistant ferritic steel based on a tempered martensitic structure, Heat STBA28*(9Cr-1Mo—V—Nb) φ54.0×t10.2 mm

[0036] 2. Austenite stainless steel Heat SUSTP347H*(18Cr-8Ni—Nb) φ45.0×t11.2 mm.

[0037] Steel tubes of heat exchanging boilers set forth on FIG. 8 in “Construction of technical standard for hydraulic and thermal electrical apparatus” edited by former Agency of natural resources and energy.

[0038] With regard to the above three kinds of base metal, joint welding with a U groove form shown in the upper part of FIG. 1 was carried out by a multi layer laminate welding as shown in the lower part of FIG. 1 under the following condition.

[0039] Welding method: TIG automatic welding

[0040] Welding wire: φ1.2 mm

[0041] Preheat: none

[0042] Welding voltage: 7-12 v

[0043] Welding current: 100-200 A

[0044] Heat treatment after welding: STB24 720° C.×0.5 h

[0045] Heat STBA28 740° C.×0.5 h

[0046] Heat SUSTP347H none

[0047] Test specimens were taken from the three kinds of sample material of the base metal and welding joints. That is, creep test specimens shown in FIG. 2(A) and FIG. 2(B) were cut out from base metal part and welding part respectively by grind-cutting operation.

[0048] Creep testing was conducted under the following conditions:

[0049] 550° C.×110 MPa for base metal and welding joints of 1A, STBA20;

[0050] 600° C.×130 MPa for base metal and welding joints of 1B, Heat STBA28;

[0051] 656° C.×130 MPa for base metal and welding joints of 2, heat SUSTP347H.

[0052] Relation between creep suspend time and creep damage rate is shown in FIG. 8.

[0053] A small piece was cut out from parallel part of a suspended creep test piece. The small piece was buried in resin in parallel with the direction of stress load, polished with till #1200 Emery paper and finally finished with 0.1 μm diamond paste to mirror surface. The polished surface was electro polished in 10% perchloric acid/ethanol solution with an applied voltage of approximately 15 volts to remove the processed layer.

[0054] Then, crystal orientation was analyzed with the test piece obtained above by a crystal orientation-analyzing instrument. Crystal orientation analyzing was made by a known EBDP (Electron Backscatter Diffraction Pattern) method. EBSP method has an accuracy of; a spacial resolution of 0.1 μm, a measuring depth of 0.05 μm, an angle range of ±40°, and a bearing accuracy of 0.5°. The method has high spacial resolution in comparison to ECP (Electron Channeling Pattern) method though spacial resolution and bearing accuracy are inferior to those of TEM/Kikuchi line method. A SEM is shown in FIG. 3 where TEM/Kikuchi pattern emitted from a specimen 32, which is set obliquely at an angle of about 70 degrees and irradiated with electron beam 3, is observed and analyzed by taking into a TV camera 34 surface of which is coated with phosphoric acid 33. Thus, the method has distinguishing characteristics such as facile preparation of specimens and overwhelmingly quick affixing of index numbers because bulk specimens can be observed. An orientation angle difference of adjacent crystal grains or sub grains can be evaluated quantitatively.

[0055] An average grain size is estimated by regarding an interface having a crystal orientation difference of about 2 degrees or more, preferably 3 degrees or more in the crystal orientation images obtained by the SEM as a boundary. Fine crystals having a comparatively small orientation angel of adjacent crystals in a cluster of old austenite grains having a comparatively large orientation angle are herein referred to as sub crystal grains.

[0056] FIG. 4 and FIG. 5 are pattern diagrams showing structure changes of the sub crystal grains accompanied by creep damage. FIG. 4 is a pattern diagrams showing crystal changes of base metal of STBA24 and heat SUSTP347H, a part influenced by welding heat of heat STBA28 (a fine grain region), and a part influenced by welding heat of heat SUSTP347H (a coarse grain region). It can be seen that an average grain size becomes smaller as sub crystal grain clusters 2 are formed in an old austenite crystal grain cluster 1 with the increasing ratio of creep damages, 0→0.5→0.9.

[0057] FIG. 5 is a pattern diagrams showing crystal changes of a part influenced by welding heat of STBA24 (a coarse grain region), and base metal and a part influenced by welding heat of heat STBA28 (a coarse grain region) . It can be seen that an average grain size becomes larger as sub crystal grain clusters 2 are decreased in an old austenite crystal grain cluster 1 with the increasing ratio of creep damages, 0→0.5→0.9.

[0058] Martensite and bainite lath, which have the same characteristics as a sub grain cluster were also regarded as a sub grain.

[0059] Measured data of crystal orientation differences and average grain sizes accompanied by creep damage are shown in FIGS. 9 and 10.

[0060] Crystal orientation differences and average grain sizes of adjacent crystals of old austenite grain cluster 1(A-D) and sub grain cluster 2(A1-D3, A1.1-D3) accompanied by creep damage in base metal(2.25Cr-1Mo) of STBA24 are shown in FIG. 9. Crystal orientation differences and average grain sizes of adjacent crystals of old austenite grain cluster 1(A-H) and sub grain cluster 2(A1-G1) accompanied by creep damage in heat STBA28 are shown in FIG. 10.

[0061] A sub grain cluster 2 is referred to as a grain cluster of small crystal orientation difference, on the other hand an old austenite grain cluster is referred to as a large oblique angle grain cluster, generally of a big crystal orientation difference.

[0062] Sings used in FIGS. 9 and 10 correspond to those in FIGS. 4 and 5.

[0063] Behavior of grain size changes of sub grains in base material is different from that of in a part influenced by welding heat as shown in FIGS. 9 and 10. An average grain size of sub crystal grains behaves as shown in FIG. 6(A) and (B).

[0064] FIG. 6(A) illustrates that an average grain size becomes smaller as creep damage proceeds in base material of STBA24 and heat SUSTP347H but instead, it becomes larger in base material of heat STBA28, which is denoted by the curve.

[0065] As for a welding join part, FIG. 6(B) illustrates that an average grain size becomes larger as creep damage proceeds in a coarse grain region of a part influenced by welding heat of STBA24 and heat STBA28 and an average grain size turns finer in comparison to that before creep damage in a coarse grain region of a part influenced by welding heat of heat STBA28 and heat SUSTP347H.

[0066] Since stress has significant effect on the relation of creep damage to average grain size, though testing temperature has little effect on it, it is preferable to find beforehand a relation of the creep damage rate to the stress applied to the part of evaluating creep damage to the average grain size.

[0067] The curves denoting the relation of creep damage rate to average grain size are preferably prepared for a plurality levels of stress, levels having a prescribed breadth therebetween and integrated to a map such as a 3D map to which a plurality of graph charts shown in FIG. 6 for a plurality levels of stress are stacked.

[0068] After preparation of the map, creep damage is evaluated by the following flow chart shown in FIG. 7.

[0069] (S1) Selection of an evaluating material, for example, whether the material is STBA24, heat STBA28 or SUSTP347H or not.

[0070] (S2) Selection of an evaluated part, whether the part is base metal, a coarse grain region or a fine grain region of a part influenced by welding heat.

[0071] (S3) Selection of a map for the material and the evaluated part.

[0072] (S4) Selection of a loaded stress for the evaluated part.

[0073] (S5) Selection of a graph of a relation of an average grain size of crystal grains having a crystal orientation angle of about 2 degrees or more, preferably 3 degrees or more or sub crystal grains to creep damage rate corresponding to the evaluating stress, material and evaluated part from the selected map.

[0074] (S6) Measurement of an average grain size of crystal grains having an orientation angle of about 3 degree or more or of sub crystal grains of a test specimen with a crystal orientation-analyzing instrument using SEM.

[0075] (S7) A creep damage rate is found by applying the measured average grain size to the graph selected by step S5. Thus, creep damage is precisely evaluated for a short time by measuring crystal or sub crystal grain size of test pieces collected from a plant apparatus using a graph of relation of creep damage rate to average grain size.

[0076] As explained above, according to the present invention, a time consuming destructive test, which is known to be a reliable evaluation method, is not necessary but a creep damage evaluation having the same precision as a destructive test can be conducted for a very short time. Therefore, a life at a high-pressure part of a power plant incurred by creep damage is precisely evaluated so as to estimate accurately the rest of the life of the power plant, which results in improving plant reliability.

Claims

1. A high-precision method for evaluating creep damage of base metal or a part influenced by welding heat of high tension heat resistant steel used in high temperature exposing apparatuses comprising, comparing particle size behavior varying with creep damage progress of crystal grains having a crystal orientation difference of approximately 2 degrees or more at an evaluated part or sub crystal grains on the basis of a working curve or a working map prepared in advance by looking for the relation of grain sizes to creep damage extents (including creep damage rates).

2. A high-precision method for evaluating creep damage of base metal, which is used in high temperature apparatuses, of ferritic steel and austenitic stainless steel having two phases structure of ferrite and pearlite, a part influenced by welding heat of ferritic heat resistant steel based on a tempered martensitic structure or a tempered bainite structure and having a fine grain region therein, or a part influenced by welding heat of austenitic stainless steel having a coarse grain region comprising comparing particle size behavior varying with creep damage progress of crystal grains having a crystal orientation difference of approximately 2 degrees or more at an evaluated part on the basis of a working curve or a working map prepared in advance by looking for the relation of grain sizes to creep damage extents.

3. A high-precision method for evaluating creep damage of a coarse grain region of a base metal of ferritic steel, a coarse grain region influenced by welding heat of ferritic heat resistant steel having a tempered martensitic structure or a tempered bainite structure or a coarse grain region influenced by welding heat of ferritic steel having two phases structure of ferrite and pearlite comprising, comparing particle size or more preferably average particle size behavior varying with creep damage progress of crystal grains having a crystal orientation difference of approximately 2 degrees or more at an evaluated part on the basis of a working curve or a working map prepared in advance by looking for the relation of grain sizes to creep damage extents.

4. A high-precision method for evaluating creep damage according to claim 1, wherein the working map is substantially a set of working curves of creep damage extent vs. crystal grains or sub crystal grain size prepared for each prescribed stress and a curved line is selected from the working curves of the map or a curved line is made by interpolating two curved lines with regard to a loaded stress of an evaluated part and the creep damage of the part is found from thus sought curved line.

5. A high-precision apparatus for evaluating creep damage of high tension heat resistant steel used in high temperature exposing apparatuses comprising a measuring means for measuring particle size variation behavior, in accordance with creep damage progress, of crystal grains or sub grains having a crystal orientation difference of approximately 2 degrees or more with regard to a specimen at the evaluated part of high tension heat resistant steel and a working curve or a working map prepared in advance by looking for the relation of the grain sizes with respect to the creep damage extents (including creep damage rates) at every level of loaded stress wherein a creep damage extent is evaluated by comparing the grain size variation behavior, in accordance with creep damage progress, measured by the measuring means with a working curve or a working map selected on the basis of a loaded stress.

6. A high-precision apparatus for evaluating creep damage according to claim 5, wherein the measuring means is such an apparatus that an electron beam is irradiated on said specimen, which is mounted so that electron beam is irradiated at a prescribed angle, from which TEM-Kikuchi pattern appears by the irradiation, the pattern being taken into a TV camera coated with phosphoric acid on its surface to observe and analyze it.

7. A high-precision apparatus for evaluating creep damage according to claim 5, wherein the map is preferably a 3D map made by stacking a plurality of working curve charts denoting a relation of creep damage extents and average grain sizes for a plurality levels of stress.