Patent Application
20210239889
The invention relates to a high resolution full material Fresnel Zone Plate array, a process for its fabrication and an apparatus for producing high resolution full material Fresnel Zone Plate (FZP) arrays.
X-ray microscopy has been shown to be an important imaging technology. In a first approach, the resolution of a microscope is limited by the wavelength of the used radiation. In comparison to visible light, X-rays provide the advantage of a shorter wavelength, potentially allowing higher resolutions. However, refraction or reflection of X-rays by conventional lenses is very limited. Thus, the diffractive Fresnel zone plates have been established as the most popular and successful focusing devices for focusing X-rays, especially in the soft X-ray energies. A (full material) Fresnel Zone Plate is a diffractive lens, composed of multilayers of at least two materials to act as the zones of the FZP. In view of the rapid development of technologies in the nanometer range and the significant effects thereof for the development of science, in particular for use in biology, chemistry and in all life and earth sciences a further improvement of X-ray microscopy and the focusing devices (e.g. Fresnel zone plates) is sought. Furthermore, a comparatively cheap and parallel production process for FZP is in demand.
Furthermore, one of the major challenges in X-ray optics is to create optics that can focus hard X-rays down to nanometer resolutions with high diffraction efficiency. The fabrication of such an optic has been a very demanding task because it requires lenses with very high aspect ratios with zones tilted to Bragg angle. Among the possible options, multilayer type (full material) Fresnel zone plates (ML-FZP) would have been one of the best suited for accomplishing this challenge, as virtually unlimited aspect ratios can be fabricated, if zones could be tilted to Bragg angle. For the fabrication of an ML-FZP it starts with a centimeter long glass fiber substrate which has a diameter of e.g. 30 microns. Onto this substrate alternating multilayers are deposited by the atomic layer deposition technique (ALD). This has been patented under U.S. Pat. No. 9,360,603 B2. The ALD allows angstrom level precision in deposition thickness, and excellent conformality through its sequential, self-limiting surface reactions. This also eliminates the need for rotating the glass fiber that sputtered-sliced ML-FZPs suffer. Since the need for rotation of the substrate is eliminated, the accuracy could be increased and the uniformity and the resolution of the FZP could be increased significantly.
This process allows simultaneous production of virtually unlimited number of ML-FZPs from the intermediate product since many single FZPs could be sliced from the multitude of deposited glass fiber in the desired thickness e.g. via a focused ion beam.
However, qualities such as the glass fiber surface roughness, circularity and taper angle of the glass fiber, as a substrate material cannot be easily controlled. Thus, alternative methods of production of a plurality of these or similar intermediate products are sought. Consequently the object of the invention is to make available a method for producing a plurality of these or similar intermediate products as well as an array of these or similar intermediate products, which allows a simple and inexpensive production of a plurality of Fresnel zone plates, with or without zones tilted to Bragg angle, having a high resolution, high efficiency, through a high or even selectable aspect ratio and error-free layers or zones.
This object is attained by a Fresnel Zone Plate array according to claim 1, a process of its fabrication according to claim 6 and an apparatus for its fabrication according to claim 15. The Fresnel Zone Plate array, the process of its fabrication and the apparatus for its fabrication are described in more detail in the following.
A major aspect of the invention is a full material Fresnel Zone Plate precursor array which comprises a plurality of full material Fresnel Zone Plate precursors arranged on a common carrier.
In a preferred embodiment the full material Fresnel Zone Plate precursor array have controlled tapering angles. In a further preferred embodiment these tapering angles differ between some of the Fresnel Zone Plate precursors arranged on the same common carrier. This means that at least two Fresnel Zone Plate precursors arranged on the same common carrier can provide different tapering angles. Preferably, these Fresnel Zone Plate precursors are tilted to different Bragg angles optimized for different energies.
In a preferred embodiment of the full material Fresnel Zone Plate precursor array the full material Fresnel Zone Plate precursors are spaced apart from each other on the common carrier.
The full material Fresnel Zone Plate precursor array may be characterized in that the central axis of the full material Fresnel Zone Plate precursors are arranged parallel to each other on the common carrier.
In a preferred embodiment of the full material Fresnel Zone Plate precursor array the central axis of the full material Fresnel Zone Plate precursors are arranged parallel to the surface normal of the common carrier. Thus, they are arranged perpendicular to a surface of the common carrier. More preferably this surface of the common carrier is its uppermost surface.
In a preferred embodiment of the full material Fresnel Zone Plate precursor array the central axis of the full material Fresnel Zone Plate precursors are arranged perpendicular to the longitudinal direction of the common carrier. The longitudinal direction of the common carrier is understood as the direction along which the carrier provides the widest extent.
In a preferred embodiment of the full material Fresnel Zone Plate precursor array the central axis of the full material Fresnel Zone Plate precursors comprise the same material as the common carrier.
In the following the terms “Fresnel Zone Plate precursor array” and “Fresnel Zone Plate array” are used synonymously, because—as described later—it can be used as optics as a whole or one or more Fresnel Zone Plate(s) can be sliced out of the Fresnel Zone Plate precursor array to provide one or more Fresnel Zone Plate(s). The Fresnel Zone Plate precursor array (or Fresnel Zone Plate array) may comprise a plurality of pillars onto which alternating layers of material are deposited. These deposited layers form the different zones of the FZP. Preferably, the pillars are fixed on a common carrier and are immoveable with respect to each other.
In a preferred embodiment the common carrier is a wafer. However, the substrate is not limited to Si wafers. In a preferred embodiment the common carrier comprises at least one material selected from a group comprising metals, glass, oxides, alloys, sulfates and metal oxides.
In a further preferred embodiment the common carrier comprises at least one material selected from a group comprising glass, ((mono) crystalline) silicon, aluminum oxide or gold. It could be shown that some substrates, especially an Au substrate can significantly improve fabrication speed over a Si substrate.
In a preferred embodiment single crystalline Au is used as a material for the common carrier.
This material allows for improved milling rates. The sputter yield of Au is very high compared to silicon. In an even further preferred embodiment the substrate is (111) type Au single crystal. It has been shown that milling out (111) type Au single crystal is about twice as fast as using (100) Au single crystal.
In a preferred embodiment a high Z material is used as a material for the common carrier. One example for such a material is Au. Using Au as a substrate furthermore eliminates the need for an additional beam-stop deposition, which covers the zones with a Pt/C layer via parasitic deposition.
In a preferred embodiment at least one of the full material Fresnel Zone Plate precursors arranged on a common carrier differs from at least one other full material Fresnel Zone Plate precursor arranged on the same common carrier. In contrast to known methods, in which a single FZP or a plurality of FZPs is/are produced by material deposition on a longitudinal substrate (e.g. a wire), the present invention allows for parallel production of a plurality of FZPs which differ in their optical properties. FZP-production with a wire as substrate allows production of more than one single FZP, however this technique only results in FZP with identical diameter and without slanted sidewalls (or different taper angle (a)).
In another preferred embodiment, a film of material deposited onto an X-ray transparent carrier membrane and then used to fabricate the FZP precursors. The carrier membrane material can be Si, Si3N4, carbon related materials such as diamond, diamond like carbon, polycrystalline carbon, and other X-ray transparent material structured to a thickness to facilitate X-ray trans-parency for a given energy. The deposit can be either low or high Z metallic and non-metallic elements or their compounds or alloys given that they provide high enough diffraction efficiency for that given X-ray energy.
The present invention allows that a plurality of different full material Fresnel Zone Plate precursors are arranged on the same common carrier, each resulting in one or more different FZP(s). The full material Fresnel Zone Plate precursors may differ with respect to each other in parameters selected from a group comprising its diameter (width), taper angle (a), length (height) and material composition.
The present invention allows the realization of arrays of full material FZPs for the first time. In contrast to single FZPs, arrays have the advantage of being installed in X-ray microscopes directly. Preferably, the FZP arrays could be used in hard X-ray FEL's or other hard X-ray microscopes directly. Usage of arrays as a whole will be advantageous when one needs to change the focusing optic either because a different X-ray energy will be used, or like in the case of FEL's where the optic is destroyed after even one shot e.g. due to intense heat load and definitely after several shots as a result of beam damage and a new lens has to be used. Thus, the array can comprise different or similar FZPs. If the FZPs of the same array are different with respect to each other, they can differ independently from each other in length, focal length, taper angle and/or others and may be optimized to different X-ray energies.
For such an application, the produced array of FZPs can be used as is or it can be further processed. In a preferred embodiment the common carrier is changed. In such an embodiment all or some FZPs can be transferred to another substrate or common carrier. In a preferred embodiment the top surfaces of the pillars are sliced away. In an even further preferred embodiment the newly generated top surfaces of the pillars are polished.
In a preferred embodiment the pillars are attached with their top surfaces onto another substrate and all or some pillars are detached from their original substrate. Thus, the arrangement of the FZPs with respect to each other remains constant but their upper and lower surfaces can be accessible. Thus, manipulation of these surfaces with (additional) other processes (e.g. polishing) is possible.
A further major aspect of the invention is a method for producing a full material Fresnel Zone Plate precursor array. This method comprises the steps
In a preferred embodiment, the full material Fresnel Zone Plate precursors are micro-pillars.
In an alternative embodiment the full material Fresnel Zone Plate precursors are cylindrical holes. They are preferably milled out/or laser written, similar to capillaries. This embodiment provides the advantage that the FZP layers could be deposited from outer to inner. This can be advantageous since the outermost layer, which is crucial for the resolution of the FZP, is deposited first and no inaccuracies caused by other layers can propagate to the outermost layer.
In a preferred modification of this method the plurality of full material Fresnel Zone Plate precursors is produced in the common carrier by at least one process selected from the group comprising
It has been found that the full material Fresnel Zone Plate precursors could be formed via focused ion beam (FIB) in a common substrate, e.g. a wafer. However, the milling of the pillars is not limited to the conventional FIBs. As alternatives to or in addition to the above-mentioned techniques any of the recent energetic, heavy ion FIB technologies can be utilized.
It is preferred that at least some of the full material Fresnel Zone Plate precursors are produced to be parallel with respect to each other. This arrangement allows a high density of full material Fresnel Zone Plate precursors on the common carrier. Furthermore this arrangement can easily be realized by the techniques mentioned above.
In a preferred variation of the method the deposition of the alternating layers is performed via selective or non-selective, atomic layer deposition (ALD). ALD has the disadvantage that it is quite slow. However, ALD ensures uttermost precision in thickness control.
In a preferred variation of the method, the deposition of the alternating layers is performed simultaneously on a plurality of full material Fresnel Zone Plate precursors. Since some techniques, e.g. ALD, are quite slow and time consuming, it is desired to overcome this drawback.
It has been found that this disadvantage can be overcome if a plurality of full material Fresnel Zone Plate precursors can be treated by this method simultaneously. Since for ALD the material for the different layers is provided in form of gaseous precursors which can easily reach any surface of the common carrier, these precursors will reach all full material Fresnel Zone Plate precursors arranged on one or even more common carrier/s which is/are treated by ALD if the material is provided in excess. After deposition of the respective material, the surface of all full material Fresnel Zone Plate precursors will be covered by this material.
To avoid deposition of material on all accessible surfaces of the one or even more common carrier within a treatment chamber, some surfaces may be covered by a protection layer or coating, which avoids adhesion of the (gaseous) precursor molecules. Thus, the material will not be deposited on these surfaces during the deposition step.
In a preferred variation of the method it further comprises the step of
By this additional step a full material Fresnel Zone Plate precursor can be separated from the common carrier (and all other full material Fresnel Zone Plate precursors arranged on it) and handled individually. This allows for production of one or more Fresnel Zone Plates out of this single full material Fresnel Zone Plate precursor (e.g. micro-pillar) onto which alternating layers of at least two different materials have been deposited.
In a preferred variation of the method the method further comprises the step of
Usually the longitudinal axis of a full material Fresnel Zone Plate precursor is much longer than the desired thickness of a single Fresnel Zone Plate. Thus, it is possible that a plurality of Fresnel Zone Plates can be sliced from one single full material Fresnel Zone Plate precursor, e.g. a single micro-pillar. Accordingly it is preferred, that a plurality of Fresnel Zone Plates is sliced out of a full material Fresnel Zone Plate precursor or micro-pillar after deposition of the alternating layers on it.
In a further preferred variation of the method, slicing is performed by means of an ion beam.
After detaching the micro-pillar from the common carrier, it is preferred that the detached full material Fresnel Zone Plate precursor (e.g. micro-pillar) is bound to a mount. Preferably, such a mount is a TEM mount. Preferably, the detached full material Fresnel Zone Plate precursor is bound to the mount via ion beam induced metal deposition, most preferably via ion beam induced Pt deposition.
It is possible that steps a) and b) are performed independently from each other. Since the techniques of steps a) and b) differ from each other, it is possible that one or more common carriers comprising a plurality of full material Fresnel Zone Plate precursors is/are produced and stored at suitable conditions. Even transport from one production site to another one is possible if the suitable storage conditions can be maintained during transport. Afterwards, step b) can be performed independently from step a). Eventually the common carrier may be cleaned or pretreated before the deposition of the alternating layers of the at least two different materials onto the full material Fresnel Zone Plate precursor can be performed.
In a preferred variation of the method, the common carrier comprising the full material Fresnel Zone Plate precursors is pretreated before step b) is performed. Preferably, this pretreatment comprises the step of masking areas onto which no material should be deposited during step b). As described later with reference to the figures it is possible that only some surfaces of the full material Fresnel Zone Plate precursors, e.g. the micro-pillars, are not masked. For example it is possible that the micro-pillars have the form of a right circular cylinder or a section of a cone. In these special cases it is preferred that only the area of the side of this cylinder or cone section is not masked so that deposition of the alternating layers is only performed on these sides. However, also for other geometries of the full material Fresnel Zone Plate precursor or micro-pillars it is preferred that only the sidewalls are not masked and the alternating layers are deposited thereon.
The sidewalls of the full material Fresnel Zone Plate precursors or micro-pillars can be (independently from the mask) inclined/slanted with respect to its central axis. Thus, the micro-pillars can be cones or cone sections. In a preferred embodiment, the full material Fresnel Zone Plate precursors comprise a sidewall which is inclined with respect to its central axis and a planar top surface. Thus, the full material Fresnel Zone Plate precursors are preferably sections of a cone.
It is preferred that the micro-pillars comprise a sidewall which may or may not be inclined with respect to its central axis, a top surface, which is preferably circular, and a lower surface, which is adhered to the common carrier.
In a further preferred embodiment, each micro-pillar is arranged in a recess of the common carrier. The recess has a bottom surface. Preferably the micro-pillar is adhered to this bottom surface. In an even more preferred embodiment, the micro-pillar is arranged perpendicular to this bottom surface. In an even more preferred embodiment, the micro-pillar is arranged at the center of the bottom surface.
The recess in which the micro-pillar is arranged can have several forms. In a preferred embodiment, the recess is a cylinder. In an even more preferred embodiment, the cylinder is a right cylinder. This embodiment is preferred because formation of (more or less) right cylinders in the common carrier by the techniques mentioned above is quite easy. Since it is desired that in step b) the alternating layers are deposited on all sidewalls of each micro-pillar in the same thickness, it is even more preferred that the recess is a right circular cylinder and the micro-pillar is arranged in the center of such a right circular cylinder along its central axis. Thus, the distance between the micro-pillar and the inner sidewalls of the surrounding right circular cylinder is the same in all directions and the same number of layers can be deposited over the entire sidewall surface of a micro-pillar.
If an ion beam is used for producing the recesses and micro-pillars in step a) an ion beam current between 1 pA and 1.3 μA is preferred, preferably an ion beam current between 100 pA and 1 μA, more preferably an ion beam current between 1 nA and 700 nA, especially of about 60 nA or especially of about 180 nA or especially of about 480 nA is used, depending on the material of the common carrier, the processing time, the precursor height, and the desired tapering angle. Preferably, the pillars are fabricated through a multi step milling process. More preferably, during a first, so-called “rough milling step” with a high current the rough structure of the array is milled. During a following further step the fine structure of the Array, the recesses and/or the individual pillars is milled. Especially exact milling of the tapering angles is performed at low ion beam currents and/or smaller PFIB spot size.
In a preferred method an ion beam energy between 5 keV and 100 keV, preferably between 10 keV and 50 keV especially of 30 keV is used.
In a preferred embodiment, the produced FZPs are for use with operating energy E between 150 eV and 900 keV, more preferably between 1000 eV and 80 keV, especially of 1200 eV to 17 keV. The operating energy E can even be higher if Fresnel Zone Plates for applications in high energy radiation, such as gamma radiation, are used.
In a preferred embodiment, a produced FZP has a diameter between 20 μm and 500 μm, more preferably between 40 μm and 150 μm, especially of 60 μm or 100 μm.
Preferably the FZP has a height between 100 nm and 5 mm, more preferably between 200 nm and 100 μm, especially of about 5 μm.
According to another embodiment of the method in step b) preferably between 30 and 50000, preferably between 35 and 10000, more preferably between 400 and 8000, especially between 600 and 6000 layers of alternating materials are deposited on each micro-pillar. Each layer may comprise a plurality of layers of the same material. Since by ALD ideally only a single atomic layer is deposited in each cycle the ALD-process has eventually to be performed re-peatedly to provide the desired thickness of a single material-layer or period.
Since the thickness of the outermost period of the FZP is crucial with respect to its resolution, it is preferred that the outermost period or layer has a width between 0.01 nm and 1 μm, preferably between 1 nm and 250 nm, more preferably between 5 nm and 120 nm, especially of about 10 nm.
FZP with the above-mentioned characteristics are most suitable for applications in X-ray radiation or extreme ultraviolet radiation, especially for focusing X-ray radiation or extreme ultraviolet radiation since the aforementioned dimensions are of the range of the wavelengths of the used radiations so that they are suitable for use in those applications.
FZPs with slanted sidewalls, with or without altering the line to space ratio of the zones allows the appearance of higher order focus with resolutions multiple times as high as the first order depending on the diffraction order and therefore a better resolution and efficiency than known FZPs without such slanted sidewalls of the zones.
The ALD also allows the line-to-space ratio to be altered freely. This combined with a controlled tilt angle and high optical thickness, higher diffraction orders, preferably 2nd, 3rd 4th 5th, 6th and 12th could become highly efficient. Resolutions much higher than the outermost zone width could be achieved this way. This becomes important for FZPs with very high optical thick-nesses, where the alignment of the FZPs in optical axis is crucial.
Preferably the present invention allows the fabrication of full material FZPs with highly controlled tilt angles. The tilt angle is crucial for two reasons:
The tilt angle of each pillar in array may be optimized (preferably individually) to different in-coming X-ray energies. Thus, the array of FZP allows production of a plurality of different or identical FZPs in a fast and cost efficient manner.
Further goals, advantages, features and applications of the invention arise out of the following description of embodiments of the invention on the basis of the figures. Thereby all features described and shown in the figures alone or in arbitrary reasonable combination provide the subject matter of the invention independent of their conclusion in the claims or its dependency.
It shows:
However, fabrication of micro pillars (3) via FIB is preferred because it easily allows for controlling the tapering angles (a) by varying sputter time, beam energy and beam current. Independent from the above-mentioned techniques but especially when FIB is used, the fabrication of micro pillars (3) can result in controlled circularity, diameter, tilt angle and high surface smoothness.
In a preferred embodiment, Plasma FIB is used. By using Plasma FIB the milling speed can be further enhanced. With Plasma FIB, milling out pillars is about 30 times faster, compared to non-plasma FIB.
In a preferred embodiment single crystalline Au is used as a substrate material for the common carrier (2). This material allows for improved milling rates. The sputter yield of Au is very high. In an even further preferred embodiment the substrate is (111) type Au single crystal. It has been shown that milling out (111) type Au single crystal is about twice as fast as using (100) Au single crystal.
Irrespective of whether pillars (3) or cylindrical holes (4) are milled out/or laser written, circular geometries are preferred. The circularity of the (etched) structures and longer crack propagation lengths due to the trenches around pillars (3) or the (cylindrical) holes (4) may hinder crack propagation, enabling thicker depositions to be done crack-free.
As mentioned above, the step of production of the full material Fresnel Zone Plate precursor array (1) (e.g. the array of micro pillars) is followed by the deposition of alternating material layers onto it. The deposition is preferably performed by ALD. The deposition of alternating layers can be performed via selective or non-selective atomic layer deposition (ALD) and the individual layers act as the zones of the Fresnel zone plate, which can be sliced in a later step as described in detail below.
Thus, this process allows for the first time production of full material FZP (widely also known as multilayer or as sputter sliced) that does not have a micro fiber core. Until now, the micro fiber substrates could be deposited by other techniques (e.g. PLD or magnetron sputtering) than ALD although with more difficulty. However, by the currently disclosed process, highly conformal deposition onto these full material Fresnel Zone Plate precursor arrays (1), e.g. mi-cro-pillar arrays (1) can only be achieved by the ALD. This feature provides big advantages with respect to other techniques (e.g. the sputtered sliced or PLD deposited FZP intermediate products and the resultant FZPs). Here, especially circularity, diameter and tapering angle can be controlled very precisely. If a sputtering technique is to be used for the zones of the FZP, one has to start with a wire because it has to be ultimately symmetric for the following sputter deposition of the material while rotating the substrate wire core. However, rotation always results in errors such as inhomogeneous deposition of the materials.
In a preferred embodiment the arrangement of the pillars (3) or the different arrays (1) on the substrate may not be symmetrical with respect to central axis of the carrier substrate (2). However, each individual pillar (3) can be symmetric to its central axis. If the pattern of pillars as a whole is not symmetric to the central axis (L), the possibilities for conformal deposition of layers are very limited. Since patterns which are non-symmetric with respect to a (global) central axis are often utilized, ALD offers the only possibility to deposit conformal layers (or zones) of the FZP to these substrates.
So far, deposition of full material FZPs onto any other material than smooth glass fiber cores resulted in poor quality layer structures. Glass fibers provide a high circularity and smooth surface compared to metallic or ceramic fibers by its amorphous nature therefore limiting the substrate usage mostly to glass fibers. One further advantage of the method described here is that it vastly expands the possibly available materials as the substrate. Polymeric, single crystalline silicon and gold substrates have been utilized for fabrication of the pillar arrays (1) described here. However, one can envision utilization of a vast number of heat resistant polymeric, metallic, amorphous metallic, ceramic, glass, glass-ceramic and diamond based materials for the realization of the micro-pillars (3). When utilized, some of the high Z materials such as gold or lead can also act as a central stop to improve imaging contrast thus adding further advantage by avoiding the need for an external beamstop or a beamstop deposition onto the center of the full material FZP.
In a preferred embodiment the deposition process comprises the step of application of area selective ALD. One possible way would be to apply a hydrophobic material on the substrate and the top (6) of the micro pillars (3) but not onto the sidewalls. This can be achieved, for instance, by selectively functionalizing all horizontal planes with a Self-Assembled Monolayer (SAM) via a use of a proper molecule. This will ensure no deposition on those surfaces, enabling the deposition to happen only on the side walls (8) of the micro pillars (3).
In step 3 the alternating layers are deposited by ALD onto all non-coated surfaces (8). ALD is known from the prior art and will be described in more detail later. Because of the coating, ALD can be performed area selectively and the multilayer zones of the FZP can be deposited selectively onto the side walls (8) of the micro pillars (3). After deposition of the layers by ALD is completed, the coating (9) can be removed as illustrated in step 4. It remains a Fresnel Zone Plate array (1). If desired single FZP can be sliced down from this array and handled/used individually.
A tremendous advantage of ALD over other methods is that it is the only method for applying the individual layers onto the sidewalls of the pillars without rotation of the pillar (3) itself with respect to its central axis (L), hence making the process described here possible. Furthermore, because of the large excess of the precursor and their gas state, the individual molecules can easily reach every surface area, even within the holes or recesses (4) in which each individual pillar (3) is located (by using the FIB). Since the excess of precursor molecules is purged away (
Thus, ALD allows
If it is not desired to use the array of FZPs as a whole and/or if single FZPs are needed, single full material FZPs with optimum tilt angels can be sliced from the array and transferred on grids. A preferred embodiment of this process is illustrated in
As shown in
As shown in
Some advantages of the high resolution full material Fresnel Zone Plate array (column ALD ML-FZP) and the process for its fabrication are summarized in
An SEM image of one ML-FZPs (15) is shown in
In addition to the FZP (15) shown in
The sharp edges between individual layers (e.g. 19n and 19m or 19a and 19b) and the low roughness are illustrated even better in
Since the accuracy of each single layer (e.g. 19n, 19m, 19a or 19b) is extremely high, a very large number of layers in the range of thousands (19) can be applied onto a substrate without propagation of irregularities to further layers (19). Thus, the deposition thickness can be improved.
Since ALD is a cycle based deposition, it could be expected that the growth per cycle follows a linear curve. However, the correlation has been checked. The results are illustrated in
Direct imaging results which have been obtained at BESSY II are shown in
Furthermore diffraction efficiency calculations have been performed. For illustration purposes a selected FZP of different materials, the results are illustrated in
For X-rays from 1 to 1.6 keV, an imaging resolution of 15.5 nm could be achieved at a measured efficiency from 3 to 12.5% for the material system Al2O3—HfO2/Ta2O5.
For X-rays of 7.9 keV, a focal spot of 30 nm could be achieved at a measured efficiency of 15.6% for the material system Al2O3—Ta2O5.
All the features disclosed in the application documents are claimed as being essential to the invention, insofar as they are novel either individually or in combination as compared with the prior art.
| Number | Date | Country | Kind |
|---|---|---|---|
| 16184001.2 | Aug 2016 | EP | regional |
| 17161526.3 | Mar 2017 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2017/070456 | 8/11/2017 | WO | 00 |