Highly efficient manufacturing of silicon-carbon composite materials comprising ultra low Z

Information

  • Patent Grant
  • 12057569
  • Patent Number
    12,057,569
  • Date Filed
    Wednesday, August 2, 2023
    a year ago
  • Date Issued
    Tuesday, August 6, 2024
    3 months ago
Abstract
Silicon-carbon composite materials and related processes are disclosed that overcome the challenges for providing amorphous nano-sized silicon entrained within porous carbon. Compared to other, inferior materials and processes described in the prior art, the materials and processes disclosed herein find superior utility in various applications, including energy storage devices such as lithium ion batteries.
Description
BACKGROUND
Technical Field

Embodiments of the present invention generally relate to methods of manufacturing silicon-carbon composite materials with properties that overcome the challenges for providing amorphous nano-sized silicon entrained within porous carbon. Said silicon-carbon composites are produced via chemical infiltration chemical vapor infiltration to impregnate amorphous, nano-sized silicon within the pores of a porous scaffold. Suitable porous scaffolds include, but are not limited to, porous carbon scaffolds, for example carbon having a pore volume comprising micropores (less than 2 nm), mesopores (2 to 50 nm), and/or macropores (greater than 50 nm). Suitable precursors for the carbon scaffold include, but are not limited to, sugars and polyols, organic acids, phenolic compounds, cross-linkers, and amine compounds. Suitable compositing materials include, but are not limited to, silicon materials. Precursors for the silicon include, but are not limited to, silicon containing gases such as silane, high-order silanes (such as di-, tri-, and/or tetrasilane), and/or chlorosilane(s) (such as mono-, di-, tri-, and tetrachlorosilane) and mixtures thereof. Chemical vapor infiltration (CVI) of silicon into the pores of porous scaffold materials is accomplished by exposing said porous scaffold to silicon-containing gas (e.g., silane) at elevated temperatures. The porous carbon scaffold can be a particulate porous carbon.


A key outcome in this regard is to achieve the desired form of silicon in the desired form, namely amorphous nano-sized silicon. Furthermore, another key outcome is to achieve the silicon impregnation within the pores of the porous carbon. Yet another key outcome is to achieve high utilization of the silicon-containing gas, i.e., achieve a high fraction of the silicon introduced into the CVI reactor that converts into silicon impregnated into to pores of the porous carbon in the form of amorphous nano-sized silicon. Such manufacturing processes and materials produced therefore, for example, silicon-carbon composite materials, have utility as anode materials for energy storage devices, for example lithium ion batteries.


Description of the Related Art

CVI is a process wherein a gaseous substrate reacts within a porous scaffold material. This approach can be employed to produce composite materials, for instance silicon-carbon composites, wherein a silicon-containing gas decomposes at elevated temperature within a porous carbon scaffold. While this approach can be employed to manufacture a variety of composite materials, there is particular interest in silicon-carbon (Si—C) composite materials. Such Si—C composite materials have utility, for example as energy storage materials, for example as an anode material within a lithium ion battery (LIB). LIB s have potential to replace devices currently used in any number of applications. For example, current lead acid automobile batteries are not adequate for next generation all-electric and hybrid electric vehicles due to irreversible, stable sulfate formations during discharge. Lithium ion batteries are a viable alternative to the lead-based systems currently used due to their capacity, and other considerations.


To this end, there is continued strong interest in developing new LIB anode materials, particularly silicon, which has 10-fold higher gravimetric capacity than conventional graphite. However, silicon exhibits large volume change during cycling, in turn leading to electrode deterioration and solid-electrolyte interphase (SEI) instability. The most common amelioration approach is to reduce silicon particle size, for instance Dv50<150 nm, for instance Dv50<100 nm, for instance Dv50<50 nm, for instance Dv50<20 nm, for instance Dv50<10 nm, for instance Dv50<5 nm, for instance Dv50<2 nm, either as discrete particles or within a matrix. Thus far, techniques for creating nano-scale silicon involve high-temperature reduction of silicon oxide, extensive particle diminution, multi-step toxic etching, and/or other cost prohibitive processes. Likewise, common matrix approaches involve expensive materials such as graphene or nano-graphite, and/or require complex processing and coating.


It is known from scientific literature that non-graphitizable (hard) carbon is beneficial as a LIB anode material (Liu Y, Xue, J S, Zheng T, Dahn, J R. Carbon 1996, 34:193-200; Wu, Y P, Fang, S B, Jiang, Y Y. 1998, 75:201-206; Buiel E, Dahn J R. Electrochim Acta 1999 45:121-130). The basis for this improved performance stems from the disordered nature of the graphene layers that allows Li-ions to intercalate on either side of the graphene plane allowing for theoretically double the stoichiometric content of Li ions versus crystalline graphite. Furthermore, the disordered structure improves the rate capability of the material by allowing Li ions to intercalate isotropically as opposed to graphite where lithiation can only proceed in parallel to the stacked graphene planes. Despite these desirable electrochemical properties, amorphous carbons have not seen wide-spread deployment in commercial Li-ion batteries, owing primarily to low FCE and low bulk density (<1 g/cc). Instead, amorphous carbon has been used more commonly as a low-mass additive and coating for other active material components of the battery to improve conductivity and reduce surface side reactions.


In recent years, amorphous carbon as a LIB battery material has received considerable attention as a coating for silicon anode materials. Such a silicon-carbon core-shell structure has the potential for not only improving conductivity, but also buffering the expansion of silicon as it lithiates, thus stabilizing its cycle stability and minimizing problems associated with particle pulverization, isolation, and SEI integrity (Jung, Y, Lee K, Oh, S. Electrochim Acta 2007 52:7061-7067; Zuo P, Yin G, Ma Y. Electrochim Acta 2007 52:4878-4883; Ng S H, Wang J, Wexler D, Chew S Y, Liu H K. J Phys Chem C 2007 111:11131-11138). Problems associated with this strategy include the lack of a suitable silicon starting material that is amenable to the coating process, and the inherent lack of engineered void space within the carbon-coated silicon core-shell composite particle to accommodate expansion of the silicon during lithiation. This inevitably leads to cycle stability failure due to destruction of core-shell structure and SEI layer (Beattie S D, Larcher D, Morcrette M, Simon B, Tarascon, J-M. J Electrochem Soc 2008 155:A158-A163).


An alternative to core shell structure is a structure wherein amorophous, nano-sized silicon is homogeously distributed within the porosity of a porous carbon scaffold. The porous carbon allows for desirable properties: (i) carbon porosity provides void volume to accommodate the expansion of silicon during lithiation thus reducing the net composite particle expansion at the electrode level; (ii) the disordered graphene network provides increased electrical conductivity to the silicon thus enabling faster charge/discharge rates, (iii) nano-pore structure acts as a template for the synthesis of silicon thereby dictating its size, distribution, and morphology.


To this end, the desired inverse hierarchical structure can be achieved by employing CVI wherein a silicon-containing gas can completely permeate nanoporous carbon and decompose therein to nano-sized silicon. The CVI approach confers several advantages in terms of silicon structure. One advantage is that nanoporous carbon provides nucleation sites for growing silicon while dictating maximum particle shape and size. Confining the growth of silicon within a nano-porous structure affords reduced susceptibility to cracking or pulverization and loss of contact caused by expansion. Moreover, this structure promotes nano-sized silicon to remain as amorphous phase. This property provides the opportunity for high charge/discharge rates, particularly in combination with silicon's vicinity within the conductive carbon scaffold. This system provides a high-rate-capable, solid-state lithium diffusion pathway that directly delivers lithium ions to the nano-scale silicon interface. Another benefit of the silicon provide via CVI within the carbon scaffold is the inhibition of formation of undesirable crystalline Li15Si4 phase. Yet another benefit is that the CVI process provides for void space within the particle interior.


In order to quantitate the percentage loading of silicon comprising the silicon-carbon composite, thermogravimetric analysis (TGA) may be employed. For this purpose, the silicon-composite is heated from 25° C. to 1100° C., which, without being bound by theory, provides for burn off of all carbon, and oxidation of all silicon to SiO2. Thus, the % silicon comprising the silicon-carbon composite is calculated as

% Si=100×[[M1100×(28/(28+(16×2)))]/M°]

wherein M1100 is the mass of the silicon-carbon composite at 1100° C. and M° is the minimum mass of the silicon-carbon composite between 30° C. and 200° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis.


In order to gauge relative amount of silicon impregnated into the porosity of the porous carbon, thermogravimetric analysis TGA may be employed. TGA can be employed to assess the fraction of silicon residing within the porosity of porous carbon relative to the total silicon present, i.e., sum of silicon within the porosity and on the particle surface. As the silicon-carbon composite is heated under air, the sample exhibits a mass increase that initiates at about 300° C. to 500° C. that reflects initial oxidation of silicon to SiO2, and then the sample exhibits a mass loss as the carbon is burned off, and then the sample exhibits mass increase reflecting resumed conversion of silicon into SiO2 which increases towards an asymptotic value as the temperature approaches 1100° C. as silicon oxidizes to completion. For the purposes of this analysis, it is assumed that the minimum mass recorded for the sample as it heated from 800° C. to 1100° C. represents the point at which carbon buroff is complete. Any further mass increase beyond that point corresponds to the oxidation of silicon to SiO2 and that the total mass at completion of oxidation is SiO2. Thus, the percentage of unoxidized silicon after carbon burnoff as a proportion of the total amount of silicon can be determined using the formula:

Z=1.875×[(M1100−M)/M1100]×100

where M1100 is the mass of the sample at completion of oxidation at a temperature of 1100° C., and M is the minimum mass recorded for the sample as it is heated from 800° C. to 1100° C.


Without being bound by theory, the temperature at which silicon is oxidized under TGA conditions relates to the length scale of the oxide coating on the silicon due to the diffusion of oxygen atoms through the oxide layer. Thus, silicon residing within the carbon porosity will oxidize at a lower temperature than deposits of silicon on a particle surface due to the necessarily thinner coating existing on these surfaces. In this fashion, calculation of Z is used to quantitatively assess the fraction of silicon not impregnated within the porosity of the porous carbon scaffold.


BRIEF SUMMARY

Silicon-carbon composite materials and related processes are disclosed that overcome the challenges for providing amorphous nano-sized silicon entrained within porous carbon. Compared to other, inferior materials and processes described in the prior art, the materials and processes disclosed herein find superior utility in various applications, including energy storage devices such as lithium ion batteries.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1. Relationship between Z and average Coulombic efficiency for various silicon-carbon composite materials.



FIG. 2. Differential capacity vs voltage plot for Silicon-Carbon Composite 3 from 2nd cycle using a half-cell.



FIG. 3. Differential capacity vs voltage plot for Silicon-Carbon Composite 3 from 2nd cycle to 5th cycle using a half-cell.



FIG. 4. dQ/dV vs V plot for various silicon-carbon composite materials.



FIG. 5. Example of Calculation of q for Silicon-Carbon Composite 3.



FIG. 6. Z vs φ plot for various silicon-carbon composite materials.



FIG. 7. YCVI vs XSi plot for various silicon-carbon composite materials.



FIG. 8. Silane utilization (%) as determined from Fourier-transformed infrared spectroscopy (FTIR) as a function on run time for the preparation of Sample 21.





DETAILED DESCRIPTION

In the following description, certain specific details are set forth in order to provide a thorough understanding of various embodiments. However, one skilled in the art will understand that the invention may be practiced without these details. In other instances, well-known structures have not been shown or described in detail to avoid unnecessarily obscuring descriptions of the embodiments. Unless the context requires otherwise, throughout the specification and claims which follow, the word “comprise” and variations thereof, such as, “comprises” and “comprising” are to be construed in an open, inclusive sense, that is, as “including, but not limited to.” Further, headings provided herein are for convenience only and do not interpret the scope or meaning of the claimed invention.


Reference throughout this specification to “one embodiment” or “an embodiment” means that a particular feature, structure or characteristic described in connection with the embodiment is included in at least one embodiment. Thus, the appearances of the phrases “in one embodiment” or “in an embodiment” in various places throughout this specification are not necessarily all referring to the same embodiment. Furthermore, the particular features, structures, or characteristics may be combined in any suitable manner in one or more embodiments. Also, as used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the content clearly dictates otherwise. It should also be noted that the term “or” is generally employed in its sense including “and/or” unless the content clearly dictates otherwise.


A. Porous Scaffold Materials


For the purposes of embodiments of the current invention, a porous scaffold may be used, into which silicon is to be impregnated. In this context, the porous scaffold can comprise various materials. In some embodiments the porous scaffold material primarily comprises carbon, for example hard carbon. Other allotropes of carbon are also envisioned in other embodiments, for example, graphite, amorphous carbon, diamond, C60, carbon nanotubes (e.g., single and/or multi-walled), graphene and/or carbon fibers. The introduction of porosity into the carbon material can be achieved by a variety of means. For instance, the porosity in the carbon material can be achieved by modulation of polymer precursors, and/or processing conditions to create said porous carbon material, and described in detail in the subsequent section.


In other embodiments, the porous scaffold comprises a polymer material. To this end, a wide variety of polymers are envisioned in various embodiments to have utility, including, but not limited to, inorganic polymer, organic polymers, and addition polymers. Examples of inorganic polymers in this context includes, but are not limited to homochain polymers of silicon-silicon such as polysilanes, silicon carbide, polygermanes, and polystannanes. Additional examples of inorganic polymers includes, but are not limited to, heterochain polymers such as polyborazylenes, polysiloxanes like polydimethylsiloxane (PDMS), polymethylhydrosiloxane (PMHS) and polydiphenylsiloxane, polysilazanes like perhydridopolysilazane (PHPS), polyphosphazenes and poly(dichlorophosphazenes), polyphosphates, polythiazyls, and polysulfides. Examples of organic polymers includes, but are not limited to, low density polyethylene (LDPE), high density polyethylene (HDPE), polypropylene (PP), polyvinyl chloride (PVC), polystyrene (PS), nylon, nylon 6, nylon 6,6, teflon (Polytetrafluoroethylene), thermoplastic polyurethanes (TPU), polyureas, poly(lactide), poly(glycolide) and combinations thereof, phenolic resins, polyamides, polyaramids, polyethylene terephthalate, polychloroprene, polyacrylonitrile, polyaniline, polyimide, poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PDOT:PSS), and others known in the arts. The organic polymer can be synthetic or natural in origin. In some embodiments, the polymer is a polysaccharide, such as starch, cellulose, cellobiose, amylose, amylpectin, gum Arabic, lignin, and the like. In some embodiments, the polysaccharide is derived from the carmelization of mono- or oligomeric sugars, such as fructose, glucose, sucrose, maltose, raffinose, and the like.


In certain embodiments, the porous scaffold polymer material comprises a coordination polymer. Coordination polymers in this context include, but are not limited to, metal organic frameworks (MOFs). Techniques for production of MOFs, as well as exemplary species of MOFs, are known and described in the art (“The Chemistry and Applications of Metal-Organic Frameworks, Hiroyasu Furukawa et al. Science 341, (2013); DOI: 10.1126/science.1230444). Examples of MOFs in the context include, but are not limited to, Basolite™ materials and zeolitic imidazolate frameworks (ZIFs).


Concomitant with the myriad variety of polymers envisioned with the potential to provide a porous substrate, various processing approaches are envisioned in various embodiments to achieve said porosity. In this context, general methods for imparting porosity into various materials are myriad, as known in the art, including, but certainly not limited to, methods involving emulsification, micelle creation, gasification, dissolution followed by solvent removal (for example, lyophilization), axial compaction and sintering, gravity sintering, powder rolling and sintering, isostatic compaction and sintering, metal spraying, metal coating and sintering, metal injection molding and sintering, and the like. Other approaches to create a porous polymeric material, including creation of a porous gel, such as a freeze dried gel, aerogel, and the like are also envisioned.


In certain embodiments, the porous scaffold material comprises a porous ceramic material. In certain embodiments, the porous scaffold material comprises a porous ceramic foam. In this context, general methods for imparting porosity into ceramic materials are varied, as known in the art, including, but certainly not limited to, creation of porous In this context, general methods and materials suitable for comprising the porous ceramic include, but are not limited to, porous aluminum oxide, porous zirconia toughened alumina, porous partially stabilized zirconia, porous alumina, porous sintered silicon carbide, sintered silicon nitride, porous cordierite, porous zirconium oxide, clay-bound silicon carbide, and the like.


In certain embodiments, the porous scaffold comprises porous silica or other silicon material containing oxygen. The creation of silicon gels, including sol gels, and other porous silica materials is known in the art.


In certain embodiments, the porous material comprises a porous metal. Suitable metals in this regard include, but are not limited to porous aluminum, porous steel, porous nickel, porous Inconcel, porous Hasteloy, porous titanium, porous copper, porous brass, porous gold, porous silver, porous germanium, and other metals capable of being formed into porous structures, as known in the art. In some embodiments, the porous scaffold material comprises a porous metal foam. The types of metals and methods to manufacture related to same are known in the art. Such methods include, but are not limited to, casting (including foaming, infiltration, and lost-foam casting), deposition (chemical and physical), gas-eutectic formation, and powder metallurgy techniques (such as powder sintering, compaction in the presence of a foaming agent, and fiber metallurgy techniques).


B. Porous Carbon Scaffold


Methods for preparing porous carbon materials from polymer precursors are known in the art. For example, methods for preparation of carbon materials are described in U.S. Pat. Nos. 7,723,262, 8,293,818, 8,404,384, 8,654,507, 8,916,296, 9,269,502, 10,590,277, and U.S. patent application Ser. No. 16/745,197, the full disclosures of which are hereby incorporated by reference in their entireties for all purposes.


Accordingly, in one embodiment the present disclosure provides a method for preparing any of the carbon materials or polymer gels described above. The carbon materials may be synthesized through pyrolysis of either a single precursor, for example a saccharide material such as sucrose, fructose, glucose, dextrin, maltodextrin, starch, amylopectin, amlyose, lignin, gum Arabic, and other saccharides known in the art, and combinations thereof. Alternatively, the carbon materials may be synthesized through pyrolysis of a complex resin, for instance formed using a sol-gel method using polymer precursors such as phenol, resorcinol, bisphenol A, urea, melamine, and other suitable compounds known in the art, and combinations thereof, in a suitable solvent such as water, ethanol, methanol, and other solvents known in the art, and combinations thereof, with cross-linking agents such as formaldehyde, hexamethylenetetramine, furfural, and other cross-lining agents known in the art, and combinations thereof. The resin may be acid or basic, and may contain a catalyst. The catalyst may be volatile or non-volatile. The pyrolysis temperature and dwell time can vary as known in the art.


In some embodiments, the methods comprise preparation of a polymer gel by a sol gel process, condensation process or crosslinking process involving monomer precursor(s) and a crosslinking agent, two existing polymers and a crosslinking agent or a single polymer and a crosslinking agent, followed by pyrolysis of the polymer gel. The polymer gel may be dried (e.g., freeze dried) prior to pyrolysis; however drying is not necessarily required.


The target carbon properties can be derived from a variety of polymer chemistries provided the polymerization reaction produces a resin/polymer with the necessary carbon backbone. Different polymer families include novolacs, resoles, acrylates, styrenics, ureathanes, rubbers (neoprenes, styrene-butadienes, etc.), nylons, etc. The preparation of any of these polymer resins can occur via a number of different processes including sol gel, emulsion/suspension, solid state, solution state, melt state, etc for either polymerization and crosslinking processes.


In some embodiments an electrochemical modifier is incorporated into the material as polymer. For example, the organic or carbon containing polymer, RF for example, is copolymerized with the polymer, which contains the electrochemical modifier. In one embodiment, the electrochemical modifier-containing polymer contains silicon. In one embodiment the polymer is tetraethylorthosiliane (TEOS). In one embodiment, a TEOS solution is added to the RF solution prior to or during polymerization. In another embodiment the polymer is a polysilane with organic side groups. In some cases these side groups are methyl groups, in other cases these groups are phenyl groups, in other cases the side chains include phenyl, pyrol, acetate, vinyl, siloxane fragments. In some cases the side chain includes a group 14 element (silicon, germanium, tin or lead). In other cases the side chain includes a group 13 element (boron, aluminum, boron, gallium, indium). In other cases the side chain includes a group 15 element (nitrogen, phosphorous, arsenic). In other cases the side chain includes a group 16 element (oxygen, sulfur, selenium).


In another embodiment the electrochemical modifier comprises a silole. In some cases it is a phenol-silole or a silafluorene. In other cases it is a poly-silole or a poly-silafluorene. In some cases the silicon is replaced with germanium (germole or germafluorene), tin (stannole or stannaflourene) nitrogen (carbazole) or phosphorous (phosphole, phosphafluorene). In all cases the heteroatom containing material can be a small molecule, an oligomer or a polymer. Phosphorous atoms may or may not be also bonded to oxygen.


In some embodiments the reactant comprises phosphorous. In certain other embodiments, the phosphorus is in the form of phosphoric acid. In certain other embodiments, the phosphorus can be in the form of a salt, wherein the anion of the salt comprises one or more phosphate, phosphite, phosphide, hydrogen phosphate, dihydrogen phosphate, hexafluorophosphate, hypophosphite, polyphosphate, or pyrophosphate ions, or combinations thereof. In certain other embodiments, the phosphorus can be in the form of a salt, wherein the cation of the salt comprises one or more phosphonium ions. The non-phosphate containing anion or cation pair for any of the above embodiments can be chosen for those known and described in the art. In the context, exemplary cations to pair with phosphate-containing anions include, but are not limited to, ammonium, tetraethylammonium, and tetramethylammonium ions. In the context, exemplary anions to pair with phosphate-containing cations include, but are not limited to, carbonate, dicarbonate, and acetate ions.


In some embodiments, the catalyst comprises a basic volatile catalyst. For example, in one embodiment, the basic volatile catalyst comprises ammonium carbonate, ammonium bicarbonate, ammonium acetate, ammonium hydroxide, or combinations thereof. In a further embodiment, the basic volatile catalyst is ammonium carbonate. In another further embodiment, the basic volatile catalyst is ammonium acetate.


In still other embodiments, the method comprises admixing an acid. In certain embodiments, the acid is a solid at room temperature and pressure. In some embodiments, the acid is a liquid at room temperature and pressure. In some embodiments, the acid is a liquid at room temperature and pressure that does not provide dissolution of one or more of the other polymer precursors.


The acid may be selected from any number of acids suitable for the polymerization process. For example, in some embodiments the acid is acetic acid and in other embodiments the acid is oxalic acid. In further embodiments, the acid is mixed with the first or second solvent in a ratio of acid to solvent of 99:1, 90:10, 75:25, 50:50, 20:80, 10:90 or 1:90. In other embodiments, the acid is acetic acid and the first or second solvent is water. In other embodiments, acidity is provided by adding a solid acid.


The total content of acid in the mixture can be varied to alter the properties of the final product. In some embodiments, the acid is present from about 1% to about 50% by weight of mixture. In other embodiments, the acid is present from about 5% to about 25%. In other embodiments, the acid is present from about 10% to about 20%, for example about 10%, about 15% or about 20%.


In certain embodiments, the polymer precursor components are blended together and subsequently held for a time and at a temperature sufficient to achieve polymerization. One or more of the polymer precursor components can have particle size less than about 20 mm in size, for example less than 10 mm, for example less than 7 mm, for example, less than 5 mm, for example less than 2 mm, for example less than 1 mm, for example less than 100 microns, for example less than 10 microns. In some embodiments, the particle size of one or more of the polymer precursor components is reduced during the blending process.


The blending of one or more polymer precursor components in the absence of solvent can be accomplished by methods described in the art, for example ball milling, jet milling, Fritsch milling, planetary mixing, and other mixing methodologies for mixing or blending solid particles while controlling the process conditions (e.g., temperature). The mixing or blending process can be accomplished before, during, and/or after (or combinations thereof) incubation at the reaction temperature.


Reaction parameters include aging the blended mixture at a temperature and for a time sufficient for the one or more polymer precursors to react with each other and form a polymer. In this respect, suitable aging temperature ranges from about room temperature to temperatures at or near the melting point of one or more of the polymer precursors. In some embodiments, suitable aging temperature ranges from about room temperature to temperatures at or near the glass transition temperature of one or more of the polymer precursors. For example, in some embodiments the solvent free mixture is aged at temperatures from about 20° C. to about 600° C., for example about 20° C. to about 500° C., for example about 20° C. to about 400° C., for example about 20° C. to about 300° C., for example about 20° C. to about 200° C. In certain embodiments, the solvent free mixture is aged at temperatures from about 50 to about 250° C.


The reaction duration is generally sufficient to allow the polymer precursors to react and form a polymer, for example the mixture may be aged anywhere from 1 hour to 48 hours, or more or less depending on the desired result. Typical embodiments include aging for a period of time ranging from about 2 hours to about 48 hours, for example in some embodiments aging comprises about 12 hours and in other embodiments aging comprises about 4-8 hours (e.g., about 6 hours).


In certain embodiments, an electrochemical modifier is incorporated during the above described polymerization process. For example, in some embodiments, an electrochemical modifier in the form of metal particles, metal paste, metal salt, metal oxide or molten metal can be dissolved or suspended into the mixture from which the gel resin is produced


Exemplary electrochemical modifiers for producing composite materials may fall into one or more than one of the chemical classifications. In some embodiments, the electrochemical modifier is a lithium salt, for example, but not limited to, lithium fluoride, lithium chloride, lithium carbonate, lithium hydroxide, lithium benzoate, lithium bromide, lithium formate, lithium hexafluorophosphate, lithium iodate, lithium iodide, lithium perchlorate, lithium phosphate, lithium sulfate, lithium tetraborate, lithium tetrafluoroborate, and combinations thereof.


In certain embodiments, the electrochemical modifier comprises a metal, and exemplary species includes, but are not limited to aluminum isoproproxide, manganese acetate, nickel acetate, iron acetate, tin chloride, silicon chloride, and combinations thereof. In certain embodiments, the electrochemical modifier is a phosphate compound, including but not limited to phytic acid, phosphoric acid, ammonium dihydrogenphosphate, and combinations thereof. In certain embodiments, the electrochemical modifier comprises silicon, and exemplary species includes, but are not limited to silicon powders, silicon nanotubes, polycrystalline silicon, nanocrystalline silicon, amorpohous silicon, porous silicon, nano sized silicon, nano-featured silicon, nano-sized and nano-featured silicon, silicyne, and black silicon, and combinations thereof.


Electrochemical modifiers can be combined with a variety of polymer systems through either physical mixing or chemical reactions with latent (or secondary) polymer functionality. Examples of latent polymer functionality include, but are not limited to, epoxide groups, unsaturation (double and triple bonds), acid groups, alcohol groups, amine groups, basic groups. Crosslinking with latent functionality can occur via heteroatoms (e.g. vulcanization with sulfur, acid/base/ring opening reactions with phosphoric acid), reactions with organic acids or bases (described above), coordination to transition metals (including but not limited to Ti, Cr, Mn, Fe, Co, Ni, Cu, Zn, Zr, Nb, Mo, Ag, Au), ring opening or ring closing reactions (rotaxanes, spiro compounds, etc).


Electrochemical modifiers can also be added to the polymer system through physical blending. Physical blending can include but is not limited to melt blending of polymers and/or co-polymers, the inclusion of discrete particles, chemical vapor deposition of the electrochemical modifier and coprecipitation of the electrochemical modifier and the main polymer material.


In some instances the electrochemical modifier can be added via a metal salt solid, solution, or suspension. The metal salt solid, solution or suspension may comprise acids and/or alcohols to improve solubility of the metal salt. In yet another variation, the polymer gel (either before or after an optional drying step) is contacted with a paste comprising the electrochemical modifier. In yet another variation, the polymer gel (either before or after an optional drying step) is contacted with a metal or metal oxide sol comprising the desired electrochemical modifier.


In addition to the above exemplified electrochemical modifiers, the composite materials may comprise one or more additional forms (i.e., allotropes) of carbon. In this regard, it has been found that inclusion of different allotropes of carbon such as graphite, amorphous carbon, conductive carbon, carbon black, diamond, C60, carbon nanotubes (e.g., single and/or multi-walled), graphene and/or carbon fibers into the composite materials is effective to optimize the electrochemical properties of the composite materials. The various allotropes of carbon can be incorporated into the carbon materials during any stage of the preparation process described herein. For example, during the solution phase, during the gelation phase, during the curing phase, during the pyrolysis phase, during the milling phase, or after milling. In some embodiments, the second carbon form is incorporated into the composite material by adding the second carbon form before or during polymerization of the polymer gel as described in more detail herein. The polymerized polymer gel containing the second carbon form is then processed according to the general techniques described herein to obtain a carbon material containing a second allotrope of carbon.


In a preferred embodiment, the carbon is produced from precursors with little of no solvent required for processing (solvent free). The structure of the polymer precursors suitable for use in a low solvent or essentially solvent free reaction mixture is not particularly limited, provided that the polymer precursor is capable of reacting with another polymer precursor or with a second polymer precursor to form a polymer. Polymer precursors include amine-containing compounds, alcohol-containing compounds and carbonyl-containing compounds, for example in some embodiments the polymer precursors are selected from an alcohol, a phenol, a polyalcohol, a sugar, an alkyl amine, an aromatic amine, an aldehyde, a ketone, a carboxylic acid, an ester, a urea, an acid halide and an isocyanate.


In one embodiment employing a low or essentially solvent free reaction mixture, the method comprises use of a first and second polymer precursor, and in some embodiments the first or second polymer precursor is a carbonyl containing compound and the other of the first or second polymer precursor is an alcohol containing compound. In some embodiments, a first polymer precursor is a phenolic compound and a second polymer precursor is an aldehyde compound (e.g., formaldehyde). In one embodiment, of the method the phenolic compound is phenol, resorcinol, catechol, hydroquinone, phloroglucinol, or a combination thereof; and the aldehyde compound is formaldehyde, acetaldehyde, propionaldehyde, butyraldehyde, benzaldehyde, cinnamaldehyde, or a combination thereof. In a further embodiment, the phenolic compound is resorcinol, phenol or a combination thereof, and the aldehyde compound is formaldehyde. In yet further embodiments, the phenolic compound is resorcinol and the aldehyde compound is formaldehyde. In some embodiments, the polymer precursors are alcohols and carbonyl compounds (e.g., resorcinol and aldehyde) and they are present in a ratio of about 0.5:1.0, respectively.


The polymer precursor materials suitable for low or essentially solvent free reaction mixture as disclosed herein include (a) alcohols, phenolic compounds, and other mono- or polyhydroxy compounds and (b) aldehydes, ketones, and combinations thereof. Representative alcohols in this context include straight chain and branched, saturated and unsaturated alcohols. Suitable phenolic compounds include polyhydroxy benzene, such as a dihydroxy or trihydroxy benzene. Representative polyhydroxy benzenes include resorcinol (i.e., 1,3-dihydroxy benzene), catechol, hydroquinone, and phloroglucinol. Other suitable compounds in this regard are bisphenols, for instance, bisphenol A. Mixtures of two or more polyhydroxy benzenes can also be used. Phenol (monohydroxy benzene) can also be used. Representative polyhydroxy compounds include sugars, such as glucose, sucrose, fructose, chitin and other polyols, such as mannitol. Aldehydes in this context include: straight chain saturated aldehydes such as methanal (formaldehyde), ethanal (acetaldehyde), propanal (propionaldehyde), butanal (butyraldehyde), and the like; straight chain unsaturated aldehydes such as ethenone and other ketenes, 2-propenal (acrylaldehyde), 2-butenal (crotonaldehyde), 3 butenal, and the like; branched saturated and unsaturated aldehydes; and aromatic-type aldehydes such as benzaldehyde, salicylaldehyde, hydrocinnamaldehyde, and the like. Suitable ketones include: straight chain saturated ketones such as propanone and 2 butanone, and the like; straight chain unsaturated ketones such as propenone, 2 butenone, and 3 butenone (methyl vinyl ketone) and the like; branched saturated and unsaturated ketones; and aromatic-type ketones such as methyl benzyl ketone (phenylacetone), ethyl benzyl ketone, and the like. The polymer precursor materials can also be combinations of the precursors described above.


In some embodiments, one polymer precursor in the low or essentially solvent free reaction mixture is an alcohol-containing species and another polymer precursor is a carbonyl-containing species. The relative amounts of alcohol-containing species (e.g., alcohols, phenolic compounds and mono- or poly-hydroxy compounds or combinations thereof) reacted with the carbonyl containing species (e.g. aldehydes, ketones or combinations thereof) can vary substantially. In some embodiments, the ratio of alcohol-containing species to aldehyde species is selected so that the total moles of reactive alcohol groups in the alcohol-containing species is approximately the same as the total moles of reactive carbonyl groups in the aldehyde species. Similarly, the ratio of alcohol-containing species to ketone species may be selected so that the total moles of reactive alcohol groups in the alcohol containing species is approximately the same as the total moles of reactive carbonyl groups in the ketone species. The same general 1:1 molar ratio holds true when the carbonyl-containing species comprises a combination of an aldehyde species and a ketone species.


In other embodiments, the polymer precursor in the low or essentially solvent free reaction mixture is a urea or an amine containing compound. For example, in some embodiments the polymer precursor is urea, melamine, hexamethylenetetramine (HMT) or combination thereof. Other embodiments include polymer precursors selected from isocyanates or other activated carbonyl compounds such as acid halides and the like.


Some embodiments of the disclosed methods include preparation of low or solvent-free polymer gels (and carbon materials) comprising electrochemical modifiers. Such electrochemical modifiers include, but are not limited to nitrogen, silicon, and sulfur. In other embodiments, the electrochemical modifier comprises fluorine, iron, tin, silicon, nickel, aluminum, zinc, or manganese. The electrochemical modifier can be included in the preparation procedure at any step. For example, in some the electrochemical modifier is admixed with the mixture, the polymer phase or the continuous phase.


The blending of one or more polymer precursor components in the absence of solvent can be accomplished by methods described in the art, for example ball milling, jet milling, Fritsch milling, planetary mixing, and other mixing methodologies for mixing or blending solid particles while controlling the process conditions (e.g., temperature). The mixing or blending process can be accomplished before, during, and/or after (or combinations thereof) incubation at the reaction temperature.


Reaction parameters include aging the blended mixture at a temperature and for a time sufficient for the one or more polymer precursors to react with each other and form a polymer. In this respect, suitable aging temperature ranges from about room temperature to temperatures at or near the melting point of one or more of the polymer precursors. In some embodiments, suitable aging temperature ranges from about room temperature to temperatures at or near the glass transition temperature of one or more of the polymer precursors. For example, in some embodiments the solvent free mixture is aged at temperatures from about 20° C. to about 600° C., for example about 20° C. to about 500° C., for example about 20° C. to about 400° C., for example about 20° C. to about 300° C., for example about 20° C. to about 200° C. In certain embodiments, the solvent free mixture is aged at temperatures from about 50 to about 250° C.


The porous carbon material can be achieved via pyrolysis of a polymer produced from precursors materials as described above. In some embodiments, the porous carbon material comprises an amorphous activated carbon that is produced by pyrolysis, physical or chemical activation, or combination thereof in either a single process step or sequential process steps.


The temperature and dwell time of pyrolysis can be varied, for example the dwell time van vary from 1 min to 10 min, from 10 min to 30 min, from 30 min to 1 hour, for 1 hour to 2 hours, from 2 hours to 4 hours, from 4 hours to 24 h. The temperature can be varied, for example, the pyrolysis temperature can vary from 200 to 300 C, from 250 to 350 C, from 350 C to 450 C, from 450 C to 550 C, from 540 C to 650 C, from 650 C to 750 C, from 750 C to 850 C, from 850 C to 950 C, from 950 C to 1050 C, from 1050 C to 1150 C, from 1150 C to 1250 C. The pyrolysis can be accomplished in an inert gas, for example nitrogen, or argon.


In some embodiments, an alternate gas is used to further accomplish carbon activation. In certain embodiments, pyrolysis and activation are combined. Suitable gases for accomplishing carbon activation include, but are not limited to, carbon dioxide, carbon monoxide, water (steam), air, oxygen, and further combinations thereof. The temperature and dwell time of activation can be varied, for example the dwell time van vary from 1 min to 10 min, from 10 min to 30 min, from 30 min to 1 hour, for 1 hour to 2 hours, from 2 hours to 4 hours, from 4 hours to 24 h. The temperature can be varied, for example, the pyrolysis temperature can vary from 200 to 300 C, from 250 to 350 C, from 350 C to 450 C, from 450 C to 550 C, from 540 C to 650 C, from 650 C to 750 C, from 750 C to 850 C, from 850 C to 950 C, from 950 C to 1050 C, from 1050 C to 1150 C, from 1150 C to 1250 C.


Either prior to the pyrolysis, and/or after pyrolysis, and/or after activation, the carbon may be subjected to a particle size reduction. The particle size reduction can be accomplished by a variety of techniques known in the art, for example by jet milling in the presence of various gases including air, nitrogen, argon, helium, supercritical steam, and other gases known in the art. Other particle size reduction methods, such as grinding, ball milling, jet milling, water jet milling, and other approaches known in the art are also envisioned.


The porous carbon scaffold may be in the form of particles. The particle size and particle size distribution can be measured by a variety of techniques known in the art, and can be described based on fractional volume. In this regard, the Dv,50 of the carbon scaffold may be between 10 nm and 10 mm, for example between 100 nm and 1 mm, for example between 1 um and 100 um, for example between 2 um and 50 um, example between 3 um and 30 um, example between 4 um and 20 um, example between 5 um and 10 um. In certain embodiments, the Dv50 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv100 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv99 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv90 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv0 is greater than 10 nm, for example greater than 100 nm, for example greater than 500 nm, for example greater than 1 um, for example greater than 2 um, for example greater than 5 um, for example greater than 10 um. In certain embodiments, the Dv1 is greater than 10 nm, for example greater than 100 nm, for example greater than 500 nm, for example greater than 1 um, for example greater than 2 um, for example greater than 5 um, for example greater than 10 um. In certain embodiments, the Dv10 is greater than 10 nm, for example greater than 100 nm, for example greater than 500 nm, for example greater than 1 um, for example greater than 2 um, for example greater than 5 um, for example greater than 10 um.


In some embodiments, the surface area of the porous carbon scaffold can comprise a surface area greater than 400 m2/g, for example greater than 500 m2/g, for example greater than 750 m2/g, for example greater than 1000 m2/g, for example greater than 1250 m2/g, for example greater than 1500 m2/g, for example greater than 1750 m2/g, for example greater than 2000 m2/g, for example greater than 2500 m2/g, for example greater than 3000 m2/g. In other embodiments, the surface area of the porous carbon scaffold can be less than 500 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between 200 and 500 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between 100 and 200 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between and 100 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between 10 and 50 m2/g. In some embodiments, the surface area of the porous carbon scaffold can be less than 10 m2/g.


In some embodiments, the pore volume of the porous carbon scaffold is greater than 0.4 cm3/g, for example greater than 0.5 cm3/g, for example greater than 0.6 cm3/g, for example greater than 0.7 cm3/g, for example greater than 0.8 cm3/g, for example greater than 0.9 cm3/g, for example greater than 1.0 cm3/g, for example greater than 1.1 cm3/g, for example greater than 1.2 cm3/g, for example greater than 1.4 cm3/g, for example greater than 1.6 cm3/g, for example greater than 1.8 cm3/g, for example greater than 2.0 cm3/g. In other embodiments, the pore volume of the porous silicon scaffold is less than 0.5 cm3, for example between 0.1 cm3/g and 0.5 cm3/g. In certain other embodiments, the pore volume of the porous silicon scaffold is between cm3/g and 0.1 cm3/g.


In some other embodiments, the porous carbon scaffold is an amorphous activated carbon with a pore volume between 0.2 and 2.0 cm3/g. In certain embodiments, the carbon is an amorphous activated carbon with a pore volume between and 1.5 cm3/g. In certain embodiments, the carbon is an amorphous activated carbon with a pore volume between 0.5 and 1.2 cm3/g. In certain embodiments, the carbon is an amorphous activated carbon with a pore volume between 0.6 and 1.0 cm3/g.


In some other embodiments, the porous carbon scaffold comprises a tap density of less than 1.0 g/cm3, for example less than 0.8 g/cm3, for example less than 0.6 g/cm3, for example less than 0.5 g/cm3, for example less than 0.4 g/cm3, for example less than 0.3 g/cm3, for example less than 0.2 g/cm3, for example less than 0.1 g/cm3.


The surface functionality of the porous carbon scaffold can vary. One property which can be predictive of surface functionality is the pH of the porous carbon scaffold. The presently disclosed porous carbon scaffolds comprise pH values ranging from less than 1 to about 14, for example less than 5, from 5 to 8 or greater than 8. In some embodiments, the pH of the porous carbon is less than 4, less than 3, less than 2 or even less than 1. In other embodiments, the pH of the porous carbon is between about 5 and 6, between about 6 and 7, between about 7 and 8 or between 8 and 9 or between 9 and 10. In still other embodiments, the pH is high and the pH of the porous carbon ranges is greater than 8, greater than 9, greater than 10, greater than 11, greater than 12, or even greater than 13.


The pore volume distribution of the porous carbon scaffold can vary. For example, the % micropores can comprise less than 30%, for example less than 20%, for example less than 10%, for example less than 5%, for example less than 4%, for example less than 3%, for example less than 2%, for example less than 1%, for example less than 0.5%, for example less than 0.2%, for example, less than 0.1%. In certain embodiments, there is no detectable micropore volume in the porous carbon scaffold.


The mesopores comprising the porous carbon scaffold scaffold can vary. For example, the % mesopores can comprise less than 30%, for example less than 20%, for example less than 10%, for example less than 5%, for example less than 4%, for example less than 3%, for example less than 2%, for example less than 1%, for example less than 0.5%, for example less than 0.2%, for example, less than 0.1%. In certain embodiments, there is no detectable mesopore volume in the porous carbon scaffold.


In some embodiments, the pore volume distribution of the porous carbon scaffold scaffold comprises more than 50% macropores, for example more than 60% macropores, for example more than 70% macropores, for example more than 80% macropores, for example more than 90% macropores, for example more than 95% macropores, for example more than 98% macropores, for example more than 99% macropores, for example more than 99.5% macropores, for example more than 99.9% macropores.


In certain preferred embodiments, the pore volume of the porous carbon scaffold comprises a blend of micropores, mesopores, and macropores. Accordingly, in certain embodiments, the porous carbon scaffold comprises 0-20% micropores, 30-70% mesopores, and less than 10% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-20% micropores, 0-20% mesopores, and 70-95% macropores. In certain other embodiments, the porous carbon scaffold comprises 20-50% micropores, 50-80% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 40-60% micropores, 40-60% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 80-95% micropores, 0-10% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-10% micropores, mesopores, and 50-70% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-10% micropores, 70-80% mesopores, and 0-20% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-20% micropores, 70-95% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-10% micropores, 70-95% mesopores, and 0-20% macropores.


In certain embodiments, the % of pore volume in the porous carbon scaffold representing pores between 100 and 1000 A (10 and 100 nm) comprises greater than 30% of the total pore volume, for example greater than 40% of the total pore volume, for example greater than 50% of the total pore volume, for example greater than 60% of the total pore volume, for example greater than 70% of the total pore volume, for example greater than 80% of the total pore volume, for example greater than 90% of the total pore volume, for example greater than 95% of the total pore volume, for example greater than 98% of the total pore volume, for example greater than 99% of the total pore volume, for example greater than 99.5% of the total pore volume, for example greater than 99.9% of the total pore volume.


In certain embodiments, the pycnometry density of the porous carbon scaffold ranges from about 1 g/cc to about 3 g/cc, for example from about 1.5 g/cc to about 2.3 g/cc. In other embodiments, the skeletal density ranges from about 1.5 cc/g to about 1.6 cc/g, from about 1.6 cc/g to about 1.7 cc/g, from about 1.7 cc/g to about 1.8 cc/g, from about 1.8 cc/g to about 1.9 cc/g, from about 1.9 cc/g to about 2.0 cc/g, from about 2.0 cc/g to about 2.1 cc/g, from about 2.1 cc/g to about 2.2 cc/g or from about 2.2 cc/g to about 2.3 cc/g, from about 2.3 cc to about 2.4 cc/g, for example from about 2.4 cc/g to about 2.5 cc/g.


C. Silicon Production Via Chemical Vapor Infiltration (CVI)


Chemical vapor deposition (CVD) is a process wherein a substrate provides a solid surface comprising the first component of the composite, and the gas thermally decomposes on this solid surface to provide the second component of composite. Such a CVD approach can be employed, for instance, to create Si—C composite materials wherein the silicon is coating on the outside surface of silicon particles. Alternatively, chemical vapor infiltration (CVI) is a process wherein a substrate provides a porous scaffold comprising the first component of the composite, and the gas thermally decomposes on into the porosity (into the pores) of the porous scaffold material to provide the second component of composite.


In an embodiment, silicon is created within the pores of the porous carbon scaffold by subjecting the porous carbon particles to a silicon containing precursor gas at elevated temperature and the presence of a silicon-containing gas, preferably silane, in order to decompose said gas into silicon. In some embodiments, the silicon containing gas may comprise a higher-order silane (such as di-, tri-, and/or tetrasilane), chlorosilane(s) (such as mono-, di-, tri-, and tetrachlorosilane) or mixtures thereof.


The silicon containing precursor gas can be mixed with other inert gas(es), for example, nitrogen gas, or hydrogen gas, or argon gas, or helium gas, or combinations thereof. The temperature and time of processing can be varied, for example the temperature can be between 200 and 900 C, for example between 200 and 250 C, for example between 250 and 300 C, for example between 300 and 350 C, for example between 300 and 400 C, for example 300 and 500 C, for example between 350 and 450 C, for example between 350 and 400 C, for example 350 and 500 C, for example 350 to 550 C, for example between 400 and 500 C, for example between 500 and 600 C, for example between 600 and 700 C, for example between 700 and 800 C, for example between 800 and 900 C, for example between 600 and 1100 C.


The mixture of gas can comprise between 0.1 and 1% silane and remainder inert gas. Alternatively, the mixture of gas can comprise between 1% and 10% silane and remainder inert gas. Alternatively, the mixture of gas can comprise between 10% and 20% silane and remainder inert gas. Alternatively, the mixture of gas can comprise between 20% and 50% silane and remainder inert gas. Alternatively, the mixture of gas can comprise above 50% silane and remainder inert gas. Alternatively, the gas can essentially be 100% silane gas. Suitable inert gases include, but are not limited to, hydrogen, nitrogen, argon, and combinations thereof.


The pressure for the CVI process can be varied. In some embodiments, the pressure is atmospheric pressure. In some embodiments, the pressure is below atmospheric pressure. In some embodiments, the pressure is above atmospheric pressure.


C. Physico- and Electrochemical Properties of Silicon-Carbon Composite


While not wishing to be bound by theory, it is believed that the nano sized silicon achieved as a result of filling in certain, desired pore volume structure of the porous carbon scaffold (for instance, silicon filling pores in the range of 5 to 1000 nm, or other range as disclosed elsewhere herein), along with the advantageous properties of the other components of the composite, including low surface area, low pycnometry density, yield composite materials having different and advantageous properties, for instance electrochemical performance when the composite comprises an anode of a lithium ion energy storage device.


In certain embodiments, the embedded silicon particles embedded within the composite comprise nano-sized features. The nano-sized features can have a characteristic length scale of preferably less than 1 um, preferably less than 300 nm, preferably less than 150 nm, preferably less than 100 μm, preferably less than 50 nm, preferably less than 30 nm, preferably less than 15 nm, preferably less than 10 nm, preferably less than 5 nm.


In certain embodiments, the silicon embedded within the composite is spherical in shape. In certain other embodiments, the porous silicon particles are non-spherical, for example rod-like, or fibrous in structure. In some embodiments, the silicon exists as a layer coating the inside of pores within the porous carbon scaffold. The depth of this silicon layer can vary, for example the depth can between 5 nm and 10 nm, for example between 5 nm and 20 nm, for example between 5 nm and 30 nm, for example between 5 nm and 33 nm, for example between 10 nm and 30 nm, for example between 10 nm and 50 nm, for example between 10 nm and 100 nm, for example between 10 and 150 nm, for example between 50 nm and 150 nm, for example between 100 and 300 nm, for example between 300 and 1000 nm.


In some embodiments, the silicon embedded within the composite is nano sized, and resides within pores of the porous carbon scaffold. For example, the embedded silicon can be impregnated, deposited by CVI, or other appropriate process into pores within the porous carbon particle comprising pore sizes between 5 and 1000 nm, for example between 10 and 500 nm, for example between 10 and 200 nm, for example between 10 and 100 nm, for example between 33 and 150 nm, for example between and and 100 nm. Other ranges of carbon pores sizes with regards to fractional pore volume, whether micropores, mesopores, or macropores, are also envisioned.


In some embodiments, the carbon scaffold pore volume distribution can be described as the number or volume distribution of pores as determined as known in the art based on gas sorption analysis, for example nitrogen gas sorption analysis. In some embodiments the pore size distribution can be expressed in terms of the pore size at which a certain fraction of the total pore volume resides at or below. For example, the pore size at which 10% of the pores reside at or below can be expressed at DPv10.


The DPv10 for the porous carbon scaffold can vary, for example DPv10 can be between 0.01 nm and 100 nm, for example between 0.1 nm and 100 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 40 nm, for example between 1 nm and 30 nm, for example between 1 nm and 10 nm, for example between 1 nm and 5 nm.


The DPv50 for the porous carbon scaffold can vary, for example DPv50 can be between 0.01 nm and 100 nm, for example between 0.1 nm and 100 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 40 nm, for example between 1 nm and 30 nm, for example between 1 nm and 10 nm, for example between 1 nm and 5 nm. In other embodiments, the DPv50 is between 2 and 100, for example between 2 and 50, for example between 2 and 30, for example between 2 and 20, for example between 2 and 15, for example between 2 and 10.


The DPv90 for the porous carbon scaffold can vary, for example DPv90 can be between 0.01 nm and 100 nm, for example between 0.1 nm and 100 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 50 nm, for example between 1 nm and 40 nm, for example between 1 nm and 30 nm, for example between 1 nm and 10 nm, for example between 1 nm and nm. In other embodiments, the DPv50 is between 2 nm and 100 nm, for example between 2 nm and 50 nm, for example between 2 nm and 30 nm, for example between 2 nm and 20 nm, for example between 2 nm and 15 nm, for example between 2 nm and nm.


In some embodiments, the DPv90 is less than 100 nm, for example less than 50 nm, for example less than 40 nm, for example less than 30 nn, for example less than 20 nn, for example less than 15 nm, for example less than 10 nm. In some embodiments, the carbon scaffold comprises a pore volume with greater than 70% micropores (and DPv90 less than 100 nm, for example DPv90 less than 50 nm, for example DPv90 less than 40 nm, for example DPv90 less than 30 nm, for example DPv90 less than 20 nm, for example DPv90 less than 15 nm, for example DPv90 less than 10 nm, for example DPv90 less than 5 nm, for example DPv90 less than 4 nm, for example DPv90 less than 3 nm. In other embodiments, the carbon scaffold comprises a pore volume with greater than 80% micropores and DPv90 less than 100 nm, for example DPv90 less than 50 nm, for example DPv90 less than 40 nm, for example DPv90 less than 30 nm, for example DPv90 less than 20 nm, for example DPv90 less than 15 nm, for example DPv90 less than 10 nm, for example DPv90 less than 5 nm, for example DPv90 less than 4 nm, for example DPv90 less than 3 nm.


The DPv99 for the porous carbon scaffold can vary, for example DPv99 can be between 0.01 nm and 1000 nm, for example between 0.1 nm and 1000 nm, for example between 1 nm and 500 nm, for example between 1 nm and 200 nm, for example between 1 nm and 150 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 20 nm. In other embodiments, the DPv99 is between 2 nm and 500 nm, for example between 2 nm and 200 nm, for example between 2 nm and 150 nm, for example between 2 nm and 100 nm, for example between 2 nm and 50 nm, for example between 2 nm and 20 nm, for example between 2 nm and 15 nm, for example between 2 nm and 10 nm.


Embodiments of the composite with extremely durable intercalation of lithium disclosed herein improves the properties of any number of electrical energy storage devices, for example lithium ion batteries. In some embodiments, the silicon-carbon composite disclosed herein exhibits a Z less than 10, for example a Z less than 5, for example a Z less than 4, for example a Z less than 3, for example a Z less than 2, for example a Z less than 1, for example a Z less than 0.1, for example a Z less than 0.01, for example a Z less than 0.001. In certain embodiments, the Z is zero.


In certain preferred embodiment, the silicon-carbon composite comprises desirably low Z in combination with another desired physicochemical and/or electrochemical property or in combination with more than one other desired physicochemical and/or electrochemical properties. Table 1 provides a description of certain embodiments for combination of properties for the silicon-carbon composite.









TABLE 1







Embodiments for silicon-carbon composite with embodied properties.









In some embodiments the silicon-carbon composite



comprises . . .





Z
<10, <5, <4, <3, <2, <1, <0.1, <0.01, <0.01, 0


Surface Area
<100 m2/g, <50 m2/g, <30 m2/g, <20 m2/g, <10 m2/g, <5



m2/g, <4 m2/g, <3 m2/g, <2 m2/g, <1 m2/g;


First Cycle
>75%, >80%, >85%, >90%, >91%, >92%, >93%, >94%,



>95%,


Efficiency
>96%, >97%, >98%, >99%;


Reversible
>1300 mAh/g, >1600 mAh/g, >1700 mAh/g, >1800 mAh/g,


Capacity
>1900 mAh/g, >2000 mAh/g, >2100 mAh/g, >2200 mAh/g,



>2300 mAh/g, >2400 mAh/g, >2500 mAh/g, >2600 mAh/g,



>2700 mAh/g, >2800 mAh/g, >2900 mAh/g, >3000 mAh/g;



and/or


Silicon
10%-90%, 15-85%, 20%-80%, 30%-70%, 40%-60%.


Content



by weight









According to Table 1, the silicon-carbon composite may comprise combinations of various properties. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 100 m2/g, a first cycle efficiency greater than 80%, and a reversible capacity of at least 1300 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 100 m2/g, a first cycle efficiency greater than 80%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than surface area less than 20 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1800 mAh/g.


The silicon-carbon composite can comprise a combination of the aforementioned properties, in addition to also comprising a carbon scaffold comprising properties also described within this proposal. Accordingly, Table 2 provides a description of certain embodiments for combination of properties for the silicon-carbon composite.









TABLE 2







Embodiments for silicon-carbon composite with embodied properties.









In some embodiments the silicon-carbon composite



comprises . . .





Z
<10, <5, <4, <3, <2, <1, <0.1, <0.01, <0.01, 0


Surface Area
<100 m2/g, <50 m2/g, <30 m2/g, <20 m2/g, <10 m2/g, <5



m2/g, <4 m2/g, <3 m2/g, <2 m2/g, <1 m2/g;


First Cycle
>75%, >80%, >85%, >90%, >91%, >92%, >93%, >94%,


Efficiency
>95%, >96%, >97%, >98%, >99%;


Reversible
>1300 mAh/g, >1600 mAh/g, >1700 mAh/g, >1800 mAh/g,


Capacity
>1900 mAh/g, >2000 mAh/g, >2100 mAh/g, >2200 mAh/g,



>2300 mAh/g, >2400 mAh/g, >2500 mAh/g, >2600 mAh/g,



>2700 mAh/g, >2800 mAh/g, >2900 mAh/g, >3000 mAh/g;


Silicon
10%-90%, 15-85%, 20%-80%, 30%-70%, 40%-60%;


Content



by weight



Carbon
0.1-1.5 cm3/g, 0.2-1.2 cm3/g, 0.3-1.1 cm3/g, 0.4-1.0 cm3/g,


Scaffold
0.4-1.0 cm3/g, 0.5-1.0 cm3/g, 0.6-1.0 cm3/g, 0.5-0.9 cm3/g,


pore
0.4-1.0 cm3/g, >0.1 cm3/g, >0.2 cm3/g, >0.4 cm3/g, >0.6


volume
cm3/g, >0.8 cm3/g;


% silicon
15%-25%, 25%-35%, 20%-40%, 25%-50%, 30%-70%,


content
30%-60%, 60%-80%, 80%-100%;


Scaffold pore
<1 nm, 1-5 nm, 5-1000 nm, 10-500 nm, 10-200 nm, 10-100


size range
nm, 33-150 nm, 20-100 nm; and/or


Percentage of
>20%/>30%/>30%, <10/>30/>30, <5/>30/>30, <5/>40/


micro-
>40,<1/>40/>40, <10/>70/>20, <10/>20/>70, >10/>10/>80,


porosity/
<10/>80/>10, <5/>70/>20, <5/>20/>70, <5/>5/>80, <5/


meso-
>80/>10,>80%/<20%/<20%, >70/<30/<10, >70/<30/<5,


porosity/
>70/<20/<10, >70/<10/<10, >70/<10/<5, >70/<5/<5,


macro-
>80/<20/<10, >80/<20/<5, >80/<20/<1, >80/<10/<10,


porosity
>80/<10/<5, >80/<10/<1, >90/<10/<10, >90/<10/<5,


expressed as
>90/<10/<1,


percentage of
>90/<5/<1, >95/<5/<5, >90/<5/<1


total pore



volume









As used in herein, the percentage “microporosity,” “mesoporosity” and “macroporosity” refers to the percent of micropores, mesopores and macropores, respectively, as a percent of total pore volume. For example, a carbon scaffold having 90% microporosity is a carbon scaffold where 90% of the total pore volume of the carbon scaffold is formed by micropores.


According to Table 2, the silicon-carbon composite may comprise combinations of various properties. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 100 m2/g, a first cycle efficiency greater than 80%, a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises >80% micropores, <20% mesopores, and <10% macropores. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 20 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises >80% micropores, <20% mesopores, and <10% macropores. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises >80% micropores, <20% mesopores, and <10% macropores. For example, the silicon-carbon composite may comprise a Z less than surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises >80% micropores, <20% mesopores, and <10% macropores. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1800 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of cm3/g wherein the scaffold pore volume comprises >80% micropores, <20% mesopores, and <10% macropores.


Without being bound by theory, the filling of silicon within the pores of the porous carbon traps porosity within the porous carbon scaffold particle, resulting in inaccessible volume, for example volume that is inaccessible to nitrogen gas. Accordingly, the silicon-carbon composite material may exhibit a pycnometry density of less than 2.1 g/cm3, for example less than 2.0 g/cm3, for example less than 1.9 g/cm3, for example less than 1.8 g/cm3, for example less than 1.7 g/cm3, for example less than 1.6 g/cm3, for example less than 1.4 g/cm3, for example less than 1.2 g/cm3, for example less than 1.0 g/cm3.


In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.7 g·cm3 and 2.1 g/cm3, for example between 1.7 g·cm3 and 1.8 g/cm3, between 1.8 g·cm3 and 1.9 g/cm3, for example between 1.9 g·cm3 and 2.0 g/cm3, for example between 2.0 g·cm3 and 2.1 g/cm3. In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.8 g·cm3 and 2.1 g/cm3. In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.8 g·cm3 and 2.0 g/cm3. In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.9 g·cm3 and 2.1 g/cm3.


The pore volume of the composite material exhibiting extremely durable intercalation of lithium can range between 0.01 cm3/g and 0.2 cm3/g. In certain embodiments, the pore volume of the composite material can range between 0.01 cm3/g and 0.15 cm3/g, for example between 0.01 cm3/g and 0.1 cm3/g, for example between cm3/g and 0.05 cm2/g.


The particle size distribution of the composite material exhibiting extremely durable intercalation of lithium is important to both determine power performance as well as volumetric capacity. As the packing improves, the volumetric capacity may increase. In one embodiment the distributions are either Gaussian with a single peak in shape, bimodal, or polymodal (>2 distinct peaks, for example trimodal). The properties of particle size of the composite can be described by the DO (smallest particle in the distribution), Dv50 (average particle size) and Dv100 (maximum size of the largest particle). The optimal combined of particle packing and performance will be some combination of the size ranges below. The particle size reduction in the such embodiments can be carried out as known in the art, for example by jet milling in the presence of various gases including air, nitrogen, argon, helium, supercritical steam, and other gases known in the art.


In one embodiment the Dv0 of the composite material can range from 1 nm to 5 microns. In another embodiment the Dv0 of the composite ranges from 5 nm to 1 micron, for example 5-500 nm, for example 5-100 nm, for example 10-50 nm. In another embodiment the Dv0 of the composite ranges from 500 nm to 2 microns, or 750 nm to 1 um, or 1-2 um. microns to 2 microns. In other embodiments, the Dv0 of the composite ranges from 2-5 um, or >5 um.


In some embodiments the Dv50 of the composite material ranges from 5 nm to um. In other embodiments the Dv50 of the composite ranges from 5 nm to 1 um, for example 5-500 nm, for example 5-100 nm, for example 10-50 nm. In another embodiment the Dv50 of the composite ranges from 500 nm to 2 um, 750 nm to 1 um, 1-2 um. In still another embodiments, the Dv50 of the composite ranges from 1 to 1000 um, for example from 1-100 um, for example from 1-10 um, for example 2-20 um, for example 3-15 um, for example 4-8 um. In certain embodiments, the Dv50 is >20 um, for example >50 um, for example >100 um.


The span (Dv50)/(Dv90-Dv10), wherein Dv10, Dv50 and Dv90 represent the particle size at 10%, 50%, and 90% of the volume distribution, can be varied from example from 100 to 10, from 10 to 5, from 5 to 2, from 2 to 1; in some embodiments the span can be less than 1. In certain embodiments, the composite comprising carbon and porous silicon material particle size distribution can be multimodal, for example, bimodal, or trimodal.


The surface functionality of the presently disclosed the composite material exhibiting extremely durable intercalation of lithium may be altered to obtain the desired electrochemical properties. One property which can be predictive of surface functionality is the pH of the composite materials. The presently disclosed composite materials comprise pH values ranging from less than 1 to about 14, for example less than 5, from 5 to 8 or greater than 8. In some embodiments, the pH of the composite materials is less than 4, less than 3, less than 2 or even less than 1. In other embodiments, the pH of the composite materials is between about 5 and 6, between about 6 and 7, between about 7 and 8 or between 8 and 9 or between 9 and 10. In still other embodiments, the pH is high and the pH of the composite materials ranges is greater than 8, greater than 9, greater than 10, greater than 11, greater than 12, or even greater than 13.


The silicon-carbon composite material may comprise varying amounts of carbon, oxygen, hydrogen and nitrogen as measured by gas chromatography CHNO analysis. In one embodiment, the carbon content of the composite is greater than 98 wt. % or even greater than 99.9 wt % as measured by CHNO analysis. In another embodiment, the carbon content of the silicon-carbon composite ranges from about 10-90%, for example 20-80%, for example 30-70%, for example 40-60%.


In some embodiments, silicon-carbon composite material comprises a nitrogen content ranging from 0-90%, example 0.1-1%, for example 1-3%, for example 1-5%, for example 1-10%, for example 10-20%, for example 20-30%, for example 30-90%.


In some embodiments, the oxygen content ranges from 0-90%, example 0.1-1%, for example 1-3%, for example 1-5%, for example 1-10%, for example 10-20%, for example 20-30%, for example 30-90%.


The silicon-carbon composite material may also incorporate an electrochemical modifier selected to optimize the electrochemical performance of the non-modified composite. The electrochemical modifier may be incorporated within the pore structure and/or on the surface of the porous carbon scaffold, within the embedded silicon, or within the final layer of carbon, or conductive polymer, coating, or incorporated in any number of other ways. For example, in some embodiments, the composite materials comprise a coating of the electrochemical modifier (e.g., silicon or Al2O3) on the surface of the carbon materials. In some embodiments, the composite materials comprise greater than about 100 ppm of an electrochemical modifier. In certain embodiments, the electrochemical modifier is selected from iron, tin, silicon, nickel, aluminum and manganese.


In certain embodiments the electrochemical modifier comprises an element with the ability to lithiate from 3 to 0 V versus lithium metal (e.g. silicon, tin, sulfur). In other embodiments, the electrochemical modifier comprises metal oxides with the ability to lithiate from 3 to 0 V versus lithium metal (e.g. iron oxide, molybdenum oxide, titanium oxide). In still other embodiments, the electrochemical modifier comprises elements which do not lithiate from 3 to 0 V versus lithium metal (e.g. aluminum, manganese, nickel, metal-phosphates). In yet other embodiments, the electrochemical modifier comprises a non-metal element (e.g. fluorine, nitrogen, hydrogen). In still other embodiments, the electrochemical modifier comprises any of the foregoing electrochemical modifiers or any combination thereof (e.g. tin-silicon, nickel-titanium oxide).


The electrochemical modifier may be provided in any number of forms. For example, in some embodiments the electrochemical modifier comprises a salt. In other embodiments, the electrochemical modifier comprises one or more elements in elemental form, for example elemental iron, tin, silicon, nickel or manganese. In other embodiments, the electrochemical modifier comprises one or more elements in oxidized form, for example iron oxides, tin oxides, silicon oxides, nickel oxides, aluminum oxides or manganese oxides.


The electrochemical properties of the composite material can be modified, at least in part, by the amount of the electrochemical modifier in the material, wherein the electrochemical modifier is an alloying material such as silicon, tin, indium, aluminum, germanium, gallium. Accordingly, in some embodiments, the composite material comprises at least 0.10%, at least 0.25%, at least 0.50%, at least 1.0%, at least 5.0%, at least 10%, at least 25%, at least 50%, at least 75%, at least 90%, at least 95%, at least 99% or at least 99.5% of the electrochemical modifier.


The particle size of the composite material may expand upon lithiation as compared to the non-lithiated state. For example, the expansion factor, defined as ratio of the average particle size of particles of composite material comprising a porous silicon material upon lithiation divided by the average particle size under non-lithiated conditions. As described in the art, this expansion factor can be relatively large for previously known, non-optimal silicon-containing materials, for example about 4× (corresponding to a 400% volume expansion upon lithiation). The current inventors have discovered composite materials comprising a porous silicon material that can exhibit a lower extent of expansion, for example, the expansion factor can vary from 3.5 to 4, from 3.0 to 3.5, from 2.5 to 3.0, from 2.0 to 2.5, from 1.5 to 2.0, from 1.0 to 1.5.


It is envisioned that composite materials in certain embodiments will comprise a fraction of trapped pore volume, namely, void volume non-accessible to nitrogen gas as probed by nitrogen gas sorption measurement. Without being bound by theory, this trapped pore volume is important in that it provides volume into which silicon can expand upon lithiation.


In certain embodiments, the ratio of trapped void volume to the silicon volume comprising the composite particle is between 0.1:1 and 10:1. For example, the ratio of trapped void volume to the silicon volume comprising the composite particle is between 1:1 and 5:1, or 5:1 to 10:1. In embodiments, the ratio of ratio trapped void volume to the silicon volume comprising the composite particle is between 2:1 and 5:1, or about 3:1, in order to efficiently accommodate the maximum extent of expansion of silicon upon lithiation.


In certain embodiments, the electrochemical performance of the composite disclosed herein is tested in a half-cell; alternatively the performance of the composite with extremely durable intercalation of lithium disclosed herein is tested in a full cell, for example a full cell coin cell, a full cell pouch cell, a prismatic cell, or other battery configurations known in the art. The anode composition comprising the composite with extremely durable intercalation of lithium disclosed herein can further comprise various species, as known in the art. Additional formulation components include, but are not limited to, conductive additives, such as conductive carbons such as Super C45, Super P, Ketjenblack carbons, and the like, conductive polymers and the like, binders such as styrene-butadiene rubber sodium carboxymethylcellulose (SBR-Na-CMC), polyvinylidene difluoride (PVDF), polyimide (PI), polyacrylic acid (PAA) and the like, and combinations thereof. In certain embodiments, the binder can comprise a lithium ion as counter ion.


Other species comprising the electrode are known in the art. The % of active material in the electrode by weight can vary, for example between 1 and 5%, for example between 5 and 15%, for example between 15 and 25%, for example between and 35%, for example between 35 and 45%, for example between 45 and 55%, for example between 55 and 65%, for example between 65 and 75%, for example between and 85%, for example between 85 and 95%. In some embodiments, the active material comprises between 80 and 95% of the electrode. In certain embodiment, the amount of conductive additive in the electrode can vary, for example between 1 and 5%, between 5 and 15%, for example between 15 and 25%, for example between 25 and 35%. In some embodiments, the amount of conductive additive in the electrode is between 5 and 25%. In certain embodiments, the amount of binder can vary, for example between 1 and 5%, between 5 and 15%, for example between 15 and 25%, for example between 25 and 35%. In certain embodiments, the amount of conductive additive in the electrode is between 5 and 25%.


The silicon-carbon composite material may be prelithiated, as known in the art. In certain embodiments, the prelithiation is achieved electrochemically, for example in a half cell, prior to assembling the lithiated anode comprising the porous silicon material into a full cell lithium ion battery. In certain embodiments, prelithiation is accomplished by doping the cathode with a lithium-containing compound, for example a lithium containing salt. Examples of suitable lithium salts in this context include, but are not limited to, dilithium tetrabromonickelate (II), dilithium tetrachlorocuprate (II), lithium azide, lithium benzoate, lithium bromide, lithium carbonate, lithium chloride, lithium cyclohexanebutyrate, lithium fluoride, lithium formate, lithium hexafluoroarsenate (V), lithium hexafluorophosphate, lithium hydroxide, lithium iodate, lithium iodide, lithium metaborate, lithium perchlorate, lithium phosphate, lithium sulfate, lithium tetraborate, lithium tetrachloroaluminate, lithium tetrafluoroborate, lithium thiocyanate, lithium trifluoromethanesulfonate, lithium trifluoromethanesulfonate, and combinations thereof.


The anode comprising the silicon-carbon composite material can be paired with various cathode materials to result in a full cell lithium ion battery. Examples of suitable cathode materials are known in the art. Examples of such cathode materials include, but are not limited to LiCoO2 (LCO), LiNi0.8Co0.15Al0.05O2 (NCA), LiNi1/3Co1/3Mn1/3O2 (NMC), LiMn2O4 and variants (LMO), and LiFePO4 (LFP).


For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, pairing of cathode to anode can be varied. For example, the ratio of cathode-to-anode capacity can vary from 0.7 to 1.3. In certain embodiments, the ratio of cathode-to-anode capacity can vary from 0.7 to 1.0, for example from 0.8 to 1.0, for example from 0.85 to 1.0, for example from 0.9 to 1.0, for example from 0.95 to 1.0. In other embodiments, the ratio of cathode-to-anode capacity can vary from 1.0 to 1.3, for example from 1.0 to 1.2, for example from 1.0 to 1.15, for example from 1.0 to 1.1, for example from 1.0 to 1.05. In yet other embodiments, the ratio of cathode-to-anode capacity can vary from 0.8 to 1.2, for example from 0.9 to 1.1, for example from 0.95 to 1.05.


For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, the voltage window for charging and discharging can be varied. In this regard, the voltage window can be varied as known in the art, depending on various properties of the lithium ion battery. For instance, the choice of cathode plays a role in the voltage window chosen, as known in the art. Examples of voltage windows vary, for example, in terms of potential versus Li/Li+, from 2.0 V to 5.0 V, for example from 2.5 V to 4.5V, for example from 2.5V to 4.2V.


For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, the strategy for conditioning the cell can be varied as known in the art. For example, the conditioning can be accomplished by one or more charge and discharge cycles at various rate(s), for example at rates slower than the desired cycling rate. As known in the art, the conditioning process may also include a step to unseal the lithium ion battery, evacuate any gases generated within during the conditioning process, followed by resealing the lithium ion battery.


For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, the cycling rate can be varied as known in the art, for example, the rate can between C/20 and 20C, for example between C10 to 10C, for example between C/5 and 5C. In certain embodiments, the cycling rate is C/10. In certain embodiments, the cycling rate is C/5. In certain embodiments, the cycling rate is C/2. In certain embodiments, the cycling rate is 1C. In certain embodiments, the cycling rate is 1C, with periodic reductions in the rate to a slower rate, for example cycling at 1C with a C/10 rate employed every 20th cycle. In certain embodiments, the cycling rate is 2C. In certain embodiments, the cycling rate is 4C. In certain embodiments, the cycling rate is 5C. In certain embodiments, the cycling rate is 10C. In certain embodiments, the cycling rate is 20C.


The first cycle efficiency of the composite with extremely durable intercalation of lithium disclosed herein be determined by comparing the lithium inserted into the anode during the first cycle to the lithium extracted from the anode on the first cycle, prior prelithiation modification. When the insertion and extraction are equal, the efficiency is 100%. As known in the art, the anode material can be tested in a half-cell, where the counter electrode is lithium metal, the electrolyte is a 1M LiPF6 1:1 ethylene carbonate:diethylcarbonate (EC:DEC), using a commercial polypropylene separator. In certain embodiments, the electrolyte can comprise various additives known to provide improved performance, such as fluoroethylene carbonate (FEC) or other related fluorinated carbonate compounds, or ester co-solvents such as methyl butyrate, vinylene carbonate, and other electrolyte additives known to improve electrochemical performance of silicon-comprising anode materials.


Coulombic efficiency can be averaged, for example averaged over cycles 7 to cycle 25 when tested in a half cell. Coulombic efficiency can be averaged, for example averaged over cycles 7 to cycle 20 when tested in a half cell. In certain embodiments, the average efficiency of the composite with extremely durable intercalation of lithium is greater than 0.9, or 90%. In certain embodiments, the average efficiency is greater than 0.95, or 95%. In certain other embodiments, the average efficiency is 0.99 or greater, for example 0.991 or greater, for example 0.992 or greater, for example 0.993 or greater, for example 0.994 or greater, for example 0.995 or greater, for example or greater, for example 0.997 or greater, for example 0.998 or greater, for example 0.999 or greater, for example 0.9991 or greater, for example 0.9992 or greater, for example 0.9993 or greater, for example 0.9994 or greater, for example 0.9995 or greater, for example 0.9996 or greater, for example 0.9997 or greater, for example or greater, for example 0.9999 or greater.


In still other embodiments the present disclosure provides a composite material exhibiting extremely durable intercalation of lithium, wherein when the composite material is incorporated into an electrode of a lithium-based energy storage device the composite material has a volumetric capacity at least 10% greater than when the lithium based energy storage device comprises a graphite electrode. In some embodiments, the lithium based energy storage device is a lithium ion battery. In other embodiments, the composite material has a volumetric capacity in a lithium-based energy storage device that is at least 5% greater, at least 10% greater, at least 15% greater than the volumetric capacity of the same electrical energy storage device having a graphite electrode. In still other embodiments, the composite material has a volumetric capacity in a lithium based energy storage device that is at least 20% greater, at least 30% greater, at least 40% greater, at least 50% greater, at least 200% greater, at least 100% greater, at least 150% greater, or at least 200% greater than the volumetric capacity of the same electrical energy storage device having a graphite electrode.


The composite material may be prelithiated, as known in the art. These lithium atoms may or may not be able to be separated from the carbon. The number of lithium atoms to 6 carbon atoms can be calculated by techniques known to those familiar with the art:

#Li=Q×3.6×MM/(C %×F)


wherein Q is the lithium extraction capacity measured in mAh/g between the voltages of 5 mV and 2.0V versus lithium metal, MM is 72 or the molecular mass of 6 carbons, F is Faraday's constant of 96500, C % is the mass percent carbon present in the structure as measured by CHNO or XPS.


The composite material can be characterized by the ratio of lithium atoms to carbon atoms (Li:C) which may vary between about 0:6 and 2:6. In some embodiments the Li:C ratio is between about 0.05:6 and about 1.9:6. In other embodiments the maximum Li:C ratio wherein the lithium is in ionic and not metallic form is 2.2:6. In certain other embodiments, the Li:C ratio ranges from about 1.2:6 to about 2:6, from about 1.3:6 to about 1.9:6, from about 1.4:6 to about 1.9:6, from about 1.6:6 to about 1.8:6 or from about 1.7:6 to about 1.8:6. In other embodiments, the Li:C ratio is greater than 1:6, greater than 1.2:6, greater than 1.4:6, greater than 1.6:6 or even greater than 1.8:6. In even other embodiments, the Li:C ratio is about 1.4:6, about 1.5:6, about 1.6:6, about 1.6:6, about 1.7:6, about 1.8:6 or about 2:6. In a specific embodiment the Li:C ratio is about 1.78:6.


In certain other embodiments, the composite material comprises an Li:C ratio ranging from about 1:6 to about 2.5:6, from about 1.4:6 to about 2.2:6 or from about 1.4:6 to about 2:6. In still other embodiments, the composite materials may not necessarily include lithium, but instead have a lithium uptake capacity (i.e., the capability to uptake a certain quantity of lithium, for example upon cycling the material between two voltage conditions (in the case of a lithium ion half cell, an exemplary voltage window lies between 0 and 3 V, for example between 0.005 and 2.7 V, for example between 0.005 and 1 V, for example between 0.005 and 0.8 V). While not wishing to be bound by theory, it is believed the lithium uptake capacity of the composite materials contributes to their superior performance in lithium based energy storage devices. The lithium uptake capacity is expressed as a ratio of the atoms of lithium taken up by the composite. In certain other embodiments, the composite material exhibiting extremely durable intercalation of lithium comprise a lithium uptake capacity ranging from about 1:6 to about 2.5:6, from about 1.4:6 to about 2.2:6 or from about 1.4:6 to about 2:6.


In certain other embodiments, the lithium uptake capacity ranges from about 1.2:6 to about 2:6, from about 1.3:6 to about 1.9:6, from about 1.4:6 to about 1.9:6, from about 1.6:6 to about 1.8:6 or from about 1.7:6 to about 1.8:6. In other embodiments, the lithium uptake capacity is greater than 1:6, greater than 1.2:6, greater than 1.4:6, greater than 1.6:6 or even greater than 1.8:6. In even other embodiments, the Li:C ratio is about 1.4:6, about 1.5:6, about 1.6:6, about 1.6:6, about 1.7:6, about 1.8:6 or about 2:6. In a specific embodiment the Li:C ratio is about 1.78:6.


EXAMPLES

Example 1. Production of silicon-carbon composite material by CVI. The properties of the carbon scaffold (Carbon Scaffold 1) employed for producing the silicon-carbon composite is presented in Table 3. Employing Carbon Scaffold 1, the silicon-carbon composite (Silicon-Carbon Composite 1) was produced by CVI as follows. A mass of 0.2 grams of amorphous porous carbon was placed into a 2 in.×2 in. ceramic crucible then positioned in the center of a horizontal tube furnace. The furnace was sealed and continuously purged with nitrogen gas at 500 cubic centimeters per minute (ccm). The furnace temperature was increased at 20° C./min to 450° C. peak temperature where it was allowed to equilibrate for 30 minutes. At this point, the nitrogen gas is shutoff and then silane and hydrogen gas are introduced at flow rates of 50 ccm and 450 ccm, respectively for a total dwell time of 30 minutes. After the dwell period, silane and hydrogen were shutoff and nitrogen was again introduced to the furnace to purge the internal atmosphere. Simultaneously the furnace heat is shutoff and allowed to cool to ambient temperature. The completed Si—C material is subsequently removed from the furnace.









TABLE 3







Description of carbon scaffold employed for Example 1.












Carbon
Surface
Pore
%
%
%


Scaffold
Area
Volume
Micro-
Meso-
Macro-


#
(m2/g)
(cm3/g)
pores
pores
pores





1
1710
0.762
93.1
6.8
0.1









Example 2. Analysis of various silicon-composite materials. A variety of carbon scaffold materials were employed, and the carbon scaffold materials were characterized by nitrogen sorption gas analysis to determine specific surface area, total pore volume, and fraction of pore volume comprising micropores, mesopores, and macropores. The characterization data for the carbon scaffold materials is presented in Table 4, namely the data for carbon scaffold surface area, pore volume, and pore volume distribution (% micropores, % mesopores, and % macropores), all as determined by nitrogen sorption analysis.









TABLE 4







Properites of various carbon scaffold materials.












Carbon
Surface
Pore
%
%
%


Scaffold
Area
Volume
Micro-
Meso-
Macro-


#
(m2/g)
(cm3/g)
pores
pores
pores















1
1710
0.762
93.1
6.8
0.1


2
1744
0.72
97.2
2.7
0.1


3
1581
0.832
69.1
30.9
0.1


4
1710
0.817
80.1
19.9
0


5
1835
0.9
82.2
17.8
0


6
1475
1.06
52.4
47.6
0


7
453
0.5
3.9
91.1
5.1


8
787
2.284
0
59.1
40.9


9
1713
0.76
91
9
0


10
1690
0.741
92.6
7.3
0.1


11
1918
0.858
89.9
10.1
0









The carbons scaffold sample as described in Table 4 were employed to produce a variety of silicon-carbon composite materials employing the CVI methodology in a static bed configuration as generally described in Example 1. These silicon-carbon samples were produced employing a range of process conditions: silane concentration 1.25% to 100%, diluent gas nitrogen or hydrogen, carbon scaffold starting mass 0.2 g to 700 g.


The surface area for the silicon-carbon composites was determined. The silicon-carbon composites were also analyzed by TGA to determine silicon content and the Z. Silicon-carbon composite materials were also tested in half-cell coin cells. The anode for the half-cell coin cell can comprise 60-90% silicon-carbon composite, 5-20% Na-CMC (as binder) and 5-20% Super C45 (as conductivity enhancer), and the electrolyte can comprise 2:1 ethylene carbonate:diethylene carbonate, 1 M LiPF6 and 10% fluoroethylene carbonate. The half-cell coin cells can be cycled at 25° C. at a rate of C/5 for 5 cycles and then cycled thereafter at C/10 rate. The voltage can be cycled between 0 V and 0.8 V, alternatively, the voltage can be cycled between 0 V and 1.5 V. From the half-cell coin cell data, the maximum capacity can be measured, as well as the average Coulombic efficiency (CE) over the range of cycles from cycle 7 to cycle 20. Physicochemical and electrochemical properties for various silicon-carbon composite materials are presented in Table 5.









TABLE 5







Properites of various silicon-carbon materials.













Silicon-








Carbon
Carbon
Surface
Si

Max
Average


Composite
Scaffold
Area
content

Capacity
CE


#
#
(m2/g)
(%)
Z
(mAh/g)
(7-20)
















 1
 1
7
45.0
 0.2
1433
0.9981


 2
 1
7
45.4
 0.6
1545
0.9980


 3
 1
6
45.8
 0.6
1510
0.9975


 4
 2
3.06
50.1
 1.0
1665
0.9969


 5
 2
1.96
51.3
 2.0
1662
0.9974


 6
 3
140
43.1
 3.2
 832
0.9941


 7
 2
1.61
48.7
 2.8
1574
0.9977


 8
 2
2
48.5
 3.0
1543
0.9972


 9
 1
8
46.3
 0.2
1373
0.9976


10
 4
44
51.2
 6.2
1614
0.9975


11
 5
94
48.9
 6.2
1455
0.9969


12
 6
61
52.1
10.6
2011
0.9869


13
 7
68.5
34.6
17.2
1006
0.9909


14
 8
20
74
33.5
2463
0.9717


15
 8
149
57.7
34.5
1892
0.9766


16
 8
61.7
68.9
38.7
2213
0.9757


17
 9
11
46.1
 0.8
1675
0.9990


18
 9
11
46.7
 2.0
1739
0.9985


19
 9
15.1
46.8
 1.7
1503
0.9980


20
 9
4.1
47.9
 4.2
1790
0.9953


21
 9
5
48.1
 4.6
1861
0.9962


22
10
5.1
44.5
 0
ND
ND


23
10
8.4
43.6
 0
ND
ND


24
11
13.6
45.0
 0.92
1848
Pending





ND = not determined






A plot of the average Coulombic efficiency as a function of the Z is presented in FIG. 1. As can seen there was dramatic increase in the average Coulombic efficiency for silicon-carbon samples with low Z. In particular, all silicon-carbon samples with Z below 10.0 exhibited average Coulombic efficiency ≥0.9941, and all silicon-carbon samples with Z above 10 (Silicon-Carbon Composite Sample 12 through Silicon-Carbon Composite Sample 16) were observed to have average Coulombic efficiency ≤0.9909. Without being bound by theory, higher Coulombic efficiency for the silicon-carbon samples with Z<10 provides for superior cycling stability in full cell lithium ion batteries. Further inspection of Table reveals the surprising and unexpected finding that the combination of silicon-carbon composite samples with Z<10 and also comprising carbon scaffold comprising >69.1 microporosity provides for average Coulombic efficiency ≥0.9969.


Therefore, in a preferred embodiment, the silicon-carbon composite material comprises a Z less than 10, for example less Z less than 5, for example less Z less than 3, for example less Z less than 2, for example less Z less than 1, for example less Z less than 0.5, for example less Z less than 0.1, or Z of zero.


In certain preferred embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >70% microporosity, for example Z less than 10 and >80% microporosity, for example Z less than 10 and >90% microporosity, for example Z less than 10 and >95% microporosity, for example Z less than 5 and >70% microporosity, for example Z less than 5 and >80% microporosity, for example Z less than 5 and >90% microporosity, for example Z less than 5 and >95% microporosity, for example Z less than 3 and >70% microporosity, for example Z less than 3 and >80% microporosity, for example Z less than 3 and >90% microporosity, for example Z less than 3 and >95% microporosity, for example Z less than 2 and >70% microporosity, for example Z less than 2 and >80% microporosity, for example Z less than 2 and >90% microporosity, for example Z less than 2 and >95% microporosity, for example Z less than 1 and >70% microporosity, for example Z less than 1 and >80% microporosity, for example Z less than 1 and >90% microporosity, for example Z less than 1 and >95% microporosity, for example Z less than 0.5 and >70% microporosity, for example Z less than 0.5 and >80% microporosity, for example Z less than 0.5 and >90% microporosity, for example Z less than 0.5 and >95% microporosity, for example Z less than 0.1 and >70% microporosity, for example Z less than 0.1 and >80% microporosity, for example Z less than 0.1 and >90% microporosity, for example Z less than 0.1 and >95% microporosity, for example Z of zero and >70% microporosity, for example Z of zero and >80% microporosity, for example Z of zero and >90% microporosity, for example Z of zero and >95% microporosity.


In certain preferred embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 100 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 30 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 30 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 30 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g.


In certain preferred embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g.


Example 3. dV/dQ for various silicon-composite materials. Differential capacity curve (dQ/dV vs Voltage) is often used as a non-destructive tool to understand the phase transition as a function of voltage in lithium battery electrodes (M. N. Obrovac et al. Structural Changes in Silicon Anodes during Lithium Insertion/Extraction, Electrochemical and Solid-State Letters, 7 (5) A93-A96 (2004); Ogata, K. et al. Revealing lithium-silicide phase transformations in nano-structured silicon-based lithium ion batteries via in situ NMR spectroscopy. Nat. Commun. 5:3217). Differential capacity plots presented here is calculated from the data obtained using galvanostatic cycling at 0.1C rate between 5 mV to 0.8V in a half-cell coin cell at 25° C. Typical differential capacity curve for a silicon-based material in a half-cell vs lithium can be found in many literature references (Loveridge, M. J. et al. Towards High Capacity Li-Ion Batteries Based on Silicon-Graphene Composite Anodes and Sub-micron V-doped LiFePO4 Cathodes. Sci. Rep. 6, 37787; doi: 10.1038/srep37787 (2016); M. N. Obrovac et al. Li15Si4Formation in Silicon Thin Film Negative Electrodes, Journal of The Electrochemical Society, 163 (2) A255-A261 (2016); Q. Pan et al. Improved electrochemical performance of micro-sized SiO-based composite anode by prelithiation of stabilized lithium metal powder, Journal of Power Sources 347 (2017) 170-177). First cycle lithiation behavior is dependent on the crystallinity of the silicon and oxygen content among other factors.


After first cycle, previous amorphous silicon materials in the art exhibit two specific phase transition peaks in the dQ/dV vs V plot for lithiation, and correspondingly two specific phase transition peaks in the dQ/dV vs V plot for dilithiation. For lithiation, one peak corresponding to lithium-poor Li—Si alloy phase occurs between 0.2-0.4 V and another peak corresponding to a lithium-rich Li—Si alloy phase occurs below 0.15 V. For dilithiation, one dilithiation peak corresponding to the extraction of lithium occurs below 0.4 V and another peak occurs between 0.4 V and V. If the Li15Si4 phase is formed during lithiation, it is delithiated at ˜0.45V and appears as a very narrow sharp peak.



FIG. 2 depicts the dQ/dV vs Voltage curve for cycle 2 for the silicon-carbon composite material corresponding to Silicon-Carbon Composite 3 from Example 1. Silicon-Carbon Composite 3 comprises a Z of 0.6. For ease of identification, the plot is divided into regimes I, II, II, IV, V, and VI. Regimes I (0.8 V to 0.4 V), II (0.4 V to V), III (0.15 V to 0 V) comprise the lithiation potentials and Regimes IV (0 V to V), V (0.4 V to 0.55 V), VI (0.55 V to 0.8 V) comprise the dilithiation potential. As described above, previous amorphous silicon-based materials in the art exhibit phase-transition peaks for two regimes (Regime II and Regime III) in the lithiation potential and two regimes (Regime IV and Regime V) in the dethiation potentials.


As can be seen in FIG. 2, the dQ/dV vs Voltage curve reveals surprising and unexpected result that Silicon-Carbon Composite 3, which comprises a Z of 0.6, comprises two additional peaks in the dQ/dV vs Voltage curve, namely Regime I in the lithiation potential and Regime VI in the delithiation potential. All 6 peaks are reversible and observed in the subsequent cycles as well, as shown in FIG. 3.


Without being bound by theory, such trimodal behavior for the dQ/dV vs V curve is novel, and likewise reflects a novel form of silicon.


Notably, the novel peaks observed in Regime I and Regime VI are more pronounced in certain scaffold matrixes and completely absent in others samples illustrating the prior art (silicon-carbon composite samples with Z>10, see explanation and table below).



FIG. 4 presents the dQ/dV vs V curve for Silicon-Carbon Composite 3, wherein the novel peaks in Regime I and Regime VI are evident, in comparison to Silicon-Carbon Composite 15, Silicon-Carbon Composite 16, and Silicon-Carbon Composite 14, all three of which comprise Z>10 and whose dQ/dV vs V curves are devoid of the any peaks in Regime I and Regime VI.


Without being bound by theory, these novel peaks observed in Regime I and Regime VI relate to the properties of the silicon impregnated into the porous carbon scaffold, i.e., related to the interactions between and among the properties of the porous carbon scaffold, the silicon impregnated into the porous carbon scaffold via CVI, and lithium. In order to provide a quantitative analysis, we herein define the parameter gyp, which is calculated as the normalized peak I with respect to peak III as:

φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III)

where dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V; the half-cell coin cell is produced as known in the art. If the Si—C sample shows peaks associated with graphite in regime III of the differential curve, it is omitted in favor of Li—Si related phase transition peaks for the calculation of D factor. For this example, the half-cell coin cell comprises an anode comprising 60-90% silicon-carbon composite, 5-20% SBR-Na-CMC, and 5-20% Super C45. An example for φ calculation is shown in FIG. 5 for Silicon-Carbon Composite 3. In this instance, the maximum peak height in the regime I is −2.39 and is found at voltage 0.53V. Similarly, maximum peak height in regime III is −9.71 at 0.04V. In this instance, φ can be calculated using the above formula, yielding φ=−2.39/−9.71=0.25. The value of φ was determined from the half-cell coin cell data for the various silicon-carbon composites presented in Example 2. These data are summarized in Table 6.









TABLE 6







Properites of various silicon-carbon materials.













Silicon-








Carbon
Surface
Si

Average

First


Composite
Area
content

CE

Cycle


#
(m2/g)
(%)
Z
(7-20)
φ
Efficiency
















 1
7
45.0
 0.2
0.9981
0.24
76.3


 2
7
45.4
 0.6
0.9980
0.24
76.8


 3
6
45.8
 0.6
0.9975
0.25
75.5


 4
3.06
50.1
 1.0
0.9969
0.18
80.9


 5
1.96
51.3
 2.0
0.9974
0.18
80.3


 6
140
43.1
 3.2
0.9941
0.13
52.3


 7
1.61
48.7
 2.8
0.9977
0.19
79.2


 8
2
48.5
 3.0
0.9972
0.19
78.3


 9
8
46.3
 0.2
0.9976
0.20
73.3


10
44
51.2
 6.2
0.9975
0.13
78.1


11
94
48.9
 6.2
0.9969
0.15
72.7


12
61
52.1
10.6
0.9869
0
80.2


13
68.5
34.6
17.2
0.9909
0
64


14
20
74
33.5
0.9717
0
85


15
149
57.7
34.5
0.9766
0
69


16
61.7
68.9
38.7
0.9757
0
79.3


17
11
46.1
 0.8
0.9990
0.35
82.2


18
11
46.7
 2.0
0.9985
0.34
82.5








(92.1*)


19
15.1
46.8
 1.7
0.9980
0.34
79.9








(90.3*)


20
4.1
47.9
 4.2
0.9953
0.34
83.3








(92.6*)


21
5
48.1
 4.6
0.9962
0.32
82.9








(92.2*)


22
5.1
44.5
 0
ND
ND
ND


23
8.4
43.6
 0
ND
ND
ND


24
13.6
46.0
 0.92
Pending
0.30
81.9








(91.2*)





ND = not determined;


*These data for first cycle effiency in parenthesis were measured for voltage window of 5 mV to 1.5 V.






The data in Table 6 reveal an unexpected relationship between decreasing Z and increasing cp. All silicon-carbon composites with Z<10 had φ≥0.13, and all silicon-carbon composites with Z>10 had φ<0.13, indeed, all silicon-carbon composites with where Z>10 had φ=0. This relationship is also evidenced in FIG. 6. Without being bound by theory, silicon materials comprising φ≥0.10, for example φ≥0.13, correspond to a novel form of silicon. Alternatively, silicon materials comprising φ>0 correspond to a novel form of silicon. Without being bound by theory, silicon materials comprising φ>0 are characteristic to silicon material wherein the silicon is amorphous, nano-sized silicon confined within pores, for example pores of a porous carbon scaffold. The silicon-carbon composite material comprising silicon comprising φ≥0.10, for example φ≥0.13, corresponds to a novel silicon-carbon composite material. Alternatively, silicon-carbon composite materials comprising φ>0 corresponds to a novel silicon-carbon composite material.


In certain embodiments, the silicon-carbon composite comprises a φ≥0.1, φ≥0.11, φ≥0.12, φ≥0.13, φ≥0.14, φ≥0.15, φ≥0.16, φ≥0.17, φ≥0.18, φ≥0.19, φ≥0.20, φ≥0.24, φ≥0.24, φ≥0.25, φ≥0.30 or φ≥0.35. In some embodiment, φ>0. In some embodiments, φ≥0.001, φ≥0.01, φ≥0.02, φ≥0.05, φ≥0.1, φ≥0.11, or φ≥0.12.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ>0.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ>0, for example Z less than 10 and >70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ>0.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ>0.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ>0, for example Z less than 10 and >80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ>0.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ≥0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ>0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ>0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ>0.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ>0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than m2/g, and φ>0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ>0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ>0, for example Z less than 10 and >90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ>0.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ≥0.1, for example Z less than 5 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1.


In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ>0, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than m2/g, and φ>0, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ>0, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ>0, for example Z less than 10 and >95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ>0.


Example 4. Particle size distribution for various carbon scaffold materials. The particle size distribution for the various carbon scaffold materials was determined by using a laser diffraction particle size analyzer as known in the art. Table 7 presented the data, specifically the Dv1, Dv10, Dv50, and Dv90, and Dv100.









TABLE 7







Properites of various carbon scaffold materials.








Carbon Scaffold



#
Particle Size Characteristics











1
Dv,1 = 1.2 um, Dv,10 = 2.5 um, Dv,50 = 6.9 um,



Dv90 = 11.5 um, Dv100 = 20.1 um


2
Dv,1= 1.09, Dv10 = 3.4 um, Dv50 = 7.67 um,



Dv,90 = 13.3 um, Dv100 = 17.8


4
Dv,1= 0.81, Dv10 = 1.9 um, Dv50 = 6.4 um,



Dv,90 = 16.6 um, Dv100 = 26.5


5
Dv,1= 0.62, Dv10 = 1.1 um, Dv50 = 4.2 um,



Dv,90 = 15.8 um, Dv100 = 29.8


8
Dv,1= 1.3, Dv10 = 3.7 um, Dv50 = 16 um,



Dv,90 = 35.2 um, Dv100 = 50.7


9
Dv,1 = 1.2 um, Dv,10 = 2.7 um, Dv,50 = 7.6 um,



Dv,90 = 12.3 um, Dv100 = 20.7 um


10
Dv,1 = 1.09 um, Dv,10 = 2 um, Dv,50 = 6.8 um,



Dv,90 = 12.6 um, Dv100 = 19.8 um


11
Dv,1 = 1.3 um, Dv,10 = 2.7 um, Dv,50 = 7.7 um,



Dv,90 = 12.9 um, Dv100 = 22.7 um









Example 5. Effect of CVI process variables on fractional conversion of silicon-containing gas into elemental silicon for production for various silicon-composite materials. Table 8 presents several key CVI process parameters employed for producing the various silicon-carbon materials. For these examples, two reactor types were employed, static bed (SB) type, wherein the bed of porous carfon scaffold is fixed and resides within the heated zone of the reactor, and a horizontally moving bed (HMB), wherein the bed of porous carbon is horizontally traversed through the hot zone. Silicon-Carbon Composite Sample 4, Silicon-Carbon Composite Sample 5, Silicon-Carbon Composite Sample 7, and Silicon-Carbon Composite Sample 8 were produced employing the HMB configuration, and all other Silicon-Carbon Composite Samples listed in Table 8 were produced employing the SB configuration. Other reactor types are envisioned. In other embodiments, the CVI reactor type can be varied, for example the CVI reactor can be a vibro-thermal assisted CVI (VTA-CVI) reactor. In other embodiments, the CVI reactor type can be a convection-thermal assisted CVI (CTA-CVI) reactor. In other embodiments, the CVI reactor type can be a rotating CVI kiln. In other embodiments, the CVI reactor type can be a fluidized bed CVI (FB-CVI) reactor. In the current Example, the CVI process was carried out as a batch process with a of between 1 and 6 hours. In other embodiments, the CVI process can be run as a semi-batch process. In certain other embodiments, the CVI process can be run as a continuous process.









TABLE 8







CVI Process data for producing various silicon-carbon materials.

















Carbon
YCVI



Silicon-



Scaffold
((mol



Carbon
CVI
Conc.

Bed
silicon/h)/



Composite
Temp
Silane
Diluent
Loading
mol carbon
Xsi


#
(° C.)
(%)
Gas
(g/cm2)
scafold)
(%)





 1
450
 10
H2
0.0081
 2.90
10


 2
450
 30
H2
0.0156
16.83
 8.5


 3
450
 40
H2
0.0158
22.74
 7.5


 4
525
 1.25
N2
0.0078
 0.37
64


 5
525
 1.25
N2
0.0078
 0.37
63


 6
450
 1.25
N2
0.0077
 1.07
43


 7
525
 1.25
N2
0.0078
 0.37
66


 8
525
 1.25
N2
0.0078
 0.37
65


 9
450
 10
N2
0.0079
 2.83
10


10
450
 1.25
N2
0.0039
 2.11
25


11
450
 1.25
N2
0.0056
 1.48
35


12
450
 1.25
N2
0.0039
 2.11
22


13
450
 1.25
N2
0.0078
 1.07
37


14
450
 1.25
N2
0.0039
 2.14
17


15
450
 1.25
N2
0.0059
 1.41
22


16
450
 1.25
N2
0.0039
 2.14
18


17
430
 40
H2
0.1684
 0.28
64.7


18
430
 40
H2
0.1688
 0.28
66.4


19
430
 40
H2
0.1769
 0.27
69.9


20
400
100
None
0.5434
 0.27
59.8


21
420
100
None
0.3026
 0.12
85.2


22
420
100
None
0.168
 0.28
88.9


23
420
100
None
0.164
 0.28
91.4


24
375
Varied*
N2
0.375
 0.11
73.7





*For this sample, the silane flow rate was varied, therefore, in this case YCVI is calculated as the overall mol silane per hour, i.e., calculated as the total mol of silane delivered to the CVI reactor divided by the total CVI reaction time.






As presented in Table 8, for samples produced per this example, the CVI temperature was varied from 400° C. to 525° C. Other temperature ranges can be employed for the CVI process, for example from 350° C. to 550° C., for example from 350° C. to 500° C., for example from 350° C. to 450° C., for example from 375° C. to 450° C., for example from 380° C. to 450° C., for example from 385° C. to 450° C., for example from 390° C. to 450° C.


Also presented in Table 8, for samples produced per this example, the silicon-containing precursor gas was silane, and the concentration of silane as the mass fraction of the total gas composition was varied from 1.25% to 100%. For samples where the silane gas was mixed with a diluent gas, the diluent gas was varied, either hydrogen (H2) or nitrogen (N2). Other diluent gases are envisioned, for example argon.


The CVI process may be carried out where in the gas introduced into the CVI reactor comprises 100% silane. Alternatively, gas introduced into the CVI reactor comprises less than 100% silane, and also comprises a diluent gas comprising hydrogen, nitrogen, argon, or combinations thereof.


Also presented in Table 8, for samples produced per this example, the areal loading of the starting carbon scaffold material within the bed was varied, from 0.0039 g/cm2 to 0.5434 g/cm2. In other envisioned embodiments, the areal loading of the carbon scaffold material within the bed can be varied, for example from 0.001 g/cm2 to g/cm2. In other embodiments, the areal loading of the carbon scaffold material within the bed can be varied, for example from 1 g/cm2 to 5 g/cm2. In other envisioned embodiments, the areal loading of the carbon scaffold material within the bed can be varied, for example from 5 g/cm2 to 10 g/cm2. In other envisioned embodiments, the areal loading of the carbon scaffold material within the bed can be greater 10 g/cm2.


Alternatively, the areal loading of the starting carbon scaffold material within the bed can vary from 0.0001 to g/cm2 to 1 g/cm2. For example, the areal loading of the starting carbon scaffold material within the bed can vary from 0.001 to g/cm2 to 1 g/cm2, or from 0.002 to g/cm2 to 1 g/cm2, or from 0.003 to g/cm2 to 1 g/cm2, or from to g/cm2 to 1 g/cm2, or from 0.005 to g/cm2 to 1 g/cm2. In some embodiments, the areal loading of the starting carbon scaffold material within the bed can vary from g/cm2 to 1 g/cm2.


Also presented in Table 8, for samples produced per this example, the silane flow rate into the CVI reactor can be normalized to the carbon scaffold. Thusly, the carbon scaffold normalized silane flow rate can vary. Since one mol of silane gas comprise one mol of silicon, it can also be described that the carbon scaffold normalized silicon flow rate can be varied. This process parameter can be expressed as:







Y

CV

1


=


mol


silicon


introduced


into


the


CVI


reactor


per


hour


mol


carbon


scaffold


in


the






CVI


reactor






In the current example, since the silicon containing gas employed for the CVI process is silane, and each mol of silane comprises one mol of silicon, the above equation can be alternatively expressed as:







Y

CV

1


=


mol


silane


per


hour


mol


carbon


scaffold


in


the


CVI


reactor






A surprising and unexpected result relates to the utilization of the silane gs during CVI processing to prepare the silicon-carbon composite. This utilization as a percentage can be defined as:







X
Si

=

100
×


mol


silicon


in


the


silicon
-
carbon


composite


mol


silicon


feedstock







Wherein the mol silicon in the silicon-carbon composite is determined after CVI processing is completed and from the % silicon in the silicon-carbon composite as determined by TGA. Also for this determination, the mole silicon feedstock is the total mol of silicon introduced into the CVI reactor in for form of silicon containing gas for the duration of CVI processing to convert the porous carbon scaffold and the silicon containing gas into the silicon-carbon composite. For the embodiment wherein the silicon containing gas is silane, there is 1 mol silicon per mol silane thus:







X
Si

=

100
×


mol


silicon


in


the


silicon
-
carbon


composite


mol


silicon


feedstock







In certain embodiments, the silane flow rate is kept constant for the duration of the CVI reaction. In this case, the mol silane per hour used to calculate YCVI is the molar silane flow rate in the units of mol/h. In some embodiments, the silane flow is varied, for example in a stepwise fashion, and/or as a ramp. In some embodiments, the silane flow rate at the beginning and end of the CVI reaction duration are lower. In a case where the flow rate has been varied, YCVI is calculated as the overall mol silane per hour, for instance is calculated as the total mol of silane delivered to the CVI reactor divided by the total CVI reaction time.


The data for XSi are included in Table 8. As can be seen, XSi increases dramatically as YCVI decreases (see FIG. 7). In some embodiments for employing CVI to produce the silicon-carbon composite, YCVI<1 and XSi>50%. In a preferred embodiment for employing CVI to produce the silicon-carbon composite, YCVI<0.5 and XSi>50%. In a further preferred embodiment for employing CVI to produce the silicon-carbon composite, YCVI<0.4 and XSi>60%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.3 and XSi>70%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.2 and XSi>70%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.3 and XSi>80%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.2 and XSi>80%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.3 and XSi>85%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.2 and XSi>85%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.3 and XSi>90%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.2 and XSi>90%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.3 and XSi>95%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.2 and XSi>95%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.2 and XSi>99%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.1 and XSi>90%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.1 and XSi>95%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.1 and XSi>99%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.05 and XSi>90%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.05 and XSi>95%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.05 and XSi>99%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.01 and XSi>90%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.01 and XSi>95%. In a further preferred embodiment for employing CVI to produce the silicon carbon composite, YCVI<0.01 and XSi>99%.


Example 6. In-line process monitoring of silane utilization during CVI processing as determined from Fourier-transformed infrared (FTIR) spectroscopy. Fourier-transformed infrared (FTIR) spectroscopy is a suitable method for quantitation of concentration of gas in the gas phase for silane gas. To this end, for the preparation of Silicon-Carbon Composite 21, the gas exiting the reactor was routed into a gas tight FTIR cell within the FTIR spectrophotometer. The % silane concentration exiting the reactor, i.e., concentration of silane exiting the reactor as a percentage of the silane concentration entering the reactor, was quantitated by determining the peak height at 979 cm-1 in the FTIR spectrum for the gas exiting the reactor, and dividing that value by the peak height at 979 cm-1 in the FTIR spectrum for the control, namely unreacted silane gas, and multiplying said value by 100 to convert into percentage. The % silane utilization was then calculated as 100 minus the % silane concentration exiting the reactor. FIG. 8 depicts the in-line process data for % silane utilization as a function of time for preparation of Sample 21. As can be seen, the peak utilization is 98%. Without being bound by theory, based on the analysis from the previous example, the silane flow rate during the initial and final CVI reaction phases can be modulated, i.e., reduced, in order to increase the silane utilization during these phases. In this fashion, XSi can be further increased, for example XSi greater than 85%, or XSi greater than 90%, or XSi greater than 95%, or XSi greater than or equal to 98%. Without being bound by theory, these data also demonstrate the feasibility of conducting the CVI processing in a continuous reactor wherein it is possible to achieve XSi greater than or equal to 98%.


Example 7. CVI Processes Comprising Recycle or Recycle with Purge Stream. The process to create the silicon-carbon compositor particles may comprise a recycle stream. Accordingly, the gas exiting the CVI reactor may contain unreacted silane gas, hydrogen gas (created as a result of consumed silane), and diluent gas (if employed) and this gas stream may be re-introduced as one or more feed streams back into the CVI reactor. In certain embodiments, the CVI reactor comprises multiple zones, and the silane recycle stream can be fed as one or more feed streams into one or more zones of the CVI reactor. In certain embodiments, the recycle stream comprises a purge stream. Accordingly, any hydrogen or diluent gas present in the recycle stream can be separated from the silane present in the recycle stream, for example, by gas separation techniques such as distillation or membrane gas separation. Employing such a recycle stream or recycle stream with puring can further increase net silane tilization, resulting in XSi greater than 50%, for example greater than 60%, for example greater than 70%, for example greater than 85%, for example greater than 90%, for example greater than 95%, for example greater than 98%, for example greater than 99%.


EXPRESSED EMBODIMENTS

Embodiment 1. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.5 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold); and
    • d. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 2. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.5 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° ° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis.


Embodiment 3. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.5 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 4. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.5 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a silicon content of 30% to 60% by weight;
      • ii. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° ° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis;
      • iii. a surface area less than 30 m2/g; and
      • iv. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 5. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.4 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold); and
    • d. wherein XSi of the process is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 6. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.4 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis.


Embodiment 7. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.4 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 8. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.4 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a silicon content of 30% to 60% by weight;
      • ii. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° ° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis;
      • iii. a surface area less than 30 m2/g; and
      • iv. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 9. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold); and
    • d. wherein XSi of the process is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 10. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis.


Embodiment 11. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 12. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a silicon content of 30% to 60% by weight;
      • ii. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° ° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° ° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis;
      • iii. a surface area less than 30 m2/g; and
      • iv. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 13. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold); and
    • d. wherein XSi of the process is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 14. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° ° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis.


Embodiment 15. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 16. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a silicon content of 30% to 60% by weight;
      • ii. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° ° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis;
      • iii. a surface area less than 30 m2/g; and
      • iv. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 17. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold); and
    • d. wherein XSi of the process is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 18. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis.


Embodiment 19. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 20. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
    • b. heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
    • c. providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
    • d. wherein XSi of the process is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • e. wherein the silicon-carbon composite comprises:
      • i. a silicon content of 30% to 60% by weight;
      • ii. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis;
      • iii. a surface area less than 30 m2/g; and
      • iv. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 21. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 20 wherein the pore volume comprises greater than 80% microporosity.


Embodiment 22. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 21 wherein the pore volume comprises greater than 90% microporosity.


Embodiment 23. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 22 wherein the pore volume comprises greater than 95% microporosity.


Embodiment 24. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 23 wherein the temperature is between 400° C. and 525° C.


Embodiment 25. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 24 wherein the silicon-carbon composite comprises a silicon content of 40-60%.


Embodiment 26. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 25 wherein the silicon-carbon composite comprises a Z less than 5.


Embodiment 27. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 26 wherein the silicon-carbon composite comprises a surface area less than 10 m2/g.


Embodiment 28. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 27 wherein the silicon-carbon composite comprises a φ of greater than or equal to 0.2, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 29. The process for preparing silicon-carbon composite particles of any of Embodiments 1 through Embodiment 28 wherein the silicon-carbon composite comprises a φ of greater than or equal to 0.3, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 30. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 29 wherein the silicon-carbon composite comprises a Dv50 between 5 nm and 20 microns.


Embodiment 31. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 30 wherein the silicon-carbon composite comprises a capacity of greater than 900 mAh/g.


Embodiment 32. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 31 wherein the silicon-carbon composite comprises a capacity of greater than 1300 mAh/g.


Embodiment 33. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 32 wherein the silicon-carbon composite comprises a capacity of greater than 1600 mAh/g.


Embodiment 34. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 33 wherein the process is a batch process.


Embodiment 35. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 34 wherein the process is a continuous process.


Embodiment 36. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 35 wherein the reactor type is a static bed reactor, a horizontally moving bed reactor, a vibro-thermal assisted reactor, a convection-thermal assisted reactor, or a fluidized bed reactor.


Embodiment 37. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 36 wherein the concentration of silane as the mass fraction of the total gas composition is 1.25% to 100%.


Embodiment 38. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 36 wherein the gas comprises silane and an inert gas selected from nitrogen, hydrogen, argon, or helium, or combinations thereof.


Embodiment 39. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 38 wherein the areal loading of carbon scaffold is 0.001 g/cm2 to 10 g/cm2.


Embodiment 40. An energy storage device comprising a silicon-carbon composite prepared as described by any of Embodiments 1 to Embodiment 39.


Embodiment 41. A lithium ion battery comprising a silicon-carbon composite prepared by any of the embodiments from Embodiment 1 to Embodiment 39.


Embodiment 42. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises one or more micropores and one or more mesopores;
    • b. heating the porous carbon scaffold in the presence of silane gas to a temperature between 350° C. and 550° C.; and
    • c. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 43. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises one or more micropores and one or more mesopores;
    • b. heating the porous carbon scaffold in the presence of silane gas to a temperature between 350° C. and 550° C.;
    • c. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • d. wherein the silicon-carbon composite comprises:
      • ii. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis.


Embodiment 44. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises one or more micropores and one or more mesopores;
    • b. heating the porous carbon scaffold in the presence of silane gas to a temperature between 350° C. and 550° C.;
    • c. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • d. wherein the silicon-carbon composite comprises:
      • ii. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 45. A process for preparing silicon-carbon composite particles comprising:

    • a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises one or more micropores and one or more mesopores;
    • b. heating the porous carbon scaffold in the present of silane gas to a temperature between 350° C. and 550° C.;
    • c. wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; and
    • d. wherein the silicon-carbon composite comprises:
      • v. a silicon content of 30% to 70% by weight;
      • vi. a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis;
      • vii. a surface area less than 30 m2/g; and
      • viii. a φ of greater than or equal to 0.1, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.


Embodiment 46. The process for preparing silicon-carbon composite particles of Embodiment 42 wherein the XSi is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 47. The process for preparing silicon-carbon composite particles of Embodiment 43 wherein the XSi is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 48. The process for preparing silicon-carbon composite particles of Embodiment 44 wherein the XSi is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 49. The process for preparing silicon-carbon composite particles of Embodiment 45 wherein the XSi is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 50. The process for preparing silicon-carbon composite particles of Embodiment 42 wherein the XSi is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 51. The process for preparing silicon-carbon composite particles of Embodiment 43 wherein the XSi is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 52. The process for preparing silicon-carbon composite particles of Embodiment 44 wherein the XSi is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 53. The process for preparing silicon-carbon composite particles of Embodiment 45 wherein the XSi is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 54. The process for preparing silicon-carbon composite particles of Embodiment 42 wherein the XSi is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 55. The process for preparing silicon-carbon composite particles of Embodiment 43 wherein the XSi is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 56. The process for preparing silicon-carbon composite particles of Embodiment 44 wherein the XSi is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 57. The process for preparing silicon-carbon composite particles of Embodiment 45 wherein the XSi is greater than 85%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 58. The process for preparing silicon-carbon composite particles of Embodiment 42 wherein the XSi is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 59. The process for preparing silicon-carbon composite particles of Embodiment 43 wherein XSi is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 60. The process for preparing silicon-carbon composite particles of Embodiment 44 wherein the XSi is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 61. The process for preparing silicon-carbon composite particles of Embodiment 45 wherein the XSi is greater than 90%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.


Embodiment 62. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 61 wherein the silane gas comprises a recycle stream.


Embodiment 63. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 61 wherein the silane gas comprises a recycle stream comprising a purge stream.


Embodiment 64. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 64 where the silicon-carbon composite particles comprise a first cycle efficiency of >75% when measured in a half cell for voltage window of 5 mV to 0.8 V.


Embodiment 65. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 64 where the silicon-carbon composite particles comprise a first cycle efficiency of >80% when measured in a half cell for voltage window of 5 mV to 0.8 V.


Embodiment 66. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 64 where the silicon-carbon composite particles comprise a first cycle efficiency of >85% when measured in a half cell for voltage window of 5 mV to 1.5 V.


Embodiment 67. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 64 where the silicon-carbon composite particles comprise a first cycle efficiency of >90% when measured in a half cell for voltage window of 5 mV to 1.5 V.


Embodiment 68. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 64 where the silicon-carbon composite particles comprise a first cycle efficiency of >91% when measured in a half cell for voltage window of 5 mV to 1.5 V.


Embodiment 69. The process for preparing silicon-carbon composite particles of any of the embodiments from Embodiment 1 through Embodiment 64 where the silicon-carbon composite particles comprise a first cycle efficiency of >92% when measured in a half cell for voltage window of 5 mV to 1.5 V.


From the foregoing it will be appreciated that, although specific embodiments of the invention have been described herein for purposes of illustration, various modifications may be made without deviating from the spirit and scope of the invention. Accordingly, the invention is not limited except as by the appended claims.

Claims
  • 1. A process for preparing silicon-carbon composite particles, the process comprising: a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;b. heating the porous carbon scaffold to a temperature from 300° C. to 500° ° C.;c. contacting the carbon scaffold with a silane feedstock gas to obtain a silicon-impregnated carbon scaffold, wherein the silane feedstock gas corresponds to a YCVI less than 0.4 wherein YCVI=(mole of silane feedstock gas per hour)/(mol of carbon scaffold); andd. providing a layer of carbon to at least partially covering a surface of the silicon-impregnated carbon scaffold,wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock gas), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.
  • 2. The process for preparing silicon-carbon composite particles of claim 1, wherein the pore volume comprises greater than 90% microporosity.
  • 3. The process for preparing silicon-carbon composite particles of claim 1, wherein the silicon-carbon composite particles comprise a surface area less than 10 m2/g.
  • 4. The process for preparing silicon-carbon composite particles of claim 1, wherein the silicon-carbon composite particles comprise a Dv50 ranging from 5 nm to 20 microns.
  • 5. The process for preparing silicon-carbon composite particles of claim 1, wherein the feedstock gas comprises silane and an inert gas selected from the group consisting of nitrogen, hydrogen, argon, and helium, and combinations thereof.
  • 6. The process for preparing silicon-carbon composite particles of claim 1, wherein the concentration of silane as the mass fraction of the total feedstock gas composition is 1.25% to 100%.
  • 7. The process for preparing silicon-carbon composite particles of claim 1, wherein the process is a continuous process.
  • 8. The process for preparing silicon-carbon composite particles of claim 1, wherein the process is conducted in a fluidized bed reactor.
  • 9. The process for preparing silicon-carbon composite particles of claim 1, wherein the porous carbon scaffold comprises a span (Dv50)/(Dv90−Dv10) from 100 to less than 1.
  • 10. The process for preparing silicon-carbon composite particles of claim 1, wherein the silane gas comprises a recycle stream.
  • 11. The process for preparing silicon-carbon composite particles of claim 10, wherein the recycle stream comprises a purge stream.
  • 12. The process for preparing silicon-carbon composite particles of claim 1, wherein the flow rate of the silane feedstock gas is varied.
  • 13. A process for preparing silicon-carbon composite particles, the process comprising: a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;b. heating the porous carbon scaffold to a temperature from 350° C. to 550° C.;c. contacting the carbon scaffold with a silane feedstock gas to obtain a silicon-impregnated carbon scaffold, wherein the silane feedstock gas corresponds to a YCVI less than 0.2, wherein YCVI=(mole of silane feedstock gas per hour)/(mol of carbon scaffold); andd. providing a layer of carbon on the silicon-impregnated carbon scaffold,wherein:XSi of the process is greater than 60%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock gas), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; andthe silane gas comprises a recycle stream.
  • 14. The process for preparing silicon-carbon composite particles of claim 13, wherein the pore volume comprises greater than 90% microporosity.
  • 15. The process for preparing silicon-carbon composite particles of claim 13, wherein the silicon-carbon composite particles comprise a surface area less than 10 m2/g.
  • 16. The process for preparing silicon-carbon composite particles of claim 13, wherein the silicon-carbon composite particles comprise a Dv50 ranging from 5 nm to 20 microns.
  • 17. The process for preparing silicon-carbon composite particles of claim 13, wherein the feedstock gas comprises silane and an inert gas selected from the group consisting of nitrogen, hydrogen, argon, and helium, and combinations thereof.
  • 18. The process for preparing silicon-carbon composite particles of claim 13, wherein the concentration of silane as a mass fraction of the total feedstock gas composition is 1.25% to 100%.
  • 19. The process for preparing silicon-carbon composite particles of claim 13, wherein the porous carbon scaffold comprises a span (Dv50)/(Dv90−Dv10) from 100 to less than 1.
  • 20. The process for preparing silicon-carbon composite particles of claim 13, wherein the recycle stream comprises a purge stream.
  • 21. The process for preparing silicon-carbon composite particles of claim 13, wherein the flow rate of the silane feedstock gas is varied.
  • 22. A process for preparing silicon-carbon composite particles, the process comprising: a. providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;b. heating the porous carbon scaffold to a temperature from 350° C. to 550° C.;c. contacting the carbon scaffold with a silane feedstock gas to obtain a silicon-impregnated carbon scaffold, wherein the silane feedstock gas corresponds to a YCVI less than 0.2 wherein YCVI=(mole of silane feedstock gas per hour)/(mol of carbon scaffold); andd. providing a layer of carbon at least partially covering the silicon-impregnated carbon scaffold,wherein:XSi of the process is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock gas), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis; andthe silane gas comprises a recycle stream.
  • 23. The process for preparing silicon-carbon composite particles of claim 22, wherein the pore volume comprises greater than 90% microporosity.
  • 24. The process for preparing silicon-carbon composite particles of claim 22, wherein the silicon-carbon composite particles comprise a surface area less than 10 m2/g.
  • 25. The process for preparing silicon-carbon composite particles of claim 22, wherein the silicon-carbon composite particles comprise a Dv50 ranging from 5 nm to 20 microns.
  • 26. The process for preparing silicon-carbon composite particles of claim 22, wherein the feedstock gas comprises silane and an inert gas selected from the group consisting of nitrogen, hydrogen, argon, and helium, and combinations thereof.
  • 27. The process for preparing silicon-carbon composite particles of claim 22, wherein the concentration of silane as a mass fraction of the total feedstock gas composition is 1.25% to 100%.
  • 28. The process for preparing silicon-carbon composite particles of claim 22, wherein the porous carbon scaffold comprises a span (Dv50)/(Dv90−Dv10) from 100 to less than 1.
  • 29. The process for preparing silicon-carbon composite particles of claim 22, wherein the recycle stream comprises a purge stream.
  • 30. The process for preparing silicon-carbon composite particles of claim 22, wherein the flow rate of the silane feedstock gas is varied.
US Referenced Citations (384)
Number Name Date Kind
2282235 Moberly May 1942 A
3518123 Katsoulis et al. Jun 1970 A
3582288 Jenkins et al. Jun 1971 A
3619428 David Nov 1971 A
3634028 Hohne Jan 1972 A
3790659 Storp et al. Feb 1974 A
3876505 Stoneburner Apr 1975 A
3892580 Messing Jul 1975 A
3977901 Buzzelli Aug 1976 A
4082694 Wennerberg et al. Apr 1978 A
4159913 Birchall et al. Jul 1979 A
4198382 Matsui Apr 1980 A
4543341 Barringer et al. Sep 1985 A
4580404 Pez et al. Apr 1986 A
4769197 Kromrey Sep 1988 A
4843015 Grubbs, Jr. et al. Jun 1989 A
4862328 Morimoto et al. Aug 1989 A
4873218 Pekala Oct 1989 A
4954469 Robinson Sep 1990 A
4997804 Pekala Mar 1991 A
4999330 Bose et al. Mar 1991 A
5061416 Willkens et al. Oct 1991 A
5093216 Azuma et al. Mar 1992 A
5260855 Kaschmitter et al. Nov 1993 A
5294498 Omaru et al. Mar 1994 A
5416056 Baker May 1995 A
5420168 Mayer et al. May 1995 A
5465603 Anthony et al. Nov 1995 A
5508341 Mayer et al. Apr 1996 A
5529971 Kaschmitter et al. Jun 1996 A
5614460 Schwarz et al. Mar 1997 A
5626637 Baker May 1997 A
5626977 Mayer et al. May 1997 A
5670571 Gabrielson et al. Sep 1997 A
5674642 Le et al. Oct 1997 A
5710092 Baker Jan 1998 A
5726118 Ivey et al. Mar 1998 A
5744258 Bai et al. Apr 1998 A
5789338 Kaschmitter et al. Aug 1998 A
5834138 Yamada et al. Nov 1998 A
5858486 Metter et al. Jan 1999 A
5882621 Doddapaneni et al. Mar 1999 A
5891822 Oyama et al. Apr 1999 A
5908896 Mayer et al. Jun 1999 A
5945084 Droege Aug 1999 A
5965483 Baker et al. Oct 1999 A
6006797 Bulow et al. Dec 1999 A
6064560 Hirahara et al. May 2000 A
6069107 Kuznetsov et al. May 2000 A
6072693 Tsushima et al. Jun 2000 A
6096456 Takeuchi et al. Aug 2000 A
6117585 Anani et al. Sep 2000 A
6147213 Poli et al. Nov 2000 A
6153562 Villar et al. Nov 2000 A
6205016 Niu Mar 2001 B1
6225257 Putyera et al. May 2001 B1
6242127 Paik et al. Jun 2001 B1
6268081 Clough Jul 2001 B1
6309446 Nakanoya et al. Oct 2001 B1
6310762 Okamura et al. Oct 2001 B1
6339528 Lee et al. Jan 2002 B1
6509119 Kobayashi et al. Jan 2003 B1
6574092 Sato et al. Jun 2003 B2
6592838 Nomoto et al. Jul 2003 B1
6631072 Paul et al. Oct 2003 B1
6631073 Sakata et al. Oct 2003 B1
6697249 Maletin et al. Feb 2004 B2
6764667 Steiner, III Jul 2004 B1
6815105 Cooper et al. Nov 2004 B2
6865068 Murakami et al. Mar 2005 B1
7245478 Zhong et al. Jul 2007 B2
7419649 Lundquist et al. Sep 2008 B2
7582902 Tano et al. Sep 2009 B2
7626804 Yoshio et al. Dec 2009 B2
7722991 Zhang et al. May 2010 B2
7723262 Feaver et al. May 2010 B2
7754178 Tano et al. Jul 2010 B2
7785495 Kikuchi et al. Aug 2010 B2
7816413 Feaver et al. Oct 2010 B2
7835136 Feaver et al. Nov 2010 B2
8158556 Feaver et al. Apr 2012 B2
8293818 Costantino et al. Oct 2012 B2
8329252 Makarov et al. Dec 2012 B2
8361659 Richard Jan 2013 B2
8366979 Dai et al. Feb 2013 B2
8404384 Feaver et al. Mar 2013 B2
8411415 Yoshinaga et al. Apr 2013 B2
8467170 Feaver et al. Jun 2013 B2
8480930 Suh et al. Jul 2013 B2
8482900 Gadkaree et al. Jul 2013 B2
8580870 Costantino et al. Nov 2013 B2
8654507 Costantino et al. Feb 2014 B2
8691177 Pfeifer et al. Apr 2014 B2
8709971 Feaver et al. Apr 2014 B2
8734991 Takano et al. May 2014 B2
8797717 Feaver et al. Aug 2014 B2
8809230 Worsley et al. Aug 2014 B2
8906978 Costantino et al. Dec 2014 B2
8916296 Feaver et al. Dec 2014 B2
8999202 Mulik et al. Apr 2015 B2
9005812 Ma et al. Apr 2015 B2
9067848 Stadie et al. Jun 2015 B2
9112230 Feaver et al. Aug 2015 B2
9133295 Qureshi et al. Sep 2015 B2
9133337 Ludvik et al. Sep 2015 B2
9136064 Gadkaree et al. Sep 2015 B2
9186174 Krishnan Nov 2015 B2
9269502 Chang et al. Feb 2016 B2
9287556 Neumann et al. Mar 2016 B2
9409777 Geramita et al. Aug 2016 B2
9412523 Costantino et al. Aug 2016 B2
9464162 Kron et al. Oct 2016 B2
9580321 Feaver et al. Feb 2017 B2
9666860 Lam et al. May 2017 B2
9680159 Feaver et al. Jun 2017 B2
9704685 Lozano et al. Jul 2017 B2
9714172 Geramita et al. Jul 2017 B2
9985289 Costantino et al. May 2018 B2
10008338 Stadermann et al. Jun 2018 B2
10049824 Tsukada et al. Aug 2018 B2
10141122 Feaver et al. Nov 2018 B2
10147950 Sakshaug et al. Dec 2018 B2
10173900 Ludvik et al. Jan 2019 B2
10195583 Costantino et al. Feb 2019 B2
10273328 Kron et al. Apr 2019 B2
10287170 Feaver et al. May 2019 B2
10361428 Kim et al. Jul 2019 B2
10454094 Xia et al. Oct 2019 B2
10454103 Sakshaug et al. Oct 2019 B2
10490358 Feaver et al. Nov 2019 B2
10508335 Yilmaz et al. Dec 2019 B1
10522836 Thompkins et al. Dec 2019 B2
10590277 Costantino et al. Mar 2020 B2
10600581 Feaver et al. Mar 2020 B2
10608254 Sakshaug et al. Mar 2020 B2
10658659 Mason et al. May 2020 B1
10711140 Costantino et al. Jul 2020 B2
10714744 Sakshaug et al. Jul 2020 B2
10756347 Sakshaug et al. Aug 2020 B2
10763501 Feaver et al. Sep 2020 B2
10784512 Sakshaug et al. Sep 2020 B2
10814304 Costantino et al. Oct 2020 B2
10923722 Sakshaug et al. Feb 2021 B2
10938027 Mason et al. Mar 2021 B2
11011748 Mason et al. May 2021 B2
11165054 Mason et al. Nov 2021 B2
11174167 Dhanabalan et al. Nov 2021 B1
11335903 Costantino et al. May 2022 B2
11401363 Geramita et al. Aug 2022 B2
11437621 Sakshaug et al. Sep 2022 B2
11492262 Dhanabalan et al. Nov 2022 B2
11495793 Sakshaug et al. Nov 2022 B2
11495798 Sakshaug et al. Nov 2022 B1
11498838 Dhanabalan et al. Nov 2022 B2
11611070 Costantino et al. Mar 2023 B2
11611071 Costantino et al. Mar 2023 B2
11611073 Feaver et al. Mar 2023 B2
11639292 Costantino et al. May 2023 B2
11661517 Costantino et al. May 2023 B2
11718701 Geramita et al. Aug 2023 B2
11732079 Geramita et al. Aug 2023 B2
20010002086 Webb May 2001 A1
20020031706 Dasgupta et al. Mar 2002 A1
20020031710 Kezuka et al. Mar 2002 A1
20020036885 Lee et al. Mar 2002 A1
20020075627 Shinozaki et al. Jun 2002 A1
20020086211 Umeno et al. Jul 2002 A1
20020104474 Wakamatsu et al. Aug 2002 A1
20020114126 Hirahara et al. Aug 2002 A1
20020122985 Sato et al. Sep 2002 A1
20020168314 Roemmler Nov 2002 A1
20020172637 Chesneau et al. Nov 2002 A1
20030012722 Liu Jan 2003 A1
20030013606 Hampden-Smith et al. Jan 2003 A1
20030064564 Lin Apr 2003 A1
20030064565 Maletin et al. Apr 2003 A1
20030108785 Wu et al. Jun 2003 A1
20030170548 Otsuki et al. Sep 2003 A1
20040010090 Chino et al. Jan 2004 A1
20040106040 Fukuoka et al. Jun 2004 A1
20040132845 Rhine et al. Jul 2004 A1
20040141963 Umekawa et al. Jul 2004 A1
20040180264 Honbo et al. Sep 2004 A1
20040241237 Pirard et al. Dec 2004 A1
20040248730 Kim et al. Dec 2004 A1
20040248790 Hinuma et al. Dec 2004 A1
20050014643 Lini et al. Jan 2005 A1
20050041370 Wilk et al. Feb 2005 A1
20050058589 Lundquist et al. Mar 2005 A1
20050058907 Kurihara et al. Mar 2005 A1
20050063893 Ayala et al. Mar 2005 A1
20050079349 Hampden-Smith et al. Apr 2005 A1
20050079359 Fujita et al. Apr 2005 A1
20050135993 Xu et al. Jun 2005 A1
20050153130 Long et al. Jul 2005 A1
20050196336 Chatterjee et al. Sep 2005 A1
20050221981 Wagh et al. Oct 2005 A1
20050233195 Arnold et al. Oct 2005 A1
20050250011 Mitchell et al. Nov 2005 A1
20050253220 Lin et al. Nov 2005 A1
20050266990 Iwasaki et al. Dec 2005 A1
20050282062 Manako et al. Dec 2005 A1
20060008408 Ho Yoon et al. Jan 2006 A1
20060057355 Suzuki et al. Mar 2006 A1
20060079587 Albert et al. Apr 2006 A1
20060093915 Lundquist et al. May 2006 A1
20060223965 Trifu Oct 2006 A1
20060240979 Hirahara et al. Oct 2006 A1
20070002523 Ando et al. Jan 2007 A1
20070008677 Zhong et al. Jan 2007 A1
20070048605 Pez et al. Mar 2007 A1
20070104981 Lam et al. May 2007 A1
20070142222 Erkey et al. Jun 2007 A1
20070166602 Burchardt Jul 2007 A1
20070281216 Petrat et al. Dec 2007 A1
20080011986 Yamakawa et al. Jan 2008 A1
20080044726 Feng et al. Feb 2008 A1
20080107804 Kondo May 2008 A1
20080112876 Dailey May 2008 A1
20080132632 Schiraldi et al. Jun 2008 A1
20080145757 Mah et al. Jun 2008 A1
20080145761 Petrat et al. Jun 2008 A1
20080201925 Zhong et al. Aug 2008 A1
20080204973 Zhong et al. Aug 2008 A1
20080206638 Takahashi et al. Aug 2008 A1
20080241640 Rajeshwar et al. Oct 2008 A1
20080261116 Burton et al. Oct 2008 A1
20080268297 Quayle et al. Oct 2008 A1
20080286653 Sano et al. Nov 2008 A1
20080293911 Qureshi et al. Nov 2008 A1
20080297981 Endo et al. Dec 2008 A1
20080299456 Shiga et al. Dec 2008 A1
20090035344 Thomas et al. Feb 2009 A1
20090053594 Johnson et al. Feb 2009 A1
20090097189 Tasaki et al. Apr 2009 A1
20090104509 Kwak et al. Apr 2009 A1
20090104530 Shizuka et al. Apr 2009 A1
20090114544 Rousseau et al. May 2009 A1
20090117466 Zhamu et al. May 2009 A1
20090145482 Mitzi et al. Jun 2009 A1
20090185327 Seymour Jul 2009 A1
20090213529 Gogotsi et al. Aug 2009 A1
20090239151 Nakanishi et al. Sep 2009 A1
20090253248 Sun et al. Oct 2009 A1
20090286160 Kozono et al. Nov 2009 A1
20090305131 Kumar et al. Dec 2009 A1
20100008021 Hu et al. Jan 2010 A1
20100047671 Chiang et al. Feb 2010 A1
20100051881 Ahn et al. Mar 2010 A1
20100092370 Zhang et al. Apr 2010 A1
20100097741 Zhong et al. Apr 2010 A1
20100098615 Tennison et al. Apr 2010 A1
20100110613 Zhong et al. May 2010 A1
20100163791 Fukui et al. Jul 2010 A1
20100213104 Hughes et al. Aug 2010 A1
20100215563 Yambayashi Aug 2010 A1
20100279172 Hwang et al. Nov 2010 A1
20100288970 Watanabe et al. Nov 2010 A1
20100310941 Kumta et al. Dec 2010 A1
20100316907 Yamamoto et al. Dec 2010 A1
20100331179 Feaver et al. Dec 2010 A1
20110002086 Feaver et al. Jan 2011 A1
20110028599 Costantino et al. Feb 2011 A1
20110053765 Feaver et al. Mar 2011 A1
20110111284 Maeshima et al. May 2011 A1
20110159375 Feaver et al. Jun 2011 A1
20110177393 Park et al. Jul 2011 A1
20110199716 Feaver et al. Aug 2011 A1
20110200848 Chiang et al. Aug 2011 A1
20110223494 Feaver et al. Sep 2011 A1
20110261501 Gadkaree et al. Oct 2011 A1
20110281180 Kim et al. Nov 2011 A1
20110287189 Shembel et al. Nov 2011 A1
20110300447 Archer Dec 2011 A1
20110311873 Schulz et al. Dec 2011 A1
20120045685 Seki et al. Feb 2012 A1
20120081838 Costantino et al. Apr 2012 A1
20120129049 Rayner May 2012 A1
20120156493 Maisels et al. Jun 2012 A1
20120156567 Ayme-Perrot et al. Jun 2012 A1
20120183856 Cui et al. Jul 2012 A1
20120202033 Chang et al. Aug 2012 A1
20120241691 Soneda et al. Sep 2012 A1
20120251876 Jagannathan Oct 2012 A1
20120264020 Burton et al. Oct 2012 A1
20120305651 Anderson et al. Dec 2012 A1
20120308870 Okuda et al. Dec 2012 A1
20120321959 Yushin et al. Dec 2012 A1
20130004841 Thompkins et al. Jan 2013 A1
20130020349 Feaver et al. Jan 2013 A1
20130077207 Kirschbaum Mar 2013 A1
20130082213 Duncan et al. Apr 2013 A1
20130157151 Feaver et al. Jun 2013 A1
20130169238 Rojeski Jul 2013 A1
20130189472 Takaoka Jul 2013 A1
20130189575 Anguchamy et al. Jul 2013 A1
20130196158 Yoshida et al. Aug 2013 A1
20130244862 Ivanovici et al. Sep 2013 A1
20130252082 Thompkins et al. Sep 2013 A1
20130280601 Geramita et al. Oct 2013 A1
20130295462 Atanassova et al. Nov 2013 A1
20130321982 Feaver et al. Dec 2013 A1
20130337334 Tao et al. Dec 2013 A1
20130344363 Upadhyaya Dec 2013 A1
20130344391 Yushin et al. Dec 2013 A1
20140038042 Rios et al. Feb 2014 A1
20140057179 Yushin et al. Feb 2014 A1
20140094572 Costantino et al. Apr 2014 A1
20140162873 Gu Jun 2014 A1
20140170482 Park et al. Jun 2014 A1
20140220456 Costantino et al. Aug 2014 A1
20140287317 Tiquet et al. Sep 2014 A1
20140302396 Lu et al. Oct 2014 A1
20140335410 Loveridge et al. Nov 2014 A1
20150037249 Fu Feb 2015 A1
20150062781 Feaver et al. Mar 2015 A1
20150087731 Dong et al. Mar 2015 A1
20150155546 Yushin et al. Jun 2015 A1
20150162603 Yushin et al. Jun 2015 A1
20150207148 Kimura et al. Jul 2015 A1
20150238917 Mulik et al. Aug 2015 A1
20150255781 Hashimoto Sep 2015 A1
20150255800 Feaver et al. Sep 2015 A1
20150283534 Costantino et al. Oct 2015 A1
20150306570 Mayes et al. Oct 2015 A1
20160010250 Taninaka et al. Jan 2016 A1
20160039970 Kron et al. Feb 2016 A1
20160043384 Zhamu et al. Feb 2016 A1
20160104882 Yushin et al. Apr 2016 A1
20160122185 Feaver et al. May 2016 A1
20170015559 Costantino et al. Jan 2017 A1
20170152340 Geramita et al. Jun 2017 A1
20170155148 Costantino et al. Jun 2017 A1
20170170477 Sakshaug et al. Jun 2017 A1
20170200566 Stadermann et al. Jul 2017 A1
20170316888 Geramita et al. Nov 2017 A1
20170346084 Sakshaug et al. Nov 2017 A1
20170349442 Feaver et al. Dec 2017 A1
20180097240 Feaver et al. Apr 2018 A1
20180130609 Feaver et al. May 2018 A1
20180294484 Fredrick et al. Oct 2018 A1
20180331356 Feaver et al. Nov 2018 A1
20190088931 Abrahamson et al. Mar 2019 A1
20190097222 Feaver et al. Mar 2019 A1
20190103608 Costantino et al. Apr 2019 A1
20190144287 Park et al. May 2019 A1
20190259546 Kron et al. Aug 2019 A1
20190267622 Sakshaug et al. Aug 2019 A1
20190280298 Sakshaug et al. Sep 2019 A1
20190287737 Feaver et al. Sep 2019 A1
20190358607 Costantino et al. Nov 2019 A1
20200020935 Costantino et al. Jan 2020 A1
20200048098 Feaver et al. Feb 2020 A1
20200144619 Hamilton et al. May 2020 A1
20200148886 Costantino et al. May 2020 A1
20200152983 Sakshaug et al. May 2020 A1
20200259178 Chang et al. Aug 2020 A1
20200259181 Thompkins et al. Aug 2020 A1
20200280070 Sakshaug et al. Sep 2020 A1
20200290882 Fredrick et al. Sep 2020 A1
20200303737 Kang et al. Sep 2020 A1
20200365896 Sakshaug et al. Nov 2020 A1
20200373561 Mason et al. Nov 2020 A1
20210054213 Costantino et al. Feb 2021 A1
20210057736 Feaver et al. Feb 2021 A1
20210126251 Sakshaug et al. Apr 2021 A1
20210175498 Feaver et al. Jun 2021 A1
20210237029 Costantino et al. Aug 2021 A1
20210276875 Mason et al. Sep 2021 A1
20220048774 Yan et al. Feb 2022 A1
20220055905 Dhanabalan et al. Feb 2022 A1
20220055906 Costantino et al. Feb 2022 A1
20220059818 Dhanabalan et al. Feb 2022 A1
20220059820 Costantino et al. Feb 2022 A1
20220064008 Dhanabalan et al. Mar 2022 A1
20220074045 Yilmaz et al. Mar 2022 A1
20220231296 Sakshaug et al. Jul 2022 A1
20220246910 Mason et al. Aug 2022 A1
20220246914 Costantino et al. Aug 2022 A1
20220352517 Sakshaug et al. Nov 2022 A1
20220389146 Geramita et al. Dec 2022 A1
20230016325 Geramita et al. Jan 2023 A1
20230022154 Geramita et al. Jan 2023 A1
20230058348 Sakshaug et al. Feb 2023 A1
Foreign Referenced Citations (91)
Number Date Country
2176452 Nov 1997 CA
1762900 Apr 2006 CN
1877888 Dec 2006 CN
1986401 Jun 2007 CN
101284665 Oct 2008 CN
101292389 Oct 2008 CN
101318648 Dec 2008 CN
101604743 Dec 2009 CN
101292389 Sep 2010 CN
101969120 Feb 2011 CN
102163720 Aug 2011 CN
102214817 Oct 2011 CN
102623680 Aug 2012 CN
102820455 Dec 2012 CN
103094528 May 2013 CN
103456929 Dec 2013 CN
103746098 Apr 2014 CN
104108698 Oct 2014 CN
102509781 Nov 2015 CN
105680023 Jun 2016 CN
106207108 Dec 2016 CN
108475779 Aug 2018 CN
10 2014 211012 Dec 2015 DE
0126191 Nov 1984 EP
0649815 Apr 1995 EP
0861804 Sep 1998 EP
0891943 Jan 1999 EP
1049116 Nov 2000 EP
1052716 Nov 2000 EP
1514859 Mar 2005 EP
2117068 Nov 2009 EP
2330676 Jun 2011 EP
2983186 Feb 2016 EP
H02300222 Dec 1990 JP
H0390615 Apr 1991 JP
H03137010 Jun 1991 JP
H0459806 Feb 1992 JP
H04139174 May 1992 JP
H05117493 May 1993 JP
H05156121 Jun 1993 JP
H05311512 Nov 1993 JP
H05320955 Dec 1993 JP
H0859919 Mar 1996 JP
H08112539 May 1996 JP
H0963905 Mar 1997 JP
H09275042 Oct 1997 JP
H10297912 Nov 1998 JP
2001089119 Apr 2001 JP
2001278609 Oct 2001 JP
2003303588 Oct 2003 JP
2004067498 Mar 2004 JP
2004203715 Jul 2004 JP
2004221332 Aug 2004 JP
2004315283 Nov 2004 JP
2005132696 May 2005 JP
2005136397 May 2005 JP
2005187320 Jul 2005 JP
2006117475 May 2006 JP
2006248848 Sep 2006 JP
2006264993 Oct 2006 JP
2007039289 Feb 2007 JP
2007115749 May 2007 JP
2008007387 Jan 2008 JP
2008008539 Jan 2008 JP
2008094925 Apr 2008 JP
2009259803 Nov 2009 JP
5339107 Nov 2013 JP
2015130287 Jul 2015 JP
5796263 Oct 2015 JP
2016027222 Feb 2016 JP
2016100225 May 2016 JP
2016100226 May 2016 JP
2016132608 Jul 2016 JP
10-2004-0080010 Sep 2004 KR
10-2007-0030881 Mar 2007 KR
10-2014-0112451 Sep 2014 KR
WO 9501165 Jan 1995 WO
WO 0239468 May 2002 WO
WO 2004087285 Oct 2004 WO
WO 2004099073 Nov 2004 WO
WO 2005043653 May 2005 WO
WO 2009032104 Mar 2009 WO
WO 2010138760 Dec 2010 WO
WO 2011157013 Dec 2011 WO
WO 2014133070 Sep 2014 WO
WO 2014143213 Sep 2014 WO
WO 2022035879 Feb 2022 WO
WO 2022040327 Feb 2022 WO
WO 2022040328 Feb 2022 WO
WO 2022067030 Mar 2022 WO
WO 2022072715 Apr 2022 WO
Non-Patent Literature Citations (112)
Entry
Translation WO 2018165610; Sep. 13, 2018.
“Bestimmung der Porenvolumenverteilung und der spezifischen Oberfläche von Feststoffen durch Quecksilberintrusion,” Duetsche Norm, No. DIN 66133, XP007921315, Jun. 1993. (3 Pages).
“Chemical Basics of Polymer Insulation Materials: 3.6 Implementation Method of Stepwise Polymerization,” in Changming Li (eds.), HITP Harbin Institute of Technology Press, 2007, pp. 73 (With English Translation) (4 Pages).
Abraham et al., “A Polymer Electrolyte-Based Rechargeable Lithium/Oxygen Battery,” J. Electrochem. Soc. 143(1):1-5, Jan. 1996.
Abánades et al., “Experimental Analysis of Direct Thermal Methane Cracking,” International Journal of Hydrogen Energy 36(20):12877-12886, 2011.
Alcañiz-Monge et al., “Methane Storage in Activated Carbon Fibres,” Carbon 35(2):291-297, 1997.
Alias et al., “Silicon/graphite nanocomposite electrodes prepared by low pressure chemical vapor deposition,” Journal of Power Sources 174:900-904, 2007.
Andreasen et al., “Ueber die Beziehung zwischen Kornabstufung und Zwischenraum in Produkten aus losen Körnern (mit einigen Experimenten),” Kolloid-Zeitschrift 50(3):217-228, Mar. 1930, with translation of summary. (17 pages).
Babić et al., “Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction,” Electrochimica Acta 51:3820-3826, 2006.
Babić et al., “Characterization of carbon cryogel synthesized by sol-gel polycondensation and freeze-drying,” Carbon 42:2617-2624, 2004.
Babić et al., “Characterization of carbon cryogels synthesized by sol-gel polycondensation,” J. Serb. Chem. Soc. 70(1):21-31, 2005.
Barbieri et al., “Capacitance limits of high surface area activated carbons for double layer capacitors,” Carbon 43:1303-1310, 2005.
Barton et al., “Tailored Porous Materials,” Chem. Mater. 11:2633-2656, 1999.
Beattie et al., “High-Capacity Lithium-Air Cathodes,” J. Electrochem. Soc. 156(1):A44-A47, 2009.
Besenhard, “Handbook of battery materials,” Weinheim, Wiley-VCH, Weinheim, New York, 398-401, Dec. 31, 1999.
Bock et al., “Structural Investigation of Resorcinol Formaldehyde and Carbon Aerogels Using SAXS and BET,” Journal of Porous Materials 4:287-294, 1997.
Bomchil et al., “Pore Size Distribution in Porous Silicon Studied by Adsorption Isotherms,” Journal of the Electrochemical Society 130(7):1611-1614, Jul. 1983. (5 pages).
Buiel et al., “Li-insertion in hard carbon anode materials for Li-ion batteries,” Electrochimica Acta 45:121-130, 1999.
Burchell et al., “Low Pressure Storage of Natural Gas for Vehicular Applications,” The Engineering Society for Advancing Mobility Land Sea Air and Space, Government/Industry Meeting, Washington D.C., Jun. 19-21, 2000, 7 pages.
Cao et al., “Li-ion capacitors with carbon cathode and hard carbon/stabilized lithium metal powder anode electrodes,” Journal of Power Sources 213:180-185, Apr. 2012.
Chang et al., “Carbon Materials Comprising Enhanced Electrochemical Properties,” U.S. Appl. No. 14/988,625, filed Jan. 5, 2016, 112 pages.
Chmiola et al., “Anomalous Increase in Carbon Capacitance at Pore Sizes Less Than 1 Nanometer,” Science 313:1760-1763, Sep. 22, 2006.
Conway et al., “Partial Molal Volumes of Tetraalkylammonium Halides and Assignment of Individual Ionic Contributions,” Trans. Faraday Soc. 62:2738-2749, 1966.
Coppey et al., “Fluidized Bed Chemical Vapor Deposition of Silicon on Carbon Nanotubes for Li-Ion Batteries,” Journal of Nanoscience and Nanotechnology 11(9):8392-8395, 2011.
Czakkel et al., “Influence of drying on the morphology of resorcinol-formaldehyde-based carbon gels,” Microporous and Mesoporous Materials 86:124-133, 2005.
De Lange et al., “Adsorptive characterization of porous solids: Error analysis guides the way,” Microporous and Mesoporous Materials 200:199-215, Sep. 2014.
Ding et al., “How Conductivities and Viscosities of PC-DEC and PC-EC Solutions of LiBF4, LiPF6, LiBOB, Et4NBF4, and Et4NBF6 Differ and Why,” Journal of The Electrochemical Society 151(12):A2007-A2015, 2004.
Dinger et al., “Particle Packing III—Discrete versus Continuous Particle Sizes,” Interceram 41(5):332-334, 1992.
Dinger et al., “Particle Packing IV—Computer Modelling of Particle Packing Phenomena,” Interceram 42(3):150-152, 1993.
Débart et al., “α-MnO2 Nanowires: A Catalyst for the O2 Electrode in Rechargeable Lithium Batteries,” Agnew. Chem. Int. Ed. 47:4521-4524, 2008.
Eikerling et al., “Optimized Structure of Nanoporous Carbon-Based Double-Layer Capacitors,” Journal of The Electrochemical Society 152(1):E24-E33, 2005.
Endo et al., “Morphology and organic EDLC applications of chemically activated AR-resin-based carbons,” Carbon 40:2613-2626, 2002.
Feaver et al., “Activated carbon cryogels for low pressure methane storage,” Carbon 44:590-593, 2006.
Fotouhi et al., “A Low Cost, Disposable Cable-Shaped AI-Air Battery for Portable Biosensors,” J. Micromech. Microeng. 26:055011, 2016. (8 pages).
Fraas, “Using vibrations in fluidized beds For processes that do not require a high flow rate of sweep gas, the complex-mode vibration fluidized bed offers lower power needs, attrition rates, and elutriation rates than gas-fluidized beds or rotary kilns,” Mechanical Engineering:76-79, Jan. 7, 1998.
Fu et al., “Accurate characterization of full pore size distribution of tight sandstones by low-temperature nitrogen gas adsorption and high-pressure mercury intrusion combination method,” Energy Science & Engineering 9(1):80-100, Sep. 2020.
Furnas, “Grading Aggregates I—Mathematical Relations for Beds of Broken Solids of Maximum Density,” Industrial and Engineering Chemistry 23(9):1052-1058, 1931.
Gao et al., “Nitrogen-rich graphene from small molecules as high performance anode material,” Nanotechnology 25:415402, 2014, 8 pages.
Hahn et al., “A dilatometric study of the voltage limitation of carbonaceous electrodes in aprotic EDLC type electrolytes by charge-induced strain,” Carbon 44:2523-2533, 2006.
Hasegawa et al., “Preparation of carbon gel microspheres containing silicon powder for lithium ion battery anodes,” Carbon 42:2573-2579, 2004.
Hirscher et al., “Are carbon nanostructures an efficient hydrogen storage medium?” Journal of Alloys and Compounds 356-357:433-437, 2003.
Hogness et al. “The Thermal Decomposition of Silane,” J. Am. Chem. Soc. 58(1):108-112, 1936.
Hong et al., “Hydrogen evolution inhibition with diethylenetriamine modification of activated carbon for a lead-acid battery,” RSC Adv. 4:33574-33577, 2014.
Hsieh et al., “Synthesis of mesoporous carbon composite and its electric double-layer formation behavior,” Microporous and Mesoporous Materials 93:232-239, 2006.
Hu et al., “Effects of electrolytes and electrochemical pretreatments on the capacitive characteristics of activated carbon fabrics for supercapacitors,” Journal of Power Sources 125:299-308, 2004.
Huang et al., “Nitrogen-containing mesoporous carbons prepared from melamine formaldehyde resins with CaCl2 as a template,” J. Colloid Interface Sci. 363(1):193-198, 2011.
Indo German Carbons Limited, “Activated Carbon,” Apr. 2009, URL=http://www.igcl.com/php/activated_carbon.php, download date Nov. 29, 2018, 3 pages.
Inomata et al., “Natural gas storage in activated carbon pellets without a binder,” Carbon 40:87-93, 2002.
Jariwala et al., “In Situ Gas-Phase Hydrosilylation of Plasma-Synthesized Silicon Nanocrystals,” ACS Applied Materials & Interfaces 3:3033-3041, Jul. 2011. (9 pages).
Job et al., “Carbon aerogels, cryogels and xerogels: Influence of the drying method on the textural properties of porous carbon materials,” Carbon 43:2481-2494, 2005.
Job et al., “Highly dispersed platinum catalysts prepared by impregnation of texture-tailored carbon xerogels,” Journal of Catalysis 240:160-171, 2006.
Job et al., “Synthesis of transition metal-doped carbon xerogels by solubilization of metal salts in resorcinol-formaldehyde aqueous solution,” Carbon 42:3217-3227, 2004.
Katsaros et al., “Preparation and characterisation of gas selective microporous carbon membranes,” Microporous and Mesoporous Materials 99:181-189, 2007.
Kim et al., “Adsorption of phenol and reactive dyes from aqueous solution on carbon cryogel microspheres with controlled porous structure,” Microporous and Mesoporous Materials 96:191-196, 2006.
Kim et al., “Correlation between the capacitor performance and pore structure,” Tanso 221:31-39, 2006 (English Abstract).
Kocklenberg et al., “Texture control of freeze-dried resorcinol-formaldehyde gels,” Journal of Non-Crystalline Solids 225:8-13, 1998.
Kowalczyk et al., “Estimation of the pore-size distribution function from the nitrogen adsorption isotherm. Comparison of density functional theory and the method of Do and co-workers,” Carbon 41:1113-1125, 2003.
Leventis et al., “Click synthesis of monolithic silicon carbide aerogels from polyacrylonitrile-coated 3D silica networks,” Chemistry of Materials 22(9):2790-2803, Mar. 2010. (14 pages).
Lozano-Castelló et al., “Influence of pore structure and surface chemistry on electric double layer capacitance in non-aqueous electrolyte,” Carbon 41:1765-1775, 2003.
Lozano-Castelló et al., “Powdered Activated Carbons and Activated Carbon Fibers for Methane Storage: A Comparative Study,” Energy & Fuels 16:1321-1328, 2002.
McEwen et al., “Nonaqueous Electrolytes and Novel Packaging Concepts for Electrochemical Capacitors,” The 7th International Seminar on Double Layer capacitors and Similar Energy Storage Devices, Deerfield Beach, FL Dec. 8-10, 1997, 56 pages.
Miller, “Pulse Power Performance of Electrochemical Capacitors: Technical Status Of Present Commercial Devices,” Proceedings of the 8th International Seminar on Double Layer Capacitors and Similar Energy Storage Devices, Deerfield Beach, Florida, Dec. 7-9, 1998, 9 pages.
Mäkilä et al., “Confinement Effects on Drugs in Thermally Hydrocarbonized Porous Silicon,” Langmuir 30:2196-2205, Feb. 2014. (10 pages).
Naoi et al., “Second generation ‘nanohybrid supercapacitor’: Evolution of capacitive energy storage devices,” Energy Environ. Sci. 5:9363-9373, 2012.
Nishihara et al., “Preparation of resorcinol—formaldehyde carbon cryogel microhoneycombs,” Carbon 42:899-901, 2004.
Ogasawara et al., “Rechargeable LI2O2 Electrode for Lithium Batteries,” Journal of the American Chemical Society 128(4):1390-1393, 2006.
Otowa et al., “Production and adsorption characteristics of MAXSORB: High-surface-area active carbon,” Gas Separation and Purification 7(4):241-245, 1993.
Pekala et al., “Aerogels derived from multifunctional organic monomers,” Journal of Non-Crystalline Solids 145:90-98, 1992.
Pekala et al., “Structure of Organic Aerogels. 1. Morphology and Scaling,” Macromolecules 26:5487-5493, 1993.
Pekala, “Organic aerogels from the polycondensation of resorcinol with formaldehyde,” Journal of Materials Science 24:3221-3227, 1989.
Perrin et al., “Methane Storage within Dry and Wet Active Carbons: A Comparative Study,” Energy & Fuels 17:1283-1291, 2003.
Pimenta et al., “Studying disorder in graphite-based systems by Raman spectroscopy,” Phys. Chem. Chem. Phys. 9:1276-1291, 2007.
Pojanavaraphan et al., “Prevulcanized natural rubber latex/clay aerogel nanocomposites,” European Polymer Journal 44:1968-1977, 2008.
Pääkkö, “Long and entangled native cellulose I nanofibers allow flexible aerogels and hierarchically porous templates for functionalities,” Soft Matter 4:2492-2499, 2008.
Qu et al., “Studies of activated carbons used in double-layer capacitors,” Journal of Power Sources 74:99-107, 1998.
Ravikovitch et al., “Unified Approach to Pore Size Characterization of Microporous Carbonaceous Materials from N2, Ar, and CO2 Adsorption Isotherms,” Langmuir 16:2311-2320, 2000.
Read et al., “Oxygen Transport Properties of Organic Electrolytes and Performance of Lithium/Oxygen Battery,” J. Electrochem. Soc. 150(10):A1351-A1356, 2003.
Read, “Characterization of the Lithium/Oxygen Organic Electrolyte Battery,” J. Electrochemical Soc. 149(9):A1190-A1195, 2002.
Read, “Ether-Based Electrolytes for the Lithium/Oxygen Organic Electrolyte Battery,” J. Electrochem. Soc. 153(1):A96-A100, 2006.
Reichenauer et al., “Microporosity in carbon aerogels,” Journal of Non-Crystalline Solids 225:210-214, 1998.
Salitra et al., “Carbon Electrodes for Double-Layer Capacitors I. Relations Between Ion and Pore Dimensions,” Journal of The Electrochemical Society 147(7):2486-2493, 2000.
Setoyama et al., “Simulation Study On The Relationship Between A High Resolution αs-Plot And The Pore Size Distribution For Activated Carbon,” Carbon 36(10):1459-1467, 1998.
Simon et al., “Materials for electrochemical capacitors,” Nature Materials 7:845-854, Nov. 2008.
Sivakkumar et al., “Evaluation of Lithium-ion capacitors assembled with pre-lithiated graphite anode and activated carbon cathode,” Electrochimica Acta 65:280-287, Jan. 2012.
Tamon et al., “Influence of freeze-drying conditions on the mesoporosity of organic gels as carbon precursors,” Carbon 38:1099-1105, 2000.
Tamon et al., “Preparation of mesoporous carbon by freeze drying,” Carbon 37:2049-2055, 1999.
Tonanon et al., “Influence of surfactants on porous properties of carbon cryogels prepared by sol-gel polycondensation of resorcinol and formaldehyde,” Carbon 41:2981-2990, 2003.
Toyo Tanso Carbon Products, “Special Graphite and Compound Material Products,” Toyo Tanso Co., Ltd. Catalog published 2008.
Toyo Tanso, “Graphite Applications,” Toyo Tanso Co., Ltd. Catalog published 1998. (Machine Translation Attached).
Toyo Tanso, “Isotropic Graphite Engineering Data,” Toyo Tanso Co., Ltd. Catalog published 1994.
Toyo Tanso, “Isotropic Graphite Technical Data,” Toyo Tanso Co., Ltd. Catalog published 1997.
Ue, “Mobility and Ionic Association of Lithium and Quaternary Ammonium Salts in Propylene Carbonate and γ-Butyrolactone,” J. Electrochem. Soc. 141(12):3336-3342, Dec. 1994.
Wang et al., “MnO Nanoparticles Interdispersed in 3D Porous Carbon Framework for High Performance Lithium-Ion Batteries,” ACS Applied Materials & Interfaces 3:12713-12718, 2014.
Wang et al., “Nanostructured Si-C composite anodes for lithium-ion batteries,” Electrochemistry Communications 6:689-692, Jun. 2004. (4 pages).
Wei et al., “A novel electrode material for electric double-layer capacitors,” Journal of Power Sources 141:386-391, 2005.
Williford et al., “Air electrode design for sustained high power operation of Li/air batteries,” Journal of Power Sources 194:1164-1170, 2009.
Woo et al., “Silicon Embedded Nanoporous Carbon Composite for the Anode of Li Ion Batteries,” Journal of The Electrochemical Society 159(8):A1273-A1277, 2012.
Wu et al., “Engineering Empty Space between Si Nanoparticles for Lithium-Ion Battery Anodes,” Nano Letters 12:904-909, Jan. 2012. (6 pages).
Wu et al., “Fabrication and nano-structure control of carbon aerogels via a microemulsion-templated sol-gel polymerization method,” Carbon 44:675-681, 2006.
Xiang et al., “Beneficial effects of activated carbon additives on the performance of negative lead-acid battery electrode for high-rate partial-state-of-charge operation,” Journal of Power Sources 241:150-158, 2013.
Xie et al., “Pore size control of Pitch-based activated carbon fibers by pyrolytic deposition of propylene,” Applied Surface Science 250:152-160, 2005.
Xu et al., “Comparison of sizing small particles using different technologies,” Powder Technology 132:145-153, 2003.
Xu et al., “Optimization of Nonaqueous Electrolytes for Primary Lithium/Air Batteries Operated in Ambient Environment,” Journal of the Electrochemical Society 156(10):A773-A779, 2009.
Xu et al., “Synthesis of mesoporous carbon and its adsorption property to biomolecules,” Microporous and Mesoporous Materials 115:461-468, 2008.
Yamamoto et al., “Control of mesoporosity of carbon gels prepared by sol-gel polycondensation and freeze drying,” Journal of Non-Crystalline Solids 288:46-55, 2001.
Yamamoto et al., “Porous properties of carbon gel microspheres as adsorbents for gas separation,” Carbon 42:1671-1676, 2004.
Yamamoto et al., “Preparation and characterization of carbon cryogel microspheres,” Carbon 40:1345-1351, 2002.
Yang et al., “Preparation of highly microporous and mesoporous carbon from the mesophase pitch and its carbon foams with KOH,” Carbon 42:1872-1875, 2004.
Zhang et al., “Discharge characteristic of non-aqueous electrolyte Li/O2 battery,” Journal of Power Sources 195:1235-1240, 2010.
Zhang et al., “Highly Reversible and Large Lithium Storage in Mesoporous Si/C Nanocomposite Anodes with Silicon Nanoparticles Embedded in a Carbon Framework,” Adv. Mater. 26:6749-6755, 2014.
Zhao et al., “Facile Synthesis for LiFePO4 Nanospheres in Tridmensional Porous Carbon Framework for Lithium Ion Batteries,” The Journal of Physical Chemistry 115:2888-2894, 2011.
Zhao et al., “Highly-Ordered Mesoporous Carbon Nitride with Ultrahigh Surface Area and Pore vol. as a Superior Dehydrogenation Catalyst,” Chem. Mater. 26(10):3151-3161, 2014.
Related Publications (1)
Number Date Country
20240030410 A1 Jan 2024 US
Provisional Applications (2)
Number Date Country
63078806 Sep 2020 US
63075566 Sep 2020 US
Continuations (3)
Number Date Country
Parent 18156939 Jan 2023 US
Child 18364411 US
Parent 17715840 Apr 2022 US
Child 18156939 US
Parent 17405870 Aug 2021 US
Child 17715840 US
Continuation in Parts (1)
Number Date Country
Parent 16996694 Aug 2020 US
Child 17405870 US