This invention is directed to a package that has a type of hologram image on at least a part of its exterior surface, and the process to produce this hologram image that has on the exterior surface of a package. More particularly, this invention is directed to producing a hologram image on paper, paperboard, plastics and related substrates that can be used to package products.
Holograms have been used to enhance the appearance of packages for many years. They have been formed on labels and substrates that are applied to and are used as a layer on the surface of packages, such as cartons. However, the conventional hologram image on packages is expensive and usually requires the production of a hologram containing laminate film and the bonding of this film to a package surface. This requires several processing steps and costly materials. It would be more efficient and less costly to form the hologram on the packaging material in line with the printing of other image and information onto the packaging material.
In U.S. Pat. No. 5,889,598 there is disclosed the printing of a hologram onto a surface followed by the printing of another image onto the same surface. The hologram design is embossed onto the surface followed by a metallizing of the hologram design surface, in turn followed by the cutting of the surface into sheets for subsequent printing of other image and information. This process requires the subsequent metallizing of the embossed hologram design. This metallizing is by a relatively slow vapor deposition process. U.S. Pat. No. 5,003,915 discloses the forming of a hologram directly onto the desired end product paper or other sheet material. However, after the embossing of a hologram design there is a required step of metallizing the hologram surface. This could be by vapor deposition to produce a reflective film or refractive layer onto the hologram. A protective layer can be coated over this hologram. U.S. Pat. No. 6,979,487 discloses the printing of textured pattern over a substrate. A reflective ink or foil can be deposited or laminated onto this textured pattern layer. This produces an effect of depth and dimensionality. This is interesting but does not disclose the production of a hologram. This process would be inoperable to produce a holographic image. U.S. Pat. No. 6,638,386 discloses the technique of forming a holographic image or a diffraction grating image onto a composite sheet and the subsequent attachment of this sheet to a substrate. This involves the operation of separately forming the hologram on a composite sheet and applying this composite sheet onto a substrate to produce the finished hologram on a package or other item. All of these processes have the differing drawbacks. However, all are less efficient than the holograms on a package surface produced by the present processes.
The present processes produce a hologram image directly on the package surface solely through printing steps. Further, no subsequent metallizing steps are required. Such steps which usually involve the vapor deposition of a metal, such as aluminum, onto a hologram surface are relatively slow as compared to printing techniques and require specialized equipment. In the present processes a hologram image is produced on a substrate solely through the use of printing techniques and equipment.
The present invention comprises a hologram image directly on packaging material, and the process to produce this hologram image directly on the packaging material. The process comprises having a paper, paperboard or plastic surface, which in one embodiment can be a substantially white paperboard surface, coating onto at least a part of this surface a polymeric radiation curable coating that contains a particulate metal component, curing this polymeric radiation curable coating, coating the cured polymeric radiation curable coating containing the particulate metal with a radiation curable and substantially transparent polymer coating, contacting this radiation curable substantially transparent coating with the negative of a hologram on a shim, and at least partially curing the radiation curable coating while the shim carrying the negative of the hologram is in contact with this coating. The combination of these two coatings and the negative of the hologram produce a hologram image in the areas where there also is an underlying particulate metal coating. An effective hologram image is formed by the technique of at least partially curing the substantially transparent radiation curable coating while the shim is in contact with this coating.
In a preferred embodiment a substantially white paperboard stock comprising blanks for the production of carton comprising a blank for the production of cartons is in a first step coated over at least a part of its surface with a coating that contains a particulate metal, this coating is cured, one or more image and/or information layers are then coated onto the cured particulate metal coated layer and each cured, coating these image and/or in formation layers with a substantially transparent radiation curable coating, and contacting this substantially transparent radiation curable coating with a shim that contains the negative of a hologram, and at least partially curing the radiation curable coating while the shim is in contact with the radiation curable coating. In this preferred embodiment the coatings are applied to the paperboard stock using printing techniques. A preferred technique is the use of flexographic printing. However, other commercially available printing techniques and equipment can be used.
After the paper or paperboard stock has been printed and contains the hologram it is finished by forming it into a package. The paper or paperboard stock usually will be in the form of a continuous sheet. The paper or paperboard stock can be use directly to make packages or it can be formed into cartons. To make cartons the continuous sheet will be formed into individual carton blanks. The carton blanks are shipped to the place where a product is to be packaged and placed in the magazine of a carton making and filling machine. The cartons containing a product are filled with a product, sealed and then usually placed in corrugated shipping cartons.
The invention will be described now in more detail in its preferred embodiments. Modifications can be made to the hologram materials and the processes of their manufacture, however all such materials and processes will be within the concepts disclosed herein.
The substrate material on which the hologram is formed, is in the preferred embodiments, a paper material which includes various grades of paper and paperboard. However, plastics and other substrate materials can be used. When a paper, the paper material in this preferred embodiment will have a thickness of about 0.001 inch (0.00254 cm) to about 0.005 inch (0.0127 cm), and when a paperboard will have a thickness of about 0.010 inch (0.0254 cm)to about 0.050 inch (0.127 cm). Plastics and other substrate materials will have a range of thicknesses. The substrate material can be of essentially any color or hue. However, it is preferred that the substrate material be from a brown paperboard color to white. If white the whiteness of the substrate material preferably will be about TAPPI Whiteness of about 70 or better and preferably about 75 to 95.The substrate material can be a CCNB (Clay Coated News Back) recycled paperboard or an SBS (Solid Bleach White Sulfate) virgin paperboard. White or lightly colored substrate materials are preferred. The preferred processes for forming the hologram on the substrate material are printing processes such as flexographic printing processes. Flexographic printing processes have been found to be very useful. In this process the substrate material is fed to a set of rolls, usually the first set of rolls, which will coat the substrate material with a radiation curable thermoplastic polymer composition containing a particulate metal having a particle size of about 5 to 40 microns, and preferably about 10 to 25 microns. The useful particulate metals include aluminum, silver and zinc. These are applied using a solvent/polymer carrier mixture. Useful coating compositions are ULTRASTAR UV FP-8209 flexo silver having a particulate metal content of 3.25% applied using a 200 to 300 analox flexo roller. Another useful coating composition is ULTRASTAR UV SP-8700 screen print silver having a pigment content of 2.5% applied using a Rotomesh 150 to 250 line mesh screen. The analox flexo roller will deposit a wet polymer film coating of about 2 to 12 microns while the Rotomesh screen will deposit a wet polymer film coating of about 12 to 20 microns. In general a wet film coating of about 1 to 40 microns will be useful. The viscosity of the polymer coating products will be about 150 to 350 cps. The UTRASTAR products are available from Eckhart America LP of Painsville, Ohio. This coating can be over the entire surface of the substrate material, but for reasons of economy it only will be in the areas that are to contain a hologram. This usually will be less than 50% of the substrate material surface.
Prior to the application of the radiation curable thermoplastic containing the particulate metal, a primer can be applied to the material substrate which usually will be a paper or a paperboard. This will seal the substrate material and provide a better base for the radiation curable thermoplastic polymer containing the particulate metal. This primer coating can be a water based acrylic lacquer. Also useful in place of a primer is a lamination of a polyethylene terephthalate (PET) film which can have a white surface of a TAPPI Whiteness of about 75 to 95.
After the application and radiation curing of the radiation curable thermoplastic polymer containing the particulate metal the substrate can be printed with image and information material. The radiation curing usually will be through the use of commonly used 300 watt ultraviolet lamps. They will be chosen emit a range of wavelengths depending on the polymers to be set. Electron beam radiation also can be used. However, ultraviolet radiation is preferred. The printing with image and information material, if to be used, usually will be in a number of printing steps since different printing rolls will be required for each image color. The inks used will preferably be ultraviolet curing inks which can be cured within seconds using 300 watt ultraviolet lamps. The substrate material is not printed with image and information material in the areas where there is to be a hologram. The cured metal coating will be exposed in these areas. This is needed for the application of an effective hologram in a subsequent step.
In a next step the substrate material with the above cured coatings is coated with a substantially transparent radiation curable coating. This preferably is a high gloss coating and is 100% radiation curable. The viscosity will be in the range of about 150 to 350 cps. The application weight is about 0.04 lbs (18.1 gms.) to about 0.12 lbs (54.4 gms) per 1000 square feet (93 sq.m). A useful coating material is CORKCURE 1093RHG-10 from Cork Industries, Inc. in Foxcroft, Pa. This is an ultra high gloss, solvent-less coating for lithographic and flexographic coating equipment. It is a 100% ultraviolet radiation curable coating having a viscosity of 210(+/−20) cps. It is applied to the substrate material at a last set of flexographic rolls. It is applied at a weight of 0.06 lbs (27.2 gms.) to 0.09 lbs (41 gms) per 1000 square feet (93 sq.m). It is curable at 150 feet per minute using a 300 watt ultraviolet source. Just subsequent to the substrate material being coated, and prior to the coating being cured, the coating is contacted with the negative of a hologram. This negative of a hologram is a micro-grid which is on a shim that is a part of the flexographic roll, which usually is the final roll. There can be more than one shim. The shim is a substantially transparent plastic, such as a thermoplastic. A useful material for the shim is polypropylene. However, other substantially transparent polymeric materials such as polyethylene terephthalate can be used. The substantially transparent radiation curable coating is at least partially cured when the shim is in contact with this coating, with the curing bring completed just after contact with this coating. There can be a protective coating over the coating containing the hologram as long as the hologram is not affected.
Assuming that the coated and hologram containing substrate material is to be used to make packaging cartons the decorative substrate material from the printing operations is then fed to a carton blank forming machine. This machine forms carton blanks by cutting the substrate material to length and trimming the edges to form the foldable flaps. Weakened fold points to fold the panels and end foldable flaps into a carton also are formed. The foldable flaps form the ends of the carton. These carton blanks can be loaded into the magazine of a carton forming machine which is in-line with the equipment making the primary package that is to be packaged in the carton. The primary package can be a tube, bottle or any other container, or the product itself if the product is a solid. This has been found to be useful in the packaging of dentifrice products.
The primary system for UV curing is based on acrylate polymers and monomers and cured through free radical polymerization. The acrylate polymers and monomers are high boiling which reduces VOC contamination. These systems include pigments, oligomers, reactive acrylated resins, monomers that usually are multifunctional, photoinitiators and additives. The UV energy is absorbed by the photoinitiators to produce free radicals which in turn initiate the polymerization of the acrylate polymers and monomers. Useful photoinitiators include benzoin derivatives, benzil ketals, acetophenone derivatives and benzophenone. The particular acrylate systems are chosen for a particular process depending on the compatibility with other components, the speed of the cure needed, cost, and end product appearance. Useful systems for UV curing utilizing acrylate chemistry are disclosed U.S. Pat. No. 3,418,292, which is incorporated herein in its entirety by reference. Cationic curing systems also can be used. These are based on vinyl ethers and epoxy resins for the oligomers, reactive resins, and monomers. However systems based on acrylate chemistry are preferred.
Another system that can be used is electron beam curing. The compositions for electron beam curing are based on acrylate chemistry similar to the free radical induced polymerization compositions. The primary difference is that a photoinitiator is not used. The electron beam causes the acrylate double bonds to directly cleave forming free radicals which initiate the polymerization. Although fast curing and have a low odor there is the processing drawback in that the curing must be done in an oxygen free atmosphere. Oxygen inhibits free radical formation. This requires the use of an inert gas. Electron beam systems are disclosed in U.S. Pat. No. 3,948,739, which is incorporated herein in its entirety by reference.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US07/87348 | 12/13/2007 | WO | 00 | 6/15/2009 |
| Number | Date | Country | |
|---|---|---|---|
| 60869983 | Dec 2006 | US |