Patent Application
20190225798
The present disclosure pertains to housings for consumer devices made from polycarbonate compositions designed to have high flow, high impact and good release properties.
Trends in plastic part design are driving toward more thin, more complex parts with advanced styling. Materials with good flow and sufficient release are required to achieve such a narrow and complex structure with enhanced styling, while also maintaining high impact performance.
These and other shortcomings are addressed by aspects of the present disclosure.
The disclosure concerns housings for a consumer device including: from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer; from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer; and from about 0.05 wt % to about 1.0 wt % of at least one release agent. The housing exhibits: a melt volume flow rate (MVR) of at least about 25 cubic centimeters per 10 minutes (cm3/10) min, as determined according to ISO 1133 at 300 degrees Celsius (° C.) using a 1.2 kilogram (kg) load; a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 millimeter (mm); and a tensile yield strength retention of 80% and higher after exposure of an ISO tensile bar for 24 hours to sunscreen under 1% strain compared to a non-exposed reference tested according to ISO 22088-3. The disclosure also concerns methods for forming a housing for a consumer device.
The compositions and methods described herein may be used to form articles including, but not limited to, a housing for a consumer device, such as a cellular phone, a tablet computer, a laptop computer, a desktop computer, a television, a battery, or an adapter.
For some applications in the market that require low temperature impact performance, blends of polycarbonate/polysiloxanes are used because compositions including these blends may have high impact and good aesthetics in addition to very good release properties compared with normal polycarbonate. Current commercial products are based on a blend of polycarbonate and a polysiloxane copolymer in different ratios; depending on these ratios the properties of the final product, such as release performance, can vary.
It has been surprisingly found that blends including (i) a polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5.0 wt % based on the total weight of the blend and (ii) at least one polycarbonate have an improved balance of high flow, high impact at room temperature and lower temperatures, compared to substantially similar compositions without the polycarbonate-siloxane or polycarbonates with alternative impact modifiers, such as acrylic or silicone based core-shell rubbers. In addition, these compositions demonstrate good retention of tensile properties after prolonged exposure to chemicals like sunscreen.
In making plastic parts, materials are generally fed into the heated barrel of an injection molding machine, melted, and then injected under high pressure into a mold cavity. After this melt cools, a plastic component is realized. The process of cooling shrinks the melt on the mold core, necessitating an ejection force to demold the component from the mold of the machine.
The disclosed thermoplastic compositions can exhibit, for example, improved mechanical, or impact, thermal, or flow and release, and/or morphological, or stylistic properties, without adversely affecting other mechanical and thermal properties.
In making plastic parts, materials are generally fed into the heated barrel of an injection molding machine, melted, and then injected under high pressure into a mold cavity. After this melt cools, a plastic component is realized. The process of cooling shrinks the melt on the mold core, necessitating an ejection force to demold the component from the mold of the machine.
In the ejection stage of injection molding the parts are mechanically forced to separate from the molding surfaces (especially from the cores). If the force required to remove the mold is too high (e.g., due to the strength with which the plastic sticks to the mold core), the machine's ejector pins may punch through and damage the plastic component. Ideally, the molded part should slip down easily from the mold core. The friction coefficient refers to the sticking or adhesive force that exists between the plastic part and the metal surface of the mold. Reduce this force, and demolding will be more efficient. Friction is normally understood as the resistance offered by bodies in contact to relative motion. In injection molding the bodies in contact are steel molding surfaces and polymer moldings.
Aesthetics and functionality of products may require the use of small draft angles. Small draft angles, however, lead to an increase of the ejection forces.
In polymer injection molding, adhesion force(s) between part and the tool are a complex interaction due to the dependency of part geometry and process parameters such as temperature and pressure. Ejection force, also called release force, has been identified in literature as a total friction between the tool and the polymer interface.
Holding pressure and surface temperature may influence the ejection force.
It is known that very good, polished, mirror-like surfaces can be difficult to separate by the local formation of vacuum. The testing of demolding, particularly for those developing raw materials, has focused on speeding up cycle times and reducing the amount of release agents used in the thermoplastic. The typical percentage of a release agent in the melt is about 1.0%, or even about 0.5%. If this amount of release agent can be reduced to about 0.2%, a reduction of problems observed in the molding process that relate to high contents of release agents can be avoided.
A high gloss surface needs more draft than rough surfaces. Amongst polycarbonates, typical market solutions for bezels include use of PC having a melt flow volume rate (MVR) of about 8 up to about 20 cm3/10 min as tested according to ISO 1133. Such polycarbonates are available from Covestro and SABIC. PC resins with an MVR of greater than about 35 cm3/10 min are not currently used because the low Mw results in brittleness and consequently to demolding failures or in-use part failures.
Friction between the thermoplastic part and the injection mold core not only depends on the mechanical relationship between the two surfaces, but also on an adhesive component inherent in the properties of the two materials at processing conditions.
While the deformation (or mechanical) component of friction tends to be more easily defined, the adhesion component is rather more complex.
For polymers, the surface forces consist of van der Waals, coulombic and possibly hydrogen bonding forces. The higher the surface free energy of the polymer, the greater the adhesive force.
Equations developed for the ejection force for deep injection molded parts derive from the friction-based concept FR=f×pA×A, where FR is the ejection (or release) force, f is the coefficient of friction between the mold and the part, pA is the contact pressure of the part against the mold core, and A is the area of contact.
Contact pressure can be defined as p=E(T)×Δdr×sm, and therefore ejection force is: FR=Cf×E(T)Δdr×sm×2πL, where E(T) is the modulus of the thermoplastic part material at ejection temperature, Δdr is the relative change in diameter of the part immediately after ejection, sm, is the thickness of the part, and L is the length of the part in contact with the mold core.
Statistical analyses for demolding forces are used to determine the effects of packing time, cooling time and packing pressure on ejection force for materials or grade combinations. One common analysis is to do injection molding of sleeves, then measure the ejection force necessary to remove the sleeve from the core. At the opening of the mold, the part remains on the core due to the material contraction. At the end of the opening stroke, the ejector pins detach the part from the core. The force applied to the part for demolding is registered as the Mold Release Force (FR).
The friction properties of pairs of materials are usually represented by the coefficient of friction. The coefficient of friction is defined (e.g. in ASTM G40 test standard) as: μ=F/N In which, F is friction force and N is normal contact force. The same standard defines a coefficient of static friction, μs, corresponding to the maximum force that must be overcome to initiate macroscopic motion between the two bodies. A coefficient of kinetic friction is obtained from the average friction force necessary to maintain the macroscopic relative motion between the two bodies. It is represented by μk.
The plastic tends to stick over the surface of the cores. For example, the sidewalls that are perpendicular to the mold's parting line must be drafted. Draft angles increase the shape dimensions. Other areas that require draft angles include mounting flanges, gussets, holes, hollow bosses, louvers other holes or ribs. As a result, dimensions like rib height are limited, and the wall thickness rib ratio is correlated to the draft angle. The plastic design rules define the shape of: a hole, a core, the rib height, the height of a side wall or the wall thickness rib ratio.
Mold drafts facilitate part removal from the mold. The draft is generally in an offset angle that is parallel to the mold opening and closing. The ideal draft angle for a given part depends on the depth of the part in the mold and its required end-use function. The mold part line will need to be located in a way that splits the draft in order to minimize it. If no draft is acceptable due to design/styling considerations, a side action mold (side slider) may be required in some aspects.
As a result, designers typically design parts according to the general plastic rules to ensure good manufacturing performance and aesthetics of the part.
The terms “polycarbonate” or “polycarbonates” as used herein include copolycarbonates, homopolycarbonates, (co)polyester carbonates and combinations thereof.
The term polycarbonate can be further defined as compositions have repeating structural units of the formula (1):
in which at least 60 percent of the total number of R1 groups are aromatic organic radicals and the balance thereof are aliphatic, alicyclic, or aromatic radicals. In a further aspect, each R1 is an aromatic organic radical and, in particular, a radical of the formula (2):
-A1-Y1-A2- (2),
wherein each of A1 and A2 is a monocyclic divalent aryl radical and Y1 is a bridging radical having one or two atoms that separate A1 from A2. In various aspects, one atom separates A1 from A2. For example, radicals of this type include, but are not limited to, radicals such as —O—, —S—, —S(O)—, —S(O2)-, —C(O)—, methylene, cyclohexyl-methylene, 2-[2.2.1]-bicycloheptylidene, ethylidene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cyclododecylidene, and adamantylidene. The bridging radical Y1 may be a hydrocarbon group or a saturated hydrocarbon group such as methylene, cyclohexylidene, or isopropylidene.
Polycarbonate materials include materials disclosed and described in U.S. Pat. No. 7,786,246, which is hereby incorporated by reference in its entirety for the specific purpose of disclosing various polycarbonate compositions and methods for manufacture of same. Polycarbonate polymers can be manufactured by means known to those skilled in the art.
Some polycarbonates are linear bisphenol-A polycarbonates produced by melt polymerization. The melt polycarbonate process is based on continuous reaction of a dihydroxy compound and a carbonate source in a molten stage. The reaction can occur in a series of reactors where the combined effect of catalyst, temperature, vacuum, and agitation allows for monomer reaction and removal of reaction by-products to displace the reaction equilibrium and effect polymer chain growth. A common polycarbonate made in melt polymerization reactions is derived from bisphenol A (BPA) via reaction with diphenyl carbonate (DPC). This reaction can be catalyzed by, for example, tetra methyl ammonium hydroxide (TMAOH) or tetrabutyl phosphonium acetate (TBPA), which can be added into a monomer mixture prior to being introduced to a first polymerization unit and sodium hydroxide (NaOH), which can be added to the first reactor or upstream of the first reactor and after a monomer mixer.
The melt polycarbonate in some aspects may have a molecular weight (Mw) of about 15,000 to about 40,000 Dalton when measured using GPC methods on a polycarbonate basis. The melt polycarbonate product may have an endcap level of about 45% to about 80%. Some polycarbonates have an endcap level of about 45% to about 75%, about 55% to about 75%, about 60% to about 70% or about 60% to about 65%. Certain polycarbonates have at least 200 ppm of hydroxide groups. Certain polycarbonates have 200-1100 parts per million (ppm) or 950 to 1050 ppm hydroxide groups.
The polycarbonate polymer may contain endcapping agents. Any suitable endcapping agents can be used provided that such agents do not significantly adversely impact the desired properties of the polycarbonate composition (transparency, for example). Endcapping agents include mono-phenolic compounds, mono-carboxylic acid chlorides, and/or mono-chloroformates. Mono-phenolic endcapping agents are exemplified by monocyclic phenols such as phenol and C1-C22 alkyl-substituted phenols such as p-cumyl-phenol, resorcinol monobenzoate, and p- and tertiary-butyl phenol; and monoethers of diphenols, such as p-methoxyphenol.
Apart from the main polymerization reaction in polycarbonate production, there is a series of side reactions consisting of chain rearrangements of the polymer backbone that lead to branching that are often referred to as Fries rearrangement. Some of these polycarbonates include from about 200 to about 2000 ppm, or from about 250 to about 1800 ppm Fries products. The Fries species specifically found in bisphenol A melt polycarbonates include the ester type of structures A, B, and C.
A. Linear Fries:
B. Branched Fries:
C. Acid Fries:
The Fries reaction is induced by the combined effect of basic catalysts, temperature, and residence time, which generally result in melt-produced polycarbonates being branched as compared with the interfacial polycarbonates since their manufacturing temperatures are lower. Because high branching levels in the resin can have a negative effect on the mechanical properties of the polycarbonate (for example, on impact strength), a product with lower branched Fries product may be desirable.
In some aspects the polycarbonate polymer is a linear bisphenol-A polycarbonate produced by a melt polymerization process. In other aspects the polycarbonate polymer is a linear bisphenol-A polycarbonate produced by an interfacial polymerization process.
In some compositions, the polycarbonate polymer comprises at least one polycarbonate polymer having a molecular weight (Mw) of at least 20,000 grams per mole (g/mol) and a second polycarbonate polymer have a molecular weight (Mw) of less than 20,000 g/mol. In some compositions, the molar ratio of said first polycarbonate polymer to said second polycarbonate polymer is about 1.4:1 to about 3.2:1. In other compositions, the molar ratio of said first polycarbonate polymer to said second polycarbonate polymer is about 1.5:1 to about 3.0:1.
In certain aspects, polycarbonate produced by interfacial polymerization may be utilized. In some processes, bisphenol A and phosgene are reacted in an interfacial polymerization process. Typically, the disodium salt of bisphenol A is dissolved in water and reacted with phosgene which is typically dissolved in a solvent that not miscible with water (such as a chlorinated organic solvent like methylene chloride).
In some aspects, the polycarbonate comprises interfacial polycarbonate having a weight average molecular weight of from about 10,000 Daltons to about 50,000 Daltons, preferably about 15,000 to about 45,000 Daltons. Some interfacial polycarbonates have an endcap level of at least 90% or preferably 95%.
As used herein, the term “polycarbonate-polysiloxane copolymer” is equivalent to polysiloxane-polycarbonate copolymer, polycarbonate-polysiloxane polymer, or polysiloxane-polycarbonate polymer. In various aspects, the polycarbonate-polysiloxane copolymer can be a block copolymer comprising one or more polycarbonate blocks and one or more polysiloxane blocks. In some aspects, the polysiloxane-polycarbonate copolymer comprises polydiorganosiloxane blocks comprising structural units of the general formula (3) below:
wherein the polydiorganosiloxane block length (E) is from 10 to 100, preferably 20 to 60, more preferably 30 to 50; wherein each R group can be the same or different, and is selected from a C1-13 monovalent organic group; wherein each M can be the same or different, and is selected from a halogen, cyano, nitro, C1-C8 alkylthio, C1-C8 alkyl, C1-C8 alkoxy, C2-C8 alkenyl, C2-C8 alkenyloxy group, C3-C8 cycloalkyl, C3-C8 cycloalkoxy, C6-C10 aryl, C6-C10 aryloxy, C7-C12 aralkyl, C7-C12aralkoxy, C7-C12 alkylaryl, or C7-C12 alkylaryloxy, and where each n is independently 0, 1, 2, 3, or 4.
The polysiloxane-polycarbonate copolymer also comprises polycarbonate blocks comprising structural units of the general formula (4) below:
wherein at least 60 percent of the total number of R1 groups comprise aromatic moieties and the balance thereof comprise aliphatic, alicyclic, or aromatic moieties.
Certain polycarbonate-polysiloxane resins comprise allylphenol capped siloxanes. Such resins comprise the structure of the formula (5) below:
where R is an alkyl group having 1-3 carbon atoms, n1 is an integer of from 2 to 4 and n2 is an integer of from 1 to 200. Polycarbonate-polysiloxane copolymers comprising such structures can be found in European Patent Application No. 1757634 which is hereby incorporated by reference in its entirety for the specific purpose of disclosing various compositions and methods for manufacture of same.
In a particular aspect the polycarbonate-siloxane copolymer comprises bisphenol carbonate units of the formula (6) below:
wherein Ra and Rb are each independently C1-12 alkyl, C1-12 alkenyl, C3-8 cycloalkyl, or C1-12 alkoxy,
p and q are each independently 0 to 4, and
Xa is a single bond, —O—, —S—, —S(O)—, —S(O)2—, —C(O)—, a C1-11 alkylidene of formula —C(Rc)(Rd)— wherein Rc and Rd are each independently hydrogen or C1-10 alkyl, or a group of the formula —C(═Re)— wherein Re is a divalent C1-10 hydrocarbon group; and siloxane units of the formulae (7), (8) below:
or a combination comprising at least one of the foregoing, wherein
Certain polysiloxane-polycarbonates materials include materials disclosed and described in U.S. Pat. No. 7,786,246, which is hereby incorporated by reference in its entirety for the specific purpose of disclosing various compositions and methods for manufacture of same.
The polycarbonate-siloxane copolymer comprises about 10 wt % to about 40 wt % siloxane. In particular aspects, the polycarbonate-siloxane copolymer comprises about 15 to about 25 wt % siloxane. Certain polycarbonate-polysiloxane copolymers have a polydiorganosiloxane block having from about 20 to about 60 diorganosiloxane units. The polycarbonate-siloxane copolymer is present in an amount effective to provide a total siloxane content of 1 wt % to 5 wt % based on the total weight of the composition.
In some aspects, the polycarbonate in the polycarbonate-siloxane copolymer is a linear bisphenol-A polycarbonate produced by a melt polymerization process. In other aspects the polycarbonate in the polycarbonate-siloxane copolymer is a linear bisphenol-A polycarbonate produced by an interfacial polymerization process. In some aspects, the composition comprises from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer.
Examples of mold release agents include both aliphatic and aromatic carboxylic acids and their alkyl esters, for example, stearic acid, behenic acid, pentaerythritol stearate, glycerin tristearate, and ethylene glycol distearate. Polyolefins such as high-density polyethylene, linear low-density polyethylene, low-density polyethylene, and similar polyolefin homopolymers and copolymers can also be used a mold release agents.
Some compositions use pentaerythritol tetrastearate, glycerol monostearate, glycerol tristearate, a wax or a poly-alpha-olefin.
Mold release agents are typically present in the composition at 0.05 wt % to 1 wt %, based on total weight of the composition, and in particular aspects from about 0.1 wt % to about 0.7 wt %, from about 0.1 wt % to about 0.5 wt %, or from about 0.1 wt % to about 0.4 wt %. Particular aspects have less than about 0.3 wt %, or even less than about 0.2 wt % release agent.
In some aspects the mold release agents will have high molecular weight, typically greater than 300, to prevent loss of the release agent from the molten polymer mixture during melt processing.
The additive composition can include an impact modifier, flow modifier, antioxidant, heat stabilizer, light stabilizer, ultraviolet (UV) light stabilizer, UV absorbing additive, plasticizer, lubricant, antistatic agent, anti-fog agent, antimicrobial agent, colorant (e.g., a dye or pigment), surface effect additive, flame retardant, radiation stabilizer, anti-drip agent (e.g., a PTFE-encapsulated styrene-acrylonitrile copolymer (TSAN)), or a combination thereof. For example, a combination of a heat stabilizer and ultraviolet light stabilizer can be used. In general, the additives are used in the amounts generally known to be effective. For example, the total amount of the additive composition can be from about 0.001 wt % to about 10.0 wt %, or from about 0.01 wt % to about 5 wt %, each based on the total weight of all ingredients in the composition.
The composition can include various additives ordinarily incorporated into polymer compositions of this type, with the proviso that the additive(s) are selected so as to not significantly adversely affect the desired properties of the thermoplastic composition (good compatibility for example). Such additives can be mixed at a suitable time during the mixing of the components for forming the composition.
Examples of impact modifiers include natural rubber, fluoroelastomers, ethylene-propylene rubber (EPR), ethylene-butene rubber, ethylene-propylene-diene monomer rubber (EPDM), acrylate rubbers, hydrogenated nitrile rubber (HNBR), silicone elastomers, styrene-butadiene-styrene (SBS), styrene-butadiene rubber (SBR), styrene-(ethylene-butene)-styrene (SEBS), acrylonitrile-butadiene-styrene (ABS), acrylonitrile-ethylene-propylene-diene-styrene (AES), styrene-isoprene-styrene (SIS), styrene-(ethylene-propylene)-styrene (SEPS), methyl methacrylate-butadiene-styrene (MBS), high rubber graft (HRG), and the like. Some suitable impact modifies include PC (polycarbonate)/ABS (such as Cycoloy PC/ABS) and MBS type formulations.
The polycarbonate compositions may optionally include flame retardants. Various types of flame retardants can be utilized. In one aspect, the flame retardant additives include, for example, flame retardant salts such as alkali metal salts of perfluorinated C1-C16 alkyl sulfonates such as potassium perfluorobutane sulfonate (Rimar salt), potassium perfluoroctane sulfonate, tetraethylammonium perfluorohexane sulfonate, potassium diphenylsulfone sulfonate (KSS), and the like, sodium benzene sulfonate, sodium toluene sulfonate (NATS) and the like; and salts formed by reacting for example an alkali metal or alkaline earth metal (for example lithium, sodium, potassium, magnesium, calcium and barium salts) and an inorganic acid complex salt, for example, an oxo-anion, such as alkali metal and alkaline-earth metal salts of carbonic acid, such as Na2CO3, K2CO3, MgCO3, CaCO3, and BaCO3 or fluoro-anion complex such as Li3AlF6, BaSiF6, KBF4, K3AlF6, KAlF4, K2SiF6, and/or Na3AlF6 or the like. Rimar salt and KSS and NATS, alone or in combination with other flame retardants, are particularly useful in the compositions disclosed herein.
Some aspects of the composition disclosed herein may comprise a halogen containing flame retardant additive.
In some aspects, the flame retardant additive may comprise from about 0.1 wt % to about 25 wt % of the composition disclosed herein.
The polycarbonate compositions can optionally include a colorant composition containing pigment and/or dye additives. Useful pigments can include, for example, inorganic pigments such as metal oxides and mixed metal oxides such as zinc oxide, titanium dioxides, iron oxides, or the like; sulfides such as zinc sulfides, or the like; aluminates; sodium sulfo-silicates sulfates, chromates, or the like; carbon blacks; zinc ferrites; ultramarine blue; organic pigments such as azos, di-azos, quinacridones, perylenes, naphthalene tetracarboxylic acids, flavanthrones, isoindolinones, tetrachloroisoindolinones, anthraquinones, enthrones, dioxazines, phthalocyanines, and azo lakes; Pigment Red 101, Pigment Red 122, Pigment Red 149, Pigment Red 177, Pigment Red 179, Pigment Red 202, Pigment Violet 29, Pigment Blue 15, Pigment Blue 60, Pigment Green 7, Pigment Yellow 119, Pigment Yellow 147, Pigment Yellow 150, and Pigment Brown 24; or combinations comprising at least one of the foregoing pigments.
Dyes are generally organic materials and include coumarin dyes such as coumarin 460 (blue), coumarin 6 (green), nile red or the like; lanthanide complexes; hydrocarbon and substituted hydrocarbon dyes; polycyclic aromatic hydrocarbon dyes; scintillation dyes such as oxazole or oxadiazole dyes; aryl- or heteroaryl-substituted poly (C2-8) olefin dyes; carbocyanine dyes; indanthrone dyes; phthalocyanine dyes; oxazine dyes; carbostyryl dyes; napthalenetetracarboxylic acid dyes; porphyrin dyes; bis(styryl)biphenyl dyes; acridine dyes; anthraquinone dyes; cyanine dyes; methine dyes; arylmethane dyes; azo dyes; indigoid dyes, thioindigoid dyes, diazonium dyes; nitro dyes; quinone imine dyes; aminoketone dyes; tetrazolium dyes; thiazole dyes; perylene dyes, perinone dyes; bis-benzoxazolylthiophene (BBOT); triarylmethane dyes; xanthene dyes; thioxanthene dyes; naphthalimide dyes; lactone dyes; fluorophores such as anti-stokes shift dyes which absorb in the near infrared wavelength and emit in the visible wavelength, or the like; luminescent dyes such as 7-amino-4-methylcoumarin; 3-(2′-benzothiazolyl)-7-diethylaminocoumarin; 2-(4-biphenylyl)-5-(4-t-butylphenyl)-1,3,4-oxadiazole; 2,5-bis-(4-biphenylyl)-oxazole; 2,2′-dimethyl-p-quaterphenyl; 2,2-dimethyl-p-terphenyl; 3,5,3″″,5″″-tetra-t-butyl-p-quinquephenyl; 2,5-diphenylfuran; 2,5-diphenyloxazole; 4,4′-diphenylstilbene; 4-dicyanomethylene-2-methyl-6-(p-dimethylaminostyryl)-4H-pyran; 1,1′-diethyl-2,2′-carbocyanine iodide; 3,3′-diethyl-4,4′,5,5′-dibenzothiatricarbocyanine iodide; 7-dimethylamino-1-methyl-4-methoxy-8-azaquinolone-2; 7-dimethylamino-4-methylquinolone-2; 2-(4-(4-dimethylaminophenyl)-1,3-butadienyl)-3-ethylbenzothiazolium perchlorate; 3-diethylamino-7-diethyliminophenoxazonium perchlorate; 2-(1-naphthyl)-5-phenyloxazole; 2,2′-p-phenylen-bis(5-phenyloxazole); rhodamine 700; rhodamine 800; pyrene, chrysene, rubrene, coronene, or the like; or combinations comprising at least one of the foregoing dyes.
Heat stabilizer additives include organophosphites (e.g. triphenyl phosphite, tris-(2,6-dimethylphenyl)phosphite, tris-(mixed mono- and di-nonylphenyl)phosphite or the like), phosphonates (e.g., dimethylbenzene phosphonate or the like), phosphates (e.g., trimethyl phosphate, or the like), or combinations comprising at least one of the foregoing heat stabilizers. The heat stabilizer can be tris(2,4-di-t-butylphenyl) phosphate available as Irgafos® 168. Heat stabilizers are generally used in amounts of from about 0.01 wt % to about 5 wt %, based on the total weight of polymer in the composition.
There is considerable overlap among plasticizers, lubricants, and mold release agents, which include, for example, glycerol tristearate (GTS), phthalic acid esters (e.g., octyl-4,5-epoxy-hexahydrophthalate), tris-(octoxycarbonylethyl)isocyanurate, tristearin, di- or polyfunctional aromatic phosphates (e.g., resorcinol tetraphenyl diphosphate (RDP), the bis(diphenyl) phosphate of hydroquinone and the bis(diphenyl) phosphate of bisphenol A); poly-alpha-olefins; epoxidized soybean oil; silicones, including silicone oils (e.g., poly(dimethyl diphenyl siloxanes); esters, for example, fatty acid esters (e.g., alkyl stearyl esters, such as, methyl stearate, stearyl stearate, and the like), polyethylene, waxes (e.g., beeswax, montan wax, paraffin wax, or the like), or combinations comprising at least one of the foregoing plasticizers, lubricants, and mold release agents. These are generally used in amounts of from about 0.01 wt % to about 5 wt %, based on the total weight of the polymer in the composition.
Light stabilizers, in particular ultraviolet light (UV) absorbing additives, also referred to as UV stabilizers, include hydroxybenzophenones (e.g., 2-hydroxy-4-n-octoxy benzophenone), hydroxybenzotriazines, cyanoacrylates, oxanilides, benzoxazinones (e.g., 2,2′-(1,4-phenylene)bis(4H-3,1-benzoxazin-4-one, commercially available under the trade name CYASORB UV-3638 from Cytec), aryl salicylates, hydroxybenzotriazoles (e.g., 2-(2-hydroxy-5-methylphenyl)benzotriazole, 2-(2-hydroxy-5-tert-octylphenyl)benzotriazole, and 2-(2H-benzotriazol-2-yl)-4-(1,1,3,3-tetramethylbutyl)-phenol, commercially available under the trade name CYASORB 5411 from Cytec) or combinations comprising at least one of the foregoing light stabilizers. The UV stabilizers can be present in an amount of from about 0.01 wt % to about 1 wt %, specifically, from about 0.1 wt % to about 0.5 wt %, and more specifically, from about 0.15 wt % to about 0.4 wt %, based upon the total weight of polymer in the composition.
Antioxidant additives include organophosphites such as tris(nonyl phenyl)phosphite, tris(2,4-di-t-butylphenyl)phosphite, bis(2,4-di-t-butylphenyl)pentaerythritol diphosphite, distearyl pentaerythritol diphosphite; alkylated monophenols or polyphenols; alkylated reaction products of polyphenols with dienes, such as tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)] methane; butylated reaction products of para-cresol or dicyclopentadiene; alkylated hydroquinones; hydroxylated thiodiphenyl ethers; alkylidene-bisphenols; benzyl compounds; esters of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of beta-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of thioalkyl or thioaryl compounds such as distearylthiopropionate, dilaurylthiopropionate, ditridecylthiodipropionate, octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate; amides of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid, or combinations comprising at least one of the foregoing antioxidants. Antioxidants are used in amounts of from about 0.01 wt % to about 0.1 wt %, based on 100 parts by weight of the total composition, excluding any filler.
Anti-drip agents can also be used in the composition, for example a fibril forming or non-fibril forming fluoropolymer such as polytetrafluoroethylene (PTFE). The anti-drip agent can be encapsulated by a rigid copolymer, for example styrene-acrylonitrile copolymer (SAN). PTFE encapsulated in SAN is known as TSAN. A TSAN comprises about 50 wt % PTFE and about 50 wt % SAN, based on the total weight of the encapsulated fluoropolymer. The SAN can comprise, for example, about 75 wt % styrene and about 25 wt % acrylonitrile based on the total weight of the copolymer. Anti-drip agents can be used in amounts of about 0.1 wt % to about 10 wt %, based on 100 parts by weight of the total composition, excluding any filler.
The polymer compositions can be formed by techniques known to those skilled in the art. Extrusion and mixing techniques, for example, may be utilized to combine the components of the polymer composition.
The polymer composition may comprise from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer; from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer; and from about 0.05 wt % to about 1.0 wt % of at least one release agent, wherein the composition exhibits a melt volume flow rate (MVR) of at least about 25 cm3/10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load and a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 mm; In some aspects, certain polymer compositions exhibit melt volume ratios of at least about 35 cm3/10 min, 45 cm3/10 min, or 55 cm3/10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load.
In some aspects, the polymer composition disclosed herein may exhibit a heat distortion temperature (HDT) of 120 degrees Celsius at 1.8 megapascals (MPa) as determined by ISO 75/Ae.
The composition may comprise siloxane content of about 1 wt % to about 5 wt %. In some aspects, the housing has a siloxane content of about 1 wt % to 2 wt %.
The composition may be a notched Izod impact strength of at least about 40 kilojoules per square meter (kJ/m2) at 23° C., as determined according to ISO 1801/A on a 3 mm thick bar. In some aspects, certain compositions exhibit a notched Izod impact strength of at least about 40 kJ/m2 at 10° C. or lower temperatures, as determined according to ISO 1801/A on a 3 mm thick bar.
In some aspects, the housing may also exhibit good chemical resistance to certain compounds and fluids such as sunscreen. Environmental Stress Cracking Resistance (“ESCR”) describes the accelerated failure of polymeric materials, as a combined effect of environment, temperature, and stress. The failure mainly depends on the characteristics of the material, chemical, exposure condition, and the magnitude of the stress. ESCR may be determined according to the ISO 22088-3 standard according to the procedure described below. In some aspects, the compositions have retention of tensile strength of 80% or higher after exposure to sunscreen (e.g., Banana Boat® sunscreen) for 24 hours at room temperature under 1% strain. As used herein, good chemical resistance may also relate to the material being unaffected in its performance when exposed with regards to time, temperature and stress according to a test incorporating exposure to the chemical under defined conditions including temperatures between 20° C. and 80° C.) and stress (0.5 and 1% strain) for a time period of seven days.
Molds for forming molded articles are well known to those skilled in the art and can be formed from conventional materials. In the instant disclosure, molded parts may include draft angles of about 0.1 degree to about 7 degrees. In some aspects, molded parts include draft angles that are less than about 5 degrees or less than about 0.1 degrees or less than about 1 degree or less than about 3 degrees.
In some aspects, the disclosure concerns heating a composition and feeding the heated composition into a heated barrel of an injection molding machine and allowing the composition to melt. The melted composition can then be injected at elevated pressure into a mold cavity. Once the composition solidifies (either by passive or active cooling) forming a molded composition, the molded composition may be ejected from the mold. In some aspects, a demolding ejection force of less than about 400 Newtons (N), or less than about 350 N, or less than about 300 N, or even less than about 250 N is required to remove the molded composition from the mold.
In some aspects, a demolding coefficient of friction of less than about 20, or less than about 18, or less than about 16, or even less than about 14 is measured according to UL410.
As illustrated in
The composition and housings disclosed herein may require an ejection force at least 50% lower than an ejection force required for a substantially identical reference compositions/housings without a polycarbonate-polysiloxane copolymer.
In some aspects, the composition/housing may exhibit a coefficient of friction for removal of at least 15% lower than a coefficient of friction for removal of a substantially identical reference composition/housing without a polycarbonate-polysiloxane copolymer.
In certain aspects the housing exhibits a process window that allows processing at increased temperatures for the purpose of creating large, thin, or complex parts. The process window may be broad relative to the process window of a substantially identical reference housing without a polycarbonate-polysiloxane copolymer.
It is to be understood that the terminology used herein is for the purpose of describing particular aspects only and is not intended to be limiting. As used in the specification and in the claims, the term “comprising” can include the aspects “consisting of” and “consisting essentially of.” Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. In this specification and in the claims which follow, reference will be made to a number of terms which shall be defined herein.
As used in the specification and the appended claims, the singular forms “a,” “an” and “the” include plural equivalents unless the context clearly dictates otherwise. Thus, for example, reference to “a polycarbonate polymer” includes mixtures of two or more polycarbonate polymers.
Ranges can be expressed herein as from one value (first value) to another value (second value). When such a range is expressed, the range includes in some aspects one or both of the first value and the second value. Similarly, when values are expressed as approximations, by use of the antecedent ‘about,’ it will be understood that the particular value forms another aspect. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint. It is also understood that there are a number of values disclosed herein, and that each value is also herein disclosed as “about” that particular value in addition to the value itself. For example, if the value “10” is disclosed, then “about 10” is also disclosed. It is also understood that each unit between two particular units are also disclosed. For example, if 10 and 15 are disclosed, then 11, 12, 13, and 14 are also disclosed. When more than one range for a particular value is disclosed, the ranges are combinable to form additional aspects.
As used herein, the terms “about” and “at or about” mean that the amount or value in question can be the designated value, approximately the designated value, or about the same as the designated value. It is generally understood, as used herein, that it is the nominal value indicated ±5% variation unless otherwise indicated or inferred. The term is intended to convey that similar values promote equivalent results or effects recited in the claims. That is, it is understood that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but can be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art. In general, an amount, size, formulation, parameter or other quantity or characteristic is “about” or “approximate” whether or not expressly stated to be such. It is understood that where “about” is used before a quantitative value, the parameter also includes the specific quantitative value itself, unless specifically stated otherwise.
References in the specification and concluding claims to parts by weight of a particular element or component in a composition or article denotes the weight relationship between the element or component and any other elements or components in the composition or article for which a part by weight is expressed. Thus, in a compound containing 2 parts by weight of component X and 5 parts by weight component Y, X and Y are present at a weight ratio of 2:5, and are present in such ratio regardless of whether additional components are contained in the compound.
As used herein the terms “weight percent,” “weight %,” and “wt %” of a component, which can be used interchangeably, unless specifically stated to the contrary, are based on the total weight of the formulation or composition in which the component is included. For example if a particular element or component in a composition or article is said to have 8% by weight, it is understood that this percentage is relative to a total compositional percentage of 100% by weight.
As used herein, the terms “weight average molecular weight” or “Mw” can be used interchangeably, and are defined by the formula:
where Mi is the molecular weight of a chain and Ni is the number of chains of that molecular weight. Mw can be determined for polymers, e.g. polycarbonate polymers, by methods well known to a person having ordinary skill in the art using molecular weight standards, e.g. polycarbonate standards or polystyrene standards, and in particular certified or traceable molecular weight standards. Polystyrene basis refers to measurements using a polystyrene standard.
The term “siloxane” refers to a segment having a Si—O—Si linkage.
The term “flowable” means capable of flowing or being flowed. Typically a polymer is heated such that it is in a melted state to become flowable.
° C. is degrees Celsius, m is micrometer, kG is kilogram.
“Interfacial polycarbonate” is produced by a process where typically the disodium salt of bisphenol A (BPA) is dissolved in water and reacted with phosgene which is typically dissolved in a solvent that not miscible with water.
“Melt polycarbonate” is produced by a process where BPA reacts with diphenyl carbonate (DPC) in a molten state without the solvent.
Melt Volume Flow Rate (MVR) is measured according to ISO 1133 at 300° C. and using a 1.2 kg load.
Ejection force may be measured by injection molding sleeves in a core and then measuring the force necessary to remove the sleeve from the core. At the opening of the mold, the sleeve remains on the core due to the material contraction. At the end of the opening stroke, the ejector pins detach the sleeve from the core. The force applied to the sleeve for demolding is measured as the mold release force. The surface temperature of the sleeve is kept constant so that an accurate comparison of ejection forces can be made.
“Draft angle” concerns the slope of the wall of a mold as depicted in, e.g.,
Aspect 1. A housing for a consumer device comprising a thermoplastic composition comprising:
(a) from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer;
(b) from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5.0 wt % based on the total weight of the thermoplastic composition; and
(c) from about 0.05 wt % to about 1.0 wt % of at least one release agent,
wherein the housing exhibits
a melt volume flow rate (MVR) of at least about 25 cm3/10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load;
a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 mm; and
a tensile yield strength retention of 80% and higher after exposure of an ISO tensile bar for 24 hours to sunscreen under 1% strain compared to a non-exposed reference tested according to ISO 22088-3.
Aspect 2. The housing of Aspect 1, wherein the polycarbonate-siloxane copolymer comprises bisphenol carbonate units of the formula
wherein Ra and Rb are each independently C1-12 alkyl, C1-12 alkenyl, C3-8 cycloalkyl, or C1-12 alkoxy,
p and q are each independently 0 to 4, and
Xa is a single bond, —O—, —S—, —S(O)—, —S(O)2—, —C(O)—, a C1-11 alkylidene of formula —C(Rc)(Rd)— wherein Rc and Rd are each independently hydrogen or C1-10 alkyl, or a group of the formula —C(═Re)— wherein Re is a divalent C1-10 hydrocarbon group; and siloxane units of the formulae
or a combination comprising at least one of the foregoing, wherein
Aspect 3. The housing of any one of Aspects 1 to 2, wherein the polycarbonate polymer is a melt polycarbonate polymer, an interfacial polycarbonate polymer, or a combination thereof.
Aspect 4. The housing of any one of Aspects 1 to 3, wherein the release agent comprises pentaerythrityl tetrastearate.
Aspect 5. The housing of any one of Aspects 1 to 3, wherein the release agent comprises glycerol tristearate.
Aspect 6. The housing of any one of Aspects 1 to 5, wherein the thermoplastic composition has a coefficient of friction of less than about 20 as determined by UL 410.
Aspect 7. The housing of any one of Aspects 1 to 6, wherein the thermoplastic composition further comprises a processing aid, a heat stabilizer, an antioxidant, an ultra violet light absorber, or a combination thereof.
Aspect 8. The housing of any one of Aspects 1 to 7, wherein the thermoplastic composition comprises a MVR of at least about 35 cm3/10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load.
Aspect 9. The housing of any one of Aspects 1 to 8, wherein the thermoplastic composition comprises a MVR of at least about 45 cm3/10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load.
Aspect 10. The housing of any one of Aspects 1 to 9, wherein the thermoplastic composition exhibits a heat distortion temperature of at least about 120° C. at about 1.8 MPa, as determined according to ISO 75/Ae.
Aspect 11. The housing of any one of Aspects 1 to 10, wherein the thermoplastic composition comprises a notched Izod impact strength of at least about 40 kJ/m2 at 23° C., as determined according to ISO 1801/A on a 3 mm thick bar.
Aspect 12. The housing of any one of Aspects 1 to 11, wherein the thermoplastic composition comprises a notched Izod impact strength of at least about 40 kJ/m2 at 10° C., as determined according to ISO 1801/A on a 3 mm thick bar.
Aspect 13. The housing of any one of Aspects 1 to 12, wherein the thermoplastic composition further comprises a flame retardant, an anti-drip agent, or a combination thereof, wherein optionally the flame retardant comprises an alkali metal salt or a perfluorinated C1-C16 alkyl sulfonate, an inorganic acid complex salt, or a combination thereof.
Aspect 14. The housing of any one of Aspects 1 to 13, wherein a demolding ejection force of less than about 400 N, or less than about 350 N, or less than about 300 N, or less than about 250 N is required to remove the housing from a mold.
Aspect 15. The housing of any one of Aspects 1 to 14, wherein the thermoplastic composition exhibits good chemical resistance to at least one of oxybenzone, avobenzone, octisalate, octocrylene, homosalate, octinoxate, zinc oxide, and titanium dioxide.
Aspect 16. The housing of any one of Aspects 1 to 15, wherein the thermoplastic composition exhibits flame retardant characteristics and further comprises a flame retardant present in an amount ranging from greater than about 0 wt % to about 25 wt %.
Aspect 17. The housing of Aspect 16, wherein the flame retardant comprises an organic compound comprising phosphorous.
Aspect 18. The housing of Aspect 16, wherein the flame retardant comprises a halogen containing compound.
Aspect 19. The housing of any one of Aspects 1 to 18, wherein the composition is used in a housing for a consumer device.
Aspect 20. The housing of any one of Aspects 1 to 19, wherein the consumer device is a cellular phone, a tablet computer, a laptop computer, a desktop computer, a television, a battery or an adapter.
Aspect 21. A method for forming a housing for a consumer device, comprising:
forming a thermoplastic composition comprising:
injection molding, extruding, rotational molding, blow molding or thermoforming the thermoplastic composition in a mold to form the housing.
Aspect 22. The method of Aspect 21, further comprising removing the article from the mold, wherein the removal requires an ejection force at least about 50% lower than the ejection force required for a substantially identical reference article without a polycarbonate-polysiloxane copolymer.
Aspect 23. The method of Aspect 22, wherein the removal comprises a coefficient of friction that is at least about 15% lower than a coefficient of friction for removal of a substantially identical reference housing without a polycarbonate-polysiloxane copolymer.
Aspect 24. The method of any one of Aspects 21 to 23, wherein the mold comprises at least one draft angle from about greater than 00 to about 3°.
Aspect 25. The method of any one of Aspects 21 to 24, wherein the polycarbonate polymer is a melt polycarbonate polymer, an interfacial polycarbonate polymer, or a combination thereof.
Aspect 26. The method of any one of Aspects 21 to 25, wherein the housing exhibits a process window that allows processing at increased temperatures for the purpose of creating large, thin, or complex parts, wherein the process window is broad relative to the process window of a substantially identical reference housing without a polycarbonate-polysiloxane copolymer.
Aspect 27. The method of any one of Aspects 21 to 26, wherein the composition is used in a housing for a consumer device.
Aspect 28. The method of Aspect 27, wherein the consumer device is a cellular phone, a tablet computer, a laptop computer, a desktop computer, a television, a battery or an adapter.
The following non-limited examples illustrate certain aspects of the disclosure.
The ingredients utilized in the examples are shown in Table 1:
Unless stated otherwise, the compositions/housings were made by the following procedures. All solid additives (e.g., stabilizers, colorants) were dry blended off-line as concentrates using one of the primary polymer powders as a carrier and starve-fed via gravimetric feeder(s) into the feed throat of the extruder. The remaining polymer(s) were starve-fed via gravimetric feeder(s) into the feed throat of the extruder as well,
Extrusion of all materials was performed on a 25 mm Werner-Pfleiderer ZAK twin-screw extruder (L/D ratio of 33/1) with a vacuum port located near the die face. The extruder had 9 zones, which were set at temperatures of 40° C. (feed zone), 200° C. (zone 1), 250° C. (zone 2), 270° C. (zone 3), and 280° C. (zone 4 to 8). Screw speed was 300 revolutions per minute (rpm) and throughput was between 15 and 25 kilograms per hour (kg/hr).
The housings were molded after drying at 120° C. for 2 hours on a 45-ton Engel molding machine with a 22 mm screw or a 75-ton Engel molding machine with a 30 mm screw operating at a temperature around 300° C. with a mold temperature of 80° C.
Physical testing (e.g., Vicat softening temperature, heat deflection temperature, melt volume flow rate, melt flow rate, melt viscosity, Izod notched impact, multiaxial impact) was performed according to ISO or ASTM standards. Unless specified to the contrary herein, all test standards are the most recent standard in effect at the time of filing this application.
Notched Izod Impact (INI) Strength may be used to compare the impact resistances of plastic materials. For these examples, notched Izod impact strength was determined using a 3 mm thick molded, notched Izod impact bar according to ISO 180-2000. Tests were conducted at room temperature (23° C.) and at low temperatures (10° C. and lower). Ductile to brittle transition temperature (Temp D/B) was determined as the temperature at which the material changes from ductile fracture with high impact energy above 30 kJ/m2 to brittle fracture with low impact energy below 20 kJ/m2.
Heat deflection temperature (HDT) was determined as flatwise under a 0.45 MPa loading with a 4 mm thickness bar according to ISO75-2013.
Melt volume rate (MVR) was measured at 300° C./1.2 kg per ISO 1133-2011.
Spiral flow was measured under a molding temperature of 300° C., a mold temperature of 80° C., and an injection pressure of 2200 bar/s. The resulting molded parts had a thickness of 1 mm.
Environmental Stress Cracking Resistance (“ESCR”) describes the accelerated failure of polymeric materials, as a combined effect of environment, temperature, and stress. The failure mainly depends on the characteristics of the material, chemical, exposure condition, and the magnitude of the stress. The tests followed ISO 22088-3 standard and used ISO tensile bars under 1% strain for 24 hours at room temperature with chemical Banana Boat® sunscreen applied on the surface. After 24 hours, the retention of tensile strength and elongation to break, measured according to ISO 527, compared to the non-exposed reference.
Ejection force was measured by injection molding sleeves in a core and then measuring the force necessary to remove the sleeve from the core. At the opening of the mold, the sleeve remained on the core due to the material contraction. At the end of the opening stroke, the ejector pins detached the sleeve from the core. The force applied to the sleeve for demolding was measured as the ejection force. The surface temperature of the sleeve was kept constant so that an accurate comparison of ejection force could be made. An exemplary sleeve suitable for determining ejection force is shown in
An exemplary apparatus suitable for determining coefficient of friction is shown in
The improvement in the balance of flow, impact, and aesthetics and/or the balance of flow, impact, and chemical resistance to sunscreen resulting from adding different amounts of polysiloxane copolymer to polycarbonate, compared to the addition of alternative core-shell impact modifiers is illustrated in Table 2:
As demonstrated by the data:
This demonstrates that the compositions containing PC and PC—Si can achieve a good balance of impact (ductile Izod notched impact at room temperature or lower temperatures), high flow (indicated by high MVR and/or spiral flow) and good chemical resistance to chemicals such as, but not limited to, sunscreen.
As demonstrated by the data:
This demonstrates that compositions containing PC, Si—PC and release (PETS and/or GTS) have a good performance in having high flow, with MVR above 30, and good release performance, far outperforming similar compositions without PC—Si, having a coefficient of friction below 20 and ejection force below 400, which was not achieved by the comparative examples. As such, these compositions are more suitable for molds with relatively sharp draft angles.
Tables 4A and 4B: Example and Control Compositions
As demonstrated by the data:
This demonstrates that compositions containing PC, Si—PC and release (PETS and/or GTS) have a good performance in having high flow, with MVR above 25, and good release performance, far outperforming similar compositions without PC—Si or release, having a coefficient of friction below 20, more preferred below 15 or even 10, and ejection force below 400, more preferred below 300 or even 250, which was not achieved by the comparative examples. As such, these compositions are more suitable for molds with relatively sharp draft angles.
As demonstrated by the data:
This demonstrates that compositions containing PC, PC—Si and release (PETS and/or GTS) have a good performance in having high flow and impact performance for siloxane loadings of 1% and higher in the total composition.
As demonstrated by the data:
This demonstrates that compositions containing PC, PC—Si and release (PETS and/or GTS) have a good performance in having high flow and impact performance for siloxane loadings of 1% and higher in the total composition.
| Number | Date | Country | Kind |
|---|---|---|---|
| 16382404.8 | Aug 2016 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2017/054635 | 7/28/2017 | WO | 00 |