IN-SITU ELECTROLYTE PREPARATION IN FLOW BATTERY

Abstract

A method of in-situ electrolyte preparation in a flow battery includes providing a vanadium-based electrolyte solution having vanadium ions of predominantly vanadium V4+ to a first electrode and a second electrode of at least one cell of a flow battery. The vanadium V4+ at the first electrode is converted to vanadium V3+ and the vanadium V4+ at the second electrode is converted to vanadium V5+ by providing electrical energy to the electrodes. A reducing agent is then provided to the vanadium V5+ at the second electrode to reduce the V5+ to vanadium V4+. The vanadium V3+ at the first electrode is then converted to vanadium V2+ and the vanadium V4+ at the second electrode is then converted to vanadium V5+ by providing electrical energy to the electrodes. A simple method to produce predominantly vanadium V4+ electrolyte from a V5+ source, such as V2O5, is also taught.

Description

BACKGROUND

Flow batteries, also known as redox flow batteries or redox flow cells, are designed to convert electrical energy into chemical energy that can be stored and later released when there is demand. As an example, a flow battery may be used with a renewable energy system, such as a wind-powered system, to store energy that exceeds consumer demand and later release that energy when there is greater demand.

A typical flow battery includes a redox flow cell that has a negative electrode and a positive electrode separated by an electrolyte layer, which may include a separator, such as an ion-exchange membrane. A negative fluid electrolyte (sometimes referred to as the anolyte) is delivered to the negative electrode and a positive fluid electrolyte (sometimes referred to as the catholyte) is delivered to the positive electrode to drive electrochemically reversible redox reactions. Upon charging, the electrical energy supplied causes a chemical reduction reaction in one electrolyte and an oxidation reaction in the other electrolyte. The separator prevents the electrolytes from freely and rapidly mixing but permits selected ions to pass through to complete the redox reactions. Upon discharge, the chemical energy contained in the liquid electrolytes is released in the reverse reactions and electrical energy can be drawn from the electrodes. Flow batteries are distinguished from other electrochemical devices by, inter alia, the use of externally-supplied, fluid electrolyte solutions that include reactants that participate in reversible electrochemical reactions.

SUMMARY

Disclosed is a method of in-situ electrolyte preparation in a flow battery includes providing a vanadium-based electrolyte solution having vanadium ions of predominantly vanadium V⁴⁺ to a first electrode and a second electrode of at least one cell of a flow battery. The vanadium V⁴⁺ at the first electrode is converted to vanadium V³⁺ and the vanadium V⁴⁺ at the second electrode is converted to vanadium V⁵⁺ by providing electrical energy to the electrodes. A reducing agent is then provided to the vanadium V⁵⁺ at the second electrode to reduce the V⁵⁺ to vanadium V⁴⁺. The vanadium V³⁺ at the first electrode is then converted to vanadium V²⁺ and the vanadium V⁴⁺ at the second electrode is then converted to vanadium V⁵⁺ by providing electrical energy to the electrodes.

Also disclosed is a method of preparing a vanadium-based electrolyte solution having vanadium ions of predominantly V⁴⁺. The method includes providing a first solution and a second solution. At least one of the solution and the second solution includes vanadium V⁵⁺. At least one of the first solution and the second solution includes a reducing agent, and a ratio of moles of the reducing agent to moles of the vanadium V⁵⁺ is 2:1 or greater. The first solution and the second solution are then combined. The reducing agent reduces the V⁵⁺ to V⁴⁺.

BRIEF DESCRIPTION OF THE DRAWINGS

The various features and advantages of the present disclosure will become apparent to those skilled in the art from the following detailed description. The drawings that accompany the detailed description can be briefly described as follows.

FIG. 1 illustrates an example flow battery.

FIG. 2 illustrates an example method of in-situ electrolyte preparation in a flow battery.

FIG. 3 illustrates an example method of preparing a vanadium-based electrolyte solution having vanadium ions of predominantly V⁴⁺.

DETAILED DESCRIPTION

FIG. 1 schematically shows portions of an example flow battery 20 that can be used for selectively storing and discharging electrical energy. As an example, the flow battery 20 can be used to convert electrical energy generated in a renewable energy system to chemical energy that is stored until a later time when there is greater demand, at which time the flow battery 20 then converts the chemical energy back into electrical energy. The flow battery 20 can supply the electric energy to an electric grid, for example.

The flow battery 20 includes a fluid electrolyte 22 that has an electrochemically active specie 24 which, under charge and discharge conditions, functions in a redox pair with regard to an additional fluid electrolyte 26 that has an electrochemically active specie 28. In this example, the electrochemically active species 24/28 are based on vanadium and the fluid electrolytes 22/26 are thus vanadium-based electrolyte solutions. The fluid electrolytes 22/26 are contained in a supply/storage system 30 that includes first and second vessels 32/34 and pumps 35.

The fluid electrolytes 22/26 are delivered from the first and second vessels 32/34, using the pumps 35, to at least one cell 36 of the flow battery 20 through respective feed lines 38. The fluid electrolytes 22/26 are returned from the cell 36 to the vessels 32/34 via return lines 40. The feed lines 38 and the return lines 40 connect the vessels 32/34 with first and second electrodes 42/44 of the cell. Multiple cells 36 can be provided as a stack.

The cell or cells 36 each include the first electrode 42, the second electrode 44 spaced apart from the first electrode 42, and an electrolyte separator layer 46 arranged between the first electrode 42 and the second electrode 44. For example, the electrodes 42/44 are porous carbon structures, such as carbon paper or felt. In general, the cell or cells 36 can include bipolar plates, manifolds and the like for delivering the fluid electrolytes 22/26 through flow field channels to the electrodes 42/44. The bipolar plates can be carbon plates, for example. It is to be understood, however, that other configurations can be used. For example, the cell or cells 36 can alternatively be configured for flow-through operation where the fluid electrolytes 22/26 are pumped directly into the electrodes 42/44 without the use of flow field channels.

The electrolyte separator layer 46 can be an ionic-exchange membrane, an inert micro-porous polymer membrane or an electrically insulating microporous matrix of a material, such as silicon carbide (SiC), that prevents the fluid electrolytes 22/26 from freely and rapidly mixing but permits selected ions to pass through to complete the redox reactions while electrically isolating the electrodes 42/44. In this regard, the fluid electrolytes 22/26 are generally isolated from each other during normal operation of the flow battery, such as in charge, discharge and shutdown states.

The fluid electrolytes 22/26 are delivered to the cell 36 to either convert electrical energy into chemical energy or, in the reverse reaction, convert chemical energy into electrical energy that can be discharged. The electrical energy is transmitted to and from the cell 36 through an electric circuit 48 that is electrically coupled with the electrodes 42/44.

In the charge, discharge and shutdown state after charge or discharge, the vanadium in the first fluid electrolyte 22 has vanadium ions of V²⁺/V³⁺ and the vanadium in the second fluid electrolyte 26 has vanadium ions of V⁴⁺/V⁵⁺ (which can also be denoted as V(ii)/V(iii) and V(iv)/V(v), although the valences of the vanadium species with oxidation states of 4 and 5 are not necessarily 4+ and 5+), the concentrations of which depend upon the charge state of the flow battery 20. In the illustrated example, however, the flow battery 20 is shown in an in-situ preparation state, prior to any charging or discharging of the fluid electrolytes 22/26, for preparing the fluid electrolytes 22/26 from starting materials. In the in-situ preparation state, the fluid electrolytes 22/26 each have vanadium ions of predominantly V⁴⁺. The term “predominantly” and variations thereof used herein with reference to ions of a particular oxidation state means that the particular oxidation state is the highest concentration oxidation state among all oxidation states of the electrochemically active species. In further examples, equivalent amounts (by volume) or substantially equivalent amounts of the fluid electrolytes 22/26 are provided to the electrodes 42/44 such that there are also equivalent or substantially equivalent concentrations of V⁴⁺ at the electrodes 42/44. For example, the fluid electrolytes 22/26 are provided from the same source batch or starting material such that, once the starting material is divided, the fluid electrolytes 22/26 have equivalent or substantially equivalent concentrations of V⁴⁺. The fluid electrolytes 22/26 thus also have equivalent or substantially equivalent amounts (by moles) of V⁴⁺. The term “substantially equivalent” used herein with reference to amounts or concentrations means that the amounts or concentrations are within +/−5%.

The preparation of vanadium-based fluid electrolytes for flow batteries can be relatively expensive. For example, vanadium-based fluid electrolyte can be produced, ex-situ with respect to a flow battery, from vanadyl sulfate (VOSO₄) crystals. Vanadyl sulfate is expensive and thus greatly increases the cost of preparing a vanadium-based fluid electrolyte. As will be described, the flow battery 20 can be used for the in-situ preparation of the fluid electrolytes 22/26 from relatively inexpensive vanadium oxide (V₂O₅) powder.

FIG. 2 illustrates an example method 50 of in-situ electrolyte preparation in a flow battery, such as the flow battery 20. As shown, the method 50 generally includes steps 52, 54, 56 and 58. The example method 50 will be described with reference to the flow battery 20. However, it is to be understood that the method 50 is not limited to the illustrated configuration of the flow battery 20 disclosed herein and may be utilized with other flow batteries having different configurations. In this example, step 52 includes providing a vanadium-based electrolyte solution having vanadium ions of predominantly vanadium V⁴⁺ to the first electrode 42 and the second electrode 44. With reference to FIG. 1, the vanadium-based electrolyte solution can be provided in the vessels 32/34 and then pumped into the cell 36 to the respective first and second electrodes 42/44. In one example, the vanadium ions provided to each of the first electrode 42 and the second electrode 44 has a concentration of 90% or greater, or alternatively 95% or greater, of V⁴⁺.

After providing the vanadium-based electrolyte solution to the first and second electrodes 42/44, the vanadium V⁴⁺ at the first electrode 42 and the second electrode 44 are converted, respectively, to vanadium V³⁺ and vanadium V⁵⁺ by providing electrical energy through the electric circuit 48 to the first and second electrodes 42/44.

The electrical energy is then stopped and, at step 56, a reducing agent is provided into the second fluid electrolyte 26 to reduce the vanadium V⁵⁺ to vanadium V⁴⁺. In other words, the charging cycle of the flow battery 20 at step 52 converts the V⁴⁺ to, respectively, V³⁺ and V⁵⁺, while the reducing agent then converts the V⁵⁺ back to V⁴⁺. At this stage in the method 50, the vanadium-based electrolyte solution at the first fluid electrolyte 22 is thus predominantly V³⁺ and the vanadium-based second electrolyte solution at fluid electrolyte 26 is predominantly V⁴⁺.

At step 58, which represents a second charging cycle, electrical energy is again provided through the electric circuit 48 to the first and second electrodes 42/44 to convert the V³⁺ at the first electrode 42 to V²⁺ and convert the V⁴⁺ at the second electrode 44 to V⁵⁺. Thus, after step 58, the vanadium-based electrolyte solution at the first electrode 42 and the second electrode 44 are in a fully charged state. Moreover, because equal parts of the vanadium-based electrolyte solution are provided to the first and second electrodes 42/44 at step 52, the concentration of the V²⁺ at the first electrode 42 is equal to the concentration of the V⁵⁺ at the second electrode 44 after step 58. For example, the concentrations are equal within +/−5%.

In one example, the reducing agent that is added at step 56 includes an acid. In a further example, the acid is selected from oxalic acid, formic acid or combinations thereof. Alcohol can alternatively be used. In one example based upon the use of oxalic acid, a byproduct of the reaction between the electrolyte and the oxalic acid is the generation of carbon dioxide, which is not harmful to the flow battery 20. Thus, the use of oxalic acid additionally provides the benefit of avoiding the generation of toxic chemicals or chemicals that would otherwise debit the performance of the flow battery 20.

FIG. 3 illustrates an example method 60 of preparing the vanadium-based electrolyte solution having vanadium ions of predominantly V⁴⁺. As an example, the method 60 can be used to prepare the vanadium-based electrolyte solution that is used in the method 50. The method 60 includes steps 62 and 64. At step 62, a first solution and a second solution are provided. At least one of the first solution and the second solution includes vanadium V⁵⁺. In one example, the vanadium V⁵⁺ is the predominant vanadium ion. At least one of the first solution and the second solution includes a reducing agent, and a ratio of moles of the reducing agent to moles of the vanadium V⁵⁺ is 2:1 or greater.

At step 64, the first solution and the second solution are combined. Once combined, the reducing agent reduces the vanadium V⁵⁺ to vanadium V⁴⁺ and thus results in the production of the vanadium-based electrolyte solution with vanadium ions of predominantly V⁴⁺.

In a further example, the first solution includes the reducing agent and the second solution includes an acid. In a further example, the reducing agent includes oxalic acid, formic acid or a combination thereof, and the acid of the second solution includes sulfuric acid. The oxalic acid can be provided as oxalic acid dihydrate, for example. Alternatively, or in addition to the oxalic acid and formic acid, the reducing agent can include an alcohol. In one further example, the first solution includes the reducing agent and the vanadium V⁵⁺.

The one of the first solution or the second solution that includes the vanadium V⁵⁺ can be prepared using vanadium oxide (V₂O₅) powder. For example, the vanadium oxide powder can be combined with the reducing agent and water (e.g., deionized water) to form the first solution or can be combined with the acid of the second solution.

Equations I and II below illustrate the underlying chemical reactions of the reduction of the vanadium oxide powder to produce vanadium V⁴⁺. In Equation I, the reaction product of VO₂⁺ represents the oxidation state of vanadium V⁵⁺. In Equation II, the reaction product of VO²⁺ represents the oxidation state of vanadium V⁴⁺. The reduction of V⁵⁺ to V⁴⁺ in Equation II is an endothermic reaction. In method 60, the combining of the first solution and the second solution provides heat to drive this endothermic reaction. For example, the dilution of the acid of the second solution is exothermic and thus provides heat to drive the reduction of V⁵⁺ to V⁴⁺. Moreover, the use of the noted ratio of 2:1 provides a sufficient amount of reducing agent to reduce substantially all of the V⁵⁺ to V⁴⁺. Thus, the resulting vanadium-based electrolyte solution has predominantly V⁴⁺. In one further example, step 64 is carried out at room temperature without the application of external heat. The exothermic reaction of the dilution of the acid of the second solution can heat the mixture of the first solution and the second solution to a temperature above room temperature (approximately 23° C.), such as about 60° C. Furthermore, although the method 60 can also be carried out in-situ in the flow battery 20, the method 60 can alternatively be carried out ex-situ, separate from the flow battery 20, with equal amounts of the resulting electrolyte solution having vanadium ions of predominantly V⁴⁺ subsequently provided into the first and second electrodes 32/44 of flow battery 20 for execution of method 50.

V₂O_5(s)+2H⁺→⁶2VO₂⁺+H₂O  EQUATION I:

2VO₂⁺+H₂C₂O₄+2H⁺→2VO²⁺+2CO₂+2H₂O  EQUATION II:

Although a combination of features is shown in the illustrated examples, not all of them need to be combined to realize the benefits of various embodiments of this disclosure. In other words, a system designed according to an embodiment of this disclosure will not necessarily include all of the features shown in any one of the Figures or all of the portions schematically shown in the Figures. Moreover, selected features of one example embodiment may be combined with selected features of other example embodiments.

The preceding description is exemplary rather than limiting in nature. Variations and modifications to the disclosed examples may become apparent to those skilled in the art that do not necessarily depart from the essence of this disclosure. The scope of legal protection given to this disclosure can only be determined by studying the following claims.

Claims

1. A method of in-situ electrolyte preparation in a flow battery, the method comprising: (a) providing a vanadium-based electrolyte solution having vanadium ions of predominantly vanadium V4+ to a first electrode and a second electrode of at least one cell of a flow battery, the second electrode being spaced apart from the first electrode, with an electrolyte separator layer arranged between the first electrode and the second electrode;(b) converting the vanadium V4+ in the vanadium-based electrolyte solution at the first electrode to vanadium V3+ and converting the vanadium V4+ in the vanadium-based electrolyte solution at the second electrode to vanadium V5+ by providing electrical energy through an electric circuit to the first electrode and the second electrode;(c) after said step (b), providing a reducing agent to the vanadium-based electrolyte solution of the second electrolyte to reduce the vanadium V5+ to vanadium V4+, wherein the reducing agent includes formic acid; and(d) after said step (c), converting the vanadium V3+ of said step (b) in the vanadium-based electrolyte solution at the first electrode to vanadium V2+ and converting the vanadium V4+ of said step (c) in the vanadium-based electrolyte solution at the second electrode to vanadium V5+ by providing electrical energy through the electric circuit to the first electrode and the second electrode.

2. (canceled)

3. (canceled)

4. (canceled)

5. (canceled)

6. The method as recited in claim 1, wherein the vanadium ions of said step (a) have a concentration of 90% or greater of the vanadium V4+.

7. The method as recited in claim 1, wherein the vanadium ions of said step (a) have a concentration of 95% or greater of vanadium V4+.

8. The method as recited in claim 1, wherein the vanadium-based electrolyte solution includes sulfuric acid.

9. The method as recited in claim 1, wherein equal parts of the vanadium-based electrolyte solution in said step (a) are provided to the first electrode and the second electrode.

10. The method as recited in claim 9, wherein the concentration of the vanadium V2+ of said step (d) in the vanadium-based electrolyte solution at the first electrode is equal to the concentration of the vanadium V5+ of said step (d) in the vanadium-based electrolyte solution at the second electrode within +/−5%.

11. The method as recited in claim 1, further comprising preparing the vanadium-based electrolyte solution having vanadium ions of predominantly vanadium V4+ of said step (a) by: (i) providing a first solution and a second solution, at least one of the first solution and the second solution including vanadium V5+, at least one of the first solution and the second solution including a reducing agent, and a ratio of moles of the reducing agent to moles of vanadium V5+ is 2:1 or greater; and(ii) combining the first solution and the second solution, the reducing agent reducing the vanadium V5+ to the vanadium V4+.

12. (canceled)

13. (canceled)

14. (canceled)

15. (canceled)

16. (canceled)

17. (canceled)

18. (canceled)

19. A flow battery comprising: at least one cell including a first electrode, a second electrode spaced apart from the first electrode and an electrolyte separator layer arranged between the first electrode and the second electrode;a supply/storage system external of the at least one cell, the supply/storage system including first and second vessels fluidly connected with the at least one cell; andfirst and second fluid electrolytes in, respectively, the first and second vessels, each of the first and second fluid electrolytes having vanadium ions of predominantly vanadium V4+, the first and second fluid electrolytes having substantially equivalent amounts of vanadium ions of predominantly vanadium V4+.

20. The flow battery as recited in claim 19, wherein the battery is initially charged to a fully charged state by two separate electrochemical charging steps with the addition of a reducing fluid to one of the electrolytes in between the two charging steps.

21. The flow battery as recited in claim 19, wherein the vanadium ions of said first and second fluid electrolytes have a concentration of 90% or greater of the vanadium V4+.

22. The flow battery as recited in claim 21, wherein the vanadium ions of said first and second fluid electrolytes have a concentration of 95% or greater of vanadium V4+.

23. The flow battery as recited in claim 19, wherein the first and second vessels are supplied with a common starting material.

24. The flow battery as recited in claim 19, further comprising an electric circuit configured to provide electrical energy to the first and second fluid electrolytes to convert the vanadium V4+ to vanadium V3+, and vanadium V5+, respectively.

25. A method of in-situ electrolyte preparation in a flow battery, the method comprising: (a) providing a vanadium-based electrolyte solution having vanadium ions of predominantly vanadium V4+ to a first electrode and a second electrode of at least one cell of a flow battery, the second electrode being spaced apart from the first electrode, with an electrolyte separator layer arranged between the first electrode and the second electrode;(b) converting the vanadium V4+ in the vanadium-based electrolyte solution at the first electrode to vanadium V3+ and converting the vanadium V4+ in the vanadium-based electrolyte solution at the second electrode to vanadium V5+ by providing electrical energy through an electric circuit to the first electrode and the second electrode;(c) after said step (b), providing a reducing agent to the vanadium-based electrolyte solution of the second electrolyte to reduce the vanadium V5+ to vanadium V4+, wherein the reducing agent includes an alcohol; and(d) after said step (c), converting the vanadium V3+ of said step (b) in the vanadium-based electrolyte solution at the first electrode to vanadium V2+ and converting the vanadium V4+ of said step (c) in the vanadium-based electrolyte solution at the second electrode to vanadium V5+ by providing electrical energy through the electric circuit to the first electrode and the second electrode.

26. The method as recited in claim 25, wherein the vanadium ions of said step (a) have a concentration of 90% or greater of the vanadium V4+.

27. The method as recited in claim 25, wherein the vanadium ions of said step (a) have a concentration of 95% or greater of vanadium V4+.

28. The method as recited in claim 25, wherein the vanadium-based electrolyte solution includes sulfuric acid.

29. The method as recited in claim 25, wherein equal parts of the vanadium-based electrolyte solution in said step (a) are provided to the first electrode and the second electrode.

30. The method as recited in claim 29, wherein the concentration of the vanadium V2+ of said step (d) in the vanadium-based electrolyte solution at the first electrode is equal to the concentration of the vanadium V5+ of said step (d) in the vanadium-based electrolyte solution at the second electrode within +/−5%.

31. The method as recited in claim 25, further comprising preparing the vanadium-based electrolyte solution having vanadium ions of predominantly vanadium V4+ of said step (a) by: (i) providing a first solution and a second solution, at least one of the first solution and the second solution including vanadium V5+, at least one of the first solution and the second solution including a reducing agent, and a ratio of moles of the reducing agent to moles of vanadium V5+ is 2:1 or greater; and(ii) combining the first solution and the second solution, the reducing agent reducing the vanadium V5+ to the vanadium V4+.