Input window of a radiographic image intensifier and method for making same

Abstract

In a radiographic image intensifier having an input window, and a method for its production, an intermediate layer is deposited on a substrate for a luminous layer, thereby smoothing the surface of the substrate. This intermediate layer serves to smooth the surface of the substrate and is thus a good base for a uniform growth of the crystal structure of the luminous layer.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention The present invention is directed to an input window for a radiographic image intensifier as well as to a method for making such an input window.

[0002] 2. Description of the Prior Art

[0003] German PS 43 42 219 discloses a radiographic image intensifier with an input window wherein a layer of luminous material is deposited on a carder, this layer converting the incident x-rays into light. A photocathode is usually vacuum evaporated (metallized) on the layer of luminous material, this photocathode converting the light that emanates from the layer of luminous material into electrons. The electrons are opto-electronically projected onto the output window, which is situated opposite the input window. The output window is formed as an output luminescent screen by means of which the energy of the electrons is converted into light, which is detected by a downstream camera, for example, and this light is displayed at a display apparatus via an image intensifier video chain as an image of a transirradiated subject. As a substrate, the aforementioned carrier consists of an aluminum sheet to which a collar form is imparted by rolling, deep-drawing or roll-pressing. In known fashion, the inner concave surface of the collar-shaped substrate must be optimally smooth and/or structurally homogenous, so that in the evaporation of a luminous layer consisting of cesium iodide, for example, the cesium iodide grows uniformly in the column structure.

SUMMARY OF THE INVENTION

[0004] It is an object of the present invention to provide an input window for a radiographic image intensifier and a method for making it wherein the substrate has a smooth and structurally homogenous surface on which the uniform growth of the crystal structure is possible.

[0005] This object is achieved in accordance with the principles of the present invention in an image intensifier having an input window and a method for making same wherein an intermediate layer is deposited on a substrate for a luminous layer, smoothing the surface of the substrate. The surface flaws and damaged locations, as well as unevenness and fissures, holes and depressions which are brought about in the rolling, deep-drawing or roll-pressing, are compensated by the intermediate layer, so that there is a good base for the growth of the crystal structure of the luminous substance on the intermediate layer.

DESCRIPTION OF THE DRAWINGS

[0006] The single FIGURE is a sectional view of a radiographic image intensifier constructed and manufactured in accordance with the principles of the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0007] The FIGURE illustrates a cross-section of a portion of a radiographic image intensifier, having a vacuum vessel 1. A substrate 2 of an input window of the radiographic image intensifier is in vacuum-tight contact with the vacuum vessel 1. The substrate 2, which is fashioned into a collar shape by means of rolling, deep-drawing, or roll-pressing, inventively has an intermediate layer 3 on its inner, concave surface, on which layer a luminous layer 4 is deposited, which converts incident radiation, such as X-rays, into light. On the side of the vacuum vessel 1 situated opposite the substrate 2 there is the output window (not illustrated).

[0008] The intermediate layer 3 is deposited on the substrate 2 in a fluid or highly viscous state, for instance as a slip, suspension, or solution, by a deposition method such as injection, centrifuging (hydro extraction), or immersion, and it has a surface tension such that a smooth surface arises after drying. If the intermediate layer 3 is aluminum enamel, then it is dried subsequent to deposition on the substrate 2 and subsequently undergoes a combustion process. The intermediate layer 3 can also 2 comprise a polyimide, which is produced in an imidization process subsequent to the deposition of the starting substance, e.g. in the form of the allotherm 610 polyamidocarboxylic acid (commercially available from: BASF), and to drying at 70-100° C. The intermediate layer 3 is preferably optically opaque, so that it does not let light that is reflected at the substrate surface pass through to the luminous layer 4, or does so only slightly. Light deflected at the substrate 2 could unintentionally generate photoelectrons on the photocathode (not illustrated) adjacent the luminous layer 4, which would degrade the imaging characteristics. An imaging onto the output luminescent screen, via the light that is reflected at the surface of the input window and scattered, by defects, surface damage, and unevenness, particularly of the substrate 2 is prevented. Such scattering may appear on the display apparatus via the image intensifier video chain and could lead to misinterpretations of an X-ray image.

[0009] The opaque appearance of the polyimide intermediate layer can be achieved by mixing TiO2 powder, preferably having a preferably submicrometer grain.

[0010] Besides the possible materials already mentioned for the intermediate layer 3, other suitable materials can be used which have a surface tension for generating a smooth surface and which are vacuum stable, which means that residuals of the solvents, for example, cannot vent into the vacuum of the image intensifier.

[0011] The substrate 2 preferably consists of aluminum or of an aluminum alloy in a thickness of approximately 1 mm. Preferably, alloys of the form AlMg, (x=1-3) or AlMgSix (x=0,5-2) are used, which have a sufficient stability for withstanding the vacuum pressure given a wall thickness of less than 1 mm and have a homogenous distribution of alloy components. Under these conditions, other alloy compositions can be determined by those skilled in the art.

[0012] In the context of the invention, it is particularly preferable for a layer of pure (99.5% Al) or ultrapure (Al>99.5%) aluminum to be deposited on the substrate 2, for instance by rolling, on which layer the smoothing layer of enamel or polyimide is then deposited. The pure Al layer thickness can be in the range from 20 μm to 80 μm, preferably in the region of 50 μm; however, care must be taken that the total layer density of the substrate 2 remains in the range <1 mm, in order to keep the X-ray absorption optimally low, but the density must be sufficiently high so that the substrate 22 can withstand the pressure load. Due to the use of the pure aluminum layer, disturbances due to alloy components such as Mg no longer appear. Because of this construction, an input window of an X-ray image intensifier is thus obtained wherein the aluminum substrate 2 guarantees the resistance to pressure, and the pure aluminum layer, which is preferably deposited on the substrate 2 as sheet metal by rolling, guarantees an improved base for a good enameling for a smoother surface with few local flaws.

[0013] Although modifications and changes may be suggested by those skilled in the art, it is the intention of the inventor to embody within the patent warranted hereon all changes and modifications as reasonably and properly come within the scope of his contribution to the art.

Claims

1. A method for producing an input window of a radiographic image intensifier, comprising the steps of: providing a substrate having a substrate surface; depositing an intermediate layer on said substrate surface and thereby smoothing said substrate surface; and applying a luminous layer on said intermediate layer on said surface of said substrate.

2. A method as claimed in claim I wherein the step of providing a substrate comprises providing a substrate having an interior-facing concave surface, and forming said substrate into a collar.

3. A method as claimed in claim 1 wherein the step of depositing said intermediate layer on said substrate surface comprises flowing said substrate onto said substrate surface by a technique selected from the group of techniques consisting of injection, centrifuging and immersion and subsequently drying said intermediate layer on said substrate surface, and selecting a material comprising said intermediate layer having a surface tension so that a smooth surface of said intermediate layer arises when said intermediate layer is dried.

4. A method as claimed in claim 3 wherein said intermediate layer comprises aluminum enamel and comprising the additional step of, after said intermediate layer has dried, of firing said intermediate layer.

5. A method as claimed in claim 3 wherein said intermediate layer comprises a polyimide, and comprising the additional step, after said intermediate layer has dried, of imidizing said polyimide intermediate layer.

6. An input window of a radiographic image intensifier comprising: a substrate having a substrate surface; an intermediate layer deposited on said substrate surface to smooth said substrate surface.

7. An input window as claimed in claim 6 further comprising a luminous layer applied on said intermediate layer on said substrate surface.

8. An input window as claimed in claim 6 wherein said intermediate layer is opaque.

9. An input window as claimed in claim 6 wherein said intermediate layer comprises material selected from the group consisting of aluminum enamel and a polyimide.

10. An input window as claimed in claim 6 wherein said substrate has a collar-like shape.