The invention relates to an integrated circuit device comprising (i) a substrate; (ii) metallic circuit lines positioned on the substrate and (iii) a dielectric material positioned on the circuit lines. The dielectric material comprises the reaction product of an organic polysilica and uncondensed precursor polymer preferably terminated with an alkoxysilyl alkyl group.

Description

FIELD OF THE INVENTION

The present invention relates to an integrated circuit comprising an improved dielectric material and process for manufacturing the integrated circuit.

BACKGROUND OF THE INVENTION

There is a continuing desire in the microelectronics industry to increase the circuit density in multilevel integrated circuit devices e.g., memory and logic chips, thereby increasing their performance and reducing their cost. In order to accomplish this goal, there is a desire to reduce the minimum feature size on the chip e.g., circuit linewidth, and also to decrease the dielectric constant of the interposed dielectric material to enable closer spacing of circuit lines without an increase in crosstalk and capacitive coupling. Further, there is a desire to reduce the dielectric constant for the dielectric materials such as utilized in the back end of the line (BEOL) portion of integrated circuit devices, which contain input/output circuitry, to reduce the requisite drive current and power consumption for the device. The present dielectric is silicon dioxide which has a dielectric constant of about 4.0. This material has the requisite mechanical and thermal properties to withstand processing operations and thermal cycling associated with semiconductor manufacturing. However, it is desired that dielectric materials for future integrated circuit devices exhibit a lower dielectric constant (e.g., <3.0) than exhibited by silicon dioxide.

It is therefore an object of the present invention to provide an improved integrated circuit device comprising an improved dielectric material.

Other objects and advantages will be apparent from the following disclosure.

SUMMARY OF THE INVENTION

The present invention relates to an integrated circuit device comprising (i) a substrate; (ii) interconnecting metallic circuit lines positioned on the substrate and (iii) a dielectric material positioned contiguous to the circuit lines (over and/or between the circuit lines). The dielectric material comprises the reaction product of an organic polysilica and a precursor polymer selected from uncyclized polybenzoxazole, polybenzothiazole and polybenzimidazole polymer. The precursor polymer is preferably terminated with a trialkoxysilylaryl group. In one embodiment, the organic polysilica is silsesquioxane and the dielectric material has small phase domains.

The present invention also relates to an integrated circuit packaging structure and the processes for forming the integrated circuit device of the present invention.

A more through disclosure of the present invention is presented in the detailed description which follows and from the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of a portion of the integrated circuit device of the present invention.

FIGS. 2-5 show a process for making the integrated circuit device of the present invention.

FIGS. 6-8 show an alternative process for making the integrated circuit device of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

An embodiment of the integrated circuit device of the present invention is shown in FIG. 1. The device generally comprises substrate 2, metallic circuit lines 4 and dielectric material 6. The substrate 2 has vertical metallic studs 8 formed therein. The circuit lines function to distribute electrical signals in the device and to provide power input to and signal output from the device. Suitable integrated circuit devices will generally comprise multiple layers of circuit lines which are interconnected by vertical metallic studs.

Suitable substrates for the device of the present invention comprises silicon, silicon dioxide, glass, silicon nitride, ceramics, aluminum, copper and gallium arsenide. Other suitable substrates will be known to those skilled in the art. In a multilayer integrated circuit device, an underlying layer of insulated, planarized circuit lines can also function as a substrate.

Suitable circuit lines generally comprise a metallic, electrically conductive material such as copper, aluminum, tungsten, gold, silver or alloys thereof. Optionally, the circuit lines may be coated with a metallic liner such as a layer of nickel, tantalum or chromium or other layers such as barrier or adhesion layers (e.g., SiN, TiN).

Another embodiment of the present invention relates to an integrated circuit packaging device (multichip module) for providing signal and power current to a one or more integrated circuit chips comprising: (1) a substrate having electrical conductor for connection to a circuit board, (ii) a plurality of alternating electrically insulating and conducting layers positioned on the substrate wherein at least of the conducting layers comprises the improved dielectric film of the present invention and (iii) a plurality of vias for electrically interconnecting electrical conductor, conducting layers and integrated circuit chips.

The integrated circuit packaging device is an intermediate level of packaging between the integrated circuit chip and the circuit board. The integrated circuit chips are mounted on the integrated circuit packaging device which is in turn mounted on the circuit board.

The substrate of the packaging device is generally an inert substrate such as glass, silicon or ceramic. The substrate can optionally have integrated circuits disposed therein. The substrate is provided with electrical conductor such as input/output pins (I/O pins) for electrically connecting the packaging device to the circuit board. A plurality of electrically insulating and electrically conducting layers (layers having conductive circuits disposed in an dielectric insulating material) are alternatively stacked up on the substrate. The layers are generally formed on the substrate in a layer by layer process wherein each layer is formed in a separate process step.

The packaging device also comprises receiving means for receiving the integrated circuit chips. Suitable receiving means include pinboards for receipt of chip I/O pins or metal pads for solder connection to the chip. Generally, the packaging device also comprises a plurality of electrical vias generally vertically aligned to electrically interconnect the I/O pins, the conductive layers and integrated circuit chips disposed in the receiving means. The function structure and method of manufacture of the integrated circuit packaging devices are well known to those skilled in the art disclosed in U.S. Pat. Nos. 4,489,364, 4,508,981, 4,628,411 and 4,811,082, the disclosures of which are incorporated herein by reference.

The key feature of the present invention is the dielectric material which is positioned over the circuit lines and/or between the circuit lines and on the substrate. In multilevel integrated circuit devices, the dielectric material is often planarized to function as a substrate for lithographic formation of the next layer of circuit lines. The dielectric material comprises the reaction product of an organic polysilica and a precursor polymer selected from linear, uncyclized (uncondensed) polybenzoxazole, polybenzothiazole and polybenzimidazole. The precursor polymer is preferably terminated (end group) with (RO).sub.m (R").sub.n SiR'--, where m is 1, 2 or 3; m+n=3; R and R" are hydrocarbyl groups and R' is hydrido or a hydrocarbyl group preferably terminated with a tri C.sub.1-10 alkoxysilyl C.sub.1-10 alkyl group or a tri C.sub.1-10 alkoxysilyl aryl group. The end group is preferably a mono, di or tri C.sub.1-6 alkoxysilyl C.sub.1-6 alkyl or aryl group (e.g., phenylene, benzylene, napthylene or anthracenylene) group. As used herein, hydrocarbyl group means hydrocarbon based group (mono or difunctional) having a carbon atom attached to the remainder of the molecule and having predominantly hydrocarbon character. Hydrocarbyl groups include the following:

(1) Hydrocarbon groups; that is, aliphatic, (e.g., C.sub.1 -C.sub.10 alkyl or alkenyl and C.sub.5-10 cycloalkyl or cycloalkenyl), aromatic, aliphatic substituted aromatic, aromatic-substituted aliphatic and the like. Such groups are known to those skilled in the art; examples include methyl (methylene for difunctional hydrocarbyl group) ethyl, butyl, hexyl, octyl, decyl, dodecyl, tetradecyl, octadecyl, cyclohexyl, phenyl, naphthyl, benzyl and anthracenyl (all isomers being included). (2) Substituted hydrocarbon groups; that is, groups containing non-hydrocarbon substituents which, in the context of this invention, do not alter predominantly hydrocarbon character of the group. Those skilled in the art will be aware of suitable substituents (e.g., halo, alkoxy, carbalkoxy, nitro). (3) Hetero groups; that is, groups which, while predominantly hydrocarbon in character within the context of this invention, contain atoms other than carbon present in a chain or ring otherwise composed of carbon atoms. Suitable hetero atoms will be apparent to those skilled in the art and include, for example, nitrogen, oxygen and sulfur.

In general, no more than about three substituents or hetero atoms, and preferably no more than one, will be present for each 10 carbon atoms in the hydrocarbon-based group.

The precursor uncondensed polymer with the end group is preferably formed from the reaction of an aminoalkoxysilane with the starting monomers of the precursor polymer. Suitable AA and BB monomers for poly(benzoxazole) and poly(benzothiazole) are (i) dicarboxylic acids or their derivatives (such as terephthalic acid or terephthaloyl chloride) and (ii) diaminophenol compound such as 4,6 diamino-1,3 benzenediol dihydrochloride; 1,4-dihydroxy-3,6-diaminobenzene; 2,5-diamino-1,4-benzenedithiol dihydrochloride; 2,2' bis(3-amino-4 hydroxyphenyl) propane; 2,2'bis(3-amino-4 hydroxyphenyl) hexafluoro propane and 3,3'-dihydroxybenzidine. Suitable AB monomers are 3-amino-4-hydroxybenzoic acid hydrochloride and 3-mercapto-4-aminobenzoic hydrochloride. Suitable monomers for polybenzimidazoles are tetramines (bis-ortho-diamines) and dicarboxylic acid or derivatives thereof e.g., esters, amides and acid chlorides.

Suitable tetramines are:

1,2,4,5-tetraminobenzene 1,3-bis(methylamino)-1,6-diaminobenzene 1,3-dianilino-4,6-diaminobenzene 3,3',4,4'-tetraminodiphenylmethane 3,3',4,4'-tetraminodiphenyl ether 3,3',4,4'-tetraminobenzophenone 3,3'-diaminobenzidine 3,3'-dianilinobenzidine 3,3'-diamino-4,4'-dianilinobiphenyl 1,2-bis(3,4-diaminophenyl)ethane 2,2-bis(3,4-diaminophenyl)propane 1,4,5,8-tetraminonaphthalene

Suitable dicarboxylic acids include:

3,4-diaminobenzoic acid diphenyl-2,2'-dicarboxylic acid diphenyl-4,4'-dicarboxylic acid phthalic acid terephthalic acid naphthalene-dicarboxylic acid 4,4'-oxybisbenzoic acid benzophenone-4,4'-dicarboxylic acid

Other suitable monomers for use in the synthesis of the polymers of the present invention will be known to those skilled in the art such as disclosed in Polymer Preprints 34, 1 (3/93) and Encyclopedia of Polymer Science and Eng., 11, page 601-635 (1988) and Encyclopedia of Polymer Science and Eng., 11, page 188-239 (1988), the disclosures of which are incorporated herein by reference.

Poly (aryl ether benzoxazoles), poly(aryl ether benzothiazoles) and poly(aryl ether benzimidazoles) can also be utilized in the present invention as disclosed in Macromolecules 23, No. 11 (1990) and Macromolecules 24, 6361 (1991), the disclosures of which are incorporated herein by reference.

Suitable aminoalkoxysilanes have the formula (H.sub.2 NR'Si(R").sub.m (OR).sub.n) where m+n=3 (n is preferably 3) R is preferably C.sub.16 alkyl and R' is a spacer group preferably a C.sub.1-6 alkylene (e.g., methylene) or a nonheteroatom aryl group (a hydrocarbon aromatic group without heteroatoms) such as phenylene, benzylene or napthylene) which is positioned between the amino group and the silicon atom. Since R is cleaved and removed from the composition during the reaction, R can be any organic group which does not unacceptably interfere with the reaction and those groups should be contemplated as equivalent to those claimed herein. If n is less than 3, R" is preferably hydrido or lower C.sub.1-6 alkyl. A preferred silane is aminophenyltrimethoxysilane. Other suitable silane reactants will be known to those skilled in the art.

To form the precursor uncyclized linear polymer, the silane and monomer reactants are dissolved in a suitable solvent (such as NMP) in proper stoichiometric amounts (e.g., the monomer reactants (e.g., terephthalic acid and diaminophenol in 1:1 ratio) with the amount of silane calculated from the Carothers equation to provide the desired molecular weight of the precursor polymer product) resulting in alkoxy silylalkyl end capping of the precursor polymer. The alkoxysilylalkyl end capped precursor polymer reactant will have a molecular weight (Mn) of about 5,000 to 20,000 g/mol. A suitable alkoxysilylalkyl end capped uncondensed poly(benzoxazole) precursor polymer has the structure: ##STR1## wherein R is aryl or C.sub.1-6 alkyl.

Organic polysilica is a polymeric compound comprising silicon, carbon, oxygen and hydrogen atoms. Suitable organic polysilica include (i) partially condensed alkoxysilanes (e.g., partially condensed by controlled hydrolysis C.sub.1-6 alkoxysilane having an Mn of about 500 to 20,000 e.g., tetraethoxysilane); (ii) organically modified silicates having the composition R SiO.sub.3 and R.sub.2 SiO.sub.2 wherein R is an organic substituent (iii) partially condensed orthosilicates having the composition SiOR.sub.4 (iv) siloxanes and (v) silsesquioxanes. Silsesquioxanes are polymeric silicate materials of the type RSiO.sub.1.5 where R is an organic substituent.

Suitable organic polysilica for use in the present invention are known to those skilled in the art. Preferably, the organic polysilica is a tetraethoxysilane, silsesquioxane or a mixture thereof. Suitable silsesquioxane for the present invention is alkyl(methyl) phenyl silsesquioxane which is commercially available (e.g., GR950, GR908, GR650, GR100 etc. from Techniglass Perrysburg, Ohio). Other suitable silsesquioxanes will be known to those skilled in the art such as disclosed in U.S. Pat. No. 5,384,376 and Chem. Rev. 95, 1409-1430 (1995), the disclosures of which are incorporated herein by reference.

The dielectric composition suitably comprises about 5 to 95 weight % of the precursor polymer component and is formed in a two step process. The first step involves dissolving the silsesquioxane and the alkoxysilylalkyl end capped precursor polymer in a suitable solvent (high boiling solvent e.g., N-methyl-2-pyrrolidone NMP) at room temperature. The composition is heated to an elevated temperature directly or in a step wise fashion (e.g., 200.degree. C. for 2 hrs. and then ramped up to 400.degree. C. and held for 2 hrs.) to cause chain extension and ring closure (condensation) of the precursor polymer, and cross condensation of the precursor polymer with the polysilica.

The dielectric composition of the present invention has a dielectric constant less than 3.2 preferably less than 3 and more preferably less than 2.9 at 80.degree. C. The composition preferably has phase domains less than 0.5 microns, which result in enhanced mechanical and polishing characteristics and isotropic, optical and dielectric properties. Further, the dielectric composition has mechanical properties that resist cracking and enable it to be chemically/mechanically planarized to facilitate lithographic formation of additional circuit levels in multilevel integrated circuit devices. The dielectric composition has increased breakdown voltage, enhanced toughness and increased crack resistance, even in high ambient humidity with a thick film. The dielectric composition undergoes minimal shrinkage during heating.

The present invention also relates to processes for manufacturing the integrated circuit device. Referring to FIG. 2, the first step of one process embodiment involves disposing on a substrate 2 a layer 10 of the dielectric composition of the present invention comprising trialkoxysilylalkyl end capped precursor polymer and a silsesquioxane. The substrate 2 is shown with vertical metallic studs 8. The composition is dissolved in a suitable solvent such as N,N'-dimethylpropyleneurea (DMPU), NMP or the like and is applied to the substrate by art known methods such as spin or spray coating or doctor blading. The second step of the process involves heating the composition to an elevated temperature to cause ring closure of the precursor polymer and to cross condense the silyl reactive groups by the sol-gel process. The composition is maybe heated in the presence of a base such as an amine or Bronsted base. The base catalyzes the reaction enabling a lower initial cure temperature. Suitably, the base is an organic amine. Other suitable bases will be known to those skilled in the art. Similarly, the reaction can be catalyzed by Bronsted or Lewis acids.

Referring to FIG. 3, the third step of the process involves lithographically patterning the layer 10 of dielectric composition to form trenches 12 (depressions) in the layer of composition. The trenches 12 shown in FIG. 3 extend to the substrate 2 and to the metallic stud 8. Lithographic patterning generally involves (i) coating the layer 10 of dielectric composition with a positive or negative photoresist such as those marketed by Shipley or Hoechst Celanese (AZ photoresist), (ii) imagewise exposing (through a mask) the photoresist to radiation such as electromagnetic e.g., UV or deep UV (iii) developing the image in the resist e.g., with suitable basic developer and (iv) transferring the image through the layer 10 of dielectric composition to the substrate 2 with a suitable transfer technique such as reactive ion beam etching. (RIE) Suitable lithographic patterning techniques are well known to those skilled in the art such as disclosed in Thompson et al., "Introduction to Microlithography", (1994), the disclosure of which is incorporated herein by reference.

Referring to FIG. 4, in the fourth step of the process for forming the integrated circuit of the present invention, a metallic film 14 is deposited onto the patterned dielectric layer 10. Preferred metallic materials include copper, tungsten and aluminum. The metal is suitably deposited onto the patterned dielectric layer by art known techniques such as chemical vapor deposition (CVD), plasma enhanced CVD, electro and electroless deposition, sputtering or the like.

Referring to FIG. 5, the last step of the process involves removal of excess metallic material (e.g., planarizing the metallic film 14) so that film 14 is generally level with the patterned dielectric layer 10. Planarization can be accomplished using chemical/mechanical polishing or selective wet or dry etching. Suitable chemical/mechanical polishing are known to those skilled in the art.

Referring to FIGS. 6-8, there is shown an alternative embodiment of the process of the present invention for making the integrated circuit devices. The first step of the process in this embodiment involves depositing a metallic film 16 onto a substrate 18. Substrate 18 is also provided with vertical metallic studs 20. Referring to FIG. 7, in the second step of the process, the metallic film is lithographically patterned through a mask to form trenches 22. Referring to FIG. 8, in the third step of the process, a layer 24 of dielectric composition of the present invention is deposited onto the patterned metallic film 16. In the last step of the process, the composition is heated to cause ring closure of the precursor polymer and condense the silyl reactants. Optionally, the dielectric layer may then be planarized for subsequent process in a multilayer integrated circuit.

Although this invention has been described with respect to specific embodiments, the details thereof are not to be construed as limitations for it will be apparent that various embodiments, changes, and modifications may be resorted to without departing from the spirit and scope thereof, and it is understood that such equivalent embodiments are intended to be included within the scope of this invention.

Claims

1. A process for forming an integrated circuit comprising:

(a) positioning on a substrate a layer of dielectric composition, the composition comprising reactants organic polysilica and a precursor polymer selected from uncondensed polybenzothiazole and polybenzimidazole which is; terminated with (RO).sub.m (R").sub.n SiR'-- where R and R' are independently a hydrocarbyl group; R" is hydrido or hydrocarbyl group; m is 1, 2 or 3 and n+m=3;

(b) heating the composition to react the reactants;

(c) lithographically patterning the dielectric layer;

(d) depositing a metallic film onto the patterned dielectric layer; and

(e) planarizing the film to form the integrated circuit.

2. The process of claim 1 wherein the organic polysilica is C.sub.1-6 alkoxysilane, silsesquioxane or mixtures thereof.

3. The process of claim 1 wherein the precursor polymer is terminated with tri C.sub.1-10 alkoxysilyl C.sub.1-10 alkyl group or a tri C.sub.1-10 alkoxysilyl aryl group.

4. A process for forming an integrated circuit comprising:

(a) depositing a metallic film on a substrate;

(b) lithographically patterning the metallic film;

(c) depositing on the patterned metallic film, a layer of a dielectric composition comprising reactants organic polysilica and a precursor polymer selected from uncondensed polybenzothiazole and polybenzimidazole which is; terminated with (RO).sub.m (R").sub.n SiR'-- where R and R' are independently a hydrocarbyl group; R" is hydrido or hydrocarbyl group; m is 1, 2 or 3 and n+m=3;

(d) heating the composition to react the reactants.

5. The process of claim 4 wherein the organic polysilica is C.sub.1-6 alkoxysilane, silsesquioxane or mixtures thereof.

6. The process of claim 4 wherein the precursor polymer is end capped with a tri C.sub.1-10 alkoxysilyl C.sub.1-10 alkyl group or a tri C.sub.10 alkoxysilylaryl group.