Interconnection of aluminum components

Information

  • Patent Grant
  • 6422451
  • Patent Number
    6,422,451
  • Date Filed
    Wednesday, March 14, 2001
    23 years ago
  • Date Issued
    Tuesday, July 23, 2002
    22 years ago
Abstract
A method of interconnecting components (10, 16) of aluminium having a purity of at least 95%, the method comprising brazing the components (10, 16) together and then surface treating the assembled componetns (10, 16) by subjecting them to a Bohmitting procedure.
Description




The present invention concerns the interconnection of aluminum components, especially but not exclusively the interconnection of aluminum components of heat exchangers by brazing.




It is well known to provide heat exchangers and radiators by interconnecting conduits for primary heat exchange fluid and providing means for circulating secondary heat exchange fluid over the conduits, the external surface area of which is often extended by fixing fins thereto. The fins are normally attached to the conduits by brazing. The conduits and cooling fins are manufactured from aluminum and the brazing process involves joining one to the other with a brazing alloy (Al—Si). The alloy's melting point is lower than that of the component being joined so that when heat is applied to the joint area it melts, but not the component. A metallurgical bond is thus formed between the components. Normal brazing processes are carried out in:




a) a vacuum atmosphere without flux;




b) a molten salt bath with coating;




c) a protective gas atmosphere with coating and with flux;




d) air with coating and with flux.




The process is often assisted by coating one, other or both of the aluminum components being brazed together with a AlSi 8-12 or additional brazing material e.g. strips, bars or powder.




According to the present invention there is provided a method of interconnecting components of aluminum having a purity of at least 95% comprising brazing the components together and thereafter surface treating assembled components by subjecting them to a Boehmitting procedure.




Preferably the components are brazed together in a dry oxygen containing atmosphere in the presence of the suitable flux or paste.




Preferably at least one component is extruded.




Preferably the atmosphere in which the brazing is carried out is ambient air.




Preferably the brazing flux is an insoluble flux consisting of potassium tetrafluoraluminate with solid foils or particles of aluminum silicate (AlSi


10


) powder, or coated core material.




Preferably the brazing paste includes potassium tetrafluoraluminate with a constituent creating a thixotrophic characteristic and aluminum silicate (AlSi) powder.




Preferably the components allow a brazing temperature in the range 590°-625° C. simultaneously and remain at this temperature for substantially six minutes.




Preferably the Boehmitting procedure comprises subjecting the components to deionized water at a temperature of about 100° C.




Alternatively the Boehmitting procedure comprises subjecting the components to wet steam at a temperature of about 150° C.




Preferably the assembled components are further surface treated by a solution of silicate of sodium (Na


2


SiO


4


) in water at about 90-100° C.




Alternatively the assembled components are further surface treated by:




a) subjecting them to 10% boracic acid at about 80-100° C. mixed with water or;




b) subjecting them to 5-10% borax at about 80-100° C. mixed with water or;




c) subjecting them to waterglass (Na


2


SiO


4


) at about 90-100° C. mixed with water or;




d) subjecting them to a low viscosity resin coating.




Preferably the Boehmitting procedure is carried out only on the material surface of the conduit.











BRIEF DESCRIPTION OF THE DRAWINGS




The drawing shows a heat exchanger or radiator manufactured in accordance with the method of the present invention.











An embodiment of the present invention will now be described by way of example only with reference to the accompanying drawing.




A heat exchanger or radiator comprises a plurality of conduits


10


formed in a closed rectangular box section member


12


sub-divided to provide the side by side conduits by partitions


14


extruded integrally with the box section member


12


. The member is extruded from 3003 grade aluminum. The extrusion process resulting in a member whose surfaces are generally clean and free from grease. An example of a heat exchanger of this general type is shown in DE19846346.




The external heat exchange surface of the box section member


10


has its area extended by fixing corrugated fins


16


thereto, the fins being made from 3003 grade aluminum coated with a suitable coating (AlSi 8-12) and attached to the outer surface of the box section member


10


at the roots


18


of the corrugations by a continuous automated brazing process which does not form part of the present invention and consequently will not be described here in detail. The brazing is carried out in air utilizing a flux comprising potassium tetrafluoraluminate.




By utilizing this brazing technique it is not necessary to provide a surrounding inert atmosphere or vacuum, or molten salt bath in which the brazing is carried out so that the capital cost of the brazing equipment can be considerably reduced and the brazed components will exhibit an enhanced resistance to corrosion due to the surface coating formed during the brazing process.




The brazing process in the presence of air results in an increase in the thickness of the oxide layer of the 3003 grade aluminum which increases its resistance to corrosion in the working environment.




It has been found that there is at least a perceived reluctance to utilize aluminum heat exchangers (as an alternative to, say, copper or brass heat exchangers) in view of alleged corrosion problems and consequently product approval is more likely to be achieved if the resistance to corrosion of the heat exchange surfaces can be increased. Increased corrosion resistance by chemical oxidization such as chromatizing, anodizing, painting with epoxy resin, galvanizing with various metals, anodic or cathodic protection using existing, known techniques has proved to be impractical due to the failure of the process to provide efficient protection within long tubular members, for example heat exchanger conduits.




In the present embodiment the assembled components of the heat exchanger are subjected to a further surface heat treatment which involves elevating the temperature of the assembled components to Isoac and subjecting the assembly to a water vapor enriched atmosphere.




It can be shown that by using this process the resistance to corrosion of the surface of the assembled heat exchanger components is significantly increased due to the approximately 80-fold increase in the thickness of oxide/boehmit layer compared to other brazing methods.




Various modifications can be made without departing from the scope of the invention. For example the brazing process of the present invention can be utilized to interconnect separate heat exchange primary fluid conduits, the connection being made in side by side, intersecting or any other relationship.




The brazing flux may be substituted by a brazing paste for example, a paste including potassium tetrafluoraluminate with a constituent creating a thixotrophic characteristic and aluminum silicate (AlSi) powder.




The brazing techniques may be modified to those involving an inert or vacuum atmosphere, or a molten salt bath technique.




The Boehmitting process may be modified. It may involve subjecting the area to be treated to deionized water at a temperature of about 100° C.




Other modified and known Boehmitting procedures can be carried out.




In a further modification the Boehmitting process is carried out only to the internal surfaces of the conduit.




In another modification the surface treatment can be enhanced by subjecting the assembled components to a silicate of sodium/water wash.




Alternatively the assembled components are further surface treated by:




a) subjecting them to 10% boracic acid at about 80-100° C. mixed with water or;




b) subjecting them to 5-10% borax at about 80-100° C. mixed with water or;




c) subjecting them to waterglass (Na


2


SiO


4


) at about 90-100° C. mixed with water or;




d) subjecting them to a low viscosity resin coating.




Preferably the Boehmitting procedure is carried out only on the material surface of the conduit.




The use of extruded material for the conduit means that normal cleaning process carried out prior to Boehmitting is unnecessary. The could involve degreasing, water flushing, pickling, further water flushing, neutralizing and further flushing.




Whilst endeavoring in the foregoing specification to draw attention to those features of the invention believed to be of particular importance it should be understood that the Applicant claims protection in respect of any patentable feature or combination of features hereinbefore referred to and/or shown in the drawings whether or not particular emphasis has been placed thereon.



Claims
  • 1. A method of interconnecting components of aluminum having a purity of at least 95% comprising brazing the components together in an oxygen containing atmosphere and thereafter surface treating assembled components by subjecting them to a Boehmitting procedure.
  • 2. A method as claimed in claim 1, in which the components are brazed together in a dry oxygen containing atmosphere in the presence of a suitable flux or paste.
  • 3. A method as claimed in claim 1, in which at least one component is extruded.
  • 4. A method as claimed in claim 1, in which the atmosphere in which the brazing is carried out is ambient air.
  • 5. A method as claimed in claim 1, in which the components are brazed together in the presence of an insoluble brazing flux consisting of potassium tetrafluoraluminate with solid foils or particles of aluminum silicate powder, or coated core material.
  • 6. A method as claimed in claim 5, comprising brazing the components together in an atmosphere of ambient air.
  • 7. A method as claimed in claim 1, in which the components are brazed together in the presence of a brazing paste including potassium tetrafluoraluminate with a constituent creating a thixotrophic characteristic and aluminum silicate powder.
  • 8. A method as claimed in claim 7, comprising brazing the components together in an atmosphere of ambient air.
  • 9. A method as claimed in claim 1, in which the components allow a brazing temperature in the range 590°-625° C. simultaneously and remain at this temperature for substantially six minutes.
  • 10. A method as claimed in claim 1, in which the Bohmitting procedure comprises subjecting the components to deionized water at a temperature of about 100° C.
  • 11. A method as claimed in claim 1, in which the Bohmitting procedure comprises subjecting the components to wet steam at a temperature of about 150° C.
  • 12. A method as claimed in claim 1, in which the assembled components are further surface treated by a solution of silicate of, sodium (Na2SiO4) in water at about 90°-100° C.
  • 13. A method as claimed in claim 1, in which the assembled components are further surface treated by:a) subjecting them to 10% boracic acid at about 80°-100° C. mixed with water or; b) subjecting them to 5-10% borax at about 80-100° C. mixed with water or; c) subjecting them to waterglass (Na2SiO4) at about 90°-100° C. mixed with water or; d) subjecting them.to a low viscosity resin coating.
  • 14. A method as claimed in claim 1, in which the Boehmitting procedure is carried out only on the material surface of the conduit.
Priority Claims (1)
Number Date Country Kind
0006773 Mar 2000 GB
US Referenced Citations (19)
Number Name Date Kind
3945899 Nikaido et al. Mar 1976 A
3963568 Nikaido et al. Jun 1976 A
4421789 Kaneko et al. Dec 1983 A
4531979 Bohler et al. Jul 1985 A
4723597 Sonoda Feb 1988 A
4759805 Saruwatari et al. Jul 1988 A
4878963 Bibber Nov 1989 A
4962880 Iwai et al. Oct 1990 A
4986897 Chin Jan 1991 A
5055019 Meyer et al. Oct 1991 A
5148862 Hashiura et al. Sep 1992 A
5333776 Garg et al. Aug 1994 A
5362335 Rungta Nov 1994 A
5520768 Crook et al. May 1996 A
5569325 Barclay et al. Oct 1996 A
5692300 Conn et al. Dec 1997 A
6068711 Lu et al. May 2000 A
6178630 Jimarez et al. Jan 2001 B1
6261706 Fukuda et al. Jul 2001 B1
Foreign Referenced Citations (5)
Number Date Country
198 46 346 Mar 2000 DE
03165967 Jul 1991 EP
2360477 Sep 2001 GB
560000280 Jan 1981 JP
100130862 May 1998 JP
Non-Patent Literature Citations (1)
Entry
US 2001/0023889 A1 Bendall et al. (Sep. 27, 2001).