Patent Application
20130082239
1. Field of Invention
Embodiments of the invention relate generally to semiconductor light emitting diodes (LEDs), and more particularly, to a LED fabricated on a substrate, where the substrate is subsequently removed from the LED in a non-destructive manner using an epitaxial lift-off (ELO) technique.
2. Description of Related Art
III-V semiconductor devices are conventionally formed by first growing the active layers of the device, comprising a variety of materials in various combinations, on a bulk semiconductor substrate by metal-organic chemical vapor deposition (MOCVD) or molecular beam epitaxy (MBE). The substrate provides a crystal template (e.g., GaAs or InP) consisting of a highly periodic arrangement of atoms on which the active layers are grown. The substrate does not contribute to the operation of the device. The substrate either remains as part of the final device or is removed during fabrication, leaving the active layers attached to some other structure, or handle, which provides at least partial mechanical stability. Most commonly, the substrate is removed through a combination of mechanical grinding and chemical etching. The substrate is thus effectively removed, but destroyed in the process.
Example embodiments described herein include, but are not limited to, methods for fabricating thin film light emitting diode structures using epitaxial lift-off, and thin film light emitting diode structures produced using epitaxial lift-off.
An embodiment of a method of fabricating a thin film light emitting diode using an epitaxial lift-off process includes forming a sacrificial layer on a substrate and forming a light emitting diode structure on the sacrificial layer by epitaxial deposition. The method also includes forming a light reflecting layer on the light emitting diode structure. The method further includes removing the sacrificial layer from the substrate using an etching process to separate the substrate from the light emitting diode structure.
In some embodiments, the method further includes forming a first contact layer on the sacrificial layer. The method may further include forming a first cladding layer on the first contact layer, forming a multiple quantum well active layer on the first cladding layer, and forming a second cladding layer on the multiple quantum well active layer. The method may also include forming a second contact layer on the second cladding layer.
In some embodiments, the method also includes attaching a handle to the light-reflecting layer prior to removing the sacrificial layer.
In some embodiments, the method also includes dicing the light emitting diode structure and the light reflecting layer subsequent to removing the sacrificial layer to form a plurality of light emitting diodes.
In some embodiments, forming the light emitting diode structure includes forming a III-V semiconductor light emitting diode structure. In some embodiments, the substrate has a diameter in the range of approximately 3 inches to approximately 12 inches.
In some embodiments, after fabrication of a first light emitting diode, the method further includes fabricating one or more additional thin film light emitting diodes using the substrate. In some embodiments, the method includes receiving a substrate previously used to form a thin film light emitting diode using an epitaxial lift-off process, and using the substrate to form an additional thin film light emitting diode.
Another embodiment is a thin film III-V semiconductor light emitting diode free of a substrate, the light emitting diode includes a first contact layer and a first cladding layer formed over the first contact layer. The light emitting diode further includes a multiple quantum well active layer formed over the first cladding layer. The light emitting diode also includes a second cladding layer formed over the multiple quantum well active layer, a second contact layer formed over the second cladding layer, and a light reflecting layer formed over the second contact layer.
In some embodiments, the light-reflecting layer includes a metallic layer. In some embodiments, the light-reflecting layer includes at least one layer of dielectric material.
In some embodiments, the light emitting diode further includes a handle coupled to the light-reflecting layer. In some embodiments, the handle includes a metal, a polymer, or both. In some embodiments, the handle is in the range of approximately 5 μm to approximately 50 μm thick.
In some embodiments, the handle is permanently coupled to the light reflecting layer. In some embodiments, the handle is temporarily coupled to the light reflecting layer.
Another embodiment includes a III-V semiconductor stack for forming a thin film light emitting diode using epitaxial lift-off. The stack includes a substrate and a sacrificial layer formed over the substrate. The stack also includes an LED structure formed over the sacrificial layer, a light reflecting layer formed over the LED structure, and a handle attached to the light reflecting layer.
In some embodiments, the light-reflecting layer includes a metallic layer. In some embodiments, the substrate has a diameter in the range of between approximately 3 inches and approximately 12 inches. In some embodiments, the LED structure includes a first contact layer formed over the sacrificial layer, a first cladding layer formed over the first contact layer, and a multiple quantum well active layer formed over the first cladding layer. The LED structure also includes a second cladding layer formed over the multiple quantum well active layer, and a second contact layer formed over the second cladding layer. In some embodiments, the first contact layer and the second contact layer are more heavily doped than the first cladding layer and the second cladding layer.
In some embodiments, the sacrificial layer includes an AlGaAs material.
The summary above is provided merely to introduce a selection of concepts that are further described below in the detailed description. The summary is not intended to identify key or essential features of the claimed subject matter, nor is it intended to be used as an aid in limiting the scope of the claimed subject matter.
These figures are intended to illustrate the embodiments taught herein and are not intended to show relative sizes and dimensions (e.g., they are not drawn to scale), or to limit the scope of examples or embodiments. In the drawings, each identical or nearly identical component that is illustrated in various figures is represented by a like numeral.
Exemplary embodiments use epitaxial lift-off (ELO) techniques during fabrication of light-emitting diodes (LEDs), and in particular, thin film LEDs free of a substrate. As discussed above, conventional fabrication techniques can destroy the substrate after the device is formed or leave the substrate in place. By contrast, an epitaxial lift-off process, in accordance with some embodiments, provides a non-destructive way of removing the substrate from a wafer of LED structures after the LED structures are formed on the wafer such that the substrate can be reused for fabricating more LEDs. For example, in some embodiments, a 4-inch wafer may accommodate between 5,000 and 20,000 LED structures. In some embodiments, a 4-inch wafer may accommodate more than 20,000 LED structures. A chemical etch can be used to remove a sacrificial release layer grown between the substrate and epitaxial layers, resulting in separation of the epitaxial layers from the substrate. The substrate remains intact and, after a re-polishing step, may be used again as the crystal template for another growth run. In some embodiments, the substrate may be reused up to ten times for forming additional epitaxial layers thereon. In some embodiments, the substrate may be reused more than ten times for forming additional thin films of LED structures. The ability to remove the epitaxially-grown layers while maintaining the integrity of the substrate is unique to the ELO process and is difficult or impossible to achieve with other known techniques.
In one embodiment, an LED fabrication process begins with epitaxially growing one or more LED structures over an epitaxial sacrificial release layer on a substrate. In some embodiments, the release layer is 8-10 nanometers thick. In some embodiments, the epitaxial sacrificial release layer is lattice-matched to the substrate on which it is grown. The material for the sacrificial release layer has an extremely high etch rate compared with the etch rates of the other layers in the LED structure. For example, in some embodiments, a sacrificial release layer for epitaxial growth on a GaAs substrate includes high Al-content AlGaAs. A light reflecting layer and a handle may be formed over the LED structures. After the layers and the handle are formed, the release layer is removed by an etching process, which separates the wafer of LED structures from the substrate in a manner that does not damage the substrate or the LED structures. Tensile strain provided by the handle and/or the light reflecting layer enables lift-off of the thin film layers without any external mechanical intervention: it is not necessary to add weights to the LED structure or to add Kapton or wax over the substrate or release layer for lift-off.
Each LED structure comprises transparent n- and p-type cladding layers surrounding an undoped multiple quantum well active layer, which is designed to emit light at the design wavelength of the LED. One or more light reflecting layers are deposited on the top of the wafer, which forms the back of the LED. In some embodiments, each of the one or more light reflecting layers a thickness between 10 nm and 1,000 nm. The light-reflecting layer(s) may include, for example, a metallic layer (e.g., silver) and/or multiple layers of dielectric materials. The light-reflecting layer serves at least two purposes: it forms an optical reflector to reflect light emitted by the device, as well as acting as an adhesion layer between a handle and the epitaxial layers. In some embodiments, the light-reflecting layer may provide at least some strength to the LED structure. In embodiments including a handle layer, the handle is applied to, or formed on, the light reflecting layer to provide mechanical stability to the epitaxial layers after the ELO process. In some embodiments, the handle may be formed of a material that includes copper, another similar metal, or combination of metals. In some embodiments, the handle may be formed of a material that includes a polymer, a combination of polymers, or a combination of one or more metal and one or more polymers. In some embodiments, the handle may have a thickness in the range 5 μm to 50 μm.
The LED structure 110 includes several epitaxial layers including a multiple quantum well (MQW) active layer 120, a first cladding layer 122 formed on one side of the MQW active layer 120, a second cladding layer 124 formed on an opposite side of the MQW active layer 120 from the first cladding layer 122, a top contact layer 126 formed on the first cladding layer 122, and a back contact layer 128 formed on the second cladding layer 124. In some embodiments, the top contact layer 126 is doped in a range of 2×1018 (2E18) cm−3 to 5E18 cm −3 and the back contact layer 128 is doped in a range of 2E18 cm−3 to 5E18 cm−3. The release layer 118 may be grown before any layers of the LED structure 110 are grown and formed between the substrate 116 and the top contact layer 126. The light reflecting layer 112 may be formed on the back contact layer 128 and may be configured to reflect light generated by the LED structure 110, and more particularly, light generated by the MQW active layer 120. Any of the epitaxial layers, for example, the LED structure 110, the release layer 118, the substrate 116, and/or the light reflecting layer 112, may be formed directly on an adjacent layer or indirectly over the adjacent layer with a buffer or diode in between.
The handle 114 may be affixed to or formed on the light-reflecting layer 112 to provide mechanical support for the LED structure 110 and the light-reflecting layer 112 after the device 100 is separated from the substrate 116. The handle 118 may be permanently or temporarily affixed to the light-reflecting layer 112.
After all of the epitaxial layers are grown, a chemical etch is used to remove the release layer 118, thus separating the epitaxial layers of the device 100 from the substrate 116. In some embodiments, the substrate 116 may be reused up to 10 times for fabricating additional wafers.
After the release layer 118 is removed, the LED structure 110 can be flexible because it is no longer mechanically supported by the substrate 116. In some embodiments, the back contact layer 128, the light reflecting layer 112 and/or the handle 114 have enough tensile strength to provide mechanical support to the LED structure 110 such that the integrity of the LED structure 110 is not compromised during handling after the release layer is removed 118, which can allow for high manufacturing yields. For example, some embodiments may result in a manufacturing yield of at least 90% functional devices from the deposition and lift-off process. In some embodiments, a manufacturing yield of at least 95% functional devices from the deposition and lift-off process may be attained.
In one embodiment, a LED fabricated using an ELO process, such as described above with respect to
In another embodiment, at step 314, a handle (e.g., handle 114) is affixed to or formed over the light-reflecting layer prior to removing the sacrificial layer at step 310. In yet another embodiment, at step 316, the substrate is polished and reused to fabricate another light emitting diode. In this embodiment, process 300 then returns to step 302 to repeat the fabrication process.
The process for performing step 306 begins at step 402. At step 404, a first contact layer (e.g., top contact layer 126) is formed over the sacrificial layer. At step 406, a first cladding layer (e.g., cladding 122) is formed over the first contact layer. At step 408, a MQW active layer (e.g., MQW active layer 120) is formed over the first cladding layer. At step 410, a second cladding layer (e.g., cladding 124) is formed over the MQW active layer. At step 412, a second contact layer (e.g., back contact layer 128) is formed over the second cladding layer. The process for performing step 306 ends at step 414.
According to some embodiments, the ELO process can produce a device that is comparable to devices fabricated using a conventional substrate grinding/etching removal process. Because the substrate cost in III-V semiconductor manufacturing can be a significant component of the overall cost, the ability to reuse the substrate multiple times can provide significant cost savings. By using ELO, LEDs can be manufactured at a lower cost than possible with other manufacturing techniques through the reuse of the substrate. Further, the ELO process, according to some embodiments, can permit high manufacturing yields. Material defects resulting from the epitaxial growth, or from the ELO process, affect only the device at the location where the defect occurs. Therefore, other devices, including adjacent ones, are unaffected by such defects.
Another advantage of the ELO process is that it results in the complete removal of the substrate. In some embodiments, this allows the ELO LED to be mounted directly on a heat sink without an intervening substrate layer. Accordingly, the absence of the substrate will result in the LED operating at a lower temperature than it would if the substrate were present. Lowering the operating temperature increases LED efficiency and increases LED lifetime.
Having thus described several exemplary embodiments of the invention, it is to be appreciated that various alterations, modifications, and improvements will readily occur to those skilled in the art. For example, in some embodiments, the ELO process may be used to fabricate LED structures on large size substrates (e.g., between approximately 3- and 12-inches in diameter). In some embodiments, the ELO process may be used to fabricate a variety of LEDs, from small, low-brightness LEDs to large, high-brightness LEDs. Such alterations, modifications, and improvements are intended to be part of this disclosure, and are intended to be within the scope of the invention. Accordingly, the foregoing description and drawings are by way of example only.
This application claims priority under 35 U.S.C. §119(e) to U.S. Provisional Patent Application Ser. No. 61/541,896, entitled “Epitaxial Liftoff (ELO) for Light Emitting Diode (LED) Fabrication,” filed on Sep. 30, 2011, which is hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61541896 | Sep 2011 | US |