Light-emitting diode

Abstract

A light-emitting diode (LED) is provided, wherein the LED comprises an epitaxial structure, a bonding layer and a composite substrate. The composite substrate comprises a patterned substrate having a pattern and a conductive material layer disposed around the patterned substrate. The bonding layer is formed on the composite substrate. The epitaxial structure is formed on the bonding layer.

Description

TECHNICAL FIELD

The present invention relates to a light-emitting diode (LED), and more particularly relates to an LED that has good thermal conductivity and good processability.

BACKGROUND

An LED is composed of an epitaxial structure such as a homo-structure, a single hetero-structure, a double hetero-structure or a multiple quantum well. An LED having a p-n junction interface that can emit light with various wavelengths has several characteristics, such as a low electrical power consumption, low heat generation, long operational life, small volume, good impact resistance, fast response and excellent stability; thus the LED has been popularly used in electrical appliances and electronic devices as a light source.

Typically, an LED is composed of an epitaxial structure having a substrate, an n-type cladding layer formed over the substrate, a p-type cladding layer and an active layer formed between the n-type cladding layer and the p-type cladding layer. Light is emitted as current flows through the epitaxial structure. The light wavelength can be altered by varying the composition of the epitaxial structure material.

To improve performance, an LED requires some downstream processes to increase its brightness, thermal conductivity or the effectiveness of current diffusion. The downstream processes, such as a cutting process, may require a substrate transferring technology or a wafer bonding technology for forming additional substrates made of metal or III-V semiconductor materials. Either copper having good thermal conductivity or silicon with good process abilities (for example, with high rigidity and low coefficient of thermal expansion) is appropriate for forming the additional substrates. However, applying copper or silicon individually cannot improve both the yield of the downstream processes and the performance of an LED simultaneously, even though copper has good thermal conductivity and silicon has good processability. The process yield can be improved with copper due to its high thermal conductivity, but its poor rigidity and large coefficient of thermal expansion creates bad processability, particularly when a thinner copper substrate is required. Meanwhile, the performance of an LED can be improved with silicon since its coefficient of thermal expansion compliments downstream processes, but its poor thermal conductivity creates poor process yield.

It is desired, therefore, to provide a method for forming an LED having good thermal conductivity and good processability so as to improve the yield and performance thereof.

SUMMARY

One of the objectives of the present invention is to provide an LED having good thermal conductivity and good processability. The LED comprises an epitaxial structure, a bonding layer and a composite substrate. The composite substrate comprises a patterned substrate having a pattern and a conductive material layer disposed around the patterned substrate. The bonding layer is formed on the composite substrate. The epitaxial structure is formed on the bonding layer.

Accordingly, the feature of the present invention is to provide a composite substrate having good thermal conductivity and good processability via the composite substrate, so as to resolve the prior art problems by improving processing yield and the performance of an LED.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing aspects and many of the attendant advantages of this invention will become more readily appreciated as the same becomes better understood by reference to the following detailed description, when taken in conjunction with the accompanying drawings, wherein:

FIG. 1 illustrates a cross-sectional view of an LED structure in accordance with the first embodiment of the present invention.

FIG. 2 illustrates a cross-sectional view of an epitaxial structure for forming the LED structure in accordance with the first embodiment of the present invention.

FIG. 3 a illustrates a cross-sectional view of a patterned second substrate for forming the LED structure in accordance with the first embodiment of the present invention.

FIG. 3 b illustrates a top view of the second substrate after the patterning process is conducted in accordance with the first embodiment of the present invention.

FIG. 4 is a cross-sectional view of the structure after the patterned second substrate is adhered to the epitaxial structure in accordance with the first embodiment of the present invention.

FIG. 5 is a cross-sectional view of the structure after a portion of the patterned second substrate is removed in accordance with the first embodiment of the present invention.

FIG. 6 is a cross-sectional view of the structure after a metal layer is formed over the patterned silicon layer in accordance with the first embodiment of the present invention.

FIG. 7 illustrates a cross-sectional view of an LED structure in accordance with the second embodiment of the present invention.

FIG. 8 illustrates a cross-sectional view of an epitaxial structure for forming the LED structure in accordance with the second embodiment of the present invention.

FIG. 9 is a cross-sectional view of the structure after a second substrate is adhered to the epitaxial structure in accordance with the second embodiment of the present invention.

FIG. 10 a is a cross-sectional view of the structure after a portion of the second substrate is removed in accordance with the second embodiment of the present invention.

FIG. 10 b illustrates a top view of the second substrate after the patterned silicon layer is formed in accordance with the second embodiment of the present invention.

FIG. 11 is a cross-sectional view of the structure after a metal layer is formed over the patterned silicon layer in accordance with the second embodiment of the present invention.

FIG. 12 is a cross-sectional view of the structure after a first electrode and a second electrode are formed on the epitaxial structure in accordance with the first embodiment of the present invention.

FIG. 13 is a cross-sectional view of another structure after a first electrode and a second electrode are formed on the epitaxial structure in accordance with the first embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

The feature of the present invention is to provide a composite substrate having good thermal conductivity via copper and good processability via silicon, so as to improve processing yield and the performance of an LED.

The foregoing aspects and many of the attendant advantages of this invention will become more readily appreciated as the same becomes better understood by reference to the following detailed description.

FIG. 1 illustrates a cross-sectional view of an LED structure in accordance with the first embodiment of the present invention. The LED comprises an epitaxial structure 102, a bonding layer 104 and a composite substrate 300. The bonding layer 104, located over one side of the epitaxial structure 102, is used for adhering the composite substrate 300 to the epitaxial structure 102. The composite substrate 300 comprises a patterned silicon layer 106a penetrated through by at least one opening 103 and a metal layer 108 covering the patterned silicon layer 106a, wherein a portion of the metal layer 108 is filled in the openings 103.

FIG. 2 illustrates a cross-sectional view of an epitaxial structure for forming the LED structure in accordance with the first embodiment of the present invention. According to the first embodiment of the present invention, forming the LED structure comprises the following steps:

First, the epitaxial structure 102 is formed on a first substrate 100. The epitaxial structure 102 is formed over the first substrate 100. In various embodiments of the present invention, the epitaxial structure 102 comprises a homo-structure, a single hetero-structure, a double hetero-structure, a multiple quantum well or any arbitrary combination thereof. In the present embodiment, the epitaxial structure 102 includes an n-type cladding layer 112 made of AlGaInP, an active layer 114 and a p-type cladding layer 116 made of AlGaInP deposited sequentially over the first substrate 100 by an epitaxial process, wherein the active layer 114 is a multiple quantum well made of AlGaInP. In the present embodiment, the epitaxial structure 102 further comprises a contact layer 109 formed over the p-type cladding layer 116 and a reflection layer 110 formed over the contact layer 109.

FIG. 3 a illustrates a cross-sectional view of a patterned second substrate 106 for forming the LED structure in accordance with the first embodiment of the present invention. In the present invention, the second substrate 106 made of silicon and having a first surface 111 and a second surface 115. Then, a patterning process, such as an etch process, is conducted on the first surface 111 to form a plurality of openings 103.

FIG. 3 b illustrates a top view of the second substrate after the patterning process is conducted. In various embodiments of the present invention, the shapes of the openings 103 are circular, triangular, rectangular, polygonal, irregular or any arbitrary combination thereof, and the openings are arranged regularly or irregularly. In the present embodiment, the openings 103 are circular and arranged regularly.

Next, an adhering process is conducted to adhere the first surface 111 of the second substrate 106 to the side of the epitaxial structure 102 away from the first substrate 100.

FIG. 4 is a cross-sectional view of the structure after the patterned second substrate is adhered with the epitaxial structure 102 in accordance with the first embodiment of the present invention. In the present embodiment, the adhering process is conducted by the following steps. First, the bonding layer 104 is formed on the reflection layer 110 of the epitaxial structure 102. For example, the bonding layer 104 including organic material, such as B-staged bisbenzocyclobutene (BCB) resin, metal material, such as AuBe/Au alloy or the combination thereof is formed on the reflection layer 110 of the epitaxial structure 102 by a spin coating process. Subsequently, a bonding process follows to adhere the first surface 111 of the patterned second substrate 106 to the bonding layer 104.

A portion of the patterned second substrate 106 is removed after the adhering process is conducted.

FIG. 5 is across-sectional view of the structure after a portion of the patterned second substrate 106 is removed in accordance with the first embodiment of the present invention. In the present embodiment, a portion of the patterned second substrate 106 is removed by an etch process or a chemical mechanical polishing process to form at least one through-hole penetrating through the openings 103 and exposing a portion of the bonding layer 104 through the through-holes. The remaining portion of the patterned second substrate 106 formed as the patterned silicon layer 106a has a thickness that is substantially between 1 μm and 200 μm.

Then, a metal layer 108 is formed over the patterned silicon layer 106a.

FIG. 6 is a cross-sectional view of the structure after the metal layer 108 is formed over the patterned silicon layer 106a in accordance with the first embodiment of the present invention. A sputtering process, anodic oxidation process or the combination thereof forms the metal layer 108. The thickness of the metal layer 108 is substantially between 0.5 μm and 100 μm. In addition, a portion of the metal layer 108 is filled into the through-holes penetrating through the openings 103 and contacts the bonding layer 104.

The structure of the metal layer 108 depends on the steps of sputtering process selected for forming thereof. For example, the metal layer 108 can be a single metal layer structure, multi-hetero metal interlace structure, single layer alloy structure or any combination thereof and depends on the various sputtering steps, such as co-deposition, interlaced deposition and single deposition, and the material used for the sputtering process. The material of the metal layer 108 can be Cu, Ni, CuO or Cu/Ni alloy and is deposited over the patterned silicon layer 106a. In the present embodiment, the metal layer 108 is made of copper. The metal layer 108 comprises a single copper structure, a Cu/Ni interlace structure or a Cu/Ni alloy structure.

Next, the first substrate 100 is removed to produce the structure illustrated in FIG. 1.

Another method for forming the LED structure is disclosed by the second embodiment. The method of the second embodiment is substantially similar to the first embodiment, merely varying in the methods for forming the patterned silicon layer 106a.

FIG. 7 illustrates a cross-sectional view of an LED structure in accordance with the second embodiment of the present invention. The LED comprises an epitaxial structure 202, a bonding layer 204 and a composite substrate 400. The bonding layer 204, located over one side of the epitaxial structure 202, is used for adhering the composite substrate 400 to the epitaxial structure 202. The composite substrate 400 comprises a patterned silicon layer 206a penetrated by at least one opening 203, and a metal layer 208 covering the patterned silicon layer 206a, wherein a portion of the metal layer 208 is filled in the openings 203.

FIG. 8 illustrates a cross-sectional view of an epitaxial structure 202 for forming the LED structure, in accordance with the second embodiment of the present invention. According to the second embodiment of the present invention, forming the LED structure comprises the following steps:

First, an epitaxial structure 202 is formed on a first substrate 200. The epitaxial structure 202 is formed over the first substrate 200. In various embodiments of the present invention, the epitaxial structure 202 comprises a homo-structure, a single hetero-structure, a double hetero-structure, a multiple quantum well or any arbitrary combination thereof. In the present embodiment, the epitaxial structure 202 includes an n-type cladding layer 212 made of AlGaInP, an active layer 214 and a p-type cladding layer 216 made of AlGaInP deposited sequentially over the first substrate 200 by an epitaxial process, wherein the active layer 214 is a multiple quantum well made of AlGaInP. In the present embodiment, the epitaxial structure 202 further comprises a contact layer 209 formed over the p-type cladding layer 216 and a reflection layer 210 formed over the contact layer 209.

Simultaneously, a second substrate 206 is provided. In the present invention, the second substrate 206 is made of silicon and has a first surface 211 and a second surface 215. Then, an adhering process is conducted to adhere the first surface 211 of the second substrate 206 to the side of the epitaxial structure 202 away from the first substrate 200.

FIG. 9 is a cross-sectional view of the structure after the second substrate 206 is adhered to the epitaxial structure in accordance with the second embodiment of the present invention. In the present embodiment, the adhering process is conducted by the following steps:

First, a bonding layer 204 is formed on the reflection layer 210 of the epitaxial structure 202. For example, the bonding layer 204 including organic material, such as B-staged bisbenzocyclobutene (BCB) resin, metal material, such as AuBe/Au alloy, or the combination thereof is formed on the reflection layer 210 of the epitaxial structure 202 by a spin coating process.

Subsequently, a bonding process follows to adhere the first surface 211 of the second substrate 206 to the bonding layer 204.

A portion of the second substrate 206 is removed after the adhering process is conducted.

FIG. 10 a is a cross-sectional view of the structure after a portion of the second substrate 206 is removed in accordance with the second embodiment of the present invention. In the present embodiment, a portion of the second substrate 206 is removed by an etch process or a chemical mechanical polishing process to form at least one penetrating opening 203 exposing a portion of the bonding layer 204. The remaining portion of the patterned second substrate 206 formed as a patterned silicon layer 206a has a thickness that is substantially between 1 μm and 200 μm.

FIG. 10 b illustrates a top view of the second substrate 206 after the patterned silicon layer 206a is formed. In some embodiments of the present invention, the shapes of the penetrating openings 203 are circular, triangular, rectangular, polygonal, irregular or any arbitrary combination thereof, and the penetrating openings 203 are arranged regularly or irregularly. In the present embodiment, the penetrating openings 203 are circular and arranged regularly.

Next, a metal layer 208 is formed over the patterned silicon layer 206a.

FIG. 11 is a cross-sectional view of the structure after the metal layer 208 is formed over the patterned silicon layer 206a in accordance with the second embodiment of the present invention. A sputtering process, anodic oxidation process or the combination thereof forms the metal layer 208. The thickness of the metal layer 208 is substantially between 0.5 μm and 100 μm. In addition, a portion of the metal layer 208 is filled into the through-holes penetrating through the openings 203 and contacts the bonding layer 204.

The structure of the metal layer 208 depends on the steps of sputtering process selected for forming thereof. For example, the metal layer 208 is a single metal layer structure, multi-hetero metal interlace structure, single layer alloy structure or any combination thereof depending on the various sputtering steps, such as co-deposition, interlaced deposition and single deposition, and the material used for the sputtering process. The material of the metal layer 208 can be Cu, Ni, CuO or Cu/Ni alloy and is deposited over the patterned silicon layer 206a. In the present embodiment, the metal layer 208 is made of copper. The metal layer 208 comprises a single copper structure, a Cu/Ni interlace structure or a Cu/Ni alloy structure.

Then, the first substrate 200 is removed to produce the structure illustrated in FIG. 7.

In the preferred embodiments of the present invention, the LED structure further comprises a first electrode and a second electrode.

FIG. 12 is a cross-sectional view of the structure after the first electrode and the second electrode are formed on the epitaxial structure in accordance with the first embodiment of the present invention. In the present embodiment, the first electrode 130 and the second electrode 140 are located on the epitaxial structure 102 on the same side of the patterned silicon layer 106a.

The following steps form the first electrode 130 and the second electrode 140:

First, an etch process is conducted from the n-type cladding layer 112 downward through the active layer 114 to the p-type cladding layer 116, so that a portion of the p-type cladding layer 116 is exposed. Then, the first electrode 130 and the second electrode 140 are formed on the n-type cladding layer 112 and the p-type cladding layer 116, respectively, by a deposition process.

In another preferred embodiment, the first electrode 130 and the second electrode 140 are connected on the epitaxial structure 102 and, respectively, located on different sides of the patterned silicon layer 106a.

FIG. 13 is a cross-sectional view of another structure after the first electrode and the second electrode are formed on the epitaxial structure in accordance with the first embodiment of the present invention. In the present embodiment, the metal layer 108 acts as the second electrode 140, and the first electrode 130 is formed on the n-type cladding layer 112 by a deposition process.

Accordingly, the advantage of the present invention is to provide a composite substrate having good thermal conductivity via copper and good processability via silicon, so as to resolve the prior art problems to improve the processing yield and performance of an LED.

As is understood by a person skilled in the art, the foregoing preferred embodiments of the present invention are illustrated of the present invention rather than limiting of the present invention. It is intended to cover various modifications and similar arrangements included within the spirit and scope of the appended claims, the scope of which should be accorded the broadest interpretation so as to encompass all such modifications and similar structure.

Claims

1. A light-emitting device comprising: a composite substrate having a first surface and a second surface wherein the first surface is opposite to the second surface comprising a patterned structure having a pattern surface thereon and a conductive material layer disposed to cover the entire first surface of the composite substrate;a bonding layer formed on the second surface of the composite substrate; andan epitaxial structure formed on the bonding layer.

2. The light-emitting device of claim 1, wherein the epitaxial structure comprises a structure selected from a group consisting of a homo-structure, a single hetero-structure, a double hetero-structure, a multiple quantum well and the combination thereof.

3. The light-emitting device of claim 1, wherein the bonding layer is selected from a group consisting of organic materials, metal materials and the combination thereof.

4. The light-emitting device of claim 1, wherein the bonding layer comprises a material selected from benzocyclobutene (BCB) resin, AuBe/Au alloy and the combination thereof.

5. The light-emitting device of claim 1, wherein the conductive material layer comprises at least one material selected from a material group consisting of Cu, Ni, CuO, Cu/Ni alloy and the combination thereof.

6. The light-emitting device of claim 1, wherein the conductive material layer is a single metal layer structure, a multi-hetero metal interlace structure, a single layer alloy structure and any combination thereof.

7. The light-emitting device of claim 1, wherein the thickness of the conductive material layer is between 0.5 μm and 100 μm.

8. The light-emitting device of claim 1, wherein the patterned structure comprises silicon.

9. The light-emitting device of claim 1, wherein the thickness of the patterned structure is between 1 μm and 200 μm.

10. The light-emitting device of claim 1, wherein the pattern is in a shape of circular, triangular, rectangular, polygonal, irregular or any combination thereof.

11. The light-emitting device of claim 1, wherein the pattern is a matrix.

12. The light-emitting device of claim 1, wherein the pattern is regular or irregular.

13. The light-emitting device of claim 1, wherein the pattern penetrates through the patterned structure.

14. The light-emitting device of claim 13, wherein at least a portion of the conductive material layer is contacted with the bonding layer.

15. The light-emitting device of claim 1, further comprising a contact layer formed between the bonding layer and the epitaxial structure.

16. The light-emitting device of claim 1, further comprising a first electrode and a second electrode on the epitaxial structure, wherein the first electrode and the second electrode are located on the same side of the epitaxial structure.

17. The light-emitting device of claim 1, further comprising a first electrode and a second electrode, wherein the first electrode and the second electrode are respectively located on different sides of the epitaxial structure.

18. The light-emitting device of claim 17, wherein the second electrode is disposed on the bottom of the composite substrate.

19. The light-emitting device of claim 17, wherein the second electrode is the conductive material layer.

20. A light-emitting device comprising: a composite substrate comprising a patterned structure having a pattern and a conductive material layer disposed on the patterned structure, and the conductive material layer filling into a two dimensional array of openings formed in the patterned structure, wherein the two dimensional array of openings are formed inside one single LED element comprising of one single epitaxial structure;a bonding layer formed on the composite substrate;an epitaxial structure formed on the bonding layer;at least one electrode on a side of epitaxial structure opposite to the bonding layer.

21. The light-emitting device of claim 20, wherein the epitaxial structure comprises a structure selected from a group consisting of a homo-structure, a single hetero-structure, a double hetero-structure, a multiple quantum well and the combination thereof.

22. The light-emitting device of claim 20, wherein the bonding layer is selected from a group consisting of organic materials, metal materials and the combination thereof.

23. The light-emitting device of claim 20, wherein the bonding layer comprises a material selected from benzocyclobutene (BCB) resin, AuBe/Au alloy and the combination thereof.

24. The light-emitting device of claim 20, wherein the conductive material layer comprises at least one material selected from a material group consisting of Cu, Ni, CuO, Cu/Ni alloy and the combination thereof.

25. The light-emitting device of claim 20, wherein the conductive material layer is a single metal layer structure, a multi-hetero metal interlace structure, a single layer alloy structure and any combination thereof.

26. The light-emitting device of claim 20, wherein the thickness of the conductive material layer is between 0.5 μm and 100 μm.

27. The light-emitting device of claim 20, wherein the patterned structure comprises silicon.

28. The light-emitting device of claim 20, wherein the thickness of the patterned structure is between 1 μm and 200 μm.

29. The light-emitting device of claim 20, wherein the pattern is in a shape of circular, triangular, rectangular, polygonal, irregular or any combination thereof.

30. The light-emitting device of claim 20, wherein the pattern is a matrix.

31. The light-emitting device of claim 20, wherein the pattern is regular or irregular.

32. The light-emitting device of claim 20, wherein the pattern penetrates through the patterned structure.

33. The light-emitting device of claim 32, wherein at least a portion of the conductive material layer is contacted with the bonding layer.

34. The light-emitting device of claim 20, further comprising a contact layer formed between the bonding layer and the epitaxial structure.

35. The light-emitting device of claim 20, wherein the at least one electrode comprises a first electrode and a second electrode on the epitaxial structure, wherein the first electrode and the second electrode are located on the same side of the epitaxial structure.

36. The light-emitting device of claim 20, wherein the at least one electrode comprises a first electrode and a second electrode, wherein the first electrode and the second electrode are respectively located on the different sides of the epitaxial structure.

37. The light-emitting device of claim 36, wherein the second electrode is disposed on the bottom of the composite substrate.

38. The light-emitting device of claim 36, wherein the second electrode is the conductive material layer.