Claims
- 1. A light-transmitting fiber comprising a polymer as a core component and a polymer having a refractive index smaller than that of the core component as a sheath component, wherein the core component is a methacrylimide group-containing polymer prepared by a process comprising polymerizing methacrylic acid, a methacrylic acid ester, or a monomer mixture predominantly comprised of methacrylic acid or an ester thereof in the absence of a chain transfer agent and then reaction the thus-prepared polymer with a compound represented by the following general formula:
- R--NH.sub.2
- wherein R stands for H, an alkyl group having 1 to 12 carbon atoms, a cycloalkyl group having 7 to 11 carbon atoms or an aryl group having 6 to 10 carbon atoms,
- in the presence of a mixed solvent comprising methanol and a solvent having a solubility parameter .delta. of 8.5 to 13.9 (cal/cm.sup.3).sup.1/2.
- 2. The light-transmitting fiber according to claim 1, wherein methacrylic acid, a methacrylic acid ester or the monomer mixture is polymerized in the presence of 10 to 60% by weight of an inert solvent, based on the total weight of the inert solvent and the methacrylic acid, methacrylic acid ester or the monomer mixture.
- 3. The light-transmitting fiber according to claim 1, wherein the solvent having a solubility parameter .delta. of 8.5 to 13.9 (cal/cm.sup.3).sup.1/2 is an aromatic hydrocarbon.
- 4. The light-transmitting fiber according to claim 1, wherein the imidation reaction is carried out in an imidation reaction zone where the reaction mixture is thoroughly stirred.
- 5. The light-transmitting fiber according to claim 4, wherein the imidation reaction is carried out in a continuous manner and in an imidation reaction zone having at least two divided sections.
- 6. The light-transmitting fiber according to claim 1, wherein the imidation reaction is carried out at a temperature of 180.degree. to 250.degree. C.
- 7. The light-transmitting fiber according to claim 1, wherein the polymerization of methacrylic acid or the ester thereof or the monomer mixture and the imidation reaction of the obtained polymer are carried out in a continuous manner.
Priority Claims (1)
Number |
Date |
Country |
Kind |
63-215774 |
Aug 1988 |
JPX |
|
Parent Case Info
This is a division, of application Ser. No. 07/398,976, filed on Aug. 28, 1989 (U.S. Pat. No. 5,023,301).
US Referenced Citations (10)
Foreign Referenced Citations (4)
Number |
Date |
Country |
0155567 |
Sep 1985 |
EPX |
0232795 |
Aug 1987 |
EPX |
0234726 |
Sep 1987 |
EPX |
0273092 |
Jul 1988 |
EPX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
398976 |
Aug 1989 |
|