LOW-SURFACE AREA FUMED SILICON DIOXIDE POWDER

Abstract
Fumed silicon dioxide powder with a BET surface area of 20 to 35 m2/g, characterized in that a) the number-based median particle diameter is 60 to 150 nm, and b) the proportion of particles with a diameter of 200 nm or more is at most 10%, and c) the proportion of particles with a diameter of up to 60 nm is at most 20%, based in each case on the total number of particles.
Description

The invention relates to a low-surface area fumed silicon dioxide powder, and to the preparation and use thereof.


The invention further relates to a surface-modified silicon dioxide powder obtainable therefrom, and to the preparation and use thereof.


Fumed silicon dioxide powders are notable for their high purity. The particles generally have no internal surface area and have reactive groups on their surface. Fumed silicon dioxide can be prepared by flame hydrolysis, flame oxidation, or in a process in which these reaction types proceed alongside one another. In this process, an evaporated or gaseous hydrolyzable silicon halide is mixed with a flame which has been formed by burning a water-forming fuel and an oxygenous gas. The combustion flame provides water for the hydrolysis of the silicon halide and sufficient heat for the hydrolysis reaction. In the flame oxidation, instead of the hydrolysis, carbon-containing starting materials are oxidized.


The powders thus obtained can be surface modified in a subsequent step.


A problem is the preparation of fumed silicon dioxide powders with low BET surface area.


EP-A-1361195 discloses a fumed silicon dioxide powder with a BET surface area of 30 m2/g and a median particle diameter d50 of 195 nm, where the distribution of the particle diameters, expressed by the (d10−d90)/2d50 ratio, is 34.4.


The fumed silicon dioxide powder is obtained by hydrolyzing an evaporated starting compound of the silicon dioxide, for example silicon tetrachloride, in a flame. This is achieved by setting a flame temperature above the melting point of silicon dioxide.


DE-A-10139320 discloses a powder of spherical silicon dioxide particles with a BET surface area of 25 m2/g, which has a particle distribution of 50 nm to 1 μm. It is obtained by atomizing hexamethyldisiloxane into an auxiliary flame of a combustion gas and oxygen. An essential feature in the performance of the reaction is a high siloxane content in the reaction mixture. Accordingly, only small amounts of combustion gas and only a low stoichiometric excess of oxygen are used. Higher proportions lead to aggregated silicon dioxide particles with high BET surface area.


The silicon dioxide powders disclosed in EP-A-1361195 and DE-A-10139320 exhibit large median particle diameters and a broad distribution of the particle diameters. This limits the possible uses of the powders. EP-A-1361195 addresses a narrow distribution of the particle diameters. However, the object remains of providing powders of fumed silicon dioxide particles with small median particle diameters and a narrow distribution of the particle diameters compared to the prior art.


Moreover, the wide distribution of the particle sizes in the prior art indicates an unstable process regime. It is therefore a further object of the invention to provide a process for preparing a fumed, low-surface area silicon dioxide powder, which can be operated stably.


It was a further object of the invention to provide a powder of surface-modified fumed silicon dioxide particles, and a process for preparation thereof.


The invention provides a fumed silicon dioxide powder with a BET surface area of 20 to 35 m2/g, preferably of 23 to 28 m2/g, in which

  • a) the number-based median particle diameter is 60 to 150 nm, preferably 80 to 130 nm, and
  • b) the proportion of particles with a diameter of 200 nm or more is at most 10%, and
  • c) the proportion of particles with a diameter of up to 60 nm is at most 20%, based in each case on the total number of particles.


The BET surface area is determined based on DIN 66131. The number-based median particle diameter, the proportion of particles with a diameter of 200 nm and the proportion of particles with a diameter of up to 60 nm are obtained by counting the particles from TEM images (TEM=Transmission Electron Microscopy).


The inventive silicon dioxide powder is X-ray-amorphous. The proportion of chloride is not more than 100 ppm, generally less than 50 ppm.


The particles are predominantly isolated spherical individual particles, and aggregated non-spherical particles consisting of up to three particles joined to one another. At least some of the particles of the inventive silicon dioxide powder are aggregated non-spherical particles. In general, the proportion of non-spherical aggregated particles is 0.5 to 10% by weight, based on the powder. Non-spherical particles can offer advantages in use, when the object is to use a substrate to form a maximum common surface area.


In a particular embodiment of the invention, the proportion of particles with a diameter of 200 nm or more is 0 to 5%, based on the total number of particles.


In a further particular embodiment of the invention, the proportion of particles with a diameter of up to 60 nm is 0 to 10%, based on the total number of particles.


An advantageous embodiment may be one in which

  • a) the BET surface area is from 23 to 28 m2/g,
  • b) the number-based median particle diameter is 100±20 nm,
  • c) the proportion of particles with a diameter of 200 nm or more is 0 to 5%,
  • d) the proportion of particles with a diameter of up to 60 nm is at most 0 to 10%, based in each case on the total number of particles, and
  • e) the proportion of non-spherical aggregated particles is 0.5 to 10% by weight, based on the powder.


The invention further provides a process for preparing a silicon dioxide powder with a BET surface area of 10 to 40 m2/g, preferably 20 to 35 m2/g, more preferably 23 to 28 m2/g, in which

  • a) an aerosol obtained by atomizing at least one liquid siloxane is introduced with an oxygen-containing gas into a flame obtainable by igniting a hydrogenous combustion gas and an oxygen-containing gas, preferably oxygen-enriched air, with an oxygen content of 25 to 35% by volume, said siloxane being selected from the group consisting of the linear siloxanes of the general formula (R1)3SiO[SiR2R3O]mSi (R1)3 and
    • the cyclic siloxanes of the general formula [SiR1R2O]n,
    • where R1, R2, R3=Me or Et, m=1 to 20, n=3 to 7,
    • where R1, R2, R3, m and n are independent of one another, and where
  • b) at the time of injection into the flame,
    • b1) the molar ratio of oxygen used/oxygen required for complete oxidation of the siloxane is 1.1 to 2.5, preferably 1.5 to 2,
    • b2) the molar oxygen/hydrogenous combustion gas ratio is 0.5 to 1, preferably 0.7 to 0.9, and
    • b3) the ratio of oxygen used/oxygen required for oxidation of the siloxane and of the combustion gas is 0.80 to 0.99, preferably 0.85 to 0.95,
  • c) air is additionally introduced along the flame, where the quantitative ratio of air to the oxygen-enriched air used to generate the flame is 0.9 to 1.40, preferably 0.95 to 1.2,
  • d) then water is added to the reaction mixture for cooling, where the amount of water is 0.1 to 1.5 kg/m3 (STP) of process gas, preferably 0.6 to 1 kg/m3 (STP) of process gas, and
  • e) the solid is removed.


One essential feature of the process according to the invention is that, as stated in feature b3), the ratio of oxygen used/oxygen required for oxidation of the siloxane and of the combustion gas is 0.80 to 0.99, i.e. substoichiometric, while the conditions specified in b1) and b2) are met.


A further essential feature is the rapid cooling of the process stream with water in order to prevent undesired, uncontrolled coalescence of particles.


Siloxanes used with preference are hexamethyldisiloxane, octamethyltrisiloxane, octamethylcyclotetrasiloxane (D4) and decamethylcyclopentasiloxane (D5), and mixtures thereof. More preferably, octamethylcyclotetrasiloxane (D4) can be used.


The oxygen-containing gas used for atomization may be air, oxygen or oxygen-enriched air. In general, air is used.


The droplets formed in atomization should not be larger than 100 μm, more preferably smaller than 50 μm. According to the structure of the siloxane, the preferred droplet size can be achieved by the change in the viscosity.


The atomization pressure with which the aerosol is introduced into the flame is preferably 1 to 3 bar gauge.


The hydrogen-containing combustion gas according to the invention is preferably hydrogen, methane, ethane, propane and mixtures thereof. More preferably, hydrogen can be used.


“Process gas” is understood to mean the sum of the gaseous unconverted feedstocks and of the gaseous products including oxygen, nitrogen, water vapour and carbon dioxide.


The invention further provides a surface-modified fumed silicon dioxide powder with a BET surface area of 10 to 30 m2/g, obtainable by reacting the fumed silicon dioxide powder with one or more surface modifiers. The carbon content may be in the range from 0.1 to 5% by weight, preferably 0.3 to 2% by weight, based in each case on the powder.


The surface modifiers used may, for example, be silanes, individually or as a mixture. Examples include:


Organosilanes (RO)3Si (CnH2n+1) and (RO)3Si (CmH2m−1)

where R=alkyl, such as methyl, ethyl, n-propyl, i-propyl, butyl, n=1-20, m=2-20.


Organosilanes (R1)x(RO)ySi(CnH2n+1) and (R1)x(RO)ySi(CmH2m−1)


where R=alkyl, such as methyl, ethyl, n-propyl, i-propyl, butyl; R1=alkyl, such as methyl, ethyl, n-propyl, i-propyl, butyl, cycloalkyl; n=1-20; m=2-20; x+y=3, x=1, 2; y=1, 2.


Haloorganosilanes X3Si(CnH2n+1) and X3Si(CmH2m−1)

where X=Cl, Br; n=1-20; m=1-20.


Haloorganosilanes X2(R)Si(CnH2n+1) and X2(R)Si(CmH2m−1)

where X=Cl, Br; R=alkyl, such as methyl, ethyl, n-propyl, i-propyl, butyl, cycloalkyl; n=1-20; m=2-20.


Haloorganosilanes X(R)2Si(CnH2n+1) and X(R)2Si(CmH2m−1)

where X=Cl, Br; R=alkyl, such as methyl, ethyl, n-propyl, i-propyl, butyl, cycloalkyl; n=1-20; m=2-20.


Organosilanes (RO)3Si(CH2)m—R1

where R=alkyl, such as methyl, ethyl, propyl; m=0.1-20; R1=methyl, aryl such as —C6H5, substituted phenyl radicals, C4F9, OCF2—CHF—CF3, C6F13, OCF2CHF2, Sx—(CH2)3Si(OR)3.


Organosilanes (R2)x(RO)ySi(CH2)m—R1

where R1=methyl, aryl, such as C6H5, substituted phenyl radicals, C4F9, OCF2—CHF—CF3, C6F13, OCF2CHF2, Sx—(CH2)3Si(OR)3, SH, NR3R4R5 with R3=alkyl, aryl; R4═H, alkyl, aryl; R5═H, alkyl, aryl, benzyl, C2H4NR6R2 with R6═H, alkyl and R2═H, alkyl; R2=alkyl; x+y=3; x=1, 2; y=1, 2; m=0.1 to 20.


Haloorganosilanes X3Si(CH2)m—R


where X=Cl, Br; R=methyl, aryl such as C6H5, substituted phenyl radicals, C4F9, OCF2—CHF—CF3, C6F13, O—CF2—CHF2, Sx—(CH2)3Si(OR1)3, where R1=methyl, ethyl, propyl, butyl and x=1 or 2, SH; m=0.1-20.


Haloorganosilanes R1X2Si(CH2)mR2

where X=Cl, Br; R1=alkyl, such as methyl, ethyl, propyl, R2=methyl, aryl such as C6H5, substituted phenyl radicals, C4F9, OCF2—CHF—CF3, C6F13, O—CF2—CHF2, —OOC(CH3)C═CH2, —Sx—(CH2)3Si(OR2)3, where R3=methyl, ethyl, propyl, butyl and x=1 or 2, m=0.1-20.


Haloorganosilanes R12XSi(CH2)mR2

with X=Cl, Br; R1=alkyl, such as methyl, ethyl, propyl, R2=methyl, aryl such as C6H5, substituted phenyl radicals, C4F9, OCF2—CHF—CF3, C6F13, O—CF2—CHF2, —Sx—(CH2)3Si (OR3)3, where R3=methyl, ethyl, propyl, butyl and x=1 or 2, SH; m=0.1-20.


Silazanes R2R12SiNHSiR12R2 where R1, R2=alkyl, vinyl, aryl.


Cyclic polysiloxanes D3, D4, D5 and homologues thereof, where D3, D4 and D5 are understood to mean cyclic polysiloxanes having 3, 4 or 5 units of the —O—Si(CH3)2 type, e.g. octamethylcyclotetrasiloxane=D4.


Polysiloxanes or silicone oils of the Y—O—[(R1R2SiO)m(R3R4SiO)n]u—Y type, where


R1, R2, R3, R4=each independently alkyl such as CnH2n+1, n=1-20; aryl, such as phenyl radicals and substituted phenyl radicals, (CH2)n—NH2, H


Y═CH3, H, CnH2n+1, n=2-20; Si (CH3)3, Si(CH3)2H, Si(CH3)2OH, Si(CH3)2(OCH3), Si(CH3)2(CnH2n+1), n=2-20


m=0, 1, 2, 3, . . . ∞, preferably 0, 1, 2, 3, . . . 100 000,


n=0, 1, 2, 3, . . . ∞, preferably 0, 1, 2, 3, . . . 100 000,


u=0, 1, 2, 3, . . . ∞, preferably 0, 1, 2, 3, . . . 100 000.


Specific mention should be made of trimethylchlorosilane, dimethyldichlorosilane, methyltrichlorosilane, trimethyl-alkoxysilane, dimethylalkoxysilane, methyltrialkoxysilane, hexamethyldisilazane, decyltrimethoxysilane or polydimethylsiloxane.


The surface-modified fumed silicon dioxide powder with a BET surface area of 10 to 30 m2/g can be obtained by spraying the inventive fumed silicon dioxide powder with a surface modifier and then subjecting the mixture to a one-stage or multistage thermal treatment. The thermal treatment can be effected at 20 to 400° C. over a period of 0.1 to 6 h. Alternatively, the inventive fumed silicon dioxide powder can be treated with a surface modifier in vapour form, and the mixture can then be treated thermally at a temperature of 50 to 800° C. over a period of 0.1 to 6 h.


The invention further provides for the use of the fumed silicon dioxide powder as a filler in rubber, silicone rubber and plastics, for producing dispersions, for polishing surfaces, for adjusting the rheology in paints and coatings, as a support for catalysts and as an antiblocking agent, especially for PET films, and as a constituent of toner compositions.







EXAMPLES
Example 1

The aerosol formed from the atomization of 10 kg/h (0.0337 kmol/h) of octamethylcyclotetrasiloxane (D4) with 12 m3 (STP)/h of air is introduced with a pressure of 1.2 bar gauge into a flame formed by igniting a mixture of 60 m3 (STP)/h of oxygen-enriched air (O2 content 32% by volume) and 27 m3 (STP)/h (1.205 kmol/h) of hydrogen. The oxygen component from the atomization air and the oxygen introduced to form the flame is 21.72 m3 (STP)/h (0.969 kmol/h). In addition, 60 m3 (STP)/h of an air stream which surrounds the flame are introduced, and the process mixture is subsequently cooled with 0.4 kg/m3 (STP) of process gas.


The product deposited at a filter has a BET surface area of 25 m2/g and a median particle diameter of 84 nm, 2% of the particles having a particle diameter of more than 200 nm and 9% of the particles a particle diameter of less than 60 nm. The proportion of the non-spherical aggregated particles is approx. 4%.


V, as the molar ratio of O2 used/O2 required for complete oxidation of the siloxane, is 1.796. X, as the molar O2/H2 ratio, is 0.804. Y, as the ratio of O2 used/O2 required for oxidation of siloxane and combustion gas, is 0.946. Z, as the quantitative ratio of air/oxygen-enriched air used to generate the flame, is 1.


Examples 2 to 6 are performed analogously. Feedstocks and amounts used are reproduced in the table. The table also reproduces the properties of the powders obtained.


In Example 2, a higher proportion of oxygen is used compared to Example 1.


In Example 3, hexamethyldisiloxane (HMDSO) is used in place of D4.


In Example 4, a higher proportion of HMDSO and a lower proportion of oxygen are used compared to Example 3.


Examples 5 and 6 are comparative examples. In Example 5, X is 0.621. In Example 6, V is 2.698.


In Examples 1 to 4, inventive powders are obtained. In Examples 5 and 6, powders for which at least one parameter is outside the range claimed are obtained.


Example 7: Surface modification of the powder from Example 1 with hexamethyldisilazane


In a mixer, 100 parts by weight of the silicon dioxide powder from Example 1, with intensive mixing, are sprayed first with 1 part by weight of water and then with 7.5 parts by weight of hexamethyldisilazane. Once the spraying has ended, mixing is continued for another 15 min and is followed by heat treatment at 200° C. for 30 min.


The surface-modified silicon dioxide powder has a BET surface area of 19 m2/g and a carbon content of 0.29% by weight.


Example 8: Surface modification of the powder from Example 2 with polydimethylsiloxane


In a mixer, 100 parts by weight of the silicon dioxide powder from Example 1, with intensive mixing, are sprayed with 5 parts by weight of polydimethylsiloxane. Once the spraying has ended, mixing is continued for another 15 min and is followed by heat treatment at 300° C. for 20 min.


The surface-modified silicon dioxide powder has a BET surface area of 15 m2/g and a carbon content of 1.40% by weight.









TABLE 1







Feedstocks and amounts used; powder properties














Example

1
2
3
4
5a)
6a)

















Siloxane

D4
D4
HMDSO
HMDSO
D4
D4



kg/h
10
10
6
7
15
8



kmol/h
0.0337
0.0337
0.0370
0.0431
0.0506
0.0270


Atomization
m3
12
7
12
12
7
10


air
(STP)/h


Pressure
bar g
1.2
1.9
1.2
1.2
1.2
1.2


Air
m3
60
60
60
55
45
75


O2 content
(STP)/h



Vol. %
32
35
32
32
34
32


Total O2
m3
21.72
22.47
21.72
20.12
16.77
26.1



(STP)/h



kmol/h
0.969
1.002
0.969
0.898
0.748
1.164


Combustion gas
m3
27
27
25
25
27
27


H2
(STP)/h



kmol/h
1.205
1.205
1.115
1.115
1.205
1.205


Air
m3
60
60
70
60
60
60



(STP)/h


Water
kg/m3
0.4
0.4
0.3
0.3
0.6
0.3



(STP)















Calculated
V1)

1.796
1.858
2.185
1.735
0.925
2.698



X2)

0.804
0.832
0.869
0.805
0.621
0.967



Y3)

0.946
0.963
0.901
0.788
0.632
1.149



Z4)

1
1
1.17
1.09
1.33
0.80







Powder properties














BET surface
m2/g
25
22
33
28
16
41


area


Median
nm
84
108
64
72
131
48


>200 nm
%
2
3.5
1.5
2
5
2


<60 nm
%
9
8
8
7
11
10


Non-spherical
%
approx. 6
8
4
5
8
8






a)Comparative example;




1)V = molar ratio of O2 used/O2 required for complete oxidation of the siloxane;




2)X = molar O2/H2 ratio;




3)Y = ratio of O2 used/O2 required for oxidation of siloxane and combustion gas;




4)Z = quantitative ratio of air/oxygen-enriched air used to generate the flame






Claims
  • 1. A fumed silicon dioxide powder, having a BET surface area of 20 to 35 m2/g, wherein a) a number-based median particle diameter is 60 to 150 nm,b) a proportion of particles with a diameter of 200 nm or more is at most 10%, andc) a proportion of particles with a diameter of up to 60 nm is at most 20%, based in each case on a total number of particles.
  • 2. The powder of claim 1, comprising 0.1 to 10% by weight, based on the powder, of at least one non-spherical aggregated particle.
  • 3. The powder of claim 1, wherein the proportion of particles with a diameter of 200 nm or more is 0 to 5%, based on the total number of particles.
  • 4. The powder of claim 1, wherein the proportion of particles with a diameter of up to 60 nm is 0 to 10%, based on the total number of particles.
  • 5. A process for preparing a silicon dioxide powder with a BET surface area of 10 to 40 m2/g, the process comprising a) introducing an aerosol obtained by atomizing at least one liquid siloxane with an oxygen-comprising gas into a flame obtained by igniting a hydrogenous combustion gas and an oxygen-comprising gas with an oxygen content of 25 to 35% by volume, in a reaction mixture, said siloxane being at least one selected from the group consisting of a linear siloxane of formula (I) (R1)3SiO[SiR2R3O]mSi(R1)3  (I)and a cyclic siloxane of formula (II) [SiR1R2O]n  (II),wherein R1, R2, and R3 are independently Me or Et, m is 1 to 20, n is 3 to 7, and R1, R2, R3, m and n are independent of one another, and whereinb) at a time of injection into the flame, b1) a molar ratio of oxygen employed/oxygen required for complete oxidation of the siloxane is 1.1 to 2.5,b2) a molar oxygen/hydrogenous combustion gas ratio is 0.5 to 1, andb3) a ratio of oxygen employed/oxygen required for oxidation of the siloxane and of the combustion gas is 0.80 to 0.99,c) additionally introducing air along the flame, wherein a quantitative ratio of air to oxygen-enriched air employed to generate the flame is 0.9 to 1.40,d) then adding water to the reaction mixture for cooling, wherein an amount of water is 0.1 to 1.5 kg/m3 (STP) of process gas, ande) removing a solid obtained in d).
  • 6. The process of claim 5, wherein an atomization pressure with which the aerosol is introduced into the flame is 1 to 3 bar gauge.
  • 7. A surface-modified fumed silicon dioxide powder, having a BET surface area of 10 to 30 m2/g, obtained by reacting the fumed silicon dioxide powder of claim 1 with one or more surface modifiers.
  • 8. A rubber, silicone rubber, plastic, dispersion, a surface polishing composition, paint coatings, a support for a catalyst an antiblocking agent, or a toner composition, comprising the fumed silicon dioxide powder of claim 1.
  • 9. The powder of claim 2, wherein the proportion of particles with a diameter of 200 nm or more is 0 to 5%, based on the total number of particles.
  • 10. The powder of claim 2, wherein the proportion of particles with a diameter of up to 60 nm is 0 to 10%, based on the total number of particles.
  • 11. The powder of claim 3, wherein the proportion of particles with a diameter of up to 60 nm is 0 to 10%, based on the total number of particles.
  • 12. The powder of claim 1, which is x-ray amorphous.
  • 13. The powder of claim 1, comprising a proportion of chloride of not more than 100 ppm.
  • 14. The powder of claim 1, comprising a proportion of chloride of not more than 50 ppm.
  • 15. The powder of claim 1, wherein a proportion of non-spherical aggregated particles is 0.5 to 10% by weight, based on the powder.
  • 16. The powder of claim 1, wherein the BET surface area is 23 to 28 m2/g.
  • 17. The powder of claim 1, having a number-based median particle diameter of 100±20.
  • 18. The powder of claim 1, wherein a proportion of non-spherical aggregated particles is 4 to 10% by weight, based on the powder.
  • 19. The powder of claim 1, wherein a proportion of non-spherical aggregated particles is 0.5 to 8% by weight, based on the powder.
  • 20. The powder of claim 1, wherein a proportion of non-spherical aggregated particles is 4 to 8% by weight, based on the powder.
Priority Claims (1)
Number Date Country Kind
102008064284.3 Dec 2008 DE national
PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/EP2009/064819 11/9/2009 WO 00 6/7/2011