The present invention relates generally to etching processes.
The resistivity of interconnect materials is the primary determinant of integrated circuit (IC) speed for current and future devices. Patterns are normally generated in these materials by plasma-assisted (subtractive) etching. However, due to the inability to form volatile copper (Cu) etch products during halogen-based plasma etching, damascene technology was introduced to avoid the need for Cu plasma etching. Although damascene technology played an essential role in the initial implementation of Cu metallization, a critical limitation has arisen where the electrical resistivity of Cu increases rapidly as lateral dimensions are reduced below 100 nm, approaching the electron mean free path in Cu (40 nm at 25° C.).
Briefly described, embodiments of the present invention are directed towards methods of etching a metal interconnect layers used in IC products through the use of non-halogen gas based plasma wherein the metal has not been reacted with a halogen gas such as chlorine or bromine, “a non-halogenated metal”. In one embodiment of the present invention, in a reaction chamber, a substrate having a metal interconnect layer comprising a non-halogenated metal deposited thereon is exposed to a plasma formed of non-halogen gas. The plasma generated is maintained for a certain period of time to provide for a desired or expected etching of the metal. In some embodiments, the metal interconnect layer is copper but may also include other metals such as titanium, silver, and gold.
Another exemplary embodiment of the present invention is a method for etching in a reaction chamber a metal interconnect layer comprising a non-halogenated metal deposited on a substrate, the method comprising introducing a gas stream comprised of a non-halogen gas into the reaction chamber; initiating a plasma from the gas stream by energizing one or more electrodes, maintaining the plasma for a desired period of time to etch at least a portion of the metal interconnect layer, abating the gas stream and extinguishing the plasma. In some embodiments of the present invention, the substrate includes, but is not limited to, a silicon wafer or a polymeric substrate such as a printed circuit board. In further embodiments of the present invention, the non-halogen gas may include, but is not limited to, hydrogen, helium, or combinations of hydrogen or helium with other gases such as argon. An exemplary way in which the reaction chamber may create a plasma is a combination of a high voltage electrode connected to a high frequency voltage source such as a high voltage radio frequency (rf) generator and a ground (usually the reaction chamber itself).
The foregoing summarizes beneficial aspects of the present invention, but is not intended to be reflective of the full scope of the present invention as claimed. Additional features and advantages of the present invention are set forth in the following description, are apparent from the description, or learned by practicing the present invention. Moreover, the foregoing summary and following detailed description are exemplary and explanatory, and are intended to provide further explanation of the present invention as claimed.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate multiple exemplary embodiments of the present invention and, together with the description, serve to explain the principles of the present invention. They are not intended in any manner to limit the scope of the present invention. Headings provided herein are for convenience only and do not necessarily affect the scope or meaning of the claimed invention.
a-2e are scanning electron microscope (SEM) images after processing according to an exemplary embodiment of the present invention.
a and 3b are X-ray photoelectron spectroscopy taken from etched samples according to an exemplary embodiment of the present invention.
a and 4b illustrate Cu etch rate and the corresponding DC bias of H2 plasmas under different platen power and coil power according to an exemplary embodiment of the present invention.
a and 5b show the Cu (˜180 nm) edge profile before and after a 8 min H2 plasma when RF2=700 W according to an exemplary embodiment of the present invention.
The subject matter of the various embodiments is described with specificity to meet statutory requirements. However, the description itself is not intended to limit the scope of the claimed invention. Rather, it has been contemplated that the claimed invention can be embodied in other ways, to include different steps or elements similar to the ones described in this document, in conjunction with other present or future technologies. Although the term “step” can be used herein to connote different aspects of methods employed, the term should not be interpreted as implying any particular order among or between various steps herein disclosed unless and except when the order of individual steps is explicitly required. The following description is illustrative and non-limiting to any one aspect.
It should also be noted that, as used in the specification and the claims, the singular forms “a,” “an” and “the” include plural references unless the context clearly dictates otherwise. For example, reference to a component is intended to also include composition of a plurality of components. References to a composition containing “a” constituent are intended to include other constituents in addition to the one named. Also, in describing preferred embodiments, terminology will be resorted to for the sake of clarity. It is intended that each term contemplates its broadest meaning as understood by those skilled in the art and includes all technical equivalents that operate in a similar manner to accomplish a similar purpose.
Ranges can be expressed herein as from “about” or “approximately” one particular value and/or to “about” or “approximately” another particular value. When such a range is expressed, other exemplary embodiments include from the one particular value and/or to the other particular value. The terms “comprising” or “containing” or “including” mean that at least the named component, element, particle, or method step is present in the system or article or method, but does not exclude the presence of other components, materials, particles, or method steps, even if the other such components, material, particles, and method steps have the same function as what is named.
It is also to be understood that the mention of one or more method steps does not preclude the presence of additional method steps or intervening method steps between those steps expressly identified. Similarly, it is also to be understood that the mention of one or more components in a system or composition does not preclude the presence of additional components than those expressly identified. To facilitate an understanding of the principles and features of the present invention, embodiments are explained hereinafter with reference to implementation in illustrative embodiments.
Initially, the transition from patterning Al to patterning Cu in semiconductor processing was unsuccessful because, unlike Al, Cu did not form volatile halogenated etch products at temperatures below 180° C. This limitation inhibited the subtractive plasma etching of Cu at temperatures compatible with organic resist materials. Even with the implementation of “hard” masks such as SiO2, difficulties were encountered because considerable sputtering of the mask material occurred as a result of the combined effects of significant ion bombardment energy and elevated temperature needed to obtain adequate etch rates and anisotropic etch profiles. These restrictions led to the introduction of damascene technology in 1997. In this process, the need to subtractively pattern or etch Cu is avoided by first plasma etching trenches or vias in a dielectric layer to form the regions where Cu interconnects are to be placed. Cu films are then electroplated into the vias, followed by chemical mechanical planarization/polishing (CMP) removal of the Cu overburden that exists above the dielectric film.
Damascene technology has played an essential role in the initial implementation of Cu metallization. However, a critical limitation in this approach to Cu patterning has arisen due to the adherence of the IC industry to Moore's Law and thus the reduction of minimum feature sizes, currently (2010) at 45 nm, as described by the International Technology Roadmap for Semiconductors (ITRS). This limitation is the “size effect” of Cu, a phenomenon in which the electrical resistivity of Cu increases rapidly as lateral dimensions are reduced below 100 nm, thereby approaching the electron mean free path in Cu (40 nm at 25° C.). As a result of the resistivity increase, device and circuit speed decrease with decreasing pattern or feature size. The size effect is caused by electron scattering from both Cu sidewalls and grain boundaries. Two approaches exist to reduce or eliminate this size effect: decrease the Cu sidewall/surface roughness and grow larger Cu grains. However, grain growth of Cu in damascene technology is dramatically hindered by the narrow geometries and impurities introduced into Cu that result from CMP and plating processes; that is, grain boundaries are pinned at the sidewalls, thereby limiting grain growth and electroplating is a liquid process where solvents and additives are present to permit defect-free filling of narrow, high aspect ratio trenches. Therefore, the Cu size effect that causes degradation of current and future device speed cannot be suppressed by existing Cu patterning technology.
With the exception of Cu, plasmas are used to define patterns for the films used in IC fabrication. In comparison to damascene technology, subtractive plasma etching begins with a blanket, high purity (sputtered or evaporated instead of plated) and annealed Cu film which therefore has reasonable grain size (˜1.5 times the film thickness in the sub-100 nm regime). The resistivity of the blanket, high purity, annealed Cu film should therefore increase only moderately when patterned by plasma etching. An increase in resistivity is expected due to the small line width (<100 nm) and thus surface scattering that takes place in Cu patterns with widths similar to the electron mean free path. Because plasma-based etching can be used to pattern metal (conducting) films other than Cu, this method of reducing the size effect can be evaluated.
Halogen-based (specifically chlorine-containing) plasmas have to date been the ones investigated to plasma etch Cu. In large part this has occurred because copper chlorides have the highest volatility of any halogen-containing Cu compound. Furthermore, other conducting films such as Al, W, and heavily doped polycrystalline silicon have been successfully etched by chlorine-based plasmas for many years. However, removal of Cu etch products from the surface is hindered due to the low volatility of Cu halides. High temperatures (>180° C.) have been generally invoked to enhance desorption of Cu chlorides. Alternatively, photon-enhanced removal of Cu chlorides at temperatures below 100° C. by laser, UV, or infrared radiation has been reported. Both these approaches introduce complexity and control issues into the patterning process. For example, high temperatures greatly limit the choice of mask materials and lead to etch system compatibility issues, while exposure of the etching surface to photons increases etch reactor complexity although more reasonable temperatures are apparently possible. In order to avert problems with product desorption, Cu chlorides formed by chlorine- or bromine-containing plasmas have been removed by immersion of the halogenated Cu layers in dilute HCl solutions.
The present invention provides a relatively low-temperature alternative than described above. Metal interconnect layers comprised of non-halogenated metals may be etched using non-halogen gas based plasmas at relatively low temperatures when compared to the chlorination etch processes described above.
Silicon wafer 102 has deposited thereon a non-halogenated copper layer 104. Copper layer 104 can be deposited in reaction chamber 100 or another processing machine, such as a dedicated Cu deposition machine. The present invention is not limited to the use of non-halogen gas based plasmas to etch copper; rather, the scope of the present invention includes, but is not limited to, other metals such as gold and silver. Additionally, the present invention is not limited to the etching of interconnect metal layers but can be used to etch other metal components such as vias or pads.
Copper layer 104 is deposited onto an intermediate layer, such as titanium, to provide for adhesion of copper layer 104 to silicon wafer 100. A mask, such as SiO2 (not shown), can be used to provide a means for pattern generation in the Cu layer, where the mask protects certain regions of the copper layer 104 from etching. It should be noted that the mask is not limited to SiO2 but may also include, but is not limited to, SiNx or other types of hard masks. To etch copper layer 104 according to various embodiments of the present invention, a non-halogen gas is introduced into reaction chamber 100 through gas inlet 106. The present invention is described as using hydrogen, helium or combinations of the two with other gases such as argon, though it should be understood that other gases or gas combinations having similar molecular properties as the previously listed gases are considered to be within the scope of the present invention.
After the non-halogen gas is introduced into reaction chamber 100 via gas inlet 106, a plasma is ignited within reaction chamber 100. To facilitate the generation of the plasma, reaction chamber 100 has electrodes 108 powered by a high frequency, high voltage power source which, in combination with the grounding of reaction chamber 100, provide for a potential across reaction chamber 100. Electrodes 108 can be comprised of at least one high potential electrode and at least one low potential electrode. In typical applications, the low potential electrode is the chamber walls of the reaction chamber 100, as the chamber is typically grounded. The potential causes the excitation of the hydrogen gas introduced through gas inlet 106. In some examples, reaction chamber 100 can also be configured with a rotating magnetic source that causes the plasma to rotate and to be centralized over silicon wafer 102, thereby enhancing the etching effect. The plasma is maintained for a desired period of time, interacting with copper layer 104 to etch at least a portion of copper layer 104.
Experiment I
Plasma etching of 100 nm Cu films was performed in an inductively coupled plasma (ICP) reactor.
Further etch studies on blanket Cu samples were performed. X-ray photoelectron spectroscopy (XPS) was used to probe blanket Cu surfaces before and after an 8 min H2 etch cycle.
Because Ar ion bombardment should assist in the removal of Cu etch products due to the high atomic weight and thus momentum transfer, the effect of different H2/Ar plasma mixtures was investigated.
Preliminary effects of temperature changes were also investigated by increasing the substrate temperature from 10° C. to 40° C. in 15° C. increments. H2 plasma etch conditions were substantially or the same as those of previous etch studies, although 300 nm thick Cu samples were used to allow etch depths to be measured by profilometry and thereby obtain etch rates. Over this small temperature regime, etch rates were not affected by temperature. Etch rates for all experiments were ˜13 nm/min. Without being held to any specific theory of operation, it is believed that hydrogen, especially in the atomic form, has a high chemical reactivity and lattice mobility. H embrittlement of Cu is an important source of Cu degradation. In a plasma environment, H+ or H− can react with film material and release H into the solid, which can cause the formation of defects or highly metastable phases. Introduction of hydrogen into face centered cubic (f.c.c) metals has resulted in microstructure changes; specifically with copper, micro bubbles can be generated. These observations suggest that Cu hydrides can form as a result of plasma exposure. However, thermodynamic calculations indicate that the vapor pressures of Cu hydrides (CuH, CuH2 or other CuHx species) are too low to substantially enhance vapor phase Cu removal or etching. Because it was observed that the Cu etch rate in a pure H2 plasma was higher than that for the two-step etch process (chlorination followed by hydrogen treatment), alternate mechanisms for Cu etch product desorption may be occurring.
In a H2 plasma, the Cu surface is bombarded by ions and electrons, as well as UV and visible photons. Without being held to any specific theory of operation, it is believed that these particles and photons supply energy to the Cu surface and can enhance etch product removal. Photodesorption of metal atoms have been reported upon exposure of alkali metals such as Na, K, and Cs to photons. Specifically, desorption of sodium atoms was detected even with 40 mW/cm2 cw laser exposure, where the excitation wavelength was 514 nm. As indicated by the atomic spectrum of hydrogen, intense atomic lines in the UV wavelength range of 90-120 nm will be present in the H2 plasma. Although CuH is reported to be thermally unstable, even at 0° C., more recent studies suggest that in the presence of a high hydrogen pressure or high hydrogen activity, CuH might be formed. It is also likely that this reaction can be promoted by the presence of H (e.g., from the plasma atmosphere) which can react with Cu. If sufficient stability of CuH is achieved, desorption of this product can be enhanced by ion and/or photon bombardment. Therefore, photon-assisted desorption of products such as CuH can be important in Cu removal using H2 plasmas.
Experiment II
Copper films of 100 or 300 nm thickness were deposited by e-beam evaporation (CVC E-Beam Evaporator) onto silicon wafers that had been coated with 20 nm of titanium to promote Cu adhesion to silicon. Electroplated Cu films (145 nm electroplated Cu films grown from an 80 nm physical vapor deposited (PVD) seed layer followed by annealing at 200° C. in forming gas for 30 sec) were also created. Cu-coated substrates were sectioned into etch samples ˜1 cm2. Plasma etching of thin Cu films was performed in an inductively coupled plasma (ICP) reactor (Plasma Therm ICP). The substrate temperature was maintained at ˜10° C. using a water cooled chiller connected to the substrate electrode. The H2 gas flow rate was 50 standard cubic centimeters per minute (sccm) and the reactor pressure was maintained at 20 mtorr. The radio frequency power applied to the ICP coil (RF2) was 500 W, whereas the power applied to the substrate (RF1) was 100 W. Both blanket and masked Cu films were investigated in these plasma etch atmospheres. Masked Cu films invoked SiO2 (˜150 nm) as the mask layer. The SiO2 film was deposited in a Plasma Therm PECVD (plasma enhanced chemical vapor deposition) system with 400 sccm SiH4 and 900 sccm N2O as precursors; the substrate electrode was heated to 250° C., the power applied to the electrode was 25 W, and the pressure was maintained at 900 mtorr during the deposition process. Mask patterns were generated by fluorine-based plasma etching within the same ICP reactor: the etch gas was a mixture of 25 sccm Ar, 2 sccm O2, 14 sccm CF4 and 6 sccm C4F6, RF1 was 200 W and RF2 was 100 W, while the process pressure was maintained at 5 mtorr. Chemical analysis of the films and surfaces before and after plasma etching was performed using X-ray photoelectron spectroscopy (XPS). XPS spectra were collected using a Thermo Scientific K-Alpha XPS. Cu film patterns were examined with a scanning electron microscope (SEM, Zeiss SEM Ultra60). Thickness changes of the Cu layer were determined from SEM images and a Wyko Profilometer.
As discussed previously, the reaction chamber is configured with means to produce plasma. The selection of the means to produce the plasma depends on the type of plasma used. In typical semiconductors, the plasma produced is a non-equilibrium or non-thermal plasma. These types of plasmas, which can be used to describe a single plasma, are used to prevent spot heating of reaction products. An examples of a thermal plasma can be a lightning strike or an arc from an arc welder. In one embodiment of the present invention, a reaction chamber has two power supplies, one for coil power (for plasma generation), and the other for platen power (to accelerate ions). Both ion bombardment and photon impingement will likely be influenced by power from these two rf sources. Therefore the Cu etch rate and the corresponding DC bias of H2 plasmas under different platen power (RF1,
a and 5b show the Cu (˜180 nm) edge profile before and after a 8 min H2 plasma when RF2=700 W. Higher coil power yields higher etch rate (˜20 nm/min) but no obvious enhancement of SiO2 mask ablation was observed for higher coil power (RF2). Such results are consistent with an increased ion flux for the process with higher plasma generation power. These observations further confirm that ion bombardment flux is an important component in the low temperature Cu etch process.
Preliminary studies at zero platen power and zero coil power (with the other power supply kept constant) were performed. Because of the inability to strike a plasma without platen power in the Plasma Therm ICP reactor, these experiments were performed in an STS SOE ICP reactor. These initial studies used the same pressure as well as platen and coil powers as those used in the Plasma Therm reactor. Due to the different reactor configuration/size, and the inability to cool the platen to 10° C., the Cu etch rates obtained were different. That is, for this preliminary investigation, reactor power conditions were not adjusted to obtain identical etch rates in the two reactors.
The presently disclosed embodiments are considered in all respects to be illustrative and not restrictive. The scope of the invention is indicated by the appended claims, rather than the foregoing description, and all changes that come within the meaning and range of equivalents thereof are intended to be embraced therein.
This application claims benefit under 35 U.S.C. §119(e) of U.S. Provisional Patent Application No. 61/332,915 filed 10 May 2010, and entitled “Low Temperature Etching and Patterning of Copper by Hydrogen, Helium and Argon-hydrogen Plasma”, which is incorporated by reference as if set forth herein in its entirety.
This invention was made with Government support under Agreement No. CBET-0755607, awarded by the National Science Foundation. The United States Government has certain rights in the invention.
| Number | Date | Country | |
|---|---|---|---|
| 61332915 | May 2010 | US |