Claims
- 1. A method of forming a luminescent coating on a substrate comprising:
- applying a coating composition comprising hydrogen silsesquioxane resin and a phosphor filler onto a substrate; and
- heating the coated substrate at a temperature sufficient to convert the coating composition into a ceramic coating.
- 2. The method of claim 1 wherein the coating composition is applied to the substrate by a process which comprises coating the substrate with a liquid mixture comprising a solvent, the hydrogen silsesquioxane resin and the filler and then evaporating the solvent.
- 3. The method of claim 2 wherein the coated substrate is heated at a temperature in the range of between about 50.degree. C. and about 800.degree. C. for less than about 3 hours.
- 4. The method of claim 1 wherein the coating composition also contains modifying ceramic oxide precursors comprising a compound containing an element selected from the group consisting of titanium, zirconium, aluminum, tantalum, vanadium, niobium, boron and phosphorous wherein the compound contains at least one hydrolyzable substituent selected from the group consisting of alkoxy and acyloxy and the compound is present in an amount such that the coating contains 0.1 to 30 percent by weight modifying ceramic oxide.
- 5. The method of claim 1 wherein the coating composition also contains a platinum, rhodium or copper catalyst in an amount of between about 5 and about 500 ppm platinum, rhodium or copper based on the weight of hydrogen silsesquioxane resin.
- 6. The method of claim 1 wherein the coating composition also contains a material which modifies the surface of the filler.
- 7. The method of claim 1 wherein the coating composition also contains a suspending agent.
- 8. The method of claim 1 wherein the filler is selected from the group consisting of zinc sulfide and cadmium sulfide.
- 9. The method of claim 1 wherein the filler has a particle size in the range of less than about 50 microns.
- 10. The method of claim 1 wherein the filler is present in the coating composition in an amount less than about 90 weight percent.
Parent Case Info
This is a continuation-in-part of copending application Ser. No. 08/028,063 filed on Mar. 8, 1993.
US Referenced Citations (5)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
28063 |
Mar 1993 |
|