Patent Application
20080277823
The present invention relates to a manufacturing method of a film insert molded article.
A film insert molded article in which a film printing a pictograph, a mark, a design or the like thereon is molded integrally with an injection-molded article is formerly known as one of decorating techniques of the injection-molded article.
For example, the film insert molded article is manufactured as follows (see Japanese Patent Laid-Open No. 63-34814). Namely, a decorating film having a display section of a keyboard printed on a face of the front side of a synthetic resin film able to be thermoformed is thermoformed in a shape of a surface of a keyboard panel so that a film for coating is made. The film for coating is then arranged within a die, and molten resin is injected from a rear side of the film for coating into the die so that the film insert molded article is manufactured.
In the above former manufacturing method of the film insert molded article, the film is thermally shrunk when the film arranged within the die is thermoformed. A heat shrinking amount due to the thermoforming is increased as a product size is increased. Therefore, in the former manufacturing method of the film insert molded article, the size of the film arranged within the die is determined by predicting the heat shrinking amount in advance.
However, when the product size of the film insert molded article is increased, variation in the heat shrinking amount is also increased. Accordingly, there are disadvantages in that the actual heat shrinking amount becomes larger than the predicted heat shrinking amount, and no entire surface of the keyboard panel can be coated with the film for coating, and a resin layer is seen in the front in some cases.
Further, when the actual heat shrinking amount is reversely smaller than the predicted heat shrinking amount, there are disadvantages in that an excessive portion is generated in the film for coating arranged within the die, and a wrinkle is generated in the film when the surface of the film insert molded article is coated.
An object of the present invention is to provide a manufacturing method of the film insert molded article in which such disadvantages are dissolved and a resin layer is seen in the front and no wrinkle is generated in the film on the surface of the film insert molded article coated with the film even when dispersion is generated in the heat shrinking amount due to the thermoforming of the film.
Therefore, the present invention is characterized in a manufacturing method of a film insert molded article in which a film for coating thermoformed in a predetermined shape in advance is arranged within a cavity of an injection molding die, and molten resin is injected into the cavity and is molded integrally with the film for coating, and the film insert molded article having a coating plane coated with the film for coating is obtained; the manufacturing method comprising a process for performing printing on a raw material film and forming a printing ink layer; a process for forming a binder layer on the printing ink layer; a process for forming the film for coating by cutting out the raw material film into a size for coating the coating plane and being able to form an outer circumferential bending portion arranged in an outer circumferential side portion of the coating plane of the film insert molded article by adding a width exceeding a heat shrinking amount of the film due to the thermoforming; a process for forming a predetermined three-dimensional shape and the outer circumferential bending portion, by preheating the film for coating and thermoforming the film for coating thereafter; and a process for injecting molten resin into a cavity within which the film for coating forming the three-dimensional shape and the outer circumferential bending portion therein is arranged so as to make the binder layer come into contact with molten resin.
In the manufacturing method of the film insert molded article of the present invention, printing is first performed on the raw material film so that the printing ink layer is formed, and the binder layer is formed on the printing ink layer.
Next, the raw material film is cut out and the film for coating is formed. The film for coating has a size for coating the coating plane of the film insert molded article, and also has a size able to form the outer circumferential bending portion arranged in the outer circumferential side portion of the coating plane of the film insert molded article by adding a width exceeding a heat shrinking amount of the film due to the thermoforming.
Next, after the film for coating is preheated, the film for coating is thermoformed so that the predetermined three-dimensional shape and the outer circumferential bending portion are formed. At this time, the film for coating is formed at a size exceeding the heat shrinking amount of the film due to the thermoforming and able to form the outer circumferential bending portion. Accordingly, even when the heat shrinking amount of the film becomes larger than a predicted heat shrinking amount by its dispersion, the film can be set to a size sufficient to coat the coating plane of the film insert molded article. The three-dimensional shape has a shape formed along the shape of the coating plane of the film insert molded article.
Next, the film for coating in which the three-dimensional shape and the outer circumferential bending portion are formed, is arranged within the cavity of the injection molding die such that the binder layer comes into contact with molten resin. The molten resin is then injected into the cavity. Thus, the molten resin filled within the cavity is cooled and solidified so that the injection-molded article of a shape formed along an shape of the inner plane of the cavity can be obtained. Further, since the binder layer is melted by heat of the molten resin and becomes an adhesive layer, the film for coating is molded integrally with the injection-molded article through the adhesive layer. As a result, it is possible to obtain the film insert molded article in which the coating plane is coated with the film for coating.
At this time, the film for coating has the outer circumferential bending portion and a size sufficient to coat the coating plane of the film insert molded article. Accordingly, it is possible to prevent a resin layer from being seen from the front of the coating plane. Further, since the film for coating has the outer circumferential bending portion, no excessive portion is generated in a portion for coating the coating plane when the film for coating is arranged within the die. Accordingly, it is possible to prevent a wrinkle from being generated in the film on the coating plane.
In the manufacturing method of the present invention, for example, a film made from polyethylene terephthalate resin can be used as the raw material film. When the raw material film is the film constructed by polyethylene terephthalate resin, the film for coating is preferably preheated at a temperature in a range of 150° C. to 190° C. When the preheating temperature is less than 150° C., there is a case in which the predetermined three-dimensional shape and the outer circumferential bending portion cannot be formed in the film for coating. Further, when the preheating temperature exceeds 190° C., there is a case in which the film for coating is damaged.
In accordance with study of the present inventors, the heat shrinkage due to the thermoforming of the film for coating lies within 1% of a maximum width of the film for coating, and variation in the heat shrinking amount lies within ±10% with respect to the heat shrinking amount. Therefore, in the manufacturing method of the present invention, the outer circumferential bending portion of the film for coating preferably has a width (α) of 1.1% or more of the maximum width (L) of the coating plane. In accordance with such a construction, the outer circumferential bending portion arranged in the outer circumferential side portion of the coating plane can be formed in the film for coating after the thermoforming even when the heat shrinkage due to the thermoforming of the film for coating becomes the largest. Thus, it is possible to reliably prevent a resin layer from being seen in the front on the coating plane.
Further, in the manufacturing method of the present invention, the three-dimensional shape of the film for coating may include an emboss portion. When a switch member or the like is arranged below the emboss portion, the emboss portion becomes a pressing portion with respect to the switch member.
Further, in the manufacturing method of the present invention, when the three-dimensional shape of the film for coating includes the emboss portion, the injection molding die preferably has a shape in which a portion corresponding to the emboss portion of the film insert molded article becomes a through hole. In accordance with the injection molding die, it is possible to obtain the film insert molded article having the through hole in the portion corresponding to the emboss portion, and a switch member or the like operated by pressing the emboss portion can be arranged in the through hole.
a) and 1(b) are a plan view and an explanatory sectional view showing the structure of a raw material film in an embodiment of the present invention;
An embodiment of the present invention will next be explained in further detail with reference to the accompanying drawings.
First, as shown in
A film made from polyethylene terephthalate resin is preferably used as the plastic film 10 since it is excellent in aptitude with respect to printing, thermoforming property or the like. However, a film constructed by other resins such as polycarbonate resin or the like may be also used. The above printing can be performed by a silk screen method or an offset method. A color number of ink forming the printing ink layer 20 can be suitably determined by a design of the film insert molded article as a product.
Next, a binder is printed so as to be overlapped on the printing ink layer 20 so that a binder layer 30 is formed. The binder is an adhesive with respect to molding resin, and is dissolved by heat of molten resin in injection molding so that an adhesive layer is formed and adheres the printing ink layer 20 and an injection-molded article.
Next, the plastic film 10 is cut with respect to each printing ink layer 20, and a film 11 for coating shown in
At this time, the film 11 for coating has a size that coats the coating plane of the film insert molded article added with a width exceeding a heat shrinking amount due to thermoforming of the film 11 for coating. The film 11 for coating is cut out to a size able to form an outer circumferential bending portion 12 arranged in an outer circumferential side portion of the coating plane.
Specifically, the film 11 for coating has a heat shrinking amount of 1% by the thermoforming, and variation in the heat shrinking amount is +10% of the heat shrinking amount. Namely, the film 11 for coating shows heat shrinkage of 0.9 to 1.1% by the thermoforming.
Here, when a maximum width of the coating plane is set to L and a maximum width of the film 11 for coating is set to be equal to the maximum width of the coating plane, the maximum width of the film 11 for coating after the thermoforming becomes 0.989 L to 0.991 L and becomes smaller than L. Accordingly, a resin layer is seen from the front on the coating plane.
Therefore, in this embodiment, the film 11 for coating is formed at a size to which a width a of 1.1% or more of the maximum width L of the coating plane, which exceeds the heat shrinking amount, is added, i.e., at a size of L+α. The heat shrinking amount in the thermoforming of the film 11 for coating is 1% (0.01 L), and dispersion (Δ) of the heat shrinking amount is 10% of its maximum (Δ=0.01 L×0.1=0.001 L) of the heat shrinking amount (0.01 L).
However, if the above width α is added, the film 11 for coating becomes a size in the range of 0.989 L+α to 0.991 L+α by the heat shrinkage. Further, since α>1.1, the entire size becomes larger than L, and it is possible to prevent the resin layer from being seen from the front on the coating plane.
Next, the film 11 for coating is thermoformed. Specifically, the film 11 for coating is first preheated. In the case of a polyethylene terephthalate film, the temperature at this time is in a range of 150° C. to 190° C., and is preferably about 160° C. After the film 11 for coating is heated for several seconds, the film 11 for coating is set to a press die, and is pressed.
As this result, as shown in
The three-dimensional shape 13 is formed along the shape of the coating plane of the film insert molded article. It is possible to prevent the generation of a wrinkle on the coating plane of the film insert molded article by forming the three-dimensional shape 13 in advance.
Next, as shown in
When the molten resin is injected into the cavity 15 by the injection molding, the molten resin filled within the cavity 15 is cooled and solidified. Thus, as shown in
At this time, as shown in
In the case where there is no outer circumferential bending portion 12, as shown in
In the manufacturing method of this embodiment, as shown in
Therefore, when the film 11 for coating has the emboss portion 13a, as shown in
Further, when the film 11 for coating has the emboss portion 13a, as shown in
| Number | Date | Country | Kind |
|---|---|---|---|
| 2007-124505 | May 2007 | JP | national |